METHOD OF PRODUCING SILVER FINE PARTICLES

Abstract

A method of producing silver fine particles includes continuously reducing silver ions contained in a silver compound to precipitate silver fine particles by introducing at least two fluids from separate flow paths and mixing the fluids, wherein one fluid of the at least two fluids contains the silver compound, and another fluid contains a reducing agent, and at least one fluid of the at least two fluids contains an amino acid. With this method, silver fine particles can be produced with sufficient continuous productivity and quality uniformity, without problems of deterioration of working environment and generation of explosive fulminating silver due to the use of a large amount of ammonia.

Claims

1. A method of producing silver fine particles, comprising continuously reducing silver ions contained in a silver compound to precipitate silver fine particles by introducing at least two fluids from separate flow paths and mixing the fluids, wherein one fluid of the at least two fluids contains the silver compound, and another fluid contains a reducing agent, and at least one fluid of the at least two fluids contains an amino acid.

2. The method of producing silver fine particles according to claim 1, wherein formation of a silver mirror is suppressed by the amino acid.

3. The method of producing silver fine particles according to claim 1, wherein the amino acid is contained in the fluid containing the silver compound.

4. The method of producing silver fine particles according to claim 1, wherein 0.1 to 4 mol of the amino acid is used with respect to 1 mol of the silver ion.

5. The method of producing silver fine particles according to claim 1, wherein a concentration of the silver ion in the fluid containing the silver compound is 0.1 to 5% by mass.

6. The method of producing silver fine particles according to claim 1, wherein a dispersing agent is contained in at least one fluid of the at least two fluids.

7. The method of producing silver fine particles according to claim 1, wherein the amino acid is glycine.

8. The method of producing silver fine particles according to claim 1, wherein the at least two fluids are mixed between at least two processing surfaces arranged so as to be capable of approaching to and separating from each other, at least one of which rotates relative to the other.

9. The method of producing silver fine particles according to claim 1, wherein ammonia is not used.

Description

DESCRIPTION OF THE INVENTION

[0040] Hereinafter, embodiments of the present invention are described in detail.

[0041] The method of producing silver fine particles of the present invention is a method of producing silver fine particles, comprising continuously reducing silver ions contained in a silver compound to precipitate silver fine particles by introducing at least two fluids from separate flow paths and mixing the fluids, wherein one fluid of the at least two fluids contains the silver compound, and another fluid contains a reducing agent, and at least one fluid of the at least two fluids contains an amino acid.

[0042] <Production Apparatus of Silver Fine Particles>

[0043] A production apparatus of the silver fine particles used in the present invention includes a continuous reactor having at least two flow paths and having a structure in which the flow paths are in contact with each other at the merging portion. The structure of the merging portion in the continuous reactor is not particularly limited. For example, a Y-letter shaped pipe passage, a T-letter shaped pipe passage, a coaxial double pipe passage, or the like can be used as the flow path that merges at the merging portion. Further, for the purpose of promoting mixing, a static mixer and an in-line mixer may be installed in the flow path of the downstream of the merging portion, or a mechanism for mechanically stirring may be provided at the merging portion. As the mechanism for mechanically stirring, a stirrer of various shear type, friction type, high pressure jet type, ultrasonic type and the like, or a dissolver, an emulsifier, a disperser, a pulverizer, a homogenizer and the like can be used. These continuous reactors include, for example, a continuous type emulsifier such as ULTRA-TURRAX (IKA Japan Co. Ltd.), HOMOMIXER (Primix Corporation), Milder (Pacific Machinery & Engineering, Co., Ltd.), HOMOMETIC LINE FLOW (Primix Corporation), Cavitron (Euro Tech, Co., Ltd.), Fine Flow Mill (Pacific Machinery & Engineering, Co., Ltd.) and the like; a pulverizer such as Slasher (NIPPON COKE & ENGINEERING, Co., Ltd.), Trigonal (Mitsui Miike Chemical Engineering Machinery, Co., Ltd.) and the like; a continuous stirrer such as Clearmix (M. Technique Co., Ltd.), Clearmix Dissolver (M. Technique Co., Ltd.), SWINGSTIR (Shinko Eco-Solutions Co., Ltd.), FILMIX (Primix Corporation), and the like.

