Perovskite core-shell nanocrystals
10538540 · 2020-01-21
Assignee
Inventors
- Tze Chien Sum (Singapore, SG)
- Weiqiang Chen (Singapore, SG)
- Subodh Gautam MHAISALKAR (Singapore, SG)
- Nripan MATHEWS (Singapore, SG)
- Sjoerd Antonius Veldhuis (Singapore, SG)
- Saikat Bhaumik (Singapore, SG)
Cpc classification
C01P2002/70
CHEMISTRY; METALLURGY
International classification
Abstract
Provided is a nanocrystal comprising a core comprised in a shell, wherein the core comprises a first material of a perovskite structure comprising a first organic cation not exceeding a molar weight of about 45 g/mol, a first divalent metal and a first counter anion, and, wherein the shell comprises a second material of a perovskite structure comprising a second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, optionally the first organic cation, a second divalent metal and a second counter anion. Provided is further a matrix having the nanocrystal as defined above encapsulated therein. Provided is further a process for the synthesis of a nanocrystal comprising a core comprised in a shell, the process comprising a) preparing a precursor solution containing at least one divalent metal, a first organic cation not exceeding a molar weight of about 45 g/mol, a second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, and at least one counter anion in a polar aprotic solvent; and b) subjecting the precursor solution to a non-polar solvent to form the nanocrystal.
Claims
1. A nanocrystal comprising a core comprised in a shell, wherein the core comprises a first perovskite structure, wherein the first perovskite structure comprises a first organic cation not exceeding a molar weight of about 45 g/mol, a first divalent metal and a first counter anion, and wherein the shell comprises a second perovskite structure, wherein the second perovskite structure comprises a second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, optionally the first organic cation, a second divalent metal and a second counter anion, wherein the first organic cation and the second organic cation each comprise an ammonium ion, and wherein the second organic cation comprises at least one alkyl moiety.
2. The nanocrystal of claim 1, wherein the ammonium ion is independently selected from the group consisting of a primary, a secondary, a tertiary and a quaternary ammonium ion.
3. The nanocrystal of claim 1, wherein the first organic cation comprises at least one alkyl moiety.
4. The nanocrystal of claim 1, wherein the first organic cation comprises an imine moiety.
5. The nanocrystal of claim 1, wherein the first perovskite structure material comprises material of the general formula (SNH.sub.3)MX.sub.3 and wherein the second material comprises material of the general formula (C.sub.4-12-Alk-NH.sub.3).sub.2(SNH.sub.3).sub.n1M.sub.nX.sub.3n+1 wherein S is CH.sub.3 or CHNH; n is an integer selected from 1 to 4; M is a divalent metal; and X is a counter anion.
6. The nanocrystal of claim 1, wherein the first organic cation and the second organic cation each comprises at least one alkoxysilane.
7. The nanocrystal of claim 1, wherein the second organic cation in the second perovskite structure is configured to separate the second divalent metal from the second counter anion, thereby increasing the d-spacing.
8. The core-shell nanocrystal of claim 1, wherein the first and/or second counter anion is a halogen.
9. The nanocrystal of claim 1, wherein the first and/or second divalent metal is a heavy metal.
10. The nanocrystal of claim 1, wherein the elements of the second perovskite structure are arranged in a substantially 2-dimensional layer.
11. The nanocrystal of claim 1, wherein the nanocrystal is spherical.
12. The nanocrystal of claim 1, wherein the nanocrystal has a diameter of about 1-50 nm.
13. The nanocrystal of claim 1, wherein the nanocrystal is further encapsulated in SiO.sub.x and/or SiO.sub.2.
14. The nanocrystal of claim 1, wherein the nanocrystal is further encapsulated with solid lipid structures.
15. A matrix having a nanocrystal of claim 1 encapsulated therein.
16. The nanocrystal of claim 1, wherein the second perovskite structure comprises the second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, and the first organic cation, not exceeding a molar weight of about 45 g/mol, a second divalent metal and a second counter anion.
17. A process for the synthesis of a nanocrystal comprising a core comprised in a shell, wherein the core comprises a first perovskite structure and wherein the shell comprises a second perovskite structure, the process comprising a) preparing a precursor solution containing at least one divalent metal, a first organic cation not exceeding a molar weight of about 45 g/mol, a second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, and at least one counter anion in a polar aprotic solvent; and b) subjecting the precursor solution to a non-polar solvent to form the nanocrystal comprising a core comprised in a shell, wherein the first organic cation and the second organic cation each comprise an ammonium ion, and wherein the second organic cation comprises at least one alkyl moiety.
18. The process for the synthesis of a nanocrystal of claim 17, wherein the molar ratio of the first organic cation to the second organic cation is in the range of 9:1 to 1:9.
19. The process for the synthesis of a nanocrystal of claim 17, wherein the formation of the nanocrystal proceeds in a one-pot process.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
(1) In the drawings, like reference characters generally refer to the same parts throughout the different views. The drawings are not necessarily drawn to scale, emphasis instead generally being placed upon illustrating the principles of various embodiments. In the following description, various embodiments are described with reference to the following drawings.
(2)
(3)
(4)
(5)
(6)
(7)
(8)
(9)
(10)
(11)
(12)
(13)
(14)
(15)
(16)
(17)
(18)
(19)
(20)
(21)
(22)
(23)
(24)
(25)
(26)
(27)
(28)
(29)
(30)
(31)
DESCRIPTION
(32) The disclosure presents the utilization of core-shell type organic-inorganic perovskite nanocrystals with different sizes and shapes for applications in optical limiting, multiphoton excited upconversion PL and lasing. As an example, CH.sub.3NH.sub.3PbBr.sub.3 (MAPbBr.sub.3) single crystals have demonstrated relatively large two-photon absorption coefficients. Its corresponding nanocrystals have also shown high photoluminescence quantum yield (PLQY), tunable bandgap and PL wavelengths. Accordingly, in a first aspect, the present disclosure provides a nanocrystal comprising a core comprised in a shell, wherein the core comprises a first material of a perovskite structure comprising, or essentially consisting of a first, small organic cation not exceeding a molar weight of about 45 g/mol, a first, divalent metal and a first counter anion, and wherein the shell comprises a second material of a perovskite structure comprising, or essentially consisting of a second, large organic cation having a molar weight between about 74 g/mol and about 187 g/mol, optionally the first organic cation, a second divalent metal and a second counter anion. In this context, nanocrystal refers to a nanometer-scale crystalline particle. The nanocrystal is provided as a core-shell nanocrystal, which refers to a 3-dimensional core enclosed in a substantially 2-dimensional shell. The core may be encapsulated in the shell. The crystal structures in the core may differ from the crystal structures in the shell. However, both crystal structures may be in an inorganic-organic perovskite modification.
(33) An inorganic-organic perovskite refers to a modification wherein the elements are arranged in a cubic structure with the general formula of AMX.sub.3. In this structure, an A-site ion, is on the corners of the lattice. M site ions, on the center of the lattice, could be 3d, 4d, and 5d transition metal elements. Crystals of perovskite appear as cubes, but are pseudocubic and crystallize in the orthorhombic system. Perovskites may be structured in layers, with the above AMX.sub.3 structure separated by thin sheets of intrusive material.
(34) The first core material may comprise a first small organic cation. The first small organic cation may occupy the A-site of the formula AMX.sub.3 described above. This may result in an inorganic-organic perovskite structure. The first, small organic cation may be any organic moiety with a molecular weight not exceeding 45 g/mol. It may further include a cationic functional group, which may include an ammonium cation.
(35) The first core material may further comprise a first divalent metal. The first divalent metal may occupy the M-site of the formula AMX.sub.3 described above. Divalent metal in this context refers to any metal which may form the perovskite structure as described above. Notably, the divalent metal may be selected from the group consisting of transition metals, lanthanoids, post-transition metals and heavy metals. Divalent refers to the metal being present in the oxidation state +II.
