Self-leveling concrete

Abstract

The invention relates to uniformed concrete comprising, in percentages by weight, (d) 87% to 98% of particles comprising more than 90 wt.-% alumina, (c) 1% to 7% silica fume particles, (f) 1% to 8% particles of a hydraulic cement, the fraction of said particles having a size less than 40 m being distributed as follows, in percentage by weight in relation to the weight of the unformed concrete: fraction <0.5 m: 4%, fraction <2 m: 5%, fraction <10 m: 19%, fraction <40 m: 34%-52%, fraction between 2 m and 40 m: 26.5%-34%,
the concentration of Zro2, in percentage by weight on the basis of the uniformed concrete, being less than 2%, and the concentration of organic fibres, in percentage by weight on the basis of the uniformed concrete, being less than or equal to 0.03%.

Claims

1. An unshaped concrete configured for the preparation of a self-levelling fresh concrete, said unshaped concrete comprising, as percentages by weight, (a) 87% to 98% of particles comprising more than 90% by weight of alumina, (a) 1% to 7% of particles of silica fume, (c) more than 3% and up to 8% at most of particles of a hydraulic cement, the hydraulic cement comprising, as main constituents, alumina and calcium aluminates, the fraction of said particles having a size of less than 40 m being distributed, as percentages by weight with respect to the weight of the unshaped concrete, in the following way: fraction <0.5 m: 4%, fraction <2 m: 5%, fraction <10 m: 19%, fraction <40 m: 34%-52%, provided that the percentage by weight, with respect to the weight of unshaped concrete, of the fraction of between 2 m and 40 m is between 26.5% and 34%, the content of ZrO.sub.2, as percentage by weight on the basis of the unshaped concrete, being less than 2% and the content of organic fibers, as percentage by weight on the basis of the unshaped concrete, being less than or equal to 0.03%.

2. The unshaped concrete as claimed in claim 1, comprising from 0.075% to 1% of a surface-active agent and/or comprising a setting accelerator.

3. The unshaped concrete as claimed in claim 1, in which the hydraulic cement constitutes up to 6% of the weight of the unshaped concrete.

4. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <0.5 m: 5% and/or fraction <2 m: 7.5% and/or fraction <10 m: 25% and/or fraction <40 m: 35% and 52%, and/or fraction of between 2 m and 40 m: 27% and/or 32%.

5. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <0.5 m: 6% and/or fraction <2 m: 8% and/or fraction <10 m: 27% and/or fraction <40 m: 37% 52%, and/or fraction of between 2 m and 40 m: 30%.

6. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <0.5 m: 8% and/or fraction <2 m: 10% and/or fraction <10 m: 40% and/or fraction <40 m: 50% and 34%.

7. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <2 m: 16% and/or fraction <10 m: 35% and/or fraction <40 m: 47% and 34%.

8. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <2 m: 15% and/or fraction <40 m: 43% and 34%.

9. The unshaped concrete as claimed in claim 1, in which the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <2 m: 13%.

10. The unshaped concrete as claimed in claim 1, which exhibits a ZrO.sub.2 content of less than 1.5%.

11. The unshaped concrete as claimed in claim 10, which exhibits a ZrO.sub.2 content of less than 1%.

12. The unshaped concrete as claimed in claim 11, which exhibits a ZrO.sub.2 content of less than 0.5%.

13. The unshaped concrete as claimed in claim 1, which comprises for a total of more than 95% of the weight of said unshaped concrete: Al.sub.2O.sub.3: 81.5%-98.5% SiO.sub.2: 0.8%.

14. The unshaped concrete as claimed in claim 1, which exhibits the composition by weight such that: Al.sub.2O.sub.3: 93% and/or SiO.sub.2: 1.5%.

15. The unshaped concrete as claimed in claim 13, which exhibits the composition by weight such that: Al.sub.2O.sub.3: 97% and/or SiO.sub.2: 4%.

16. The unshaped concrete as claimed in claim 1 in which the surface-active agent is a modified polycarboxylate ether.

17. The unshaped concrete as claimed in claim 1, in which the maximum size of the particles is less than or equal to 10 mm.

18. The unshaped concrete as claimed in claim 1, in which the fraction of the particles with a size of less than 500 m represents more than 50% of the weight of said unshaped concrete.

