CAPSULE FOR ISOSTATIC PRESSING AND METHOD

Abstract

A capsule 2 for HIPing comprises a rigid, self-supporting additive manufactured (AM) component 3 which is welded to inner and outer cylindrical liners 4, 6 through which cooling channel tubes 8, 10 extend. A solid end plate 11 is welded to ends of the liners 4, 6 and tubes 8, 10 extend through the end plate 11 and open to the outside. A fill tube 12 communicates with an annular void 14 defined between liners 4, 6 which is filled with powder 16. In use, the capsule 2 is subjected to Hot Isostatic Pressing (HIP). Thereafter, the inner and outer liners 4, 6 are removed to define a valve seat assembly comprising the AM component 3, tubes 8, 10, HIPed powder 16 and end plate 11.

Claims

1-28. (canceled)

29. A capsule for hot isostatic pressing, the capsule comprising: (i) an additive manufactured (AM) element; (ii) a capsule element (A), wherein the capsule element (A) is arranged to define at least part of a void for containing a powder arranged to be subjected to hot isostatic pressing.

30. A capsule according to claim 1, wherein the AM element includes a selective surface, wherein the AM element includes an opening which extends from a first position on the AM element to a second position on the AM element, with a void being defined between the first and second positions.

31. A capsule according to claim 1, wherein the AM element includes an array of substantially identical parts.

32. A capsule according to claim 1, wherein the AM element includes a first volume which has a density of 98% of its fully dense density or greater.

33. A capsule according to claim 1, wherein the AM element is not substantially homogenous, does not comprise a single mass of material and the density of the mass of material which is incorporated in the AM element is not substantially constant across its entire extent.

34. A capsule according to claim 1, wherein the AM element includes unconsolidated powder which is flowable within a volume (A) defined in the AM element, wherein the volume (A) is fully enclosed by a solid wall of the AM element.

35. A capsule according to claim 6, wherein the volume (A) comprises support elements which extend between upper and lower walls which define volume (A) and are arranged to support parts of the AM component during manufacture of the AM element.

36. A capsule according to claim 6, wherein the volume (A) or each wall which defines volume (A) does not incorporate a selective surface.

37. A capsule according to claim 1, wherein the AM element of the capsule for hot isostatic pressing comprises a supplemented AM element wherein additional powder has been incorporated into an AM element which is the direct product of an AM process.

38. A capsule according to claim 1, wherein the outer surfaces of the AM element are a direct product of an AM manufacturing technique.

39. A capsule according to claim 1, wherein the AM element is arranged to define at least part of a void including a powder therein.

40. A capsule according to claim 1, wherein capsule element (A) is secured to the AM element and capsule element (A) is made from a different material compared to that of the AM element, wherein the capsule element (A) comprises a sheet material which is secured to the AM element and, preferably, the capsule includes a capsule element (B) which comprises a sheet material which is secured to the AM element.

41. A capsule according to claim 1, wherein the AM element includes a surface which is an outer surface of the capsule and the AM element is not fully encapsulated by other regions of the capsule.

42. A capsule according to claim 1, wherein a void for containing a powder is defined, at least in part, by capsule element (A), capsule (B) and the AM element.

43. A method of producing a component, the method comprising: (i) selecting a capsule according to claim 1; (ii) subjecting the capsule to hot isostatic pressing.

44. A method according to claim 15, wherein subsequent to step (ii) a part of the capsule is removed from association with the AM element.

45. A method according to claim 16, wherein less 10% of the outer surface of the component is treated after removal of parts of the capsule which are not included in the component.

46. A method of producing a capsule, comprising: (i) selecting an additive manufactured (AM) element; (ii) constructing a capsule, wherein a first region of the capsule is defined, at least in part, by the AM element.

47. A method according to claim 18, wherein step (ii) of the method comprises constructing regions of the capsule around the AM element so that a first region of the capsule is defined by the AM element and, optionally, a second region of the capsule is defined by the AM element wherein step (ii) comprises constructing the capsule by selecting at least three individual and/or separate elements which are made from sheet material and associating the three elements with the AM element to define a capsule with a void being defined at least in part by the AM element, wherein, subsequent to step (ii), a powder is introduced into a void in the capsule.

