Method of welding overlapped portion, method of manufacturing overlap-welded member, overlap-welded member, and automotive part
10549388 ยท 2020-02-04
Assignee
Inventors
Cpc classification
Y10T428/12347
GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
B23K2103/08
PERFORMING OPERATIONS; TRANSPORTING
B23K11/166
PERFORMING OPERATIONS; TRANSPORTING
B23K11/115
PERFORMING OPERATIONS; TRANSPORTING
B23K2101/34
PERFORMING OPERATIONS; TRANSPORTING
B23K28/02
PERFORMING OPERATIONS; TRANSPORTING
B23K2103/50
PERFORMING OPERATIONS; TRANSPORTING
B23K26/32
PERFORMING OPERATIONS; TRANSPORTING
B23K11/16
PERFORMING OPERATIONS; TRANSPORTING
International classification
Abstract
A method of welding an overlapped portion according to the present invention in which a plurality of steel sheet members are joined at an overlapped portion, and at least one of the plurality of steel sheet members contains martensite, includes: forming a spot-welded portion having a nugget in the overlapped portion; and emitting a laser beam to form a melted and solidified portion crossing an end of the nugget and located between the nugget and a position externally spaced apart from an end of the nugget by not less than 3 mm, this melted and solidified portion being formed in the steel sheet member containing the martensite so as to have a depth of not less than 50% of the thickness of the steel sheet member containing the martensite at a position externally spaced apart from the end of the nugget by 1 mm.
Claims
1. A method of welding an overlapped portion in which a plurality of steel sheet members are joined at the overlapped portion, the method including: arranged an overlapped portion of the plurality of steel sheet members, wherein at least one of the plurality of steel sheet members contains martensite, and the plurality of steel sheet members comprise steel sheets in which a heat affected zone (HAZ) softened portion of which a hardness is less than a base material is scheduled to be formed by a spot welding, the method including; forming a spot-welded portion having a nugget in the overlapped portion; and reducing the area of a HAZ softening zone of the spot-welded portion by forming a melted and solidified portion crossing an end of the nugget, the melted and solidified portion being formed in the steel sheet member containing the martensite so as to have a depth of not less than 50% of a thickness of the steel sheet member containing the martensite at a position externally spaced apart from the end of the nugget by 1 mm, wherein forming the melted and solidified portion comprises: emitting a laser beam from a position which is located between the nugget and a position externally spaced apart from the end of the nugget by not less than 3 mm; emitting the laser beam to run in a direction along a longitudinal direction of the steel sheet member containing the martensite to intersect with the spot-welded portion such that direction of run of the laser beam crosses the end of the nugget so as to have an intersection angle within 30 with respect to an expected direction of stress.
2. A method of manufacturing an overlap-welded member, including: overlapping a plurality of steel sheet members at an overlapped portion; and performing a welding in accordance with the method of welding the overlapped portion according to claim 1.
3. An automotive part which includes the overlap-welded member according to claim 2.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1)
(2)
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
(14)
(15)
(16)
(17)
(18)
(19)
(20)
(21)
(22)
(23)
(24)
(25)
(26)
(27)
(28)
(29)
(30)
(31)
(32)
(33)
(34)
(35)
(36)
(37)
(38)
(39)
(40)
(41)
(42)
(43)
(44)
(45)
(46)
(47)
(48)
(49)
(50)
(51)
(52)
(53)
(54)
(55)
EMBODIMENTS OF THE INVENTION
(56) In order to solve the problems described above, the present inventors carried out a study of techniques of preventing fracture of a HAZ softening zone in a spot-welded portion in an overlapped portion in an overlap-welded member formed by joining together a plurality of steel sheet members.
(57) As a result, it was found that the strength of the spot-welded portion can be improved by emitting a laser beam onto the spot-welded portion to form a melted and solidified portion so as to cross an end of a nugget and range from the nugget up to the outside of the softest zone in a HAZ.
(58) The present invention is based on findings that, in the case where a plurality of steel sheet members are overlapped and joined through resistance spot welding, if at least one of the plurality of steel sheet members contains martensite, it is possible to make full use of the strength of a high-strength steel sheet or hot stamped member by emitting a laser beam onto an area ranging from a nugget of the spot-welded portion and crossing an end of the nugget to form a melted and solidified portion, whereby a HAZ softening zone in the spot-welded portion is hardened to prevent fractures in the HAZ.
(59) In this specification, the high-strength steel sheet containing martensite includes, for example, a steel sheet member (for example, press formed article) made out of a high-strength steel sheet of 980 MPa class, or a 1200 MPa class or higher, and a hot stamped member containing martensite generated through forming using hot stamping.
(60) Further, the present inventors found that, regardless of whether the steel sheet member made out of the high-strength steel sheet or the hot stamped member is contained, in the case where the plurality of steel sheet members are overlapped and joined through resistance spot welding, and laser beam is emitted onto the spot-welded portion to form the melted and solidified portion extending from the nugget to the outside of the nugget, if at least one of the steel sheet members is made out of a galvanized steel sheet having a hot-dip galvanneal coating or a hot-dip galvanizing coating formed thereon, it is significantly effective to form the melted and solidified portion in a manner such that the depth of the melted and solidified portion at a portion corresponding to a contacting surface of the spot-welded portion is shallower than a contacting surface having a hot-dip galvanneal coating or a hot-dip galvanizing coating formed thereon.
(61) Hereinbelow, the present invention made on the basis of the findings described above will be described with reference to the first embodiment and the second embodiment described below.
(62) First, the first embodiment according to the present invention will be described with reference to
(63) (First Embodiment)
(64)
(65)
(66) It should be noted that the flange 1 is formed by overlapping a flange 2F, which is a formed article (steel sheet member) 2 made out of a steel sheet, and a flange 3F, which is a formed article (steel sheet member) 3 made out of a steel sheet.
(67) In this first embodiment, either of or both of the steel sheets formed into the formed article 2 and the formed article 3 are:
(68) (a) a steel sheet member obtained by cold press forming a high-strength steel sheet (for example, high-strength steel sheet of 1200 MPa class or higher) containing martensite, or
(69) (b) a hot stamped member (for example, steel sheet member having a tensile strength of 1200 MPa or higher) having martensite generated as a result of forming a steel sheet for a hot stamped member using hot stamping.
(70) This means that at least one steel sheet member containing the martensite is included.
(71) When the overlapped portion of the steel sheet members obtained by forming the high-strength steel sheet or the steel sheet members made out of the hot stamped member is subjected to resistance spot welding, a HAZ softening zone is formed in the spot-welded portion.
(72) Due to this HAZ softening zone, the strength of the spot-welded portion is significantly lower than that of the high-strength steel sheet (base metal). However, through emission of a laser beam, the melted and solidified portion is formed.
