Abstract

The present invention provides a polyamide (preferably Nylon 66) yarn for weaving or knitting clothes articles which have a cooling effect on the skin of the wearer. The yarn contains an inorganic additive (preferably Titanium dioxide) in an amount of between 0.3 and 3.0 wt % and is characterized by a low crimp modulus and a flat cross section.

Claims

1. A yarn for use in knitting or weaving fabric for a wearer experiencing increased physical effort or being exposed to higher external temperature, the yarn i) consisting of Nylon 66 and titanium dioxide (TiO.sub.2), wherein said Nylon 66 is polymerized from a mixture of monomers with TiO.sub.2, said TiO.sub.2 being present in the yarn in an amount of 0.3 wt % to 1.5 wt %, ii) exhibiting low crimp characterized by a crimp modulus between 2% and 3%, and iii) having an elliptic cross-section characterized by a ratio between a minor axis and a major axis of between 3:7 and 6:7, wherein the combination of the crimp with the ratio and with the chemical composition affects heat conductivity and the structural properties of the fabric knitted or woven from said yarn, resulting in cooling the skin of the wearer, the effects being confirmed and quantized in laboratory tests, and being compared with a comparative fabric sample on an inanimate manikin model.

2. A fabric knitted or woven solely from one type of a yarn according to claim 1.

3. An article comprising a yarn according to claim 1, selected from underwear, sporting clothes, hosiery, socks, shapers, shirts, working cloth, sports wear, suits, and trousers.

4. A process for manufacturing a fabric for cooling the skin of a wearer experiencing increased physical effort or being exposed to higher external temperature, comprising i) providing a yarn according to claim 1; and ii) weaving or knitting a fabric or a textile article.

5. A process according to claim 4, wherein said step of providing the yarn comprises spinning Nylon 66 fibers while using spinning capillaries in the shape of the letter I.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The above and other characteristics and advantages of the invention will be more readily apparent through the following examples, and with reference to the appended drawings, wherein:

(2) FIG. 1 is a photo of a manikin used for testing a fabric sample according to one embodiment of the invention, the sample being put as a sleeve on the mode's hand;

(3) FIG. 2 is a graph showing a temperature course on the surface of a manikin wearing a fabric sample according to one embodiment of the invention (lower curve), compared with a temperature course on the surface of the manikin wearing a comparative fabric sample (upper curve), both samples were of Nilit white Nylon type;

(4) FIG. 3 is a graph showing temperature courses similar as in FIG. 2, in a repeated test, again using samples of Nilit white Nylon type, one sample according to the invention and another one comparative; and

(5) FIG. 4 shows the shape of the spinning capillary in one embodiment of the method according to the invention; the special cross-section of the capillary, in the shape of the letter I, in contrast to the usual round shape capillary, provides the desired yarn filaments cross section.

DETAILED DESCRIPTION OF THE INVENTION

(6) It has now been found that a Nylon fiber containing an inorganic additive and being structured to have a low crimp and a flat cross-section confers surprisingly efficient ventilation abilities to textile articles to be worn by a person exposed to heat challenge, such as experiencing increased physical effort or being exposed to higher external temperature. The superior cooling properties of apparel knitted of the yarn was confirmed on manikin model.

(7) The invention relates to a special yarn, to fabric comprising then yarn, and to apparel articles comprising said fabric, enabling superior surface cooling on the skin of the wearer, whereas the wear articles are comfortable to touch and feel cool. The cooling effects of the materials according to the invention are confirmed in objective laboratory tests. The yarn is made of polyamide, has a flat or oval cross-section, and has a very low texture degree. The yarn preferably contains Nylon 66 and titanium dioxide dispersed in the Nylon.

(8) The feature of a special texture comprising low crimp combined with the flat cross-section, in a yarn made of Nylon 66 containing an admixture of inorganic additive, provides cooling properties quantized in objective tests. For example, when measured on manikin model, a knitted sample employing 78/68/1 Nylon 66 provided a surface temperature reduction of about 0.5 C.

