METHODS AND MATERIALS SYSTEMS FOR ENHANCING CORROSION RESISTANCE OF SOLID MATERIALS AND CORROSION RESISTANT DEVICES MADE THEREFROM
20200010958 ยท 2020-01-09
Assignee
Inventors
Cpc classification
International classification
Abstract
A method for enhancing corrosion resistance of a solid material exposed to a liquid. The method includes providing a solid material which can form a solid product layer when exposed to the corrosive liquid, and maintaining the concentration of the solid product material in the liquid either at saturation or elevated level. A materials system containing a solid material capable of forming a solid product layer when exposed to air or a liquid environment containing dissolved oxygen at levels sufficient for oxidation of at least one constituent of the solid material, wherein the solid product layer is in contact with a liquid containing an elevated or saturated concentration of the dissolved solid product layer. A corrosion-resistant device containing a solid material with a solid-product layer exposed to a molten salt solution, wherein the concentration of the solid-product dissolved in the molten salt solution is at saturation or elevated level.
Claims
1. A method for enhancing corrosion resistance of a solid material exposed to a liquid, the method comprising; providing a solid material whose corrosion resistance to a liquid is desired to be enhanced and which is capable of forming a solid product layer when exposed to a gas or to the liquid containing chemical elements needed to react with the solid material to form the solid product layer; and maintaining the concentration of the solid product material in the liquid either at saturation level or at an elevated level.
2. The method of claim 1, wherein the liquid is a molten salt or a molten salt solution.
3. The method of claim 1, wherein the solid material is a metallic material.
4. The method of claim 3, wherein the metallic material is one or more than one of chromium, chromium-bearing material, aluminum, aluminum-bearing material, silicon, silicon-bearing material, beryllium, beryllium-bearing material, nickel, nickel-bearing material, iron, iron-bearing material, cobalt, cobalt-bearing material, copper, copper-bearing material, manganese, manganese-bearing material, titanium, titanium-bearing material, zirconium, zirconium-bearing material, hafnium, hafnium-bearing material, tungsten, tungsten-bearing material, molybdenum, molybdenum-bearing material, niobium, niobium-bearing material, vanadium, vanadium-bearing material, tantalum, tantalum-bearing material, yttrium, and yttrium-bearing material.
5. The method of claim 1, wherein the solid product material is one or more than one of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2) , ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
6. (canceled)
7. The method of claim 2, wherein the molten salt or molten salt solution is one of a molten NaCl-bearing solution, a molten KCl-bearing solution, and a molten CaCl.sub.2-bearing solution.
8. (canceled)
9. The method of claim 1, wherein the solid material is non-metallic.
10. The method of claim 9, wherein the solid product material is an oxide of the non-metallic solid material or an oxide of a constituent of the non-metallic solid material.
11. The method of claim 9, wherein the non-metallic material is one or more than one of a boride, a boride-bearing material, a carbide, a carbide-bearing material, a nitride, a nitride-bearing material, a sulfide, a sulfide-bearing material, an oxide, and an oxide-bearing material.
12. (canceled)
13. (canceled)
14. The method of claim 10, wherein the oxide is one or more of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
15. The method of claim 9, wherein the molten salt solution is one of a molten NaCl-bearing solution, a molten KCl-bearing solution, and a molten CaCl.sub.2-bearing solution.
16. A materials system comprising: a solid material capable of forming a solid product layer when exposed to an oxygen-bearing gas or a liquid environment containing dissolved oxygen at levels sufficient for oxidation of at least one constituent of the solid material, wherein the solid product layer is in contact with a liquid containing an elevated or saturated concentration of the dissolved solid product layer.
17. The materials system of claim 16, wherein the liquid is a molten salt or a molten salt solution is one of a molten NaCl-bearing solution, a molten KCl-bearing solution, and a molten CaCl.sub.2-bearing solution.
18. The materials system of 16, wherein the solid material is a metallic material.
19. The materials system of claim 18, wherein the metallic material is one or more than one of chromium, chromium-bearing material, aluminum, aluminum-bearing material, silicon, silicon-bearing material, beryllium, beryllium-bearing material, nickel, nickel-bearing material, iron, iron-bearing material, cobalt, cobalt-bearing material, copper, copper-bearing material, manganese, manganese-bearing material, titanium, titanium-bearing material, zirconium, zirconium-bearing material, hafnium, hafnium-bearing material, tungsten, tungsten-bearing material, molybdenum, molybdenum-bearing material, niobium, niobium-bearing material, vanadium, vanadium-bearing material, tantalum, tantalum-bearing material, yttrium, and yttrium-bearing material.
20. The materials system of claim 16, wherein the solid product material is one or more than one of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
21. (canceled)
22. (canceled)
23. (canceled)
24. The materials system of claim 16, wherein the solid material is non-metallic.
25. The materials system of claim method of claim 24, wherein the solid product material is an oxide of the non-metallic solid material or an oxide of a constituent of the non-metallic solid material is one or more than one of a boride, a boride-bearing material, a carbide, a carbide-bearing material, a nitride, a nitride-bearing material, a sulfide, a sulfide-bearing material, an oxide, and an oxide-bearing material.
26. (canceled)
27. (canceled)
28. (Canceled)
29. The materials system of claim 25, wherein the oxide is one or more of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
30. (canceled)
31. A corrosion-resistant device comprising: a solid material comprising a solid-product layer exposed to a molten salt solution, wherein the concentration of the solid-product dissolved in the molten salt solution is at saturation or at an elevated level.
32. The corrosion resistant device of claim 31, wherein the device is in contact with the molten salt and the device is a container, a pipe, a valve, a pump, or a heat-transfer device.
33. The corrosion-resistant device of claim 31, wherein the solid product material is an oxide.
34. The corrosion-resistant material of claim 33, wherein the oxide is one or more than one of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
Description
BRIEF DESCRIPTION OF DRAWINGS
[0015] Some of the figures shown herein may include dimensions. Further, some of the figures shown herein may have been created from scaled drawings or from photographs that are scalable. It is understood that such dimensions or the relative scaling within a figure are by way of example, and not to be construed as limiting. Further, in this disclosure, the figures shown for illustrative purposes are not to scale and those skilled in the art can readily recognize the relative dimensions of the different segments of the drawings depending on how the principles of the disclosure are used in practical applications.
[0016]
[0017]
[0018]
[0019]
[0020]
[0021]
[0022]
[0023]
[0024]
[0025]
[0026]
[0027]
[0028]
[0029]
[0030]
[0031]
DETAILED DESCRIPTION
[0032] For the purposes of promoting an understanding of the principles of the disclosure, reference will now be made to the embodiments illustrated in the drawings and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the disclosure is thereby intended, such alterations and further modifications in the illustrated device, and such further applications of the principles of the disclosure as illustrated therein being contemplated as would normally occur to one skilled in the art to which the disclosure relates.
