Article with glass layer and glass-ceramic layer and method of making the article

Abstract

A glass-ceramic composition is disclosed herein including: from about 60 mol. % to less than 72.0 mol. % SiO2; from about 10 mol. % to about 17 mol. % Al2O3; from about 3 mol. % to about 15 mol. % Na2O; from about 1 mol. % to about 8 mol. % Li2O; and from about 3 mol. % to about 7 mol. % TiO2. The glass-ceramic composition can be used to form one, two, or more, cladding layers of a laminated glass article, wherein the layer(s) of glass-ceramics material can be cerammed to form one or more glass layers.

Claims

1. A glass article comprising: a glass core layer disposed between a first glass cladding layer and a second glass cladding layer; wherein the glass core layer has a composition which is different from the composition of the first and second glass layers; wherein the first glass cladding layer and the second glass cladding layer are formed from a glass-ceramic composition comprising: from about 60 mol. % to less than 72.0 mol. % SiO.sub.2; from about 10 mol. % to about 17 mol. % Al.sub.2O.sub.3; from about 3 mol. % to about 15 mol. % Na.sub.2O; from about 1 mol. % to about 8 mol. % Li.sub.2O; and from about 3 mol. % to about 7 mol. % TiO.sub.2; and wherein a net CTE difference between at least one of the first and second glass cladding layers, and the glass core layer, is from about 2010.sup.7/C to 62710.sup.7/C.

2. The glass article of claim 1, wherein the first glass cladding layer and the second glass cladding layer comprise: from about 64 mol. % to less than 72.0 mol. % SiO.sub.2; from about 11 mol. % to about 16 mol. % Al.sub.2O.sub.3; from about 4 mol. % to about 13 mol. % Na.sub.2O; from about 2 mol. % to about 7 mol. % Li.sub.2O; and from about 4 mol. % to about 6 mol. % TiO.sub.2.

3. The glass article of claim 1, wherein the first and second glass cladding layers have a coefficient of thermal expansion of from about 510.sup.7/C to about 2510.sup.7/C.

4. The glass article of claim 1, wherein the first and second glass cladding layers have a coefficient of thermal expansion of from about 1010.sup.7/C to about 2010.sup.7/C.

5. The glass article of claim 1, wherein: a first surface of the glass core layer is directly adjacent the first glass cladding layer; and wherein a second surface of the glass core layer is directly adjacent the second glass cladding layer.

6. The glass article of claim 1, wherein the first glass cladding layer and the second glass cladding layer are compressively stressed.

7. The glass article of claim 1, wherein the first glass cladding layer and the second glass cladding layer further comprise an alkaline earth oxide.

8. A use of the glass article of claim 1 for cover glass or glass backplane applications in consumer or commercial electronic devices, for touch screen or touch sensor applications, for portable electronic devices, for photovoltaic applications, for architectural glass applications, for automotive or vehicular glass applications, or for commercial or household appliance applications.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 schematically depicts a cross section of a laminated glass article according to one or more embodiments shown and described herein; and

(2) FIG. 2 schematically depicts a fusion draw process for making the glass article of FIG. 1.

DETAILED DESCRIPTION

(3) Reference will now be made in detail to embodiments of glass-ceramic compositions disclosed herein and articles incorporating the same, examples of which are illustrated in the accompanying drawings. Whenever possible, the same reference numerals will be used throughout the drawings to refer to the same or like parts. The glass ceramic compositions described herein may be utilized in conjunction with core glass compositions to produce laminated glass articles which are compressively stressed without being ion-exchanged. In some embodiments, a difference between the CTE of the core and the clad layers is less than 510.sup.7/C when the core and clad layers are in a molten or viscous state.

