INK CUP LINED WITH NON-STICK COATING

Abstract

An improvement to the present ink cup technology is presented, resulting in reduced clean-up time, by measurement at least three times faster producing a significant reduction in labor cost. Exposure by employees to high-VOC solvents and emulsifiers is eliminated, and low-VOC solvents mixed with water can be used. This is a significant saving in environmental damage and disposal costs.

Claims

1. An ink cup, the ink cup having a concave shape, the concave shape possessing an external and an internal surface, the ink cup comprised of a rigid material such that the internal surface is porous to ink, the internal surface of said ink cup is covered with a uniform thickness of a non-stick coating, the coating is sprayed and then baked onto the ink cup internal surface at approximately 500 degrees Fahrenheit, the baked non-stick coating possessing a non-porous surface with a low coefficient of friction such that vertical sections of said internal surface shed ink due to the force of gravity, the baked internal surface coating is water proof, washable and resistant to low-VOC solvent.

2. The ink cup of claim 1 where the rigid material is aluminum and the non-stick coating is spray-able 958-203 TEFLON.

3. A method of using the ink cup of claim 2 comprised of the steps of obtaining said ink cup, filling the ink cup with ink, using the ink cup in a printing process, cleaning the ink cup with water or water mixed with low Volatile Organic Compound (VOC) solvents, reusing the ink cup as in this method.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] FIG. 1. Ink Cup With TEFLON Spray Coating

[0009] FIG. 2. Coated Ink Cup with Ink Residue

DETAILED SPECIFICATION

[0010] FIG. 1 illustrates the interior cavity 105 of the ink cup 101 being sprayed with a TEFLON coating 102. The thickness of the coating 102 is exaggerated. This coating is baked onto the ink cup 101 at approximately 500 degrees Fahrenheit until the finish is hard and smooth.

[0011] In FIG. 2, the concept of the present invention is shown. The TEFLON coating 102 causes ink 103 to bead near the surface and drain, so that after the ink cup has been emptied, the ink 103 can be easily wiped away or removed with a gentle, low-VOC solvent. The present state-of-the-art with an uncoated cup requires more extensive clean-up with high-VOC solvents that require the use of gloves and a ventilated area.

[0012] The ink cup 101 can be made with any material that is rigid and that stands up to the baking temperature. Aluminum is the preferred embodiment for the current ink cup. Because aluminum is porous to most fluids, an aluminum ink cup 101 would normally trap ink in the pores of its interior surface. Hence, the coating 102 seals these pores and presents a smooth, non-porous interior surface to ink 103 stored in the ink cup 101.

[0013] The TEFLON coating 102 possesses a low coefficient of friction

[0014] In the preferred embodiment, the TEFLON coating is selected as 958-203 TEFLON FEP for its spray-able characteristics, but other TEFLON and other non-stick coatings can be used. TEFLON FEP possesses a low coefficient of static friction ranging from 0.12 to 0.2, which will allow ink 103 to bead up on the sprayed interior surface 102 of the cup 101 and slide off due to the force of gravity, if nothing else. These values are from the Physics Factbook, edited by Glenn Elert.

[0015] Since surfaces coated with Teflon coatings are both oleophobic and hydrophobic, they are not readily wetted. Cleanup is easier and more thoroughin many cases, surfaces are self-cleaning. The improvement to the present technology results in reduced clean-up time, by measurement at least three times faster. This is a significant reduction in labor cost. Low-VOC solvents mixed with water can be used and therefore exposure by employees to high-VOC solvents and emulsifiers is eliminated. This is a significant saving in environmental damage and disposal costs.

[0016] This invention has other applications, potentially, and one skilled in the art could discover these. The explication of the features of this invention does not limit the claims of this application; other applications developed by those skilled in the art will be included in this invention.