[0033] The present disclosure relates to methods for achieving corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure also relates to methods for achieving the corrosion resistance of mechanically-robust metals such as but not limited to metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure also relates to methods for achieving the corrosion resistance of thermally-conductive metals such as but not limited to metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure particularly relates to methods for achieving the corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environment. It should be noted that the corrosive liquid environment can include a molten salt, where the molten salt includes, but is not limited to any one of the following materials or any combinations of the following materials: a chloride-bearing liquid, a fluoride-bearing liquid, a nitrate-bearing liquid, a sulfate-bearing liquid, a carbonate-bearing liquid, and a hydroxide-bearing liquid,
[0034] The present disclosure also relates to solid materials and liquid materials used to achieve corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure particularly relates to mechanically robust solid materials and liquid materials used to achieve the corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure particularly relates to thermally conductive solid materials and liquid materials used to achieve the corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. The present disclosure also relates to a system of solid materials and liquid materials used to achieve the corrosion resistance of metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments. It should be noted that the corrosive liquid environment can include a molten salt, where the molten salt includes, but is not limited to any one of the following materials or any combinations of the following materials: a chloride-bearing liquid, a fluoride-bearing liquid, a nitrate-bearing liquid, a sulfate-bearing liquid, and a hydroxide-bearing liquid.
[0035] The present disclosure also provides methods for achieving the corrosion resistance of solid metals, metallic alloys, metal-bearing composites, ceramics, and ceramic-bearing composites in high-temperature corrosive liquid environments for use in components in high-temperature systems. Examples of such high-temperature systems include, but are not limited to, systems for transportation, energy (e.g., electrical power) production, energy storage, waste heat recovery, propulsion, national defense, chemical processing, and chemical and waste storage. Examples of transportation systems in the context of this disclosure include, but are not limited to, systems for automobiles, trucks, trains, aircraft, spacecraft, ships, and submarines. Examples of electrical power production systems in the context of this disclosure include, but are not limited to, systems for fossil fuel-derived power, solar energy-derived power, nuclear energy-derived power, and thermionics. Solar energy-derived power production systems in the context of this disclosure include but not limited to concentrating solar power production systems. Energy storage systems in the context of this disclosure include, but are not limited to, systems for the storage of solids, liquids, gases, or plasmas. Examples of propulsion systems in the context of this disclosure include, but are not limited to, systems for chemical fuel-based propulsion, nuclear fuel-based propulsion, and ion propulsion. Examples of national defense systems in the context of this disclosure include, but are not limited to, systems for hypersonic aircraft and hypersonic missiles. Components in the context of this disclosure suitable for use in such high temperature systems include, but are not limited to, heat exchangers, piping, valves, storage containers for high-temperature solids and liquids, pumps, bearings, heat sinks, liquid metal handling equipment, engine components (such as turbine blades, pistons, compressors, combustion chambers), leading edges of hypersonic aircraft and missiles, and energy conversion devices. Examples of high-temperature corrosive liquid environments in the context of this disclosure include, but are not limited to, environments comprising a high-temperature molten salt.
[0036] In this disclosure, the term solid material is used to denote the material whose corrosion resistance to a liquid is desired to be enhanced. The term solid product material, in the context of this disclosure denotes the corrosion product formed due to the interaction of the solid material with an atmosphere and/or with the liquid. It should be noted that in certain situations, the solid material in contact with a liquid may itself be a solid product material formed previously and corrosion resistance in such a case implies eliminating or diminishing further dissolution of the solid product material into the liquid or an undesirable chemical reaction with the liquid. The rate of corrosion of a solid material in contact with a corrosive liquid may be significantly reduced by introducing into such a corrosive liquid one or more products of one or more corrosion reactions between the liquid and the solid.
[0037] The following description provides specific examples of the above general concepts of this disclosure with reference to several solid materials, alloys, solid products and liquids. These are merely exemplary embodiments and are not intended to limit the scope of this disclosure. In this disclosure the term metal is intended to include an alloy of the metal. For example the term Ni includes metallic nickel as well as nickel-bearing alloys.
[0038] The rate of corrosion of a solid material in contact with a corrosive liquid in a given gaseous environment may be significantly reduced by introducing into such a corrosive liquid one or more products of one or more corrosion reactions between the liquid and the solid or between the solid and a suitable gaseous atmosphere. Thus an aspect of the disclosure is a materials system which comprises a combination of a solid material capable of forming a solid product layer (via exposure to an oxygen-containing and/or water containing environment, such as air or a molten salt with a sufficient amount of dissolved oxygen and/or water) in contact with a molten salt containing an elevated or saturated concentration of the dissolved solid product layer.
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049] It should be recognized that the principles of this disclosure apply to solid materials that are not metallic. For example, the non-metallic solid material whose corrosion resistance, when exposed to molten salts needs enhancement, include but not limited to be non-metallic oxides, non-metallic compounds, non-metallic solid-solutions or a non-metallic composites and ceramic composite materials. In several of these cases, the corrosion product is the solid-material itself or one or more a constituents of the solid material. In these cases, if the corrosion product is the solid-material itself, there is no need to prepare a scale prior to exposing the material to the molten-salt environment. Several examples of utilizing the principles of this disclosure to enhance the hose corrosion resistance of non-metallic materials to molten salts are described below.
[0050] In one embodiment, of the disclosure, zirconia (ZrO.sub.2) or a ZrO.sub.2-bearing compound or a ZrO.sub.2-bearing solid solution or a ZrO.sub.2-bearing composite can be considered to be the solid material. Consider further that this ZrO.sub.2 or ZrO.sub.2-bearing compound or ZrO.sub.2-bearing solid solution or ZrO.sub.2-bearing composite is exposed to a molten salt, containing a mixture of NaCl and KCl (such as an equimolar mixture of NaCl and KCl), at 727 C. in air. The ZrO.sub.2 or ZrO.sub.2 in the ZrO.sub.2-bearing compound or ZrO.sub.2 in the ZrO.sub.2-bearing solid solution or ZrO.sub.2 in the ZrO.sub.2-bearing composite will dissolve into the NaCl-KCl molten salt at 727 C. if the NaCl-KCl salt is not saturated with ZrO.sub.2. Such dissolution of ZrO.sub.2 or ZrO.sub.2 in the ZrO.sub.2-bearing compound or ZrO.sub.2 in the ZrO.sub.2-bearing solid solution or ZrO.sub.2 in the ZrO.sub.2-bearing composite upon exposure to the NaCl-KCl salt at 727 C. in air can be significantly reduced if the NaCl-KCl salt is doped with ZrO.sub.2 prior to exposure of the ZrO.sub.2 or ZrO.sub.2-bearing compound or ZrO.sub.2-bearing solid solution or ZrO.sub.2-bearing composite to this salt. That is, the corrosion rate of ZrO.sub.2 or ZrO.sub.2-bearing compound or ZrO.sub.2-bearing solid solution or ZrO.sub.2-bearing composite in the molten NaCl-KCl salt at 727 C. in air will be significantly reduced if the NaCl-KCl salt is saturated with ZrO.sub.2. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten NaCl-KCl salt) at high temperatures (such as at 727 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved ZrO.sub.2), so as to dramatically lower the rate of corrosion of an oxide (such as ZrO.sub.2) or an oxide-bearing compound (such as a ZrO.sub.2-bearing compound) or an oxide-bearing solid solution (such as a ZrO.sub.2-bearing solid solution) or an oxide-bearing composite (such as a ZrO.sub.2-bearing composite) exposed to such a molten salt.