(9) The crimp modulus is preferably from 1 to 4, whereas usual values are from 6 to 14. The crimp and bulkiness of the yarn according to the invention is lower then in normally textured nylon. A special fiber having a flat cross-section is provided in a special texturing procedure, while employing special settings which does not distort the filament shape and its cross-section is maintained. The instant texturing procedure makes a yarn having a disk configuration of 1-2-1, compared with standard 1-7-1 configuration. A special setting provides for low crimp of the yarn, and for low bulkiness of the textured yarn, and in addition it does not distort too much the original flat cross section of the filaments as it would happen in normal texturing. With normal texturing the effect of the special cross section would diminish. The combination of low crimp and flat cross-section was found to achieve surprising cooling effects during laboratory tests, for a nylon yarn containing an inorganic additive, such as nylon 66 with TiO.sub.2.

(10) A low crimp of the nylon fibers was achieved by special texturing conditions. The low crimp is achieved by texturing setting; mainly using the 1-2-1 disk configuration. The special capillary gives the shape of the cross section during spinning. The capillary with I-shape design is employed. Usually, dtex is in the range of 17-78 and the number of filaments in the yarn is 3-68, such as in 78/68/1 yarn. Of course, modifications are employed, for example using 1 ply or 2 ply yarns, and other changes. The elastic properties measurements of the textured yarns was performed in an equipment called Texturmat (TEXTECHNO, Germany), and the crimp modulus was measured as % shrinkage of the textured yarn; the crimp modulus is usually more then 7% in normal yarns, often up to 20% and more.

(11) The yarn according to the invention has a flat cross-section, for example an oval cross-section. The flatness is characterized as aspect ratio throughout the present text. Aspect ratio is the ratio between the minimal linear dimension of the cross-section and its maximal linear dimension; for example, the aspect ratio of an elliptic cross-section would be the ratio between the minor axis and the major axis of the ellipse. The aspect ratio of a yarn according to the invention is usually between 3:7 and 6:7.

(12) The invention aims at providing a special yarn for knitting or weaving a nylon fabric which feels pleasant and cool on the skin of a wearer using a wear article made of said fabric. The invention, thus, relates to a manufacturing process comprising steps of i) providing Nylon, preferably Nylon 66 containing an inorganic additive selected from oxides, silicates, sulfates, or mixtures thereof, in an amount between 0.5 and 5.0 wt %, ii) melt spinning said Nylon while employing a spinneret capillaries with a cross-section shaped as the letter I, iii) knitting or weaving a fabric to be used in making apparel, for example pantyhose, socks, underwear, sport knitted fabrics, working clothes, special sport garments. Said step i) may comprise mixing monomer and TiO.sub.2 in an amount of 0.3-1.5% and polymerizing, said step ii) includes spinning the polymer to fiber which is flat in cross-section and low-crimped or not crimped at all, and said step iii) may provide apparels such as hosiery, sportsware, and underwear. The texturing setting is specially adapted to get the required touch and smoothness; for example, trial samples of titer 78/68/1 with different polymers and texturing setting were produced during the development stages and compared to the standard yarns with the same titer; Nylon 66 was preferred; the cooling effect of the yarn/fabric was confirmed by laboratory tests on inanimate model. Said step i) preferably comprises incorporating inorganic additives into the polymer, preferably comprising oxides, and possibly other materials selected from carbonates, silicates, sulfates, wherein the particle size of the inorganic additive may be from 0.1 m to 2 m. The fiber shape combined with its chemical composition results in refreshing feeling in human when checked in an actual sensory test, confirmed by laboratory tests on inanimate models. The total effect of the wear article according to the invention results from the structural properties of the fabric, including physical properties of the fiber affecting its heat conductivity and its sensory effects on the skin.

(13) The articles to be made of the yarn according to the invention include, in one embodiment, underwear such as knitted leg-wear and body-wear garment, and sports wear. The invention provides articles, knitted or woven from a flat or low crimp Nylon 66 fiber, which provide excellent feeling on skin touch. The garment according to the invention induces sensation of cool feeling in a wearer using it, and also helps in mitigating heat stress which can occur when the cooling mechanisms of the body cannot by themselves dissipate excessive heat. The yarn and cooling garment according to the invention, thus, help to maintain body temperature within safe levels during physical effort or during exposure to a high external temperature. The articles of the invention will, therefore, be specially useful in sport events or in hot environment. Of course, the articles of the invention may be used in a broad range of situations.

(14) The invention will be further described and illustrated in the following examples.