(36) The first core material may further comprise a first counter anion. The first counter anion may be selected from any anion which may form the perovskite structure as described above. Preferably, the weight of one counter anion may not exceed about 100 g/mol. More preferably, the counter anion is selected from the group of the non-metals. More preferably, the counter anion is selected from the group of the halogens. The disclosure may refer to a first or a second counter anion at several sections and for several functions, wherein each may be the same or they may be different from each other.
(37) Within the core of the core-shell nanocrystal, the elements may be arranged in a 3-dimensional network. This network may be arranged in a crystalline modification. The crystalline modification may be a perovskite modification. Further, it may be in a cubic arrangement.
(38) The second shell material may be substantially 2-dimensional. In the second shell material, parts or all of the first small organic cation may be replaced by a second, large organic cation, thereby breaking the cubic symmetry. In the second shell material, a layered structure as described above may be present, wherein the above AMX.sub.3 structure is separated by thin sheets of intrusive material, the intrusive material being the second, large cation. The number of layers may be described with the integer n. The second, larger cations may lead to a larger d-spacing of the divalent metal atoms to their counter anions, which influences the optical properties as well as the stability of the ensuing nanocrystal.
(39) The second shell material may additionally comprise a second divalent metal and a second counter anion, which may be described as the first divalent metal and the first counter anion. The specific divalent metal and counter anion used in the shell may differ from those used in the core. Alternatively, they may be the same.
(40) The second shell material may additionally comprise residues of the first, smaller organic cation. The core material may additionally comprise residues of the second, larger organic cation.
(41) Advantageously, by keeping within the weight ranges of the first, smaller organic cation and the second, larger organic cation, the perovskite modification is tuned to an optimal ratio, leading to the observed core-shell configuration. By controlling the weight range of the organic cations, the unique properties of the nanocrystals with regard to optical limiting, multiphoton excited upconversion PL and lasing can be obtained.
(42) To further explain the above, in order to form a 3D core perovskite material, only small organic cations that fit in the cuboctahedral cavity of the metal-counter anion octahedra can be used. This cation selection is limited only to those cations with molar weight of about 32 to 45 g/mol. With respect to the second organic cation (from the shell material), sizes may range from molar weights of 74 to 187 g/mol. Organic cations of lower weight (shorter chain), e.g. C.sub.2-C.sub.3-Alkyls, may yield an unstable product, hence it cannot be used for shell formation. Similarly, organic cations of higher weight than 187 g/mol (longer chain, C.sub.13 and longer) may face difficulties forming a 2D shell material concomitantly to 3D core formation during coprecipitation, due to slower reaction/formation kinetics.
(43) The term any organic moiety as used herein refers to carbon-containing moieties. These moieties can be linear or branched, substituted or unsubstituted, and are derived from hydrocarbons, typically by substitution of one or more carbon atoms by other atoms, such as oxygen, nitrogen, sulfur, phosphorous, or functional groups that contain oxygen, nitrogen, sulfur, phosphorous. The organic moiety can comprise any number of carbon atoms, but preferably it is a low molecular weight organic moiety. It is preferred that the organic moiety is compatible with the reaction described herein and does not adversely affect the described formation of nanocrystals. Suitable groups and moieties are well known to those skilled in the art or can be readily identified by routine experimentation.
(44) In a preferred embodiment, the organic moiety can be a linear or branched, substituted or unsubstituted alkyl with 1 to x carbon atoms; linear or branched, substituted or unsubstituted alkenyl with 2 to x carbon atoms; linear or branched, substituted or unsubstituted alkinyl with 2 to x carbon atoms; linear or branched, substituted or unsubstituted alkoxy with 1 to x carbon atoms; substituted or unsubstituted cycloalkyl with 3 to x carbon atoms; substituted or unsubstituted cycloalkenyl with 3 to x carbon atoms; substituted or unsubstituted aryl with 6 to x carbon atoms; and substituted or unsubstituted heteroaryl with 3 to x carbon atoms; with x being any integer of 2 or more, depending on the weight range as indicated above.
(45) In a further embodiment of the present disclosure, the organic moiety can be a linear or branched, substituted or unsubstituted alkyl with 1 to 11 carbon atoms; linear or branched, substituted or unsubstituted alkenyl with 3 to 11 carbon atoms; linear or branched, substituted or unsubstituted alkoxy with 1 to 11 carbon atoms, substituted or unsubstituted cycloalkyl with 5 to 11 carbon atoms; substituted or unsubstituted cycloalkenyl with 5 to 11 carbon atoms; substituted or unsubstituted aryl with 5 to 11 carbon atoms; and substituted or unsubstituted heteroaryl with 5 to 11 carbon atoms, depending on the weight range as indicated above.
(46) The organic moiety can also be a combination of any of the above-defined groups, including but not limited to alkylaryl, arylalkyl, alkyl heteroaryl and the like, to name only a few, all of which may be substituted or unsubstituted.
(47) The term substituted as used herein in relation to the above moieties refers to a substituent other than hydrogen. Such a substituted is preferably selected from the group consisting of halogen, OH, OOH, NH.sub.2, NO.sub.2, ONO.sub.2, CHO, CN, CNOH, COOH, SH, OSH, CSSH, SCN, SO.sub.2OH, CONH.sub.2, NHNH.sub.2, NC, CSH, OR, NRR, NR, C(O)R, C(O)OR, (CO)NRR, NRC(O)R, OC(O)R, aryl with 5 to 10 carbon atoms, cycloalk(en)yl with 3 to 10 carbon atoms, 3- to 8-membered heterocycloalk(en)yl, and 5- to 10-membered heteroaryl, wherein R and R are independently selected from hydrogen, alkyl with 1 to 10 carbon atoms, alkenyl with 2 to 10 carbon atoms, alkynyl with 2 to 10 carbon atoms, aryl with 5 to 10 carbon atoms, cycloalk(en)yl with 3 to 10 carbon atoms, 5- to 10-membered heteroaryl, comprising 1 to 4 heteroatoms selected from nitrogen, oxygen, and sulfur, and 5- to 10-membered heterocycloalk(en)yl, comprising 1 to 4 heteroatoms selected from nitrogen, oxygen, and sulfur. Any of these substituents may again be substituted, it is however preferred that these substituents are unsubstituted.
(48) Alkyl, or abbreviated alk, refers to a saturated hydrocarbon moiety, such as methyl, ethyl, and the like. Alkenyl and Alkynyl comprise at least one carbon-carbon double bonds or triple bonds, respectively, and are otherwise defined as alkyl above.
(49) Cycloalkyl refers to a non-aromatic carbocyclic moiety, such as cyclopentanyl, cyclohexanyl, and the like.
(50) Cycloalkenyl refers to non-aromatic carbocyclic compounds that comprise at least one CC double bond.
(51) Similarly, heterocycloalk(en)yl relates to cycloalk(en)yl groups wherein 1 or more ring carbon atoms are replaced by heteroatoms, preferably selected from nitrogen, oxygen, and sulfur.
(52) Aryl relates to an aromatic ring that is preferably monocyclic. Preferred aryl substituents are moieties with 6 carbon atoms, such as phenyl.
(53) Heteroaryl refers to aromatic moieties that correspond to the respective aryl moiety wherein one or more ring carbon atoms have been replaced by heteroatoms, such as nitrogen, oxygen, and sulfur.
(54) All of the afore-mentioned groups can be substituted or unsubstituted. When substituted, the substituent can be selected from the above list of substituents.
(55) The term at least one as used herein relates to one or more, for example 1, 2, 3, 4, 5, 6, 7, 8, 9 or more of the referenced species.
(56) Halogen as used herein refers to F, Cl, Br, and I.