19. The unshaped concrete as claimed in claim 1, in which the fraction of the particles with a size of between 40 m and 500 m is between 8% and 25%, with respect to the weight of said unshaped concrete.

Description

DETAILED DESCRIPTION

(1) Nature of the Particles

(2) Preferably, the sum of the assemblies (a), (b) and (c) represents more than 95%, preferably more than 97%, preferably more than 98%, indeed even more than 99%, of the weight of the unshaped concrete.

(3) Preferably, the zirconia content of the unshaped concrete, as percentage by weight on the basis of the weight of the unshaped concrete, is less than 1.5%, preferably less than 1%, indeed even less than 0.5%, and indeed even substantially zero. In one embodiment, the zirconia is an impurity, that is to say is not deliberately added.

(4) Preferably, the unshaped concrete exhibits the following composition by weight, for a total of more than 95%, preferably for a total of more than 97%, preferably for a total of more than 98%, indeed even for a total of more than 98.9%: Al.sub.2O.sub.3: 81.5% -98.5% SiO.sub.2: 0.8%-7%.

(5) Preferably, Al.sub.2O.sub.3: 85%, preferably 87%, preferably 90%, preferably 92%, preferably 93%, and/or 97%, and/or SiO.sub.2: 1%, preferably 1.5%, preferably 2%, and/or 5%, preferably 4%.

(6) The unshaped concrete may also exhibit a composition, as percentages by weight and for a total of more than 97%, preferably for a total of more than 98%, indeed even for a total of more than 98.9%, such that: Al.sub.2O.sub.3: 93%-97%, SiO.sub.2: 2%-4%.

(7) In a preferred embodiment, the assembly ((a)+(b)+(c)) exhibits a composition, the remainder of which to 100% with Al.sub.2O.sub.3, SiO.sub.2 and ZrO.sub.2 is composed of CaO (which results conventionally from the presence of hydraulic cement) and of impurities. The impurities may, for example, be Na.sub.2O, K.sub.2O, metal particles and/or TiO.sub.2.

(8) The particles (a) may be formed from one or more sources of starting materials, exhibiting different chemical analyses. The particle size distributions of the particles may also differ according to said sources.

(9) The following sources may in particular be used:

(10) an fused-cast refractory product, such as Jargal M, produced and sold by the Socit Europenne des Produits Rfractaires, exhibiting the following typical chemical analysis: Al.sub.2O.sub.3: 95%, SiO.sub.2: 0.5%, Na.sub.2O: 4%, others: 0.5%, the size of the particles of Jargal M preferably being greater than 50 m and less than 10 mm;

(11) fused-cast alumina, which is provided in the form of a powder, the particles of which have a size preferably of between 10 m and 10 mm;

(12) tabular alumina, which is provided in the form of a powder, the particles of which have a size preferably of between 10 m and 10 mm;

(13) calcined alumina, which is provided in the form of a powder, the particles of which have a size preferably of between 1 m and 50 m;

(14) reactive alumina or a mixture of reactive aluminas, comprising more than 99% of Al.sub.2O.sub.3, it being possible for the median size of the particles of reactive alumina to preferably vary from 0.5 m to 3 m.

(15) Preferably, the assembly of the particles (a) of the unshaped concrete:

(16) exhibits a content by weight of alumina of greater than 92%, preferably greater than 95%, preferably greater than 98%, preferably greater than 99%, and/or

(17) represents more than 90%, preferably more than 91%, and/or less than 96%, preferably less than 94%, of the weight of the unshaped concrete, and/or

(18) comprises reactive alumina in an amount by weight of greater than 7%, greater than 10%, greater than 12%, and/or of less than 18%, less than 16%, less than 15%, on the basis of the weight of the unshaped concrete, and/or

(19) comprises calcined alumina in an amount by weight of greater than 10%, greater than 14%, and/or of less than 25%, less than 22%, less than 20%, and/or

(20) comprises fused-cast alumina in an amount by weight of greater than 50%, greater than 55%, greater than 60%, and/or of less than 75%, less than 70%, less than 65%, on the basis of the weight of the unshaped concrete.

(21) Preferably, the assembly of the particles (b) of the unshaped concrete:

(22) exhibits a content by weight of silica of greater than 90%, indeed even greater than 92%, indeed even greater than 95%, and/or

(23) represents more than 2%, preferably more than 3%, and/or less than 6%, preferably less than 5%, of the weight of the unshaped concrete.

