Methods of applying active components

Abstract

Method for applying an active component comprising providing a composition comprising: (a) at least one active component selected from a lubricating agent, an insecticidal agent, and an herbicidal agent; and (b) a carrier in an amount effective to solvate or emulsify said active component, said carrier comprising a monochlorotrifluoropropene; and removing the carrier from the composition.

Claims

1. A method of providing a coating in the form of a paint comprising: (a) providing at least a first surface to be coated; (b) delivering a coating composition to said at least first surfaces, said coating composition comprising: (ii) an active paint-forming component; and (b) a carrier solvating and/or emulsifying said active paint-forming component, said carrier comprising a monochlorotrifluoropropene; and (c) forming a layer of paint on said at least first surface by step(s) comprising evaporating said carrier.

2. The method of claim 1 wherein said monochlorotrifluoropropene comprises 1-chloro-3,3,3-trifluoropropene (HCFO-1233zd).

3. The method of claim 2 wherein said 1-chloro-3,3,3-trifluoropropene comprises trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

4. The method of claim 3 wherein said 1-chloro-3,3,3-trifluoropropene consists essentially of trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

5. The method of claim 4 wherein said carrier further comprises a co-carrier in addition to said 1-chloro-3,3,3-trifluoropropene.

6. The method of claim 2 wherein said 1-chloro-3,3,3-trifluoropropene comprises cis-1-chloro-3,3,3-trifluoropropene (cis-HCFO-1233zd).

7. The method of claim 1 wherein said delivering step comprises spraying said coating composition.

8. The method of claim 7 wherein said 1-chloro-3,3,3-trifluoropropene comprises trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

9. The method of claim 7 wherein said 1-chloro-3,3,3-trifluoropropene consists essentially of trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

10. The method of claim 7 wherein said 1-chloro-3,3,3-trifluoropropene consists of trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

11. The method of claim 10 wherein said carrier consists essentially of said cis trans-HCFO-1233zd.

12. A method for applying an active component to a surface comprising: providing a composition comprising at least one active component selected from the group consisting of a coating agent, a lubricating agent, an insecticidal agent, and an herbicidal agent; and a carrier in an amount effective to solvate and/or emulsify said active component, said carrier comprising 1-chloro-3,3,3-trifluoropropene; applying the composition to the surface of a substrate; and removing the carrier from the active component.

13. The method of claim 12 wherein the 1-chloro-3,3,3-trifluoropropene comprises trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

14. The method of claim 12 wherein the carrier is removed by evaporation.

15. The method of claim 12 wherein the composition is applied to the substrate by a spray-on application.

16. The method of claim 12 wherein said 1-chloro-3,3,3-trifluoropropene comprises trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

17. The method of claim 12 wherein said 1-chloro-3,3,3-trifluoropropene consists essentially of trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

18. The method of claim 12 wherein said 1-chloro-3,3,3-trifluoropropene consists of trans-1-chloro-3,3,3-trifluoropropene (trans-HCFO-1233zd).

Description

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

(1) Although it is contemplated that the carrier of the present invention will comprise a major proportion of the composition, and in preferred embodiments the carrier will comprise from about 5% to about 95% of the composition, in further embodiments it comprises at least about 50% by weight, and even further embodiments at least about 80% by weight of a monochlorotrifluoropropene. It will be appreciated that other material may be included in the carrier in order to supplement or enhance the overall performance of the composition, method or system. The inclusion of any and all of such supplemental and additional materials in the carrier is within the broad scope of the present invention.

(2) Examples of additional or supplemental materials that may be used in combination with the monchlorotrifluoropropene carrier component of the present invention include other hydrocarbons, other fluorocarbons, including other fluorochlorocarbons, fluoroethers, fluoroketones, alcohols, ketyones and/or formates. As mentioned above, these additional or supplemental components may be added, for example, to decrease the overall environmental impact and/or improve the performance of the composition, method or system.

(3) In certain applications and embodiments, the carrier contributes to one or more of the following properties of the composition, method or system: flexibility of the material after removal of the carrier and curing or further processing of the active component; quality finish of the material after removal of the carrier and curing or further processing of the active component, quick dry times, and easy and/or effectiveness of application of the composition.

(4) Coating Compositions, Methods and Systems

(5) As mentioned above, the preferred coating compositions of the present invention comprise a coating agent and a carrier comprising a monochloro,trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The coating methods of the present invention comprise providing a coating composition according to the present invention and applying the coating composition to the substrate, body and/or surface to be coated. In certain embodiments, the methods comprise a further step which will aid, enhance or achieve removal of at least a substantial portion of the carrier from the substrate, body and/or surface so as to allow or enhance development of the desired coating by the coating agent. Although such further step may take many forms according to the present methods, in many applications such step simply comprises allowing the coating composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably substantially all of, the monotrifluoropropene. It will be appreciated that in some embodiments evaporation will be enhanced by heating of the coating composition once it is applied, which heating step may also provide additional benefits, for example by helping to accelerate development/curing of the coating and/or develop desirable properties in the coating once formed.

