RESISTANCE WELDING OF UNWELDABLE METALS WITH THERMAL SPRAYED INTERLAYERS

Abstract

A method for joining of at least two materials, non-weldable directly to each other with thermal joining processes in a lap joint configuration includes a two step sequence including a first step to apply a thermomechanical or mechanical surface protection layer on the surface of a (stainless) steel substrate and a second step where, a thermal joining process is used to weld the sprayed layer with an applied aluminum sheet without having brittle intermetallic phases in the whole material configuration.

Claims

1-15. (canceled)

16. A method for joining at least two materials, non-weldable directly to each other with a thermal joining processes in a lap joint configuration, comprising a first step of applying a thermomechanical or mechanical surface protection layer on a surface of a steel substrate and a second step of welding, via a thermal joining process, an aluminium sprayed layer with an applied aluminum sheet without having brittle intermetallic phases in the whole material configuration.

17. The method according to the claim 16, wherein only the aluminium sprayed layer to aluminium sheet contact area melts without having brittle intermetallic phases in a contact zone between the aluminium sprayed layer and the steel substrate.

18. The method according to the claim 16, wherein the thermomechanical or mechanical surface protection layer is applied by a thermomechanical coating method.

19. The method according to the claim 16, wherein the thermomechanical or mechanical surface protection layer is applied by a thermal spraying method.

20. The method according to claim 16, wherein the welding of the whole material configuration is set-up as a lap joint.

21. The method according to claim 16, wherein the sprayed layer is at least one of aluminum, an aluminum based alloy or a combination of aluminum with carbides.

22. The method according to claim 16, wherein the sprayed layer is welded with the applied sheet by a resistance welding method.

23. The method according to claim 16, wherein a ratio of the sprayed layer thickness to a reached spot weld diameter is at most equal to 0.25 mm.

24. The method according to claim 16, wherein a total sheet thickness comprising substrate, sprayed layer and applied sheet, is at least 1.5 mm and at most 6.0 mm.

25. The method according to claim 16, wherein a thickness of the sprayed layer is at least 0.25 and at most 1.5 mm.

26. The method according to claim 16, wherein a temperature of a transition zone between the sprayed layer and the base material is at most 350 C.

27. The method according to claim 16, wherein the substrate to be thermal sprayed comprises carbon steel having the carbon equivalent (CEV) of at least 0.65%, where CEV is calculated using a formula (element contents by weight %) CEV=C+Mn/6+(Cu+Ni)/15+(Cr+Mo+V)/5.

28. The method according to claim 16, wherein the substrate to be sprayed comprises a carbon steel material.

29. The method according to claim 16, wherein the substrate to be sprayed comprises stainless steel.

30. The method according to claim 16, further comprising the step of pretreating the substrate surface by cleaning and blasting.

31. The method according to claim 28, wherein the carbon steel material comprises carbon steel with a galvanized surface coating.

32. The method according to claim 22, wherein the resistance welding method comprises at least one of weld bonding, spot welding, projection welding or roller steam welding.

Description

[0034] The invention is described in more details in the following referring to the drawings, wherein

[0035] FIG. 1 illustrates as described in the prior art of the invention binary system Fe/Al intermetallic growth of phases between aluminium and steel,

[0036] FIG. 2 illustrates as described in the prior art of the invention a relation of intermetallic layer thickness and resulting strength level,

[0037] FIG. 3 illustrates one preferred embodiment of the thermal sprayed layer with the (stainless) steel substrate of the invention schematically from the side view and it shows the first step of sprayed aluminum layer to the base material/substrate,

[0038] FIG. 4 illustrates another preferred embodiment of the resistance spot welded thermal sprayed aluminum layer with an aluminum flat sheet of the invention schematically from the side view, where the welded thermal sprayed layer/stainless steel with another aluminum flat sheet is shown.

[0039] One kind of example is to create an aluminium thermal sprayed layer on to the top of stainless steel surface, which uses the effect of diffusion, adhesion, mechanical interlocking of the layer, chemical binding and where the layer on stainless steel is consisting of an aluminium-based alloy and which combination is welded by a resistance welding with an applied aluminum sheet to avoid intermetallic brittle phases.

[0040] In FIG. 1 illustrates a theoretical background for a binary system, which only works for infinitely long cooling rates and as a result of that the resistance spot welding has1,500 K/s cooling rate with brittle intermetallic phases: FeAl.sub.3 and Fe.sub.2Al.sub.5. A binary system* of Fe/Al is represented with a temperature range. *The source is from Guimaraens, E., university of Bayreuth, 2005.

[0041] In FIG. 2 illustrates a theoretical background for a phase growth, which is formulated with parabolic growth curve. The relation of intermetallic layer thickness and tensile strength is presented. As a result a layer thickness for typical spot welds is more than or equal to 15 m. The curve shows a strength decrease of more than 50% in comparison to aluminium base material (280 N/mm.sup.2). Because of that phenomenon in the present invention a method regarding to this any growth of an intermetallic phase during welding must avoid.

[0042] In FIG. 3 illustrates a schematic view of the preferred embodiment of the invention from the side view. The thermomechanical or mechanical Al-alloyed surface coating manufactured with a thermal sprayed interlayer (2) is on the top of substrate material (1) like stainless steel, which is non-weldable directly to each other.

[0043] In FIG. 4 illustrates a schematic view of the preferred embodiment of the invention from the side view, where conventional resistance welding process between thermal sprayed coating layer (2) on substrate (1) and an applied aluminium (3) sheet is used to join the material combination. There exist between the substrate (1), thermal sprayed interlayer (2) and aluminium sheet (3) a spot weld area (4). The temperature in the contact area between the substrate (1) and the thermal sprayed coating layer is under 350 Celsius degree.