(24) The assembly of the particles (b) is preferably a silica fume powder sold by the Socit Europenne des Produits Rfractaires. This vitreous silica powder comprises more than 93% of silica (SiO.sub.2), the particles having a size of between 0.1 and 5 m and a median size of 0.5 m.

(25) Advantageously, the presence of silica makes it possible to reduce the amount of water necessary to render the fresh concrete flowable. It appears that the very fine silica particles are well distributed and subsequently make it possible to obtain good binding in the cured and sintered concrete. For this reason, it is considered that it is preferable to have between 3% and 5% of silica fume in an unshaped concrete according to the invention.

(26) The assembly of particles (c) of hydraulic cement preferably constitutes more than 3% and/or less than 6% by weight of the unshaped concrete. The hydraulic cement (c) may be a high-alumina cement or a mixture of different cements. In order to limit the lime (CaO) content, it is preferable to use a cement having a high alumina content, such as the CA25 cement from Almatis. The CA25 cement comprises more than 78% of Al.sub.2O.sub.3 and less than 19% of CaO. The particles of the CA25 cement have a median size of approximately 8 m.

(27) Preferably, the alumina content of the hydraulic cement is greater than 60% by weight. More preferably, the hydraulic cement comprises, as main constituents, alumina and calcium aluminates.

(28) The organic fibers (d) are, for example, polypropylene, polyacrylonitrile or polyvinyl alcohol fibers.

(29) In one embodiment, the unshaped concrete comprises more than 0.01% of fibers. Preferably, the mean length (arithmetic mean) of these fibers is greater than 6 mm, preferably between 18 and 24 mm.

(30) The presence of organic fibers makes it possible to improve the green strength of the cured concrete and limits the formation of cracks as it is being dried. Furthermore, the organic fibers are removed during the sintering or the phase of temperature rise of the furnace, thus creating a network of small channels which makes possible a more efficient evacuation of the water. However, these fibers are not essential.

(31) Furthermore, the addition of fibers reduces the property of the fresh concrete to be self leveling. Above 0.03%, the presence of fibers prevents the fresh concrete from being self leveling. Preferably, the unshaped concrete comprises less than 0.03% of fibers, indeed even comprises substantially no fibers. In one embodiment, the unshaped concrete comprises less than 0.03% of fibers, indeed even comprises substantially no fibers exhibiting a length of greater than 6 mm, in particular between 18 and 24 mm.

(32) Preferably, the unshaped concrete according to the invention also comprises at least one surface-active agent (e), preferably in a proportion of 0.1% to 1%, preferably of greater than or equal to 0.2%, and/or of less than 0.5%, more preferably less than 0.4%. The role of this surface-active agent is in particular to modify the rheological properties of the fresh concrete in order to facilitate the pumping thereof. Use is preferably made of surface-active agents chosen from long-chain sodium polyphosphates, sodium polyacrylates, ammonium polyacrylates, modified polycarboxylates and their mixtures. Preferably, the surface-active agents are chosen from modified polycarboxylates, preferably of modified polycarboxylate ether type, more preferably based on polyethylene glycol.

(33) Preferably, the unshaped concrete according to the invention also comprises at least one setting accelerator (f), preferably in a proportion of 0.01% to 0.15%. The setting accelerators are well known by a person skilled in the art.

(34) Particle Size Distribution

(35) Preferably, the maximum size of the particles of unshaped concrete according to the invention is less than or equal to 10 mm, preferably less than or equal to 8 mm, preferably less than or equal to 5 mm.

(36) In one embodiment, the fraction of the particles with a size of greater than 500 m is greater than 40%, indeed even greater than 44%.

(37) In one embodiment:

(38) the fraction of the particles with a size of greater than 500 m is greater than 40%, greater than 44% and less than 50%, and/or

(39) the fraction of the particles with a size of greater than 1250 m is greater than 8%, greater than 15%, greater than 19%, greater than 23% and less than 27%, and/or

(40) the fraction of the particles with a size of greater than 2500 m is greater than 4%, greater than 10%, greater than 13% and less than 17%.