[0044] <Forced Thin Film Reactor>

[0045] A preferable embodiment of the production apparatus of silver fine particles used in the present invention includes, for example, a forced thin film reactor in which at least two types of fluids to be processed can be contacted and mixed with each other between at least two processing surfaces, at least one of which rotates relative to the other. More specifically, it may be a forced thin film reactor, wherein the reactor has the first processing surface and the second processing surface being capable of approaching to and separating from each other, at least one of which rotates relative to the other; at least two types of fluids to be processed are introduced between the at least two processing surfaces, and a separation force acting in the direction of separating the first processing surface and the second processing surface is generated by the pressure applied between the first processing surface and the second processing surface; a minute interval is maintained between the first processing surface and the second processing surface by the pressure balance with the pressure in the direction of bringing the processing surfaces closer to each other; a thin film fluid is formed by passing the at least two types of fluids to be processed between the first processing surface and the second processing surface kept at the minute interval; and the fluids to be processed are contacted and mixed with each other in the thin film fluid. Among them, a preferable forced thin film reactor used in the present invention has a mechanism for promoting mixing by relatively moving the processing surfaces while maintaining a constant interval at the mixing portion of the fluids to be processed. Specifically, for example, the forced thin film type fluid processing apparatus shown in JP 2010-189661 is preferably used.

[0046] <Silver Compound>

[0047] The silver compound used in the present invention includes, for example, monovalent, divalent or trivalent silver compounds which can be dissolved in a solvent used in a fluid containing the silver compound, preferably monovalent silver compound. Specific examples of the silver compounds include silver nitrate, silver fluoride, silver sulfate, silver phosphate and the like, and more preferably silver nitrate. A concentration of silver ions in the fluid containing the silver compound is preferably, for example, 0.1% by mass or more in order to increase productivity. Further, it is preferably, for example, 5% by mass or less, because it becomes difficult to suppress formation of a silver mirror when a concentration of silver ions is too high. A concentration of silver ions is more preferably 0.5% by mass or more and 4.5% by mass or less, further preferably 1% by mass or more and 4% by mass or less, and even more preferably 1.5% by mass or more and 3% by mass or less.

[0048] <Reducing Agent>

[0049] As the reducing agent used in the present invention, any reducing agent may be used, as long as it can reduce silver ions contained in the silver compound and precipitate silver fine particles. Preferred reducing agents include, for example, ascorbic acid, ferrous sulfate, sulfite, alkanolamine, formic acid, hydroquinone, glucose, formalin, sodium borohydride, hydrazine, a hydrazine compound (hydrazine sulfate, hydrazine chloride, etc.) and the like. Among these agents, for example, hydrazine, hydrazine compounds and the like are more preferable. The amount of the reducing agent used is preferably 1 equivalent or more, more preferably 1 equivalent or more and 20 equivalents or less, still more preferably 1.5 equivalents or more and 15 equivalents or less, and even more preferably 2 equivalents or more and 10 equivalents or less with respect to a silver ion in order to increase the reaction yield of silver fine particles. In the redox reaction, electrons are transferred between the compounds, and a silver ion receives one electron and is reduced to silver. A number of electrons transferred from one molecule differs for each of the above reducing agents. For example, hydrazine provides 4 electrons in the reduction reaction. Therefore, when hydrazine which transfers 4 electrons is a reducing agent, 1 equivalent or more with respect to a silver ion means 0.25 mol or more of hydrazine with respect to 1 mol of a silver ion. When a reducing agent having a weak reducing power is used, preferred are 2 equivalents or more, more preferably 2 equivalents or more and 50 equivalents or less, further preferably 5 equivalents or more and 30 equivalents or less, and even more preferably 10 equivalents or more and 20 equivalents or less with respect to a silver ion. A concentration of the reducing agent in the fluid containing the reducing agent is preferably, for example, 1% by mass or more in order to increase productivity. Further, a concentration is preferably, for example, 50% by mass or less, because silver fine particles become non-uniform when a concentration of the reducing agent is too high. Amore preferable concentration of the reducing agent is 2.5% by mass or more and 40% by mass or less, and more preferably 5% by mass or more and 25% by mass or less.

