PRECIOUS METAL RECOVERY FROM CARBON FINES

Abstract

A method for the recovery of a precious metal from activated carbon fines which includes the steps of adsorption of the precious metals from the activated carbon fines onto a weak-base anion exchange resin which contains guanidine functional groups in the presence of at least one suitable lixiviant, or adsorption of the precious metals from activated carbon fines onto a mixed-base resin which contains amine functional groups in the presence of at least one suitable lixiviant and eluting the resin with a suitable eluant to produce a precious metal-containing eluate.

Claims

1. A method for the recovery of a precious metal from activated carbon fines which includes the steps of: (a)(i) adsorption of the precious metals from the activated carbon fines onto a weak-base anion exchange resin which contains guanidine functional groups in the presence of at least one suitable lixiviant, or (a)(ii) adsorption of the precious metals from the activated carbon fines onto a mixed-base resin which contains amine functional groups in the presence of at least one suitable lixiviant wherein the lixiviant is a combination of an alkaline cyanide solution, caustic or lime and an organic reagent which promotes the release of the precious metal from the carbon fines during leaching; and (b) eluting the resin with a suitable eluant to produce a precious metal-containing eluate.

2. A method according to claim 1 wherein the precious metal is silver or gold.

3. A method according to claim 1 wherein the organic reagent is diesel.

4. A method according to claim 1 wherein the method is carried out at a temperature of 60° C.

5. A method according to claim 1 wherein the alkaline cyanide solution is a sodium or a metal cyanide reagent.

6. A method according to claim 1 wherein loading of the weak-base guanidine resin or the mixed-base amine resin in the lixiviant is done in a resin-in-leach (RIL) process.

7. A method according to claim 1 wherein the elution of the precious metal loaded onto the weak-base guanidine resin or mixed-base amine resin is done with a sodium hydroxide eluant which contains any one of the following additives: sodium lauryl sulphate, 2-ethyl-hexanoic, benzoic acid, versatic acid, or any other organic carboxylic acid group forming salts.

8. A method according to claim 7 wherein the organic carboxylic acid forming salts include 4-methylbenzoic acid sodium salt, sodium benzoate or sodium versatate

9. A method according to claim 1 wherein the precious metal containing eluate undergoes further processing including electrowinning, precipitation or cementation for final recovery of the precious metal.

10. A lixiviant suitable for leaching a precious metal from carbon fines in a resin-in-leach (RIL) process in the presence of a weak-base guanidine ion exchange resin or a mixed-base amine ion exchange resin, the lixiviant including a cyanide solution, an alkaline agent and an organic blinding agent.

11. A lixiviant according to claim 9 wherein the organic blinding agent is diesel.

12. (canceled)

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0029] The invention is further described by way of example with reference to the accompanying drawings wherein:

[0030] FIG. 1 is a flow diagram showing steps of a method for recovering precious metals from activated carbon fines according to the invention;

[0031] FIG. 2 is a graph depicting an equilibrium adsorption isotherm showing the efficiency of gold absorption onto a resin from carbon fines using a method according to the invention;

[0032] FIG. 3 is a graph depicting equilibrium adsorption data showing efficiency of gold adsorption using a method according to the invention at relatively low grade carbon fines;

[0033] FIG. 4 is a graph depicting an equilibrium elution isotherm, comparing gold elution efficiency from the resin using various eluants according to the invention; and

[0034] FIG. 5, FIG. 6 and FIG. 7 are graphs depicting gold elution breakthrough curves using the method of the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0035] FIG. 1 is a flowsheet of a method 10 according to the invention which includes the steps of combining finely milled carbon 12 and process water 14 in a step 16 to produce fine carbon slurry 18.

[0036] The fine carbon slurry 18 is exposed to a weak-base guanidine resin or mixed-base amine resin 20 in the presence of a lixiviant 22 during an RIL process step 24.

[0037] Subsequently, a separation step 26 is carried out to remove a loaded resin 28 from a carbon waste slurry 30.

