PROCESS FOR PRODUCING A COMPOSITE MATERIAL

Abstract

A process for producing a composite material comprising at least one particulate material and at least one polymeric binder, wherein the at least one particulate material and the at least one polymeric binder are mixed with one another and mechanically processed in the presence of at least one process auxiliary which reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder, essentially dispensing with the use of solvents, characterized in that the weight ratio of process auxiliary to polymeric binder is within a range from 3:10 to 0.1:20.

Claims

1. A process for producing a composite material comprising at least one particulate material and at least one polymeric binder, wherein the at least one particulate material and the at least one polymeric binder are mixed with one another and mechanically processed in the presence of at least one process auxiliary which reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder, essentially dispensing with the use of solvents, and wherein the weight ratio of process auxiliary to polymeric binder is within a range from 3:10 to 0.1:20.

2. The process according to claim 1, wherein a mixture comprising the at least one particulate material, the at least one polymeric binder and the at least one process auxiliary is first provided and is then mechanically processed.

3. The process according to claim 1, wherein the weight ratio of process auxiliary to polymeric binder is within a range from 2:10 to 0.1:10.

4. The process according to claim 1, wherein the process auxiliary is used in the form of particles, and the ratio of the average particle diameter of the particulate material to the average particle diameter of the particulate process auxiliary is within a range from 2000:1 to 0.4:1.

5. The process according to claim 1, wherein the process auxiliary is selected from solid-state lubricants and separating agents.

6. The process according to claim 1, wherein the at least one particulate material comprises at least one electrode active material for an electrochemical energy storage means and the polymeric binder comprises at least one polymer electrolyte.

7. The process according to claim 1, wherein the at least one particulate material accounts for at least 85% by weight of the constituents used, based on the total weight of the composite composition.

8. The process according to claim 1, wherein the composite material is provided in the form of a homogeneous film having a thickness of less than 300 m.

9. A process for producing a composite material comprising at least one particulate material, at least one polymeric binder and at least one process auxiliary, wherein the particulate material comprises at least one electrode active material and the polymeric binder comprises at least one polymer electrolyte, wherein the at least one particulate material and the at least one polymeric binder are mixed with one another and mechanically processed in the presence of at least one process auxiliary which reduces the mechanical and/or chemical interaction between the surfaces of the at least one particulate material and of the at least one polymeric binder, essentially dispensing with the use of solvents, and wherein the weight ratio of process auxiliary to polymeric binder is within a range from 3:10 to 0.1:20.

10. A composite material comprising at least one particulate material, at least one polymeric binder and at least one process auxiliary, characterized in that the weight ratio of process auxiliary to polymeric binder is within a range from 3:10 to 0.1:20.

11. The composite material according to claim 10, wherein the particulate material comprises at least one electrode active material and the polymeric binder comprises at least one polymer electrolyte.

12. The composite material according to claim 10, wherein the composite material is essentially free of pores.

13. The composite material according to claim 10, wherein the composite material has the following composition: (i) 85.0% to 98.9% by weight of the at least one particulate material; (ii) 1.0% to 14.9% by weight of the at least one polymeric binder; (iii) 0.1% to 3.0% by weight of the at least one process auxiliary; and (iv) 0% to 10% by weight of further process auxiliaries, based in each case on the total weight of the composite composition.

14. An electrochemical energy storage device or an electrochemical energy converter device having an electrode made of a composite material according to claim 10.

15. An electrochemical energy storage device or electrochemical energy converter device comprising a composite material according to claim 10.

Description

EMBODIMENTS OF THE INVENTION

[0077] The working examples which follow illustrate the subject matter of the invention.

[0078] Composite compositions having the following composition are provided: [0079] polymeric binder(s): 0.1-5% by weight, especially 0.2-3% by weight; [0080] process auxiliary/auxiliaries: 0.5-2% by weight; [0081] conductivity additive in the production of an anode: 0-2% by weight or [0082] conductivity additive in the production of a cathode: 1-5% by weight, especially 1.5-3% by weight.

[0083] The remaining proportion of the composite composition is formed by the at least one particulate material, resulting in a total amount of 100% by weight based on the total weight of all constituents of the composite composition.

[0084] The examples which follow give a detailed description of the selection of the individual components and processing thereof.

