Composite layers for bonding components of a wind turbine rotor blade

Abstract

The present disclosure is directed to a method for bonding composite blade components of a rotor blade of a wind turbine. The method includes providing a first blade component being constructed of a first composite material. The method also includes providing a second blade component being constructed of a second composite material. Further, the method includes arranging the first and second blade components together at an interface. Another step includes placing one or more layers of a wetted composite material between the first and second blade components at the interface. The method also includes allowing the one or more layers of the wetted composite material at the interface to cure.

Claims

1. A method for bonding composite blade components of a rotor blade of a wind turbine, the method comprising: providing a resin bath that contains a resin that includes one of a thermoset or thermoplastic material; forming a wetted fiber material by drawing a fiber material through the resin bath, the formed wetted fiber material comprising the fiber material and the resin; further processing the formed wetted fiber material into strips or roles to form at least one layer of wetted fiber material; providing a first blade component being constructed of a first composite material; providing a second blade component being constructed of a second composite material; arranging the first and second blade components adjacent to each other; placing the at least one layer of processed, wetted fiber material in a wetted state between the first and second blade components at an interface therebetween; and curing the at least one layer of the processed, wetted fiber material at the interface.

2. The method of claim 1, wherein placing the at least one layer of the processed, wetted fiber material at the interface further comprises unrolling the wetted fiber material at the interface.

3. The method of claim 1, further comprising layering the processed wetted fiber material at the interface.

4. The method of claim 1, wherein the fiber material comprises at least one of glass fibers, carbon fibers, metal fibers, polymer fibers, ceramic fibers, nanofibers, or combinations thereof.

5. The method of claim 1, wherein the first and second composite materials comprise prefabricated composite materials, the prefabricated composite materials comprising one or more cured resin materials reinforced with at least one fiber material.

6. The method of claim 1, wherein the first blade component comprises a shear web of the rotor blade and the second blade component comprises a spar cap of the rotor blade.

7. The method of claim 1, wherein the first blade component comprises a spar cap of the rotor blade and the second blade component comprises a blade shell of the rotor blade.

8. The method of claim 1, wherein the first blade component comprises a pressure side of the rotor blade and the second blade component comprises a suction side of the rotor blade.

9. A method for bonding a shear web between opposing spar caps of a rotor blade of a wind turbine, the shear web having a first end and a second end, the method comprising: providing a resin bath that contains a resin that includes one of a thermoset or thermoplastic material; forming a wetted fiber material by drawing a fiber material through the resin bath, the formed wetted fiber material comprising the fiber material and the resin; further processing the formed wetted fiber material into strips or roles to form at least one layer of wetted fiber material; arranging the shear web between the opposing spar caps, wherein the first end of the shear web contacts an upper spar cap at a first interface and the second end of the shear web contacts a lower spar cap at a second interface; placing the at least one layer of processed, wetted fiber material in a wetted state at the first and second interfaces; and curing the at least one layer of the processed, wetted fiber material at the first and second interfaces.

10. The method of claim 9, wherein placing the processed wetted fiber material at the first and second interfaces further comprises unrolling the wetted fiber material at the first and second interfaces.

11. The method of claim 9, further comprising layering the fiber material at the first and second interfaces.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) A full and enabling disclosure of the present invention, including the best mode thereof, directed to one of ordinary skill in the art is set forth in the specification, which makes reference to the appended figures, in which:

(2) FIG. 1 illustrates a perspective view of one embodiment of a wind turbine according to the present disclosure;

(3) FIG. 2 illustrates a perspective view of one embodiment of a rotor blade of a wind turbine according to the present disclosure;

(4) FIG. 3 illustrates a cross-sectional view of the rotor blade of FIG. 2 along line 3-3;

(5) FIG. 4 illustrates a detailed, cross-sectional view of a bonded interface between the shear web and spar cap of FIG. 3 according to conventional construction;

(6) FIG. 5 illustrates a flow diagram of one embodiment of a method for bonding a shear web between opposing spar caps of a rotor blade of a wind turbine;

(7) FIG. 6 illustrates a schematic diagram of one embodiment of a process for bonding composite blade components of a rotor blade of a wind turbine according to the present disclosure;

(8) FIG. 7 illustrates a detailed, cross-sectional view of one embodiment of a bonded interface between the shear web and spar cap of FIG. 3 according to the present disclosure;

(9) FIG. 8 illustrates a schematic diagram of another embodiment of a process for bonding composite blade components of a rotor blade of a wind turbine according to the present disclosure; and

(10) FIG. 9 illustrates a flow diagram of one embodiment of a method for bonding composite blade components of a rotor blade of a wind turbine according to the present disclosure.