(41) Preferably, the fraction of the particles of the unshaped concrete with a size of less than 500 m represents more than 50% by weight of said unshaped concrete.

(42) Preferably, the fraction of the particles of the unshaped concrete with a size of between 40 m and 500 m is between 8% and 25%, is preferably greater than 9%, greater than 11% and/or less than 25%, less than 23%, less than 21%, less than 17%, less than 15%, on the basis of the weight of said unshaped concrete.

(43) Preferably, the particles of the unshaped concrete are distributed in the following way, as percentages by weight: fraction <0.5 m: 5%, preferably 6% and/or 8%, and/or fraction <2 m: 7.5%, preferably 8%, preferably 10% and/or 16%, preferably 15%, preferably 13%, and/or - fraction <10 m: 25%, preferably 27% and/or 40%, preferably 35%, and/or fraction <40 m: 35%, preferably greater than 37% and/or 50%, preferably 47%, preferably less than 43%, and/or fraction of between 2 m and 40 m: 27% and/or 32%, preferably 30%.

(44) Preferably, the particles of the unshaped concrete are distributed in the following way: fraction <0.5 m: 5% fraction <2 m: 7.5%-16% fraction <10 m: 19% fraction <40 m: 34%-50% fraction of between 2 m and 40 m: 26.5%-34%.

(45) More preferably, the particles of the unshaped concrete are distributed in the following way: fraction <0.5 m: 6% fraction <2 m: 8%-15% fraction <10 m: 25%-40% fraction <40 m: 35%-47% fraction of between 2 m and 40 m : 27%-32%.

(46) Preferably still, the particles of the unshaped concrete are distributed in the following way: fraction <0.5 m: 6%-8% fraction <2 m: 10%-13% fraction <10 m: 27%-35% fraction <40 m: 37%-43% fraction of between 2 m and 40 m: 27%-30%.

(47) Without being committed to a theory, the inventors consider that a proportion of particles with a size of between 2 m and 40 m of between 26.5% and 34% facilitates the laying of the fresh concrete under its own weight, said particles promoting the displacement of the particles with respect to one another and preventing segregation. A proportion of particles with a size of between 2 m and 40 m of greater than 34% or less than 26.5% destroys the self-leveling nature of the fresh concrete.

(48) Compaction models, such as the Fuller-Bolomey model or the Andreasen model, may be used to determine the most suitable particle size distribution.

(49) An unshaped concrete according to the invention may be packaged in bags or in drums.

(50) Preferably, the unshaped concrete is ready-for-use, that is to say incorporates all the constituents except water.

(51) Use

(52) In order to manufacture a fresh concrete starting from an unshaped concrete of the invention, the various components are intimately mixed with an amount of water (g) of between 5% and 9%, indeed even of less than 8% or less than 7%, as percentages by weight with respect to the weight of said unshaped concrete. The water content may be adjusted as a function of the concrete.

(53) Advantageously, this fresh concrete may be transported directly into the glass furnace, for example in order to produce the floor underlayer, by flowing by gravity inside a shute. It may also be pumped using a piston pump. It may then be processed by simple vibration-free pouring.

(54) The cured concrete according to the invention is then left to stand at ambient temperature. The rise in temperature of the furnace subsequently brings about sintering of the cured concrete and results in a cured and sintered concrete according to the invention. A sintering temperature of between 1000 and 1500 C. is highly suitable. If the cured concrete is sintered in a furnace, the time for maintaining at a stationary phase may be between 1 and 20 hours, preferably between 5 and 10 hours.

(55) Preferably, the sintering is carried out in situ.

(56) The unshaped concrete of the invention may also be used to manufacture shaped components having varied dimensions and which are in particular intended to be assembled in a glass furnace.

EXAMPLES

(57) The nonlimiting examples which will follow are given for the purpose of illustrating the invention.

(58) The self-leveling nature and the segregation are evaluated by the following test:

(59) 25 kg of fresh concrete are prepared in a mixer, with a mixing time of 15 minutes, and then poured into a preoiled hopper, in the form of a truncated pyramid, positioned to point down, and exhibiting a height of 320 mm, an inlet opening with an upper square cross section of 350 mm350 mm and an outlet opening with a lower square cross section of 130130 mm, initially closed by a trapdoor.