(73) This makes it possible to harden the HAZ softening zone, and prevent fractures caused by stress concentration on the HAZ softening zone, whereby it is possible to make full use of the strength of the high-strength steel sheet or hot stamped member.
(74)
(75)
(76) It should be noted that, in
(77) It should be noted that, in this specification, the high-strength steel sheet includes an unformed high-strength steel sheet, a steel sheet member obtained by forming a high-strength steel sheet, and a hot stamped member obtained by forming a hot-stamping steel sheet through hot stamping.
(78) Further, the low-strength steel sheet includes an unformed low-strength steel sheet, and a steel sheet member obtained by forming a low-strength steel sheet member.
(79) Yet further, the steel sheet includes an unformed high-strength steel sheet, an unformed low-strength steel sheet, a steel sheet member obtained by forming a high-strength steel sheet, a hot stamped member obtained by forming a hot-stamping steel sheet through hot stamping, and a steel sheet member obtained by forming a low-strength steel sheet.
(80) In
(81) The melted and solidified portion 15 is formed, for example, so as to start from a distance of L1 externally away from one end of the nugget 12 through the nugget 12 to a distance of L2 externally away from the other end of the nugget.
(82) Further, the melted and solidified portion 15 is formed throughout the entire thickness t5 (100%) of the high-strength steel sheet 5H and further to a middle point in the thickness t6 of the high-strength steel sheet 6H in a direction from the high-strength steel sheet 5H toward the low-strength steel sheet 7L.
(83) Here, the end of the nugget 12 means the maximum shape (outer boundary) of the nugget 12 when the overlapped portion formed by overlapping a plurality of steel sheet members is viewed from the surface of the steel.
(84) The reference characters LD5 and LD6 in
(85) To prevent fractures in the HAZ softening zone, it is effective for the high-strength steel sheet to have the depth of the melted and solidified portion 1550% of the thickness (here, LD550% of t5 and LD650% of t6 for the high-strength steel sheets 5H, 6H, respectively).
(86) It should be noted that, in
(87) Thus, the effect can be sufficiently achieved by setting the depth LD6 of the melted and solidified portion 15 in the high-strength steel sheet 6H to be larger than or equal to 50% of the thickness t6.
(88) Here, the depth LD of the melted and solidified portion 15 is defined at the position externally spaced apart from the end of the nugget 12 by 1 mm. This is based on the fact that, as shown in
(89) It should be noted that
(90) Further, in the case where the melted and solidified portion 15 crosses two positions, it may be possible for these positions to be located on the same extended line and on both sides of the central portion of the nugget 12. However, the positions do not necessarily have to be located on the same extended line and at both sides of the central portion of the nugget 12.
(91) Further, in the case where the melted and solidified portion 15 is formed so as to cross two or more ends of the nugget 12, it is preferable that the depth LD of the melted and solidified portion 15 at a position externally spaced apart from the end of the nugget 12 by 1 mm satisfies LD50% of the thickness. However, it may be possible that a certain part of the melted and solidified portion 15 crossing the end of the nugget 12 does not satisfy LD(50% of the thickness).
(92) Further, it is preferable that the melted and solidified portion 15 is formed so as to extend from the end of the nugget 12 for a length of 3 mm or longer. However, the length may be 3 mm or shorter.
(93)
(94) More specifically,
(95)
(96) It should be noted that, for the purpose of explanation, the left half of the view in
(97) Further,
(98) The conventional spot-welded portion 10 is similar to that of the left half of
(99) This means that a large area of the HAZ softening zone 13 is pulled when tensile load is applied in the horizontal direction.
(100) This leads to a reduction in strength against tensile load, and fractures are more likely to occur resulting from tensile load.
(101) On the other hand, in the case where the melted and solidified portion 15 is formed between the nugget 12 and the HAZ softening zone 13 so as to cross the end of the nugget 12 by emission of a laser beam as shown in the right half of
(102) As a result, the strength of the spot-welded portion 10 improves, and the tensile strength improves.
(103) On the other hand, the melted and solidified portion 15 and a HAZ softening zone 15A are formed in a portion indicated by the broken line C in
(104) Next, an example of an effect obtained by the present invention will be described with reference to
(105)
(106)
(107)
(108) As shown in
(109) As described above, by forming the melted and solidified portion 15 so as to extend across the nugget 12 of the spot-welded portion 10 to obtain the configuration as shown in
(110) With this configuration, it is possible to improve deformability until fracture at the time when tensile load is received.
(111)
(112)
(113) In
(114) As shown in
(115) In the first example, the high-strength steel sheet 32H is the only high-strength steel sheet, and the melted and solidified portion 15 has the depth LD32 formed throughout the entire thickness of the high-strength steel sheet 32H in the thickness direction (LD32=(100% of the thickness t32)>(50% of the thickness t32)). Thus, it is possible to achieve sufficient effects.
(116)
(117) In
(118) As shown in
(119) In the second example, the high-strength steel sheet 31H and the high-strength steel sheet 32H are the high-strength steel sheets, and the melted and solidified portion 15 is formed throughout the entire thickness of the high-strength steel sheet 32H (LD32=(100% of the thickness t32)>(50% of the thickness t32)). Thus, by setting the depth LD31 in the high-strength steel sheet 31H to be LD31(50% of thickness t31), it is possible to achieve sufficient effects.
(120)
(121) In
(122) As shown in
(123) In the third example, the high-strength steel sheet 32H is the only high-strength steel sheet. Thus, by setting the depth LD32 of the melted and solidified portion 15 in the high-strength steel sheet 32H to be LD32(50% of the thickness t32), it is possible to achieve sufficient effects.
(124)
(125) In
(126) As shown in
(127) In the fourth example, the high-strength steel sheet 31H and the high-strength steel sheet 32H are the high-strength steel sheets. Thus, by setting the depth LD32 of the melted and solidified portion 15 in the high-strength steel sheet 32H to be LD32(50% of the thickness t32), it is possible to achieve sufficient effects.
(128) The first embodiment is directed to the overlap-welded member in which a plurality of steel sheet members are joined at the overlapped portion, and the steel sheet members, at least one of which steel sheet member contains the martensite, are joined through resistance spot welding.
(129) The first embodiment is applied to form various kinds of structures including, for example, a monocoque body constituting an automotive vehicle body, and an automotive part (assembly part) such as an A-pillar and a B-pillar constituting the monocoque body.
(130) The overlapped portion of the steel sheet member is usually a flange (overlapped portion) formed at the edge of each steel sheet as a tab for spot welding with another steel sheet. However, the overlapped portion is not limited to the flange. The overlapped portion may be one obtained by applying resistance spot welding to a portion where a flange overlaps with, for example, a shaped portion (portion other than the flange).
