Two-way shape memory polymer composite material and preparation method thereof

Abstract

A two-way shape memory polymer composite material is provided, which comprises two interpenetrating network polymers, wherein one polymer is a shape memory polymer made of crystalline cross-linked polymer, the other one is a cross-linked elastomeric material. The composite material is formed by interpenetration of two network polymers, wherein one network polymer will shrink under heating and the other network polymer acts as the segment for energy storage. When the first polymer network shrinks under heating, it presses the second polymer network, while the heating is cancelled the pressed second polymer network will enforce the first polymer network to recover the original shape, therefore it has the behavior of two-way shape memory.

Claims

1. A polymer composite material with two-way shape memory, comprising: a first polymer network formed of a crystalline cross-linked polymer as a shape memory polymer, and a second polymer network formed of a cross-linked elastomeric material; wherein the first polymer network and the second polymer network interpenetrate with each other to form an interpenetrating structure, and wherein the first polymer network and the second polymer network within the interpenetrating structure have been cross-linked independently of each other; wherein the first polymer network acts as a shape memory shrinkage segment which is capable of shrinking from an original state upon heating to a first temperature higher than a transition temperature and reverting to the original state when the temperature is cooled to a second temperature lower than the transition temperature, and the second polymer network acts as an energy storage segment.

2. The polymer composite material of claim 1, wherein the hardness and/or modulus of the cross-linked elastomeric material are/is between that of rubber and plastics.

3. The polymer composite material of claim 2, wherein the cross-linked elastomeric material is one or more selected from the group consisting of polyurethane elastomer resin, SBS resin, propylene-butene copolymer, hard rubber.

4. The polymer composite material of claim 1, wherein a raw material of the first polymer network is a polymer containing crystalline polymer segment, and a raw material of the second polymer network is an elastomeric polymer material.

5. The polymer composite material of claim 4, wherein the crystalline polymer segment is polyester, polyether or polyolefin.

6. The polymer composite material of claim 4, wherein the polymer containing crystalline polymer segment and the elastomeric polymer material are respectively crosslinked to form the first polymer network and the second polymer network.

7. The polymer composite material of claim 1, wherein the crystalline cross-linked polymer is one or more selected from the group consisting of polyurethane, polyethylene, and polynorbonene.

8. A method for preparing the polymer composite material of claim 1, wherein the method comprises: obtaining a polymer containing crystalline polymer segment; obtaining a elastomeric material polymer; blending the polymer containing crystalline polymer segment and the elastomeric material polymer to obtain a mixture, and cross-linking the polymer of the crystalline polymer segment in the mixture by means of a first stimulation; stretching the obtained mixture and fixing it, then cross-linking the elastomeric material polymer by means of a second stimulation to obtain the two-way shape memory polymer composite material, wherein the first stimulation and the second stimulation are different with each other or the first stimulation and the second stimulation have the same type but with different intensity.

9. The method of claim 8, wherein the crystalline polymer segment is polyester, polyether or polyolefin.

10. The method of claim 8, wherein the first stimulation is UV stimulation, and the second stimulation is thermal stimulation.

11. The method of claim 8, wherein the method further comprises: after the two-way shape memory polymer composite material is produced, shaping the two-way shape memory polymer composite material to a membrane, form, fiber, or block.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) The present application will be described in detail in the following description with reference to the accompanying drawings and specific examples, of which:

(2) FIG. 1 shows the molecular structure in the mixture prepared by the manufacture method of two-way shape memory polymer material according to one embodiment of the present invention.

(3) FIG. 2 shows the molecular structure of the cross-linked polymer in the mixture after the first stimulation.

(4) FIG. 3 shows the molecular structure of the cross-linked polymer after stretched.

(5) FIG. 4 shows the molecular structure of the interpenetrated network of the two-way shape memory polymer composite material obtained by the second stimulation to the mixture.

DETAILED DESCRIPTION OF THE INVENTION

(6) Objects, advantages and embodiments of the present application will be explained below in detail with reference to the accompanying drawings and examples. However it should be appreciated that the following description of the example is merely exemplary in nature and is not intended to limit this application.

(7) A polymer composite material with two-way shape memory comprising two interpenetrating polymer networks is provided, wherein a first shape memory polymer network is made of crystalline cross-linked polymer as a shape memory polymer and a second polymer network is made of a cross-linked elastomeric material.