(6) The coating agent can be a wide variety of materials and combinations according to the broad scope of the present invention. One embodiment of the coating aspects of the present invention comprises paints, painting methods and painting systems, or coating on one or more of a wide array of articles or devices. In the particular embodiment of paints, the active component can also take many forms and can comprise many materials. In certain preferred embodiments, the active component comprises an active resin that forms the paint coating when the carrier is at least partially removed and/or when the resin is cured. Although all known resins for this purpose can be used in accordance with the present invention, in certain embodiments the paint resin comprises a component such as oils, natural and/or synthetic polymers based on materials such as alkyds, acrylics, vinyl-acrylics, vinyl acetate/ethylene (VAE), polyurethanes, polyesters, melamine resins, epoxy, and combinations and mixtures of any two or more of these and/or other resin materials. In addition, the active component may comprise in addition to the resin one or more other materials such as aesthetic additives, pigments, binders and the like as is desired and/or needed to achieve the desired finish and other properties of the coating.

(7) With respect to coating systems, it is contemplated although not generally preferred that the coating methods may require the application of two or more different compositions or material to achieve the desired final finish or coated surface. In such cases the systems of the present invention will comprise the present coating composition together with such additional materials or compositions which are intended to be or which are used together with the present coating compositions to achieve a coating according to the present invention.

(8) As also noted above, for many coating applications, the selection of a particular HCFO-1233zd isomer may be based on its properties, the method of application and/or its solubility or miscibility with the coating agent. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the coating agent. In such applications, the trans-isomer may be used with coating agents such as those provided above. In further non-limiting embodiments, the coating agents specifically may include acrylics, urethanes, styrene rubber, hydrocarbon rosin, ester rosin or heparin. In non-spray applications (e.g. dipping, pouring, brushing, immersing, etc.), it is particularly desirable that the carrier/active component combination form an at least partially soluble and/or at least partially emulsifiable mixture and that the selection of the isomer used may be based upon its solubility with the coating agent. In certain non-spray applications, the cis-HCFO-1233zd isomer is preferred because it exhibits better solubility with certain coating agents, particularly coating agents within the general categories provided above, and in further non-limiting and specific embodiments, high impact poly styrene, acrylonitrile-butadiene-styrene and some acrylics. Alternatively, in non-spray applications where the trans-HCFO-1233zd isomer may be preferred or otherwise used, it may be provided alone, or in certain embodiments, in conjunction with one or more co-carriers, particularly one or more co-carriers that improve solubility or miscibility of trans-1233zd with the coating agent. Examples of co-carriers in a coating application may include, but are not limited to, other hydrocarbons, other fluorocarbons, including other fluorochlorocarbons, fluoroethers, fluoroketones, alcohols, ketyones, formats, lower alcohols (such as methanol, ethanol, and the like), maphtha, terpene-based solvents, (such as d-limonene), other high evaporation rate organic materials (such as isoprene, hexane, heptane, styrene liquid, xylene, toluene, methylcyclohexane, cyclohexane. 2,2-dichloropropane, methylene chloride, diisobutyl ketone, diisopropylketone, methyl isobutyl ketone, methyl isopropyl ketone, methyl cyclohexanone, cyclohexanone, isobutyl acetate, isopropyl acetate, butyl acetate, propyl acetate, ethyl acetate, diethyl ether, dimethyl ether, diethylene glycol, 2-ethythexanol) and mixtures of any of these with or without further materials used as co-carriers.

(9) Applicants note that in the foregoing embodiments where one particular isomer may be preferred does not necessarily preclude the inclusion of the other or both isomers. Rather, it simply identifies qualities of one isomer that may be preferred for that application. Either isomer can be the provided in such applications alone, or otherwise in an isomeric mixture.

(10) Adhesive Compositions, Bonding Methods and Adhesive Systems

(11) As mentioned above, the preferred adhesive compositions of the present invention comprise a bonding agent and a carrier comprising a monochloro,trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The bonding methods of the present invention comprise providing a bonding composition according to the present invention and applying the bonding composition to at least one of the body(s) and/or surface(s) to be bonded. In most embodiments, the methods comprise bringing the bodies or surfaces together such that the bonding agent is able to effect a bond between the bodies/surfaces being adhered to one another. In some embodiments, the carrier or portion thereof is removed, preferably by evaporation, prior to the bodies/surfaces being brought together, while in other embodiments, the carrier or portion thereof is removed after the bodies/surfaces have been brought together. Of course embodiments may be used in which a portion of the carrier is removed before, during and after the bodies/surfaces are brought together.

