Piezoresponsive Fibre Reinforced Polymer Composite

Abstract

A fibre-reinforced polymer composite comprising fibres bound within a solid polymer matrix, wherein at least some of the fibres are in contact with graphene, and wherein the composite changes electrical resistance when deformed.

Claims

1. A fibre-reinforced polymer composite comprising glass fibres bound within a solid polymer matrix, wherein at least some of the glass fibres are in contact with graphene, and wherein the composite changes electrical resistance when deformed.

2. A fibre-reinforced polymer composite comprising multidimensional glass fibre dispersion within a solid polymer matrix, wherein at least some of the glass fibres are in contact with graphene dispersed in said polymer, and wherein the composite displays changes in bulk electrical resistance or electrical conductivity when said composite is physically deformed.

3. The fibre-reinforced polymer composite of claim 1, wherein said change in resistance is reversible.

4. The fibre-reinforced polymer composite of claim 1, wherein the fibres are oriented in at least two directions.

5. The fibre-reinforced polymer composite of claim 1, wherein the fibres comprise the fibres of a textile.

6. The fibre-reinforced polymer composite of claim 5, wherein the textile is nonwoven.

7. The fibre-reinforced polymer composite of claim 5, wherein the textile is woven.

8. The fibre-reinforced polymer composite of claim 1, wherein the fibres comprise polyester fibres.

9. The fibre-reinforced polymer composite of claim 1, wherein the composite comprises a laminate structure in which the fibres are arranged in multiple fibrous layers within the polymer matrix.

10. The fibre-reinforced polymer composite of claim 1, wherein the graphene is present as a coating on the fibres.

11. The fibre-reinforced polymer composite of claim 5, wherein the graphene is present as a coating on the textile.

12. The fibre-reinforced polymer composite of claim 1, wherein the graphene is contained within the fibres.

13. The fibre-reinforced polymer composite of claim 1, wherein the fibres are distributed throughout the binding polymer.

14. The fibre-reinforced polymer composite of claim 1, wherein the composite acts as a strain sensor with a gauge factor greater than 8.

15. The fibre-reinforced polymer composite of claim 1, wherein the composite acts as a strain sensor with a gauge factor greater than 10.

16. The fibre-reinforced polymer composite of claim 1, wherein the composite acts as a strain sensor with a gauge factor greater than 12.

17. The fibre-reinforced polymer composite of claim 1, wherein the composite acts as a strain sensor with a gauge factor greater than 14.

18. A strain gauge comprising the fibre-reinforced polymer composite of claim 1.

19. Use of the fibre-reinforced polymer composite of claim 1 in the manufacture of a strain gauge.

20. Use of the detection of change in the electrical resistance, or electrical conductivity, of the fibre-reinforced polymer composite of claim 1 in the measurement of strain or deformation.

21. A structure which incorporates an integrated strain gauge for monitoring strain in the structure, wherein the structure of the strain gauge incorporates the fibre-reinforced polymer composite of claim 1.

Description

BRIEF DESCRIPTION OF THE FIGURES

[0022] FIG. 1 is a load-time graph for ten subsequent cycles of three-point bending of an FRP according to the invention, and the change in electrical response of an FRP according to the invention during ten subsequent cycles of three-point bending.

[0023] FIG. 2 shows graphed data for both compressive and tensile changes in an FRP according to the invention.

[0024] FIG. 3 shows the graphed results of a three-point compression bending mode up to a maximum force and cycled 10 times on a FRP according to the invention.

[0025] FIG. 4 shows the graphed voltage response of an FRP according to invention when subjected to impact compression.

[0026] FIG. 5 shows the graphed change in gauge factor of an FRP according to the invention under different levels of force.

DETAILED DESCRIPTION OF THE INVENTION

[0027] The present invention is embodied in a fibre-reinforced polymer (FRP) that incorporates sufficient graphene that is in contact with said fibres for e.g. piezoresistive qualities to be imparted to said polymer. This allows the polymer to be used as a sensor, wherein a physical deformation in the sensor will produce a measurable change in electrical properties of the FRP.

[0028] Various forms of graphene exist. Ideal graphene is pure carbon and is free of compositional defects and/or other chemical impurities, such as oxygen. Ideal graphene is highly conductive. Graphene oxide (GO) is a highly oxidised form of graphene that is an electrical insulator.

[0029] Intermediary species of GO can be referred to by various descriptions, such as partially reduced graphene oxide (prGO) or functionalised graphene, where various different chemical groups are attached to the edges and/or basal planes of the graphene.

[0030] Taking advantage of this functionality allows tailoring of the electrical and physical properties of the graphene, for example to make it easier to incorporate into or onto materials, such as plastics, to form composites.

[0031] Incorporation of heteroatoms, where carbon atoms are replaced by other atoms, such as nitrogen, and other covalently bonded atoms can also be used to tailor the properties of graphene.