[0038] The loaded resin 28 is eluted in a step 32 by exposing the loaded resin 28 to a suitable eluant 34 to strip the precious metals into a resulting eluate 36 and to regenerate the resin 20 (eluted resin).

[0039] Assuming the gold-loaded fine milled carbon 12 is received dry, the process water 14 is added during the step 16 to make up the carbon slurry 18 containing 10-30% solids m/m. The carbon slurry 18 is then be leached using the lixiviant 22 containing sodium cyanide, caustic and diesel in the presence of the resin 20 to form the precious metal loaded weak-base guanidine resin or mixed-base amine resin in hydroxide form 28.

[0040] Following the step 24, the loaded resin 28 is separated in the step 26 from the waste carbon slurry 30 via screening.

[0041] The loaded resin 28 is then contacted with a hydroxide-based eluant 34 in the step 32 to form a gold-containing eluate 36.

[0042] The eluant 34 can be a sodium hydroxide eluant with a carboxylic acid additive such as sodium lauryl sulphate, 4-methylbenzoic acid forming salts such as 4-methylbenzoic acid sodium salt, sodium benzoate, sodium versatate or any other suitable eluant

[0043] The gold containing eluate 34 can be processed directly via electrowinning. The waste carbon slurry 28 can be disposed of in a tailings facility.

[0044] The eluted resin 20 is returned to the RIL process step 24 for adsorption of gold from carbon fines.

EXPERIMENTAL RESULTS

Carbon Head Grade

[0045] Fine carbon from 2 different sources was used for the test work, namely samples A and B. Sample B had a significantly higher metal loading compared to sample A, with gold grades at 655 g/t and 287 g/t respectively. Table 1 shows the loading of metals on the resin. Carbon samples A and B had a size fraction of 80% passing 105 μm.

TABLE-US-00001 TABLE 1 Element Sample A analysis, g/t Sample B analysis, g/t Au 287 655 Ag 897 3745 Al 14233 14040 Ca 62385 73860 Co 45 70 Cu 304 545 Fe 20732 25030 Ni 1202 1640 Zn 278 350

Equilibrium Adsorption Isotherm

[0046] Carbon sample B was used to generate two equilibrium adsorption isotherms. The test work conditions were as follows: test temperature of 60° C., carbon slurry solids content of 25% m/m and contact time of 12 hours. The lixiviants used and resin are summarised in the Table below. Variable resin-slurry ratios were used to generate the equilibrium adsorption isotherm. On completion of the test, the carbon, resin and solutions were analysed. The equilibrium adsorption result is shown in FIG. 2.

TABLE-US-00002 TABLE 2 Cyanide Sodium Diesel concen- Hydro- concen- tration xide tration (added as concen- (blinding NaCN) tration reagent) Test ID Resin Tested mg/L mg/L mg/L Adsorption Weak-Base (WB) 3 4 0 Test 1 guanidine Adsorption Weak-Base (WB) 1 4 4 Test 2 guanidine

[0047] The recovery of the gold from the carbon was effective. The leach and adsorption data are comparable for Test 1 and Test 2. It has been observed that the cyanide concentration can be reduced significantly with the addition of the diesel as a blinding reagent as this reagent allows the carbon to more effectively release the gold during leaching.

[0048] The addition of the blinding reagent is both a cost effective and a more environmentally acceptable option.

[0049] Carbon sample A was used to generate an equilibrium adsorption isotherm for the mixed-base amine resin. The test work conditions were as follows: test temperature of 60° C., carbon slurry solids content of 25% m/m and contact time of 12 hours. The lixiviant used was 3 g/L cyanide as sodium cyanide, and sodium hydroxide was used to maintain the leach between pH 10.2-10.5. Variable resin-slurry ratios were used to generate the equilibrium adsorption isotherm. On completion of the test, the carbon, resin and solutions were analysed. The equilibrium adsorption result is shown in FIG. 3.