(12) Although it is not considered necessary for many embodiments, in certain embodiments it may be desirable to use a co-carrier in the adhesive aspects of the present invention. Such co-carrier may include, in addition to those mentioned above, lower alcohols (such as methanol, ethanol, and the like), terpene-based solvents, (such as d-limonene), other high evaporation rate organic materials (such as isoprene, hexane, heptane, styrene liquid, xylene, toluene, methylcyclohexane, cyclohexane. 2,2-dichloropropane, methylene chloride, diisobutyl ketone, diisopropylketone, methyl isobutyl ketone, methyl isopropyl ketone, methyl cyclohexanone, cyclohexanone, isobutyl acetate, isopropyl acetate, butyl acetate, propyl acetate, ethyl acetate, diethyl ether, dimethyl ether, diethylene glycol, 2-ethythexanol) and mixtures of any of these with or without further materials used as co-carriers.

(13) With respect to the method steps, the compositions of the present invention can be applied using a variety of techniques and steps, including but not limited to spraying, dipping, pouring, brushing, and combinations of these and other steps and techniques.

(14) Other optional steps may be used to aid, enhance or achieve removal of at least a portion of the carrier from the composition and/or from the substrate, body and/or surface so as to allow or enhance development of the desired bond. Although such further steps may take many forms according to the present methods, in many applications such optional step comprises allowing the adhesive composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably of substantially all of, the monotrifluoropropene. It will be appreciated that in some embodiments evaporation will be enhanced by heating of the adhesive composition once it is applied, which heating step may also provide additional benefits, for example by helping to accelerate development/curing/reaction of the components of the bonding agent and/or develop desirable properties in the adhesive once the bond is formed.

(15) The bonding agent can be a wide variety of materials and combinations according to the broad scope of the present invention. By way of non-limiting example, the active adhesive may be an acrylic adhesive, and epoxy adhesive, a styrenic adhesive, and combinations of these.

(16) With respect to adhesive systems, it is contemplated although not necessarily preferred that the adhesive methods may require the application of two or more different compositions or materials to achieve the desired final bond. In such cases the systems of the present invention will comprise the present adhesive composition together with such additional materials or compositions which are intended to be or which are used together with the present adhesive compositions to achieve a bond according to the present invention.

(17) As also noted above, for many adhesive applications, the selection of a particular HCFO-1233zd isomer may be based on its properties, the method of its application, and/or its solubility/miscibility with the bonding agent. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the bonding agent. In such applications, the trans-isomer may be used with bonding agents, such as those within the general categories provided above. In certain aspect, the bonding agent specifically includes, but is not limited to, urethanes or styrene rubber. In non-spray applications, it is particularly desirable that the carrier/active component combination form an at least partially soluble and/or at least partially emulsifiable mixture and that the selection of the isomer used may be based upon its solubility with the bonding agent. In certain non-spray applications, the cis-HCFO-1233zd isomer may be preferred because it exhibits better solubility with the bonding agents, such as those within the general categories provided above, but particularly bonding agents that include, but are not limited to, acrylics, SBS or other styrenes, or the like. Alternatively, in alternative non-spray applications where the trans-HCFO-1233zd isomer may be preferred or otherwise used, it may be provided alone, or in certain embodiments, in conjunction with one or more of the co-carriers identified above, particularly a co-carrier that facilitates or otherwise improves solubility or emulsification of trans-1233zd with the bonding agent.

(18) Applicants note that in the foregoing embodiments where one particular isomer may be preferred does not necessarily preclude the inclusion of both isomers. Rather, it simply identifies qualities of one isomer that are preferred for that application. Either isomer can be the provided in such applications alone, or otherwise in an isomeric mixture.

(19) Sealant Compositions, Sealing Methods and Sealant Systems

(20) As mentioned above, the preferred sealant compositions of the present invention comprise a sealing agent and a carrier comprising a monochloro,trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The sealing methods of the present invention preferably comprise providing a sealant composition according to the present invention and applying the sealant composition to at least one of the body(s) and/or surface(s) to be sealed. In many embodiments, the sealant is used to create a seal, and in certain embodiments a water seal, between two surfaces or bodies. In such embodiments, the methods preferably comprise bringing the bodies or surfaces together after the sealant has been applied to one or both bodies/surfaces such that the gap or space between them is relatively resistant to the flow of one or more fluids. In other embodiments, a gap exists or is created between the bodies/surfaces and the sealant is applied to the surfaces/bodies substantially simultaneously to fill and seal at least a portion of the gap. Additional embodiments include sound and air abatement and, the like. In either of such embodiments, pressure may be applied to the bodies and/or the sealant composition to improve the seal. In other embodiments, the sealant composition may be used to create in a relatively porous material, such as a fabric or the like, an increased resistance to the passage of one or more fluids, such as water, through the portion of the material which has been treated with the sealant of the present invention. In some embodiments, the carrier or portion thereof is removed, preferably by evaporation, prior to the bodies/surfaces being brought together, while in other embodiments, the carrier or portion thereof is removed after the bodies/surfaces have been brought together. Of course embodiments may be used in which a portion of the carrier is removed before, during and after the bodies/surfaces are brought together.