[0051] Consider, as yet another embodiment of the disclosure, zirconia (ZrO.sub.2) or a ZrO.sub.2-bearing compound or a ZrO.sub.2-bearing solid solution or a ZrO.sub.2-bearing composite exposed to a molten salt, containing CaCl.sub.2 and NaCl (such as a liquid solution containing 48 mole % CaCl.sub.2 and 52 mole % NaCl), at 750 C. in air. The ZrO.sub.2 or ZrO.sub.2 in the ZrO.sub.2-bearing compound or ZrO.sub.2 in the ZrO.sub.2-bearing solid solution or ZrO.sub.2 in the ZrO.sub.2-bearing composite will dissolve into the CaCl.sub.2-NaCl molten salt at 750 C. if the CaCl.sub.2-NaCl salt is not saturated with ZrO.sub.2. Such dissolution of ZrO.sub.2 or ZrO.sub.2 in the ZrO.sub.2-bearing compound or ZrO.sub.2 in the ZrO.sub.2-bearing solid solution or ZrO.sub.2 in the ZrO.sub.2-bearing composite upon exposure to the CaCl.sub.2-NaCl salt at 750 C. in air can be significantly reduced if the CaCl.sub.2-NaCl salt is doped with ZrO.sub.2 prior to exposure of the ZrO.sub.2 or ZrO.sub.2-bearing compound or ZrO.sub.2-bearing solid solution or ZrO.sub.2-bearing composite to this salt. That is, the corrosion rate of ZrO.sub.2 or ZrO.sub.2-bearing compound or ZrO.sub.2-bearing solid solution or ZrO.sub.2-bearing composite in the molten CaCl.sub.2-NaCl salt at 750 C. in air will be significantly reduced if the CaCl.sub.2-NaCl salt is saturated with ZrO.sub.2. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten CaCl.sub.2-NaCl salt) at high temperatures (such as at 750 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved ZrO.sub.2), so as to dramatically lower the rate of corrosion of an oxide (such as ZrO.sub.2) or an oxide-bearing compound (such as a ZrO.sub.2-bearing compound) or an oxide-bearing solid solution (such as a ZrO.sub.2-bearing solid solution) or an oxide-bearing composite (such as a ZrO.sub.2-bearing composite) exposed to such a molten salt.
[0052] Consider, alumina (Al.sub.2O.sub.3) or an Al.sub.2O.sub.3-bearing compound or an Al.sub.2O.sub.3-bearing solid solution or an Al.sub.2O.sub.3-bearing composite. Consider further that this Al.sub.2O.sub.3 or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite is exposed to a molten salt, containing a mixture of NaCl and KCl (such as an equimolar mixture of NaCl and KCl), at 727 C. in air. The Al.sub.2O.sub.3 or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing composite will dissolve into the NaCl-KCl molten salt at 727 C. if the NaCl-KCl salt is not saturated with Al.sub.2O.sub.3. Such dissolution of Al.sub.2O.sub.3 or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing composite upon exposure to the NaCl-KCl salt at 727 C. in air can be significantly reduced if the NaCl-KCl salt is doped with Al.sub.2O.sub.3 prior to exposure of the Al.sub.2O.sub.3 or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite to this salt. That is, the corrosion rate of Al.sub.2O.sub.3 or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite in the molten NaCl-KCl salt at 727 C. in air will be significantly reduced if the NaCl-KCl salt is saturated with Al.sub.2O.sub.3. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten NaCl-KCl salt) at high temperatures (such as at 727 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved Al.sub.2O.sub.3), so as to dramatically lower the rate of corrosion of an oxide (such as Al.sub.2O.sub.3) or an oxide-bearing compound (such as a Al.sub.2O.sub.3-bearing compound) or an oxide-bearing solid solution (such as a Al.sub.2O.sub.3-bearing solid solution) or an oxide-bearing composite (such as a Al.sub.2O.sub.3-bearing composite) exposed to such a molten salt.
[0053] Consider, alumina (Al.sub.2O.sub.3) or an Al.sub.2O.sub.3-bearing compound or an Al.sub.2O.sub.3-bearing solid solution or an Al.sub.2O.sub.3-bearing composite. Consider further that this Al.sub.2O.sub.3 or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite is exposed to a molten salt, containing CaCl.sub.2 and NaCl (such as a liquid solution containing 48 mole % CaCl.sub.2 and 52 mole % NaCl), at 750 C. in air. The Al.sub.2O.sub.3 or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing composite will dissolve into the CaCl.sub.2-NaCl molten salt at 750 C. if the CaCl.sub.2-NaCl salt is not saturated with Al.sub.2O.sub.3. Such dissolution of Al.sub.2O.sub.3or Al.sub.2O.sub.3 in the Al.sub.2O.sub.3-bearing composite upon exposure to the CaCl.sub.2-NaCl salt at 750 C. in air can be significantly reduced if the CaCl.sub.2-NaCl salt is doped with Al.sub.2O.sub.3 prior to exposure of the Al.sub.2O.sub.3or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite to this salt. That is, the corrosion rate of Al.sub.2O.sub.3 or Al.sub.2O.sub.3-bearing compound or Al.sub.2O.sub.3-bearing solid solution or Al.sub.2O.sub.3-bearing composite in the molten CaCl.sub.2-NaCl salt at 750 C. in air will be significantly reduced if the CaCl.sub.2-NaCl salt is saturated with Al.sub.2O.sub.3. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten CaCl.sub.2-NaCl salt) at high temperatures (such as at 750 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved Al.sub.2O.sub.3), so as to dramatically lower the rate of corrosion of an oxide (such as Al.sub.2O.sub.3) or an oxide-bearing compound (such as a Al.sub.2O.sub.3-bearing compound) or an oxide-bearing solid solution (such as a Al.sub.2O.sub.3-bearing solid solution) or an oxide-bearing composite (such as a Al.sub.2O.sub.3-bearing composite) exposed to such a molten salt.
