COMBINED APPARATUS FOR LAYER-BY-LAYER INTERACTIVE ADDITIVE MANUFACTURING WITH LASER THERMAL/MECHANICAL EFFECTS

Abstract

The present invention relates to additive manufacturing field and laser shock peening (LSP) field, in particular to a combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects. In the apparatus, a LSP module and a SLM module operate in alternate so as to perform LSP for the formed part in the forming process of the formed part, and thereby a better strengthening effect of the formed part is achieved. The present invention effectively overcomes the challenges of shape control against deformation and cracking of the formed parts incurred by internal stress and property control against poor fatigue property of the formed parts incurred by metallurgical defects during additive manufacturing, improves fatigue strength and mechanical properties of the formed parts, and realizes high-efficiency and high-quality holistic processing of the formed parts.

Claims

1. A combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects, which comprises: a laser shock peening (LSP) module; a water jetting module; a selective laser melting (SLM) module; a waterproof layer application module comprising a waterproof layer, a drum, a drum support, a threaded lead screw and a motor; a water channel in shape of a hollow square that is enriched with another hollow square; a pneumatic module comprising an air compressor, an air cylinder and a control valve; a base; a hydraulic lifting module comprising a hydraulic cylinder, an electrical system and an liftable workbench; a guide rail; and a powder spreading module comprising a powder supply box, a scraper plate and a motor; wherein, the LSP module and the SLM module are disposed right above the formed part, and can be moved by a mechanical arm; the waterproof layer is disposed at the front side of the formed part, and can be moved front and back by driving the threaded lead screw with the motor, and can be moved up and down by the pneumatic module; a set of drum, drum support, threaded lead screw and motor is disposed at the left side and right side of the formed part respectively, wherein, the drum is disposed on the drum support, and the drum support is disposed on the threaded lead screw; the formed part may be placed on the liftable workbench; the powder spreading module is disposed at the back side of the formed part, and can be moved front and back in a reciprocating manner along the guide rail; the water channel in shape of a hollow square which is enriched with another hollow square is disposed around the liftable workbench, and the pneumatic module is disposed below the water channel; the base is disposed at the lowest part of the entire apparatus.

2. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the LSP module and the SLM module may operate in alternate to attain an effect of strengthening the formed part during forming of the part.

3. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the parameters of LSP are: spot diameter: 3 mm; pulse width: 830 ns; pulse energy: 215 J; and overlapping rate in transverse direction and longitudinal direction: 50%; the parameters of SLM forming are: spot diameter: 80 m; laser wavelength: 1.061.10 m; laser power: 2001,000 W; scanning speed: 5001,000 mm/s; and thickness of spread powder layer: 0.010.1 mm.

4. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the powder spreading module is moved along the guide rail to realize uniform powder spreading and reset; and the liftable workbench of the hydraulic lifting module is lifted/lowered smoothly and steadily by means of the hydraulic lifting module, and is lowered as the height of the workpiece is increased.

5. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the movement trajectory of the SLM module is controlled by a mechanical arm during SLM forming; and the movement trajectory of the LSP module is controlled by a mechanical arm during LSP.

6. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the waterproof layer application module maneuvers the waterproof layer by means of the motor and the pneumatic module, so that the waterproof layer moves, attaches, detaches and resets automatically during LSP of the external surface of the formed part; that is to say, the waterproof layer application module is moved in the vertical direction by means of the pneumatic module so as to control the attachment/detachment of the waterproof layer to/from the external surface of the formed part; the waterproof layer application module is moved in the horizontal direction by means of the motor, so that the waterproof layer is moved and reset, without impact on the removal of the formed part and the following SLM forming.

7. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the waterproof layer is made of a self-adhesive waterproof aluminum foil; after the processing of a formed part is finished, the waterproof layer application module drives the drum to move intermittently by means of the motor, so that the waterproof layer can be replaced and water leakage resulted from reuse of the waterproof layer can be avoided.

8. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, a uniform deionized water film in thickness of 12 mm is formed as a confinement layer by means of the water jetting module during LSP, to increase the peak pressure of the shock wave.

9. The combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects according to claim 1, wherein, the liftable workbench is disposed at the center and surrounded by the water channel in shape of a hollow square that is enriched with another hollow square, to prevent the formed part and the powder from being wetted or flooded by splashed water; and the water in the water channel in shape of a hollow square that is enriched with another hollow square may be recycled via a water circulation module.

10. A method for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects which is performed with the combined apparatus according to claim 1, wherein, specific steps of the method are as follows: before SLM is executed, the powder spreading module is moved along the guide rail in a reciprocating manner to spread powder uniformly on the liftable workbench, and then the powder spreading module automatically returns to its initial position after it accomplishes powder spreading, without any impact on the following operation of the SLM forming module and the LSP module; the movement trajectory of the SLM forming module is controlled by a mechanical arm during its operation; at that point, the waterproof layer is in a safe area, and does not impact the operation of the SLM forming module; SLM forming is performed; the operation of the SLM forming module is finished after a layer of powder is melted; then, LSP is performed by the LSP module; before the LSP module operates, the SLM forming module is moved away by the mechanical arm from the space above the liftable workbench; likewise, the movement trajectory of the LSP module is controlled by the mechanical arm during the operation of the LSP module; after LSP, the operation of the LSP module is finished, the liftable workbench is lowered by the hydraulic lifting module by a certain height, and thereby a space is left for the following powder spreading operation; after the powder spreading module finishes the powder spreading, the SLM forming module melts the next layer of powder; in that way, the SLM module and the LSP module operate in alternate and can be switched freely, till the processing of a given formed part is accomplished; finally, the waterproof layer is moved by the threaded lead screw driven by the motor to the space above the formed part, and is rotated via the drum, so that the waterproof layer used in the previous process deviates from the external surface of the formed part; next, a new waterproof layer is lowered by the pneumatic module to a position 1 mm below the external surface of the formed part, and then is attached to the external surface of the formed part; the water jetting module operates together with the LSP module to provide a confinement layer for LSP on the external surface of the formed part; the waterproof layer and the water channel in shape of a hollow square which is enriched with another hollow square are designed to prevent the formed part and the powder from being wetted or flooded by splashed water, and the water in the water channel may be recycled; and after the LSP, the LSP module and the water jetting module stop operation, the waterproof layer is lifted by the pneumatic module to the initial elevation and detached from the formed part, and is returned by the threaded lead screw driven by the motor to its initial position; thus, the next formed part can be processed.