(4) In one set of embodiments, a glass-ceramic composition for the skin, or clad, layer(s) comprises from about 64 mol. % to less than 72.0 mol. % SiO.sub.2; from about 11 mol. % to about 16 mol. % Al.sub.2O.sub.3; from about 4 mol. % to about 13 mol. % Na.sub.2O; from about 2 mol. % to about 7 mol. % Li.sub.2O; and from about 4 mol. % to about 6 mol. % TiO.sub.2 as glass-ceramic network formers. The glass composition may further comprise from about 0.1 mol. % to about 5 mol. % alkaline earth oxide. The alkaline earth oxide comprises at least MgO. The MgO may be present in the glass composition in a concentration from about 0.5 mol. % to about 2 mol. %. In some embodiments, the glass-ceramic composition has a liquidus in the range of greater than about 20,000 poise, and in some embodiments greater than about 25,000 poise and in some embodiments greater than about 28,000 poise. The glass-ceramic composition has, before ceramming, a coefficient of thermal expansion (CTE) of from about 3510.sup.7 to about 8010.sup.7, and in some embodiments from about 4010.sup.7 to about 7210.sup.7; in some embodiments, the glass composition of the glass core will have a corresponding coefficient of thermal expansion. The glass-ceramic composition has, after ceramming, a coefficient of thermal expansion of from about 510.sup.7 to about 2510.sup.7, and in some embodiments from about 1010.sup.7 to about 2010.sup.7. The net CTE difference then between the final clad (skin) composition, after ceramming, and the core will be in the range of about 2010.sup.7 to 6210.sup.7. Thus, the possible CTE difference between the final skin/clad composition and the glass core can be higher than that achieved using glass pairs alone. For example, a core glass with a CTE of 9010.sup.7 (such as glass code 2317) could be utilized with a skin as one of the glass ceramic compositions with, e.g., a pre-ceram CTE of 7010.sup.7; this combination can be cut on the draw tower, then the outer skin cerammed to, e.g., a CTE of 5 to 2010.sup.7, resulting in a final CTE difference between the skin and core of about 70 to 8510.sup.7, which can be much higher than known capabilities of glass compositions alone, resulting in higher compressive stress as well. In some embodiments, glass ceramic materials can have negative CTE, and therefore a very high CTE difference between the core and skin can be achieved using the glass ceramic clad. In some embodiments, a difference between the CTE of the core and the clad layers is less than 510.sup.7/C when the core and clad layers are in a molten or viscous state. The glass compositions and glass articles formed from the glass compositions will be described in more detail herein with specific reference to the appended drawings.

(5) The term liquidus viscosity, as used herein, refers to the shear viscosity of the glass composition at its liquidus temperature.

(6) The term liquidus temperatures, as used herein, refers to the highest temperature at which devitrification occurs in the glass composition

(7) The term CTE, as used herein, refers to the coefficient of thermal expansion of the glass composition averaged over a temperature range from about 20 C. to about 300 C.

(8) The term substantially free, when used to described the absence of a particular oxide component in a glass composition, means that the component is present in the glass composition as a contaminant in a trace amount of less than 1 mol. %.

(9) In the embodiments of the glass compositions described herein, the concentration of constituent components (e.g., SiO.sub.2, Al.sub.2O.sub.3, Na.sub.2O and the like) are given in mole percent (mol. %) on an oxide basis, unless otherwise specified.

(10) The glass-ceramic compositions described herein have properties, such as the liquidus viscosity and the liquidus temperature, which make the glass-ceramic compositions particularly well suited for use with fusion forming processes, such as the fusion down draw process and/or the fusion lamination process. These properties are attributable to the specific compositions of the glasses, as will be described in more detail herein.

(11) In the embodiments of the glass compositions described herein SiO.sub.2 is the largest constituent of the composition and, as such, SiO.sub.2 is the primary constituent of the glass network formed from the glass-ceramic compositions. Pure SiO.sub.2 has a relatively low CTE and is alkali free. However, pure SiO.sub.2 has an extremely high melting point. Accordingly, if the concentration of SiO.sub.2 in the glass compositions described herein is too high, the formability of the glass composition may be diminished as higher concentrations of SiO.sub.2 increase the difficulty of melting the glass which, in turn, adversely impacts the formability of the glass.

(12) The glass compositions described herein also comprise Al.sub.2O.sub.3. Al.sub.2O.sub.3 serves as a glass network former, similar to SiO.sub.2. Like SiO.sub.2, Al.sub.2O.sub.3 increases the viscosity of the glass composition due to its tetrahedral coordination in a glass melt formed from the glass composition. However, when the concentration of Al.sub.2O.sub.3 is balanced against the concentration of SiO.sub.2 and the concentration of alkaline earth oxides in the glass composition, Al.sub.2O.sub.3 can reduce the liquidus temperature of the glass melt, thereby enhancing the liquidus viscosity and improving the compatibility of the glass composition with certain forming processes such as the fusion forming process.

(13) In the embodiments described herein, the concentration of Al.sub.2O.sub.3 in the glass compositions is generally less than or equal to about 20 mol. % in order to achieve compositions having the desired liquidus temperature. For example, in some embodiments, the concentration of Al.sub.2O.sub.3 in the glass compositions is greater than or equal to about 10 mol. % and less than or equal to about 16 mol. %.

