Water disintegrable flushable catheter

Abstract

A water disintegratable catheter having a barrier layer disposed on an outer surface and/or inner surface of the catheter wherein the barrier layer comprises a hydrophobic component.

Claims

1. A water disintegrable catheter comprising: a catheter shaft formed from a water disintegrable material; a water barrier layer disposed on an outer surface of the catheter shaft, wherein the water barrier layer comprises a hydrophobic component; and a lubricious hydrophilic coating disposed on the water barrier layer.

2. The catheter of claim 1 wherein the water barrier layer is a coating on the outer surface.

3. The catheter of claim 1 wherein the hydrophobic component of the water barrier layer comprises a hydrophobic polymer.

4. The catheter of claim 1 wherein the hydrophobic component of the water barrier layer comprises ethyl cellulose.

5. The catheter of claim 1 wherein the water disintegratable material of the catheter comprises polyvinyl alcohol.

6. The catheter of claim 1 wherein the water barrier layer has a thickness of between about 1 micron and about 1000 microns.

7. The catheter of claim 1 wherein the water barrier layer has a thickness of between about 600 microns and about 1000 microns.

8. The catheter of claim 1 wherein the water barrier layer has a thickness of between about 10 microns and about 600 microns.

9. The catheter of claim 1 wherein the water barrier layer comprises a reactive monomer or oligomer.

10. The catheter of claim 1 further including a second water barrier layer disposed on an inner surface of the catheter shaft.

11. The catheter of claim 1 wherein the catheter shaft comprises a urinary catheter shaft.

12. (presented presented) The catheter of claim 1 wherein the water barrier layer comprises a hydrophilic component.

13. The catheter of claim 12 wherein the hydrophobic polymer is between about 80 wt% and about 90 wt% of the water barrier layer and the hydrophilic component is between about 10 wt% and about 20 wt% of the water barrier layer.

14. The catheter of claim 12 wherein the hydrophobic polymer is about 85 wt% of the water barrier layer and the hydrophilic component is about 15 wt% of the water barrier layer.

15. The catheter of claim 12 wherein the hydrophilic component of the water barrier layer comprises hydroxyl propyl methyl cellulose, poly(ethylene glycol) and/or poly(ethylene glycol) diacrylate.

Description

BRIEF DESCRIPTION OF THE DRAWING

(1) FIG. 1 is a longitudinal cross-section of a portion of a catheter tube having a water barrier layer according to the present disclosure.

DETAILED DESCRIPTION OF THE EMBODIMENTS

(2) The present disclosure relates to a water disintegrable flushable product, such as a medical product, that will dissolve, hydrolyze or biodegrade in water. The medical product may be, for example, a urinary catheter. While the subject matter described herein is described relative to a flushable urinary catheter, it will be understood that the subject matter is applicable to other flushable devices and products as well.

(3) The urinary catheters of the present disclosure are made from a water disintegrable material(s). The urinary catheters also include a water barrier layer disposed on the inner and/or the outer surfaces of the catheter shaft. The water barrier layer prevents or limits the ingress of water to the water disintegrable material for a desired time period. As explained in more detail below, the water barrier may be a coating that is applied over the inner and/or outer surfaces of the catheter. The water barrier layer is preferably biodegradable. Additionally, the water barrier layer, optionally, supports or is an attachment for a lubricous hydrophilic coating, when one is used on the catheter.

(4) FIG. 1 illustrates a portion of a catheter 10 according to the present disclosure. The catheter includes a catheter shaft tube 12, which is made of a water disintegratable material. A water barrier layer, such as water barrier coating 14, is disposed on the outer surface of the catheter shaft 12. A lubricous hydrophilic coating 16 is disposed on the barrier coating 14. Optionally, a barrier coating 18 may be disposed on the inner surface of the catheter shaft tube. A radial eyelet 20 may be located in the catheter shaft tube 12 for the drainage of urine through the tube. A suitable tip (not shown) will be formed at the right end (as seen in FIG. 1) of the tube.

(5) The catheter shaft may be made from one or more water (for example, water, urine or fluids utilized in toilet and plumbing systems) disintegrable materials. Such material may include, for example, water soluble, water hydrolysable or enzymatically hydrolysable materials, which at least partially dissolve or breakdown when in contact with water. The material of the catheter shaft may be designed to partially or fully dissolve and/or breakdown depending on the desired use. The water disintegrable materials are preferably flushable materials which are suitable for disposal in a toilet or sanitary system and, even more preferably, biodegradable flushable materials which may be chemically broken down over time by water, living organisms or other biological means.