(60) The trapdoor of the hopper is subsequently opened with a sharp movement and the fresh concrete flows under its own weight, through the outlet opening, into the upper end (at 700 mm from the ground) of a preoiled semicircular straight gutter made of PVC, exhibiting a diameter of 170 mm and a length of 1600 mm, the lower end of the gutter being at 380 mm from the ground.

(61) The fresh concrete flows in the gutter and is poured into a mold positioned under the gutter, under the lower end of the gutter. The mold is a wooden mold having dimensions of 300 mm300 mm60 mm, which is oiled and positioned horizontally on the ground.

(62) The fresh concrete is subsequently left to stand until it is cured in the form of a slab.

(63) The thickness of the slab is measured on each of the four side faces of the slab, at both ends and at mid-length of the face.

(64) The self-leveling (SL) nature is acquired if the upper surface of the slab appears to be substantially smooth to the eye and if the difference E between the smallest thickness measured and the greatest thickness measured is less than or equal to 2 mm on each of the four side faces.

(65) After stoving at 110 C. for 24 hours, the slab is sawn in two through its center, thus exposing two sawn faces. Segregation causes the coarsest particles to migrate, moving away from the upper face of the slab. It is considered that there is segregation when the sawn faces reveal a surface laitance layer extending, from the upper face of the slab, over a depth e of 3 mm or more.

(66) The compositions of the particulate mixtures (a)+(b)+(c) are provided in table 1. The particle size distributions of the fused-cast alumina particles used are also shown.

(67) The calcined aluminate used is the HVA FG alumina sold by Almatis.

(68) The silica fume is a silica fume comprising more than 90% of silica by weight, being provided in the form of a powder, the particles of which have a size of between 0.1 and 5 m and a median size of less than 0.6 m, sold by the Socit Europenne des Produits Rfractaires.

(69) The cement used is CA25R cement, sold by Almatis.

(70) The chemical compositions of the fresh concretes tested and also the results of the tests carried out are provided in table 2.

(71) All the examples incorporate 0.2% of surface-active agent (long-chain sodium polyphosphate for the examples Comp 1 to Comp 3 and compound of the family of the modified polycarboxylate ethers for the other examples). The choice of a surfactant for the surfactants generally used by a person skilled in the art will be guided by the results of simple tests, such as those described in the present patent application, according to the performance levels desired (density of the cured concrete obtained, dilatometric properties of the cured concrete obtained). All the examples, except Comp 1, Comp 2 and Comp 3, incorporate 0.1% of a setting accelerator: Silubit BL05, sold by Zchimmer & Schwarz.

(72) In table 2, the remainder to 100% of Al.sub.2O.sub.3+SiO.sub.2+ZrO.sub.2+organic fibers+surface-active agent+setting accelerator is composed of CaO and of impurities.

(73) The addition of water (g) is provided as percentage by weight on the basis of the unshaped concrete.

(74) The distribution of the sizes of particles of less than 500 m, measured using a Horiba laser particle sizer, is also provided in table 2.

(75) TABLE-US-00001 TABLE 1 Particulate mixture (a) + (b) + (c), as percentages by weight Fused-case Fused-case Fused-case alumina alumina alumina 0.5 mm- 10 m- 40 m- Calcined Reactive Silica No. 3.5 mm 200 m 1 mm alumina aluminas fume Cement Comp 1 55 25 0 6 0 8 6 Comp 2 55 25 0 6 0 8 6 Comp 3 55 25 0 6 0 8 6 Comp 4 39 1 26 13 13 3 5 1 39 6 20 14 13 3 5 2 47 15 0 17 13 3 5 3 45 12 0 22 13 3 5 4 45 9 0 22 16 3 5 Comp 5 44 10 0 25 13 3 5 5 47 15 0 17 13 3 5 Comp 6 47 15 0 17 13 3 5

