PROCESS OF MANUFACTURING SELF-LUBRICATING ELEMENTS WITH NANOMETRIC LUBRICANTS

Abstract

A process for the manufacturing of self-lubricating elements such as bearings, plates, bushings and the like with composites obtained by impregnating special synthetic fabrics with thermosetting resins, catalyst and nano graphite and/or molybdenum disulfide nano and/or nano PTFE and/or nanoboron nitride, each of these, or other nanometric lubricants, added according to the tribological applications and requirements of the product.

Claims

1. A process of manufacturing self-lubricating elements with nanometric lubricants comprising using a combination of polyester fabric impregnated with thermosetting resins, added with homogenized nanometric lubricants in mixers, being quantitatively and qualitatively according to the tribological requirements.

2. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the process comprises using: polyester fabrics with thermosetting resins selected from the group consisting of 65% to 83% polyester and 70% to 91% epoxy; and solid lubricants selected from the group consisting of 15% to 19% nanographite, up 4.5% nanoboron nitride, up to 10% PTFE, and 5% to 7% MoS.sub.2.

3. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the components and respective percentages are included, in a unitary way, in part or in total for the impregnation of the fabric.

4. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 2, wherein the components and respective percentages are included, in a unitary way, in part or in total for the impregnation of the fabric.

5. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the process uses Vortex type mixers for higher viscosity resins and ultrasonic mixers for lower viscosity resins.

6. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the fabric is impregnated in a tank containing the resin mixture plus the nanometric lubricants.

7. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, further comprising wrapping the fabric with reinforcement material selected from the group consisting of aramid fiber and carbon fiber.

8. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 6, further comprising wrapping the fabric with reinforcement material selected from the group consisting of aramid fiber and carbon fiber.

9. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the material follows on to a press for production of plates or to filament winding equipment for production of dowels.

10. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 6, wherein the material follows on to a press for production of plates or to filament winding equipment for production of dowels.

11. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the material follows on to an oven at a temperature of between 110 C.-250 C.

12. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 6, wherein the material follows on to an oven at a temperature of between 110 C.-250 C.

13. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 1, wherein the material, in plate or dowel form, is subject to machining to provide an end product.

14. The process of manufacturing self-lubricating elements with nanometric lubricants according to claim 6, wherein the material, in plate or dowel form, is subject to machining to provide an end product.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0039] The invention will now be described in detail, based on the illustrations set out in the accompanying drawings:

[0040] FIG. 1 is a flow chart of the process of manufacturing self-lubricating elements with nanometric lubricants; and

[0041] FIG. 2 is a schematic view of the process of manufacturing self-lubricating elements with nanometric lubricants.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0042] The instant process of manufacturing self-lubricating elements with nanometric lubricants, the object of this application for patent of invention, refers to the manufacturing of self-lubricating elements such as bearings, plates, bushings and the like with composites obtained from the impregnation of synthetic fabrics with special thermosetting resins, catalyst and nano graphite and/or molybdenum disulfide and/or nano PTFE and/or nanoboron nitride, each of these, or other nanometric lubricants added in accordance with the applications and tribological needs of the product.

[0043] More particularly, the composites used in the manufacturing process of the self-lubricating elements are obtained by impregnating fabrics in polyester thermosetting resins of polyester (65% to 83%) or thermosetting resins in epoxy (70% to 91%) and solid lubricants such as nano graphite (15% to 19%) and/or nano boron nitride (up 4.5%) and/or PTFE (10%) and/or even MoS.sub.2 (5% to 7%) in which limits are adjusted according to the tribological needs for that self-lubricating system. The above components and their respective percentages can be included in a unitary way, in part or in total for the impregnation of the fabric.

[0044] The definition of which component should be used is directly related to the needs required for the end product, such as, for example, the conditions of the environment. In this context, the nano PTFE is indicated for use in environments where there is a galvanic and submerged corrosion. The nano graphite and MoS.sub.2 are recommended for general use, provided that the maximum temperature does not exceed 200 C. In contrast, the combination of PTFE and MoS.sub.2 is ideal for the food and pharmaceutical industry.

[0045] In the initial stage of the process for obtaining solid lubricant nanoparticles, ultrasonic mixers are used for thermosetting low viscosity resins and Vortex-type mixers for higher viscosity resins. Thus, the impregnation occurs by bathing the polyester fabric in an immersion tank with the mixture of thermosetting resin and the nanolubricant(s) to be used. In this step, if necessary the fabric can be wrapped with reinforcement material, such as, for example, aramid fiber or carbon fiber, with the aim of increasing resistance to shock and/or pressure of the nanometric self-lubricating composite in the filament winding equipment. This process involves filament winding under different tension conditions over a mandrel or male mold. Accordingly, the mandrel rotates while a car moves horizontally, establishing the desired pattern of the nano composite lubricant, resin and fabric. Since the mandrel is completely covered with the desired material thickness, the same is forwarded to the oven in order to cure the fabric, resin and solid nano lubricant combination, which occurs between 110 C. and 250 C. The mandrel can then be removed. In this process, it is possible to define different dimensions for the initial internal and external diameters and for the length, the latter defined by the length measurement of the mandrel and the maximum length of the filament winding equipment. After the above steps, the resulting product is cut to the desired length and machined in accordance with the internal and external diameter requirements for that end product represented by a bushing or bearing.

[0046] A manufacturing variation is intended for obtaining the self-lubricating element in the form of a plate whose process is similar to that of the bearing and bushing in which the fabric is rolled. However, in this variation the polyester fabric is impregnated with orthophtalic resin and the pertinent nanolubricants, it being equally possible to add carbon fiber and aramid fiber for reinforcement.

[0047] After impregnation, the fabric is pressed with vacuum for the perfect penetration of resin and nano lubricants, and withdrawal of the surplus. After pressing, the material is taken to the oven set to attain the resin curing temperature between 110 C. and 250 C. The composition for impregnation and respective quantities are the same as for those presented for manufacturing the composite in tube form.

[0048] As shown in FIGS. 1 and 2, the resin E1 and the nanoscale lubricants E2, duly dosed, are directed to a mixer E3 where they are homogenized. The mixer varies according to the resin. In the case of high viscosity thermosetting resins it is of the Vortex type and thermosetting resins of low viscosity of the ultrasonic type. The mixed and homogenized resin and the lubricant E4 are ready to impregnate A polyester fabric E5. Such impregnation occurs with passage of the fabric 1 in an immersion tank 2 containing the mixture 3 in paste form. At this point, the process enters a decision-making stage E6 that defines which type of raw material or self-lubricating final element is desired.

[0049] For the production of plates B, when the impregnated fabric leaves the tank, it is directed to a press E7, whereas for the production of dowels Cbushings and bearingsthe fabric is wrapped by filament winding equipment E8. In both situations, the products are placed in an oven/stove E9 between 110 C. and 250 C. so that the raw material E10 in plate or dowel attains curing temperature. Thereafter, the process follows on to machining E11 in order to obtain the finished product E12.

[0050] In an example of applying the process for producing a bushing for use in grain harvesting equipment, an analysis is made of the dimensions such as inner diameter, outer diameter, length, speed, temperature, friction coefficient and load factor on the bearing and other data necessary for the proper functioning of the self-lubricating element. Thus, the manufacturing process of this bushing uses polyester fabric with appropriate measures to achieve the measurement of the end product.

[0051] The impregnation of the fabric is with high viscosity polyester resin (75%), nano PTFE (10%), nano MoS.sub.2 (4%) to complement the solid lubrication and catalyst for the resin (11%), these being homogenized in a Vortex mixer. After impregnation of the fabric, the resin+nanolubricant+fabric combination is wrapped in filament winding equipment, with diameters pre-defined for the end product. The internal diameter of the bushing is given by the outer diameter of the mandrel. After winding, the raw material is placed in an oven to attain curing temperature, in this case 150 C.

[0052] After curing and cooling, the bushing is machined to achieve the final design measurements.