(21) Other optional steps may be used to aid, enhance or achieve removal of at least a portion of the carrier from the composition and/or from the body and/or surface being treated so as to allow or enhance development of the desired seal. Although such further steps may take many forms according to the present methods, in many applications such optional step comprises allowing the sealant composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably of substantially all of, the monotrifluoropropene. It will be appreciated that in some embodiments evaporation will be enhanced by heating of the sealant composition once it is applied, which heating step may also provide additional benefits, for example by helping to accelerate development/curing/reaction of the components of the sealing agent and/or develop desirable properties in the sealant once the sealant is applied.

(22) The sealing agent can be a wide variety of materials and combinations according to the broad scope of the present invention. By way of non-limiting example, the active sealing component may comprise one or more of silicone sealants, poly(alpha-monoalkenyl arene)/poly(conjugated diene) block copolymer or hydrogenated or partially hydrogenated derivatives thereof, and combinations of these with or without other active sealing agents.

(23) With respect to adhesive systems, it is contemplated although not necessarily preferred that the sealant methods may require the application of two or more different compositions or materials to achieve the desired final bond. In such cases the systems of the present invention will comprise the present sealant composition together with such additional materials or compositions which are intended to be or which are used together with the present sealant compositions to achieve a seal according to the present invention.

(24) As also noted above, for many sealant applications, the selection of a particular HCFO-1233zd isomer may be based on its properties, the method of application, and/or its solubility/miscibility with sealing agents. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the sealing agent. In such applications, the trans-isomer may be used with sealing agents such as, but not limited to, those within the general categories provided above, but the cis-isomer may also be provided, as necessary, to assist with solubility of the sealing agent. In non-spray applications, it is particularly desirable that the carrier/active component combination form an at least partially soluble and/or at least partially emulsifiable mixture and that the selection of the isomer used may be based upon its solubility with the sealing agent. In certain non-spray applications, the cis-HCFO-1233zd isomer may be preferred because it exhibits better solubility with the sealing agents, such as, but not limited to, those within the general categories provided above. In alternative non-spray applications where the trans-HCFO-1233zd isomer may be preferred or otherwise used, it may be provided alone, or in certain embodiments, in conjunction with one or more co-carriers, particularly one or more co-carriers that improve solubility or emulsification of trans-1233zd with the sealing agent. Examples of co-carriers in a sealing application may include, but are not limited to, other hydrocarbons, other fluorocarbons, including other fluorochlorocarbons, fluoroethers, fluoroketones, alcohols, ketyones, formats, lower alcohols (such as methanol, ethanol, and the like), naphtha, terpene-based solvents, (such as d-limonene), other high evaporation rate organic materials (such as isoprene, hexane, heptane, styrene liquid, xylene, toluene, methylcyclohexane, cyclohexane. 2,2-dichloropropane, methylene chloride, diisobutyl ketone, diisopropylketone, methyl isobutyl ketone, methyl isopropyl ketone, methyl cyclohexanone, cyclohexanone, isobutyl acetate, isopropyl acetate, butyl acetate, propyl acetate, ethyl acetate, diethyl ether, dimethyl ether, diethylene glycol, 2-ethythexanol) and mixtures of any of these with or without further materials used as co-carriers.

(25) Applicants note that in the foregoing embodiments where one particular isomer may be preferred does not necessarily preclude the inclusion of both isomers. Rather, it simply identifies qualities of one isomer that are preferred for that application. Either isomer can be provided in such applications alone, or otherwise in a mixture of isomers.

(26) Lubricant Compositions, Lubricating Methods and Lubricant Systems

(27) As mentioned above, the preferred lubricant compositions of the present invention comprise a lubricating agent and a carrier comprising a monochloro,trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The lubricating methods of the present invention preferably comprise providing a lubricating composition according to the present invention and applying the lubricating composition to at least one of the body(s) and/or surface(s) to be lubricated. In many embodiments, the lubricant is used to create an area, region or surface of a body or material that exhibits a reduced level of friction when it comes in friction producing contact with another body. The selection of a particular HCFO-1233zd isomer may be based on its properties, the method of application, and/or its solubility/miscibility with lubricating agents. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the lubricant. In non-spraying applications, cis- or trans-isomer may be used based, at least in part, on its solubility or miscibility with the lubricating agent. Applicants note, however, that the preference for one isomer does not necessarily preclude the inclusion of both isomers. Rather, it simply identifies qualities of one isomer that may be preferred for that application. Either isomer can be the provided in such applications alone, or otherwise in a mixture of isomers.