[0054] Consider silica (SiO.sub.2) or a SiO.sub.2-bearing compound or a SiO.sub.2-bearing solid solution or a SiO.sub.2-bearing composite. Consider further that this SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite is exposed to a molten salt, containing a mixture of NaCl and KCl (such as an equimolar mixture of NaCl and KCl), at 727 C. in air. The SiO.sub.2 or SiO.sub.2 in the SiO.sub.2-bearing compound or SiO.sub.2 in the SiO.sub.2-bearing solid solution or SiO.sub.2 in the SiO.sub.2-bearing composite will dissolve into the NaCl-KCl molten salt at 727 C. if the NaCl-KCl salt is not saturated with SiO.sub.2. Such dissolution of SiO.sub.2 or SiO.sub.2 in the SiO.sub.2-bearing compound or SiO.sub.2 in the SiO.sub.2-bearing solid solution or SiO.sub.2 in the SiO.sub.2-bearing composite upon exposure to the NaCl-KCl salt at 727 C. in air can be significantly reduced if the NaCl-KCl salt is doped with SiO.sub.2 prior to exposure of the SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite to this salt. That is, the corrosion rate of SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite in the molten NaCl-KCl salt at 727 C. in air will be significantly reduced if the NaCl-KCl salt is saturated with SiO.sub.2. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten NaCl-KCl salt) at high temperatures (such as at 727 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved SiO.sub.2), so as to dramatically lower the rate of corrosion of an oxide (such as SiO.sub.2) or an oxide-bearing compound (such as a SiO.sub.2-bearing compound) or an oxide-bearing solid solution (such as a SiO.sub.2-bearing solid solution) or an oxide-bearing composite (such as a SiO.sub.2-bearing composite) exposed to such a molten salt.
[0055] Consider silica (SiO.sub.2) or a SiO.sub.2-bearing compound or a SiO.sub.2-bearing solid solution or a SiO.sub.2-bearing composite. Consider further that this SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite is exposed to a molten salt, containing CaCl.sub.2 and NaCl_(such as a liquid solution containing 48 mole % CaCl.sub.2 and 52 mole % NaCl), at 750 C. in air. The SiO.sub.2 or SiO.sub.2 in the SiO.sub.2-bearing compound or SiO.sub.2 in the SiO.sub.2-bearing solid solution or SiO.sub.2 in the SiO.sub.2-bearing composite will dissolve into the CaCl.sub.2-NaCl molten salt at 750 C. if the CaCl.sub.2-NaCl salt is not saturated with SiO.sub.2. Such dissolution of SiO.sub.2 or SiO.sub.2 in the SiO.sub.2-bearing compound or SiO.sub.2 in the SiO.sub.2-bearing solid solution or SiO.sub.2 in the SiO.sub.2-bearing composite upon exposure to the CaCl.sub.2-NaCl salt at 750 C. in air can be significantly reduced if the CaCl.sub.2-NaCl salt is doped with SiO.sub.2 prior to exposure of the SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite to this salt. That is, the corrosion rate of SiO.sub.2 or SiO.sub.2-bearing compound or SiO.sub.2-bearing solid solution or SiO.sub.2-bearing composite in the molten CaCl.sub.2-NaCl salt at 750 C. in air will be significantly reduced if the CaCl.sub.2-NaCl salt is saturated with SiO.sub.2. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten CaCl.sub.2-NaCl salt) at high temperatures (such as at 750 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved SiO.sub.2), so as to dramatically lower the rate of corrosion of an oxide (such as SiO.sub.2) or an oxide-bearing compound (such as a SiO.sub.2-bearing compound) or an oxide-bearing solid solution (such as a SiO.sub.2-bearing solid solution) or an oxide-bearing composite (such as a SiO.sub.2-bearing composite) exposed to such a molten salt.
[0056] Consider chromia (Cr.sub.2O.sub.3) or a Cr.sub.2O.sub.3-bearing compound or a Cr.sub.2O.sub.3-bearing solid solution or a Cr.sub.2O.sub.3-bearing composite. Consider further that this Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite is exposed to a molten salt, containing a mixture of NaCl and KCl (such as an equimolar mixture of NaCl and KCl), at 727 C. in air. The Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing composite will dissolve into the NaCl-KCl molten salt at 727 C. if the NaCl-KCl salt is not saturated with Cr.sub.2O.sub.3. Such dissolution of Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing composite upon exposure to the NaCl-KCl salt at 727 C. in air can be significantly reduced if the NaCl-KCl salt is doped with Cr.sub.2O.sub.3 prior to exposure of the Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite to this salt. That is, the corrosion rate of Cr.sub.2O.sub.3or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite in the molten NaCl-KCl salt at 727 C. in air will be significantly reduced if the NaCl-KCl salt is saturated with Cr.sub.2O.sub.3. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten NaCl-KCl salt) at high temperatures (such as at 727 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved Cr.sub.2O.sub.3), so as to dramatically lower the rate of corrosion of an oxide (such as Cr.sub.2O.sub.3) or an oxide-bearing compound (such as a Cr.sub.2O.sub.3-bearing compound) or an oxide-bearing solid solution (such as a Cr.sub.2O.sub.3-bearing solid solution) or an oxide-bearing composite (such as a Cr.sub.2O.sub.3-bearing composite) exposed to such a molten salt.
[0057] Consider chromia (Cr.sub.2O.sub.3) or a Cr.sub.2O.sub.3-bearing compound or a Cr.sub.2O.sub.3-bearing solid solution or a Cr.sub.2O.sub.3-bearing composite. Consider further that this Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite is exposed to a molten salt, containing CaCl.sub.2 and NaCl (such as a liquid solution containing 48 mole % CaCl.sub.2 and 52 mole % NaCl), at 750 C. in air. The Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing composite will dissolve into the CaCl.sub.2-NaCl molten salt at 750 C. if the CaCl.sub.2-NaCl salt is not saturated with Cr.sub.2O.sub.3. Such dissolution of Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3in the Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3 in the Cr.sub.2O.sub.3-bearing composite upon exposure to the CaCl.sub.2-NaCl salt at 750 C. in air can be significantly reduced if the CaCl.sub.2-NaCl salt is doped with Cr.sub.2O.sub.3 prior to exposure of the Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite to this salt. That is, the corrosion rate of Cr.sub.2O.sub.3 or Cr.sub.2O.sub.3-bearing compound or Cr.sub.2O.sub.3-bearing solid solution or Cr.sub.2O.sub.3-bearing composite in the molten CaCl.sub.2-NaCl salt at 750 C. in air will be significantly reduced if the CaCl.sub.2-NaCl salt is saturated with Cr.sub.2O.sub.3. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten CaCl.sub.2-NaCl salt) at high temperatures (such as at 750 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved Cr.sub.2O.sub.3), so as to dramatically lower the rate of corrosion of an oxide (such as Cr.sub.2O.sub.3) or an oxide-bearing compound (such as a Cr.sub.2O.sub.3-bearing compound) or an oxide-bearing solid solution (such as a Cr.sub.2O.sub.3-bearing solid solution) or an oxide-bearing composite (such as a Cr.sub.2O.sub.3-bearing composite) exposed to such a molten salt.
