Method for synthesizing pre-hydrolyzed alkyl polysilicate
10647820 ยท 2020-05-12
Assignee
Inventors
Cpc classification
International classification
Abstract
The present invention relates to a two-step synthesis method of a pre-hydrolyzed alkyl polysilicate. In the method, a silica precursor hydrated to 90 to 100% is added to maximize a condensation reaction rate, and a silica precursor hydrated to 25 to 70% is additionally added to terminate a condensation reaction, so that a condensation reaction time may be remarkably shortened relative to a conventional one-step synthesis method and may be shortened even without the use of a condensation catalyst, so that the catalyst purchase cost and the catalyst separation step in the process may not be required, thus having a simple process and reducing the production cost. Also, the amount and time point of the silica precursor additionally added may be controlled, thereby easily controlling the gelation reaction time and the weight average molecular weight, and synthesizing the pre-hydrolyzed alkyl polysilicate excellent in storage stability and processabilty.
Claims
1. A method for synthesizing a pre-hydrolyzed alkyl polysilicate, the method comprising: 1) adding a first silica precursor to perform a first condensation reaction; and 2) adding a second silica precursor to perform a second condensation reaction, wherein the first silica precursor is hydrated to 90 to 100%, and the second silica precursor is hydrated to 25 to 75%.
2. The method of claim 1, wherein the first silica precursor is hydrated with 1.8 to 2 equivalents of water.
3. The method of claim 1, wherein the second silica precursor is hydrated with 0.5 to 1.5 equivalents of water.
4. The method of claim 1, wherein the first condensation reaction rate is faster than the second condensation reaction rate.
5. The method of claim 1, wherein the silica precursor is at least one selected from the group consisting of tetra methyl ortho silicate (TMOS), tetra ethyl ortho silicate (TEOS), methyl triethyl ortho silicate, dimethyl diethyl ortho silicate, tetra propyl ortho silicate, tetra isopropyl ortho silicate, tetra butyl ortho silicate, tetra secondarybutyl ortho silicate, tetra tertiarybutyl ortho silicate, tetra hexyl ortho silicate, tetra cyclohexyl ortho silicate and tetra dodecyl ortho silicate.
6. The method of claim 1, wherein the mass ratio of the added first silica precursor and second silica precursor is 10:1 to 10:3.
7. The method of claim 1, wherein the second silica precursor is added after 1 to 3 hours from adding the first silica precursor.
8. The method of claim 1, wherein the total condensation reaction time of the synthesis method is 3 to 10 hours.
9. The method of claim 1, wherein the first and second condensation reactions are performed without a condensation catalyst.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1) The following drawings attached to the specification illustrate preferred examples of the present invention by example, and serve to enable technical concepts of the present invention to be further understood together with detailed description of the invention given below, and therefore the present invention should not be interpreted only with matters in such drawings.
(2)
(3)
(4)
(5)
MODE FOR CARRYING OUT THE INVENTION
(6) Hereinafter, the present invention will be described in more detail to allow for a clearer understanding of the present invention. It will be understood that terms or words used in the present specification and claims shall not be interpreted as the meaning defined in commonly used dictionaries. It will be further understood that the words or terms should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the technical idea of the invention, based on the principle that an inventor may properly define the meaning of the words or terms to best explain the invention.
(7) A method for synthesizing a pre-hydrolyzed alkyl polysilicate according to an embodiment of the present invention includes the steps of: 1) adding a first silica precursor to perform a first condensation reaction; and 2) adding a second silica precursor to perform a second condensation reaction, wherein the first silica precursor is hydrated to 90 to 100%, and the second silica precursor is hydrated to 25 to 75%.
(8) Generally, when a monomer such as TEOS is used as a silica precursor, the molecular weight of a final product or the gelation reaction time is difficult to be controlled, and the stability is lowered. So, a pre-hydrolyzed alkyl poly silicate oligomer having a molecular weight of about 1000 is prepared and used. This is because, unlike a monomer such as TEOS, when an oligomer type material is used, the stability may be obtained even when the hydration degree is increased for controlling the gelation reaction time. However, the pre-hydrolyzed alkyl polysilicate has a very low condensation reaction rate and thus needs a long time for synthesis thereof, and when a catalyst is used to increase the synthesis rate, the molecular weight of the oligomer, which is a final product, is difficult to be controlled, the additional cost resulting from catalyst purchase occurrs, and a catalyst separation process is added in the synthesis step, so that the process may be complicated and the production cost may be increased.