(8) According to one embodiment of the present invention, the crystalline cross-linked polymer may be one or more selected from the group consisting of polyurethane, polyethylene, polynorbonene, trans-polyisoprene and styrene-butadiene copolymer.

(9) The hardness and/or modulus of the cross-linked elastomeric material are/is between that of rubber and plastics, which characteristic ensures that this material may automatically recover from stretching and extension deformation, so as to achieve the desired memory function. For this purpose, the cross-linked elastomeric material may be one or more selected from the group consisting of polyurethane elastomer resin, SBS resin (styrene-butadiene-styrene triblock copolymer), propylene-butene copolymer, hard rubber and silicon rubber, so as to ensure the deformation of the elastomeric material.

(10) Alternatively, there may be additive(s) added into the above obtained mixture, such as dimethoxybenzoin, and PPG diamine.

(11) In accordance with the present invention, the shape memory polymer of crystalline cross-linked polymer and cross-linked elastomeric material are interpenetrated with each other to obtain a polymer composite material of network structure. When the temperature of this composite material rises, the elastic restoring force of the elastomeric material will decrease, while the shape memory polymer will have stronger restoring force when the deformation occurs at a temperature above the shape recovery temperature, therefore the composite material will shrink as the restoring force of the shape memory polymer is larger than the elastic force of the elastomeric material. As the deformation of the elastomeric material increases meanwhile the restoring elastic force thereof grows up until the balance of the forces of these two types of polymer, at that time and the shape of the composite material remains unchanged. When the temperature decreases the restoring elastic force of the elastomeric material will increase meanwhile the restoring force of the shape memory polymer decreases, as a result the increasing elastic force drive the soft segment of the shape memory polymer to re-crystalline in the reverse direction meanwhile the length increases to recover the original state. The two materials independently play their roles and the above cycle continues. Therefore the polymer composite material obtained by interpenetrating and cross linking a shape memory polymer material with secondary deformation with an elastomeric material has the effect of two-way shape memory, large two-way shape recovery ratio, good shape stability. Meanwhile the deformation temperature of the obtained polymer composite material can be adjusted over a wide temperature range, including room temperature, body temperature and other circumstances, and this material always has two-way shape-memory behavior in the above situations.

(12) In the two-way shape memory polymer composite material according to the present invention, the polymer material containing the crystalline polymer segment can maintain the original shape under a lower temperature (T1), it will deform when heated to a higher temperature than the transition temperature (Tt), and keep the deformed shape unchanged over a higher temperature (T2) range. Further, when the polymer material containing crystalline polymer segment is cooled from a higher temperature (T2) to a lower temperature (T1) under ambient temperature, it can recover the original shape at lower temperature without external force. According to the present invention, the above transition temperature is the crystalline melting temperature of the crystalline polymer, and the lower temperature (T1) is a temperature lower than transition temperature (Tt), and the higher temperature (T2) is a temperature higher than transition temperature (Tt). During the use of the material of the present invention, the shape memory effect thereof can be achieved by the change of the external stimulus condition, and the transition condition depends on the melting temperature of the crystalline polymer in the polymer material or other restoring conditions. Therefore, this material makes use of the ability of recovery to original shape with the change of the temperature of the shape memory polymer and the elastic recovery of the deformed elastomeric material and the deformation with the change of temperature has been achieved; that is, the polymer material has an active deformation when the temperature increases, and it will recover the original shape when temperature decreases, thus it has two-way memory behavior with multiple cycle memory for two shape states.

(13) The two-way shape memory polymer according to the present invention is made based on the characteristic and the structural principle of the interpenetrating network polymer composite material. The memory polymer material is formed by interpenetration of two polymer networks, wherein the first polymer network, as a shape memory shrinkage segment, will shrink under heating, and the second polymer network acts as the segment for storage of energy. The first polymer network shrinks and presses the second polymer network under heating, while the heating is cancelled the pressed second polymer network will provide a restoring force to the first polymer network to recover the original shape, therefore the interpenetrating network polymer composite material has the behavior of two-way shape memory.