[0032] Graphene can also come in various physical formats, including single layers or multiple layers of graphene. Various terminologies have been used to describe the structural variations and some attempts have been made at standardising terminology. The various single-layer and multi-layer graphene structures are all referred to herein as “graphene” unless otherwise specified.

[0033] The various forms of graphene lie on a continuous scale from electrically conductive to electrically insulating. This means many forms of graphene can be used as electrical conductors. Even relatively poorly conducting graphene can serve the purpose, especially where its other physical properties make it useful for a given application.

[0034] Graphene can be produced by many synthesis routes, including but not limited to: anodic bonding; carbon nanotube cleavage; chemical exfoliation; chemical synthesis; chemical vapour deposition; electrochemical exfoliation; electrochemical intercalation; growth on silicon carbide; liquid phase exfoliation; micromechanical cleavage; microwave exfoliation; molecular beam epitaxy; photo-exfoliation; precipitation from metal, and; thermal exfoliation.

[0035] Some of these routes give rise to materials referred to variously as: chemically converted graphene; few-layer graphene; GO; graphene; graphene oxide; graphene nanoflakes; graphene nanoplatelets; graphene nanoribbons; graphene nanosheets; graphite nanoflakes; graphite nanoplatelets; graphite nanosheets; graphite oxide; LCGO; liquid crystal graphene oxide; multi-layer graphene; partially reduced graphene oxide; partially reduced graphite oxide; prGO; rGO; reduced graphene oxide; reduced graphite oxide.

[0036] Incorporation of graphene into or onto glass fibres can be achieved by many methods, but in each case the properties of the fibres and the textile will affect the method of incorporation. The method of incorporation will depend on graphene chemistry, graphene shape and processes used to incorporate the graphene into or onto the fibres.

[0037] For synthetic or composite fibres, preferred methods include mixing the graphene into the polymer or composite prior to forming synthetic fibres. Both natural and synthetic fibres can be coated with graphene to make a conductive fibre. One method of coating glass fibres with graphene is described below in example 1.

[0038] The conductivity and piezoresistive response of the composite can be controlled by adjusting the amount of graphene included in the composite. In general, the greater the amount of graphene, the greater the conductivity of the composite facilitating detection by electrical means.

[0039] Below the electrically conductive threshold, no electrical signal can be extracted from the polymer, so no piezoresistive response would normally be detected. However, above the electrical percolation threshold the piezoresistive response depends on the strength of the interactions between the graphene platelets and can be optimised to give an optimal signal to noise ratio.

[0040] For dispersion of graphene into a polymer suitable for making synthetic or composite fibres, the graphene can be present as a powder or as a dispersion in a fluid. Pre-dispersion of the graphene in a suitable fluid facilitates dispersion of the graphene throughout the polymer.

[0041] Methods of incorporating graphene into a polymer include: melt-compounding of graphene into the polymer; in-situ polymerisation of the polymer with the graphene; and solution blending. Whichever technique is used, it is desirable that the graphene is sufficiently dispersed to achieve electrical conductivity with a minimum of added graphene. In some cases, additives are required to reduce phase separation of the graphene and the polymer.

[0042] In one embodiment of the present invention, the glass fibres are in the form of a textile. The concentrated form of the graphene polymer dispersion is mixed and diluted in the melt extrusion process to obtain the desired concentration of graphene in the fibres.

[0043] In another embodiment, a concentrated form of graphene is dispersed in a fluid, such as: oil, solvent or water prior to incorporate in or on the glass fibres.

[0044] Electrical measurements rely on electrical conductivity to form a circuit. The electrical resistance of said circuit depends on the size and length of the conductive path and the conductivity of the conductive media. This combination of variables gives a wide range over which the measurements can be effective.

[0045] Where the measurement is made using an FRP according to the invention, tuning the measurement method to the desired outcome and conditions will typically be required. This allows the electrical resistance of the composite to also be tailored to the desired application and measurement methods. Methods for doing this are well known in the art.

[0046] In some cases, the change in resistance is large and the circuit path is short. In some embodiments, the resistance of a circuit may be measured, in others it is the capacitance or inductance of the circuit that may be measured.

[0047] The glass fibres in the FRP are preferably oriented in at least two directions. For example, the glass fibres can be arranged in a bi-directional structure. In one embodiment, the glass fibres are woven together to form a fibrous two-dimensional layer such that some glass fibres in the layer are substantially orthogonal to other fibres in the layer.

[0048] In another embodiment, the fibres are formed into a three-dimensional structure, for example the glass fibres may comprise a textile in which fibres are oriented randomly in three dimensions.

[0049] The present invention will now be described with reference to the following non-limiting examples.

Example 1: Composite Laminate

[0050] The type of structure used in this example was glass fibre woven into a twill weave, with a weight of 300 g per sq/m.

[0051] The glass fibres were coated on each side with a graphene dispersion. The dispersion comprised 2 wt% graphene nanoplatelets (GNP), 94 wt% water, 4 wt% acrylic polymer, and <1 wt% cellulose polymer.

