METHOD OF PREPARING HETEROGENEOUS LINEAR CARBONATE USING BASIC ION EXCHANGE RESIN

Abstract

The present specification provides a method of preparing a heterogeneous linear carbonate, including transesterifying an aliphatic alcohol and a symmetric linear carbonate in the presence of a catalyst, wherein the catalyst is a porous type basic ion exchange resin having an exchange capacity of 1 (eq/l-wet resin) or more and 1.5 (eq/l-wet resin) or less. The preparation method of the present specification provides a method of preparing a heterogeneous, symmetric linear carbonate and asymmetric linear carbonate in high yield without a process of reactive distillation.

Claims

1. A method of preparing a heterogeneous linear carbonate, comprising transesterifying an aliphatic alcohol and a symmetric linear carbonate in the presence of a catalyst, wherein the catalyst is a porous type basic ion exchange resin having an exchange capacity of 1 (eq/l-wet resin) or more and 1.5 (eq/l-wet resin) or less.

2. The method of claim 1, wherein an exchange group of the basic ion exchange resin is trimethylammonium (TMA) or dimethylethanolammonium (DMEA), and an ion type is a chlorine anion (Cl.sup.) or a hydroxy group anion (OH.sup.).

3. The method of claim 1, wherein in the transesterification reaction, a mass ratio of the aliphatic alcohol and the symmetric linear carbonate (aliphatic alcohol:symmetric linear carbonate) is 1:10 or more and 10:1 or less.

4. The method of claim 1, wherein the transesterification reaction is performed in a fixed bed reactor or a continuous stirred tank reactor (CSTR).

Description

MODES OF THE INVENTION

[0015] Advantages and features of the present invention and methods of achieving them will become apparent with reference to the embodiments described below in detail. However, the present invention is not limited to the embodiments disclosed below and may be embodied in various different forms, and the embodiments merely serve to complete the disclosure of the present invention and to fully inform the scope of the invention to those skilled in the art to which the invention pertains, which is defined only by the spirit of the claims. Throughout the specification, like reference numerals refer to like components.

[0016] Unless otherwise defined, all terms (including technical and scientific terms) used in the present specification may be used in a meaning commonly understood by those of ordinary skill in the art to which the present invention belongs. In addition, terms defined in commonly used dictionaries are not interpreted ideally or excessively unless explicitly specifically defined.

[0017] Throughout the specification, when a part is said to include a component, this means that the part may further include other components rather than excluding other components unless specifically stated to the contrary.

[0018] Hereinafter, the present invention will be described in detail.

[0019] One embodiment of the present invention provides a method of preparing a heterogeneous linear carbonate, including transesterifying an aliphatic alcohol and a symmetric linear carbonate in the presence of a catalyst, wherein the catalyst is a porous type basic ion exchange resin having an exchange capacity of 1 (eq/l-wet resin) or more and 1.5 (eq/l-wet resin) or less.

[0020] In one embodiment of the present invention, the porous type basic ion exchange resin is a porous strong basic ion exchange resin. The porous strong basic ion exchange resin is an ion type, and may include a bromine anion (Br.sup.), a thiocyanate anion (SCN.sup.), a chlorine anion (Cl.sup.), an acetate anion (CH.sub.3COO.sup.), a hydroxy group anion (OH.sup.), a fluorine anion (F.sup.), and the like. The porous weak basic ion exchange resin is an ion type, and may include a citrate anion (C.sub.3H.sub.5O(COO).sub.3.sup.3), sulfate (SO.sub.4.sup.2), and the like.

[0021] In the present specification, the aliphatic alcohol is not particularly limited, but may include alcohols having 1 to 10 carbon atoms, specifically methanol, ethanol, propanol, isopropanol, butanol, isobutanol, and the like. In one embodiment of the present specification, the aliphatic alcohol is ethanol.

[0022] In one embodiment of the present invention, the symmetric linear carbonate, which is a reactant in the transesterification reaction, is dimethyl carbonate (DMC).

[0023] In one embodiment of the present invention, heterogeneous linear carbonates produced after the transesterification reaction are symmetric linear carbonates and asymmetric linear carbonates.

[0024] In one embodiment, the asymmetric linear carbonate produced after the transesterification reaction is ethyl methyl carbonate (EMC).

[0025] In one embodiment, the symmetric linear carbonate produced after the transesterification reaction is diethyl carbonate (DEC).

[0026] According to one embodiment of the present invention, the transesterification reaction produces a heterogeneous linear carbonate, namely an asymmetric linear carbonate and an asymmetric linear carbonate. The asymmetric linear carbonate of the product in the transesterification reaction is ethyl methyl carbonate (EMC), and the symmetric linear carbonate is diethyl carbonate (DEC).

[0027] In the preparation method according to one embodiment of the present invention, a porous type basic ion exchange resin is used as a catalyst in a transesterification reaction between an aliphatic alcohol and a symmetric linear carbonate. Since the porous type basic ion exchange resin has many (about 10 to 1000) macro pores on its surface, the resin is chemically stable compared to the gel-type strong basic ion exchange resin and can maximize contact with a reactant due to a large surface area, so that the reaction rate is fast and the internal diffusion rate is excellent, and it is possible to simultaneously prepare heterogeneous linear carbonates with high reaction efficiency.

[0028] In addition, a heat resistance temperature of the porous type basic ion exchange resin is about 40 C. to 100 C., and an operating range is wider than the heat resistance temperature of about 40 C. to 80 C. of the gel type strong basic ion exchange resin, so that there is little risk that the pH of the product will increase due to the elution of the exchange group in the event of a runaway reaction such as an exothermic reaction.

[0029] In addition, since the porous type basic ion exchange resin used in one embodiment of the present invention has excellent decoloring properties, it is possible to relatively reduce the washing time of the ion exchange resin and the amount of washing solvent used at the beginning of the reaction, and due to its excellent strength, the loss of exchange groups and formation of fine powders are reduced during reuse, so that the reuse cycle is long and productivity can be improved.

[0030] In one embodiment of the present invention, the catalyst is a porous type basic ion exchange resin having an exchange capacity of 1 (eq/l-wet resin) or more and 1.5 (eq/l-wet resin) or less. In general, the higher the degree of crosslinking of the ion exchange resin, the more exchange groups are attached to the matrix, so that the exchange capacity tends to be high, but the reaction efficiency decreases because the exchange groups participating in the reaction decrease due to a strong bond between the matrix and the exchange groups. When the exchange capacity of the catalyst exceeds 1.5 (eq/l-wet resin), the reaction rate is too slow, and when the exchange capacity of the catalyst is less than 1 (eq/l-wet resin), the reaction rate is fast, but the bond between the matrix and the exchange groups is weakened, resulting in a decrease in strength against rapid volume change.

[0031] In the present specification, the exchange capacity means that the ability of an ion exchange resin to adsorb ions is expressed as an equivalent amount of ions obtained by adsorbing a certain volume of the resin, that is, may mean an exchange amount that can be removed by 1 liter of resin.

[0032] In the present specification, the unit of the exchange capacity is eq/l-wet resin, and means a value expressed as an equivalent of exchange capacity per liter of the ion exchange resin.

[0033] In one embodiment of the present invention, an exchange group of the basic ion exchange resin is trimethylammonium (TMA) or dimethylethanolammonium (DMEA), and an ion type is a chloride anion (Cl.sup.) or a hydroxy group anion (OH.sup.).

[0034] In one embodiment of the present specification, a matrix of the basic ion exchange resin is a copolymer of styrene and divinylbenzene.

[0035] In one embodiment, the transesterification reaction is performed at a temperature of 40 C. or more and 100 C. or less. More specifically, the transesterification reaction is performed at a temperature of 40 C. or more and 80 C. or less. When the transesterification reaction is performed below 40 C., there is a problem in that the reaction rate is lowered, and when the transesterification reaction is performed above 100 C., there are problems that an exchange group of the strong basic ion exchange resin is decomposed and the activity is lowered, and the reuse cycle is shortened and the pH of the product increases.

[0036] In one embodiment of the present invention, in the step of transesterifying an aliphatic alcohol and a symmetric linear carbonate in the presence of a catalyst, a mass ratio of the aliphatic alcohol and the symmetric linear carbonate (aliphatic alcohol:symmetric linear carbonate) is 1:10 or more and 10:1 or less. Specifically, in another embodiment, the mass ratio of the aliphatic alcohol and the symmetric linear carbonate (aliphatic alcohol:symmetric linear carbonate) is 1:2 or more and 5:1 or less. In the transesterification reaction, when a mass ratio of the aliphatic alcohol and the symmetric linear carbonate is less than 1:10, since the amount of aliphatic alcohol is small, the symmetric linear carbonate remains in excess, and the catalyst is not sufficiently swelled, the contact with the catalyst is lowered and the efficiency is lowered, resulting in a decrease in productivity, and when the mass ratio of the aliphatic alcohol and the symmetric linear carbonate exceeds 10:1, after the reaction, a size of the distillation process to separate the heterogeneous symmetric linear carbonate (DEC) and asymmetric linear carbonate (EMC) and aliphatic alcohol increases, and as the aliphatic alcohol and asymmetric linear carbonate (EMC) are azeotropes, the larger the amount of aliphatic alcohol, the more columns with high separation efficiency are required, a lot of energy is consumed in the decompression and/or pressurization process, a large amount of asymmetric linear carbonate (EMC) is lost to the top of the distillation process, which makes the process unproductive.

[0037] In one embodiment of the present invention, the transesterification reaction is performed in a fixed bed reactor or a continuous stirred tank reactor (CSTR).

[0038] In one embodiment of the present invention, the transesterification reaction is performed in the fixed bed reactor. In this case, operation is simple and energy costs can be saved.

[0039] In one embodiment of the present invention, the fixed bed reactor may be operated in a series type. In one embodiment, the fixed bed reactor may be a reactor composed of one or more and four or less reactors in series.

[0040] Meanwhile, the method of preparing a heterogeneous linear carbonate according to the present invention may further include conventional steps known in the art before or after each of the above steps, in addition to the above steps.

[0041] Hereinafter, examples will be given to describe the present invention in detail. However, the examples according to the present invention may be modified in various other forms, and the scope of the present invention is not to be construed as being limited to the examples described below. The examples of the present specification are provided to more completely explain the present invention to those of ordinary skill in the art.

EXAMPLE 1

[0042] A fixed bed reactor was used as a series 4, and 80 cc (58 g) of a porous type basic anion exchange resin having trimethylammonium (TMA) as an exchange group and a chlorine anion (Cl) as an ion type was charged in each reactor. An exchange capacity (equivalent/l-wet resin per unit volume) was 1.3, and Samyang Corporation's TRILITE AMP-18 product was used. A mass ratio of ethanol to DMC was 0.8 and the reactor was operated continuously at 50 C. at 2 cc/min.

EXAMPLE 2

[0043] The reactor was operated in the same manner as in Example 1, except that a reaction temperature was set to 80 C. instead of 50 C. in Example 1.

EXAMPLE 3

[0044] The reactor was operated in the same manner as in Example 1, except that Samyang Corporation's TRILITE AMP-14, whose catalyst exchange capacity is 1.0 (eq/l-wet resin) instead of 1.3 (eq/l-wet resin), was used, and the reaction temperature was 80 C. instead of 50 C.

EXAMPLE 4

[0045] The reactor was operated in the same manner as in Example 1, except that Samyang Corporation's TRILITE AMP-14, whose catalyst exchange capacity is 1.0 (eq/l-wet resin) instead of 1.3 (eq/l-wet resin), was used, a mass ratio of ethanol to DMC was 0.3 instead of 0.8, and the reaction temperature was 70 C. instead of 50 C.

EXAMPLE 5

[0046] The reactor was operated in the same manner as in Example 1, except that Samyang Corporation's TRILITE AMP-14, whose catalyst exchange capacity is 1.0 (eq/l-wet resin) instead of 1.3 (eq/l-wet resin), was used, a mass ratio of ethanol to DMC was 2 instead of 0.8, and the reaction temperature was 70 C. instead of 50 C.

EXAMPLE 6

[0047] The reactor was operated in the same manner as in Example 1, except that Samyang Corporation's TRILITE AMP-14, whose catalyst exchange capacity is 1.0 (eq/l-wet resin) instead of 1.3 (eq/l-wet resin), was used, a mass ratio of ethanol to DMC was 4 instead of 0.8, and the reaction temperature was 70 C. instead of 50 C.

EXAMPLE 7

[0048] The reactor was operated in the same manner as in Example 4, except that a mass ratio of ethanol and DMC was 0.05 instead of 0.3 in Example 4.

EXAMPLE 8

[0049] The reactor was operated in the same manner as in Example 1, except that a reaction temperature was set to 120 C. instead of 50 C. in Example 1.

Comparative Example 1

[0050] The reactor was operated in the same manner as in Example 1, except that, in Example 1, Samyang Corporation's TRILITE SAR-10 product (exchange capacity is 1.3 (eq/l-wet resin)), which is a gel type (micropore) strong basic ion exchange resin having trimethylammonium (TMA) as an exchange group instead of a porous type basic anion exchange resin catalyst, and a chloride anion (Cl.sup.) as an ion type, was used.

Comparative Example 2

[0051] The reactor was operated in the same manner as in Comparative Example 1, except that a reaction temperature was set to 120 C. instead of 50 C. in Comparative Example 1.

Comparative Example 3

[0052] The reactor was operated in the same manner as in Example 1, except that, in Example 1, Samyang Corporation's DIAION WA-20 product (exchange capacity is 2.5 (eq/l-wet resin)), which is a porous type basic anion exchange resin having a secondary amine as an exchange group and a hydroxyl anion (OH.sup.) as an ionic type, instead of a porous type basic anion exchange resin catalyst having trimethylammonium (TMA) as an exchange group and a chlorine anion (Cl) as an ion type, was used.

[0053] The results of the reactor operation of Examples 1 to 8 and Comparative Examples 1 to 3 are shown in Table 1 below.

TABLE-US-00001 TABLE 1 Classification Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Conditions Exchange group TMA TMA TMA TMA TMA TMA Ion type Cl.sup.- Cl.sup.- Cl.sup.- Cl.sup.- Cl.sup.- Cl.sup.- Type Porous Porous Porous Porous Porous Porous Exchange capacity 1.3 1.3 1.0 1.0 1.0 1.0 1 (eq/1-wet resin) EtOH/DMC 0.8 0.8 0.8 0.3 2 4 Mass ratio Reaction 50 80 80 70 70 70 temperature ( C.) Results DMC 64 68 71 66 87 94 conversion rate (%) EMC 75 70 67 72 53 47 selectivity (%) DEC 25 30 33 28 47 53 selectivity [%] Comp. Comp. Comp. Classification Ex. 7 Ex. 8 Ex. 1 Ex. 2 Ex. 3 Conditions Exchange group TMA TMA TMA TMA SEA Ion type Cl.sup.- Cl.sup.- Cl.sup.- Cl.sup.- OH.sup.- Type Porous Porous Gel type Gel type Porous Exchange capacity 1.3 1.3 1.3 1.3 2.5 1 (eq/1-wet resin) EtOH/DMC 0.05 0.8 0.8 0.8 0.8 Mass ratio Reaction 70 120 50 80 80 temperature ( C.) Results DMC 20 58 50 45 10 conversion rate (%) EMC 92 80 82 87 98 selectivity (%) DEC 8 20 18 13 2 selectivity [%] *Ex.: Example; Comp. Ex.: Comparative Example

[0054] In Table 1, TMA is trimethylammonium, SEA is secondary amine, DMC is dimethyl carbonate, and EMC is ethyl methyl carbonate.

[0055] Referring to the results of Table 1, it was confirmed that a preparation method according to one embodiment of the present invention had a high DMC conversion rate by using a porous type basic ion exchange resin as a catalyst. In particular, when comparing Example 1 and Comparative Example 1, and Example 2 and Comparative Example 2 in detail, it was confirmed that, under the same conditions, the case where the porous type basic ion exchange resin was used, has a higher DMC conversion rate than the case where the gel type basic ion exchange resin was used. More specifically, it was confirmed that, in the case of Example 2 using the porous type basic ion exchange resin at 80 C., the DMC conversion rate was high, and in the case of Comparative Example 2 using the gel type basic ion exchange resin, elution of the exchange group progressed, resulting in low DMC conversion.

[0056] In addition, it was confirmed that, when comparing Example 2 and Example 8, even when the same porous type basic ion exchange resin was used, when the reaction was performed at 120 C. exceeding the heat resistance temperature range, elution of the exchange group progressed, resulting in low DMC conversion. Therefore, it is appropriate that the reaction temperature be performed at a temperature of 40 C. or more and 100 C. or less.

[0057] Referring to Examples 2 and 3 and Comparative Example 3, it was confirmed that under the same conditions, when an exchange capacity is low, the binding of the exchange group to the matrix is weak, and the exchange group participating in the reaction increases, so that the DMC conversion rate increases.

[0058] In addition, referring to Examples 4 to 7, it was confirmed the yield of heterogeneous symmetric linear carbonate (DEC) and asymmetric linear carbonate (EMC) as products can be controlled by controlling a mass ratio of aliphatic alcohol and symmetric linear carbonate (aliphatic alcohol:symmetric linear carbonate), that is, a mass ratio of ethanol and DMC (EtOH:DMC). However, in the case of Example 7, it was confirmed that a mass ratio of ethanol to symmetric linear carbonate (DMC) is less than 0.1, and an amount of reactive ethanol is small, leaving an excessive amount of DMC and not sufficiently swelling the catalyst, so that the contact with the catalyst is lowered and the DMC conversion rate is lowered. Therefore, it is preferred that a mass ratio of ethanol to a symmetric linear carbonate (DMC) is less than 0.1 and 10 or more.