[0050] <Amino Acid>

[0051] The amino acid in the present invention has two types of functional groups: an amino group and a carboxyl group, which can be coordinated to a silver ion in the molecule. Therefore, a mixture of various types of complexes is formed, in which an amino group, a carboxyl group, or the like is coordinated to a silver ion. The amino acid stabilizes a silver ion by forming a mixture of silver ions and various types of complexes, and decrease the reduction rate immediately after mixing silver ions and the reducing agent, and thereby the formation of a silver mirror on the inner walls of the merging portion and the flow path of the continuous reactor is suppressed, and the adhesion of silver on the inner walls of the merging portion and the flow path is suppressed. In the present invention, it is preferable not to use a large amount of ammonia to some extent causing the problems of deterioration of working environment and generation of explosive fulminating silver. It is more preferable not to use ammonia.

[0052] The amino acid includes, for example, α-amino acid, β-amino acid, derivatives thereof and the like, and may be appropriately selected depending on the physical properties such as solubility and pKa. Preferred amino acids are, for example, α-amino acids. Specific α-amino acids include, for example, glycine, arginine, phenylalanine, glutamic acid, valine, leucine, isoleucine, glutamine, aspartic acid, alanine, proline, cysteine, lysine, threonine, asparagine, serine, methionine, tyrosine, histidine, tryptophan, citrulline, ornithine and the like. More preferable α-amino acids are glycine, arginine, phenylalanine, glutamic acid and the like. Specific β-amino acids and derivatives thereof are, for example, β-alanine, taurine, creatine and the like. The amino acid may be used alone or in combination of two or more. As for an amino acid in which optical isomers are present, any of D-form, L-form, or a mixture thereof may be used.

[0053] The amount of the amino acid added is preferably 5 mol or less with respect to 1 mol of a silver ion, because the progress of reduction is inhibited when the amount of the amino acid added is too large. Further, the amount of the amino acid added is preferably 0.05 mol or more with respect to 1 mol of a silver ion, because silver ions become unstable and the formation of a silver mirror cannot be suppressed when the amount of the amino acid added is too small. A more preferable amount of the amino acid added is, for example, 0.1 mol or more and 4 mol or less, and more preferably 0.2 mol or more and 2 mol or less with respect to 1 mol of a silver ion.

[0054] In the present invention, the amino acid is contained in at least one of at least two fluids introduced from separate flow paths. Preferably, the amino acid is contained in a fluid containing the silver compound. When both the amino acid and the silver compound are contained in the same fluid, the silver ion forms a stable complex with the amino acid and can be reacted with the reducing agent in the state of the complex. Not limited to this, the present invention also includes an embodiment in which a fluid containing the silver compound, a fluid containing the reducing agent, and a fluid containing the amino acid are introduced from separate flow paths and mixed.

[0055] <Solvent>

[0056] In the present invention, the solvent used in the fluid containing the silver compound or the reducing agent may be any solvent which can dissolve the silver compound or the reducing agent, and does not cause a problem in the reduction of a silver ion. Such solvent includes, for example, water, a hydrophilic solvent, and a mixed solvent thereof, and preferably water, and a mixed solvent of water and a hydrophilic solvent, and more preferably water. In order to avoid formation of silver chloride or the like, it is desirable to use desalted water, and specific examples thereof include ion-exchanged water, RO water (reverse osmosis water), pure water, and ultrapure water and the like. The hydrophilic solvent includes, for example, an alcohol such as methanol, ethanol and ethylene glycol; a ketone such as acetone and methyl isobutyl ketone; a sulfoxide such as dimethyl sulfoxide; an amide such as dimethylformamide and dimethylacetamide; an ether such as tetrahydrofuran, dioxane, dimethoxyethane and polyethylene glycol; a carboxylic acid such as acetic acid, and the like. Preferred is an alcohol such as methanol, ethanol and ethylene glycol. For example, a mixed solvent of water and a hydrophilic solvent is preferred, when water alone is insufficient to uniformly dissolve a dispersing agent or the like, or when water alone is insufficient to obtain the viscosity required for circulation in a flow path.