[0052] The coated fabrics were left to dry overnight at room temperature, followed by drying in a vacuum oven at 40° C. to remove excess water prior to composite fabrication.

[0053] The dry graphene coating was approximately 106 .Math.m thick. An epoxy resin (bisphenol-A-(epichlorohydrin)) and its associated amine-based hardener were mixed in a ratio of 100/25 to form a polymer matrix, and the graphene-coated glass fibres were impregnated in the epoxy resin.

[0054] A composite laminate structure was created by layering ten plies of the glass fibre impregnated resin via a wet lay-up technique, followed by vacuum-assisted curing at -700 mmHg for 24 hours at 25° C. The laminate structure was then left to cure overnight in ambient conditions and post-treated at 65° C. for 6 hours, forming a composite in which layers of glass fibre were bound within a solid polymer matrix.

[0055] Mechanical and electrical testing was performed on samples of a composite prepared as described above. Three-point bending tests were performed on 120 mm × 50 mm pieces of the composite in accordance with ASTM D7264. Tensile tests were performed on 250 mm × 25 mm pieces of the composite in accordance with ASTM D3039.

[0056] FIG. 1 shows a load-time graph for ten subsequent cycles of three-point bending and the change in electrical response during the ten cycles. The change in voltage indicates the change in resistance of the sample.

[0057] Each loading cycle was performed at a rate of 0.5 mm sec.sup.-1 and a sampling frequency of 100 Hz, reaching a maximum force of 300 N.

[0058] As can be seen in FIG. 1, the voltage changes in response to the applied bending load, indicating an increase in resistance with deformation of the FRP. In each loading cycle, the resistance increases in proportion to the applied load and recovers to the original value after unloading, which is consistent with piezoresistive behaviour. In other words, the composite is acting as a strain sensor in which mechanical bending displacement is converted into an electrical response.

[0059] It is hypothesised that the graphene layers within the FRP composite create an electrically conductive network which is responsive to dimensional changes. When a mechanical load is applied to the composite, the electrical resistance of the composite changes due to changes in electrical conductivity between graphene platelets.

[0060] When the composite is bent, one side is under is placed under tension and the other side is placed under compression. Tension increases the overall sensor resistance by increasing the distance between graphene platelets, while compression decreases the resistance by decreasing the distance between graphene platelets. These two opposing behaviours reduce the net change in sensor resistance.

[0061] Gauge factor is a well-known measure of the sensitivity of the electrical response of an FRP. Typically, a gauge factor of around 11 is desirable, but higher is advantageous. Most FRP composites have a gauge factor in the range 3 to 10. However, as can be seen in FIG. 5, the FRP of the present example demonstrates a gauge factor in excess of 11 at loadings of less than 4000 N.

Example 2: Coated Glass Fibre Composite

[0062] GF-epoxy composites were formed from four piles of continuous filaments of Advantex glass in random orientation (from Owens Corning Pty Ltd) while epoxy resin consisting of Prime 20 LV and Prime 20 slow hardener (from Gruit) at weight ratio 100:26 and mixed for 2 mins. This was was spread within the fabrics using a brush. The laminate was vacuumed at -700 mmHg for 24 hrs at 25° C., followed by post-curing in an oven at 65° C. for 6 hrs. The 0.5 mm thick laminate was cut to 15×4 cm tokens using a diamond cutter.

[0063] Two samples of the laminate were dip coated with two different concentrations (28 mg/ml and 65 mg/ml) of aqueous GNP dispersion in acrylic. Each face was coated four times. Each side was electrically insulated from the other. Electrical contacts were made to both top (compressive) and bottom (tensile) coatings. Silver conductive paint was used to minimise contact resistance changes during testing.

[0064] The samples were subjected to three-point bending tests at a rate of 30 mm/min with a maximum force of 6 N applied using an Instron material testing machine. FIG. 2 shows data for each sample for both compressive and tensile changes.

Example 3: Coated Glass Fibre Composite Bend Test

[0065] A sample of the FRP from Example 2 was tested in three-point compression bending mode up to a maximum force and cycled 10 times. Two different tests used maximum forces of 150 N and 250 N. The results are shown in FIG. 3.

Example 4: Coated Glass Fibre Composite Impact Test

[0066] A sample of the FRP from Example 2 was adhered to a force plate (Type 9260AA6, Kistler, Winterthur, Switzerland) and a series of impacts up to 200 N were applied and the voltage response recorded, as can be seen in FIG. 4.

[0067] Three sets of data were recorded and linear fits to each set gave relatively linear relationship between applied force and voltage change with R.sup.2=0.89 (±0.02).

[0068] A similar test at higher impacts up to 1000 N showed the response is relatively linear with R.sup.2=0.898.

[0069] It will be appreciated by those skilled in the art that the above described embodiment is merely one example of how the inventive concept can be implemented. It will be understood that other embodiments may be conceived that, while differing in their detail, nevertheless fall within the same inventive concept and represent the same invention.