[0050] The mixed-base amine resin was also effective in recovering the gold from the carbon. The mixed-base amine resin performed better than the guanidine resin under the same conditions. A resin loading of 17989 g/t was observed in equilibrium with a residual of 106 g/t on the carbon.

Elution Equilibrium Isotherm

[0051] A gold solution generated during the stripping of various loaded resin from the leaching section was used to pre-load the weak-base guanidine resin and the mixed-base amine resin for elution testwork. The composition of the eluate can be seen in Table 3. This was done in a batch process at a pH 10.5. The gold loadings for the weak-base guanidine resin and the mixed-base amine resin were 840 mg/L and 621 mg/L respectively. The loaded resin was then used for the subsequent elution testwork. The elution equilibrium tests were conducted at 60° C. for 12 hours at variable eluant to resin ratios.

TABLE-US-00003 TABLE 3 Element Solution analysis, mg/L Au 60.4 Ag 178 Al 0.51 Ca 41.2 Co 0.63 Cu 8.9 Fe 9 Ni 7.6 Zn 0.88

[0052] The weak-base guanidine resin elution was tested using sodium lauryl sulphate, 4-methylbenzoic acid sodium salt and sodium versatate in subsequent tests at a concentration of 0.35 mol/L carboxylic acid and 30 g/L sodium hydroxide. FIG. 4 shows the equilibrium elution data points which were fitted with a Freundlich equilibrium isotherm. Based on the data generated, sodium versatate performed best followed by sodium lauryl sulphate and 4-methylbenzoic acid sodium salt.

Column Elution Test

[0053] The column elution test was done at a temperature of 60° C., at a flowrate of 3 BV/h. The gold loadings for the weak-base guanidine resin and 840 mg/L. Tests were done with sodium lauryl sulphate, sodium versatate and 4-methylbenzoic acid sodium salt at 0.35 mol/L carboxylic acid and sodium hydroxide at 30 g/L for each test. FIG. 5 illustrates the column elution test results. 4-methylbenzoic acid sodium salt performed the best achieving a peak concentration of 65 mg/L Au after 6 BV. The elution efficiencies for Au on all reagents ranged between 65-75% after 30 BV. This overall relatively low elution efficiency is as a result of the low Au loading of the resin.

[0054] A weak-base guanidine resin was pre-loaded with carbon sample B to a loading of 5916 mg/L. Elution was done using a 0.35 mol/L versatic acid and 30 g/L sodium hydroxide eluant composition. The column elution test was done at a temperature of 60° C., at a flowrate of 2 BV/h. FIG. 6 illustrates the elution profile obtained. The peak concentration achieved was 1200 mg/L Au in the eluate after 4 BV. An elution efficiency for Au of 87% was achieved after 9 BV. The initial Au loading on the resin has a significant impact on the elution efficiency of the resin.

[0055] The column elution test was done on a mixed-base amine resin at a temperature of 60° C., at a flowrate of 3 BV/h. The gold loading for the mixed-base amine resin was 621 mg/L. Tests were done with sodium hydroxide at a concentration of 30 g/L. FIG. 7 illustrates the column elution test results. A peak concentration of 166 mg/L Au after 2 BV with a elution efficiency of 91% achieved after 10 BV.

BENEFITS OF THE INVENTION

[0056] Using RIL with the weak-base guanidine resin or mixed-base amine resin for the recovery of precious metals from carbon fines is a cost-effective process with lower capital and operating costs, compared to current incineration treatment processes.

[0057] High overall precious metal recoveries are achievable with this process route.

[0058] The gold eluate produced from the process is caustic-based and can fed directly into the existing carbon eluate stream to an electrowinning circuit.

[0059] High gold grades are achievable in the elution and hence there is minimal impact of dilution on the carbon eluate stream.

[0060] This process plant can be built as a module in an existing gold processing plant; therefore, the gold producer can realise the gold revenue immediately.

[0061] This process solution limits security risks and hence high transport costs as the fine carbon is treated onsite at the gold producer.