[0057] <Dispersing Agent>

[0058] In the method of producing silver fine particles of the present invention, it is also preferable to add a dispersing agent. The dispersing agent is not particularly limited, and may be appropriately selected depending on the intended purpose. Examples thereof include a fatty acid and a salt thereof, a surfactant, an organometallic compound, a chelating agent, a polymer dispersing agent and the like. The fatty acid and a salt thereof include, for example, propionic acid, caprylic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid, arachidonic acid, ricinoleic acid and a salt thereof.

[0059] The surfactant includes, for example, an anionic surfactant such as an alkyl sulfonate and an alkylbenzene sulfonate; a cationic surfactant such as an alkylpyridinium salt and a quaternary alkylammonium salt; a nonionic surfactant such as a polyoxyethylene alkyl ether; or a mixture thereof and the like. Specific examples of the surfactant include Ajisper (registered trademark, Ajinomoto Fine Techno Co., Inc.), Hypermer (registered trademark, Croda International Plc.), Tween (registered trademark), Solplus (registered trademark, Lubrisol Japan Ltd.), SN Sparse (San Nopco Ltd.), Futagent (registered trademark, Neos Co., Ltd.), Beaulite (registered trademark, Sanyo Kasei Kogyo Co., Ltd.), Perex (registered trademark, Kao Co., Ltd.), Kaosera (registered trademark), Homogenol (registered trademark), Pluronic (registered trademark, BASF SE), Catiogen (registered trademark, Dai-Ichi Kogyo Seiyaku Co., Ltd.), Hitenol (registered trademark), Plysurf (registered trademark), Neugen (registered trademark), Epan (registered trademark), Sorgen (registered trademark), DK ester (registered trademark), Surfinol (registered trademark, Nisshin Kagaku Kogyo Co., Ltd.), Megafac (registered trademark, DIC Corporation), and the like. The organometallic compound include, for example, acetylacetone tributoxyzirconium, magnesium citrate, diethylzinc, dibutyltin oxide, dimethylzinc, tetra-n-butoxyzirconium, triethylindium, triethylgallium, trimethylindium, trimethylgallium, monobutyltin oxide, tetraisocyanatosilane, tetramethylsilane, tetramethoxysilane, monomethyltriisocyanatosilane, silane coupling agent, titanate-based coupling agent, aluminum-based coupling agent, and the like.

[0060] The chelating agent includes, for example, an azole compounds such as imidazole, oxazole, thiazole, selenazole, pyrazole, isoxazole, isothiazole, 1H-1,2,3-triazole, 2H-1,2,3-triazole, 1H-1,2,4-triazole, 4H-1,2,4-triazole, 1,2,3-oxadiazole, 1,2,4-oxadiazole, 1,2,5-oxadiazole, 1,3,4-oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,5-thiadiazole, 1,3,4-thiadiazole, 1H-1,2,3,4-tetrazole, 1,2,3,4-oxatriazole, 1,2,3,4-thiatriazole, 2H-1,2,3,4-tetrazole, 1,2,3,5-oxatriazole, 1,2,3,5-thiatriazole, indazole, benzoimidazole and benzotriazole, or a salt thereof; a dicarboxylic acid such as oxalic acid, succinic acid, malonic acid, glutaric acid and adipic acid, or a salt thereof; ethylenediamine tetraacetic acid, ethylenediamine-N,N′-disuccinic acid and the like.