(57) The small organic cation and the large organic cation core-shell nanocrystal may each comprise a cationic functional group. This cationic functional group may serve as the counter ion in the perovskite structure. The cationic functional group may be any functional group which possesses a positive charge and is stable under the reaction conditions which result in the nanocrystal. In some embodiments, the cationic functional group may be an ammonium ion. The ammonium ion may be a primary, a secondary, a tertiary or a quaternary ammonium ion. The ammonium may be substituted with the organic moiety. Depending on whether the cationic functional group is a primary, a secondary, a tertiary or a quaternary ammonium ion, the small organic cation and the large organic cation may comprise one, two, three or four organic moieties.
(58) In some embodiments, the organic moiety may be at least one alkyl moiety. The alkyl moiety may be branched or linear. In some embodiments, the at least one alkyl moiety may be at least one linear alkyl moiety.
(59) In some embodiments of the first organic cation, the organic moiety may be a substituted alkyl moiety. In particular, the alkyl moiety may be substituted with a nitrogen functionality. In one example, the organic moiety may be an imine. The resulting first organic cation would therefore be a formamidinium cation.
(60) In the core-shell nanocrystal, the first material of the core may comprise, or may essentially consist of, material of the general formula (SNH.sub.3)MX.sub.3 and the shell may comprise, or may essentially consist of, a second material of the general formula (C.sub.4-12-Alk-NH.sub.3).sub.2(SNH.sub.3).sub.n1M.sub.nX.sub.3n+1 wherein
(61) S is CH.sub.3 or CHNH;
(62) n is an integer selected from 1 to 4;
(63) M is a divalent metal; and
(64) X is a counter anion,
(65) wherein M and X of the core and M and X of the shell may be the same or different.
(66) In this embodiment, the first, small organic cation is described as SNH.sub.3 and the second, large organic cation is described as C.sub.4-12-Alk-NH.sub.3. The molecular weight limitation is determined through the sizes of the organic moieties within the formula. Hence, the first, small organic cation may comprise a primary ammonium cation and an optionally substituted methyl, wherein the substitution may be another nitrogen functionality. In one example, the first, small organic cation is methyl ammonium. Alternatively, it may be a formamidinium cation. The second, large organic cation may comprise a primary ammonium cation and a butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl or dodecyl moiety. In one example, the second, large organic cation is octyl ammonium. n signifies the number of layers within the shell structure with n=1 being a pure 2-dimensional layer and n=2-4 being a quasi-2-dimensional layered structure (substantially 2-dimensional). In one example, n is 2.
(67) In some embodiments, it may be desired to stabilize the nanocrystal by additionally providing at least one alkoxysilane to each of the first, small and the second, large organic cation. Advantageously, this may allow for sol-gel reactions which may further increase the stability of the nanocrystals. In one example, the alkoxysilane is 3-aminopropyltriethoxysilane (APTES).
(68) As mentioned previously, the second, large organic cation in the shell material may separate the metal from the counter ion, thereby increasing the d-spacing. An increased d-spacing within the shell has the advantage of altering the optical properties, resulting in the unique optical nonlinear properties which are observed in the present disclosure.
(69) The first and second counter anion may be a halogen, preferably selected from the group consisting of fluoride, chloride, bromide and iodide. In one example, the counter anion is bromide.
(70) The first and second divalent metal in the core-shell nanocrystal may be a heavy metal. Heavy metals may be associated with a higher density and a lower reactivity than other (light) metals. As such, the divalent heavy metal may be selected from zinc, mercury, lead, iron, copper, tin, silver, gold, platinum, gallium, thallium, hafnium, cobalt, ruthenium and indium. In one example, the divalent metal is lead.
(71) Additionally or alternatively, the first and/or second divalent metal in the core-shell nanocrystal may be a post-transition metal. Post-transition metals may refer to the metallic elements in the periodic table located between the transition metals (to their left) and the metalloids (to their right). These elements may include gallium, indium thallium, tin, lead, bismuth, cadmium, mercury and aluminum. In one example, the divalent metal is lead.
(72) The nanocrystal of the present disclosure may be in a spherical. This may be seen in contrast to a cubic shape. The diameter of the nanocrystal may be about 1-50 nm, preferably 5-30 nm, more preferably 5-20 nm, or approximately about 8-15 nm.
(73) The photoluminescence quantum yield of the nanocrystal may be higher than 50% one month after synthesis. Additionally or alternatively, it may be higher than 10% two months after synthesis. Photoluminescence quantum yield (PLQY) is usually measured by two methods. One method is called relative PLQY, which is measured by comparing with reference sample. Another method is called absolute PLQY, which is measured with integrating sphere. The PLQY of the NCs in the present application is measured with integrating sphere and is absolute PLQY. This method does not depend on reference sample and its concentration. Absolute PLQY measurement is more reproducible compared to relative PLQY because there is no variable and constraints are fixed all time. After 2 months, the PLQY measured is accurate too.
(74) In one embodiment, the core-shell nanocrystal may be further encapsulated with SiO.sub.x and/or SiO.sub.2. The silicon oxide may be utilized as an additional shell or as a medium to embed several nanoparticles. In another embodiment, the core-shell nanocrystal may be further encapsulated with solid lipid structures. Here, the term lipid should be used in a broad sense of materials, such as long-chain saturated fatty acids (e.g. stearic acid), mono- di- and triglycerides, copolymer micelles, nonionic ABC triblock copolymers composed of a central hydrophobic chain (B) surrounded by hydrophilic moieties (A and C), steroids, waxes, or mixtures of the aforementioned. Furthermore, the core and core-shell nanocrystals may be further encapsulated in the voids of porous metal-organic frameworks, such as Cu.sub.3(1,3,5-benzene tricarboxylate).sub.2 (HKUST-1), Zn.sub.4O nodes with 1,4-benzodicarboxylic acid struts (IRMOF-1), other IRMOF series (like IRMOF-10 and IRMOF-16), zinc ions coordinated by four imidazolate rings (ZIF-8), UiO-66 made up of [Zr.sub.6O.sub.4(OH).sub.4] clusters with 1,4-benzodicarboxylic acid struts, etc. to enhance the multiphoton absorption property and improve stability and biocompatibility.
(75) Hence, in a second aspect, there is provided a matrix having a nanocrystal as described above encapsulated therein. The matrix material may be any material listed above, notably it may be a solid material. It may be an inorganic or an organic material, or a combination thereof. The inorganic matrix material may be selected from silica, for example SiO.sub.2 and/or SiO.sub.x. The organic matrix material may be selected from lipids. Where the matrix is a combination of an inorganic and an organic material, this may be a metal-organic framework (MOF). Advantageously, the nanocrystal is embedded in the voids of the matrix material. This may be beneficial in relation with stability and/or cytotoxicity of the nanocrystal.
(76) In a third aspect, the present disclosure provides a process for the synthesis of a nanocrystal comprising a core comprised in a shell, the process comprising a) preparing a precursor solution containing a first and a second divalent metal, a first organic cation not exceeding a molar weight of about 45 g/mol, a second organic cation having a molar weight between about 74 g/mol and about 187 g/mol, and a first and second counter anion in a polar aprotic solvent; and b) subjecting the precursor solution to a non-polar solvent to form the nanocrystal comprising a core comprised in a shell. The formation of the core-shell nanocrystal may occur in a one-pot-approach, as the precursor solution is mixed into non-polar solvent without any distinction of a process part relating to the core and a process part relating to the shell. Surprisingly, it has been found that the process resulting in a core-shell nanocrystal provides optimal results when the core-shell nanocrystal is produced in a one-pot approach. An alternative process wherein the core was produced in a first step and the shell was envisaged to be produced in a second step, was proven to be unsuccessful.
(77) The polar aprotic solvent may be selected from the group consisting of tetrahydrofuran, ethyl acetate, acetone, N,N-dimethylformamide, acetonitrile, dimethyl sulfoxide, nitromethane and propylene carbonate, and mixtures thereof. In one example, the polar aprotic solvent is N,N-dimethylformamide (DMF).