(6) Such water disintegrable materials may include, for example, polyvinyl alcohol, including but not limited to an extrudable polyvinyl alcohol, polyacrylic acids, polylactic acid, polyesters, polyglycolide, polyglycolic acid, poly lactic-co-glycolic acid, polylactide, amines, polyacrylamides, poly(N-(2-Hydroxypropyl) methacrylamide), starch, modified starches or derivatives, amylopectin, pectin, xanthan, scleroglucan, dextrin, chitosans, chitins, agar, alginate, carrageenans, laminarin, saccharides, polysaccharides, sucrose, polyethylene oxide, polypropylene oxide, acrylics, polyacrylic acid blends, poly(methacrylic acid), polystyrene sulfonate, polyethylene sulfonate, lignin sulfonate, polymethacrylamides, copolymers of aminoalkyl-acrylamides and methacrylamides, melamine-formaldehyde copolymers, vinyl alcohol copolymers, cellulose ethers, poly-ethers, polyethylene oxide, blends of polyethylene-polypropylene glycol, carboxymethyl cellulose, guar gum, locust bean gum, hydroxyproply cellulose, vinylpyrrolidone polymers and copolymers, polyvinyl pyrrolidone-ethylene-vinyl acetate, polyvinyl pyrrolidone-carboxymethyl cellulose, carboxymethyl cellulose shellac, copolymers of vinylpyrrolidone with vinyl acetate, hydroxyethyl cellulose, gelatin, poly-caprolactone, poly(p-dioxanone), or combinations, blends or co-polymers of any of the above materials. The water disintegrable or enzymatically hydrolysable materials may also be any of those that are included in certified flushable products that meet the National Sanitation Foundation standards for flushability or materials and products that meet INDA/EDANA Flushability Guidelines or the UK Water Industry Research, test protocols set forth in Test Protocol to Determine the Flushability of Disposable Products, Review of the Manufactures 3.sup.rd Ed. Guidance Document, 2013, by Drinkwater et al. While catheters made from water disintegrable or enzymatically hydrolysable materials may be disposed of in a toilet, it is not necessary to dispose of such catheters in a toilet and such catheters may also be disposed in normal municipal waste systems or garbage collection systems.

(7) The water barrier layer may include one or more hydrophobic polymers. The hydrophobic polymers may include, for example, hydrophobic celluloses, ethyl cellulose, acrylates, methyl acrylate-methacrylic acid copolymers, methyl methacrylate-methacrylic acid copolymers, beeswax and/or other suitable waxes, chitosan, plastarch material (PSM), poly-3-hydroxybutyrate (PHB), polyhydroxyalkanoate (PHA), polycaprolactone, polyvinyl acetate phthalate (PVAP), shellac, sodium alginate, alginates, zein or combinations thereof.

(8) The water barrier layer may also include one or more hydrophilic components, such as a water soluble polymer, blended or combined with the hydrophobic components. The hydrophilic components may include for example, hydroxyl propyl methyl cellulose, poly(ethylene glycol) (PEG), PEG DA, oly(N-isopropylacrylamide) (PNIPAM), polyacrylamide (PAM), poly(2-oxazoline), polyethylenimine (PEI), acrylic polymers, poly(acrylic acid), polymethacrylate, poly(ethylene oxide), poly(vinyl alcohol) (PVA), PVA copolymers, poly(vinylpyrrolidone) (PVP) and PVP copolymers, polyelectrolytes, maleic anhydride copolymers, polyethers, cucurbit[n]uril hydrate, hyaluronic acid (HA), albumin and copolymers, mixtures and bends of the above. Furthermore, the hydrophilic components may be hydrophilic polymers that are formed within the barrier layer by inclusion of reactive monomers (such as PEGDA, HEMA, Acrylic Acid, Methacrylic Acid) and combinations of monomers (such as acrylate & methacrylate monomers) and an appropriate initiator system (triggered by heat, light or other means). Such monomers may yield cross-linked polymers or linear polymers or variations thereof.

(9) Other hydrophilic additives that may help achieve the desired degrees of film porosity could include ethyl cellulose type films prepared as dispersions with water soluble organic and inorganic salts or compounds.

(10) Such hydrophilic components may be used to increase the hydrophilicity of the barrier layer and/or to attenuate or vary the amount of water ingress into the water disintegratable material and/or tailor the disintegration rate of the barrier. For example, the hydrophilic component may be used to tailor or attenuate the porosity of the hydrophobic barrier layer. In one embodiment, the hydrophilic barrier is a porous polymer coating wherein the coating includes a desired amount of the hydrophilic component to tailor the porosity of the coating.