DETAILED DESCRIPTION OF THE INVENTION

(11) Reference now will be made in detail to embodiments of the invention, one or more examples of which are illustrated in the drawings. Each example is provided by way of explanation of the invention, not limitation of the invention. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the scope or spirit of the invention. For instance, features illustrated or described as part of one embodiment can be used with another embodiment to yield a still further embodiment. Thus, it is intended that the present invention include such modifications and variations as come within the scope of the appended claims and their equivalents.

(12) Generally, the present disclosure is directed a method for bonding composite blade components of a rotor blade of a wind turbine. For example, the method includes arranging two or more composite blade components together at an interface. Another step includes placing one or more layers of a wetted composite material between the first and second blade composite components at the interface and allowing the one or more layers of the wetted composite material at the interface to cure. Thus, the method of the present disclosure replaces conventional bond paste with hand-lay up (HLU) resin layers reinforced with one or more fiber materials. Further, in certain embodiments, the HLU bonded interface can be constructed by drawing the fabric glass through a resin bath in order to wet the fabric sufficiently. The wetted fabric can then be spread, e.g. via hand, by unrolling the fabric onto the desired bond area. Thus, in certain embodiments, the wetted fiber material may include a roll of continuous fiber material that can be easily unrolled and applied at the interface. The HLU can then cure and form an effective bond between the two prefabricated composite components.

(13) The present subject matter provides numerous advantages not present in the prior art. For example, the present disclosure provides a lower cost bonding solution than conventional bond paste. Further, the method of the present disclosure provides compatibility with current resin system and manufacturing processes. In addition, the method of the present disclosure provides the ability to laminate various thicknesses and to tailor fit blade components. Thus, the method described herein provides a reinforced bonding component to join the rotor blade at multiple locations, including but not limited to the shear webs, leading and trailing edges, and spar caps.

(14) Referring now to the drawings, FIG. 1 illustrates one embodiment of a wind turbine 10 according to the present disclosure. As shown, the wind turbine 10 includes a tower 12 with a nacelle 14 mounted thereon. A plurality of rotor blades 16 are mounted to a rotor hub 18, which is in turn connected to a main flange that turns a main rotor shaft. The wind turbine power generation and control components are housed within the nacelle 14. The view of FIG. 1 is provided for illustrative purposes only to place the present invention in an exemplary field of use. It should be appreciated that the invention is not limited to any particular type of wind turbine configuration.

(15) Referring now to FIG. 2, a more detailed view of one of the rotor blades 16 of FIG. 1 is illustrated. As shown, the rotor blade 16 includes an upper shell member 20 (e.g. a suction side) and a lower shell member 22 (e.g. a pressure side). Further, the upper shell member 20 is configured as the suction side surface of the blade 16, while the lower shell member 22 is configured as the pressure side surface of the blade 16. The rotor blade 16 also includes a leading edge 24 and a trailing edge 26, as well as a root portion 28 and a tip portion 30. As is well known in the art, the upper shell member 20 and the lower shell member 22 may be joined together at the leading edge 24 and trailing edge 26 or any other suitable location. The rotor blade 16 also includes an internal cavity 25 (FIG. 3) in which various structural members, such as spar caps 32, 34 and one or more shear webs 30 according to the present disclosure, may be configured It should also be understood that the rotor blade 16 of FIG. 2 is provided for illustrative purposes only. For example, in additional embodiments, the rotor blade may be a modular rotor blade such as described in U.S. application Ser. No. 14/753,137 entitled Modular Wind Turbine Rotor Blades and Methods of Assembling Same filed on Jun. 29, 2015 and which is incorporated herein by reference in its entirety.