[0061] Various polymer dispersing agents may be used. The polymer dispersing agent includes, for example, an amine-based polymer dispersing agent such as polyethyleneimine and polyvinylpyrrolidone; a hydrocarbon-based polymer dispersing agent having a carboxylic acid group in the molecule such as polyacrylic acid and carboxymethyl cellulose; Poval (polyvinyl alcohol); a polymer dispersing agent having a polar group such as a copolymer having a polyethyleneimine moiety and a polyethylene oxide moiety in one molecule, and the like. The polymer dispersing agent preferably has a molecular weight of 100,000 or less. Commercially available products may also be used, and examples of the commercially available products include Solsperse 20000, Solsperse 24000, Solsperse 26000, Solsperse 27000, Solsperse 28000, Solsperse 41000 (registered trademark, Nippon Lubrizol Co., Ltd.), and Disperbyk 160, Disperbyk 161, Disperbyk 162, Disperbyk 163, Disperbyk 166, Disperbyk 170, Disperbyk 180, Disperbyk 181, Disperbyk 182, Disperbyk 183, Disperbyk 184, Disperbyk 190, Disperbyk 191, Disperbyk 192, Disperbyk 2000, Disperbyk 2001 (registered trademark, BYK Chemie Japan Co., Ltd.), Flowlen DOPA-158, Flowlen DOPA-22, Flowlen DOPA-17, Flowlen G-700, Flowlen TG-720W, Flowlen-730W, Flowlen-740W, Flowlen-745W (registered trademark, Kyoeisha Chemical Co., Ltd.), Ajisper PA111, Ajisper PB711, Ajisper PB811, Ajisper PB821, Ajisper PW911 (registered trademark, Ajinomoto Fine-Techno Co., Inc.), Joncryl 678, Joncryl 679, Joncryl 62 (registered trademark, by BASF SE) and the like.

[0062] These dispersing agents may be used alone or in combination of two or more.

[0063] In the present invention, the dispersing agent may be contained in at least one of at least two fluids introduced from separate flow paths. By containing the dispersing agent, the generated silver fine particles are stabilized, and the adhesion of silver on inner walls of the merging portion and the flow path is suppressed.

[0064] The amount of the dispersing agent added is preferably the amount that does not inhibit the coordination of the amino acid to a silver ion and does not adversely affect the effects of the present invention. The concentration of the dispersing agent in the fluid containing the dispersing agent is, for example, 0.0001% by mass or more and 1% by mass or less, preferably 0.0005% by mass or more and 0.5% by mass or less, more preferably 0.001% by mass or more and 0.1% by mass or less.

[0065] <pH Adjusting Agent>

[0066] A pH adjusting agent may be added as necessary to adjust difference in acidity derived from the raw material. As the pH adjusting agent, general acids and bases may be used. Examples thereof include nitric acid, sodium hydroxide, and the like.

[0067] <Reaction Temperature>

[0068] In the method of producing silver fine particles of the present invention, the reaction temperature of the reaction in which silver ions contained in a silver compound are continuously reduced by introducing at least two fluids from separate flow paths and mixing, may be a temperature at which the solvent used does not solidify or vaporize. Preferred reaction temperature includes, for example, 5° C. or higher and 80° C. or lower, more preferably 10° C. or higher and 60° C. or lower, further preferably 15° C. or higher and 50° C. or lower, and even more preferably 20° C. or higher and 40° C. or lower.

EXAMPLE

[0069] Hereinafter, the present invention is explained in more detail with reference to Examples, but the present invention is not limited only to these Examples. The terms “part” and “%” are based on mass unless otherwise specified.

Example 1

[0070] 250 parts of silver nitrate (Kishida Chemical Co., Ltd.) as a silver compound, 111 parts of glycine (Kanto Chemical Co., Inc.) as an amino acid (1 mol with respect to 1 mol of a silver ion), and 50 parts of 60% nitric acid (Kishida Chemical Co., Ltd.) as a pH adjuster were added to 9,589 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a silver compound aqueous solution (1).

[0071] 150 parts of hydrazine monohydrate (Kanto Chemical Co., Inc.) as a reducing agent, and 5 parts of 10% oleic acid methanol solution in which oleic acid (Kanto Chemical Co., Inc.) was dissolved in methanol as a dispersing agent were added to 845 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a reducing agent aqueous solution (1).

