GAS ENTRAINED REMOVABLE MANDREL

Abstract

This invention involves the incorporation of gas in the matrix of a mandrel. The incorporation of gas, as foam, into the matrix of a mandrel reduces the density of the mandrel. The resulting mandrel is easier to remove from finished product by washout or disintegration. Therefore it is of great value in the use of mandrels in making hollow composite parts.

Claims

1. A mandrel for utilization in the fabrication of a plastic/composite which is formed with entrained air or gas.

2. The mandrel of claim 1 containing 5% or more of its volume as air or gas, as foam.

3. The mandrel of claim 1 produced by pneumatic means.

4. The mandrel of claim 1 produced by mixing foam into the mandrel matrix before hardening the matrix.

5. The mandrel of claim 1 produced by chemical means to entrain the gas in the matrix.

6. A mandrel that is formed utilizing entrained gas, a hardening matrix, and a binder.

7. The mandrel in claim 6 which contains a controlled amount of entrained gas greater than 5%.

8. The mandrel in claim 6 which contains a liquid matrix that is able to harden to a desired shape upon setting or curing or drying.

9. The mandrel in claim 6 which contains a binder that is able to impart special properties to the mandrel matrix including strength, dispersibility, thermal properties and/or color.

10. A mandrel formed with a dense outer shell and filled with foamed matrix material.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0017] The air-entrained mandrel can be formed in various ways. The object is to trap bubbles of air or gas within the matrix of the mandrel during the forming of the mandrel. The solid mandrel resulting from entraining air or gas is significantly less dense by 20%, 30%, 40%, 50% or more compared to a mandrel that is not entrained with air or gas. In addition to this decrease in density, the resulting mandrel is more easily removed or washed out from the finished product requiring 20% to 50% or greater less time and effort. As little as 5% or 10% foam as a percent of matrix volume can provide benefits.

[0018] Air is a mixture of gases under conditions for creating a mandrel. Entraining air is entraining gas.

[0019] Gas can be entrained in a mandrel with a matrix comprised of plaster, Portland cement, sodium silicate, starch, caboxymethylcellulose, etc.

[0020] Pneumatic Production of Air-entrained Mandrel

[0021] Compressed air or gas mixed with a foaming agent produces foam. The foam is mixed with the mandrel matrix creating a foam matrix, and the foam matrix is then cast into the desired shape. Upon hardening of the foam matrix mixture, the air or gas entrained mandrel is removed. The mandrel can then be further dried, wrapped in raw composite, and the raw composite cured, as appropriate.

[0022] The foaming agent can be in a plaster solution. Compressed air is mixed with foaming agent in the plaster solution. The foam matrix is then cast into the desired shape.

[0023] Other filler additives such as cenospheres, glass beads, talc, sand graphite, graphene, etc. can also be utilized to vary properties of the foamed matrix.

[0024] Multiple hinders or additives can be utilized to enhance the properties of the matrix, such as polyvinylpyrrolidone (PVP), PEO, PVA, PU, or other liquid dispersible polymers. Other matrix forming compounds such as starch, caboxymethylcellulose, and acetate are also helpful in modifying the foamed matrix properties. These additives may increase strength, vary viscosity, enhance removal rate, or even change the thermal properties of the material, including coefficient of thermal expansion and thermal conductivity.

[0025] Chemical Production of Air-entrained Mandrel

[0026] Air or gas can alternatively be entrained by utilizing an internal chemical reaction to generate gas in the mixture of the mandrel material prior to forming the mandrel. Appropriate chemicals are added to the mandrel matrix which is then cast into the desired shape. Gas is entrained in the foam matrix mandrel as the mandrel hardens. After hardening, the gas-entrained mandrel is removed and utilized, as appropriate, for forming a composite product.

[0027] As can be understood, foam can be incorporated into many different mandrels.

[0028] Other filler additives such as cenospheres, glass beads, talc, sand, graphite, graphene, etc. can also be utilized to vary properties of the foamed matrix. Portland cement can also be utilized.

[0029] Multiple hinders or additives can be utilized to enhance the properties of the matrix, such as PVP, PEO, PVA, PU, or other liquid dispersible polymers. Other matrix forming compounds such as starch, caboxymethylcellulose, and acetate are also helpful in modifying the foamed matrix properties. These additives may increase strength, vary viscosity, enhance removal rate, or even change the thermal properties of the material, including coefficient of thermal expansion and thermal conductivity.

[0030] Production of Air-entrained Mandrel with Dense Outer Shell

[0031] The invention further relates to the utilization of a hybrid foam system in which a dense outer shell is first cast into the desired mold cavity. The shell is much stronger than the foam matrix and produces a closed surface to better distribute force. The shell also makes sealing and handling easier. The shell is then filled with foamed matrix material, either pneumatic or chemical produced, and the foamed matrix material is allowed to harden. The hybrid shape is then post processed.

[0032] The invention can be applied in several ways, depending on what process requirement is followed. The shell may be precast and cured, and then the foam matrix applied or co-cured. The resultant water-removable shape, depending on the thickness of the shell and strength of the foam/shell hybrid, has greater strength for processing, such as under autoclave conditions.

[0033] Examples (Illustrating the Invention and not to be Limiting)

[0034] A mixture of plaster is added to 60% by volume foam mixed at a ratio of 40 parts water:1 part foaming agent. This foamed matrix is then cast into a female cavity and allowed to harden. The resultant mandrel is then post cured to result in a mandrel that is about 50% lighter than a similar plaster mandrel.

[0035] Alternatively, the plaster can contain any of a number of binders. The plaster containing binder is then mixed with the foam to produce the foamed matrix. One example is 2% polyvinylpyrrolidone in the plaster solution, mixed with an approximately equal volume of foam to produce the foamed matrix. The mixture with foam can be varied, producing a mandrel of, for example, 30% less weight.

[0036] Alternatively, a foaming agent is added to the plaster solution at 0.5%, air is injected until the volume of the plaster increases about 20%, 30%, 40% to 50%, this foamed matrix is cast into a cavity and allowed to harden.

[0037] Alternatively, gas is generated in the plaster solution containing foaming agent with chemicals, such as vinegar and baking soda, and the foamed matrix is cast and allowed to harden.

[0038] Depending on the foaming agent, it can be used at many concentrations to effectively produce the foamed matrix.

[0039] As can be understood by one skilled in the art, there are many ways to utilize this invention.

[0040] Utilization of in situ polymerization is also useful in modifying the physical properties of the foam matrix.