(14) The glass compositions described herein may optionally comprise one or more fining agents. The fining agents may comprise, for example, SnO.sub.2, As.sub.2O.sub.3, Sb.sub.2O.sub.3 and combinations thereof. The fining agents may be present in the glass compositions in an amount greater than or equal to about 0 mol. % and less than or equal to about 0.5 mol. %. In exemplary embodiments, the fining agent is SnO.sub.2. In these embodiments, SnO.sub.2 may be present in the glass composition in a concentration which is greater than about 0 mol. % and less than or equal to about 0.2 mol. % or even less than or equal to about 0.15 mol. %.

(15) In some embodiments described herein, the glass compositions may further comprise trace amounts of other oxides.

(16) In some embodiments described herein, the glass compositions are substantially free of heavy metals and compounds containing heavy metals. Glass compositions which are substantially free from heavy metals and compounds containing heavy metals may also be referred to as SuperGreen glass compositions. The term heavy metals, as used herein, refers to Ba, As, Sb, Cd, and Pb.

(17) The glass-ceramic compositions described herein have a liquidus viscosity which renders them suitable for use in a fusion draw process and, in particular, for use as a glass cladding composition in a fusion laminate process.

(18) While exemplary glass-ceramic compositions have been described hereinabove with reference to specific compositional ranges for various constituent components (such as SiO.sub.2, Al.sub.2O.sub.3, Na.sub.2O, and the like) of each glass-ceramic composition, it should be understood that each compositional range of each constituent component may include one or more narrower compositional ranges for that constituent component, as described above. Further, it should also be understood that these narrower ranges of the constituent components and/or the relationships between various constituent components may be incorporated in any of the embodiments of the glass-ceramic compositions described herein in order to produce a glass having the desired properties.

(19) Referring now to FIG. 1, the glass compositions described herein may be used to form an article, such as the laminated glass article 100 schematically depicted in cross section in FIG. 1. The laminated glass article 100 generally comprises a glass core layer 102 and a pair of glass cladding layers 104a, 104b. The glass-ceramic compositions described herein are particularly well suited for use as the glass claddings layers, as will be discussed in more detail herein.

(20) FIG. 1 illustrates the glass core layer 102 shown comprising a first surface 103a and a second surface 103b which is opposed to the first surface 103a. A first glass cladding layer 104a is fused directly to the first surface 103a of the glass core layer 102 and a second glass cladding layer 104b is fused directly to the second surface 103b of the glass core layer 102. Post-ceramming, the glass cladding layers 104a, 104b are fused to the glass core layer 102 without any additional materials, such as adhesives, polymer layers, coating layers or the like, being disposed between the glass core layer 102 and the glass cladding layers 104a, 104b. Thus, a first surface of the glass core layer is directly adjacent the first glass cladding layer, and a second surface of the glass core layer is directly adjacent the second glass cladding layer. In some embodiments, the glass core layer 102 and the glass cladding layers 104a, 104b are formed via a fusion lamination process. Diffusive layers (not shown) may form between the glass core layer 102 and the glass cladding layer 104a, or between the glass core layer 102 and the glass cladding layer 104b, or both.

(21) In at least some of the embodiments of the laminated glass article 100 described herein, the glass cladding layers 104a, 104b are formed from a first glass-ceramic composition having an average cladding coefficient of thermal expansion CTE.sub.clad and the glass core layer 102 is formed from a second, different glass composition which has an average coefficient of thermal expansion CTE.sub.core.

(22) Specifically, the glass articles 100 described herein may be formed by a fusion lamination process such as the process described in U.S. Pat. No. 4,214,886, which is incorporated herein by reference. Referring to FIG. 2 by way of example, a laminate fusion draw apparatus 200 for forming a laminated glass article comprises an upper isopipe 202 which is positioned over a lower isopipe 204. The upper isopipe 202 comprises a trough 210 into which a molten glass cladding composition 206 is fed from a melter (not shown). Similarly, the lower isopipe 204 comprises a trough 212 into which a molten glass core composition 208 is fed from a melter (not shown). In the embodiments described herein, the molten glass core composition 208 has an appropriately high liquidus viscosity to be run over the lower isopipe 204.

