MONOGLYCEROL ACRYLATE BASED POLYMER AND USES THEREOF
20240101733 ยท 2024-03-28
Inventors
Cpc classification
C08L91/00
CHEMISTRY; METALLURGY
International classification
C08L91/00
CHEMISTRY; METALLURGY
Abstract
The present document relates to amphiphilic poly(monoglycerol acrylate) (PMGA) polymers, comprising an hydrophilic repeating unit of monoglycerol acrylate and one or more biodegradable hydrophobic group and their use and methods of use in the delivery of bioactive agents. Additionally, the invention provides a method for preparing monoglycerol acrylate-based polymers.
Claims
1-41. (canceled)
42. An amphiphilic poly(monoglycerol acrylate) (PMGA) polymer, comprising an hydrophilic repeating unit of monoglycerol acrylate; and one or more biodegradable hydrophobic group; wherein the polymer is a comb polymer having an average molecular weight (Mw) ranging between 1000 and 15000, ranging between 1800 and 12000, of about 1800, of about 6500, or of about 12000; and wherein the Mw of the at least one biodegradable hydrophobic group represents at least 5%, at least 10%, at least 30%, between 5% and 30%, between 10% and 30%, about 5%, about 10% or about 30% of the average Mw of the polymer.
43. The amphiphilic PMGA polymer according to claim 42, wherein the repeating unit of monoglycerol acrylate is: ##STR00015## wherein n is an integer between 10 and 80, between 30 and 50, between 40 and 50, or about 42.
44. The amphiphilic PMGA polymer according to claim 42, wherein the PMGA polymer is of Formula (I): ##STR00016## wherein, wherein n is an integer between 10 and 80, between 30 and 50, between 40 and 50, or about 42; X is (CH.sub.2)m- with m between 0 and 4; R.sub.1 is a donor group or R.sub.1 is halogen, H, OH, SH, S(C?S)SC.sub.6-10aryl, S(C?S)SC.sub.1-24alkyl, S(C?S)C.sub.1-24alkyl, or S(C?S)Ph; Y is OH, COON, OR.sub.6, COO(CH.sub.2).sub.LNR.sub.2R.sub.3 or CONR.sub.2R.sub.3 with L between 1 and 18; R.sub.2 and R.sub.3 are each independently H, C.sub.6-10 aryl, C.sub.3-12 cycloalkyl, steroidyl groups, C.sub.3-24 alkyl, C.sub.3-24 alkenyl or C.sub.3-24 alkynyl; R.sub.4 and R.sub.5 are each independently H, CH.sub.3 or CN; and R.sub.6 is (CH.sub.2).sub.L.Math.CH.sub.3, or (CH.sub.2).sub.L.Math.NR.sub.2R.sub.3 with L between 0 and 18.
45. The polymer of formula (I) according to claim 44, wherein R.sub.2 and R.sub.3 are each independently linear C.sub.6-24 alkyl.
46. The polymer of formula (I) according to claim 44, wherein R.sub.1 is SH.
47. The polymer of formula (I) according to claim 44, wherein n is comprised between 30 and 50.
48. The polymer of formula (I) according to claim 44, wherein R.sub.4 is CH.sub.3 and R.sub.5 is CN.
49. The polymer of formula (I) according to claim 44, wherein X is CH.sub.2 CH.sub.2- and Y is CONR.sub.2R.sub.3.
50. The polymer of formula (I) according to claim 44, wherein R.sub.1 is SH, R.sub.4 is CH.sub.3, R.sub.5 is CN, X is CH.sub.2CH.sub.2- and Y is CONR.sub.2R.sub.3, wherein R.sub.2 and R.sub.3 are C.sub.18H.sub.37.
51. The polymer of formula (I) according to claim 44, wherein R.sub.1 is S(C?S)S(CH.sub.2).sub.11CH.sub.3, R.sub.4 is CH.sub.3, R.sub.5 is CN, X is CH.sub.2CH.sub.2- and Y is CONR.sub.2R.sub.3, wherein R.sub.2 and R.sub.3 are C.sub.18H.sub.37.