[0072] Using the forced thin film reactor ULREA (M-Technique Co., Ltd.), the silver compound aqueous solution (1) as the first fluid was sent at 500 mL/min, and the reducing agent aqueous solution (1) as the second fluid was sent at 50 mL/min. The solutions were introduced between the disks rotating at 500 rpm and mixed, and the discharged liquid was recovered from between the disks to obtain a slurry containing silver fine particles. In the example, the meanings of the first fluid and the second fluid are the same as those described in the forementioned JP 2010-189661.

[0073] Under the above condition, the forced thin film reactor ULREA was continuously operated for 30 minutes to produce silver fine particles. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the processing surfaces of the used discs were checked, and no silver adhesion was observed.

[0074] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders for each divided operation time were observed at a magnification of 10,000 times with a scanning electron microscope (JSM-7500F, JEOL Ltd.). An average value of the particle diameters of the 50 observed silver fine particles was calculated, and the average particle diameter was about 0.7 μm. It was confirmed that no difference of the particle diameter and shape from the start to the end of the operation of the forced thin film reactor was observed.

Example 2

[0075] 250 parts of silver nitrate (Kishida Chemical Co., Ltd.) as a silver compound, 52 parts of L-arginine (Fujifilm Wako Pure Chemical Corporation) as an amino acid (0.2 mol with respect to 1 mol of a silver ion), and 5 parts of 60% nitric acid (Kishida Chemical Co., Ltd.) as a pH adjuster were added to 9,693 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a silver compound aqueous solution (2).

[0076] 100 parts of hydrazine monohydrate (Kanto Chemical Co., Inc.) as a reducing agent, and 5 parts of 10% oleic acid methanol solution in which oleic acid (Kanto Chemical Co., Inc.) was dissolved in methanol as a dispersing agent were added to 895 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a reducing agent aqueous solution (2).

[0077] Using the forced thin film reactor ULREA (M-Technique Co., Ltd.), the silver compound aqueous solution (2) as the first fluid was sent at 500 mL/min, and the reducing agent aqueous solution (2) as the second fluid was sent at 50 mL/min. The solutions were introduced between the disks rotating at 500 rpm and mixed, and the discharged liquid was recovered from between the disks to obtain a slurry containing silver fine particles.

[0078] Under the above condition, the forced thin film reactor ULREA was continuously operated for 30 minutes to produce silver fine particles. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the processing surfaces of the used discs were checked, and no silver adhesion was observed.

[0079] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1, and the average particle diameter was about 0.6 μm. It was confirmed that no difference of the particle diameter and shape from the start to the end of the operation of the forced thin film reactor was observed.

Example 3

[0080] 250 parts of silver nitrate (Kishida Chemical Co., Ltd.) as a silver compound, 243 parts of L-phenylalanine (Fujifilm Wako Pure Chemical Corporation) as an amino acid (1 mol with respect to 1 mol of a silver ion), and 5 parts of 60% nitric acid (Kishida Chemical Co., Ltd.) as a pH adjuster were added to 9,502 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a silver compound aqueous solution (3).

[0081] 225 parts of hydrazine monohydrate (Kanto Chemical Co., Inc.) as a reducing agent, and 5 parts of 10% oleic acid methanol solution in which oleic acid (Kanto Chemical Co., Inc.) was dissolved in methanol as a dispersing agent were added to 770 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a reducing agent aqueous solution (3).

[0082] Using the forced thin film reactor ULREA (M-Technique Co., Ltd.), the silver compound aqueous solution (3) as the first fluid was sent at 500 mL/min, and the reducing agent aqueous solution (3) as the second fluid was sent at 50 mL/min. The solutions were introduced between the disks rotating at 500 rpm and mixed, and the discharged liquid was recovered from between the disks to obtain a slurry containing silver fine particles.

[0083] Under the above condition, the forced thin film reactor ULREA was continuously operated for 30 minutes to produce silver fine particles. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the processing surfaces of the used discs were checked, and no silver adhesion was observed.