(78) The non-polar solvent may be selected from the group consisting of hexane, benzene, toluene, diethyl ether, chloroform, 1,4-dioxane, and mixtures thereof. In one example, non-polar solvent is toluene.
(79) The molar ratio of the first, small organic cation to the second, large organic cation may be varied in the range of 9:1 to 1:9. Optimal results regarding optical properties may be obtained by a ratio wherein the first, small organic cation is predominantly present (i.e. in more than 50 mol %).
(80) In one embodiment, step b) of the process as described above may proceed at elevated temperature, such as between 40-200 C., preferably at between 50-100 C., more preferably at about 60 C.
(81) In a fourth aspect, there is provided use of the nanocrystal comprising a core comprised in a shell as described above for optical limiting, bioimaging and upconversion lasing application.
(82) One of the methods to enhance the stability, efficiency and brightness of semiconductor nanocrystals is by growing a shell of a larger band-gap semiconductor around it. Such nanocrystals with small regions of one material embedded in another with a wider band gap are known as core-shell semiconducting nanocrystals (CSSNCs). This type of crystal engineering improves the quantum yield of the nanocrystals by confining charge carriers, passivating non-radiative recombination sites and making them more robust to processing conditions. In a bid to explore the same advantages in perovskite nanocrystals, this disclosure investigated the possibility of developing nanocrystals comprising of a high band-gap 2D perovskite shell over a low band-gap perovskite core as shown in
(83) The LARP method was adopted for the synthesis. A first, small organic cation, a metal salt, capping agents like oleylamine and oleic acid were dissolved in DMF in an appropriate molar ratio to make the final precursor solution for the nanocrystals (Examples). While in this results section lead bromide as a first and second divalent metal with first and second counter anion, methylammonium as a first small organic cation and octylammonium as a second large cation was utilized, the results should not be understood to be limited to these compounds.
(84) This precursor solution was then swiftly injected into toluene kept at elevated temperature and stirred vigorously to form the core nanocrystals. The mixture was then centrifuged and the supernatant containing the nanocrystals was collected for further studies. For the synthesis of the mixed cations, for example methylammonium-octylammonium (MA-OA) lead bromide nanocrystals, MABr and OABr at 8:2, 6:4, 4:6, 3:7 and 2:8 molar ratios were used in the precursor solution such that the total amount of organic ammonium bromide and synthesis conditions are constant for all combinations. The structural characterization of the nanocrystals thus prepared were done using transmission electron microscopy (TEM) and X-ray powder diffraction (XRD) and their photophysical properties were evaluated by recording their optical absorption, photoluminescence (PL) and time resolved photoluminescence spectra.
(85)
(86) Next, the photophysical properties of these core-shell nanocrystals was evaluated. The optical absorption of the pure MAPbBr.sub.3 (n=c) nanocrystals (
(87) Subsequently the photoluminescence properties of these materials were studied. As shown in
(88) Generally, the organic-inorganic perovskite structure (AMX.sub.3) is formed by a three dimensional network with first, small organic cations occupying the A-site, and the first and/or second divalent metal and halides forming the MX.sub.6 octahedra. The peak positions observed for the MAPbBr.sub.3 nanocrystals (
(89) In 2D layered perovskites like (OA).sub.2PbBr.sub.4, the inorganic lead halide layers are separated by the second, large organic cations (i.e. large d-spacing). In order to explain the d-spacing values observed in the XRD patterns of the mixed nanocrystals, we recorded the XRD pattern of pure layered (OA).sub.2PbBr.sub.4 (n=1) prepared by a previously reported method (see the examples). This layered compound showed a d-spacing of approximately 10.5 . In this case the two dimensional [PbBr.sub.6]4 layers are separated by n-octylamine ligands. Knowing the exact d-spacings for the MAPbBr.sub.3 and (OA).sub.2PbBr.sub.4, it is possible to conduct a basic elucidation of the varied d-spacings noted in the mixed nanocrystals (without taking strain/solvation effects into consideration). In the XRD patterns of 3:7 and 2:8 nanocrystals (
(90) The varied d-spacings point to the co-crystallization tendency of the organic ammonium perovskites. The high PLQY and stability of the 8:2 nanocrystals could possibly be explained by the formation of such a mixed organic shell. The clear 519 nm PL signature of the nanocrystals indicates that the main emitting species is MAPbBr.sub.3. However the weak optical absorption signature at 433 nm points to the possibility of a n=2 shell. Such a higher band-gap shell would allow for efficient confinement and also impart stability. We believe that the observed PLQY and stability enhancement, in combination with the blue-shift in the 8:2 sample originate from the formation of a core-shell type structure, in which the core consists of MAPbBr.sub.3 and the shell of layered (OA).sub.2PbBr.sub.4. However, due to the low electron density contrast between the core and the shell, and the structural instability at high magnification, no direct evidence of its formation could be presented using high-resolution (HR)-TEM. Instead, its formation is rationalized via a series of indirect observations from additional experiments (for full details and explanations, see the examples). For example, replacement of the oleylamine ligand with octylamine for MABr:OABr=10:0 resulted in a significantly lower PLQY and a red-shift in PL (see Tables 1 and 4, examples), whereas a similar blue-shift is observed for the 8:2 samples. This implies that OABr is the predominant factor to form a layered perovskite. In order to explore whether the 433 nm signature originates from (OA).sub.2MAPb.sub.2Br.sub.7 (n=2), it was attempted to synthesize spherical (OA).sub.2PbBr.sub.4 nanocrystals using the LARP method without the addition of MABr; the failure to produce the expected nanocrystals suggests that a 3D MAPbBr.sub.3 core is essential for the subsequent growth of 2D layers.
(91) Experiments with OA-Br addition after the formation of MAPbBr.sub.3 NP seeds (equivalent to MABr:OABr=8:2 and 2:8), resulted in green-emitting nanocrystals with a PL maximum at 522 nm, instead of 519 nm and 438/451 nm, respectively. This further suggests, that only during coprecipitation of MABr and OABr in the presence PbBr.sub.2 core-shell type nanoparticles are formed (see the examples). Thermogravimetric analysis provided additional evidence of a structural difference between MABr:OABr 10:0 and 8:2 nanocrystals; both organic components are released at a higher temperature in the 8:2 nanocrystals than the 10:0 nanocrystals, suggesting that additional energy is required to remove intercalated OA-Br from the layered shell (see the examples).
(92) To further understand the PLQY-variation in the mixed organolead bromide nanocrystals, the PL decay kinetics of these nanocrystals were investigated (
(93) Finally the PL stability of the mixed organolead bromide perovskite nanocrystals was examined (stored under ambient conditions, at 60% RH). The photographs in
(94) By the aid of the quantum confinement effect, these core-shell type mixed perovskite nanocrystals possess large multiphoton absorption and high PLQY and are suitable for nonlinear optical applications, such as optical limiting, multiphoton excited PL/lasing. Furthermore, a high band-gap 2D shell, for example an octylammonium lead bromide (OA).sub.2PbBr.sub.4 shell (3 eV), was developed using a similar protocol to coat the lower band gap NC core. As a comparative example, all-inorganic perovskite (CsPbBr.sub.3) NCs (cuboidal shape) have been reported to possess exceptional two-photon absorption property at 800 nm with two-photon action cross-section around 2 orders larger than the conventional semiconductor NCs and organic molecules, serving as a new benchmark for two-photon absorbing materials. In order to demonstrate the outstanding multiphoton absorption properties achieved in the 3D core and multidimensional core-shell type organic-inorganic perovskite NCs as presently disclosed, their multiphoton action cross-sections to that of CsPbBr.sub.3 NCs was compared. Even larger (about 3 times) multiphoton action cross-sections than that of CsPbBr.sub.3 NCs were achieved in the multidimensional core-shell type organic-inorganic perovskite NCs as presently disclosed. The insets of
(95) Here, there is reported a breakthrough in achieving giant five-photon absorption and highly efficient upconversion fluorescence using multidimensional core-shell perovskite colloidal NCs. Organic chromophores and conventional semiconductor NCs are considered leaders in two-/three-photon absorption applications, but they face considerable challenges from their small five-photon (5P) action cross-sections (.sub.5). To date, there has only been one report of 5P excited upconversion fluorescence in the literature using carefully designed and synthesized organic chromophore; while 5P excited upconversion fluorescence from semiconductor NCs has yet to be demonstrated. Herein, the 3D core and multidimensional core-shell organic-inorganic perovskite NCs (e.g., MAPbBr.sub.3, and MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs) transcend these challenges with highly efficient five-photon excited upconversion fluorescencean unprecedented feat for semiconductor NCs. Multidimensional type-I core-shell perovskite nanocrystals (for example, three-dimensional MAPbBr.sub.3 core encapsulated with two-dimensional (OA).sub.2PbBr.sub.4 perovskite shell) exhibits .sub.5 at least 9-orders larger than state-of-the-art specially-designed organic molecules. These findings will therefore open fresh approaches for next generation multiphoton imaging applications with unmatched imaging depth, sensitivity and resolution.