[0058] The general method described above (i.e., the doping, at or below the saturation limit, of a molten salt with an oxide, or other corrosion product, so as to reduce or avoid the dissolution of the solid oxide, or other solid corrosion product, present on the surface of a solid material in contact with the molten salt) may also be conducted with molten salts and solid materials placed in contact with each other at temperatures other than 727 C. or 750 C. and in gaseous atmospheres other than air. This method may be applied to molten salts and solid materials placed in contact with each other at temperatures above the melting point of the molten salt and below the decomposition temperature or boiling point of the molten salt. This method may be applied to molten salts and solid materials placed in contact with each other in gaseous atmospheres with lower oxygen contents than is present in air (i.e., at oxygen partial pressures below 0.21 atmospheres) or in gaseous atmospheres with higher oxygen contents than is present in air (i.e., at oxygen partial pressures above 0.21 atmospheres). Some non-limiting examples of the use of this method at temperatures other than 727 C. or 750 C. and in gaseous atmospheres other than air are provided below.
[0059]
[0060]
[0061] Consider, as another non-limiting example, zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite capable of forming an external ZrO.sub.2-bearing scale upon exposure to an oxygen-bearing gaseous atmosphere at 800 C. Consider that this oxygen-bearing gaseous atmosphere includes, but, is not limited to, an inert gas (including, but not limited to, argon or helium) containing a small amount of oxygen (well below the oxygen content of air including, but not limited to, less than 10 parts per million of oxygen or less than 1 part per million of oxygen) or a reducing gas (including, but not limited to, a hydrogen-argon gas mixture or a hydrogen-water vapor gas mixture or a carbon monoxide-argon gas mixture or a carbon monoxide-carbon dioxide gas mixture) containing a small amount of oxygen (well below the oxygen content of air including, but not limited to, less than 10 parts per million of oxygen or less than 1 part per million of oxygen or less than 10.sup.10 atmospheres of oxygen or less than 10.sup.15 atmospheres of oxygen or less than 10.sup.20 atmospheres of oxygen). Consider further that this zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite is exposed to a molten salt, containing CaCl.sub.2 and NaCl (such as a liquid solution containing 48 mole % CaCl.sub.2 and 52 mole % NaCl), at 800 C. in an oxygen-bearing atmosphere containing a small amount of oxygen. If the zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite is pre-oxidized so as to form an external ZrO.sub.2-bearing scale, or if the zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite initially forms an external ZrO.sub.2-bearing scale upon exposure to the CaCl.sub.2-NaCl molten salt at 800 C. in the oxygen-bearing gaseous environment, then the ZrO.sub.2-bearing scale present on the zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite will also dissolve into the CaCl.sub.2-NaCl molten salt at 800 C. if the CaCl.sub.2-NaCl salt is not saturated with ZrO.sub.2. Such dissolution of ZrO.sub.2 in the molten salt will result in a thinning of the ZrO.sub.2-bearing scale present on the zirconium carbide surface or a zirconium carbide-bearing compound surface or a zirconium carbide-bearing solid solution surface or a zirconium carbide-bearing composite surface which, in turn, will require an enhanced rate of oxidation of the zirconium carbide or zirconium carbide in the zirconium carbide-bearing compound or zirconium carbide in the zirconium carbide-bearing solid solution or zirconium carbide in the zirconium carbide-bearing composite (relative to rate of oxidation of zirconium carbide or zirconium carbide-bearing compound or zirconium carbide-bearing solid solution or zirconium carbide-bearing composite in the low oxygen gaseous environment in the absence of the salt) in order to maintain a continuous ZrO.sub.2-bearing scale of the same thickness on the zirconium carbide surface or a zirconium carbide-bearing compound surface or a zirconium carbide-bearing solid solution surface or a zirconium carbide-bearing composite surface. Such an enhanced rate of oxidation of zirconium carbide will enhance the rate of consumption of zirconium carbide or zirconium carbide in the zirconium carbide-bearing compound or zirconium carbide in the zirconium carbide-bearing solid solution or zirconium carbide in the zirconium carbide-bearing composite and result in an undesired increase in the rate of corrosion of the zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite. Such enhanced oxidation of zirconium carbide or zirconium carbide in the zirconium carbide-bearing compound or zirconium carbide in the zirconium carbide-bearing solid solution or zirconium carbide in the zirconium carbide-bearing composite upon exposure to the molten CaCl.sub.2-NaCl salt at 800 C. in the low oxygen gaseous environment can be significantly reduced if the molten CaCl.sub.2-NaCl salt is doped with ZrO.sub.2 prior to exposure of the zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite to this salt. Hence, exposure of zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite in the low oxygen gaseous environment to a molten CaCl.sub.2-NaCl salt that has been saturated with ZrO.sub.2 at 800 C. will allow for the formation of a ZrO.sub.2-bearing scale on zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite without the subsequent dissolution of this ZrO.sub.2-bearing scale in the ZrO.sub.2-saturated CaCl.sub.2-NaCl salt. That is, the corrosion rate of zirconium carbide or a zirconium carbide-bearing compound or a zirconium carbide-bearing solid solution or a zirconium carbide-bearing composite (coated with a ZrO.sub.2-bearing scale) in the molten CaCl.sub.2-NaCl salt at 800 C. in a low oxygen gaseous environment will be significantly reduced if the molten CaCl.sub.2-NaCl salt is saturated with a modest ZrO.sub.2 addition. Such a low ZrO.sub.2 addition to the molten CaCl.sub.2-NaCl salt is also not expected to result in a significant change in the desired thermal properties (e.g., heat capacity, density, viscosity, thermal stability) of the salt for use as a heat transfer fluid or as a thermal storage fluid. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten CaCl.sub.2-NaCl salt) at high temperatures (such as at 800 C.) and low oxygen partial pressures (such as provided by an inert gas with a small amount of oxygen or a reducing gas with a small amount of oxygen), with the molten salt possessing a dissolved concentration (up to the saturation concentration) of a corrosion product (such as dissolved ZrO.sub.2), so as to dramatically lower the rate of corrosion of a ceramic (such as zirconium carbide) or a ceramic solid solution (such as a zirconium carbide-bearing solid solution that is capable of forming an external ZrO.sub.2-bearing scale) or a zirconium-bearing compound (such as a zirconium carbide-bearing compound that is capable of forming an external ZrO.sub.2-bearing scale) or a zirconium-bearing composite (such as a zirconium carbide-bearing composite that is capable of forming an external ZrO.sub.2-bearing scale) exposed to such a molten salt.