48. A capsule for hot isostatic pressing, the capsule comprising: (i) an additive manufactured (AM) element; (ii) a capsule element (A), wherein the capsule element (A) is arranged to define at least part of a void for containing a powder arranged to be subjected to hot isostatic pressing; the AM element includes a selective surface, and further wherein the AM element includes an opening which extends from a first position on the AM element to a second position on the AM element, with a void being defined between the first and second positions; the outer shape and/or entire outer surfaces of the AM element are a direct product of an AM manufacturing technique; the capsule element (A) comprises a sheet material which is secured to the AM element and the capsule includes a capsule element (B) which comprises a sheet material which is secured to the AM element; and the AM element includes a surface which is an outer surface of the capsule and the AM element is not fully encapsulated by other regions of the capsule.

49. A capsule according to claim 20, wherein the AM element includes a first volume which has a density of 98% of its fully dense density or greater; the AM element includes unconsolidated powder which is flowable within a volume (A) defined in the AM element, wherein the volume (A) is fully enclosed by a solid wall of the AM element; the volume (A) comprises support elements which extend between upper and lower walls which define volume (A) and are arranged to support parts of the AM component during manufacture of the AM element; and wherein the capsule includes powder which makes up at least 10 wt % of the total weight of the capsule.

Description

[0100] Specific embodiments of the invention will now be described, by way of example, with reference to the accompanying drawings, in which:

[0101] FIG. 1 is a cross-section through a capsule of a valve seat assembly;

[0102] FIG. 2 is a perspective view, partly cut-away, of an AM element of the assembly of FIG. 1;

[0103] FIGS. 3 to 6 show stages in the manufacture of the assembly of FIG. 1;

[0104] FIG. 7a is a perspective view of a flow meter body, with a closure plate omitted in the interests of clarity;

[0105] FIG. 7b is a view of the flow meter body of FIG. 7a showing inclusion of a fill/evac tube;

[0106] FIGS. 8 to 11 show a sequence of steps involved in forming a capsule comprising the flow meter body of FIG. 7;

[0107] FIG. 12 is a perspective view, partly cut-away, of a turbine disc;

[0108] FIG. 13 is a perspective view of a capsule comprising the turbine disc of FIG. 12; and

[0109] FIG. 14 is a cross-section through the assembly of FIG. 13.

[0110] In the figures, the same or similar parts have the same reference numerals.

[0111] Referring to FIGS. 1 to 6, a capsule 2 for HIPing comprises a rigid, self-supporting AM component 3 which is welded to inner and outer cylindrical liners 4, 6 through which cooling channel tubes 8, 10 extend (only tube 8 is shown in FIG. 1 but both tubes 8, 10 are shown in other figures). A solid end plate 11 is welded to ends of the liners 4, 6 and tubes 8, 10 extend through the end plate 11 and open to the outside. A fill tube 12 communicates with an annular void 14 defined between liners 4, 6 which is filled with powder 16. In use, the capsule 2 is subjected to HIP as described below. Thereafter, the inner and outer liners 4, 6 are removed to define a valve seat assembly comprising the AM component 3, tubes 8, 10, HIPed powder 16 and end plate 11.

[0112] The capsule 2 and its production are described in more detail below.

[0113] The AM component 3 is manufactured using a laser powder bed 3D printing process with a single laser head. The powder used for the build is a stainless steel or a nickel-based alloy. The AM component is designed and the design supplied in a STEP format to allow a CAD model to be produced for programming of the AM build. The AM component is built layer by layer using an optimised build speed to achieve a high density wall free from porosity and defects. After the build, the AM component is stress relieved and then removed from the build plate and any support structure removed.

[0114] The AM component must be able to be TIG, MIG and/or EBW welded and also compatible for joining by welding to other parts, for example liners 4, 6 of the capsule 2.

[0115] The AM component 3 defines an annular valve seat which is made in a suitable wear resistant material. It includes a wear face 17 which is frusto-conical in shape and body 18 in which are defined cooling galleries 20 which communicate with tubes 8, 10. Tubes 8, 10 are arranged to transport a cooling fluid towards and away from the wear face to cool the wear face in use.

[0116] The AM component has a maximum diameter of about 150 mm and a maximum thickness (measured perpendicular to the maximum diameter) of about 20 mm.