(96) Several aspects of this disclosure include: First realization of five-photon absorption and resultant highly efficient upconversion fluorescence in halide perovskite colloidal NCs excited at IR wavelengths (2 m). This effectively overcomes the inherent challenges of small five-photon action cross-sections in organic chromophores and conventional semiconductor NCs. First investigation, and detailed characterization of the multiphoton (2-, 3-, 4-, 5-photon) action cross-sections of the halide perovskite colloidal NCs over the wide excitation wavelength range of 675-2300 nm. First report on further achieving large enhancement of multiphoton action cross-sections in perovskite colloidal NCs utilizing a multidimensional core-shell structure. An unprecedented 9-orders larger five-photon action cross-sections (.sub.5 10.sup.136 cm.sup.10s.sup.4 photon.sup.4) than state-of-the-art specially-designed organic molecules is observed in multidimensional core-shell perovskite NCs, demonstrating the potential for next generation multiphoton imaging applications with unmatched imaging depth, sensitivity and resolution.
(97) These new insights challenge the conventional knowledge of multiphoton absorption in colloidal semiconductor NCs and enable fresh approaches for next generation of optical power limiting, low-threshold upconversion lasing and especially, multiphoton imaging applications. Below, a detailed description of the experimental and theoretical investigations is presented, which includes linear optical properties and structural characterization (incl. density function theory modelling); Five-photon absorption from the 3D core (for example MAPbBr.sub.3) and multidimensional core-shell type (MAPbBr.sub.3/(OA).sub.2PbBr.sub.4) organic-inorganic perovskite NCs, and their comparison to that of 3D all-inorganic CsPbBr.sub.3 NCs; Multiphoton excited frequency-upconverted photoluminescence (PL) measurements and characterization of multiphoton action cross-section spectra in the halide perovskite NCs; Open-aperture Z-scan measurements for quantification of the 2 PA cross-sections at 800 nm and 3 PA cross-sections at 1050 and 1100 nm; time-resolved PL measurements and discussion on the underlying physical mechanisms for the largely enhanced multiphoton action cross-sections of the multi-dimensional core-shell perovskite NCs.
EXAMPLES
Experimental Section
Example 1
(98) Materials:
(99) Lead bromide, PbBr.sub.2 (99.999%, trace metals basis, Sigma-Aldrich); oleic acid, OAc (90%, Sigma-Aldrich); oleylamine, OAm (70%, Sigma-Aldrich); N,N-Dimethylformamide, DMF (Anhydrous, 99.8%, Sigma-Aldrich); octylamine (99%, Sigma-Aldrich); butylamine (99.5%, Sigma-Aldrich); dodecylamine (99%, Sigma-Aldrich); toluene (Anhydrous, 99.7% GC, Sigma-Aldrich); hydrobromic acid, HBr (48%, Sigma-Aldrich); methylammonium bromide, MABr (Dyesol). All these chemicals were used without further purification.
Example 2
(100) Synthesis of Different Cationic Ammonium Bromide Powder:
(101) OABr was synthesized by mixing octylamine and HBr.
(102) At first octylamine was precooled in a glass beaker to 0 C. under vigorous stirring condition and HBr was added dropwise. The reacted solution was stirred for 2 hours. The reaction mixture was then transferred to a rotary evaporator to remove the solvent. The resulting precipitate was washed several times with diethylether to remove impurities and then dried in a vacuum furnace overnight at 60 C. to get a purified white colored CH.sub.3(CH.sub.2).sub.7NH.sub.3Br powder. The butylammonium bromide (BABr) and dodecylammonium bromide (DDABr) powders were synthesized by same synthetic procedure while changing the methylamine to butylamine and dodecylamine respectively.
Example 3
(103) Synthesis of MAPbBr.sub.3 and Mixed Cation Organo Lead Bromide NPs:
(104) MAPbBr.sub.3 NPs were synthesized by LARP method as reported elsewhere. At first in a glass vial 0.16 mmol of MABr, 0.2 mmol of PbBr.sub.2 were mixed in 5 mL DMF solution. Later 50 L of OAm and 0.5 mL OAc were also mixed in the DMF solution to form the final precursor solution.
(105) Another round bottom glass flask containing 5 mL of toluene was heated at 60 C. in an oil bath. Then 250 L of as prepared precursor solution was swiftly injected into toluene under vigorous stirring condition. The solution turned into green color confirms the formation of MAPbBr.sub.3NPs. The reaction was continued for 5 min and transferred into a centrifuge tube. The NPs were purified by centrifugation method that centrifuged at 7000 rpm for 10 min. The precipitate was discarded and the supernatant was collected for further characterization.
(106) For mixed cation organo MA-OA, BA-OA and DDA-OA lead bromide NPs were synthesized by the same synthetic procedure elaborated above. Here we maintained the same total molar concentration of alkyl ammonium bromide inside the precursor solution. The molar ratio of MABr and OABr were varied to 8:2, 6:4, 4:6, 3:7, and 2:8. The molar ratio of BABr-OABr and DDABr-OABr was fixed to 8:2.
Example 4
(107) Seeded (Modified) Synthesis Attempt of Mixed Cation Organo Lead Bromide NPs:
(108) In the modified synthesis, the same LARP synthetic protocol was followed as described above. Here at first there was injected MABr-PbBr.sub.2 precursor solution into toluene to grow MAPbBr.sub.3 NPs first and later the desired amount of OABr-PbBr.sub.2 precursor solution was injected.
Example 5
(109) Synthesis of (OA).sub.2PbBr.sub.4 Nanodisks:
(110) (OA).sub.2PbBr.sub.4 nanodisks were synthesized by one-pot synthetic approach as reported elsewhere. At first in a glass vial 0.4 mmol of octylamine, 0.1 mmol of PbBr.sub.2 were mixed in 200 L DMF solution. Later 50 L of HBr was mixed in this DMF solution to form the final precursor solution. In another glass beaker this precursor solution was added dropwise in 2 mL of hexane under vigorous stirring condition at room temperature. After 5 min the reaction was stopped by adding 3 mL of acetone and then centrifuged at 4500 rpm for 10 min. The precipitate obtained was collected for structural and photophysical studies.