(16) Referring now to FIGS. 3 and 5-8, various views of the rotor blade 16 of FIG. 2 are illustrated that incorporate various aspects of the present invention. As shown generally in the figures, the upper shell member 20 contains an upper spar cap 32 configured on an internal surface thereof. Similarly, the lower shell member 22 contains a lower spar cap 34 configured on an internal surface thereof. The shear web 30 extends between the spar caps 32, 34 along a longitudinal length of the blade 16 in a generally span-wise direction. Further, as shown generally in the figures, the shear web 30 has a first end 36 and a second end 38. More particularly, the shear web 30 may be constructed of a panel 35 having of a core material 28 enclosed, at least in part, by an outer skin layer 40. It should be understood that the core material 28 may include any suitable core material, including but not limited to, low-density foam, cork, composites, balsa wood, composites, or similar. Suitable low-density foam materials may include, but are not limited to, polystyrene foams (e.g., expanded polystyrene foams), polyurethane foams (e.g. polyurethane closed-cell foam), other foam rubbers/resin-based foams and various other open cell and closed cell foams.

(17) In addition, as shown, the first end 36 may be secured to the upper spar cap 32 at a first interface 42 and the second end 36 may be secured to the lower spar cap 34 at a second interface 44. More specifically, as shown in FIG. 7, the shear web 30 may be secured to the upper and lower spar caps 32, 34 at the first and second bonded interfaces 42, 44 via one or more composite materials 50 configured between the first and second ends 36, 38 of the shear web 30 and the upper and lower spar caps 32, 34, respectively. Thus, in certain embodiments, the bonded interfaces 42, 44 may include hand-lay up (HLU) resin layers reinforced with one or more fiber materials.

(18) For example, as shown in FIGS. 5-9, various figures are illustrated to illustrate the bonding process for the shear web 30 between the spar caps 32, 34 according to one embodiment of the present disclosure. More specifically, as shown in FIG. 5, a flow diagram of a method 100 for bonding the shear web 30 between opposing spar caps 32, 34 of the rotor blade 16 of the wind turbine 10 is illustrated. As shown at 102, the method 100 includes arranging the shear web 30 between the opposing spar caps 32, 34 such that the first end 35 of the shear web 30 contacts the upper spar cap 32 at the first interface 42 and the second end 38 of the shear web 30 contacts the lower spar cap 34 at the second interface 44. In addition, as shown at 104, the method 100 includes placing one or more layers of a wetted composite material 50 at the first and second interfaces 42, 44. Further, as shown at 106, the method 100 includes allowing the one or more layers of the wetted composite material 50 at the first and second interfaces 42, 44 to cure.

(19) More specifically, as shown in FIG. 6, the step of placing one or more layers of the wetted composite material at the first and second interfaces 42, 44 may include drawing a fiber material 52 through a resin bath 56. More specifically, the fiber material may include at least one of glass fibers, carbon fibers, metal fibers, polymer fibers, ceramic fibers, nanofibers, or combinations thereof. In addition, the resin material in the resin bath 56 may include a thermoset material, a thermoplastic material, or similar, or combinations thereof. The thermoplastic materials as described herein generally encompass a plastic material or polymer that is reversible in nature. For example, thermoplastic materials typically become pliable or moldable when heated to a certain temperature and returns to a more rigid state upon cooling. Further, thermoplastic materials may include amorphous thermoplastic materials and/or semi-crystalline thermoplastic materials. For example, some amorphous thermoplastic materials may generally include, but are not limited to, styrenes, vinyls, cellulosics, polyesters, acrylics, polysulphones, and/or imides. More specifically, exemplary amorphous thermoplastic materials may include polystyrene, acrylonitrile butadiene styrene (ABS), polymethyl methacrylate (PMMA), glycolised polyethylene terephthalate (PET-G), polycarbonate, polyvinyl acetate, amorphous polyamide, polyvinyl chlorides (PVC), polyvinylidene chloride, polyurethane, or any other suitable amorphous thermoplastic material. In addition, exemplary semi-crystalline thermoplastic materials may generally include, but are not limited to polyolefins, polyamides, fluropolymer, ethyl-methyl acrylate, polyesters, polycarbonates, and/or acetals. More specifically, exemplary semi-crystalline thermoplastic materials may include polybutylene terephthalate (PBT), polyethylene terephthalate (PET), polypropylene, polyphenyl sulfide, polyethylene, polyamide (nylon), polyetherketone, or any other suitable semi-crystalline thermoplastic material. Further, the thermoset materials as described herein generally encompass a plastic material or polymer that is non-reversible in nature. For example, thermoset materials, once cured, cannot be easily remolded or returned to a liquid state. As such, after initial forming, thermoset materials are generally resistant to heat, corrosion, and/or creep. Example thermoset materials may generally include, but are not limited to, some polyesters, some polyurethanes, esters, epoxies, or any other suitable thermoset material.