52. A method of preparing an amphiphilic PMGA polymer as defined in claim 42, said method comprising: providing a monoglycerol acrylate monomer, radically polymerizable monomer; providing a chain transfer agent; and polymerizing the monomer via reversible addition-fragmentation chain-transfer polymerization (RAFT), in the presence of a free radical initiator and the chain transfer agent, wherein said polymerization is carried out in conditions allowing to obtain a polymer incorporating at least 10 monomer units (n), and wherein the method optionally further comprises the removal of thiocarbonylthio end groups by chemical reaction.
53. The method according to claim 52, wherein radically polymerizable monomer is monoglycerol acrylate and/or the chain transfer agent is selected from the group consisting of: ##STR00017##
54. A lipid particle, wherein the lipid particle comprises: a ionizable lipid; a phosphatidyl choline; a sterol; and an amphiphilic PMGA polymer as defined in claim 42.
55. The lipid particle of claim 54, wherein the ionizable lipid is SM-102, the phosphatidyl choline is HSPC and/or sterol is cholesterol.
56. The lipid particle according to claim 54, wherein said particle is a lipid nanoparticle.
57. The lipid particle according to claim 56, wherein the lipid particle comprises molar ratios of 10% of HSPC, 50% of SM-102, 38.5% of cholesterol and 1.5% of the amphiphilic PMGA polymer.
58. The lipid particle according to claim 54, wherein said particle is a liposome optionally comprising a bioactive agent.
59. The lipid particle according to claim 58, wherein the lipid particle comprises molar ratios of about 58% of SM-102 and HSPC, 40% of cholesterol and 2% of the amphiphilic PMGA polymer.
60. The lipid nanoparticle according to claim 58, further wherein the bioactive agent is a drug, or a nucleic acid selected from the group consisting of mRNA, siRNA, shRNA and microRNA.
61. A pharmaceutical composition comprising the lipid particle according to claim 54, and a pharmaceutically acceptable excipient, carrier, or diluent.
Description
BRIEF DESCRIPTION OF THE FIGURES
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
[0053]
[0054]
[0055]
DETAILED DESCRIPTION
Definitions
[0056] All technical and scientific terms and expressions used herein have the same definitions as those commonly understood by a person skilled in the art to which the present technology pertains. The definition of some terms and expressions used is nevertheless provided below. To the extent the definitions of terms in the publications, patents, and patent applications incorporated herein by reference are contrary to the definitions set forth in this specification, the definitions in this specification will control. The section headings used herein are for organizational purposes only and are not to be construed as limiting the subject matter disclosed.
[0057] Chemical structures described herein are drawn according to conventional standards. Also, when an atom, such as a carbon atom, as drawn seems to include an incomplete valency, then the valency is assumed to be satisfied by one or more hydrogen atoms even though these are not necessarily explicitly drawn. Hydrogen atoms should be inferred to be part of the compound.
[0058] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. It should be noted that, the singular forms a, an, and the include plural forms as well, unless the content clearly dictates otherwise. Thus, for example, reference to a composition containing a compound also contemplates a mixture of two or more compounds. It should also be noted that the term or is generally employed in its sense including and/or unless the context clearly dictates otherwise. Furthermore, to the extent that the terms including, includes, having, has, with, or variants thereof are used in either the detailed description and/or the claims, such terms are intended to be inclusive in a manner similar to the term comprising.
[0059] The term about or approximately means within an acceptable error range for the particular value as determined by one of ordinary skill in the art, which will depend in part on how the value is measured or determined, i.e., the limitations of the measurement system. For example, about can mean within 1 or more than 1 standard deviation, per the practice in the art. Alternatively, about can mean a range of up to 20%, preferably up to 10%, more preferably up to 5%, and more preferably still up to 1% of a given value. Alternatively, particularly with respect to biological systems or processes, the term can mean within an order of magnitude, preferably within 5-fold, and more preferably within 2-fold, of a value. Where particular values are described in the application and claims, unless otherwise stated the term about meaning within an acceptable error range for the particular value should be assumed.