[0084] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1, and the average particle diameter was about 1.2 μm. It was confirmed that no difference of the particle diameter and shape from the start to the end of the operation of the forced thin film reactor was observed.

Example 4

[0085] 250 parts of silver nitrate (Kishida Chemical Co., Ltd.) as a silver compound, 65 parts of L-glutamic acid (Fujifilm Wako Pure Chemical Corporation) as an amino acid (0.3 mol with respect to 1 mol of a silver ion), and 5 parts of 60% nitric acid (Kishida Chemical Co., Ltd.) as a pH adjuster were added to 9,680 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a silver compound aqueous solution (4). The same reducing agent aqueous solution as in Example 1 was prepared and used.

[0086] Using the forced thin film reactor ULREA (M-Technique Co., Ltd.), the silver compound aqueous solution (4) as the first fluid was sent at 500 mL/min, and the reducing agent aqueous solution (1) as the second fluid was sent at 50 mL/min. The solutions were introduced between the disks rotating at 500 rpm and mixed, and the discharged liquid was recovered from between the disks to obtain a slurry containing silver fine particles.

[0087] Under the above condition, the forced thin film reactor ULREA was continuously operated for 30 minutes to produce silver fine particles. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the processing surfaces of the used discs were checked, and no silver adhesion was observed.

[0088] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1, and the average particle diameter was about 0.9 μm. It was confirmed that no difference of the particle diameter and shape from the start to the end of the operation of the forced thin film reactor was observed.

Comparative Example 1

[0089] 250 parts of silver nitrate (Kishida Chemical Co., Ltd.) as a silver compound, and 50 parts of 60% nitric acid (Kishida Chemical Co., Ltd.) as a pH adjuster were added to 9,700 parts of ion-exchanged water, and dissolved at 25° C. under an air atmosphere to prepare a silver compound aqueous solution (5). The same reducing agent aqueous solution as in Example 1 was prepared and used.

[0090] Using the forced thin film reactor ULREA (M-Technique Co., Ltd.), the silver compound aqueous solution (5) as the first fluid was sent at 500 mL/min, and the reducing agent aqueous solution (1) as the second fluid was sent at 50 mL/min. The solutions were introduced between the disks rotating at 500 rpm and mixed, and the discharged liquid was recovered from between the disks to obtain a slurry containing silver fine particles.

[0091] Under the above condition, the forced thin film reactor ULREA was continuously operated for 3 minutes to produce silver fine particles. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. The processing surfaces of the used discs were checked, and silver adhesion was observed.

[0092] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1. It was confirmed that coarse particles of 10 μm or more, fine particles of 0.1 μm or less, and particles having an irregular shape gradually increased as time passed from the start of operation, and that the adhesion (necking) between particles became intense, and the particle diameter and shape significantly changed from the start of operation to the end of operation.

Example 5

[0093] The silver compound aqueous solution (1) and the reducing agent aqueous solution (1) were prepared in the same manner as in Example 1, and used.

[0094] Silver fine particles were produced using a coaxial double pipe passage wherein an outer pipe passage has an inner diameter of 8 mm and an outer diameter of 10 mm, and an inner pipe passage has an inner diameter of 3 mm and an outer diameter of 4 mm. The silver compound aqueous solution (1) as the first fluid was sent at 500 mL/min to the outer pipe passage of the coaxial double pipe passage, and the reducing agent aqueous solution (1) as the second fluid was sent at 50 mL/min to the inner pipe passage of the coaxial double pipe passage. The solutions were contacted and mixed at the merging portion where the coaxial double pipe passage merges to form a single pipe passage, and the discharged liquid was recovered from between the single pipe passage to obtain a slurry containing silver fine particles.

[0095] Under the above condition, silver fine particles were continuously produced for 30 minutes. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the merging portion of the coaxial double pipe passage and the single pipe passage of the downstream thereof after use were confirmed, and no silver adhesion was observed.

[0096] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1, and the average particle diameter was about 0.9 μm. It was confirmed that no difference of the particle diameter and shape from the start to the end of the operation of the forced thin film reactor was observed.