[0062] It should be noted that oxide-bearing molten salts, that are not saturated with the desired oxide corrosion product, may also be used to reduce the thermodynamic driving force for dissolution of the solid oxide so as to thereby significantly slow the rate of dissolution of the solid oxide into the molten salt. This concept is another feature of this disclosure. For example, chromium or a chromium-bearing metallic alloy (such as a nickel-based chromium-bearing alloy including, but not limited to, Haynes 230 or Hastelloy C276 or Hastelloy C22 or Inconel 740H; or an iron-based chromium-bearing alloy including, but not limited to, a stainless steel alloy such as 304 stainless steel or 316 stainless steel; or a cobalt-based chromium-bearing alloy) or a chromium-bearing composite capable of forming an external Cr.sub.2O.sub.3 scale upon exposure to air at 727 C., with this Cr.sub.2O.sub.3 scale exhibiting a thickening rate that decreases with increasing time of exposure to air at 727 C. Consider further that this chromium or chromium-bearing metallic alloy or chromium-bearing composite is exposed to a molten salt, containing a mixture of NaCl and KCl (such as an equimolar mixture of NaCl and KCl), at 727 C. in air. If the chromium or chromium-bearing metallic alloy or chromium-bearing composite is pre-oxidized in air at 727 C. to form an external Cr.sub.2O.sub.3 scale, or if the chromium or chromium-bearing metallic alloy or chromium-bearing composite initially forms an external Cr.sub.2O.sub.3 scale upon exposure to the NaCl-KCl molten salt at 727 C. in an air environment, then the Cr.sub.2O.sub.3 scale present on the chromium or chromium-bearing alloy or chromium-bearing composite will also dissolve into the NaCl-KCl molten salt at 727 C. if the NaCl-KCl salt is not saturated with Cr.sub.2O.sub.3. It has been reported in literature that the solubility of Cr.sub.2O.sub.3 in a molten NaCl-KCl salt at 727 C. is less than 1 wt %. Hence, exposure of chromium or chromium-bearing metal alloy or a chromium-bearing composite in air to a molten NaCl-KCl salt that has been doped, but not saturated, with Cr.sub.2O.sub.3 (at a Cr.sub.2O.sub.3 concentration below 1 wt %) at 727 C. will allow for the formation of a Cr.sub.2O.sub.3 scale on chromium or on the chromium-bearing metallic alloy or on the chromium-bearing composite with a reduced rate of dissolution of this Cr.sub.2O.sub.3 scale in the Cr.sub.2O.sub.3-saturated NaCl-KCl salt. That is, the corrosion rate of chromium or a chromium-bearing metallic alloy or a chromium-bearing composite (coated with a Cr.sub.2O.sub.3 scale) in the molten NaCl-KCl salt at 727 C. in air will be significantly reduced if the molten NaCl-KCl salt is doped with a modest Cr.sub.2O.sub.3 addition below the saturation limit. Such a low Cr.sub.2O.sub.3 addition to the molten NaCl-KCl salt is also not expected to result in a significant change in the desired thermal properties (e.g., heat capacity, density, viscosity, thermal stability) of the salt for use as a heat transfer fluid or as a thermal storage fluid. Hence, a key aspect of the present disclosure is to provide a molten salt (such as a molten NaCl-KCl salt) at high temperatures (such as at 727 C.) and high oxygen partial pressures (such as air), with the molten salt possessing a dissolved concentration (below the saturation concentration) of a corrosion product (such as dissolved Cr.sub.2O.sub.3), so as to significantly lower the rate of corrosion of a metal (such as chromium) or a metallic alloy (such as a chromium-bearing alloy that is capable of forming an external Cr.sub.2O.sub.3 scale) or a metal-bearing composite (such as a chromium-bearing composite that is capable of forming an external Cr.sub.2O.sub.3 scale) exposed to such a molten salt.
[0063] The general method described above (i.e., the doping, at or below the saturation limit, of a molten salt with an oxide, or other corrosion product, so as to reduce or avoid the dissolution of the solid oxide, or other solid corrosion product, present on the surface of a solid material in contact with the molten salt) may also be conducted with molten salts containing other additives (including, but not limited to, other oxides) that act to reduce the solubility of the oxide corrosion product in the molten salt. For example, one or more oxides other than chromium oxide (Cr.sub.2O.sub.3), including, but not limited to, other acidic oxides than chromium oxide, may be added to a molten salt so as to reduce the solubility of chromium oxide (Cr.sub.2O.sub.3) in the molten salt. With the addition of these one or more oxides other than chromium oxide (Cr.sub.2O.sub.3) to the molten salt, the amount of chromium oxide (Cr.sub.2O.sub.3) in the molten salt required to saturate the molten salt with chromium oxide (so as to reduce or avoid the dissolution of chromium oxide present in chromium oxide or in a chromium oxide solid solution or in a chromium oxide-bearing compound or in a chromium oxide-bearing composite or in a chromium oxide-bearing scale formed on chromium or in a chromium oxide-bearing scale formed on a chromium-bearing metallic alloy or in a chromium oxide-bearing scale formed on a chromium-bearing composite) would be reduced.
[0064] In the examples described above which are illustrative of the principles of this disclosure, two molten salt mixtures have been mentioned. In some examples of the solid material both the NaCl-KCl mixture and CaCl.sub.2-NaCl were included. In some other examples of the solid material, only one of these salt mixtures is included, however, it should be recognized that for all the solid materials mentioned in the examples, either of these two molten salt mixtures can be included.
[0065] Preferred molten salt composition for this method of enhancing the corrosion resistance of solid materials in molten salts are CaCl.sub.2-NaCl-based compositions. This salt composition is inexpensive, plentifully available (CaCl.sub.2 and NaCl are readily obtained from sea water), and much more resistant to oxidation than MgCl.sub.2-bearing chloride melts. Consider the oxidation reactions for chloride species in MgCl.sub.2-KCl and CaCl.sub.2-NaCl liquids:
{MgCl.sub.2}+O.sub.2(g)=MgO(s)+2{Cl}[1]
2{KCl}+O.sub.2(g)=K.sub.2O(s)+2{Cl}[2]
{CaCl.sub.2}+O.sub.2(g)=CaO(s)+2{Cl}[3]
2{NaCl}+O.sub.2(g)=Na.sub.2O(s)+2{Cl}[4]
where { } refers to species dissolved in the MgCl.sub.2-KCl or CaCl.sub.2-NaCl liquids. The standard Gibbs free energy changes (G values) for reactions [1], [2], [3], and [4] at 750 C. are 44.3 kJ/mol, +457.3 kJ/mol, +143.5 kJ/mol, and +356.2 kJ/mol, respectively; that is, MgCl.sub.2 oxidation is much more strongly favored than the oxidation of KCl, CaCl.sub.2, or NaCl. Indeed, recent experiments conducted as part of the experiments leading to this disclosure have shown that exposure of a 32 mol % MgCl.sub.2/68 mol % KCl molten salt (T.sub.eut=427 C.) to ambient air at 750 C. for 50 h resulted in the conversion of MgCl.sub.2 to MgO (as confirmed by X-ray diffraction analysis.
NiO(s)+2{Cl}={NiCl.sub.2}+O.sub.2(g) [5]
where { } refers to species dissolved in the CaCl.sub.2-NaCl liquid. The G value for reaction [5] at 750 C. is 5.74 kJ/mol..sup.1 Equilibration of reaction [5] with the (a[Cl]).sup.2/(p[O.sub.2]).sup.1/2 ratio of 2.310.sup.8 set by reaction [3] for the 53 mol % CaCl.sub.2/47 mol % NaCl molten salt at 750 C. yields an activity for {NiCl.sub.2} dissolved in the salt of only 4.410.sup.8 (44 ppb). Hence, after extremely small amounts of reaction, NiO, should be thermodynamically stable with the eutectic CaCl.sub.2-NaCl melt at 750 C. in air (or any O.sub.2-bearing atmosphere).
