METHOD FOR THE PRODUCTION OF PELLETS OF SINTERED MATERIAL, SUCH AS BORON CARBIDE PELLETS

Abstract

A method for producing pellets of sintered material, comprising: a) forming calibrated pre-compacts by first uniaxial pressing of equal portions powder at a first threshold below the maximum green density threshold of the powder; b) providing a pressing tool set comprising a die having a plurality of cavities and pressure pistons; c) placing the pre-compacts in the cavities with first and second sintered boron nitride disks, having a thickness in the millimetre range and a density >=90%; d) forming calibrated compacts by second uniaxial pressing of the pre-compacts using the pressure pistons at a second threshold greater than the first threshold, which is less than or equal to the maximum green density of the powder; e) forming sintered compacts by applying pressure and a pulsed current to the pressing tool set to bring about a rapid rise in temperature according to a temperature-, pressure- and duration-controlled SPS sintering cycle.

Claims

1. Method for manufacturing pellets of sintered material comprising the following steps in sequence: a) formation of pre-compacts calibrated by a first uniaxial compaction on portions with equal masses of material in powder form, this first compaction being made to a first threshold below the maximum unbaked density threshold achievable for the powder material; b) supply of a compression tool comprising a die with a plurality of cavities and compression pistons designed to slide in the cavities; c) placement of the pre-compacts in the cavities of the die, first and second disks made of sintered boron nitride, with millimetric thickness and density greater than or equal to 90% being arranged in each cavity at a first and at a second end of each pre-compact; d) formation of calibrated compacts by a second uniaxial compaction on the pre-compacts, this second compaction being made in the die by means of compression pistons to a second threshold higher than the first threshold that is less than or equal to the maximum unbaked density threshold achievable for the powder material; e) formation of sintered compacts by loading and under a pulsed current in the compression tool, so as to induce a fast temperature rise in an SPS sintering cycle with regulated temperature, pressure and duration; f) extraction of sintered compacts from the die.

2. Method according to claim 1, further comprising a step between step b) and step c) in which a graphite film is applied to cover an internal wall of each cavity that will come into contact with the pre-compacts, and a compression piston contact face that will come into contact with one of the first and second boron nitride disks.

3. Method according to claim 2, further comprising another step between step b) and step c) in which a graphite film is applied to cover interfaces between the pre-compacts and the first boron nitride disks, and interfaces between the pre-compacts and the second boron nitride disks.

4. Method according to claim 1, wherein the sintered material is boron carbide (B.sub.4C).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0028] Other characteristics and advantages of the invention will become clear after reading the following detailed description of preferred embodiments of the invention, given as non-limitative examples, with reference to the appended drawings among which:

[0029] FIG. 1a is a diagrammatic representation of an example of a piston and a compression die comprising four cavities, in a perspective view;

[0030] FIG. 1b is a diagrammatic representation of the compression die in FIG. 1a, showing a top view;

[0031] FIG. 2 is a sectional view of a compression tool ready to be inserted in a chamber of an SPS device;

[0032] FIG. 3 shows a partial cross-sectional view of an example of an SPS sintering device that can be used for implementation of the method according to the invention.

[0033] It should be noted that the different elements are not shown to scale in the figures.

DETAILED PRESENTATION OF A PARTICULAR EMBODIMENT

[0034] The method according to the invention can be used to make pellets of a high density sintered material using the SPS sintering method in a multi-cavity die. This method is particularly useful for manufacturing high density B.sub.4C pellets at an industrial scale for nuclear use. These high density B.sub.4C pellets can be used particularly as neutron absorbers, particularly in 4.sup.th generation fast neutron reactors.

[0035] The use of a multi-cavity die in SPS sintering requires perfect control of the current and particularly its path in the compression tool. A bad current distribution will generate hot points and lead to the formation of heterogeneities within the sintered materials.

[0036] In order to manufacture pellets of a high density sintered material, and particularly B.sub.4C pellets, using the method according to the invention, two essential points have to be guaranteed.

[0037] Firstly, the compression tool has to be balanced and the piston height has to be adjusted.