Description

DESCRIPTION OF DRAWINGS

[0026] FIG. 1 is a front view of an example of the present invention.

[0027] FIG. 2 is a top view of FIG. 1 (excluding the laser shock peening (LSP) module and the selective laser melting (SLM) forming module).

[0028] FIG. 3 is a left view of an example of the present invention during SLM forming.

[0029] FIG. 4 is a front view of an example of the present invention during LSP.

[0030] FIG. 5 is a left view of an example of the present invention during LSP.

[0031] In the figures: 1LSP module; 2water jetting module; 3SLM forming module; 4waterproof layer; 5drum; 6drum support; 7threaded lead screw; 8water channel in shape of a hollow square which is enriched with another hollow square; 9pneumatic module; 10base; 11hydraulic lifting module; 12liftable workbench; 13formed part; 14powder; 15guide rail; 16powder spreading module.

EMBODIMENTS

[0032] To overcome the drawbacks in the prior art, the present invention provides a combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects, which performs laser shock peening (LSP) in the forming process of formed parts mainly by utilizing LSP module and selective laser melting (SLM) module to operate in alternate and switch freely (as shown in FIGS. 1 and 2), and thereby effectively overcomes the challenges of shape control against deformation and cracking of the formed parts incurred by internal stress and property control against poor fatigue property of the formed parts incurred by metallurgical defects during additive manufacturing, improves fatigue strength and mechanical properties of the formed parts, and realizes high-efficiency and high-quality holistic processing of the formed parts.

[0033] See FIGS. 1 and 2. FIG. 1 is a front view of an example of the present invention; FIG. 2 is a top view of FIG. 1 (excluding the LSP module and the SLM forming module). The figures show a combined apparatus for layer-by-layer interactive additive manufacturing with laser thermal/mechanical effects.

[0034] Before SLM is executed, the powder spreading module 16 is moved along the guide rail 15 in a reciprocating manner to spread powder uniformly on the liftable workbench 12, and then the powder spreading module 16 automatically returns to its initial position (as shown in FIG. 2) after it accomplishes powder spreading, without any impact on the following operation of the SLM forming module and the LSP module.

[0035] The movement trajectory of the SLM forming module 3 is controlled by a mechanical arm during its operation (as shown in FIG. 3); at that point, the waterproof layer 4 is in a safe area, and does not impact the operation of the SLM forming module.

[0036] The parameters of SLM forming are: spot diameter: 80 m; laser wavelength: 1.08 m; laser power: 600 W; scanning speed: 800 mm/s; thickness of spread powder layer: 0.02 mm. SLM forming is performed; the operation of the SLM forming module 3 is finished after a layer of powder material is melted; then, LSP is performed by the LSP module 1.

[0037] Before the LSP module operates (as shown in FIGS. 4 and 5), the SLM forming module 3 is moved away by the mechanical arm from the space above the liftable workbench 12; likewise, the movement trajectory of the LSP module is controlled by the mechanical arm during the operation of the LSP module (as shown in FIGS. 4 and 5).

[0038] The parameters of LSP are: spot diameter: 3 mm; pulse width: 10 ns; pulse energy: 8 J, overlapping rate in both transverse direction and longitudinal direction: 50%. LSP is performed; after LSP, the operation of the LSP module is finished, the liftable workbench 12 is lowered by the hydraulic lifting module 11 by a certain height (usually less than 1 mm, because the depth of the layer affected by LSP is about 1 mm), and thereby a space is left for the following powder spreading operation.

[0039] After the powder spreading module 16 finishes the powder spreading, the SLM forming module 3 melts the next layer of powder material.

[0040] In that way, the SLM module 3 and the LSP module 1 operate in alternate and can be switched freely, till the processing of a given formed part is accomplished. Finally, the waterproof layer 4 is moved by the threaded lead screw 7 driven by the motor to the space above the formed part 13, and is rotated by a certain angle via the drum 5, so that the waterproof layer used in the previous process deviates from the external surface of the formed part 13; next, a new waterproof layer is lowered by the pneumatic module 9 to a position 1 mm below the external surface of the formed part, and then is attached to the external surface of the formed part. The water jetting module 2 operates together with the LSP module to provide a confinement layer for LSP on the external surface of the formed part. The waterproof layer and the water channel in shape of a hollow square which is enriched with another hollow square are designed to prevent the formed part 13 and the powder from being wetted or flooded by splashed water (as shown in FIG. 2), and the water in the water channel may be recycled.

[0041] After the LSP, the LSP module 1 and the water jetting module 2 stop operation, the waterproof layer 4 is lifted by the pneumatic module 9 to the initial elevation and detached from the formed part, and is returned by the threaded lead screw 7 driven by the motor to its initial position; thus, the next formed part can be processed.