(9) Accordingly, the present invention introduces a novel two-step synthesis method in which the first silica precursor having a hydration degree of 90 to 100% is added to maximize the condensation reaction rate, and the second silica precursor having a hydration degree of 25 to 75% is further added to terminate the condensation reaction, thereby solving the above problems. In addition, the added amount of the further added second silica precursor and the time point of addition are controlled, so that there is provided a method for synthesizing a novel pre-hydrolyzed alkyl polysilicate which may easily control the gelation reaction time and weight average molecular weight and synthesize a pre-hydrolyzed alkyl polysilicate excellent in storage stability.
(10) Hereinafter, a method for synthesizing a novel pre-hydrolyzed alkyl polysilicate according to an embodiment of the present invention will be described in detail for each step.
(11) Step 1)
(12) Step 1) according to an embodiment of the present invention is a step of maximizing a condensation reaction rate to shorten a total condensation reaction time, wherein the first silica precursor is added to perform the first condensation reaction.
(13) The silica precursor usable in the present invention may be a silicon-containing alkoxide-based compound, and specifically, may be tetra alkyl silicate such as tetra methyl ortho silicate (TMOS), tetra ethyl ortho silicate (TEOS), methyl triethyl ortho silicate, dimethyl diethyl ortho silicate), tetra propyl ortho silicate, tetra isopropyl ortho silicate, tetra butyl ortho silicate, tetra secondary butyl ortho silicate, tetra tertiarybutyl ortho silicate, tetra hexyl ortho silicate, tetra cyclohexyl ortho silicate, tetra dodecyl ortho silicate, or the like. More specifically, the silica precursor in the present invention may be tetra ethyl ortho silicate (TEOS).
(14) In addition, in the present invention, the first silica precursor may be one in which the silica precursor usable in the present invention is hydrated with 1.8 to 2 equivalents of water to have a hydration degree of 90 to 100%.
(15) As shown in Reaction Formula 1 below, a conventional method for synthesizing a pre-hydrolyzed alkyl polysilicate performed the condensation reaction in which the silica precursor reacted with 1.54 equivalents of water to produce a silica precursor partially hydrated to less than 90%. In this case, there was a problem that a long condensation reaction time of 24 hours is required.
(16) ##STR00001##
(17) Accordingly, in order that the present invention solves the problem of long condensation reaction time, as shown in Reaction Formula 2, the first silica precursor having a hydration degree of 90 to 100% is hydrated with 1.8 to 2 equivalents of water to maximize the condensation reaction rate, so that the problem of long synthesis time required in the conventional method has been solved.
(18) ##STR00002##
(19) More specifically, the tetra alkyl silicate usable as the silica precursor of the present invention is hydrated theoretically with up to two equivalents of water, so that four OR groups may be substituted with OH groups, and the OH groups become a reaction site, and the condensation reaction occurs. Therefore, the greater the equivalent weight of water reacting with the tetra alkyl silicate, the more the hydration reaction occurs, and thus the more OR groups are replaced with OH groups, thereby increasing the condensation reaction rate.
(20) The first silica precursor added in Step 1) of the present invention is obtained by hydration reaction with 1.8 to 2 equivalents of water, and 90 to 100% of OR groups may be replaced with OH groups to maximize the condensation reaction rate.
(21) Accordingly, the present invention does not require the use of a phosphorus nitrogen compound (PNC) condensation catalyst such as a phosphonitrilic chloride trimer which is conventionally used as a condensation reaction catalyst, so that the molecular weight of the final product is easily controlled, and the catalyst purchase cost and the catalyst separation step in the process are not required. Therefore, there is an advantage that the process may be simple and the production cost may be reduced.
(22) On the other hand, by controlling an alcohol content added to the hydration step, a silica (SiO.sub.2) content included in the pre-hydrolyzed alkyl polysilicate finally generated may be controlled so as to be 0.1 wt % to 30 wt %. When the silica content is less than 0.1 wt %, a silica gel content generated after the gelation reaction is too low, and thus there is a possibility that a required level of chemical properties may not be expected; when the silica content exceeds 30 wt %, the excessive formation of silica gel may cause the mechanical properties, particularly flexibility, to be deteriorated.
(23) Step 2)
(24) Step 2) according to an embodiment of the present invention is a step of terminating the condensation reaction, wherein the second silica precursor is added to perform the second condensation reaction. Meanwhile, in the second silica precursor, the kind of silica precursor and the silica content, which may be used, are the same as those described in Step 1).
(25) In addition, in the present invention, the second silica precursor may be one in which the silica precursor usable in the present invention is hydrated with 0.5 to 1.5 equivalents of water to have a hydration degree of 25 to 75%.
(26) More specifically, when the tetra alkyl silicate usable as the silica precursor of the present invention is hydrated to a certain level or more to perform the condensation reaction, the condensation reaction is not terminated due to the presence of a large number of the OH groups as reaction sites, so that the pre-hydrolyzed alkyl polysilicate may be produced in which the molecular weight is not easily controlled and the molecular weight distribution is somewhat wider; when the added amount of silica precursor is reduced to terminate the condensation reaction arbitrarily, the viscosity may easily increase during storage and custody prior to the gelation reaction, so that storage stability and processability may be degraded.
(27) Thus, conventional synthesis methods have used less than 90% partially hydrated tetra alkyl silicate, so that the pre-hydrolyzed alkyl polysilicate is generally synthesized through the condensation reaction.
(28) However, in order to maximize the condensation reaction rate in the present invention, it is inevitable to use the silica precursor having a hydration degree of 90 to 100% by being hydrated with 1.8 to 2 equivalents of water. Accordingly, in order to solve the problem that the condensation reaction is not terminated, the silica precursor, which is hydrated with 0.5 to 1.5 equivalents of water to have a hydration degree of 25 to 75%, is sequentially added in two-step, thereby enabling the condensation rate to be maximized and the condensation reaction to be terminated in an adequate level, so that a pre-hydrolyzed alkyl polysilicate having optimum molecular weight, storage stability, processability was intended to be synthesized.
(29) Therefore, as shown in Reaction Formula 3 below, the present invention is characterized by providing a method for synthesizing an alkyl polysilicate pre-hydrolyzed by a two-step process, wherein the first silica precursor hydrated to 90 to 100% by being hydrated with 1.8 to 2 equivalents of water is added to obtain a maximum condensation reaction rate through the first condensation reaction, and then the condensation reaction is slowly terminated while 0.5 to 1.5 equivalents of water and the second silica precursor hydrated to 25 to 75% are added to perform the second condensation reaction.
(30) ##STR00003##
(31) On the other hand, the first condensation reaction rate is characterized to be faster than the second condensation reaction rate. The first condensation reaction is a step of maximizing the condensation reaction rate in order to shorten the time taken in the whole process, and the second condensation reaction is a step of appropriately terminating the condensation reaction to synthesize the pre-hydrolyzed alkyl polysilicate having the optimum molecular weight, storage stability and processability.
(32) In this regards, according to the synthesis method of the present invention, the condensation reaction time may be remarkably shortened from conventional 24 hours to about 4 hours, and at the same time, the molecular weight may be easily controlled according to the required physical properties, and the viscosity is maintained during a certain period of about 60 days, so that there is an effect that an pre-hydrolyzed alkyl polysilicate excellent in storage stability and processability may be synthesized.
(33) Meanwhile, the termination of the condensation reaction indicates that OR groups increase on the surface of oligomer not to condensate the silica precursor any more due to the steric hindrance of bulky OH groups, and the termination may be observed at a point where the rate of the condensation reaction is remarkably decreased and then maintained at a low level or the weight average molecular weight is stabilized without further increasing.
(34) In the present invention, in order to maximize the condensation reaction rate, synthesize the pre-hydrolyzed alkyl polysilicate oligomer in an appropriate weight average molecular weight, and control the gelation reaction time, it is important that the first and second silica precursors are added at an adequate ratio.
(35) Accordingly, the mass ratio of the first and second silica precursors added in the synthesis method of the present invention is characterized to be 10:1 to 10:3. In the present invention, when the first and second silica precursors are added based on the above numeral range, the condensation reaction rate may be maximized and the condensation reaction rate may be also terminated at an appropriate level, thereby enabling the weight average molecular weight of the finally produced oligomer, the gelation reaction time to be easily controlled and the storage stability and processabilty to improve.
(36) When a small amount of the second silica precursor is added so as to exceed the above numeral range, the condensation reaction rate may not be terminated in an appropriate level to produce an oligomer having an excessive molecular weight, and the amount of OH groups present in the surface of the oligomer is large to excessively increase the gelation reaction time, so that there may be a problem that the processability and the easiness of process is deteriorated.
(37) In addition, the present invention controls the time point of addition of the second silica precursor after the addition of the first silica precursor, thereby enabling the weight average molecular weight of the finally produced pre-hydrolyzed alkyl polysilicate to be controlled.
(38) In the synthesis method of the present invention, when the second silica precursor is added after 1 to 3 hours from the addition of the first silica precursor, a pre-hydrolyzed alkyl polysilicate having a weight average molecular weight of 1000 to 1500, more specifically 1200 to 1500, which is targeted by the present invention may be synthesized.
(39) When the second silica precursor is added earlier than the above-mentioned time, the effect of increasing the synthesis rate may be decreased due to the maximization of the first condensation reaction rate targeted by the present invention, and the oligomer having a weight average molecular weight smaller than the targeted level of the present invention may be produced; when being added later than the above-mentioned time, the oligomer having a weight average molecular weight larger than the level targeted by the present invention may be produced, thereby deteriorating viscosity properties and storage stability.
(40) In addition, the present invention provides a pre-hydrolyzed alkyl polysilicate which is synthesized by the above synthesis method to be excellent in viscosity properties, storage stability and processability.
(41) As described above, in the method for synthesizing a pre-hydrolyzed alkyl polysilicate according to an embodiment of the present invention, the first silica precursor, which is hydrated to 90 to 100% with 1.8 to 2 equivalents of water, is added to maximize the condensation reaction rate, and the second silica precursor, which is partially hydrated to 25 to 75% with 0.5 to 1.5 equivalents of water is further added to introduce a two-step process for terminating the condensation reaction, so that the condensation reaction time may be remarkably shortened in comparison with the conventional one-step synthesis method and may be shortened without the use of a condensation catalyst, thus having a simple process and reducing the production cost. Also, the added amount and time point of further adding the second silica precursor are controlled, so that there is an effect that the gelation reaction time and the weight average molecular weight may be easily controlled and the pre-hydrolyzed alkyl polysilicate excellent in storage stability and processability may be synthesized.
(42) Hereinafter, examples of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. The present invention may, however, be embodied in many different forms, and should not be construed as limited to the examples set forth herein.
Example 1
(43) 80 g of a first TEOS was stirred with 24 g of ethanol and 13.9 g of a HCl aqueous solution of pH 1.8 was added, and thus the first TEOS reacted with 2 equivalent of water to be hydrated completely. Thereafter, a first condensation reaction was performed by heating at 85 C. for 2 hours.
(44) After 2 hours from the addition of the first TEOS, 20 g of a second TEOS, which was partially hydrated with 6 g of ethanol and 0.87 g of a HCl aqueous solution of pH 1.8, was added, and thus a second condensation reaction was carried out by heating at 85 C. for 2 hours.
(45) Then, the temperature was lowered to room temperature, and the finally produced pre-hydrolyzed ethyl polysilicate oligomer was recovered.
Examples 2 and 3
(46) A pre-hydrolyzed ethyl polysilicate oligomer was synthesized in the same manner as in Example 1, except that the addition ratio of the equivalent weight of water and the first and second silica precursors to 1 mol of the second silica precursor was used in an amount as shown in Table 1 below in Example 1.
Comparative Example 1
(47) A pre-hydrolyzed ethyl polysilicate oligomer was synthesized in the same manner as in Example 1, except that only the first silica precursor was added and the second silica precursor was not added in Example 1.
Comparative Examples 2 and 3
(48) A pre-hydrolyzed ethyl polysilicate oligomer was synthesized in the same manner as in Example 1, except that the equivalent weight of water added relative to 1 mol of the first silica precursor is changed into the amount as shown in Table 1 below in Example 1.
Comparative Example 4
(49) A pre-hydrolyzed ethyl polysilicate oligomer was synthesized in the same manner as in Example 1, except that only the addition time of the second silica precursor was different from that shown in Table 1 below in Example 1.
Experimental Example 1: Measurement of Weight Average Molecular Weight (Mw, g/Mol)
(50) The weight average molecular weights of the respective pre-hydrolyzed ethyl polysilicate oligomers synthesized in Examples 1 to 3 and Comparative Examples 1 to 4 were measured, and the results were shown in
Experimental Example 2: Measurement of Gelation Reaction Time
(51) The time taken for the gelation reaction was measured by using the respective pre-hydrolyzed ethyl polysilicate oligomers synthesized in Examples 1 to 3 and Comparative Examples 1 to 4.
(52) Specifically, an ammonia catalyst diluted with ethanol was added in an amount of 10 vol % to the mixed solution produced by mixing each of pre-hydrolyzed ethyl polysilicate, ethanol and water at a weight ratio of 2:4:1, so that the pH was adjusted to 4 to 9 to perform the gelation reaction.
(53) TABLE-US-00001 TABLE 1 Addition Equivalent of time of water added Ratio of second per mol of second TEOS Number of TEOS TEOS after Condensation Gelation TEOS (mol) added adding reaction reaction additions First second to first first time time Classification (times) TEOS TEOS TEOS TEOS (hr) (min) Example 1 2 2 0.5 0.2 2 4 10 Example 2 2 2 0.5 0.1 2 8 6 Example 3 2 2 0.5 0.3 2 8 15 Comparative 1 2 Not be 4 Example 1 terminated Comparative 1 1.5 24 14 Example 2 Comparative 1 1.3 24 25 Example 3 Comparative 2 2 0.5 0.2 4 8 8 Example 4
(54) (Effects on Condensation Reaction Time Through TEOS Addition in Two Steps)
(55) As shown in Table 1, it was ascertained that the condensation reaction time was significantly shortened from 24 hours to 4 to 8 hours in Examples 1 to 3 of the present invention adding TEOS in two steps as compared with Comparative Examples 1 to 3 adding TEOS in single step like the conventional synthesis reaction method.
(56) As shown in
(57) In addition, according to
(58) (Effects of Controlling the Gelation Reaction Time Depending on the Addition Ratio of the First and Second TEOSs)
(59) As shown in Table 1, it can be observed that as the ratio of the second TEOS partially hydrated is increased, the OR group at the end of the oligomer which w is the final product increases to increase the gelation reaction time, and on the contrary, as the ratio of the second TEOS partially hydrated is decreased, the OH group at the end of the oligomer which i as the final product increases to decrease the gelation reaction time.
(60) In Examples 1 to 3 of the present invention, the condensation reaction time could be remarkably shortened, and at the same time, the desired gelation reaction time of the present invention could be also secured.
(61) Accordingly, it was found that the addition ratio of the first and second TEOSs could be controlled, thus enabling the gelation reaction time of the finally synthesized pre-hydrolyzed ethyl polysilicate oligomer to control.
(62) (Effects of Controlling the Weight Average Molecular Weight Depending on the Addition Ratio of the First and Second TEOSs)
(63) As shown in Table 1,
(64) (Measurement of Weight Average Molecular Weight Depending on the Time Point of Addition of the Second TEOS)
(65) As shown in Table 1, Comparative Example 4 in which the second TEOS was added after 4 hours from adding the first TEOS could remarkably shorten the condensation reaction time as in Example 1 in which the second TEOS was added after 2 hours, and could perform a control so as to have an appropriate gelation reaction time.
(66) However, as shown in
(67) However, in Example 1 in which the second TEOS was further added after 2 hours from when the first TEOS was added, it was ascertained that the condensation reaction time was significantly shortened and the appropriate gelation reaction time was secured, and at the same time, the pre-hydrolyzed ethyl polysilicate having an appropriate weight average molecular weight targeted by the present invention may be synthesized.
(68) Through the above experiment, it may be seen that the effects of shortening the condensation reaction time and controlling the gelation reaction time and the weight average molecular weight are obtained by introducing a novel two-step HTEOS synthesis method in which the TEOS highly hydrated to 90 to 100% is added to maximize the condensation reaction rate, and the TEOS partially hydrated 25 to 70% is further added to terminate the condensation reaction, thus controlling the amount and time point of addition of TEOS.
(69) The foregoing description of the present invention has been presented for purposes of illustration. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.