[0038] This is done by making calibrated pre-compacts starting from portions of powder (with equal masses weighed using a high precision weighscale) by a first uniaxial pressing to a first threshold lower than the maximum achievable unbaked density threshold of the powder material, then they are put into the multi-cavity die. A second uniaxial pressing of the pre-compacts is then made to a second threshold that is higher than the first threshold and that is close to the maximum unbaked density achievable for the powder material in a multi-cavity die. Preferably, the second threshold is located as close as possible (if possible equal to) the maximum density threshold achievable for the unbaked powder material. Each of the calibrated compacts thus has an equivalent density. It should be noted that the first pressing is preferably made in a single-cavity die, but it could perfectly well be made in the multi-cavity die used for the second pressing.

[0039] Thus, the compression tool is balanced and the piston height is constant. This enables the application of an equivalent (uniform) pressure on all pre-compacts during the advance movement of the pistons during the heat treatment in SPS sintering. This ensures the most uniform possible current distribution and therefore a more uniform temperature distribution, particularly for large volume compression tools. Furthermore, this second compaction maintains the multi-cavity die on the lower pistons, without it sliding when it is in the vertical position. The compacts bear on the lower faces of the cavities of the multi-cavity die.

[0040] The risk of hot points also has to be eliminated and the current necessary for SPS sintering must be channelled away from bearing points between the pistons and the pre-compacts.

[0041] This is done using sintered boron nitride (BN) disks with a millimetric thickness (for example, 2.5 mm thick) and high purity (99.7%). For example, BN disks sold under the tradename Combat BN grade AX05 made by the Saint Gobain company can be used. These disks are placed above and below the pre-compacts in the cavities of the die.

[0042] The presence of these disks assures that no current will pass from the pistons to the pre-compacts (no hot point), including for very high currents due to the significant thickness of BN disks compared with the thickness of a deposit made by spraying a suspension. Current will bypass the boron nitride disks since the disks form an electrically insulating layer, including at very high temperature.

[0043] Since the current distribution is controlled and uniform, the temperature of the pre-compacts is more uniform. The result is better uniformity in terms of density and microstructure (grain size) throughout the volume of the pellets.

[0044] The dense nature of the disks guarantees their mechanical strength and greater robustness than deposits with low cohesion made by spraying.

[0045] The millimetric thickness of the disks is such that the disks can resist SPS sintering temperatures, in other words temperatures higher than 1000 C., that can approach 2000 C. under controlled atmosphere.

[0046] Finally, unlike a fine and porous deposit of boron nitride made by spraying, a dense disk with millimetric thickness prevents potential pollution of the compact because it is much less fragile.

[0047] In order to illustrate the method according to the invention, we will now describe an example embodiment of high density B.sub.4C pellets.

[0048] In this example embodiment, we made the pre-compacts 7 using a stainless steel single-cavity die provided with a through moulding cavity, and two stainless steel pistons that will slide in the moulding cavity to compact the powder in the cavity and thus form the pre-compacts 7. To make the calibrated compacts, we used a graphite compression tool comprising a multi-cavity die 1 provided with four through moulding cavities 2 distributed symmetrically in a circular layout within the die, as illustrated in FIG. 1b, and eight pistons 3 (only one piston being shown on FIG. 1a) that will slide inside the cavities 2 to compact the pre-compacts 7 in the cavities and thus form calibrated compacts with the required shape and dimensions. The pistons operate in pairs and displace in opposite directions during the compression.

[0049] The diameter of the cavity in the single-cavity die is 20 mm and the diameter of the cavities in the multi-cavity die is 20.4 mm, the difference allowing for the 200 m thickness of Papyex.

[0050] In our example embodiment, the four cavities of the multi-cavity die are 120 mm high.

[0051] HS grade B.sub.4C powder from H. C. Starck was used as the raw material to form four portions with the same mass (15.60 g).

[0052] To make the pre-compacts 7, one of the powder portions was added into the cavity of the stainless steel single-cavity compression die and a first uniaxial compaction was made at low pressure (<10 MPa) at a density less than the maximum value achievable with the powder, namely 1 MPa for 1 minute. These operations were repeated for each powder portion.

[0053] The pre-compacts 7 thus obtained were then extracted from the single cavity die and stored while waiting to be used later.

[0054] A piece of Papyex foil 4 was cut to the internal dimensions of the internal lateral wall of each of the cavities of the multi-cavity die 1 and was placed on this internal lateral wall in each cavity.