[0066]
[0067] This high-oxygen strategy, involving the exposure of an oxidizable material (such as Ni) to an oxygen-compatible chloride melt (such as a CaCl.sub.2-NaCl melt) that is saturated with an oxide of the oxidizable material (such as NiO) may be applied to a variety of oxidizable materials (ceramics, metals, alloys of metals and/or ceramics). The basic concept is to shift from relatively fast corrosion that is rate-limited by dissolution in the molten chloride to a slower rate of corrosion that is rate-limited by the thickening of the oxide scale. This method may utilize oxidizable materials that form relatively slow-growing scales (e.g., oxidizable materials that form aluminum oxide, chromium oxide, silicon oxide, beryllium oxide, and/or nickel oxide scales) and utilizes molten salts that are saturated with respect to the slow-growing scale material.
[0068] This high-oxygen strategy is highly attractive for applications using molten chlorides for heat transfer and storage, because this corrosion mitigation method (for metal alloy piping, storage tanks, HEXs, etc.) is compatible with air at 750 C.; that is, leaks in pipes, storage tanks, and HEXs can be readily tolerated with this strategy.
[0069] From the above description, it is clear that this disclosure details a strategy for effectively eliminating or limiting the corrosion of an oxidizable material (a metal, a metallic alloy, a ceramic, a ceramic alloy, or combinations thereof) in contact with a high-temperature molten salt. For the case where the oxidizable material is a metal or metallic material, an oxide of the metal or metallic material is formed either prior to exposing the metal or metallic material to the corrosive molten salt or even during the exposure by maintaining adequate partial pressure of oxygen to form an oxide of the metal. The oxide of this metal then acts as barrier that slows the diffusion of oxygen anions or metal cations through the oxide layer. It should be recognized that the thickness of the oxide layer will directly correlate with the corrosion prevention due to the fact that the oxygen anions or metal cations must diffuse through the oxide layer to allow for further oxide formation. People skilled in the art will recognize that such diffusion through the dense, planar, adherent solid oxide layer follows a parabolic law and has a square root dependence on time. Thus the desired corrosion protection can be obtained through calculations or experiments and achieve a desired thickness for the oxide layer. As a non-limiting example, approaches and information relevant to the Ni-NiO oxide system can be found in the reference: S. Mrowec, Z. Grzesik, Oxidation of Nickel and Transport Properties of Nickel Oxide, J. Phys. Chem. Solids, 65, 1651-1657 (2004). One of skill in the art can establish a correlation between the prevailing nickel-oxide (NiO) thickness and the corrosion protection provided which can be measured in terms of the metal consumption and/or the time required to replace a container made of the metal to hold a molten salt mixture due to corrosion. Those of skill in the art can utilize the oxide formation kinetics to obtain the desired thickness of the metal oxide.
[0070] While the detailed description above mainly described enhancement of corrosion resistance in molten salt mixtures, the general principles of the disclosure are applicable to any liquid that is likely to cause corrosion of the solid material and/or dissolution of the solid-product material.
[0071] Based on the foregoing description, it is an objective of this disclosure to describe a method for enhancing corrosion resistance of a solid material exposed to a liquid. The method includes providing a solid material whose corrosion resistance to a liquid is desired to be enhanced and which is capable of forming a solid product layer when exposed to the liquid containing chemical elements needed to react with the solid material to form the solid product layer; and maintaining the concentration of the solid product material in the liquid either at saturation level or at an elevated level. In some embodiments of the method, the liquid is a molten salt. The solid materials in the method can be metallic or non-metallic (such as, but not limited to, solid solutions of non-metallic elements or compounds or ceramic materials or ceramic composite materials). Examples of solid materials for the method include, but are not limited to, chromium, chromium-bearing material, aluminum, aluminum-bearing material, silicon, silicon-bearing material, beryllium, beryllium-bearing material, nickel, nickel-bearing material, iron, iron-bearing material, cobalt, cobalt-bearing material, copper, copper-bearing material, manganese, manganese-bearing material, titanium, titanium-bearing material, zirconium, zirconium-bearing material, hafnium, hafnium-bearing material, tungsten, tungsten-bearing material, molybdenum, molybdenum-bearing material, niobium, niobium-bearing material, vanadium, vanadium-bearing material, tantalum, tantalum-bearing material, yttrium, and yttrium-bearing material. In the method described above, the solid product material can be one or more materials taken from the group consisting of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5). In some embodiments of the method, the molten salt is a molten salt solution. A molten salt solution refers herein to a single liquid salt phase that contains more than one molten salt species (e.g., a homogeneous liquid solution of NaCl and KCl). Examples of such molten salt solutions include but are not limited in the molten NaCl-KCl solution and molten CaCl.sub.2-NaCl solution. In some embodiments of the method, the solid product can be non-metallic. In some embodiments, the solid product material is the non-metallic solid material itself or a constituent of the non-metallic solid material. In some embodiments of the method, the solid material can be non-metallic. Examples of solid materials of the methods of this disclosure that are non-metallic include but are not limited an oxide, an oxide bearing solid solution, or an oxide-bearing composite material. Examples of oxide materials that can comprise a solid material of this method can be, but not limited to, one or more of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
[0072] It is another objective of this disclosure to describe a materials system for enhancing corrosion resistance of a solid material exposed to a liquid. The materials system includes a solid material capable of forming a solid product layer when exposed to air or a liquid environment containing dissolved oxygen and/or water at levels sufficient for oxidation of at least one constituent of the solid material, wherein the solid product layer is in contact with a liquid containing an elevated or saturated concentration of the dissolved solid product layer. A sufficient level of dissolved oxygen and/or water in the liquid environment refers to a concentration of oxygen and/or water dissolved in the liquid that is sufficient as to allow for the reaction of the solid material with the liquid at the temperature of interest so as to form the solid product layer on the solid material. In some embodiments of the materials system, the liquid is a molten salt. The solid materials in the materials system can be metallic or non-metallic (such as, but not limited to, solid solutions of non-metallic elements or compounds or ceramic materials or ceramic composite materials). Examples of solid materials for the materials system include, but are not limited to, chromium, chromium-bearing material, aluminum, aluminum-bearing material, silicon, silicon-bearing material, beryllium, beryllium-bearing material, nickel, nickel-bearing material, iron, iron-bearing material, cobalt, cobalt-bearing material, copper, copper-bearing material, manganese, manganese-bearing material, titanium, titanium-bearing material, zirconium, zirconium-bearing material, hafnium, hafnium-bearing material, tungsten, tungsten-bearing material, molybdenum, molybdenum-bearing material, niobium, niobium-bearing material, vanadium, vanadium-bearing material, tantalum, tantalum-bearing material, yttrium, and yttrium-bearing material. In