[0060] Unless otherwise stated, structures depicted herein are also meant to include all isomeric (e.g., enantiomeric, diastereomeric, tautomeric and geometric (or conformational) forms of the structure when applicable; for example, the R and S configurations for each asymmetric center. Therefore, single stereochemical isomers as well as enantiomeric, diastereomeric, tautomeric and geometric (or conformational) mixtures of the present compounds are within the scope of the present description. The present compounds unless otherwise noted, also encompasses all possible tautomeric forms of the illustrated compound, if any. The term also includes isotopically labeled compounds where one or more atoms have an atomic mass different from the atomic mass most abundantly found in nature. Examples of isotopes that may be incorporated into the present compounds include, but are not limited to, .sup.2H (D), .sup.3H (T), .sup.11C, .sup.13C, .sup.14C , .sup.15N , .sup.18O, .sup.17O, any one of the isotopes of sulfur, etc. The compounds may also exist in unsolvated forms as well as solvated forms, including hydrated forms. The compounds may exist in multiple crystalline or amorphous forms. In general, all physical forms are equivalent for the uses contemplated herein and are intended to be within the scope of the present invention.
[0061] The number of carbon atoms in a hydrocarbon substituent can be indicated by the prefix C.sub.x-C.sub.y or C.sub.x-y where x is the minimum and y is the maximum number of carbon atoms in the substituent.
[0062] The term alkyl as used herein, refers to a saturated, straight- or branched-chain hydrocarbon radical typically containing from 1 to 24 carbon atoms. For example, C.sub.1-8 alkyl contains from one to eight carbon atoms. Examples of alkyl radicals include, but are not limited to, methyl, ethyl, propyl, isopropyl, n-butyl, tert-butyl, neopentyl, n-hexyl, heptyl, octyl radicals and the like.
[0063] The term alkenyl as used herein, denotes a straight- or branched-chain hydrocarbon radical containing one or more double bonds and typically from 2 to 24 carbon atoms. For example, C.sub.2-8alkenyl contains from two to eight carbon atoms. Alkenyl groups include, but are not limited to, for example, ethenyl, propenyl, butenyl, 1-methyl-2-buten-1-yl, heptenyl, octenyl and the like.
[0064] The term alkynyl as used herein, denotes a straight- or branched-chain hydrocarbon radical containing one or more triple bonds and typically from 2 to 24 carbon atoms. For example, C.sub.2-8alkynyl contains from two to eight carbon atoms. Representative alkynyl groups include, but are not limited to, for example, ethynyl, 1-propynyl, 1-butynyl, heptynyl, octynyl and the like.
[0065] The term aryl used alone or as part of a larger moiety as in aralkyl, aralkoxy, aryloxy, or aryloxyalkyl, refers to aromatic groups having 4n+2 conjugated ?(pi) electrons, wherein n is an integer from 1 to 3, in a monocyclic moiety or a bicyclic or tricyclic fused ring system having a total of six to 15 ring members, wherein at least one ring in the system is aromatic and wherein each ring in the system contains three to seven ring members. The term aryl may be used interchangeably with the expression aryl ring. In certain embodiments of the present description, aryl refers to an aromatic ring or ring system which includes, but is not limited to, phenyl, biphenyl, naphthyl, azulenyl, anthracyl and the like, which may bear one or more substituents. The term aralkyl or arylalkyl refers to an alkyl residue attached to an aryl ring. Examples of aralkyl include, but are not limited to, benzyl, phenethyl, and the like. Also included within the scope of the term aryl, as it is used herein, is a group in which an aromatic ring is fused to one or more non-aromatic rings, such as indanyl, indenyl, phthalimidyl, naphthimidyl, fluorenyl, phenanthridinyl, or tetrahydronaphthyl, and the like. The term C.sub.6-naryl refers to an aryl group having from 6 to the indicated n number of atoms in the ring structure.