(131) Examples of the steel sheet member containing the martensite include a cold press-formed article made out of a high-strength steel sheet (for example, a high-tensile steel sheet having a tensile strength of 1200 MPa class or higher) having a quenched structure containing martensite formed through continuous annealing equipment, and a hot stamped member having a tensile strength of 1200 MPa or higher and strengthened by heating a steel sheet for hot stamping to austenite temperatures or higher, and quenching the steel sheet while forming it with water-cool die.
(132) The effects can be obtained if a high-strength steel sheet contains martensite posing a risk of fracture in spot welding due to softening of HAZ. However, the effects can be increased in the case of a high-strength steel sheet having a tensile strength of 1200 MPa or higher. Thus, it is preferable to set the lower limit of a tensile strength to 1200 MPa.
(133) Further, although setting the upper limit of a tensile strength is not necessary, the upper limit may be set to approximately 2000 MPa for practical consideration.
(134) Further, although setting limitation on the thickness of the steel sheet is not necessary, the lower limit of the thickness may be set to 0.7 mm for practical consideration, and it is preferable to set the upper limit to 2.6 mm.
(135) In the case of a cold rolled material, the high-strength steel sheet having a tensile strength of 1200 MPa or higher includes an uncoated steel sheet that does not have any coating on the surface thereof, and a steel sheet on which zinc-based coating, including hot-dip galvannealing (GA coating) and hot-dip galvanizing (GI coating), is formed.
(136) The hot stamped member includes an uncoated steel sheet member, an aluminized steel sheet member, a steel sheet having a coating of an intermetallic compound of iron and aluminum, and a steel sheet member having an iron-zinc solid solution layer and a zinc oxide layer coating thereon.
(137) The steel sheet to be overlapped with the high-strength steel sheet described above may be a high-strength steel sheet or hot stamped member having a tensile strength of 1200 MPa class or higher, or a steel sheet having a tensile strength of 270 MPa to 980 MPa classes.
(138) Further, the number of steel sheets to be overlapped is not limited to two, and three or more steel sheets may be overlapped.
(139) Below, resistance spot welding will be described in detail.
(140) During the resistance spot welding process, a plurality of steel sheet members are overlapped with each other, and resistance spot welding is applied to the overlapped portion, thereby forming a spot-welded portion having a nugget.
(141) Welding conditions for the resistance spot welding are not specifically limited, provided that a nugget with a nugget diameter of not less than 4t and not more than 7t (t: thickness (mm) on the thinner side in the overlapped surface) is formed at least in the steel sheet member to be joined depending on applications.
(142) For example, using a single-phase AC spot welding machine or inverter DC spot welding machine, it is only necessary to form the nugget described above in the overlapped portion, by employing the following conditions as appropriate: the diameter of the top end of a welding electrode: 6 mm to 8 mm; the radius of curvature R of the top end: 40 mm; squeezing force: 2.5 kN to 6.0 kN; electric current value of welding current: 7 kA to 11 kA; and power supply time in the range of 10/60 second to 40/60 second.
(143) It should be noted that the conditions for spot welding are not limited to those described above. The conditions may be set as appropriate depending on types of steel, thickness, or other parameters.
(144) The pitch for resistance spot welding is usually set in the range of approximately 20 mm to 60 mm. However, the pitch is not limited to this, and may be set as appropriate depending on a structure to be welded or portions of the structure to be welded.
(145) Below, formation of the melted and solidified portion through emission of a laser beam will be described in detail.
(146) In a process of forming a melted and solidified portion, a laser beam is emitted onto the overlapped portion to form the melted and solidified portion that crosses an end of the nugget and is located between the nugget of the spot-welded portion formed through resistance spot welding and the base material or HAZ located outside of the nugget.
(147) In other words, after resistance spot welding is applied, a laser beam is emitted onto the overlapped portion to form the melted and solidified portion so as to extend across the HAZ softening zone formed around the nugget, thereby hardening the HAZ softening zone.
(148) As a result, the melted and solidified portion divides the HAZ softening zone, whereby it is possible to suppress a reduction in the strength resulting from the HAZ softening zone in an expected direction of stress.
(149) Below, an example in which the present invention is applied to an automotive part will be described with reference to
(150)
(151)
(152) The B-pillar 41 has a flange on which a plurality of spot-welded portions 10 are formed along a direction in which the flange extends, and the melted and solidified portion 15 is formed through emission of a laser beam so as to extend across the plurality of spot-welded portions 10.
(153) Furthermore, for example, in the case of the B-pillar 41, it is preferable to set the expected direction of stress to a direction along an end surface of the steel sheet member of the flange (overlapped portion) of the B-pillar 41.
(154) Furthermore, the flange of the B-pillar 41 has a lower part curved in the front and rear direction of the vehicle body, and hence, it is preferable to set the expected direction of stress to a direction along the curved end surface of the steel sheet member of the flange (for example, a tangent direction at an end surface of the steel sheet member closest to each of the spot-welded portions 10).
(155) It should be noted that, as shown in
(156)
(157) Each of the A-pillar 40, the B-pillar 41, and the roof rail 42 has a plurality of spot-welded portions 10 formed along a direction in which the flange extends, and has the melted and solidified portion 15 formed with the emission of a laser beams so as to extend across the plurality of spot-welded portions 10.
(158) Further, as shown in
(159) It should be noted that, in the curved portions described above, it is preferable to set the expected direction of stress to a curved direction of the end surface of the steel sheet member of the flange as in the case shown in
(160) Further, it may be possible to form a plurality of melted and solidified portions 15, and it may be possible to employ a configuration in which not all the spot-welded portions are extended across by the melted and solidified portion 15.
(161)
(162) The side sill 43 has a flange on which a plurality of spot-welded portions 10 are formed along a direction in which the flange extends. Further, for example, the melted and solidified portion 15 extending across two adjacent spot-welded portions 10 is formed through emission of a laser beam in a manner such that the melted and solidified portion 15 is partially divided, and spaces are provided therebetween.
(163) As described above, by dividing the melted and solidified portion 15 and leaving the base metal, having no processing applied, between the melted and solidified portions 15, it is possible to achieve toughness that the high-strength steel sheet originally has.
(164) The same effect resulting from the spaces formed by dividing the melted and solidified portion 15 as described above can be obtained in the examples shown in
(165) By applying the present invention to the structural element disposed around the cabin as shown in
(166) Further, it is preferable that the melted and solidified portion 15 is formed so as to have intersection angle within 30 with respect to the expected direction of stress.