the materials system described above, solid product material can be one or more materials taken from the group consisting of than one of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5). In some embodiments of the materials system, the molten salt is a molten salt solution. A molten salt solution refers herein to a single liquid salt phase that contains more than one molten salt species (e.g., a homogeneous liquid solution of NaCl and KCl). Examples of such molten salt solutions include but are not limited to a molten NaCl-KCl solution and a molten CaCl.sub.2-NaCl solution. In some embodiments of the materials system, method, the solid product can be non-metallic. In some embodiments, the solid product material is the non-metallic solid material itself or a constituent of the non-metallic solid material. In some embodiments of the materials system, the solid material can be non-metallic. Examples of solid materials of the materials system of this disclosure that are non-metallic include but are not limited an oxide, an oxide bearing solid solution or an oxide-bearing composite material. Examples of oxide materials that can comprise a solid material of this materials system can be, but not limited to, one or more of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
[0073] It is yet another objective of this disclosure to describe a corrosion resistant device that can find applications where corrosion resistance to liquids is desired. On example of such an application is a heat transfer device where liquid flows through a heat exchanger or a heat-transfer device comprising a solid material. In such applications, the corrosion resistant device can comprise a solid-product layer, typically on the surface of a solid material, exposed to a liquid, wherein the concentration of the solid-product dissolved in the liquid is at saturation or at an elevated level. In some embodiments of the corrosion-resistant device, the solid product layer is on the surface of a solid material. In some embodiments of the corrosion-resistant device, the liquid is a molten salt. The solid materials in the corrosion-resistant device can be metallic or non-metallic (such as, but not limited to, solid solutions of non-metallic elements or compounds or ceramic materials or ceramic composite materials). Examples of solid materials for the corrosion resistant device include, but are not limited to, chromium, chromium-bearing material, aluminum, aluminum-bearing material, silicon, silicon-bearing material, beryllium, beryllium-bearing material, nickel, nickel-bearing material, iron, iron-bearing material, cobalt, cobalt-bearing material, copper, copper-bearing material, manganese, manganese-bearing material, titanium, titanium-bearing material, zirconium, zirconium-bearing material, hafnium, hafnium-bearing material, tungsten, tungsten-bearing material, molybdenum, molybdenum-bearing material, niobium, niobium-bearing material, vanadium, vanadium-bearing material, tantalum, tantalum-bearing material, yttrium, and yttrium-bearing material. In the corrosion resistant device described above, the solid product material can be one or more materials taken from the group consisting of than one of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0<x2.5), and YO.sub.x (with 0<x1.5).
[0074] In some embodiments of the corrosion resistant device, the molten salt is a molten salt solution. A molten salt solution refers herein to a single liquid salt phase that contains more than one molten salt species (e.g., a homogeneous liquid solution of NaCl and KCl). Examples of such molten salt solutions include but are not limited to a molten NaCl-KCl solution and a molten CaCl.sub.2-NaCl solution. In some embodiments of the corrosion-resistant device, the solid product can be non-metallic. In some embodiments, the solid product material is the non-metallic solid material itself or a constituent of the non-metallic solid material. In some embodiments of the corrosion-resistant device, the solid material can be non-metallic Examples of solid materials of the corrosion-resistant devices of this disclosure that are non-metallic include but are not limited an oxide, an oxide bearing solid solution, or an oxide-bearing composite material. Examples of oxide materials that can comprise a solid material of this method can be, but not limited to, one or more of Cr.sub.2O.sub.3, Al.sub.2O.sub.3, SiO.sub.2, BeO, NiO, FeO, Fe.sub.3O.sub.4, Fe.sub.2O.sub.3, CoO, Co.sub.2O.sub.3, Cu.sub.2O, MnO, Mn.sub.3O.sub.4, CuO, TiO.sub.x (with 0<x2), ZrO.sub.x (with 0<x2), HfO.sub.x (with 0<x2), WO.sub.x (where x can vary between 2.0 and 3.0), MoO.sub.x (where x can vary between 2.0 and 3.0), NbO.sub.x (with 0<x2.5), VO.sub.x (with 0<x2.5), TaO.sub.x (with 0 <x2.5), and YO.sub.x (with 0<x1.5).
[0075] It should be recognized that, in the methods, materials systems, and corrosion resistant devices of this disclosure, the solid materials whose resistance to corrosion in a liquid environment is desired to be enhanced can be a thermally conductive material.
[0076] It should be recognized that, in the methods, materials systems, and corrosion resistant devices of this disclosure, the solid materials whose resistance to corrosion in a liquid environment is desired to be enhanced can be a thermally insulating material.
[0077] It should be recognized that, in the methods, materials systems, and corrosion resistant devices of this disclosure, the non-metallic material can be one or more than one of a boride, a boride-bearing material, a carbide, a carbide-bearing material, a nitride, a nitride-bearing material, a sulfide, a sulfide-bearing material, an oxide, and an oxide-bearing material.
[0078] It should be recognized that, in the methods and materials systems of this disclosure, the solid product material can be an oxide of the non-metallic solid material or an oxide of a constituent of the non-metallic solid material.
[0079] It should be recognized that, in the methods and materials systems of this disclosure, the non-metallic material can be a composite material containing a mixture of two or more of a boride, a boride-bearing material, a carbide, a carbide-bearing material, a nitride, a nitride-bearing material, a sulfide, a sulfide-bearing material, an oxide, and an oxide-bearing material.
[0080] It should be recognized that, in the methods and materials systems of this disclosure, the non-metallic material can be an oxide solid solution containing two or more of a boride, a boride-bearing material, a carbide, a carbide-bearing material, a nitride, a nitride-bearing material, a sulfide, a sulfide-bearing material, an oxide, and an oxide-bearing material.
[0081] It should be recognized that in certain embodiments of the corrosion resistant device of this disclosure, that the device can be in contact with the molten salt and the device can be a container, a pipe, a valve, a pump, or a heat-transfer device.
[0082] The foregoing detailed description of the principles of this disclosure refers to molten salts and molten salt solutions. It should be recognized that the principles of the disclosure apply to molten salt mixtures as well. Molten salt mixtures comprise salts that are not mutually dissolvable in each other. Further when the solubility of one salt in another is exceeded in a molten salt solution, molten salt mixtures can result. Further some slurries are examples of molten salt mixtures.
[0083] While the present disclosure has been described with reference to certain embodiments, it will be apparent to those of ordinary skill in the art that other embodiments and implementations are possible that are within the scope of the present disclosure without departing from the spirit and scope of the present disclosure. For example, the components could be formed of materials other than those noted, and could be used in high-temperature applications other than those described. Accordingly, it should be understood that the disclosure is not limited to any embodiment described herein. It should also be understood that the phraseology and terminology employed above are for describing the disclosed embodiments, and do not necessarily serve as limitations to the scope of the disclosure.