[0055] The four lower pistons 3 are inserted in the lower part of the cavities and a Papyex Disk 6 with the same dimension as the head of the lower piston is placed in the bottom of each cavity.

[0056] Note that the terms lower and upper, bottom and top, below and above refer to elements as shown on FIG. 2.

[0057] A 2.5 nm thick Combat BN grade AX05 lower disk 5 is then inserted in each cavity.

[0058] The four pre-compacts 7 are introduced in the cavities 2 of the die.

[0059] According to one advantageous variant of the invention, a Papyex disk 6 is placed at the bottom and the top of the pre-compacts 7.

[0060] A 2.5 nm thick AX05 type BN upper disk 5 is then inserted in each cavity.

[0061] And a Papyex disk 6 with the same dimension as the head of the upper piston is placed on the BN upper disk.

[0062] The four upper pistons are inserted in the cavities so as to close the cavities.

[0063] The assemblies represented in FIG. 2 are thus obtained. It should be noted that the die as shown in FIG. 2 is a sectional view along line AA in FIG. 1a. Graphite plates 9 can conduct current and apply pressure uniformly on the pistons. In this embodiment, each of these plates 9 comprises four cylindrical cavities 10 machined in one of their faces. In this case, these cavities 10 have a diameter of 20.5 mm and a depth of 1 mm. They enable the pistons to anchor in them and hold the plates in place.

[0064] Maximum compaction is then made at high pressure to a threshold close to the maximum achievable unbaked density for the powder material. A pressure of 50 MPa is applied for 1 minute.

[0065] The next step is to cut the felt 8 made of a thermally insulating material, for example a graphite felt, to the dimensions of the die and it is placed above, below and around the die so as to limit thermal radiation during SPS sintering.

[0066] The die thus prepared is then placed in a chamber of an SPS sintering device 100 (FIG. 3) and a vacuum is created in the chamber 11. FIG. 3 represents an example of an SPS sintering device 100 for use of the device according to the invention, this device comprising in particular a chamber 11 and means 12 of applying a current and a load (or pressure) on the compression die 1. It should be noted that for simplification reasons, the die as shown on FIG. 3 only comprises two cavities and the Papyex foil and disks, and the boron nitride disks have not been shown.

[0067] The SPS sintering cycle is then performed, simultaneously applying a pressure and a pulsed electric current to increase the temperature of the compacts to a sufficiently high temperature plateau to cause sintering of the powder in the compacts.

[0068] In SPS sintering, the time during which the temperature plateau is maintained is relatively short and is generally between several seconds and several minutes (usually less than 10 minutes).

[0069] In a known manner, the temperature plateau, the pressure and the duration are optimised to obtain the required density.

[0070] In our example embodiment, SPS sintering was done at a pressure of 20 MPa per piston, with a temperature increase of 50 C./min, a temperature plateau of 2000 C. for a duration of 2 minutes, applying a maximum current of 5540 A.

[0071] The pressure and the temperature are then lowered and four pellets of sintered compacts are extracted from the die.

[0072] The pellet surface may possibly be ground so as to eliminate residual traces of Papyex and BN, for example by polishing with abrasive paper, using a diamond disk or a grinder fitted with a diamond tool.

[0073] The four pellets thus obtained only have an average relative density of 99.33% as measured by hydrostatic weighing, with a standard deviation of 0.03%.

[0074] Therefore the method according to the invention can increase the relative density of B.sub.4C after sintering compared with the Hot Pressing method under similar temperature and pressure conditions. Note that the relative density that can be obtained using the HP method is of the order of 96%.

[0075] It also makes it possible to refine the microstructure of the sintered material, which in the case of the B.sub.4C material, can increase the mechanical strength of the sintered material so that it has better resistance to the temperature gradient during use. Since by definition, an SPS sintering cycle is very short, enlargement of the grains is very small compared with an HP sintering cycle.

[0076] The method can also increase productivity compared with conventional SPS sintering due to the use of multi-cavity tooling and short sintering cycles.

[0077] We have illustrated the method according to the invention by manufacturing of B.sub.4C pellets, but the method can be applied to manufacturing of any element made of a sintered material and is particularly useful for applications for which it is necessary to obtain high density sintered material.