Functional polymer binder for sulfur cathode fabrication

Abstract

The present invention provides for a composition of matter, polymeric conductive binder, or electrode comprising: ##STR00001##
Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)]. The present invention also provides for a Lithium-Sulfur (LiS) battery comprising a cathode comprising: a cathode comprising a polymeric conductive binder poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)]; a separator; an anode; and, an electrolyte.

Claims

1. A polymeric conductive binder comprising: ##STR00010## Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)].

2. An electrode comprising: a polymeric conductive binder ##STR00011## Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)].

3. A Lithium-Sulfur (LiS) battery comprising: a cathode comprising a polymeric conductive binder ##STR00012## Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)]; a separator; an anode; and an electrolyte.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The foregoing aspects and others will be readily appreciated by the skilled artisan from the following description of illustrative embodiments when read in conjunction with the accompanying drawings.

(2) FIG. 1A illustrates CS single bond formation between polyvinylsulfate (PVS) and polysulfides evidenced by Raman spectra.

(3) FIG. 1B illustrates polysulfide reservation capability comparison between PVS and PVDF through low rate cycling performance.

(4) FIG. 2A illustrates characterization of chemical bonds between MPS and polysulfide: TFY spectra.

(5) FIG. 2B illustrates characterization of chemical bonds between MPS and polysulfide: FTIR spectra.

(6) FIG. 3A illustrates cycling performance of high-loading sulfur electrodes based on MPS at varying C rates.

(7) FIG. 3B illustrates cycling performance of high-loading sulfur electrodes based on MPS at varying C rates.

(8) FIG. 3C illustrates coulombic efficiency of various C rate.

(9) FIG. 3D illustrates discharge/charge voltage profiles of various C rate.

(10) FIG. 4 illustrates SEM images of sulfur electrodes with different magnification. Fresh sulfur electrode (a, b, c, d); fully discharged electrode (e, f, g, h); Fully charged electrode (i, j, k, l). (Magnification: a, c. e 1200; b, f, J 2000; c, g, k 5000; d, h, l 10000).

(11) FIG. 5 illustrates cycling performance of high-loading sulfur electrodes based on PECH, PVC and PVDF.

(12) FIG. 6A illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] at C/20.

(13) FIG. 6B illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] at C/20.

(14) FIG. 7 illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] specifically the dis-charge/charge voltage profiles of the 20th cycle.

DETAILED DESCRIPTION

(15) In the discussions that follow, various process steps may or may not be described using certain types of manufacturing equipment, along with certain process parameters. It is to be appreciated that other types of equipment can be used, with different process parameters employed, and that some of the steps may be performed in other manufacturing equipment without departing from the scope of this invention. Furthermore, different process parameters or manufacturing equipment could be substituted for those described herein without departing from the scope of the invention.

(16) These and other details and advantages of the present invention will become more fully apparent from the following description taken in conjunction with the accompanying drawings.

(17) Herein, we demonstrate a class of innovative polymer binder materials and strategy to address the challenge of polysulfides dissolution and the shuttle effect. A series of functional polymers with potential to have nucleophile reaction with polysulfides were designed to retain polysulfide in the surface electrode. The number of factors governing reactivity in nucleophilic reaction includes polarizabilities of both nucleophile and leaving group, stability of leaving group and interaction between nucleophile and leaving group. To capture the polysulfides, the choice of leaving group is the key issue. Nucleophile reaction involving good leaving groups has low activation barriers. A good leaving group must be able to stabilize a large negative charge in the transition state and product. A good measure of anion stability is the pKa of an anion's conjugate acid, with lower pKaH's being associated with better leaving group ability. Based on this, sulfate and halide ions, e.g., F, Cl, Br, I, and related polymers were adopted. The other important factor for the nucleophilic reaction is the location of leaving groups. The leaving groups at the primary carbon are preferred rather than at the secondary carbon, and the least preferred is at the tertiary position.

(18) Examples of detailed mechanisms are illustrated in scheme 1.

(19) ##STR00006## ##STR00007##

(20) Based on the above polymers illustrated in scheme 1, we built and tested high areal capacity electrodes which could buffer the polysulfides shuttle effect and help to maintain the mechanical integrity of the sulfur electrode. A simple, cheap, scalable and versatile way was chosen to obtain sulfur electrodes with high binding capability, the property gain in terms of electrochemical performance (high areal capacity with high current density) is demonstrated, which proves our approach that an effective binder is a key factor to improve the loading of sulfur electrodes. This discovery will enable high capacity, low cost and large scale production of LiS cells based on binders. The strategy developed here may also be applied to other rechargeable battery systems.