(14) The present invention further provides a method for producing the above said polymer composite material with two-way shape memory, which comprises: S10, obtaining a polymer containing crystalline polymer segment as raw material; S20, obtaining an elastomeric material polymer as another raw material; S30, blending the polymer containing crystalline polymer segment and the elastomeric material polymer to give a mixed materials, and the obtained mixed materials being treated in a first stimulation mode to cross-link the crystalline polymer in the mixed material, so as to obtain the first cross-linked polymer; S40, stretching the first cross-linked polymer and fixing it, treating it in a second stimulation mode to cross-link the elastomeric material polymer, so as to obtain the two-way shape memory polymer composite material according to the present invention.

(15) The purpose of the above steps S30 and S40 is to make the two network polymer raw materials sequentially cross-linked to form an interpenetrating structure, therefore the first stimulation mode should be different from the second stimulation mode, alternatively, these two steps employ the same stimulation mode but with different intensity, or else, these two types of network polymer may cross-link and deform with each other simultaneously, and the structure of interpenetration and the function of two-way shape memory cannot be obtained.

(16) According to the production method of the present invention, the polymer containing crystalline polymer segment and the elastomeric material polymer are preferably blended in a solvent to give a mixed materials in the above step S30, wherein the solvent may be dimethylformamide.

(17) Preferably, the ratio of the polymer containing crystalline polymer segment to the elastomeric material polymer is in the range of from 0.2:1 to 10:1.

(18) According to the present invention, the polymer containing crystalline polymer segment has such property that it can be physically or chemically or super molecular cross-linked under UV or non-thermal stimulation, and the cross-linked crystalline polymer may deform under the stimulation of heat, light, electricity, magnetism, humidity and variant pH values, so as to produce a restoring force. According to the present invention, based on the property of the raw material, UV lighting is preferably selected as the first stimulation mode to promote the crosslinking of the crystalline polymer segment in the manufacture process. Then heat stimulus is selected to be used as the second stimulation mode, and in this process the elastomeric material polymer is cross-linked meanwhile the cross-linked crystalline polymer may have deformation so as to achieve a better memory effect.

(19) Of course, the above said stimulation modes are preferred modes based on the preferred characteristics of the raw materials, and in the actual performance the first stimulus and the second stimulus may be different from the above modes, as long as the above purpose can be achieved, these other modes will not be described herein.

(20) In the step S10, the crystalline polymer segment contained in the polymer raw material may be selected from the group consisting of polyester, polyether and polyolefin.

(21) Methods of making polymer containing crystalline polymer segment are disclosed, for example, in CN publication No. 1706998A, which is incorporated herein by reference.

(22) The inner structural change of the raw materials in the above preparation process is shown in FIGS. 1-4. FIG. 1 is a molecular structure diagram showing the molecular arrangement of the two polymers in the mixed materials obtained by blending the two raw materials. After the mixing of the polymer containing crystalline polymer segment (indicated by circle block) and the elastomeric material polymer (indicated by square block), the molecules in the composite materials have an irregular crossed arrangement.

(23) Then, a first cross-linked polymer is obtained by crosslinking the crystalline polymer in the mixed materials in the first stimulus process of the step S30, the molecular structure is shown in FIG. 2, wherein the polymer containing crystalline polymer segment (indicated by circle block) forms a first crosslinked network polymer structure, and the elastomeric material polymer (indicated by square block) interpenetrates regularly or irregularly with the first crosslinked network polymer structure formed by the polymer containing crystalline polymer segment.

(24) Referring to FIG. 3, after the stretching process, the shape of this material becomes slender. Referring to FIG. 4, after the second stimulus process, the structure continues to change, the elastomeric material polymer (indicated by square block) is crosslinked to form a second crosslinked network polymer structure, meanwhile the second crosslinked network polymer structure and the first crosslinked network polymer structure interpenetrate each other to obtain an interpenetrating network structure. In the interpenetrating network structure, the irregular interpenetration accounts for a large proportion, and this structure of interpenetration is caused by irregular molecule movement in the shaping process.

(25) When the two-way shape memory polymer material is prepared by the above process, the memory ability of the product is related with the factors such as the ratio between the raw materials, elongation degree, and hardness of the elastomeric polymer, therefore the memory ability of the product may be adjusted by changing the above factors.

(26) The polymer composite material with two-way shape memory obtained by the process including the above steps may be formed to have a shape of membrane, foam, fiber, and block, furthermore, the appropriate processing can be selected according to occasion demands, so as to achieve a lightweight product and make the product easy to process.