(23) As the molten glass core composition 208 fills the trough 212, it overflows the trough 212 and flows over the outer forming surfaces 216, 218 of the lower isopipe 204. The outer forming surfaces 216, 218 of the lower isopipe 204 converge at a root 220. Accordingly, the molten glass core composition 208 flowing over the outer forming surfaces 216, 218 rejoins at the root 220 of the lower isopipe 204 thereby forming a glass core layer 102 of a laminated glass structure.

(24) Simultaneously, the molten glass-ceramic cladding compositions 206 overflows the trough 210 formed in the upper isopipe 202 and flows over outer forming surfaces 222, 224 of the upper isopipe 202. The molten glass-ceramic cladding composition 206 has a lower liquidus viscosity requirement to be run on the upper isopipe 202, and will have a CTE either equal to or less than the glass core composition 208 (for example, within about 5107) when present as a glass. The molten glass-ceramic cladding composition 206 is outwardly deflected by the upper isopipe 202 such that the molten glass cladding composition 206 flows around the lower isopipe 204 and contacts the molten glass core composition 208 flowing over the outer forming surfaces 216, 218 of the lower isopipe, fusing to the molten glass core composition and forming pre-cerammed glass cladding layers 104a, 104b around the glass core layer 102.

(25) In some embodiments, in the laminated sheet so formed, the clad thickness will also be significantly thinner than the core glass thickness so that the clad goes into compression and the core into tension. But as the CTE difference is low, the magnitude of the tensile stress in the core will be very low (e.g on the order of 10 MPa or lower) which will allow for the production of a laminated sheet that will be relatively easy to cut off the draw due to its low levels of core tension. Sheets can thus be cut from the laminate structure that is drawn from the fusion draw apparatus, and after the sheets are cut, the cut product can then be subjected to a suitable ceramming process that will ceram the clad layers to appropriate depths and extents. The ceramming can be done either just by heating the laminate structure to an appropriate temperature, or by ion exchanging the clad at appropriate high temperatures. The glass-ceramic composition on the clad will then have a significantly lower CTE than the core and, after cool down, will develop significantly higher compressive stress. That is, the clad is comprised of a glass-ceramic composition that is cerammable to a lower CTE than the core. Thus, this process can reduce difficulties with cutting highly stressed laminate products on the draw tower. The process provides high compressive stress products without issues associated with cutting at or on the draw tower by separating the steps of forming the laminate structure and subsequently creating the appropriate levels of stress in desired parts of the structure, because of the glass-ceramic composition of the clad.

(26) While specific glass-ceramic compositions for use as the glass cladding layers 104a, 104b have been described herein, it should be understood that any of the glass-ceramic compositions described herein may be used to form the glass cladding layers 104a, 104b of the laminated glass article 100.

EXAMPLES

(27) The various embodiments of the glass compositions described herein will be further clarified by the following examples.

(28) Table 1 lists the compositions of inventive glass-ceramic compositions (i.e., Examples 1-6).

(29) TABLE-US-00001 TABLE 1 Exemplary Glass-Ceramic Compositions Oxide (mol %) 1 2 3 4 5 6 SiO.sub.2 64.48 71.49 69.39 64.48 71.49 69.39 Al.sub.2O.sub.3 15.74 12.98 14.06 15.13 11.94 12.70 Na.sub.2O 12.02 5.34 4.67 12.02 5.34 4.67 Li.sub.2O 2.49 5.56 6.67 2.49 5.56 6.67 Ti.sub.2O 5.26 4.63 5.22 5.26 4.63 5.22 CaO SrO MgO 0.62 1.04 1.35

(30) The laminated glass articles disclosed herein may be employed in a variety of consumer electronic devices including, without limitation, mobile telephones, personal music players, tablet computers, LCD and LED displays, automated teller machines and the like.

(31) In some embodiments, the laminated glass article may comprises one or more layers which are opaque, transparent or translucent, such as a clad derived from a glass-ceramic composition wherein the clad layer is opaque, transparent or translucent after ceramming. Furthermore, the use of glass-ceramics in sheet form can be utilized.

(32) Further, while specific reference has been made herein to the use of the glass compositions as cladding layers of a laminated glass article, it should be understood that the glass compositions may also be used to independently form glass articles (i.e., non-laminated glass articles), such as, for example, cover glasses for electronic devices, backplane glasses for display devices and other, similar glass articles.

(33) It will be apparent to those skilled in the art that various modifications and variations can be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Thus it is intended that the specification cover the modifications and variations of the various embodiments described herein provided such modification and variations come within the scope of the appended claims and their equivalents.