[0117] The AM component 3 also includes diametrically spaced apart openings 22, 24 (FIG. 2) which are arranged to receive tubes 8, 10 which extend beyond an end 26 of liners 4, 6 and project from outer face 28 of end plate 11. The tubes 8, 10 are welded in position as represented by weld lines 30, 32 (FIG. 3).

[0118] The AM component 3 also includes inner and outer annular stepped regions 34, 36. Inner stepped region 34 is arranged to engage inner circular cross-section liner 4 and outer stepped region 36 is arranged to engage outer liner 6. The inner liner 4 is arranged to be welded to the AM component as represented by weld lines 38 (FIG. 4) and the outer liner 6 is arranged to be welded to the AM component 3 as represented by weld lines 40 (FIG. 5).

[0119] The inner and outer liners 4, 6 comprise sheet metal which may be selected from mild steel, stainless steel and aluminium.

[0120] At an opposite end to the AM component, the capsule 2 includes the end plate 11 which comprises a solid material which may be stainless steel, steel or a nickel-based alloy. The end plate is arranged to be engaged with the assembly of FIG. 5. To this end, it includes annular grooves arranged to engage the free ends of liners 4, 6 and includes openings through which tubes 8, 10 may be positioned. The end plate 11 is welded to liners 4, 6 and tubes 8, 10 as represented by weld lines 42, 44, 46, 48. When so arranged, void 14 is defined between end plate 11, liners 4, 6 and AM component 3. To provide access to the void 14, fill tube 12 is welded to an outwardly facing wall of liner 6.

[0121] The steps for manufacturing the capsule 2 of FIG. 1 are represented sequentially in FIGS. 2 to 6.

[0122] After construction of the capsule of FIG. 1, it is evacuated by connecting a vacuum line to tube 12 and then is subjected to helium leak testing to ensure it is gas-tight. Next, it is filled with powdered metal via tube 12. The powdered metal is selected from stainless steels including austenitic, ferritic and martensitic grades, duplex and super duplex stainless steels, Ni, Ti and CoCr alloys together with metal matrix/composite alloys. The metal powder may be filled up to 100% volume of the capsule void. The powder fill weight is calculated based on the capsule design and the particle size distribution of the metal powder. The metal powder is filled into the capsule void and may be vibrated preferably to achieve a known powder fill weight and an optimum powder packing density.

[0123] After filling of the capsule, it is evacuated of entrapped air by connecting a vacuum line to tube 12 and pulling a vacuum. Then, tube 12 is crimped to seal the assembly.

[0124] Next, the capsule is subjected to HIP by placing it in a HIP system and subjecting it to a predetermined temperature and pressure for a predetermined time. The HIP temperature must be suitable for both the metal powder and material from which the AM component is made and is usually driven by the material (e.g. alloy) with the lowest solidus temperature.

[0125] After HIP, the capsule is placed in a heat treatment furnace for a predetermined temperature for a predetermined time in order to achieve optimum material properties for the final component.

[0126] After HIP, parts of the capsule which are not to be included in the final component may be removed. This may be done by immersion of the post-HIPed assembly in various acids and stages for a suitable time to dissolve away the sheet steel which encases the component. In particular, liners 4, 6 are dissolved away, leaving a valve seat assembly comprising said AM component 3, HIPed powder 16 with tubes 8, 10 extending there through and end plate 12. The AM component 3 is fully dense by virtue of it having been HIPed and consolidated powdered metal 16 is also fully dense by virtue of it having been HIPed. The AM component and consolidated powdered metal are diffusion bonded to one another by virtue of the HIP process. The metallic or bi-metallic component produced has no porosity or defects. The consolidated powdered metal part will have a fine homogenous grain size and the AM component will consist of a very fine grained structure that will be homogenised and reveal less segregation than the as built condition due to the treatment of the AM element during the HIP cycle. The joining of the AM component to the powder component takes place by diffusion bonding of the powder particle surfaces to the AM component without any melting or liquid phases which eliminates the presence of a heat affected zone, this being replaced by a thin 10-50 micron diffusion zone between the powder and the AM component.

[0127] Similarly, the end plate 11 and consolidated powdered metal are diffusion bonded to one another by virtue of the HIP process. This takes place without any melting or liquid phases which eliminates the presence of a heat affected zone, this being replaced by a thin (10-50 micron) diffusion zone between the powder and AM component.