(27) According to the present method for manufacture of polymer material with two-way shape memory, it provides a simple technique to obtain a product with two-way shape memory at room temperature, and the obtained product has a lower cost, and it is easy to operate and use. The method for manufacture the above composite material will be illustrated with reference to the following Examples.

Example 1

(28) The Raw Materials:

(29) Polycaprolactone as a crystalline cross-linked polymer, laboratory-made; the main index of this polymer is: it is capped with carbon-carbon double bond, and the melting temperature thereof is from 35 to 40 C.;

(30) Polytetrahydrofuran as a cross-linked elastomeric material, laboratory-made:

(31) the main index of this polymer is: it is capped with epoxy group, and its molecular weight is in the range of from 750 to 1250;

(32) Dimethoxybenzoin, obtained from Sigma-Aldrich, Inc.;

(33) PPG diamine (brand name D230), Commercial product; the main index of this polymer is, its molecular weight is about 230.

(34) Preparation Process:

(35) S10. the polycaprolactone, polytetrahydrofuran, dimethoxybenzoin, PPG diamine of required amounts (wherein the ratio by weight of polycaprolactone to polytetrahydrofuran was 0.5:1) were mixed and dissolved in dimethylformamide to obtain a mixture, then the mixture was poured into a rectangular mold;

(36) S20. the mixture in the mold was irradiated with a UV lamp for 2 hours to give a gel;

(37) S30. the obtained gel was elongated and fixed to a certain place, then it was heated to 80 C. in an oven and kept at that temperature over 10 hours for crosslinking to give an interpenetrating network polymer composite.

(38) The obtained polymer composite has the following main performance index: the transition temperature is 35 to 45 C.; this polymer will shrink when the temperature rises above the transition temperature, and the polymer will elongate when the temperature drops below the transition temperature.

Example 2

(39) The Raw Materials:

(40) Shape memory polyurethane, laboratory-made (the preparation method please refer to CN publication No. 1706998A); it has the following main index: the hard segment is made of 4,4-diphenylmethane diisocyanate/1,4-butanediol and it has a melting temperature of from 180 to 200 C., and the soft segment is made of polycaprolactone and it has a melting temperature of from 35 to 40 C.;

(41) Polyurethane elastomer, laboratory-made; it has the following main index: the hard segment is made of hexamethylene diisocyanate/1,4-butanediol and it has a melting temperature of from 130 to 150 C., the soft segment is made of polytetrahydrofuran and it has a glass transition temperature of from 20 to 50 C.;

(42) Preparation Process:

(43) S10. the above two polyurethanes of required amounts (wherein the ratio by weight of shape memory polyurethane to polyurethane elastomer was 8:1) as raw materials were dissolved in dimethylformamide, then the obtained mixture was poured into a mold to form a film at 80 C.;

(44) S20. the obtained film was elongated to two times longer in length and it was fixed to a certain place, then it was heated to 140 C. in an oven and kept at that temperature for 1 minute;

(45) S30. the film was then transferred to an oven of 70 C. and kept at that temperature for 10 minutes, finally this film was taken out and cooled to room temperature to obtain a cross-linked interpenetrating network polymer composite.

(46) In this Example, the first stimulation (i.e. heating) is in the same way as the second stimulation, but the temperature is different in these two stimulations. The obtained shape memory polymer composite has the following main performance index: the transition temperature is from 35 to 45 C.; this polymer will shrink when the temperature is above the transition temperature and the polymer will elongate when the temperature drops below the transition temperature.

(47) The shape memory polymer composite made in the above process has the following advantages: it has two-way shape memory function, good bi-directional reversion ratio, and good stability; there are various raw materials can be selected to prepare this polymer, this polymer has a wide range of shape memory temperature; it has a lower cost and light weight, it is easy to produce, package and transportation; this polymer composite has a simple preparation process that has lower energy consumption is easy to perform, this polymer composite can be employed to make different shapes of complex structures; the composite has property of corrosion resistance, electrical insulation property and good heat preservation. The product has a wide range of potential applications in the fields of textile material, building material, machinery manufacturing, electronic communication, printing and packaging materials, health care, daily necessities, recreation and sports appliance.

(48) The embodiments above are merely the preferable embodiments of the present application and not intended to limit the present application. And all changes equivalent substitution and improvements which come within the meaning and range of equivalency of the present application are intended to be embraced therein.