(167) Further,
(168) In the case of the bumper reinforce 44 shown in
(169) In the case of the bumper reinforce 44, a bending force acts in the front and rear direction, which intersects the longitudinal direction of the bumper reinforce 44, at the time of front-end collision or rear-end collision.
(170) For this reason, it is preferable to form the melted and solidified portion 15 by emitting a laser beam so as to intersect with the longitudinal direction of the bumper reinforce 44 at an intersection angle falling within 30 on the assumption that stress is expected to act in the longitudinal direction of the bumper reinforce 44.
(171) It should be noted that, in the case of a member that receives bending as a result of collision, the expected direction of stress is a direction along the end surface of the steel sheet member, and hence, the stress acts on the member in a direction perpendicular to a plane connecting the inside and the outside of the cabin.
(172) Next, examples of how the spot-welded portions and the melted and solidified portions are formed will be described with reference to
(173)
(174)
(175) It is desirable that the direction of the melted and solidified portion 15 formed be set so as to fall within angles of +30 with respect to the direction in which the flange (joint portion) 4 extends, or with respect to the expected direction of stress (with respect to the horizontal direction in
(176) It is more preferable to set the intersection angle so as to fall within 15.
(177) For example, the A-pillar, the B-pillar, the roof rail, the side sill, and the bumper reinforce as shown in
(178) In many cases, at the time of impact, tensile load acts in a direction along the end surface of the steel sheet member of the flange.
(179) For this reason, it is preferable to emit a laser beam so that the laser beam runs in a direction along the flange, thereby forming the melted and solidified portion 15 that extends across the nugget 12 of the spot-welded portion 10.
(180) Further, in the case of the inside of a long part, tensile load frequently acts in a direction along the longitudinal direction of the part. Thus, it is preferable to emit a laser beam so that the laser beam runs in the direction along the longitudinal direction of the part, thereby forming the melted and solidified portion 15 that extends across the nugget 12 of the spot-welded portion 10.
(181)
(182) For example, in general, tensile load acts in the longitudinal direction of a member, in the case where the spot-welded member 10 is used for an overlapped member 8 to partially reinforce a member 7 that is not joined in a form of flange as shown in
(183) Thus, it is preferable to emit a laser beam along the longitudinal direction of, for example, the member, thereby forming the melted and solidified portion 15.
(184)
(185) As shown in
(186)
(187) As shown in
(188) In such cases, it is preferable that the melted and solidified portion 15 intersects with the expected direction of stress at an intersection angle falling within 30.
(189)
(190) As shown in
(191) Further, a plurality of melted and solidified portions 15 (for example, two melted and solidified portions 15) may be formed for each of the spot-welded portions 10.
(192)
(193) As shown in
(194) However, it is desirable that the melted and solidified portion 15 exist on both sides of the nugget 12 of the spot-welded portion 10, and the distance of the shorter side between the end of the nugget and the end of the melted and solidified portion 15 is 3 mm or longer.
(195) This is because, by setting the distance between the end of the nugget and the end of the melted and solidified portion 15 to 3 mm or longer, it is possible to sufficiently prevent strain from concentrating on the HAZ softening zone.
(196) The melted and solidified portion 15 may extend across a plurality of spot-welded portions 10 as described above.
(197) There is no specific limitation on conditions for emission of a laser beam, and it is only necessary that predetermined melted and solidified portions 15 described above can be obtained at necessary locations.
(198) The laser welding device used includes, for example, a disk laser, a fiber laser, a direct-diode laser, a YAG laser, and a carbon dioxide laser. The beam diameter falls in a range of 0.15 mm to 0.9 mm; the output falls in a range of 1 kW to 10 kW; and welding speed falls in a range of 1 m/min to 15 m/min.
(199) Welding is performed using a general torch. Alternatively, it may be possible to use remote welding or laser seam stepper having a clamping device.
(200) Conditions for emission of a laser beam are not limited to those shown as an example, and any conditions for emission of a laser beam can be applied, provided that the predetermined melted and solidified portions 15 described above can be obtained.
(201) It is not necessary to emit laser beams onto all the spot-welded portions 10.
(202) It is only necessary to apply laser beams only to spot-welded portions 10 that are at risk of fracture due to collision in the HAZ softening zone of the spot-welded portion 10.
(203)
(204)
(205) The laser welded portion located between two adjacent spot-welded portions 10 as described above is desirable because it shortens intervals between welded portions and torsional rigidity of the member can be improved, even in the case where the overlapped portion is raised to form a gap, and joining cannot be sufficiently performed through spot welding.
(206)
(207) As shown in
(208)
(209)
(210) As shown in
(211)
(212) As shown in
(213) In the case where the melted and solidified portions 15 are formed so as to face opposite sides to each other with respect to the spot-welded portions 10 as described above, it may be possible to arrange, between the above-described melted and solidified portions 15, one or more spot-welded portions 10, one or more spot-welded portions 10 each having the melted and solidified portion 15 formed thereon, and/or one or more melted and solidified portions 15 (laser welded portions) that do not pass through any spot-welded portions 10.
(214)
(215) As shown in
(216) In the case where the melted and solidified portions 15 are formed so as to face the directions in which the melted and solidified portions 15 are brought closer to each other with respect to the spot-welded portions 10 as described above, it may be possible to arrange, between the above-described melted and solidified portions 15, one or more spot-welded portions 10, one or more spot-welded portions 10 each having the melted and solidified portion 15 formed thereon, and/or one or more melted and solidified portions 15 (laser welded portions) that do not pass through any spot-welded portion 10.
(217)
(218) As shown in
(219) In the case where the melted and solidified portions 15 are formed on the same side of the spot-welded portions 10 as described above, it may be possible to arrange, between the above-described melted and solidified portions 15, one or more spot-welded portions 10, one or more spot-welded portions 10 each having the melted and solidified portion 15 formed thereon, and/or one or more melted and solidified portions 15 (laser welded portions) that do not pass through any spot-welded portion 10.
(220) The resistance spot welding and the formation of the melted and solidified portion 15 to the nugget 12 of the spot-welded portion 10 according to the present invention can be applied, for example, to a process of welding vehicle bodies in the automobile manufacturing processes.
(221) During an assembly-line operation such as welding of vehicle body, it is preferable to first position and clamp an overlap-welded member to apply resistance spot welding, and then, apply additional welding through resistance spot welding or emit a laser beam, because it is possible to prevent a laser beam emission onto the spot-welded portion from positionally shifting due to repositioning or re-clamping.
(222) Further, more preferably, it is preferable to apply a laser beam emission in the same station as the resistance spot welding is applied.