(11) In one embodiment of a water barrier layer, the hydrophobic component may be between about 75 wt % and about 100 wt % of the water barrier layer and the hydrophilic component may be between about 0 wt % and about 25 wt % of the water barrier layer. In another embodiment, the hydrophobic component is between about 80 wt % and about 90 wt % of the water barrier layer and the hydrophilic component is between about 10 wt % and about 20 wt % of the water barrier layer. In another embodiment, the hydrophobic component is about 85 wt % of the water barrier layer and the hydrophilic component is about 15 wt % of the water barrier layer.

(12) The thickness of the water barrier layer may vary depending on the desired use. For example, the thickness of the water barrier layer may be selected to tailor the rate of disintegration of the barrier and/or the rate of water passing through the barrier. In one embodiment, the thickness of the water barrier layer may be at least about 1 micron. In another embodiment, the thickness of the barrier layer may be less than about 1000 microns. In one example, the thickness of the water barrier layer may be between about 1 micron and about 1000 microns. In another example, the thickness of the water barrier layer may be between about 10 microns and about 600 microns. In yet another example, the thickness of the water barrier layer may be between about 600 microns and about 1000 microns. In other examples, the thickness of the barrier layer may be less than about 1 micron or greater than 1000 microns.

(13) Preferably, the barrier layer partially or totally disintegrates after use and while in the sewer system and water treatment plants. The level of disintegration of the barrier layer can be achieved by tailoring the relative solubility of the barrier layer by including hydrophilic components or other additives/agents in the barrier layer.

(14) The disintegration rate of the barrier layers can also be achieved by tailoring the mechanical properties of the barrier layer. The mechanical properties of the barrier can be modified by increasing or decreasing the amount of crosslinking in the barrier. The properties may also be modified by differing the molecular weight and/or layer thickness. For example, a thin barrier layer may breakdown (disintegrate) to the desired particle size simply as a result of the physical action of flushing and the exposure to mechanical forces in sewage pipes and water treatment plants.

(15) In addition, the balance between catheter disintegration and barrier breakdown rate can also be further tailored by using multiple layers of different barriers so as to create a functionality gradient. Relative solubility and mechanical strength can be used in tandem in order to achieve the desired breakdown rates for the barrier layers.

(16) The barrier layer also may be tailored such that the catheter shaft remains protected from the ingress of water for a selected period of time. For example, the barrier layer may be tailored such that the catheter may be used for a period of time before the functionally of the catheter diminishes due to the ingress of water causing disintegration of the catheter shaft. In one embodiment, the barrier layer is tailored to protect against the ingress of water during the time period it takes for the user to complete catheterization.

(17) In one embodiment, the barrier layer and catheter will disintegrate in such a manner as to meet the specifications for flushable products detailed in the Test Protocol to Determine the Flushability of Disposable Products UKWIR Project WM07G202.

(18) The barrier layer may also include agents that enhance adhesion of the layer to the catheter. For example, the agents may add functionality to the coating. In one embodiment, the barrier layer may include a photo-curable acrylate and photo-initiator to promote curing of same.

(19) In one example of a flushable catheter, the catheter shaft is made from a water soluble flushable PVOH. The catheter shaft also includes a water barrier layer and a hydrophilic coating that may be activated by hydration. The catheter may be used by the end-user during a defined functional period, e.g. 20-30 minutes, after which the catheter can be disposed of conveniently and hygienically by flushing down the toilet.

(20) The water barrier layer may be a coating applied to the outer and/or inner surfaces of the catheter shaft using any suitable coating processes, such as dip coating, spraying or painting a barrier solution onto the surfaces of the catheter shaft. After the barrier coating solution has been coated onto the surfaces of the catheter shaft, the coating solution may be dried and/or cured to form the water barrier layer. In a dip coating process, for example, the catheter shaft may be dipped into a barrier coating solution. After the catheter shaft is removed from the coating solution, the solution may be dried and/or cured to form the coating on the surface of the catheter shaft. The barrier coating may be adhered to the surface of the catheter by physical adhesion or chemical bonding. In one embodiment, the barrier coating may be fixed to the surface of the catheter by curing or fixed by heat, light or any other suitable manner. The barrier coating may be applied to the entire outer and/or inner surfaces of the catheter shaft or may be selectively applied to the surfaces wherein selected portions of the surface are coated while other portions remain uncoated.