(28) Various steps may be used to aid, enhance or achieve removal of at least a portion of the carrier from the composition and/or from the body and/or surface being treated so as to allow or enhance development of the desired lubricant. Although such further steps may take many forms according to the present methods, in many applications such optional step comprises allowing the lubricant composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably of substantially all of, the monotrifluoropropene. It will be appreciated that in some embodiments evaporation will be enhanced by heating of the lubricant composition once it is applied, which heating step may also provide additional benefits, for example by helping to accelerate development/curing/reaction of the components of the lubricanting agent and/or develop desirable properties in the lubricant once it is applied.

(29) The lubricating agent can be a wide variety of materials and combinations according to the broad scope of the present invention. Commonly used active lubricating agents include but are not limited to Polyol Esters (POEs) and Poly Alkylene Glycols (PAGs), PAG oils, silicone oil, mineral oil, alkyl benzenes (ABs) and poly(alpha-olefin) (PAO). Commercially available mineral oils include Witco LP 250 (registered trademark) from Witco, Zerol 300 (registered trademark) from Shrieve Chemical, Sunisco 3GS from Witco, and Calumet R015 from Calumet. Commercially available alkyl benzene lubricants include Zerol 150 (registered trademark). Commercially available esters include neopentyl glycol dipelargonate, which is available as Emery 2917 (registered trademark) and Hatcol 2370 (registered trademark). Other useful esters include phosphate esters, dibasic acid esters, and fluoroesters. Of course, different mixtures of different types of lubricants may be used.

(30) With respect to lubricant systems, it is contemplated although not necessarily preferred that the lubricating methods may require the application of two or more different compositions or materials to achieve the desired final lubricating effect. In such cases the systems of the present invention will comprise the present lubricant composition together with such additional materials or compositions which are intended to be or which are used together with the present lubricant compositions to achieve a friction reducing effect according to the present invention.

(31) Insecticide Compositions, Insecticidal Methods and Insecticide Systems

(32) As mentioned above, the preferred insecticide compositions of the present invention comprise a insecticidal agent and a carrier comprising a monochloro,trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The selection of a particular HCFO-1233zd isomer may be based on its properties, the method of application, and/or its solubility/miscibility with the insecticide. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the insecticide. In non-spraying applications, cis- or trans-isomer may be used based, at least in part, on its solubility or miscibility with the insecticide. Applicants note, however, that the preference for one isomer does not necessarily preclude the inclusion of both isomers. Rather, it simply identifies qualities of one isomer that may be preferred for that application. Either isomer can be the provided in such applications alone, or otherwise in a mixture of isomers.

(33) The insect reducing methods of the present invention preferably comprise providing an insecticidal composition according to the present invention and applying the insecticidal composition to at least one of the body(s), and/or surface(s), and/or the environment (including the air) to be treated. In many embodiments, the insecticide is used to create an area, region or surface of a body or material, or an area or region of the environment, that exhibits a relatively inhospitable condition to one or more insects and therefore reduces the presence or impact of such one or more insects on or near the region, body or the like.

(34) Various steps may be used to aid, enhance or achieve removal of at least a portion of the carrier from the composition and/or from the body and/or surface and/or region of space being treated so as to allow or enhance development of the desired insecticide. Although such further steps may take many forms according to the present methods, in many applications such optional step comprises allowing the insecticide composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably of substantially all of, the monotrifluoropropene. It will be appreciated that in some embodiments other steps may be required to help or enhance the effectiveness of the active components of the insecticidal agent and/or develop desirable properties in the insecticide once the insecticide is applied.

(35) The insecticidal agent can be a wide variety of materials and combinations according to the broad scope of the present invention. One embodiment of the insecticide aspects of the present invention comprises an improved insect spray, such as a wasp hornet or other flying insect spray. In such embodiments it is contemplated, and in some cases it is preferred that a propellant, preferably an environmentally friendly propellant such as HFO-1234ze, will be used to aid in spraying or expelling the present composition from the canister or can in which it may be stored prior to use. In such cases it is contemplated and preferred that the carrier component of the present invention preferably solvates, and even more preferably substantially completely solvates the active insecticidal components and thereby enhances the ability of the composition to penetrate into the body, surface, area or region to be treated, such as into a hornet or wasp nest, and to then relatively rapidly evaporate to allow the active ingredients to act effectively against the insects and to remain located in areas, regions or surfaces that would otherwise be difficult to treat with the insecticide.