(223) Next, with reference to
(224)
(225)
(226) In this case, the depth LD61 of the melted and solidified portion 15 in the high-strength steel sheet 61H is 100% of the thickness of the high-strength steel sheet 61H.
(227)
(228) In this case, the depth LD61 of the melted and solidified portion 15 in the high-strength steel sheet 61H is 100% of the thickness of the high-strength steel sheet 61H.
(229)
(230) In this case, it is preferable to set the depth LD61 of the melted and solidified portion 15 in the high-strength steel sheet 61H to be more than or equal to 50% of the thickness thereof.
(231)
(232) In this case, the depth LD61 of the melted and solidified portion 15 in the high-strength steel sheet 61H is 100% of the thickness of the high-strength steel sheet 61H.
(233) As shown in
(234)
(235)
(236) This case is preferable because the melted and solidified portion 15 is formed to be 100% in terms of thickness of the low-strength steel sheet 61L, the high-strength steel sheet 62H, and the low-strength steel sheet 63L, and the depth LD62 of the melted and solidified portion 15 in the high-strength steel sheet 62H is 50% or more of the thickness.
(237)
(238) In this case, as shown in
(239) It is preferable to set the depth LD62 of the melted and solidified portion 15 in the high-strength steel sheet 62H to be more than or equal to 50% of the thickness of the high-strength steel sheet 62H.
(240) (Second Embodiment)
(241) Next, the second embodiment according to the present invention will be described.
(242) The first embodiment described above relates to a case where the steel sheet is an uncoated steel sheet. However, it was found that, in the case where steel sheets having GA coating or GI coating, which is a typical zinc-coated steel sheet, are combined, hole defects may occur in the spot-welded portion 10, by forming the spot-welded portion 10 through resistance spot welding, and emitting a laser beam LB onto the spot-welded portion 10.
(243) Below, with reference to
(244)
(245) In the case of uncoated steel sheets, no hole defect occurs as shown in
(246) On the other hand,
(247) It was found that, in the case of a hot-dip galvannealing steel sheet, a hole defect 15H may occur in the melted and solidified portion as shown in
(248) The present inventors made thorough investigations on causes of occurrence of the hole defect 15H shown in
(249) The contact portion 16 shown in
(250) It is assumed that the hole defect 15H is created in a manner such that, when a laser beam LB is emitted to form the melted and solidified portion 15, the contact portion 16 having the zinc-coating formed thereon is molten through emission of a laser beam LB, zinc is explosively vaporized, and molten steel is blown away.
(251) The second embodiment is directed to joining steel sheet members including galvanized steel sheets having a hot-dip galvanneal coating or a hot-dip galvanizing coating formed thereon.
(252) The present inventors carried out a study of the problems described above. As a result, they found that, in the case where the steel sheets including these GA coating or GI coating are contained, it is possible to obtain a favorable welded joint that does not have any hole defect 15H, by controlling the depth of the melted and solidified portion 15 formed through emission of a laser beam LB in a manner that does not melt the contact portion 16 of spot welding on a surface overlapped with GA coating or GI coating.
(253) It should be noted that, in the case of an uncoated steel sheet, an aluminized steel sheet, a steel sheet having a coating of an intermetallic compound of iron and aluminum, and a steel sheet having an iron-zinc solid solution layer and a zinc oxide phase coating thereon, a boiling point of the coating is high, and hence, it is less likely that welding defects occur resulting from the coating on the overlapped surface.
(254) Further, it is preferable to set the depth LD of the melted and solidified portion 15 at a position located outside of the melted and solidified portion 15 and spaced apart from the end of the nugget 12 of the spot-welded portion 10 by 1 mm, to be more than or equal to 50% of the thickness of the high-strength steel sheet.
(255) In the second embodiment, it may be possible to arbitrarily choose whether the plurality of steel sheet members include, for example, steel sheet or hot stamped member having martensite, particularly whether the plurality of steel sheet members include a high-strength steel sheet having a tensile strength of 1200 MPa or higher. Further, it may be possible to employ a configuration in which no high-strength steel sheet is included.
(256) Further, it may be possible to combine steel sheet members made out of an uncoated steel sheet, an aluminized steel sheet, a steel sheet having a coating of an intermetallic compound of iron and aluminum, and/or a steel sheet having an iron-zinc solid solution layer and a zinc oxide phase coating thereon.
(257) Further, in the second embodiment, the plurality of steel sheet members are overlapped with each other, a spot-welded portion 10 having a nugget 12 is formed through resistance spot welding, and a laser beam LB is emitted, thereby forming a melted and solidified portion 15 that extends across the nugget 12, for example, in a manner such that the melted and solidified portion 15 crossing the end of the nugget 12 extends from the end of the nugget 12 to a position distanced not less than 3 mm from the end of the melted and solidified portion 15, this end of which is located outside of the nugget.
(258) First, in the case where the overlapped steel sheet member onto which a laser beam is emitted is a steel sheet member only formed by any of an uncoated steel sheet, an aluminized steel sheet, a steel sheet having a coating of an intermetallic compound of iron and aluminum, and a steel sheet having an iron-zinc solid solution layer and a zinc oxide phase coating thereon, the hardness of the softest zone in HAZ can be improved by forming the melted and solidified portion 15 through the emission of a laser beam with the depth LD of the melted and solidified portion 15 at a position externally spaced apart from the end of the nugget 12 by 1 mm being set to be more than or equal to 50% of each of the thicknesses of all the high-strength steel sheet.
(259) The upper limit of the depth LD of the melted and solidified portion 15 formed is 100% of the thickness of the high-strength steel sheet. It is preferable to set the depth LD of the melted and solidified portion 15 formed, to be more than or equal to 50% of the thickness, because the effect of preventing fractures in the HAZ softening zone can be sufficiently achieved with this dept. However, it may be possible to set the depth LD of the melted and solidified portion 15 to be less than 50% of the thickness.
(260) Below, descriptions will be specifically made with reference to
(261)
(262)
(263) In
(264) It should be noted that it is preferable to set the depth LD92 of the melted and solidified portion 15 in the high-strength steel sheet 92H at a position externally spaced apart from the end of the nugget 12 of the spot-welded portion 10 by 1 mm, to be more than or equal to 50% of the thickness.
(265)
(266) In this case, after spot welding, a laser beam LB is emitted from the side of the uncoated inner panel (low-strength steel sheet 93L) to be disposed on the inside of the cabin of the automobile body, thereby forming the melted and solidified portion 15 in the low-strength steel sheet 93L and the high-strength steel sheet 92H.
(267) The melted and solidified portion 15 is formed by controlling such that the melted and solidified portion 15 does not reach the contact portion 16 located on the side of the surface where the low-strength steel sheet 91LZ and the high-strength steel sheet 92H are overlapped, and the contact portion 16, where the hot-dip galvanneal coating lies, is not molten.