[0128] Advantageously, the AM component 3 does not require any machining (or other metal removal process) after HIP and removal of parts of the capsule which are not to be included in the final component. The AM component defines wear face 17 which is a selective surface which cooperates with another part of a valve (e.g. an intake or exhaust valve) (not shown). The wear face 17 is made to a close tolerance (e.g. +/0.2 to 0.3 mm) in the process so that it can accurately engage the other part of the valve.

[0129] Other parts of the final component (which may not include selective surfaces and/or which can be made to lower tolerances compared to that of the AM component) may be subjected to some machining (e.g. a clean-up operation on end plate 11 and/or bores).

[0130] Referring to FIG. 7a, an AM component 52 is arranged to define a selective surface of a fluid flow measuring device, treated in a HIP process.

[0131] The AM component 52 of FIG. 7a is manufactured using a laser powder bed 3D printing process as described for the FIG. 1 embodiment. However, in contrast to the FIG. 1 embodiment, the AM component includes powder which has not been consolidated by laser treatment in the manufacturing process. Thus, the AM component 52 includes a fully-fused area 54, defined to the left of line 56 shown in FIG. 7a. The fully-fused area defines a selective surface of component 52 which generally require no post-HIP machining.

[0132] To the right of line 56, relatively thin, solid, outer wall 58 which is part circular is defined by the laser fully fusing powder in the powder bed. The outer wall extends up from a generally circular, solid, planar base 60 which is also defined by the laser fully fusing powder in the powder bed. Inwards of the outer wall 58, support posts 62 are defined which are produced by the laser fully fusing powder in the powder bed. The support posts 62 extend upwardly from the base 60 and are arranged to support a planar top 64 (omitted from FIG. 7a in the interests of clarity, but shown in FIG. 8) which is formed by fusion of powder by energy from the laser.

[0133] Defined inwards of the outer wall 58 is an opening 65 defined by wall 66 which is produced by the laser fully fusing powder in the powder bed. Between the outer wall 58, wall 66, base 60 and top 65, the AM component 52 includes a volume 53 which includes unconsolidated powderi.e. powder which has not been impinged by the laser to melt it.

[0134] The ratio of the sum of the cross-sectional areas of the support posts (immediately below the planar top 64) divided by the area defined between the posts (immediately below the planar top 64) in which unconsolidated powder is arranged may be in the range 0.25 to 0.55, preferably in the range 0.3 to 0.45, more preferably in the range 0.33 to 0.42.

[0135] The ratio of the sum of the volumes occupied by all the support posts divided by the volume surrounding the support posts and/or occupied by unconsolidated powder may be in the range 0.25 to 0.55, preferably in the range 0.3 to 0.45, more preferably in the range 0.33 to 0.42.

[0136] The AM component has a thickness x (FIG. 7a) of about 40 mm, a width y of about 30 mm and the diameter between points Q and R is about 100 mm.

[0137] Thus, the AM component 52 of FIG. 7a defines a selective surface (which includes a cut-out volume 55) and other regions which comprise fully fused powder, together with a volume of powder which is not consolidated but is arranged between the support posts 62. By virtue of this arrangement, the AM component can be made much more rapidly (and with less energy usage) compared to a case wherein the entirety of the powder used for the component 52 is consolidated with the laser, during additive manufacturing.

[0138] The AM component 52 may be included in a capsule 70 (FIG. 11) as described with reference to FIGS. 8 to 11. However, before incorporation, additional powder is introduced, via a fill/evac tube 57 (FIG. 7b), into volume 53 to supplement the powder therein. The additional powder is packed into volume 53 and is arranged so that, after HIPing of AM component 52, the powder and posts 62 in volume 53 define a volume having a density of greater than 98% (of its fully dense density) and the volume may be substantially fully dense.

[0139] Advantageously, the tube 57 may be incorporated into the AM component 52 during manufacture of the AM component.

[0140] Referring to FIG. 8, the AM component 52 is represented including a cut-away portion 72 of the top 67 to show unconsolidated powder 74 within the component 52, although it will be appreciated that the volume which includes the powder is in reality fully closed by parts of the AM component. The AM component 52 may be incorporated in capsule 70 whilst including unconsolidated powder 74. However, in a preferred embodiment, additional powder is incorporated into volume 53 as described with reference to FIG. 7b and component 52 is then HIPed as described herein before it is incorporated into capsule 70. This may reduce the risk of failure of the AM component 52.