Example 6
(111) Structural and Photophysical Studies:
(112) The absorbance spectra of the perovskite NPs in solution phase were recorded by Shimadzu UV1800 UV-VIS Spectrophotometer and PL spectra was recorded by Shimadzu RF-5301pc Spectrofluorophotometer. The absolute PLQY was measured by Ocean-optics USB4000 spectrometer with an integrated sphere excited at 400 nm laser beam. X-Ray diffraction analysis was carried out with XRD Bruker D8 Advance. The time-resolved PL was recorded by an Optronis Optoscope streak camera system. The excitation source is 400 nm femtosecond laser with pump intensity of 0.2 J/cm.sup.2. The imaging of the NPs was recorded by transmission electron microscopy (TEM, Jeol JEM-2010). The morphological imaging was carried out using field emission scanning electron microscopy (FESEM, JEOL JSM-7600F).
(113) TABLE-US-00001 TABLE 1 Details of the photophysical properties observed for mixed organo lead bromide perovskite NPs with different molar ratio of cations with oleylamine as the capping ligand. Absorbance peak PL peak position PL FWHM PLQY MABr:OABr position (nm) (nm) (nm) (%) 10:0 513 521 24 84 8:2 433, 510 519 26 92 6:4 397, 422, 502 512 37 82 4:6 397, 433, 450, 456, 476, 490 55 55 471, 486 3:7 397, 433, 451 438, 456, 474 25 30 2:8 397, 433 438, 451 23 21
(114) TABLE-US-00002 TABLE 2 Fitted PL lifetimes and the corresponding amplitude values. The 10:0 and 8:2 samples are fitted with single exponential decay and the others are fitted with bi-exponential decay functions. .sub.avg = A.sub.1.sub.1 + A.sub.2.sub.2. MABr:OABr A.sub.1 .sub.1 (ns) A.sub.2 .sub.2 (ns) .sub.avg (ns) 10:0 1 11.7 0.1 8:2 1 10.8 0.1 6:4 0.59 6.2 0.1 0.41 2.0 0.1 2.0 0.1 3:7 0.79 2.2 0.1 0.21 2.0 0.1 2.0 0.1 2:8 0.84 2.0 0.1 0.16 2.0 0.1 2.0 0.1
(115) TABLE-US-00003 TABLE 3 PLQY obtained for the mixed organo lead bromide perovskite NPs in different time intervals. PLQY (%) (during PLQY (%) PLQY (%) (after MABr:OABr synthesis (after one month) two months) 10:0 84 45 0 8:2 92 85 60 6:4 82 60 20 4:6 55 30 0 3:7 30 10 0 2:8 21 0 0
(116) TABLE-US-00004 TABLE 4 Photospectroscopic data observed for mixed organo lead bromide perovskite NPs with different molar ratio of cations with octylamine as the capping ligand. PL Absorbance peak PL peak FWHM PLQY MABr:OABr position (nm) position (nm) (nm) (%) 10:0 509 523 20 67 8:2 433, 507 521 22 58 6:4 433, 450, 470, 486 501 36 52 4:6 433, 450, 471, 486 457, 477, 493 38 47 3:7 433, 451 438, 455, 472 40 38 2:8 397, 433 438, 451 28 25
Example 7Linear Optical Properties and Structural Characterization (Incl. Density Function Theory Modelling)
(117) Briefly, the core-only MAPbBr.sub.3 NCs and core-shell MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs are of spherical shape with diameters of ca. 8-9 nm and 9-10 nm, respectively. Whereas, the comparison standard (i.e., CsPbBr.sub.3 NCs) are approximately 9 nm-sized of cuboidal shape. The one-photon absorption (1 PA) and one-photon-excited PL spectra of the MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs in toluene are displayed in
(118) The XRD patterns of the MAPbBr.sub.3 core, MAPbBr.sub.3-(OA).sub.2PbBr.sub.4 core-shell type and CsPbBr.sub.3 NCs are displayed in
(119) Photo electron spectroscopy in air (PESA) measurements on MAPbBr.sub.3 and (OA).sub.2PbBr.sub.4 thin films were performed to estimate the valance band maximum (VBM) alignment between the core and shell in the core-shell MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs (
(120) In order to theoretically investigate the conduction and valence band-edge alignment between the core and shell in the core-shell NCs, there was employed the all-electron-like projector augmented wave (PAW) method and the Perdew-Burke-Ernserhof (PBE) exchange correlation potential, as implemented in the VASP code. The resulting band offset of MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 is then given by:
(121)
(122) The calculated band offset of MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs is presented in
Example 8Giant Five-Photon Absorption from Perovskite Colloidal NCs
(123) The schematic illustration of the type-I conduction and valence band edge alignment between the core and shell in the core-shell MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs is displayed in
(124) TABLE-US-00005 TABLE 5 Multi-photon action cross-sections .sub.n of hybrid halide perovskite NCs over their respective wavelength range.sup.# Multi-photon excitation Two-photon Three-photon .sub.2 (10.sup.6 GM) .sub.3 (10.sup.74 cm.sup.6s.sup.2photon.sup.2) Perovskite NCs (675-1000 nm) (1050-1500 nm) MAPbBr.sub.3 0.41 0.06 0.33 0.05 to 5.2 0.8 to 2.7 0.4 MAPbBr.sub.3/ 3.0 0.4 2.5 0.4 (OA).sub.2PbBr.sub.4 to 37 6 to 22 3 CsPbBr.sub.3 0.97 0.15 0.38 0.06 to 13 2 to 7.6 1.1 Multi-photon excitation Four-photon .sub.4 (10.sup.104 cm.sup.8s.sup.3 Five-photon photon.sup.3) .sub.5 (10.sup.136 cm.sup.10s.sup.4photon.sup.4) Perovskite NCs (1550-2000 nm) (2050-2300 nm) MAPbBr.sub.3 0.036 0.005 0.039 0.006 to 3.0 0.5 to 2.4 0.4 MAPbBr.sub.3/ 0.21 0.03 0.29 0.04 (OA).sub.2PbBr.sub.4 to 24 4 to 20 3 CsPbBr.sub.3 0.071 0.011 0.092 0.014 to 6.9 1.0 to 6.5 1.0 .sup.#The experimental error 15% stems mainly from the uncertainty in fluctuation of input laser pulse energy and determination of laser beam characteristics such as pulse duration and minimum beam waist, which are essential for both open-aperture Z-scan and MEPL measurements.
Example 9Multiphoton Excited Frequency-Upconverted Photoluminescence (PL) Measurements and Characterization of Multiphoton Action Cross-Section Spectra in Perovskite NCs
(125) Multi-photon excited photoluminescence (MEPL) from MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 dispersed in toluene were investigated at room temperature by utilizing fs laser pulses with excitation wavelengths ranging from 675 to 2300 nm for excitation. For comparison purpose, MEPL from toluene solution of CsPbBr.sub.3 NCs were also studies under the same excitation condition. Dilute colloidal NC solutions in toluene, contained in 2-mm-thick quartz cuvettes, were employed for the MEPL measurements.
(126) MEPL measurements have been applied on the MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs at wavelengths ranging from 675 to 2300 nm using the measured .sub.2 values at 800 nm as a standard to determine their MPA cross-sections (.sub.n), thus acquiring the MPA spectra. Through integrating .sub.n given by Eq. 2 over the entire laser focused volume and time, we quantify and obtain the MEPL strength F.sub.n.