(268) It should be noted that it is preferable to set the depth LD92 of the melted and solidified portion 15 in the high-strength steel sheet 92H at a position externally spaced apart from the end of the nugget 12 of the spot-welded portion 10 by 1 mm, to be more than or equal to 50% of the thickness.
(269) It should be noted that, in the case where a hot stamped member having an iron-zinc solid solution layer and a zinc oxide layer coating thereon or a hot stamped member 92HP having an intermetallic compound of iron and aluminum coating thereon is used in place of the high-strength steel sheet 92H, which is a reinforce, it may be possible to treat them as is the case with the uncoated hot stamped member.
(270) This is because the welding defects are less likely to occur in these surface coating, as is the case with GA coating or GI coating.
(271)
(272) In this case, after spot welding, a laser beam LB is emitted from the side of the uncoated inner panel (low-strength steel sheet 93L) to be disposed on the inside of the cabin of the automobile body, thereby forming the melted and solidified portion 15 in the low-strength steel sheet 93L and the high-strength steel sheet 92HR having a surface containing an iron-zinc solid solution phase and a zinc oxide layer.
(273) The melted and solidified portion 15 is formed by controlling such that the melted and solidified portion 15 does not reach the contact portion 16 on the side of the surface where the low-strength steel sheet 91LZ and the high-strength steel sheet 92HR having a surface containing an iron-zinc solid solution phase and a zinc oxide layer are overlapped, and the contact portion 16, where the hot-dip galvanneal coating lies, is not molten.
(274) It should be noted that it is preferable that the depth LD92 of the melted and solidified portion 15 in the high-strength steel sheet 92HR having a surface containing an iron-zinc solid solution phase and a zinc oxide layer is set at a position externally spaced apart from the end of the nugget 12 of the spot-welded portion 10 by 1 mm, to be more than or equal to 50% of the thickness.
(275)
(276) In this case, after spot welding, a laser beam LB is emitted from the side of the uncoated inner panel (high-strength steel sheet 93H) to be disposed on the inside of the cabin of the automobile body, thereby forming the melted and solidified portion 15 in the high-strength steel sheet 93H and the high-strength steel sheet 92H.
(277) The melted and solidified portion 15 is formed by controlling such that the melted and solidified portion 15 does not reach the contact portion 16 on the side of the surface where the low-strength steel sheet 91LZ and the high-strength steel sheet 92H are overlapped, and the contact portion 16, where the hot-dip galvanneal coating lies, is not molten.
(278) It should be noted that it is preferable to set the depth LD92 of the melted and solidified portion 15 in the high-strength steel sheet 92H at a position externally spaced apart from the end of the nugget 12 of the spot-welded portion 10 by 1 mm, to be more than or equal to 50% of the thickness.
(279)
(280) In this case, after spot welding, a laser beam LB is emitted from the side of the uncoated inner panel (high-strength steel sheet 93H) to be disposed on the inside of the cabin of the automobile body, and control is performed so as not to reach the contact portion 16 on the side of the surface where the low-strength steel sheet 91LZ and the low-strength steel sheet 92L are overlapped.
(281) It may be possible that the formation is performed so as not to reach the contact portion 16 on the side of the surface where the low-strength steel sheet 91LZ and the low-strength steel sheet 92L are overlapped as shown in
(282) It should be noted that, in
(283) The welded joint according to the present invention described above is suitable to be used in structural elements of automobiles made out of a high-strength steel sheet having a tensile strength of 1200 MPa or higher.
(284) The welded joint can be applied, for example, to a bumper, a door beam, a floor member, a front-side member, and a rear-side member.
(285) It should be noted that the present invention is not limited to the embodiments described above, and various modifications may be possible without departing from the scope of the present invention.
(286) In the embodiments described above, the present invention is applied, as an example, to an automotive part. However, the present invention can be applied to various over-welded members formed by joining overlapped portions through spot welding, for example, in fittings, beams, and link members of a building, or in a simple warehouse, furniture, and office furniture.
(287) Further, in the embodiments described above, for example, the targets are set to the high-strength steel sheet or the hot stamped member having a tensile strength of 1200 MPa or higher. However, the present invention can be applied to a high-strength steel sheet having a tensile strength of less than 1200 MPa and having a hardness in the HAZ softening zone less than the base material due to containing a quenched structure (martensite) such as a high-strength steel sheet of 980 MPa class.
(288) Descriptions have been made of a case where two or three high-strength steel sheets are used as a steel sheet member made out of a plurality of steel sheets. However, four or more steel sheet members may be used.
(289) Further, the plurality of steel sheets including a high-strength steel sheet means that it is only necessary that, of the plurality of steel sheets, at least one steel sheet is the high-strength steel sheet.
(290) Further, in the present invention, it may be possible to form the overlapped portion by the plurality of steel sheets overlapping each other in a manner such that a member used for partial reinforcement is joined without using a flange as shown in
EXAMPLES
(291) The present invention will be described in more detail with reference to Examples.
(292) Table 1 shows chemical components of samples. The unit in Table 1 is mass %, and the balance other than the chemical components indicated in Table 1 includes Fe and inevitable impurities.
(293) TABLE-US-00001 TABLE 1 Composition (mass %) Sample C Si Mn P S Other SQ1500 0.21 0.22 1.25 0.010 0.001 0.20Cr, 0.020Ti, 0.0015B SQZ1500 0.21 0.04 1.30 0.010 0.001 0.20Cr, 0.021Ti, 0.0016B SQ1800 0.30 0.20 1.69 0.010 0.001 0.23Cr, 0.021Ti, 0.08Nb, 0.0020B JSC1270 0.14 0.49 1.85 0.007 0.004 0.05Ti JSC440 0.11 0.07 1.10 0.021 0.003 JAC440 0.11 0.06 1.09 0.019 0.003 JSC590 0.08 0.03 2.30 0.015 0.003
(294) In Table 1, the sample SQ1500 is an uncoated steel sheet for hot stamping having a tensile strength of 1500 MPa class.
(295) The sample SQZ1500 is a steel sheet for hot stamping having an iron-zinc solid solution layer and a zinc oxide layer coating thereon and having a tensile strength of 1500 MPa class.
(296) The sample SQ1800 is an uncoated steel sheet for hot stamping having a tensile strength of 1800 MPa class.
(297) The sample JSC1270 is an uncoated cold-rolled steel sheet having a tensile strength of 1270 MPa class.
(298) Further, the sample JSC440 is an uncoated steel sheet of 440 MPa class.
(299) The sample JAC440 is a steel sheet of 440 MPa class having hot-dip galvannealing applied thereon.