(20) Still referring to FIG. 6, as shown, the wetted fiber material 52 may then be cut via a cutter 58 into strips or sheets of composite material 50. Thus, as shown in FIG. 7, the sheets or strips of composite material 50 may be easily placed into one or more layers at the interfaces 42, 44 between the shear web 30 and the spar caps 32, 34. Once placed, the method 100 may also include curing the wetted fiber material 52 at the interfaces 42, 44, e.g. by allowing the wetted material to dry.

(21) In another embodiment, the step of placing the wetted fiber material 52 at the interfaces 42, 44 may include unrolling, e.g. by hand or automatically, the wetted fiber material 52 at the interfaces 42, 44. For example, as shown in FIG. 8, the wetted fiber material 52 may be rolled into one or more rolls of composite material 50 after being drawn through the resin bath 56. Thus, the rolls of composite material 50 may be unrolled at one or more of the interfaces 42, 44 and allowed to cure. Thus, in certain embodiments, the wetted fiber material 52 may include a roll of continuous fiber material that can be easily unrolled and applied at the interface, e.g. along the span of the rotor blade 16. Accordingly, as shown, the bonded interfaces 42, 44, once cured, include one or more layers of a cured composite material 50.

(22) Referring now to FIG. 9, a flow diagram of a method 200 for bonding composite blade components of the rotor blade 16 of the wind turbine 10 is illustrated. As shown at 202, the method 200 includes providing a first blade component being constructed of a first composite material. As shown at 204, the method 200 includes providing a second blade component being constructed of a second composite material. In certain embodiments, the first and second composite materials may include prefabricated composite materials. For example, as described herein, the prefabricated composite materials may include one or more cured resin materials reinforced with at least one fiber material. More specifically, as mentioned, the first blade component may include a shear web 30 of the rotor blade 16, whereas the second blade component may include a spar cap 32, 34 of the rotor blade 16. In an alternative embodiment, the first blade component may include a spar cap 32, 34 of the rotor blade 16, whereas the second blade component may include a blade shell 20, 22 of the rotor blade 16. In yet another embodiment, the first blade component may include a pressure side 22 of the rotor blade 16 and the second blade component may include a suction side 20 of the rotor blade 16. In additional embodiments, the blade components may also include ancillary components, including but not limited to balance boxes, root close-out, and/or aerodynamic add-on features. Thus, it should also be understood that the method as described herein may encompass bonding any composite materials of the rotor blade 16 together and are not limited to the components as specifically explained herein.

(23) Thus, as shown at 206, the method 200 includes arranging the first and second blade components together at an interface. As shown at 208, the method 200 includes placing one or more layers of a wetted composite material between the first and second blade components at the interface. As shown at 210, the method 200 also includes allowing the one or more layers of the wetted composite material at the interface to cure.

(24) While the present subject matter has been described in detail with respect to specific exemplary embodiments and methods thereof, it will be appreciated that those skilled in the art, upon attaining an understanding of the foregoing, may readily produce alterations to, variations of, and equivalents to such embodiments. Accordingly, the scope of the present disclosure is by way of example rather than by way of limitation, and the subject disclosure does not preclude inclusion of such modifications, variations and/or additions to the present subject matter as would be readily apparent to one of ordinary skill in the art.