[0141] Referring to FIG. 9, a tapered tube 78, having a square cross-section, is welded (see weld lines 80) around opening 65. The tube 78 may be made from nickel alloy.

[0142] Next, referring to FIG. 10, an outer, circular cross-section, sleeve 80 is positioned around tube 78 and it is welded to the AM component 52 along weld line 82. The outer sleeve 80 may be made from mild steel, stainless steel, titanium or aluminium.

[0143] Next, referring to FIG. 11, a closure plate 84 (which may be made of the same material as outer sleeve 80) is welded to sleeve 80 along weld line 86 and to an outer edge of the tapered tube 78 along weld line 88. A fill tube 90 extends through and is welded to the closure plate 84.

[0144] After construction of the capsule of FIG. 11, it is evacuated, tested, filled with powder and subjected to HIP as described for the embodiment of FIGS. 1 to 6. After HIP, it is placed in a heat treatment furnace as described above and thereafter the outer sleeve 80, closure plate 84 and fill tube 90 are removed, for example by dissolution in acid.

[0145] Referring to FIG. 12, a turbine disc 100 (approximate diameter of 200 mm and thickness of 20 mm) is arranged to define a selective surface of a turbine wheel assembly. The disc 100 is manufactured using a laser powder bed 3D printing process as described for the FIG. 7 embodiment and therefore defines an AM component. The disc includes an annular blade ring 102 incorporating arcuate vanes 103 around its entire periphery. Inwards of the blade ring 102 are spaced apart, circular, closure plates 104, 106 (FIG. 14). Extending between the plates 104, 106 is an array of spaced apart support posts 108 which are defined by the laser fully fusing powder in the powder bed during manufacture of the disc 100. Between the plate 104, 106 and the posts 108, the disc 100 includes a volume which includes unconsolidated powderi.e. which has not been impinged by the laser to melt it. The area/volume occupied by the posts and unconsolidated powder may be as described for the component 52.

[0146] Thus, the turbine disc of FIG. 12 defines a selective surface (i.e. comprising ring 102 and vanes 103); and other regions (e.g. plates 104, 106 and posts 108) which comprise fully fused powder, together with a volume of powder 108 which is not consolidated. As described for the FIG. 7 embodiment, the disc can be made more rapidly (and with less energy usage) compared to a corresponding disc wherein there is no unconsolidated powder. In a preferred embodiment, the disc 100 of FIG. 12 includes a fill/evac tube (not shown) via which additional powder is introduced to supplement powder 108. The disc 100 is preferably HIPed as described herein before being incorporated into a capsule. After HIPing, the disc 100 may be substantially fully dense.

[0147] A capsule incorporating the disc 100 (which has preferably been HIPed as described) may be manufactured as shown in FIGS. 13 and 14. Referring to the figures, a cylindrical cap 110 incorporating a fill tube 112 is welded about its periphery at 114 to closure plate 106. A stepped cap 116, which includes fill tube 111, is welded about its periphery 118 at its lower end to closure plate 104.

[0148] The cylindrical cap 110 and stepped cap 116 may be made from mild steel, stainless steel, titanium or aluminium.

[0149] After construction of the capsule of FIGS. 13 and 14, it is evacuated, tested, filled with powder and subjected to HIP as described for the previous embodiments. After HIP, it is placed in a heat treatment furnace as described and, thereafter, caps 110, 116 including respective fill tubes 112, 111 are removed, for example by dissolution in acid.

[0150] Advantageously, the method may be used to produce relatively large components (e.g. having a maximum dimension of about 400 mm which incorporate selective surfaces which are accurately produced (and are arranged to cooperate in use with another surface or part) and other surfaces which are not selective surfaces and/or which may be made less accurately and/or with wider tolerances compared to the selective surfaces. Using the method described, components may be produced relatively rapidly and efficiently.

[0151] The invention is not restricted to the details of the foregoing embodiment(s). The invention extends to any novel one, or any novel combination, of the features disclosed in this specification (including any accompanying claims, abstract and drawings), or to any novel one, or any novel combination, of the steps of any method or process so disclosed.