(21) In various embodiments, we show a polymer strategy with sulfate and halide ions groups that can provide effective binding sites for lithium polysulfides. The strategy of this approach is not only to limit the outbound diffusion of the soluble Li.sub.2S.sub.n molecules, but also to capture the soluble species in the electrolyte to alleviate the polysulfides shuttle effect to achieve commercial promising cycle performance.

(22) To execute this method, micro-sulfur powders were mixed with conductive additives (acetylene black, e.g. super C.sub.65) through various binders to form slurry. The slurry was then coated onto an aluminum foil using doctor blade and dried vacuum to form the working electrode. LiS batteries are tested with 2325-type coin cell (National Research Council Canada) in an argon-filled glove box using lithium foil as the counter electrode. The size of the sulfur electrode and counter-electrode lithium metal disk is and 11/16-in. OD, respectively. The Li foil is purchased from FMC-Lithium Co. The separator is polypropylene film (Celgar 2400). The electrolyte used was a freshly prepared solution of lithium bis(trifluoromethanesulfonyl)imide (1M) in 1:1 v/v 1,2-dimethoxyethane and 1,3-DOL containing LiNO.sub.3 (2 wt %). The assembled cells were placed on the channels (Maccor Inc.; Tulsa, Okla.) at 30 C. for lithiation-delithiation cycles. The voltage window for cell test is 1.8-2.6 V.

(23) The nucleophilic reaction initiates the connection since the reduction of elemental sulfur to high-order soluble polysulfide resulting in shuttle effect alleviation. Raman spectra in FIG. 1A verify the evolution including leave of sulfate groups and formation of CS single bond in the intermediate molecules. The peak corresponds to the v.sub.SO4.sup.2 is centered at 981 cm.sup.1. The appearance of peak at 675 cm.sup.1 confirmed the CS bonding. After mechanism clarification, excellent cyclability with micro-sulfur particles was demonstrated based on PVS at room temperature. The cathode shows high initial discharge capacity of ca. 1500 mAh/g (based on the incorporated sulfur content) with 100% of coulombic efficiency after a few initial cycles. The cathode capacity can hold up to 900 mAh/g after 100 cycles. The capacity retention for PVS based electrode is clearly more advantageous at C/20 than a PVDF based electrode. Since the unique variable between PVS and PVDF is sulfate and fluorine, the effect of sulfate can be confirmed accordingly. This observation confirms that the PVS has extremely strong chemical bonding with diffusing polysulfides to achieve improved cycle performance.

(24) FIG. 1A illustrates CS single bond formation between PVS and polysulfides evidenced by Raman spectra. FIG. 1B illustrates polysulfide reservation capability comparison between PVS and PVDF through low rate cycling performance.

(25) High Areal Capacity Based on -Carrageenan (MPS).

(26) FIGS. 2A and 2B illustrate characterization of chemical bonds between MPS and polysulfide. FIG. 2A illustrates TFY spectra. FIG. 2B illustrates FTIR spectra.

(27) To extend the sulfate function in PVS and a simplified manufacturing process, a sulfated natural polymer -carrageenan (MPS), with high binding strength was evaluated to achieve high sulfur loading. The chemical bonding between MPS and polysulfides was initially verified as PVS. We applied S K-edge absorption spectra (XAS) to monitor the formation of chemical bonds between MPS and S. We simulated sample preparation processes by thermally treating in the DOL/DME electrolyte for 24 hours. The S K-edge XAS data of the mixtures recorded from the total fluorescence yield (TFY) before and after the treatment are presented in FIG. 2A. Before annealing, TFY spectra show peaks located at 2481.17 and 2483.56 are attributed to the RSO.sub.3.sup..sub.O-S* and SO.sub.4.sup.2.sub.C-S*, respectively. The emerging peak at 2473.67 after treatment confirms the existence of CS bond in the bulk material. In order to investing the evolution of the chemical bonding, Fourier Transform Infrared Spectroscopy (FTIR) was performed to demonstrate the leaving of sulfate group and forming of CS bond. The decrease of easter sulfate and galactose sulfate vibration is indicated in FIG. 2B.

(28) FIGS. 3A and 3B illustrate cycling performance of high-loading sulfur electrodes based on MPS at vary C rates. FIG. 3C illustrates Coulombic efficiency and FIG. 3D illustrates discharge/charge voltage profiles of various C rate.

(29) To confirm the expected cycle performance of the high loading sulfur electrodes, the galvanostatic charge/discharge profiles are shown in FIGS. 3A, 3B, 3C, and 3D. With MPS, the electrodes suffer both capacity fading and an increasing divergence between the charge and discharge capacity as a result of the polysulfide shuttle mechanism. A discharge capacity of 8.8 mAh/cm.sup.2 is achieved after the electrolytes penetrate the thick electrodes, afterwards, the capacity is maintained at around 6 mAh/cm.sup.2 for more than 120 cycles, corresponding to a specific capacity of around 850 mAh/g (FIGS. 3A and 3B). Specifically, the capture of polysulfides is well evidenced by the cycle performance at 0.05 C. In comparison, cells based on PVDF binder suffered from rapid capacity decay, indicating a greater degree of polysulfides dissolution into the electrolyte. The average Coulombic efficiency based on MPS is calculated to be more than 96% over 100 cycles, which shows little shuttle effect owing to polysulfides dissolution (FIG. 3C). As shown in FIG. 3d, two well-defined discharge plateaus were observed, which could be assigned to the multistep reduction mechanism of elemental sulfur.

(30) To track the morphology evolution during lithiation/delithiation process, the scanning electron microscopy (SEM) images are shown in FIG. 4. A clear porous structure is performed at vary scale for fresh electrode before cycle. When the cells are disassembled at fully discharged state, no delamination is observed in the electrode and none of the reddish color electrolyte, which is typical color of polysulfides. A homogeneous Li.sub.2S precipitation is observed at the top of the electrode, indicating good conductivity of the electrode. Moreover, the good reversibility is well evidenced through the decomposition of Li.sub.2S layer after fully charged. The sulfur and carbon elemental maps also clearly demonstrate that sulfur is homogeneously distributed in the framework of electrode. The increasing content of oxygen after discharge is supposed to be attributed by the leaving sulfate group from the bulk electrode.

(31) FIG. 4 illustrates SEM images of sulfur electrodes with different magnification. Fresh sulfur electrode (a, b, c, d); fully discharged electrode (e, f, g, h); Fully charged electrode (i, j, k, l). (Magnification: a, c. e 1200; b, f, J 2000; c, g, k 5000; d, h, l 10000).

(32) The molecular structure of Poly(epichlorohydrin) (PECH) and Polyvinyl Chloride (PVC) is demonstrated in scheme 1. In comparison with PVDF, the chloro group is at the primary carbon position in PECH. Therefore, the chloro group is more active than that of PVC. This will facilitate the nucleophilic attack by polysulfide to PECH. The effect is verified by the comparison of the cycle performance as shown in FIG. 5. The PECH binder based sulfur electrode can achieve around 2 times of the areal capacity than that of the PVC binder based sulfur electrode.

(33) In summary, an innovative class of polymer binders and simple electrode fabrication strategy is first successfully applied to solve the lithium sulfides shuttle effect through nucleophilic attack formed carbon-sulfur (CS) bonding. The function of the CS bonding is evidenced by the achieved areal capacity, i.e., 6 mAh/cm.sup.2, for more than 100 cycles at C/20. The Coulombic efficiency is maintained up to 96% during the cycling. The nucleophilic attack during the lithiation/delithiation is monitored through Raman, TFY and FTIR spectroscopies. This low cost and efficient design is of significance for the progress of lithium-sulfur batteries.

(34) Polymeric systems bearing positive charges are synthesized in the presence of novel cationic entities, incorporated on their backbone and/or as side chains, are considered as cationic polymers. Poly(vinylbenzyl chloride)-co-poly(vinylbenzyl trimethylammonium chloride) (PVBNC) and Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] are promising cationic polymers since its low cost and wide application. (Scheme 2 and 3) As illustrated above, the dissolution and shuttle effect of polysulfides intermediate produced after lithiation/delithiation is the most challenging issue for lithium sulfur batteries. Cationic polymers have the potential to ionically bonded with polysulfides anions.

(35) FIGS. 6A and 6B illustrate cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] C/20.

(36) FIG. 7 illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)] specifically the dis-charge/charge voltage profiles of the 20th cycle.

(37) The electrochemical performance of the sulfur electrode in FIGS. 6A, 6B, and 7 is based on cationic polymer Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)]. The specific capacity can be held for more than 1000 mAh/g for 20 cycles, meanwhile, the areal capacity is maintained above 5 mAh/cm.sup.2. The cycle performance provides strong evidence of alleviation of polysulfides shuttle effect and promotion of sulfur utilization.

(38) ##STR00008##

(39) Scheme 2.

(40) The molecular structure of Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)].

(41) ##STR00009##