EXAMPLES

Example 1

(15) Full dull polymer was spun using melt spinning pilot machine to 100 dtex 68 filaments POY yarn. Polymer properties and spinning conditions are in Tables 1 and 2 below. The pilot machine consisted mainly of extruder 4E10/24D made by BARMAG, screw diameter 40 mm. Spinning beam had 4 packs to adapt 90 mm diameter spinneret and BARMAG ACW 1200/6 winder.

(16) The spinneret used had 34 special capillaries, and filaments from 2 spinnerets were plied together in order to get the 68 filament yarn. The yarn of the above example was textured on false twist texturing machine under conditions described in table 3. Special capillary in the shape of letter I was used (FIG. 4), instead of usual round shape.

(17) TABLE-US-00001 TABLE 1 Polymer properties: Ascend FD Relative viscosity RV 41.5 Amine end groups Meq/Kg 57 TiO2 content % 1.6 Humidity Ppm 1250

(18) TABLE-US-00002 TABLE 2 Spinning conditions and POY properties 100/68 Cooling regular FD spec yarn 100/68 (production machine) Melt temperature C. 280 277 Extruder outlet pressure Bar 100 120 Spinneret initial pressure Bar 230 250 Winding speed m/min 4500 4500 Titer Dtex 98.3 94.6-99 Elongation % 68 65-73 Tenacity cN/dtex 2.93 3

(19) TABLE-US-00003 TABLE 3 Texturing conditions 78/68/1 cooling yarn 78/68/1 regular spec Winding speed m/min 567 567 Draw ratio 1.162 1.24 D/Y ratio 2.27 2.22 Disk configuration 1-2-1 1-7-1 Heater temperature C. 190 205 Titer dtex 86.6 79.8-82.2 Tenacity cN/dtex 2.43 3 Elongation % 28.3 18-26 Crimp Contraction % 6.2 23-31 Crimp Modulus % 2.6 6-14 Crimp Stability % 55.9 76

Example 2

(20) The fabric obtained from yarns described in Example 1 was checked on an inanimate model and compared with a reference fabric of Nilit (FIG. 1). The surface temperature of a thermal sweating manikin during simulated exercise and rest phases was measured. Two fabric samples in the shape of sleeves were tightly fitted to the arms of manikin Newton. The sample according to the invention was compared with a reference sample as specified below:

(21) Sample Id. PI1K094 Nilit ref. 78/68/1 NILIT REF blue

(22) Sample Id. PI1K096 Nilit ref. 78/68/1 NILIT BREEZE blue

(23) Sample Id. PI1K093 Nilit ref. 78/68/1 NILIT REF white

(24) Sample Id. PI1K095 Nilit ref. 78/68/1 NILIT BREEZE white

(25) Two samples (blue and white fabrics) were compared with reference samples, in two series of experiments, the first series A and the second B. The test conditions were: air temperature of 20 C., relative humidity of 50%, and air velocity of 0.4 m/s. The duration of the test was 3 hours. Table 4 shows test phases and conditions. The first phase is an acclimatization phase at constant temperature and with no sweating. The second phase simulates exercise with high metabolism and sweating. The third phase simulates rest (post exercise) with low metabolism and no sweating. During the test, the surface temperature of the manikin right and left arms was recorded. FIG. 2 shows the temperature courses for test A and FIG. 3 test B, both for white samples (two repetitions). The courses for blue fabrics were similar (not shown).

(26) TABLE-US-00004 TABLE 4 Manikin test Time Temperature Heat flux Sweat rate [min] Phase [ C.] [W/m.sup.2] [ml/h/m.sup.2] 0 .fwdarw. 60 Acclimatization 35 0 60 .fwdarw. 120 Exercise 250 200 120 .fwdarw. 180 Rest 50 0

(27) The heat fluxes measured during phase 1 of test A (acclimatization) were as seen in Table 5.

(28) TABLE-US-00005 TABLE 5 Heat fluxes in W/m.sup.2 Test Reference Invention A 150.1 152. B 150.1 151.0 Average 150.1 151.5

(29) A higher cooling effect can be seen in the fabric according to the invention during phases 2 (exercise) and 3 (rest), when compared to the reference fabric. In test A, the blue product according to the invention provides a surface temperature which was lower by 0.63 C. than the reference product; in test B, the difference was 0.66 C. The temperature reductions in the A and B tests with white fabric were similarly 0.46 C. and 0.6 C.

(30) While this invention has been described in terms of some specific examples, many modifications and variations are possible.