(36) By way of non-limiting example, active insecticides that may be used in accordance with the present invention comprise pyrethrins, piperonyl butoxide, and cabaryl. Optional additional ingredients may also be used, such as petroleum distillates and inert ingredients.

(37) With respect to insecticide systems, it is contemplated although not necessarily preferred that the lubricating methods may require the application of two or more different compositions or materials to achieve the desired final insecticidal effect. In such cases the systems of the present invention will comprise the present insecticide composition together with such additional materials or compositions which are intended to be or which are used together with the present insecticide compositions to achieve the insecticidal effect according to the present invention.

(38) Herbicide Compositions, Insecticidal Methods and Herbicide Systems

(39) As mentioned above, the preferred herbicide compositions of the present invention comprise a herbicidal agent and a carrier comprising a monochloro, trifluoropropene, and preferably HCFO-1233zd, and even more preferably trans-HCFO-1233zd and/or cis-HCFO-1233zd. The selection of a particular HCFO-1233zd isomer may be based on its properties, the method of application, and/or its solubility/miscibility with herbicide. With certain spray applications, for example, the trans-HCFO-1233zd isomer may be preferred because it has a much lower boiling than the cis-isomer, but the cis-isomer may also be provided, as necessary, to assist with solubility of the herbicide. In non-spraying applications, cis- or trans-isomer may be used based, at least in part, on its solubility or miscibility with the herbicide. Applicants note, however, that the preference for one isomer does not necessarily preclude the inclusion of both isomers. Rather, it simply identifies qualities of one isomer that may be preferred for that application. Either isomer can be the provided in such applications alone, or otherwise in a mixture of isomers. The plant growth impacting methods of the present invention preferably comprise providing a herbicidal composition according to the present invention and applying the herbicidal composition to at least one of the body(s), and/or surface(s), and/or the environment (including the air) to be treated. In many embodiments, the herbicide is used to have positive or negative impact on the growth or health of one or more plants and therefore reduces or increases the presence or impact of such one or more plants on or near the region of treatment.

(40) Various steps may be used to aid, enhance or achieve removal of at least a portion of the carrier from the composition and/or from the body and/or surface and/or region of space or ground being treated so as to allow or enhance development of the desired herbicide. Although such further steps may take many forms according to the present methods, in many applications such optional step comprises allowing the herbicide composition once applied to be exposed to the environment, which in many preferred embodiments will result in evaporation of at least a portion, and preferably a major proportion, and even more preferably of substantially all of, the monotrifluoropropene

(41) It will be appreciated that in some embodiments other steps may be required to help or enhance the effectiveness of the active components of the herbicidal agent and/or develop desirable properties in the herbicide once the herbicide is applied.

(42) The herbicidal agent can be a wide variety of materials and combinations according to the broad scope of the present invention. One embodiment of the herbicide aspects of the present invention comprises an improved weed or plant spray. In such embodiments it is contemplated and in some cases preferred that a propellant, preferably an environmentally friendly propellant such as HFO-1234ze, will be used to help spray or expel the present composition form the canister or can in which it may be stored prior to use. In such cases it is contemplated and preferred that the carrier component of the present invention preferably solvates, and even more preferably substantially completely solvates the active herbicidal components and thereby enhances the ability of the composition to penetrate into the body, surface, area or region to be treated, and to then relatively rapidly evaporate to allow the active ingredients to act effectively to either enhance or inhibit growth of the selected plant matter and to remain located in areas, regions or surfaces that would otherwise be difficult to treat with the herbicide.

(43) With respect to herbicide systems, it is contemplated although not necessarily preferred that the herbicidal methods may require the application of two or more different compositions or materials to achieve the desired final herbicidal effect. In such cases the systems of the present invention will comprise the present herbicide composition together with such additional materials or compositions which are intended to be or which are used together with the present herbicide compositions to achieve a growth/health regulating effect according to the present invention.

EXAMPLES

(44) The following examples are provided for the purpose of illustrating the present invention but without limiting the scope thereof.

Example 1Coating/Paint

(45) The following active components comprising a coating agent, particularly a resin for use in paint, were tested in the indicated amounts and achieved the indicated results based on combining the carrier and the resin in 40 cc septum top vials and were shaken at room temperature (the Examples designated with a single letter suffix utilize trans-HFCO-1233zd and Examples designated with a double letter suffix utlize cis-HFCO-1233zd):

(46) TABLE-US-00001 Grams of DOW* Description 1233zd(E)/ Grams of Grams of Example DESIGNATION of Material 1233zd(Z) CoCarrier Resin Results 1A Paraloid B-56 Acrylic 9.89 0 0.47 Complete polymer dissolution 1AA Paraloid B-56 Acrylic 6.30 0 0.43 Complete polymer dissolution 1B Paraloid B-66 Acrylic 9.75 0 0.46 Complete polymer dissolution 1BB Paraloid B-66 Acrylic 6.13 0 0.45 Complete polymer dissolution 1C Paraloid B-67 Acrylic 9.88 0 0.43 Complete polymer dissolution 1CC Paraloid B-67 Acrylic 6.08 0 0.45 Complete polymer dissolution 1D Paraloid AU-608B Acrylic 10.52 0 0.75 milky, emulsion polymer like liquid which phase separated 1DD Paraloid AU-608B Acrylic 4.59 0 0.51 Complete polymer dissolution 1E Paraloid AU-608B Acrylic 10.8 0.2 0.87 Complete polymer (methanol) dissolution, with no phase separation *All resins are manufactured by Dow Chemical Company and are identified herein by reference to the trade name, which may or may not be a registered trademark of Dow Chemical Company.

Example 2Adhesive

(47) The following active component comprising a bonding agent was tested in the indicated amounts and achieved the indicated results based on combining the carrier and the bonding agent in 40 cc septum top vials and were shaken at room temperature (the Examples designated with a single letter suffix utilize trans-HFCO-1233zd and Examples designated with a double letter suffix utlize cis-HFCO-1233zd):

(48) TABLE-US-00002 Grams of 3M* Description 1233zd(E)/ Grams of Grams of Example DESIGNATION of Material 1233zd(Z) CoCarrier Resin Results 2A Super 77 Aerosol 13.04 0 2.8 A milky, emulsion adhesive like material was formed. This material phase separated 2AA Super 77 Aerosol 7.72 0 0.42 A milky, emulsion adhesive like material was formed. This material phase separated 2B Super 77 Aerosol 11.57 0.23 0.46 A milky, emulsion adhesive like material was formed. This material phase separated 2BB Super 77 Aerosol 7.48 0.15 0.35 A milky, emulsion adhesive like material was formed. This material phase separated *The bonding agent is manufactured by 3M and is a aerosol adhesive identified herein by reference to the trade name, which may or may not be a registered trademark of 3M.

(49) After the observed emulsion-like material designated as 2A in the table above was formed, the liquid was poured onto a metal surface, and substantially all of the carrier evaporated upon standing. The surface with the adhesive thereon became tacky, indicating the formation of a material ready to achieve bonding.

Example 3Sealant

(50) The following active component comprising a sealing agent was tested in the indicated amounts and achieved the indicated results based on combining the carrier and the sealing agent in 40 cc septum top vials and were shaken at room temperature (the Examples designated with a single letter suffix utilize trans-HFCO-1233zd and Examples designated with a double letter suffix utlize cis-HFCO-1233zd):

(51) TABLE-US-00003 Grams of DAP* Description 1233zd(E)/ Grams of Grams of Example DESIGNATION of Material 1233zd(Z) CoCarrier Resin Results 3A Dap Silicone Silicone Caulk 14.09 0 0.77 A milky, emulsion Caulk (clear) (clear) like material was formed. This material phase separated 3AA Dap Silicone Silicone Caulk 12.15 0 0.82 A milky, emulsion Caulk (clear) (clear) like material was formed. This material phase separated 3B Super 77 Aerosol 5.49 0.11 5.34 A single phase id adhesive formed (complete dissolution) with no phase separation *The sealing agent is manufactured by DAP and is a silicon caulk identified herein by reference to the trade designation Dap Silicone Caulk (clear), which may or may not be a registered trademark of DAP.

Example 4Lubricant

(52) A carrier consisting of 1234ze(E) according to the present invention is combined with mineral oil in a relative amount which is effect to allow the carrier to carry and substantially dissolve or emulsify, or a combination thereof, the mineral oil. The mineral oil is present in an amount effective to provide lubrication upon application to a surface. In particular, the following active component comprising a lubricant in the form of mineral oil is tested in the indicated amounts and achieved the indicated results based on combining the carrier and the lubricant in 40 cc septum top vials and were shaken at room temperature (the Examples designated with a single letter suffix utilize trans-HFCO-1233zd and Examples designated with a double letter suffix utlize cis-HFCO-1233zd):

(53) TABLE-US-00004 Grams of Lubricant Description 1233zd(E)/ Grams of Grams of Example DESIGNATION of Material 1233zd(Z) CoCarrier oil Results 4A WITCO LP 150 Mineral Oil 10 0 10 Complete dissolution 4AA WITCO LP 150 Mineral Oil 10 0 10 Complete dissolution 4B DOW Corning Silicone 10 0 10 Complete 360 Silicone Lubricant dissolution 4BB DOW Corning Silicone 10 0 10 Complete 360 Silicone Lubricant dissolution

Example 5Insecticide

(54) Carriers consisting of 1233zd(E) and 1233zd(Z) according to the present invention is combined with an insecticidal material having typical insecticidal properties in a relative amount according to the teachings contained herein and which is an amount is effect to allow the carrier to carry and substantially dissolve or emulsify, or a combination thereof, the insecticide. The insecticide is present in an amount effective to provide an insecticidal effect upon application using typical application techniques.

Example 6Herbicide

(55) Carriers consisting of 1233zd(E) and 1233zd(Z) according to the present invention is combined with an insecticidal material having typical insecticidal properties in a relative amount according to the teachings contained herein and which is effect to allow the carrier to carry and substantially dissolve or emulsify, or a combination thereof, the herbicide. The herbicide is present in an amount effective to provide an insecticidal effect upon application using typical application techniques.

Example 7Measurement of Kauri-Butanol Number

(56) Measurement of Kauri-Butanol (KB) number was performed in the lab for both tr-1233zd and cis-1233zd using the ASTM method (D1133 Standard Test Method for Kauri-Butanol Value of Hydrocarbon Solvents). Kauri-Butanol number of a solvent is a measure of how well Kauri-gum resin solution is dissolved in a solvent and is used widely in industry to compare solvency of compounds. Kauri-butanol solution was obtained from Fisher Scientific. Both tr-1233zd & cis-1233zd were titrated in to the solution which were kept in a 20 cc vial with septum screw cap. KB number for tr-1233zd was found to be 25 and KB number for cis-1233zd was found to be 34. Unexpectedly the KB value of cis-1233zd increased by >30% over the KB value of the tr-1233zd. CFC-113 which was a widely used solvent in a variety of cleaning applications including but not limited to electronics cleaning, dry cleaning, metal cleaning and deposition had a KB value of 31. Cis-1233zd would be a preferred solvent due to its higher KB value when looking at electronics cleaning, dry cleaning, metal cleaning and deposition.

Example 8Solubility of Acrylic

(57) Test samples of commercial acrylic plastic sheet cut into 2 piece were placed into 20 cc vials with septum screw cap. Solvents (tr-1233zd & cis-1233zd) were slowly added by a syringe to cover the entire plastic sample inside the vial. The purpose was to observe if any degradation happens to the plastic. Acrylic materials were found to dissolve acrylic material readily in both solvents.

Example 9Solubility of High Impact Styrene

(58) Test samples of commercial high impact styrene plastic sheet cut into 2 piece were placed into 20 cc vials with septum screw cap. Solvents (tr-1233zd & cis-1233zd) were slowly added by a syringe to cover the entire plastic sample inside the vial. The purpose was to observe if any degradation happens to the plastic. High impact styrene materials were found to dissolve completely in cis-1233zd solvent whereas it only showed swelling in tr-1233zd solvent. This shows distinct uniqueness in solubility of cis-1233zd over tr-1233zd.

Example 10Solubility of Acrylonitrile-Butadiene-Styrene

(59) Test samples of commercial acrylonitrile-butadiene-styrene (ABS) sheet cut into 2 piece were placed into 20 cc vials with septum screw cap. Solvents (tr-1233zd & cis-1233zd) were slowly added by a syringe to cover the entire plastic sample inside the vial. ABS plastic materials were found to dissolve completely in cis-1233zd solvent whereas it only showed deformations in tr-1233zd solvent. This also demonstrates distinct uniqueness in solubility of cis-1233zd over tr-1233zd.

Example 11Solubility of Polycarbonate

(60) The experiment in Example 8 is repeated with commercial polycarbonate material. Tr-1233zd has some minor effect on polycarbonate in that the polycarbonate was seen to be crazed but cis-1233zd had significant effect in that the polycarbonate had severe crazing and even cracks after exposure to cis-1233zd.

Example 12Solubility of Acrylic

(61) The experiment of Example 8 was repeated with commercial Dow Polaroid Au-608-B acrylic material. This material is used in various coatings. Tr-1233zd cannot dissolve the material without any co-solvent added but cis-1233zd dissolved it completely.

Example 13Solubility of Heparin

(62) The experiment of Example 8 was repeated with blood anti-coagulant material Heparin, which is used as a coating in medical devices. Heparin is effective at preventing deep vein thromboses and pulmonary emboli in patients at risk. None of the solvents could dissolve the material. When 2 wt % methanol is added to each of the material the solution of tr-1233zd and methanol could dissolve 0.794 wt % heparin and cis-1233zd and methanol could dissolve 1.19 wt % heparin and remained clear being left overnight.