(21) In one embodiment of a water barrier coating solution, the coating solution formulation may include between about 0.75% and about 6% by weight of a hydrophobic component(s), such as ethyl cellulose, and between about 94 wt % to about 99.25 wt % solvent, such as ethanol. Optionally, the formulation may include between about 0.75 wt % and 4.25 wt % of a hydrophilic component, for example PEG DA such as PEG 400 DA, and about 0.20 wt % of a photoinitiator, such as Irgacure. In one embodiment of the water barrier coating solution, the hydrophobic component may be between about 0.75 wt % and about 6 wt %, the hydrophilic component may be between about 0.75 wt % and about 4.25 wt % and the solvent may be between about 89.75 wt % and about 98.5 wt % of the water barrier coating solution.

EXAMPLES

(22) Listed below are exemplary barrier coating formulations:

(23) TABLE-US-00001 Ethyl PEG400DA Irgacure 2959 Ethanol Formulation Cellulose wt % wt % wt % wt % 1 5.0 95 2 4.25 0.75 0.20 94.80 3 0.75 4.25 0.20 94.80

(24) Aspects of the present subject matter described above may be beneficial alone or in combination with one or more other aspects. Without limiting the foregoing description, in accordance with a first aspect, a water disintegrable urinary catheter comprising a catheter shaft formed from a water disintegrable material; and a water barrier layer disposed on an outer surface of the catheter shaft, wherein the water barrier layer comprises a hydrophobic component.

(25) Aspect 2. The catheter of aspect 1 further including a lubricious hydrophilic coating disposed on the water barrier layer.

(26) Aspect 3. The catheter of any one of the preceding aspects wherein the water barrier layer is a coating on the outer surface.

(27) Aspect 4. The catheter of any one of the preceding aspects wherein the hydrophobic component of the water barrier layer comprises a hydrophobic polymer.

(28) Aspect 5. The catheter of any one of the preceding aspects wherein the hydrophobic component of the water barrier layer comprises ethyl cellulose.

(29) Aspect 6. The catheter of any one of the preceding aspects wherein the water barrier layer comprises a hydrophilic component.

(30) Aspect 7. The catheter of aspect 6 wherein the hydrophobic polymer is between about 80 wt % and about 90 wt % of the water barrier layer and the hydrophilic component is between about 10 wt % and about 20 wt % of the water barrier layer.

(31) Aspect 8. The catheter of any one of aspects 6 and 7 wherein the hydrophobic polymer is about 85 wt % of the water barrier layer and the hydrophilic component is about 15 wt % of the water barrier layer.

(32) Aspect 9. The catheter of any one of aspect 6-8 wherein the hydrophilic component of the water barrier layer comprises hydroxyl propyl methyl cellulose, poly(ethylene glycol) and/or poly(ethylene glycol) diacrylate.

(33) Aspect 10. The catheter of any one of the preceding wherein the water disintegratable material of the catheter comprises polyvinyl alcohol.

(34) Aspect 11. The catheter of any one of the preceding aspects wherein the water barrier layer has a thickness of between about 1 micron and about 1000 microns.

(35) Aspect 12. The catheter of any one of the preceding aspects wherein the water barrier layer has a thickness of between about 600 microns and about 1000 microns.

(36) Aspect 13. The catheter of any of one aspects 1-11 wherein the water barrier layer has a thickness of between about 10 microns and about 600 microns.

(37) Aspect 14. The catheter of any one of the preceding aspects wherein the water barrier layer comprises a reactive monomer or oligomer.

(38) Aspect 15. The catheter of any one of the preceding aspects further including a second water barrier layer disposed on an inner surface of the catheter shaft.

(39) Aspect 16. A water barrier solution for forming a water barrier layer, the solution comprising: a solvent and a hydrophobic component.

(40) Aspect 17. The water barrier solution of aspect 16 wherein the hydrophobic component comprises ethyl cellulose.

(41) Aspect 18. The water barrier solution of any one of aspects 16 and 17 further comprising a hydrophilic component.

(42) Aspect 19. The water barrier solution of any one of aspects 16-18 wherein the hydrophilic component comprises hydroxyl propyl methyl cellulose, poly(ethylene glycol) and/or poly(ethylene glycol) diacrylate.

(43) Aspect 20. The water barrier solution of any one of the aspects 18-19 wherein the hydrophobic components are between about 0.75 wt % and about 6 wt %, the hydrophilic components are between about 0.75 wt % and about 4.25 wt %, and the solvent is between about 89.75 wt % and about 98.5 wt % of the water barrier solution.

(44) Aspect 21. The water barrier solution of any one of aspects 16-20 further including a reactive monomer and/or oligomer.

(45) It should be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modification can be made without departing from the spirit and scope of the invention disclosed herein.