[0066] The term donor group refers to a substituent that can donate some of its electron density to neighboring atoms, usually by resonance or inductive effects. Examples of donor groups include but are not limited to: CH.sub.3, OR.sub.a, NR.sub.aR.sub.b, SR.sub.a and PR.sub.aR.sub.b. R.sub.a and R.sub.b represent independently H or alkyl chains having at least one carbon atom.
[0067] The term hydrophobic group used herein refers to a moiety which is covalently attached via a suitable linker to the hydrophilic repeating unit of monoglycerol acrylate and permits anchoring into the lipid membrane of a lipid particles. Suitable hydrophobic groups includes alkyl, alkenyl or alkynyl chains having 3 to 24, 6 to 24, 12 to 24, 18 to 24 carbons, saturated or unsatured, fatty acids having 6 to 24, 6 to 24, 12 to 24, 18 to 24 carbons in the aliphatic group and which can be linear or branched, (e.g., (iso)lauric, (iso)myristic, (iso)palmitic, or(iso)stearic acid, lauroleic, physeteric, myristoleic, palmitoleic, petroselinic, or oleic acid), and sterols.
[0068] The term biodegradable refers a group that that can be degraded under physiological conditions, for example, by means of hydrolysis or via an enzymatic reaction. In one aspect, when a biodegradable hydrophobic group is incorporated into a polymer according to the invention, this means that the polymer when administered to a subject such as a human disappears from the body over time.
[0069] As used herein, physiological conditions refers to conditions present in an organism including a human. For example, a pH of about 7.4 and a temperature of about 37? C.
[0070] The expression reversible addition-fragmentation chain-transfer (RAFT) refers to a synthetic method allowing the preparation of synthetic polymers via a mechanism of radical polymerization. The method of polymerization RAFT as used herein involves the polymerization of monomer units by addition-fragmentation and chain-transfer. Such method can provide complex polymer structures, such as copolymers, star-polymers and branched-polymers, including but not limited to comb-polymers. The RAFT polymerization experimental conditions involve a RAFT agent, also known as chain-transfer agent, a radical source, a monomer and a solvent.
[0071] The term chain transfer agent (CTA) or RAFT agent refers to the reagent used in the RAFT polymerization reaction. The CTA is used in RAFT polymerization to control the average molecular weight of the final polymer. The CTA is involved in a chain transfer reaction as it has a least one weak chemical bond which facilitates the chain transfer. Chain transfer agents can comprise, but are not limited to, compounds having dithioester or thiocarbonylthio groups.
PMGA Based Polymers
[0072] The present invention relates to amphiphilic poly(monoglycerol acrylate) (PMGA) polymers (PMGA based polymers). The PMGA based polymers comprise a hydrophilic repeating unit of monoglycerol acrylate and one or more biodegradable hydrophobic group as defined herein.
[0073] The amphiphilic properties of the PMGA based polymers allow them to be formulated as lipid particles such as lipid nanoparticles or liposomes. In one aspect, when formulated with lipid particles such as lipid nanoparticles or liposomes, the polymers of the present description allow for stabilization of the lipid particles while improving cellular targeting and uptake.
[0074] In one aspect, there is provided a PMGA polymer of Formula (I):
##STR00002## [0075] wherein the following embodiments are present alone or in combination: [0076] wherein n is an integer between 10 and 80, between 30 and 50, between 40 and 50, or about 42; [0077] X is (CH.sub.2).sub.m-with m between 0 and 4; m is an integer between 0 and 2 or m is 0; [0078] R.sub.1 a donor group or R.sub.1 is halogen, H, OH, SH, S(C?S)SC.sub.6-10aryl, S(C?S)SC.sub.1-24alkyl, S(C?S)C.sub.1-24alkyl, S(C?S)Ph; or R.sub.1 is halogen, H, OH, SH, S(C?S)SC.sub.6-10aryl, S(C?S)SC.sub.1-24alkyl; or R.sub.1 is OH, SH, or S(C?S)SC.sub.1-24alkyl; [0079] Y is OH, COOH, OR.sub.6, COO(CH.sub.2).sub.LNR.sub.2R.sub.3 or CONR.sub.2R.sub.3 with L between 1 and 18; or Y is OH, COOH, OR.sub.6, COO(CH.sub.2).sub.LNR.sub.2R.sub.3 or CONR.sub.2R.sub.3 with L between 1 and 18; or Y is OH orCONR.sub.2R.sub.3; or Y is CONR.sub.2R.sub.3; [0080] R.sub.2 and R.sub.3 are each independently H, C.sub.6-10 aryl, C.sub.3-12 cycloalkyl, steroidyl groups, C.sub.3-24 alkyl, C.sub.3-24 alkenyl or C.sub.3-24 alkynyl; or R.sub.2 and R.sub.3 are each independently C.sub.3-24 alkyl; [0081] R.sub.4 and R.sub.5 are each independently H, CH.sub.3 or CN; and [0082] R.sub.6 is (CH.sub.2).sub.LCH.sub.3, (CH.sub.2).sub.L.Math.NR.sub.2R.sub.3 with L between 0 and 18 or R.sub.6 is (CH.sub.2)LCH.sub.3, (CH.sub.2).sub.L.Math.NR.sub.2R.sub.3 with L between 0 and 6 or R.sub.6 is (CH.sub.2).sub.L.Math.NR.sub.2R.sub.3 with L between 1 and 6.
[0083] In a further aspect, the following embodiments are present alone or in combination [0084] R.sub.2 and R.sub.3 are each independently linear C.sub.6-24 alkyl. R.sub.2 and R.sub.3 are both C.sub.18H.sub.37. [0085] R.sub.1 is halogen, H, OH, SH, S(C?S)SC.sub.6-10aryl, S(C?S)SC.sub.1-24 alkyl. R.sub.1 is halogen, H, OH or SH. R.sub.1 is S(C?S)SC.sub.10-24alkyl. R.sub.1SH. [0086] n is comprised between 30 and 50. n is 42. [0087] R.sub.4 is CH.sub.3. [0088] R.sub.5 is CN. [0089] X is CH.sub.2 CH.sub.2-. [0090] Y is CONR.sub.2R.sub.3.
[0091] In one aspect, there is provided a PMGA polymer of Formula (I):
##STR00003## [0092] wherein n is an integer between 40 and 50, or about 42; [0093] X is (CH.sub.2).sub.m- with m being 2; [0094] R.sub.1 is SH, or S(C?S)SC.sub.10-16alkyl; [0095] Y is is CONR.sub.2 R.sub.3, [0096] R.sub.2 and R.sub.3 are each independently C.sub.3-24 alkyl or C.sub.6-24 alkyl or C.sub.18-24 alkyl; and [0097] R.sub.4 and R.sub.5 are each independently H, CH.sub.3 or CN provided that one of R.sub.4 and R.sub.5 is CH.sub.3 or CN; or R.sub.4 is CN and R.sub.5 is CH.sub.3.
[0098] In one aspect, there is provided a PMGA polymer of Formula (I):
##STR00004## [0099] wherein n is about 42; [0100] X is (CH.sub.2).sub.m- with m being 2; [0101] R.sub.1 is SH, or S(C?S)SC.sub.10-14alkyl; [0102] Y is is CONR.sub.2 R.sub.3; [0103] R.sub.2 and R.sub.3 are each independently C.sub.18alkyl; and [0104] R.sub.4 is CN and R.sub.5 is CH.sub.3.
Synthesis and Characterization of Polymers
[0105] ##STR00005##
[0106] To allow anchoring of the poly(mocoglycerol acrylate) or PMGA to liposomes irrespective of the presence of the Z dodecyl-moiety, we conjugated dioctadecylamine (DODA) to the R-group of a trithiocarbonate chain transfer agent (CTA). Trithiocarbonate CTA are less active than dithioesters as transfer agents but still allow a good control over the polymerization of acrylates. Also, trithiocarbonate CTA give less retardation, are less prone to hydrolytic degradation and more readily synthesized.
##STR00006##
[0107] The CTA-PMGA-DODA polymer synthesized with the DODA-CTA contains three alkyl chains, two 18-carbon tails on the R-group (dioctadecylamine) and one dodecyl moiety on the Z-group (12 carbons). In theory, both hydrophobic segments can contribute to the polymolecular assemblies and can act as anchoring points on the lipid bilayer. However, it has been shown that longer alkyls chains remain associated with the membrane longer in biological samples due to more energy required for them to leave the bilayer. Also, CTAs with dodecyl Z-groups are sulfur analogs designed to rapidly undergo radical homolysis between the thiocarbonylthio function and the polymer. The bond created between those is normally weak enough to be prone to hydrolysis. Hydrolytic susceptibility is accelerated by the increase of temperature and pH. In Chemical Communications 2009, (24), 3580-3582, was reported substantial cytotoxicity in vitro due to the hydrolytic release of the RAFT moiety (dithiocarbonate). The authors observed no cytotoxicity with the trithiocarbonate function since they are more stable and resistant to hydrolysis. However, in Macromolecules 2011, 44 (8), 2524-2530 was demonstrated later that trithiocarbonate functions can also have apparent toxicities. They suggest that trithiocarbonate end groups attached to linear polymers are more susceptible to hydrolysis than those attached on non-linear polymer due to steric effects. While toxicity arguments support the removal of the Z-group before in vitro and in vivo experiments, we also conducted experiments with the presence of an alkylated Z-group to evaluate its influence on the stability of liposomes (CTA-PMGA-DODA polymer). The CTA-PMGA-DODA polymer can be submitted to hydrolysis using a mixture of two radical initiators, such has lauroyl peroxide (LPO) and azobisisobutironitrile (AlBN) (2:20 molar equivalent to the polymer) to afford the PMGA-DODA polymer with the thiol end group. The molecular weight of the CTA-PMGA-DODA polymer was determined by .sup.1H-NMR by integrating the signal of the CH.sub.3 at the end of the alkyl chain (0.9 ppm). The polydispersity index (M.sub.w/M.sub.n) was also evaluated by size exclusion chromatography analysis (SEC) using a Polysep-GFC P-3000 with 70% methanol in water, a mobile phase that disrupted the intermolecular interactions between the polymers. The M.sub.w/M.sub.n was around 1.30 and the molecular weight was 5904 g/mol (n=41). Reversible addition fragmentation chain-transfer (RAFT) polymerization was conducted with a CTA/initiator ratio ([CTA]/[I]) of 10, classic conditions for RAFT are 70? C. with a pressure under 200 bars and in the absence of oxygen as reported in Angewandte Chemie International Edition 2014, 53 (26), 6683-6686.
Preparation and Characterization of Liposome and Stability of the Carrier
[0108] One of the most common approaches used to prepare liposomes is the thin film hydration method also known as the Bangham method. This method relies on the spontaneous rearrangement of dried lipids into spherical vesicles in water as described in Processes 2020, 8 (9), 1022. These relatively large multilamellar vesicles are further extruded through polycarbonate membranes to form smaller monodisperse unilamellar vesicles. Here, this process allowed preparing liposomes with and without PMGA (CTA-PMGA-DODA or PMGA-DODA) with a diameter of around 100 nm, as measured by Dynamic Light Scattering (DLS).
[0109] To monitor the incorporation of the polymer into the liposomes, a fluorescent polymer was synthesized by incorporating 1 mol % of acrylic acid (AA) to the synthesis and conjugating carboxylic functions to amino-terminated fluorescein cadaverin. The molecular weight of this polymer was characterized by .sup.1H-NMR to obtain 5616 g/mol (n=39). Size exclusion chromatography (SEC) was used to evaluate the integration of the polymer in the liposomes. Chromatography methods, including SEC and ion exchange chromatography, allow the removal of free polymer chains from liposomes preparations. In SEC, liposomes can be separated from solutes with lower molecular weight by carefully choosing the gel. The Sepharose? CL-4B was evaluated. On a 1?20 cm column, both elution peaks overlapped (i.e., liposome and free polymer). We then explored whether varying the length and inner diameter of the column could result in better separation.