F.sub.n=f.sub.n=(1/n).sub.n[I.sub.i(r,z,t)].sup.n/(h).sup.ndsdzdt(2)
Factor 1/n denotes the fact that n-photons are simultaneously absorbed from infrared incident laser beam for generating each fluorophore excitation. is MEPL collection efficiency of the experimental setup, is molar concentration of NCs, is PLQY and the product of and .sub.n is multi-photon action cross-section, a direct measurement of MEPL brightness. I.sub.i(r,z,t) is the incident laser intensity at the small volume of ds.Math.dz in sample at time t. The beam waist at the sample point is w(d)=w.sub.0{square root over (1+d.sup.2/z.sub.0.sup.2)}. d is the distance of the sample to the focal point. w.sub.0 is the beam waist of laser beam at the focal point. z.sub.0 is the Rayleigh length and is related to w.sub.0 by z.sub.0=w.sub.0.sup.2/.sub.0. Taking account of the fact that NCs contained in 2-mm-thick quartz cuvettes were placed at 3.5 cm from the lens focal point and considering the spatial and temporal profiles of the laser pulses are Gaussian functions, the MEPL signal F.sub.n (n=2, 3, 4, and 5) for 2 PA, 3 PA, 4 PA and 5 PA processes can be derived as:
F.sub.2.sup.3/2.sub.2L.sub.p.sub.0.sup.2d.sup.2I.sub.0.sup.2/[8{square root over (2)}z.sub.0.sup.2(h).sup.2](3)
F.sub.3.sup.3/2.sub.3Lp.sub.0.sup.2d.sup.2I.sub.0.sup.3/[18{square root over (3)}z.sub.0.sup.2(h).sup.3](4)
F.sub.4.sup.3/2.sub.4L.sub.p.sub.0.sup.2d.sub.2I.sub.0.sup.4/[64z.sub.0.sup.2(h).sup.4](5)
F.sub.5.sup.3/2.sub.5L.sub.p.sub.0.sup.2d.sub.2I.sub.0.sup.5/[50{square root over (5)}z.sub.0.sup.2(h).sup.4](6),
respectively. In which the approximation of 1+d.sup.2/z.sub.0.sup.2d.sup.2/z.sub.0.sup.2 is taken with the fact that d.sup.2/z.sub.0.sup.2>>1. d is distance between sample and focal point of the lens (3.5 cm). .sub.p is laser pulse width at e.sup.1 maximum, I.sub.0 is laser intensity at the sample position. Through applying the expressions of F.sub.n (n=2, 3, 4, and 5) (Eqs. 3-6) and utilizing the .sub.2 values at 800 nm measured by Z-scan as standard, .sub.n (n=2, 3, 4, and 5) values of MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs can be obtained over wavelength range 675-2300 nm, as shown in
(127)
(128) Table 5 complies the elucidated .sub.n for MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs. Comparatively, the .sub.n (n=2, 3, 4, and 5) of MAPbBr.sub.3 NCs are around 2-3 times smaller than that of CsPbBr.sub.3 NCs whereas the core-shell type MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs exhibit around 3 times larger .sub.n values than that of CsPbBr.sub.3 NCs. Moreover, the .sub.2 values of the core and core-shell type halide perovskite NCs are 1-2 orders larger than that of large size CdSe/CdS dot in rod heterostructures (39 or 180 nm length CdS nanorod, .sub.2(1.11.3)10.sup.5 GM); and are 2-3 orders larger than traditional inorganic semiconductor NCs and organic chromophores ((.sub.2).sub.max10.sup.4 GM). For .sub.3 values, these NCs are 1-2 orders larger than the strongly (or overly) excited ZnSe/ZnS core-shell NCs (.sub.3 (3.14.1)10.sup.76 cm.sup.6s.sup.2 photon.sup.2, where three-photon-excited intraband absorption has a significant contribution) and the large CdSe/CdS dot-in-rod heterostructure (39 nm length CdS nanorod, .sub.3 (1.98.4)10.sup.76 cm.sup.6s.sup.2 photon.sup.2). The core and core-shell type halide perovskite NCs exhibit .sub.3 values 2-3 orders of magnitude higher than the best performing conventional inorganic semiconductor NCs (that are not overly-excited and with size 10 nm) and organic molecules ((.sub.3).sub.max 10.sup.76 cm.sup.6s.sup.2 photon.sup.2). For the higher order .sub.4 values, the NCs are about 3-5 orders larger than the best reported results of organic chromophores ((.sub.4)(1.010.sup.111)(5.610.sup.109) cm.sup.8s.sup.3 photon.sup.3). However, there are only limited research efforts devoted to studying the four-photon process in the conventional inorganic semiconductor NCs. Amazingly, the .sub.5 values of the multidimensional core-shell type NCs are >9 orders larger than specially designed organic molecules (.sub.510.sup.145 cm.sup.10s.sup.4/photon.sup.4), which is a record for semiconductor NCs. Although the Luttinger and Kohn and Pidgeon and Brown models within the k.Math.p approach have been successfully applied to conventional metal-chalcogenide NCs to model their 2 PA/3 PA spectral dependences and estimate their .sub.2/.sub.3, such approach cannot be directly applied to halide perovskite NCs. This is because these methods are only suitable for the two-photon transitions from s-type valence band to p-type conduction band as in the former, unlike the all p-type valence and conduction bands in the latter. The theoretical study on the MPA properties of the halide perovskite NCs will be the focus of a future work.
Example 10Open-Aperture Z-Scan Measurements for Quantifying 2 PA Cross-Sections at 800 nm and 3 PA Cross-Sections at 1050 and 1100 nm
(129) The 2 PA cross-sections (.sub.2 values at 800 nm) of the colloidal NCs (measured using the open-aperture Z-scan technique) were employed as a standard for multi-photon excited PL (MEPL) measurements at different wavelengths.
(130) 2 PA cross-sections (.sub.2) of the NC solutions can be obtained through fitting the normalized transmittance to the well-established Z-scan theory as:
(131)
q(z)=(1R)I.sub.00L.sub.eff/(1+z.sup.2/z.sub.0.sup.2), =N.sub.2/(h). R is reflection from the sample front surface; I.sub.00 is peak intensity at the focal point of the incident laser beam; L.sub.eff=L at 800 nm and L is sample thickness due to the negligible 1 PA at this wavelength; N is concentration of NCs; ho is the incident photon energy. .sub.2 of the MAPbBr.sub.3, and MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 at 800 nm were estimated to be approximately (0.80.1)10.sup.6 GM and (5.00.8)10.sup.6 GM, respectively. On the other hand, the .sub.2 value of the CsPbBr.sub.3 NCs at 800 nm was derived to be around and (2.00.3)10.sup.6 GM, in agreement with literature reports. Taking account of both the volume and the local field effects, the elucidated .sub.2 value of the MAPbBr.sub.3 NCs, is about three-orders of magnitude larger than the result corresponding to the recently reported 2 PA coefficient of bulk MAPbBr.sub.3 crystal (.sub.2 corresponding to the bulk MAPbBr.sub.3 crystal is derived with dielectric constants of toluene and MAPbBr.sub.3 (.sub.0=2.38 and =25.5, respectively)). Such large enhancement results from the quantum confinement effect, which has been well-documented in conventional semiconductor NCs. Moreover, the shell coating with (OA).sub.2PbBr.sub.4 has further enhanced the 60 of the MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs at 800 nm by 6.5 times. The ratio between the acquired .sub.2 values of MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs at 800 nm is consistent with that obtained from the two-photon-excited PL measurements (
(132) Moreover, the good agreement of the measured 3 PA cross-sections with those acquired from open-aperture Z-scan measurements at 1050 and 1100 nm (see
(133)
(134) To acquire the 3 PA cross-sections of the NC solutions, the below well-established Z-scan theory were applied to fit the normalized open-aperture Z-scan transmittance:
(135)
p.sub.0(z)=(2(1R).sup.2L.sub.effI.sub.00.sup.2/(1+z.sup.2/z.sub.0.sup.2).sup.2).sup.1/2, =N.sub.3/(h).sup.2. L.sub.eff=L at 1050 and 1100 nm and L is sample thickness; .sub.3 is the 3 PA cross-section. 3 PA cross-sections (.sub.3) of the MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs at 1050 nm were estimated to be approximately (2.30.3)10.sup.74 cm.sup.6s.sup.2 photon.sup.2, (203)10.sup.74 cm.sup.6s.sup.2 photon.sup.2 and (6.71.0)10.sup.74 cm.sup.6s.sup.2 photon.sup.2, respectively. Moreover, for excitation at 1100 nm, the 3 PA cross-sections (.sub.3) of the MAPbBr.sub.3, MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 and CsPbBr.sub.3 NCs were calculated to be approximately (0.550.08)10.sup.74 cm.sup.6s.sup.2 photon.sup.2, (3.30.5)10.sup.74 cm.sup.6s.sup.2 photon.sup.2 and (1.90.3)10.sup.74 cm.sup.6s.sup.2 photon.sup.2. The obtained .sub.3 of perovskite NCs through the open-aperture Z-scan measurements are highly consistent with the results acquired from multiphoton excited upconversion PL measurements (