Comparative Example 2

[0097] The silver compound aqueous solution (5) and the reducing agent aqueous solution (1) were prepared in the same manner as in Comparative Example 1, and used.

[0098] Silver fine particles were produced using a coaxial double pipe passage wherein an outer pipe passage has an inner diameter of 8 mm and an outer diameter of 10 mm, and an inner pipe passage has an inner diameter of 3 mm and an outer diameter of 4 mm. The silver compound aqueous solution (5) as the first fluid was sent at 500 mL/min to the outer pipe passage of the coaxial double pipe passage, and the reducing agent aqueous solution (1) as the second fluid was sent at 50 mL/min to the inner pipe passage of the coaxial double pipe passage. The solutions were contacted and mixed at the merging portion where the coaxial double pipe passage merges to form a single pipe passage, and the discharged liquid was recovered from between the single pipe passage to obtain a slurry containing silver fine particles.

[0099] Under the above condition, silver fine particles were continuously produced for 10 minutes. In order to evaluate the silver fine particles, the discharged liquid was divided and collected every 1 minute of operation time. After the operation was completed, the merging portion of the coaxial double pipe passage and the single pipe passage of the downstream thereof of after use were confirmed, and silver adhesion was observed.

[0100] The silver fine particles contained in the slurry were filtered under reduced pressure using a hard filter paper (opening 1 μm), and the residue after filtration was washed with ion-exchanged water three times, dried, and then crushed to obtain silver powders. The obtained silver powders were observed with a scanning electron microscope in the same manner as in Example 1. It was confirmed that coarse particles of 10 μm or more, fine particles of 0.1 μm or less, and particles having an irregular shape gradually increased as time passed from the start of operation, and that the adhesion (necking) between particles became intense, and the particle diameter and shape significantly changed from the start of operation to the end of operation.

[0101] Table 1 summarizes the added amino acids, the production apparatus, the operation time, the presence or absence of adhesion, and the time-dependent change of the particle diameter and shape of the silver fine particles of Examples 1 to 5 and Comparative Examples 1 and 2.

TABLE-US-00001 TABLE 1 Amino Production Operation Presence Time-dependent change of acid apparatus time (min) of adhesion particle diameter and shape Example 1 Glycine Forced thin film reactor 30 No No Example 2 L-Arginine Forced thin film reactor 30 No No Example 3 L-Phenylalanine Forced thin film reactor 30 No No Example 4 L-Glutamic acid Forced thin film reactor 30 No No Example 5 Glycine Coaxial double 30 No No pipe passage Comparative — Forced thin 3 Yes Yes Example 1 film reactor Comparative — Coaxial double 10 Yes Yes Example 2 pipe passage

[0102] As can be seen from Table 1, in Comparative Examples 1 and 2 in which no amino acids were added, adhesion of silver was observed on the processing surface of the discs of the forced thin film reactor and the merging portion of the coaxial double pipe passage and the single pipe passage of the downstream thereof. On the other hand, in Examples 1 to 5 in which amino acids were added, no adhesion of silver was observed. The time-dependent changes of the particle diameter and shape of the silver fine particles observed in Comparative Examples 1 and 2 were not observed in Examples 1 to 5.

[0103] As described above, in the method of producing silver fine particles of the present invention, silver does not adhere to the inner walls of the merging portion and the flow path of the continuous reactor. As a result, the shape and properties of the silver fine particles to be produced can be controlled without changing the environment of the merging portion and the flow path with lapse of time, and silver fine particles having a certain quality can be produced. Therefore, according to the method of producing silver fine particles of the present invention, silver fine particles can be produced in a wet reduction method using a continuous reactor with sufficient continuous productivity and quality uniformity, without using a large amount of ammonia causing deterioration of working environment.

INDUSTRIAL APPLICABILITY

[0104] The present invention provides a method of producing silver fine particles in the wet reduction method using a continuous reactor with sufficient continuous productivity and quality uniformity, without problems of deterioration of working environment and generation of explosive fulminating silver due to the use of a large amount of ammonia.