(76) TABLE-US-00002 TABLE 2 Composition of the fresh concrete Content as % by weight (on the basis of the unshaped concrete) Addition Organic Water % of particles of (a) + (b) + (c) No. Al.sub.2O.sub.3 SiO.sub.2 ZrO.sub.2 fibers (%) <0.5 m <2 m <10 m <40 m <500 m Comp 1 90.8 7 0.2 0 4.5 3.9 8.4 15.6 22.2 45.7 Comp 2 90.8 7 0.2 0 6.1 3.9 8.4 15.6 22.2 45.7 Comp 3 90.8 7 0.2 0 6.1 3.9 8.4 15.6 22.2 45.7 Comp 4 95.9 2.5 0.1 0 5.5 6.4 11 27.9 36.3 57.2 1 95.8 2.5 0.1 0 5.6 6.4 11.1 28.7 37.6 58.1 2 96 2.5 0.1 0 5.9 7 11.3 31.2 39.5 53.8 3 96 2.5 0.1 0 5.7 6.4 11.4 35.1 43.6 55.6 4 96 2.5 0.1 0 6 7.2 12.7 37.8 46.2 55.6 Comp 5 96 2.5 0.1 0 6.4 6.4 11.5 37.5 46.3 56.5 5 96 2.5 0.1 0.03 6.1 7 11.3 31.2 39.5 53.8 Comp 6 96 2.5 0.1 0.04 6.3 7 11.3 31.2 39.5 53.8 % of particles Results of the tests Between Between E e No. 2 and 40 m 40 and 500 m (mm) SL? (mm) Segregation? Comp 1 13.9 23.5 8 No 0 No Comp 2 13.9 23.5 2 Yes 5 Yes Comp 3 13.9 23.5 2 Yes 5 Yes Comp 4 25.3 20.9 4 No 1 No 1 26.5 20.5 2 Yes 0 No 2 28.2 14.3 0 Yes 1 No 3 32.2 12 1 Yes 1 No 4 33.5 9.4 2 Yes 0 No Comp 5 34.8 10.2 4 No 1 No 5 28.2 14.3 1 Yes 1 No Comp 6 28.2 14.3 3 No 0 No

(77) The results allow the following observations to be made:

(78) The examples Comp 1, Comp 2 and Comp 3 do not exhibit a segregation-free self-leveling nature.

(79) A comparison of the examples Comp 1 and Comp 2 shows that an increase in the water content (changed from 4.5% to 6.1%) is not sufficient to give a segregation-free self-leveling nature to the fresh concrete. The Comp 2 fresh concrete is self leveling but exhibits segregation. The increase in the water content may result in a deterioration in the properties of the cured concrete.

(80) The example Comp 4, which is outside the invention, exhibits a different particle size distribution from that of the example Comp 1, with in particular a percentage of particles with a size of between 2 m and 40 m equal to 25.3%. This example does not exhibit a self-leveling nature.

(81) Example 1, according to the invention, exhibits a similar particle size distribution to that of the example Comp 4 but with a percentage of particles with a size of between 2 m and 40 m equal to 26.5%. Example 1 advantageously exhibits a segregation-free self-leveling nature.

(82) Examples 2, 3 and 4, according to the invention, exhibit compositions similar to those of example 1, with a percentage of particles of between 2 m and 40 m equal to 28.2%, 32.2% and 33.5%, respectively. These examples also advantageously exhibit a segregation-free self-leveling nature.

(83) The example Comp 5, which is outside the invention, exhibits a composition similar to those of examples 1 to 4, with, however a percentage of particles of between 2 m and 40 m equal to 34.8%. This example does not exhibit a self-leveling nature.

(84) Examples 2 and 5 show that a limited content of fibers of up to 0.03% does not damage the self-leveling nature. The example Comp 6, which is outside the invention, shows, however, that a content of fibers of 0.04% suppresses the self-leveling nature.

(85) The unshaped concrete of example 2 is the most preferred.

(86) As is now clearly apparent, the invention provides an unshaped concrete which makes it possible to manufacture a self-leveling fresh concrete, that is to say a fresh concrete which may be laid without a vibration operation, and which does not result in segregation.

(87) Furthermore, this fresh concrete may be pumped with suction pressures of less than or equal to 180 bar.

(88) Finally, other tests have shown that a cured and sintered concrete according to the invention causes only few or no defects when it is in contact with molten glass.

(89) A fresh concrete according to the invention thus makes it possible to manufacture, without a vibration operation, a cured and sintered concrete and in particular a floor, especially for a glass furnace, where the cured and sintered concrete comes into contact with molten glass. Despite the absence of a vibration operation, this cured and sintered concrete exhibits an excellent in-service behavior.

(90) Of course, the present invention is not limited to the embodiments described, which are provided as illustrative and nonlimiting examples.