(300) The sample JSC590 is an uncoated steel sheet of 590 MPa class.
(301) It should be noted that the steel sheets for hot stamping are used by applying similar processing to hot stamping.
Example 1
(302) Below, Example 1 will be described with reference to
(303) In Example 1, strain at the time of tensile testing was evaluated in the case where two uncoated steel sheets were overlapped.
(304)
(305) In Example 1, test pieces S10 as shown in
(306) In the tensile testing, the strain was measured until each of the test pieces S10 fractured, and the strain was evaluated according to four grades.
(307) In the case of the test piece S10, two steel sheets, which were a steel sheet S11 made out of a sample 1 and a steel sheet S12 made out of a sample 2, were overlapped as shown in
(308) Then, a laser beam was emitted from the side of the steel sheet S11 thereby forming a melted and solidified portion 15.
(309) In the tensile testing, the steel sheet S11 made out of the sample 1 of the test piece S10 was pulled, whereby a tensile strength of the sample 1 was measured.
(310) It should be noted that test pieces 1 and 12 shown in Table 2 are Comparative Examples, onto which no laser beam was emitted.
(311) Spot welding was applied using a single-phase AC spot welding machine and using a DR-type electrode (top end 6 mm R40) under the following conditions.
(312) Squeezing force: 400 kgf
(313) Welding time: 20 cyc
(314) Welding current: splash occurring current 0.5 kA
(315) The diameter (mm) of a nugget was set in the rage of 5t to 6t (t: thickness (mm))
(316) Then, a laser beam was emitted onto the test piece S10 having the spot-welded portion 10 formed therein under conditions shown in Table 2, thereby forming a melted and solidified portion 15 having a straight shape.
(317) Laser beam was emitted using Nd: YAG laser under the following conditions.
(318) Beam diameter: 0.6 (mm),
(319) Speed: 2.0 to 4.0 (m/min),
(320) Shielding gas: argon 10 (1/min)
(321) In order to vary the depth of the melted and solidified portion 15, the output was varied in a range of 1.5 kW to 4 kW.
(322) The intersection angle () with the expected direction of stress for the melted and solidified portion 15 formed through emission of a laser beam or a direction along a flange (overlapped portion), the depth (%) of the melted and solidified portion 15, and the distance L (mm) from the end of the nugget 12 to the end of the melted and solidified portion 15 in
(323) It should be noted that the depth (%) of the melted and solidified portion was calculated on the basis of the steel sheet S11 in a manner such that a depth (mm) of the melted and solidified portion was measured at a position spaced apart from the end of the nugget in the spot-welded portion by 1 mm, and the measured value was divided by the thickness of the steel sheet S11.
(324) Next, tensile testing was performed for each of the test pieces.
(325) In the tensile testing, strain until each of the test pieces fractured was measured by setting the gauge length to 50 mm, and fixing the tensile rate to 3 (mm/min).
(326) (D) represents the strain until fracture being less than 3%, (C) represents the strain until fracture being not less than 3% and less than 3.5%, (B) represents the strain until fracture being not less than 3.5% and less than 4%, and (A) represents the strain until fracture being not less than 4%.
(327) Table 2 shows the test results.
(328) TABLE-US-00002 TABLE 2 Intersection Depth (%) Length (mm) angle () of of melted of melted Results of melted and and solidified and solidified tensile Number Sample 1 Sample 2 solidified portion portion portion testing Note 1 SQ1500-1.6t JSC440-1.6t Only spot welding C Comparative Example 2 SQ1500-1.6t JSC440-1.6t 0 100 10 A Example according to the present invention 3 SQ1500-1.6t JSC440-1.6t 15 100 10 A Example according to the present invention 4 SQ1500-1.6t JSC440-1.6t 30 100 10 A Example according to the present invention 5 SQ1500-1.6t JSC440-1.6t 45 100 10 C Comparative Example 6 SQ1500-1.6t JSC440-1.6t 0 20 10 B Comparative Example 7 SQ1500-1.6t JSC440-1.6t 0 50 10 A Example according to the present invention 8 SQ1500-1.6t JSC440-1.6t 0 80 10 A Example according to the present invention 9 SQ1500-1.6t JSC440-1.6t 0 100 2 C Comparative Example 10 SQ1500-1.6t JSC440-1.6t 0 100 3 A Example according to the present invention 11 SQ1500-1.6t JSC440-1.6t 0 100 20 A Example according to the present invention 12 JSC1270-1.6t JSC440-1.6t Only spot welding B Comparative Example 13 JSC1270-1.6t JSC440-1.6t 0 100 10 A Example according to the present invention 14 SQZ1500-1.6t JSC440-1.6t 0 100 10 A Example according to the present invention 15 SQ1800-1.6t JSC440-1.6t 0 100 10 A Example according to the present invention 16 SQ1500-1.6t SQ1500-l.6t 0 100 10 A Example according to the present invention 17 SQ1500-1.6t SQ1500-1.2t 0 100 10 A Example according to the present invention 18 SQ1500-1.6t JAC440-1.6t 0 80 10 A Example according to the present invention
(329) As shown in Table 2, Comparative Examples indicated as numbers 6 and 12 exhibited fracture strain in a range of not less than 3.5% and less than 4%, and hence, the test result thereof falls in (B).
(330) Further, Comparative Examples indicated as numbers 1, 5, and 9 fractured in a HAZ softening zone of the spot-welded portion with small strain, and exhibited fracture strain less than 3.5%, and hence, the test result thereof falls in (C).
(331) On the other hand, all of the test pieces of Examples according to the present invention exhibited fracture strain more than or equal to 4%.
Example 2
(332) Below, Example 2 will be described with reference to
(333) Table 3.
(334) In Example 2, the strain was evaluated through tensile testing in the case where three uncoated steel sheets were overlapped.
(335)
(336) In Example 2, test pieces S20 as shown in
(337) In the tensile testing, strain until each of the test pieces S20 fractures was measured, and the strain was evaluated according to four grades.
(338) In the case of the test piece S20, three steel sheets, which were a steel sheet S21 made out of a sample 1, a steel sheet S22 made out of a sample 2, and a steel sheet S23 made out of a sample 3, were overlapped as shown in
(339) Then, a laser beam is emitted from the side of the steel sheet S23, thereby forming a melted and solidified portion 15.
(340) In the tensile testing, the steel sheet S22 made out of the sample 2 of the test piece S20 was pulled, whereby a tensile strength of the sample 2 was measured.
(341) It should be noted that a test piece with number 1 shown in Table 3 is the Comparative Example, onto which no laser beam was emitted.
(342) Further, a test piece with number 4 is the Comparative Example, onto which a laser beam was emitted to reach a contact portion where zinc coating was formed.
(343) The test piece S20 was created by applying resistance spot welding and emitting a laser beam onto the spot-welded portion 10 in a similar manner to that in Example 1, and hence, explanation thereof will not be repeated.
(344) The intersection angle () with the expected direction of stress for the melted and solidified portion 15 formed through emission of a laser beam or a direction along a flange (overlapped portion), the depth (%) of the melted and solidified portion 15, and the distance L (mm) from the end of the nugget 12 to the end of the melted and solidified portion 15 in
(345) It should be noted that the depth (%) of the melted and solidified portion was calculated on the basis of the steel sheet S22 made out of a high-strength steel sheet in a manner such that a depth (mm) of the melted and solidified portion was measured at a position spaced apart from the end of the nugget in the spot-welded portion by 1 mm, and the measured value was divided by the thickness of the steel sheet S22.
(346) In Example 2, each of the test pieces was subjected to tensile testing and evaluation in a similar manner to that in Example 2, and hence, explanation thereof will not be repeated here.
(347) TABLE-US-00003 TABLE 3 Intersection Depth (%) of Length (mm) of angle () melted and melted and Results of of melted and solidified solidified tensile Number Sample 1 Sample 2 Sample 3 solidified portion portion portion testing Note 1 JAC270D-0.7t SQZ1500-1.6t JSC440-1.2t Only spot welding C Comparative Example 2 JAC270D-0.7t SQZ1500-1.6t JSC440-1.2t 0 70 12 A Example according to the present 3 JAC270D-0.7t SQZ1500-1.6t JSC590-1.2t 0 70 12 A Example according to the present 4 JAC270D-0.7t SQZ1500-1.2t JSC440-1.4t 0 100 12 C Comparative Example 5 JAC270D-0.7t SQ1800-1.6t JSC590-1.2t 0 70 12 A Example according to the present 6 JAC270D-0.7t SQ1800-1.8t JSC590-1.2t 0 80 12 A Example according to the present
(348) As shown in Table 3, Comparative Example indicated as number 1 fractured in a HAZ softening zone of the spot-welded portion with small strain, and exhibited fracture strain less than 3.5%, and hence, the test result thereof falls in (C).
(349) Further, Comparative Example indicated as number 4 had a hole defect, and the test result thereof falls in (C).
(350) On the other hand, all of the test pieces of Examples according to the present invention exhibited fracture strain more than or equal to 4%.
Example 3
(351) Below, Example 3 will be described with reference to Table 4.
(352) In Example 3, using the test piece S10 shown in
(353) In Example 3, a steel sheet S11 is made out of an uncoated steel sheet SQ1500 for hot stamping having a tensile strength of 1500 MPa class, and a steel sheet S12 is made out of a steel sheet SQZ1500 for hot stamping having a tensile strength of 1500 MPa class and having an iron-zinc solid solution layer and a zinc oxide layer coating thereon, or a hot-dip galvannealed steel sheet of 440 MPa class.
(354) Table 4 shows a sample 1 for the steel sheet S11, a sample 2 for the steel sheet S12, and test results.
(355) (Judgment A) means that no hole defect exists, and (Judgment C) means that at least one hole defect exists.
(356) TABLE-US-00004 TABLE 4 Depth (%) of melted and solidified Hole Number Sample 1 Sample 2 portion defect Note 1 SQ1500-1.6t JAC440-1.6t 100 C Comparative Example 2 SQ1500-1.6t SQZ1500- 100 A Example 1.6t according to the present invention 3 SQ1500-1.6t JAC440-1.6t 50 A Example according to the present invention 4 SQ1500-1.6t JAC440-1.6t 80 A Example according to the present invention
(357) As shown in Table 4, Comparative Example indicated as number 1 had the hole defect, since the melted and solidified portion formed through a laser beam emitted from the side of the steel sheet S11 is formed throughout the entire thickness of the steel sheet S11 and reaches the steel sheet S12.
(358) Thus, the test result indicates that the hole defect exists (Judgment C).
(359) In the case of Examples according to the present invention indicated as number 2 and number 3, no hole defect was found (Judgment A), since the depths of the melted and solidified portions were 80% and 50% of the thickness, and each of the melted and solidified portions does not reach the contact portion between the steel sheet S11 and the steel sheet S12.
(360) Further, in the case of the steel sheet SQZ1500 for hot stamping indicated as number 4, which has a tensile strength of 1500 MPa class and has an iron-zinc solid solution layer and a zinc oxide layer coating thereon, the melted and solidified portion was formed throughout the entire thickness of the steel sheet S11. However, in the contact portion, zinc did not explosively vaporize, and the molten steel was not blown away. Thus, no hole defect was found.
INDUSTRIAL APPLICABILITY
(361) According to the method of welding an overlapped portion, the method of manufacturing an overlap-welded member, the overlap-welded member and the automotive part of the present invention, it is possible to prevent the spot-welded portion in the overlapped portion from fracturing in HAZ softening zone. Thus, the method of welding an overlapped portion, the method of manufacturing an overlap-welded member, the overlap-welded member and the automotive part of the present invention are industrially applicable.
BRIEF DESCRIPTION OF THE REFERENCE SYMBOLS
(362) LB laser beam
(363) 1, 4, 4A Flange (overlapped portion)
(364) 2, 3 Formed article (steel sheet member)
(365) 5H, 6H, 31H, 32H, 61H, 62H, 92H, 93H High-strength steel sheet (steel sheet member)
(366) 7L, 31L, 33L, 61L, 62L, 63L, 92L, 93L Low-strength steel sheet (steel sheet member)
(367) 16 Contact portion
(368) 7 Member (steel sheet member)
(369) 8 Overlapped member (steel sheet member)
(370) 10 Spot-welded portion
(371) 12 Nugget
(372) 13 HAZ softening zone
(373) 15 Melted and solidified portion
(374) 40 A-pillar (steel sheet member)
(375) 41 B-pillar (steel sheet member)
(376) 42 Roof rail (steel sheet member)
(377) 43 Side sill (steel sheet member)
(378) 44 Bumper reinforce (steel sheet member)
(379) 45 Bulkhead (steel sheet member)
(380) 91LZ Hot-dip galvannealed low-strength steel sheet (steel sheet member)
(381) 92HR High-strength steel sheet (high-strength steel sheet having a surface containing an iron-zinc solid solution phase and a zinc oxide layer) (steel sheet member)
(382) 92HP High-strength steel sheet (hot stamped member having an iron-zinc solid solution layer and a zinc oxide layer coating thereon, or hot stamped member having an intermetallic compound of iron and aluminum coating thereon) (steel sheet member)