Example 1

[0085] Active material (lithium iron phosphate) having an average particle diameter of 0.5 m, process auxiliaries (preferably graphite, PTFE and/or molybdenum sulfide) having an average particle diameter of 0.5 m to 10 m, conductive carbon black (C65) and polymer electrolyte (mixture of polyethylene oxide, for example having a chain length of 600 000 g/mol, and LiTFSi) are mixed in dry form, the PEO is at least partly melted or dissolved, and the mixture obtained is extruded in an extruder through a die. The film thus obtained is rolled to target thickness in a roll mill.

Example 2

[0086] Active material (e.g. mixed lithium nickel cobalt manganese oxide) having an average particle diameter of 10 m, process auxiliaries (graphite having an average particle diameter of 0.5 m to 10 m or PTFE having an average particle size of 2 m to 10 m, conductive carbon black (e.g. C65) and polymer electrolyte (mixture of polyethylene oxide, for example having a chain length of 600 000 g/mol, and LiTFSi) are mixed in dry form, the PEO is at least partly melted, and the mixture obtained is extruded in an extruder through a die. The film thus obtained is rolled to target thickness in a roll mill.

Example 3

[0087] The active material is processed with a portion of polymer electrolyte (mixture of polyethylene oxide, for example having a chain length of 600 000 g/mol, and LiTFSi) and a portion of conductive carbon black (e.g. C65) to give agglomerates (for example by means of a melting process, kneading, application of solvent, or fluidized bed process). The agglomerates are mixed with the process auxiliary in order to be able to move the agglomerates easily counter to one another in the course of extruding or rolling. Subsequent forming of the film by extruding a film or rolling the agglomerates together in a calender, possibly with simultaneous degassing or application of a reduced pressure, to give a film.

Example 4

[0088] A separating agent is deliberately applied to a polymer that (partly) forms the polymeric binder or is selected in order that the polymer can be processed better. The separating agent is chemically and/or electrochemically stable in an electrochemical cell under all operating conditions. The separating agent may be a further polymer (for example PTFE) or an inert, preferably inorganic, separating agent. Preferably, an electrochemically inert separating agent (which is also stable at electrochemical potentials up to and above 5 V vs. Li/Li.sup.+) is used for this purpose, for example Al.sub.2O.sub.3, ZrO, SiC, BN, or further very stable oxides, carbides or similar (electro)chemically very stable substances.

Example 5

[0089] A separating agent is used as in example 4. However, this is selected such that the separating agent breaks down in the electrochemical cell and/or takes place in the cell reaction in an intentional and defined manner (for example as active material, i.e. material for storage of lithium ions, for example, in the lithium ion cell, for example SiO or SiO.sub.x). The separating agent is deliberately applied to a polymer that (partly) forms the polymeric binder or is selected such that the polymer can be processed better. The separating agent here is either electrochemically stable in the electrochemical cell and/or takes part in the cell reaction, for example as active material, and/or in the formation of a solid electrolyte interphase outer layer, and hence is irreversibly consumed.

Example 6

[0090] The active material is processed together with an amount of a solid-state electrolyte (e.g. oxidic, phosphatic or sulfidic glasses), polymeric binder (e.g. PEO) and a portion of conductive black (e.g. C65) to give agglomerates (for example by kneading, application of solvent, and/or by means of a fluidized bed process). The agglomerates are mixed with the process auxiliary in order to be able to move the agglomerates easily counter to one another in the course of rolling or possibly extruding. Subsequent forming of the film by extruding a film or rolling the agglomerates together in a calender to form a film. If required, additional amounts of solid-state electrolyte or active material, either in pretreated or non-pretreated form, are added in the film formation.

Example 7

[0091] The procedure is analogous to example 6, except that no active material is used; instead, only an amount of a solid-state electrolyte, polymeric binder (e.g. PEO) and a portion of conductive carbon black (e.g. C65) are processed to give agglomerates (for example by kneading, application of solvent and/or by means of a fluidized bed method). The further processing, possibly with further solid-state electrolyte, is analogous to example 6.

[0092] The invention is not limited to the working examples described here and the aspects emphasized therein. Instead, a multitude of modifications within the realm of activity of a person skilled in the art are possible within the scope defined by the claims.