(136) The core and core-shell organic-inorganic halide perovskite NCs possesses much higher .sub.n values than those of traditional inorganic semiconductor NCs and organic chromophores (Table 5), highlighting their potential for nonlinear optics and bioimaging applications, such as optical limiting, three-dimensional microscopy for deep tissue imaging and sensing. Moreover, the core-shell organic-inorganic halide perovskite NCs demonstrate larger (about 3 times) .sub.n values than the new two-photon absorbing benchmark of CsPbBr.sub.3 NCs. Apart from having high PLQY (i.e., 84%, 92% for MAPbBr.sub.3 and MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs, respectively), these lead bromide perovskite NCs also possess giant o values, which stems mainly from the intrinsic strong MPA of lead bromide perovskites. Through growing a (OA).sub.2PbBr.sub.4 shell over the MAPbBr.sub.3 core, the PLQY can be enhanced to 92% and the photostability can be improved. Most importantly, the presence of the (OA).sub.2PbBr.sub.4 shell enhances the .sub.n by almost an order compared to the core-only MAPbBr.sub.3 NCs across all wavelengths from 675 to 2300 nm. Given that both the MAPbBr.sub.3 and MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs are in the weak confinement regime (d.sub.B4 nm<<8-9 nm diameter), it is possible to enhance these .sub.n values even further through even smaller strongly-confined MAPbBr.sub.3 NCs, their core-shell counterparts (i.e., NCs' diameter<4 nm). However, at current stage, it is extremely challenging to synthesize small MAPbBr.sub.3 and CsPbBr.sub.3 NCs with high crystalline quality, low surface defects, uniform size distribution, and relatively high reaction yield, which are needed to conduct detailed investigations of the quantum confinement effect on the MPA of lead bromide perovskite NCs. Presently, there have been no reports on the synthesis of small-sized core-shell MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs. Therefore, investigation on the detailed dependence of MPA on the quantum confinement effect will one of the main future works.
Example 11Time-Resolved PL Measurements and Discussion on the Underlying Physical Mechanisms for the Largely Enhanced Multiphoton Action Cross-Sections of the Multi-Dimensional Core-Shell Perovskite NCs
(137) Previous studies on conventional inorganic semiconductor NCs have shown that the 2 PA and 3 PA cross-sections can be enhanced by an outer shell covering through: surface passivation effects; antenna-like effect; photoinduced screening of the internal field; and/or local field effects. To establish the origins for the .sub.n enhancement of the core-shell MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs and to gain more insights into the dynamics of excited photocarriers, time-resolved PL (TRPL) measurements using single (400 nm) and multi-photon (e.g., 2P (800 nm), 3P (1200 nm), 4P (1600 nm) and 5P (2100 nm)) excitation were performed.
(138) The increased PL lifetimes (from one- and multi-photon excitation
(139) Next, the relatively large lattice mismatch between the core MAPbBr.sub.3 and shell (OA).sub.2PbBr.sub.4 could also induce intrinsic piezoelectric polarization charges at the core-shell interface that result in an internal electric field. This indicates that the photoinduced screening of the internal field by the photoexcited electron-hole pairs could be another possible origin for the enhanced .sub.n in MAPbBr.sub.3/(OA).sub.2PbBr.sub.4 NCs. Furthermore, the dielectric confinement (local field effect) resulting from the relatively large difference between the dielectric constants of core MAPbBr.sub.3 and shell (OA).sub.2PbBr.sub.4 could be another factor. Therefore, it is likely that an interplay of various factors arising from the effective surface passivation, the nonradiative energy transfer from the shell to the core through antenna-like effect, the photoinduced screening of the internal field, the local field effect or its combination gives rise to the giant MPA cross-sections of these core-shell multidimensional halide perovskites NCs.
(140) The outstanding higher order nonlinear optical properties of the core and core-shell organic-inorganic halide perovskite colloidal NCs (particularly the highly efficient five-photon excited upconversion fluorescence in the multidimensional core-shell perovskite NCs (e.g., MAPbBr.sub.3/(OA).sub.2PbBr.sub.4)) indicate their great potential for developing next generation highly efficient, sensitive multiphoton imaging applications with unmatched imaging depth and resolution. Although the intrinsic low stability of halide perovskite NCs in polar solvents (such as water) and their cytoxicity from the Pb.sup.2+ ion could be an issue for the potential applications in multi-photon bio-imaging, such technical challenges could be circumvented through the following three possible encapsulation approaches:
(141) First, Encapsulation with an SiO.sub.x/SiO.sub.2 Inert Shell/Matrix.
(142) Utilizing SiO.sub.x/SiO.sub.2 either as an additional shell or as a medium to embed several NCs will help to enhance the stability as well as reduce the cytoxicity. Such approach has been successfully applied to traditional inorganic semiconductor NCs for efficient bio-imaging applications. Very recently, encapsulating lead bromide NCs into a SiO.sub.x spherical matrix (about 150 nm and 470 nm in diameter) have been realized by Huang et al. This provides a crucial proof-of-concept on the viability of the approach, although more work is required to achieve finer control of SiO.sub.x/SiO.sub.2 encapsulation for each perovskite NC.
(143) Second, Encapsulation with Ligands.
(144) Through utilizing 3-aminopropyltriethoxysilane (APTES) as a branched capping ligand to replace the conventional straight-chained ligands, Luo et al. achieved enhanced stability in the APTES-coated MAPbBr.sub.3 NCs. Such APTES-coated MAPbBr.sub.3 NCs show an increased stability in 2-propanol. Furthermore, the available silane group allows for additional sol-gel reactions which may further increase the stability of the NCs.
(145) Third, Encapsulation with Solid Lipid Structures.
(146) More recently, Gomez et al. reported the application of solid lipid structures to encapsulate CsPbBr.sub.3 NCs that were stable up to 2 months in water, albeit at a low PLQY (around 11%) likely due to initial water degradation. Further work is needed to circumvent the initial degradation and realize water-stable NCs at high PLQY.
(147) Fourth, Encapsulation in the Voids of Porous Metal-Organic Frameworks.
(148) The core and core-shell nanocrystals may be further encapsulated in the voids of porous metal-organic frameworks, such as Cu.sub.3(1,3,5-benzene tricarboxylate).sub.2 (HKUST-1), Zn.sub.4O nodes with 1,4-benzodicarboxylic acid struts (IRMOF-1), other IRMOF series (like IRMOF-10 and IRMOF-16), zinc ions coordinated by four imidazolate rings (ZIF-8), UiO-66 made up of [Zr.sub.6O.sub.4(OH).sub.4] clusters with 1,4-benzodicarboxylic acid struts, etc. to enhance the multiphoton absorption property and improve stability and biocompatibility.
(149) These examples clearly show that the potential stability and cytotoxicity issues of halide perovskite NCs in aqueous media for multiphoton imaging applications could in fact be overcome through a judicious choice of the encapsulation approach and careful optimization. Through tuning the emission wavelengths to the infrared by developing appropriate synthesis strategy, these halide perovskite colloidal nanocrystals could enable even deeper imaging for deep-tissue bio-imaging, where both penetration of incident photons and extraction of emitting photons are essential.
(150) While the invention has been particularly shown and described with reference to specific embodiments, it should be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is thus indicated by the appended claims and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced.