NEW METHOD FOR EXTRACTING LITHIUM FROM SALT LAKE BRINE

Abstract

A new method for extracting lithium from salt lake brine, comprising the following steps: a salt lake old brine raw material, desorption liquid, low-magnesium water, and adsorption tail liquid pass through an old brine feeding pipe (2), a desorption liquid feeding pipe (4), a low-magnesium water top desorption liquid feeding pipe (3), and an adsorption tail liquid top desorption liquid feeding pipe (11), respectively, which are located above and below a rotary disc of a multi-way valve system (1); and after respectively entering corresponding adsorption columns (6) by means of a duct and channel within the multi-way valve system (1), the entire process procedure is completed from an adsorption tail liquid discharge pipe (7), a qualified desorption liquid discharge pipe (10), a lithium-containing old brine discharge pipe (8), and an adsorption tail liquid top desorption liquid discharge pipe (5); and the adsorption columns (6) are connected in series or in parallel by means of channels located in the multi-way valve system (1). The feature in which a multi-way valve device is simple and easy to operate is utilized, and in comparison with a fixed bed operating system, the utilization rate of lithium adsorbent may be increased by over 20%, the utilization efficiency of the lithium adsorbent may be increased by over 40%, and production costs may be reduced by 30-50%. Therefore, the stability of a qualified desorption liquid is improved, stable production is guaranteed, and year-round constant operation may be achieved.

Claims

1. A new method for extracting lithium from salt lake brine, comprising the following steps: allowing a salt lake brine, desorption solution, low-magnesium solution and barren brine to pass through a feeding pipe for brine, a feeding pipe for desorption solution, a feeding pipe for low-magnesium solution for pushing back desorption solution and a feeding pipe for barren brine for pushing back desorption solution respectively, wherein the feeding pipes are located above and below a rotary disc of a multi-way valve system, then pass through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns, and finally discharge from a discharging pipe for barren brine, a discharging pipe for qualified liquid, a discharging pipe for lithium-containing brine and a discharging pipe for barren brine for pushing back desorption solution, thereby completing the whole process, wherein the adsorption columns are connected in series or in parallel via the channels in the multi-way valve system; and wherein the whole process comprises the following steps: (1) in an adsorption zone, carrying out: feeding an brine from a tank for brine into an adsorption tower N1 through the feeding pipe for brine to perform adsorption of lithium ions onto an adsorbent, producing an barren brine free of lithium, and discharging the barren brine free of lithium into a tank for barren brine through the discharging pipe for barren brine; (2) in a zone for replacing by low-magnesium solution, carrying out the following after the adsorbent is saturated: feeding a low-magnesium solution from a tank for low-magnesium solution into an adsorption tower N2 through a feeding pipe for low-magnesium solution to push back the lithium-containing brine that is not adsorbed by the adsorbent to the tank for brine to wait for the next adsorption; (3) in a desorption zone by desorption solution, carrying out the following after the completion of pushing back lithium-containing brine by the low-magnesium solution: feeding a desorption solution from a tank for desorption solution into an adsorption tower N3 through the feeding pipe for desorption solution to desorb the resin, producing a rich solution, of which a first half is discharged through a discharging pipe for low-magnesium to the tank for low-magnesium solution for use in the zone for replacing by low-magnesium solution, and a second half is discharged into a tank for the qualified liquid and finally sent to the next step; (4) in a zone for pushing back desorption solution by barren brine, carrying out: feeding the barren brine from the tank for barren brine into an adsorption tower N4 through the feeding pipe for barren brine for pushing back desorption solution, and discharging the desorption solution containing trace lithium through a discharging pipe for desorption solution recovery into the tank for desorption solution; and (5) setting a rotation time of the multi-way valve to realize shift of columns according to the process requirements.

2. The new method for extracting lithium from salt lake brine of claim 1, wherein the number of the adsorption towers N1, N2, N3 and N4 is one or more, connected in series or parallel mode.

3. The new method for extracting lithium from salt lake brine of claim 1, wherein the number of the adsorption towers N1, N2, N3 and N4 can be matched with the channels of the multi-way valve system according to process requirements.

4. The new method for extracting lithium from salt lake brine of claim 1, wherein each of the adsorption towers is filled with a lithium ion adsorbent.

5. The new method for extracting lithium from salt lake brine of claim 1, wherein the desorption solution is selected from the group consisting of 0.1-50% (w/w) aqueous electrolyte solution, desalted water, 0.1-50% (w/w) saline solution, 0.1-36% (w/w) hydrochloric acid solution, 0.1-50% (w/w) sodium hydroxide solution, and any mixture thereof.

6. The new method for extracting lithium from salt lake brine of claim 5, wherein the desorption solution is 0.5% (w/w) aqueous electrolyte solution, desalted water or 0.5% (w/w) hydrochloric acid solution.

7. The new method for extracting lithium from salt lake brine of claim 6, wherein the desorption solution is desalted water.

8. The new method for extracting lithium from salt lake brine of claim 1, wherein the temperature of the desorption solution is 5-60° C.

9. The new method for extracting lithium from salt lake brine of claim 8, wherein the temperature of the desorption solution is 10-50° C.

10. The new method for extracting lithium from salt lake brine of claim 9, wherein the temperature of the desorption solution is 30-40° C.

11. The new method for extracting lithium from salt lake brine of claim 1, wherein the rotation shift time of the multi-way valve system is 0.01-24 hours.

12. The new method for extracting lithium from salt lake brine of claim 1, comprising the following steps: (1) feeding the salt lake brine at a flow rate of 2 BV/h into the N1 resin tower of the multi-way valve device to perform adsorption of lithium in the feed liquid by the resin in the resin column, and discharging out the resulted barren brine from the device; (2) after the adsorbent is saturated, feeding the low-magnesium solution from the tank for low-magnesium solution into the adsorption tower N2 through the low-magnesium solution at a flow rate of 5 BV/h to push back the lithium-containing brine that is not adsorbed by the adsorbent to the tank for brine for the next adsorption; (3) desorbing the N3 resin tower with a desalted water of 38° C. at a flow rate of 15 BV/h to produce a lithium chloride solution which then enters the tank for qualified liquid; (4) replacing and recovering the water in the N4 resin tower by the barren brine at a flow rate of 0.8 BV/h; and (5) setting the multi-way valve to have a shift time of 24 min.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0019] FIG. 1 is a schematic diagram of inlet and outlet pipelines of the multi-way valve system.

[0020] FIG. 2 is a schematic diagram of process flow of lithium extraction from salt lake brine.

DETAILED DESCRIPTION

[0021] In order to make the content of the present invention easier to understand clearly, the present invention will be described in further detail below according to specific embodiments of the present invention and in conjunction with the accompanying drawings.

[0022] FIG. 1 is a schematic diagram of inlet and outlet pipelines of a multi-way valve system, wherein: 1. multi-way valve system; [0023] 2. feeding pipe for brine; [0024] 3. feeding pipe for low-magnesium solution for pushing back desorption solution; [0025] 4. feeding pipe for desorption solution; [0026] 5. discharging pipe for barren brine for pushing back desorption solution; [0027] 6. adsorption column; [0028] 7. discharging pipe for barren brine; [0029] 8. discharging pipe for lithium-containing brine; [0030] 9. discharging pipe for low-magnesium solution; [0031] 10. discharging pipe for qualified liquid; [0032] 11. feeding pipe for barren brine for pushing back desorption solution.

[0033] FIG. 2 is a schematic diagram of process flow of lithium extraction from salt lake brine, wherein: [0034] 12. tank for brine; [0035] 13. tank for desorption solution; [0036] 14. tank for barren brine; [0037] 15. tank for qualified liquid; [0038] 16. tank for low-magnesium solution; [0039] N1, N2, N3, N4: adsorption towers.

Example 1

[0040] An brine, desalted water at −38° C. as desorption solution, low-magnesium solution, and barren brine were passed through a feeding pipe 2 for brine, a feeding pipe 3 for low-magnesium solution for pushing back desorption solution, a feeding pipe 4 for desorption solution, and a feeding pipe 11 for barren brine for pushing back desorption solution respectively wherein the feeding pipes 2, 3, 4 and 11 were located above and below a rotary disc of a multi-way valve system 1 (with a valve diameter of 1.5 inches, a rotation switching time of 0.5 h), then passed through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns 6 (filled with Lithium adsorbent LX-10Li, produced by XI'AN SUNRESIN NEW MATERIALS CO., LTD.), and finally respectively discharged from the a discharging pipe 7 for barren brine, a discharging pipe 8 for lithium-containing brine, a discharging pipe 9 for low-magnesium solution and a discharging pipe 10 for qualified liquid, thereby completing the whole process.

The distribution of each zone was as follows:

[0041] 1. Adsorption zone: An brine from an tank 12 for brine entered adsorption columns 1 # to 12 # (twelve adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N1) through the feeding pipe 2 for brine, so that lithium ions were adsorbed on the adsorbent, and the brine which was free of lithium ions after adsorption entered a tank 14 for barren brine through the discharging pipe for barren brine.

[0042] 2. Zone for pushing back brine by low-magnesium solution: After the adsorbent was saturated, low-magnesium solution from the tank 16 for low-magnesium solution entered adsorption columns 13 # to 17 # (i.e. five adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N2) through the feeding pipe 3 for low-magnesium solution for pushing back desorption solution, so that the lithium-containing brine was pushed back by the low-magnesium solution to the tank 12 for brine to wait for the next adsorption.

[0043] 3. Desorption zone by desorption solution: After the completion of pushing back lithium-containing brine by the low-magnesium solution, desalted water as desorption solution from the tank 13 for desorption solution entered adsorption columns 18 # to 27 # (ten adsorption columns operated in series through the channels in the multi-way valve, forming a adsorption tower N3) through the feeding pipe 4 for desorption solution to desorb the resin, resulting in a rich solution, of which a first half was discharged from the discharging pipe 10 for low-magnesium to the tank 16 for low-magnesium solution for use in the zone for pushing back brine by low-magnesium solution, and a second half was discharged into a tank 15 for the qualified liquid and was finally sent to a next step.

[0044] 4. Zone for pushing back desorption solution by barren brine: After the desorption of the adsorbent was completed, some desorption solution containing trace lithium was left in the resin column, and in order to recover the left desorption solution and thus reduce consumption, the left desorption solution in the adsorption column was pushed back by the barren brine. The barren brine from the tank 14 for barren brine entered the adsorption column 28 # (one adsorption column operated in a single column, that is, the adsorption tower N4) through the feeding pipe 11 for barren brine for pushing back desorption solution, and the desorption solution containing trace lithium was discharged from the discharging pipe for desorption solution recovery into the tank for desorption solution.

[0045] The system had a feed flow rate of 2 t/h for the brine, twenty-eight resin columns in total, with each column being filled with 1 m.sup.3 of resin and the total amount of adsorbent in the system being 28 m.sup.3, and a switching time of 30 min. The brine at inlet had a lithium content of 3000 ppm and a magnesium ion concentration of 120 g/L. After treatment by the system, the adsorption tail fluid had a lithium ion concentration of 10 ppm and a magnesium ion concentration of 110 g/L. The qualified liquid had a lithium ion concentration of 650 ppm and a magnesium ion concentration of 1.5 g/L. For comparison, a fixed bed system had a feed flow rate of 2 t/h, three resin columns in total, with each column being filled with 20 m.sup.3 of resin and the total amount of resin in the system being 60 m.sup.3, a lithium content of 3000 ppm at inlet, and a magnesium ion concentration of 120 g/L at inlet. After treatment by the fixed bed system, the barren brine had a lithium ion content of 400 ppm, and the qualified liquid had a lithium ion concentration of 300 ppm and a magnesium ion concentration of 3 g/L.

Example 2

[0046] An brine, desalted water at −10° C. as desorption solution, low-magnesium solution, and barren brine were passed through a feeding pipe 2 for brine, a feeding pipe 3 for low-magnesium solution for pushing back desorption solution, a feeding pipe 4 for desorption solution, and a feeding pipe 11 for barren brine for pushing back desorption solution respectively wherein the feeding pipes 2, 3, 4 and 11 were located above and below a rotary disc of a multi-way valve system 1 (with a valve diameter of 1.5 inches, a rotation switching time of 1 h), then passed through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns 6 (filled with Lithium adsorbent LX-10Li, produced by XI'AN SUNRESIN NEW MATERIALS CO., LTD.), and finally respectively discharged from a discharging pipe 7 for barren brine, a discharging pipe 8 for lithium-containing brine, a discharging pipe 9 for low-magnesium solution and a discharging pipe 10 for qualified liquid, thereby completing the whole process.

The distribution of each zone was as follows:

[0047] 1. Adsorption zone: An brine from an tank 12 for brine entered adsorption columns 2 # to 13 # (twelve adsorption columns operated in parallel through the channels in the multi-way valve, forming an adsorption tower N1) through the feeding pipe 2 for brine, so that lithium ions were adsorbed on the adsorbent, and the brine which was free of lithium ions after adsorption entered a tank 14 for barren brine through the discharging pipe 7 for barren brine.

[0048] 2. Zone for pushing back brine by low-magnesium solution: After the adsorbent was saturated, low-magnesium solution from the tank 16 for low-magnesium solution entered adsorption columns 14 # to 18 # (five adsorption columns operated in parallel through the channels in the multi-way valve, forming an adsorption tower N2) through the feeding pipe 3 for low-magnesium solution for pushing back desorption solution, so that the lithium-containing brine was pushed back by the low-magnesium solution to the tank 12 for brine to wait for the next adsorption.

[0049] 3. Desorption zone by desorption solution: After the completion of pushing back lithium-containing brine by the low-magnesium solution, desorption solution from the tank 13 for desorption solution entered adsorption columns 19 # to 28 # (ten adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N3) through the feeding pipe 4 for desorption solution to desorb the resin, resulting in a rich solution, of which a first half was discharged from the discharging pipe 10 for low-magnesium to the tank 16 for low-magnesium solution for use in the zone for pushing back brine by low-magnesium solution, and a second half was discharged into the tank 15 for the qualified liquid and was finally sent to a next step.

[0050] 4. Zone for pushing back desorption solution by barren brine: After the desorption of the adsorbent was completed, some desorption solution containing trace lithium was left in the resin column, and in order to recover the left desorption solution and thus reduce consumption, the left desorption solution in the adsorption column was pushed back by the barren brine. The barren brine from the tank 14 for barren brine entered the adsorption column 1 # (one adsorption column operated in a single column, that is, the adsorption tower N4) through the feeding pipe 11 for barren brine for pushing back desorption solution, and the desorption solution containing trace lithium was discharged from the discharging pipe for desorption solution recovery into the tank for desorption solution.

[0051] The system had a feed flow rate of 2 t/h for the brine, twenty-eight resin columns in total, with each column being filled with 1 m.sup.3 of resin and the total amount of adsorbent in the system being 28 m.sup.3, and a switching time of 60 min. The brine at inlet had a lithium content of 3000 ppm and a magnesium ion concentration of 120 g/L. After treatment by the system, the adsorption tail fluid had a lithium ion concentration of 9 ppm and a magnesium ion concentration of 110 g/L. The qualified liquid had a lithium ion concentration of 430 ppm and a magnesium ion concentration of 2.7 g/L.

Example 3

[0052] An brine, desalted water at −20° C. as desorption solution, low-magnesium solution, and barren brine were passed through a feeding pipe 2 for brine, a feeding pipe 3 for low-magnesium solution for pushing back desorption solution, a feeding pipe 4 for desorption solution, and a feeding pipe 11 for barren brine for pushing back desorption solution respectively wherein the feeding pipes 2, 3, 4 and 11 were located above and below a rotary disc of a multi-way valve system 1 (with a valve diameter of 1.5 inches, a rotation switching time of 2 h), then passed through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns 6 (filled with Lithium adsorbent LX-10Li, produced by XI'AN SUNRESIN NEW MATERIALS CO., LTD.), and finally respectively discharged from the a discharging pipe 7 for barren brine, a discharging pipe 8 for lithium-containing brine, a discharging pipe 9 for low-magnesium solution and a discharging pipe 10 for qualified liquid, thereby completing the whole process.

The distribution of each zone was as follows:

[0053] 1. Adsorption zone: An brine from an tank 12 for brine entered adsorption columns 3 # to 14 # in adsorption columns sets (twelve adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N1) through the feeding pipe 2 for brine, so that lithium ions were adsorbed on the adsorbent, and the brine which was free of lithium ions after adsorption entered a tank 14 for barren brine tank through the discharging pipe 7 for barren brine.

[0054] 2. Zone for pushing back brine by low-magnesium solution: After the adsorbent was saturated, the low-magnesium solution from the tank 16 for low-magnesium solution entered adsorption columns 15 # to 19 # (five adsorption columns operated in parallel through the channels in the multi-way valve, forming an adsorption tower N2) through the feeding pipe 3 for low-magnesium solution for pushing back desorption solution, so that the lithium-containing brine was pushed back by the low-magnesium solution to the tank 12 for brine to wait for the next adsorption.

[0055] 3. Desorption zone by desorption solution: After the completion of pushing back lithium-containing brine by the low-magnesium solution, desorption solution from the tank 13 for desorption solution entered adsorption columns 20 # to 1 # (ten adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N3) through the feeding pipe 4 for desorption solution to desorb the resin, resulting in a rich solution, of which a first half was discharged from the discharging pipe 10 for low-magnesium to the tank 16 for low-magnesium solution for use in the zone for pushing back brine by low-magnesium solution, and a second half was discharged into a tank 15 for the qualified liquid and was finally sent to a next step.

[0056] 4. Zone for pushing back desorption solution by barren brine: After the desorption of the adsorbent was completed, some desorption solution containing trace lithium was left in the resin column, and in order to recover the left desorption solution and thus reduce consumption, the left desorption solution in the adsorption column was pushed back by the barren brine. The barren brine from the tank 14 for barren brine entered the adsorption column 2 # (one adsorption column operated in a single column, that is, the adsorption tower N4) through the feeding pipe 11 for barren brine for pushing back desorption solution, and the desorption solution containing trace lithium was discharged from the discharging pipe for desorption solution recovery into the tank for desorption solution.

[0057] The system had a feed flow rate of 2 t/h for the brine, twenty-eight resin columns in total, with each column being filled with 1 m.sup.3 of resin and the total amount of adsorbent in the system being 28 m.sup.3, and a switching time of 120 min. The brine at inlet had a lithium content of 3000 ppm and a magnesium ion concentration of 120 g/L. After treatment by the system, the adsorption tail fluid had a lithium ion concentration of 7 ppm and a magnesium ion concentration of 108 g/L. The qualified liquid had a lithium ion concentration of 510 ppm and a magnesium ion concentration of 2.2 g/L.

Example 4

[0058] An brine, desalted water at −30° C. as desorption solution, low-magnesium solution, and barren brine were passed through a feeding pipe 2 for brine, a feeding pipe 3 for low-magnesium solution for pushing back desorption solution, a feeding pipe 4 for desorption solution, and a feeding pipe 11 for barren brine for pushing back desorption solution respectively wherein the feeding pipes 2, 3, 4 and 11 were located above and below a rotary disc of a multi-way valve system 1 (with a valve diameter of 1.5 inches, a rotation switching time of 20 min), then passed through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns 6 (filled with Lithium adsorbent LX-10Li, produced by XI'AN SUNRESIN NEW MATERIALS CO., LTD.), and finally respectively discharged from the a discharging pipe 7 for barren brine, a discharging pipe 8 for lithium-containing brine, a discharging pipe 9 for low-magnesium solution and a discharging pipe 10 for qualified liquid, thereby completing the whole process.

The distribution of each zone was as follows:

[0059] 1. Adsorption zone: An brine from an tank 12 for brine entered adsorption columns 4 # to 15 # (twelve adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N1) through the feeding pipe 2 for brine, so that lithium ions were adsorbed on the adsorbent, and the brine which was free of lithium ions after adsorption entered a tank 14 for barren brine through the discharging pipe 7 for barren brine.

[0060] 2. Zone for pushing back brine by low-magnesium solution: After the adsorbent was saturated, low-magnesium solution from the tank 16 for low-magnesium solution entered adsorption columns 16 # to 20 # (five adsorption columns operated in parallel through the channels in the multi-way valve, forming an adsorption tower N2) through the feeding pipe 3 for low-magnesium solution for pushing back desorption solution, so that the lithium-containing brine was pushed back by the low-magnesium solution to the tank 12 for brine to wait for the next adsorption.

[0061] 3. Desorption zone by desorption solution: After the completion of pushing back lithium-containing brine by the low-magnesium solution, desorption solution from the tank 13 for desorption solution entered adsorption columns 21 # to 2 # (ten adsorption columns operated in parallel through the channels in the multi-way valve, forming an adsorption tower N3) through the feeding pipe 4 for desorption solution to desorb the resin, resulting in a rich solution, of which a first half was discharged from the discharging pipe 10 for low-magnesium to the tank 16 for low-magnesium solution for use in the zone for pushing back brine by low-magnesium solution, and a second half was discharged into a tank 15 for the qualified liquid and was finally sent to a next step.

[0062] 4. Zone for pushing back desorption solution by barren brine: After the desorption of the adsorbent was completed, some desorption solution containing trace lithium was left in the resin column, and in order to recover the left desorption solution and thus reduce consumption, the left desorption solution in the adsorption column was pushed back by the barren brine. The barren brine from the tank 14 for barren brine entered the adsorption column 3 # (one adsorption column operated in a single column, that is, the adsorption tower N4) through the feeding pipe 11 for barren brine for pushing back desorption solution, and the desorption solution containing trace lithium was discharged from the discharging pipe for desorption solution recovery into the tank for desorption solution.

[0063] The system had a feed flow rate of 2 t/h for the brine, twenty-eight resin columns in total, with each column being filled with 1 m.sup.3 of resin and the total amount of adsorbent in the system being 28 m.sup.3, and a switching time of 20 min. The brine at inlet had a lithium content of 3000 ppm and a magnesium ion concentration of 120 g/L. After treatment by the system, the adsorption tail fluid had a lithium ion concentration of 14 ppm and a magnesium ion concentration of 109 g/L. The qualified liquid had a lithium ion concentration of 550 ppm and a magnesium ion concentration of 1.9 g/L.

Example 5

[0064] An brine, desalted water at −38° C. as desorption solution, low-magnesium solution, and barren brine were passed through a feeding pipe 2 for brine, a feeding pipe 3 for low-magnesium solution for pushing back desorption solution, a feeding pipe 4 for desorption solution, and a feeding pipe 11 for barren brine for pushing back desorption solution respectively wherein the feeding pipes 2, 3, 4 and 11 were located above and below a rotary disc of a multi-way valve system 1 (with a valve diameter of 1.5 inches, a rotation switching time of 10 min), then passed through openings and channels within the multi-way valve system to respectively enter corresponding adsorption columns 6 (filled with Lithium adsorbent LX-10Li, produced by XI'AN SUNRESIN NEW MATERIALS CO., LTD.), and finally respectively discharged from the a discharging pipe 7 for barren brine, a discharging pipe 8 for lithium-containing brine, a discharging pipe 9 for low-magnesium solution and a discharging pipe 10 for qualified liquid, thereby completing the whole process.

The distribution of each zone was as follows:

[0065] 1. Adsorption zone: An brine from an tank 12 for brine entered adsorption columns 5 # to 16 # (twelve adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N1) through the feeding pipe 2 for brine, so that lithium ions were adsorbed on the adsorbent, and the brine which was free of lithium ions after adsorption entered a tank 14 for barren brine through the discharging pipe 7 for barren brine.

[0066] 2. Zone for pushing back brine by low-magnesium solution: After the adsorbent was saturated, low-magnesium solution from the tank 16 for low-magnesium solution entered adsorption columns 17 # to 21 # (five adsorption columns operated in series through the channels in the multi-way valve, forming the adsorption tower N2) through the feeding pipe for low-magnesium solution for pushing back desorption solution, so that the lithium-containing brine was pushed back by the low-magnesium solution to the tank 12 for brine to wait for the next adsorption.

[0067] 3. Desorption zone by desorption solution: After the completion of pushing back lithium-containing brine by the low-magnesium solution, desorption solution from the tank 13 for desorption solution entered adsorption columns 22 # to 3 # (ten adsorption columns operated in series through the channels in the multi-way valve, forming an adsorption tower N3) through the feeding pipe 4 for desorption solution to desorb the resin, resulting in a rich solution, of which a first half was discharged from the discharging pipe 10 for low-magnesium to the tank 16 for low-magnesium solution for use in the zone for pushing back brine by low-magnesium solution, and a second half was discharged into a tank 15 for the qualified liquid and was finally sent to a next step.

[0068] 4. Zone for pushing back desorption solution by barren brine: After the desorption of the adsorbent was completed, some desorption solution containing trace lithium was left in the resin column, and in order to recover the left desorption solution and thus reduce consumption, the left desorption solution in the adsorption column was pushed back by the barren brine. The barren brine from the tank 14 for barren brine entered the adsorption column 4 # (one adsorption column operated in a single column, that is, the adsorption tower N4) through the feeding pipe for barren brine for pushing back desorption solution, and the desorption solution containing trace lithium was discharged from the discharging pipe for desorption solution recovery into the tank for desorption solution.

[0069] The system had a feed flow rate of 2 t/h for the brine, twenty-eight resin columns in total, with each column being filled with 1 m.sup.3 of resin and the total amount of adsorbent in the system being 28 m.sup.3, and a switching time of 10 min. The brine at inlet had a lithium content of 3000 ppm and a magnesium ion concentration of 120 g/L. After treatment by the system, the adsorption tail fluid had a lithium ion concentration of 37 ppm and a magnesium ion concentration of 109 g/L. The qualified liquid had a lithium ion concentration of 609 ppm and a magnesium ion concentration of 1.6 g/L.

Examples 6-12

[0070] According to the relevant verification effects of Examples 1 to 5, parameters such as the number of resin columns and the switching time in different zones were adjusted, and statistics were performed on the operation conditions, as shown in the following table (the solution concentrations in the table were all mass percent concentrations):

TABLE-US-00001 Zone for pushing Zone for back brine pushing back Desorption by low- desorption solution Switching Adsorption magnesium Desorption solution by Desorption temp. time Examples zone solution zone barren brine solution ° C. (h) Example 12 3 15 1 desalted 35 0.5 6 in series in series in series water Example 12 4 12 2 desalted 50 0.8 7 in parallel in series in series in series water Example 6 5 10 3 desalted 25 1 8 in parallel in series in series in series water 6 in series Example 3 6 8 4 0.1% 35 2 9 in parallel in series in series in series hydrochloric 4 acid in series Example 3 7 6 1 36% 20 3 10 in parallel in series in series hydrochloric 5 acid in series Example 3 8 4 1 0.1% salt 38 0.25 11 in parallel in series in series water 3 in series Example 4 6 8 1 10% salt water 30 0.2 12 in parallel in series in series 3 in series

[0071] The above-mentioned embodiments are only examples for clear description, and are not intended to limit the implementation manner. For those of ordinary skill in the art, changes or modifications in other different forms can also be made on the basis of the above description. There is no need and cannot be exhaustive of all implementations here. And the obvious changes or changes derived from this are still within the protection scope of the present invention.