[0110]
[0111] Since polymeric micelles can be a drug delivery platform on their own, defined by their thermodynamic stability, these experiments emphasize that the system we are using is liposomes and not micellar structures. Indeed, it is known that amphiphilic structures can self-assemble on their own to created micellar structures. We characterized the critical micellar concentration (CMC) of the polymers to evaluate their ability to self-assemble into polymolecular structures. It is generally accepted that increasing the percentage of hydrophobic block results in a decrease of the CMC, suggesting polymers require fewer molecules to form micelles as discussed in Journal of Controlled Release 2005, 109 (1), 169-188. As expected, the polymer with the dodecyl moiety (CTA-PMGA-DODA) appears to have a lower CMC than the polymer on which the Z group was hydrolyzed (PMGA-DODA) (Example 4ii). To further confirm that the results of the Sepharose? CL-4B SEC are truly representative of interactions with liposomes and not the formation of micelles but also to monitor the stability of the PMGA-DODA anchoring on the liposome, we performed dialysis using the fluorescent polymer. This technique relies on the diffusion of molecules through a semi-permeable membrane to separate solutes from larger colloids. This technique can be used for purification or to study the speed at which drug delivery system (DDS) release their encapsulated molecules as shown in Chemical industry press. 2015, 1st edn., 175-177. In
[0112] Osmotic stress imposed by salt gradients can result in the disruption of the phospholipid membranes of liposomes. Liposomes swell more rapidly under hypertonic conditions, compared to isotonic environments as reported in Biochimica et Biophysica Acta (BBA)Biomembranes 1991, 1069 (1), 5-13. Interestingly, the release of the dye is much more important when put into a hypotonic medium. In fact, all the content inside the liposome is released drastically in hypotonic solutions (
Internalization of Different Cells Line
[0113] We evaluated the ability of liposomes prepared with PGMA to be internalized by different cell lines in vitro, using flow cytometry. Cellular internalization is critical for most drug delivery systems to deliver their drug content to cells. In this experiment, the liposomes were fluorescently labeled by the encapsulation of DiD (1,1-Dioctadecyl-3,3,3,3-Tetramethylindodicarbocyanine, 4-Chlorobenzenesulfonate Salt) (?ex/em: 655/675). The list of cells tested includes RAW 264.7 mouse macrophage-like lymphoma, primary dendritic cells derived from mouse, A20 mouse B cell lymphoma, U87-MG human glioblastoma cells and A549 human lung adenocarcinoma cell lines.
[0114] Macrophages are specialized phagocytic cells found in every tissue of the body. Here we used RAW 264.7 cells that are monocyte/macrophage-like murine cancer cells generated through exposition to the Abelson murine leukemia virus. Due to their phagocytic properties, the cellular uptake of both control (liposome HSPC) and PMGA-liposomes is higher in this cell line (
[0115] Murine primary dendritic cells were obtained by differentiation of mesenchymal stem cells, cellular uptake was performed 8 days after harvesting. In this cell line, the cellular uptake of PMGA-DODA containing liposomes is >20-fold higher than the control formulation (
[0116] We also investigated the uptake of PMGA-DODA liposomes in cancerous B cells (A-20), as a model for another type of immune cells. Although this cell line has decreased internalization capacities, compared to primary B cells obtained from the spleen of mice (data not shown), the difference in cellular internalization between liposomes with PMGA-DODA and their control is mostly visible at high concentrations (
Animal Study, Profile of Pharmacokinetic and Biodistribution
[0117] The impact of CTA-PGMA-DODA and PMGA-DODA on the circulation profile of radiolabeled [.sup.14C]-liposomes was studied in healthy Balb/c mice. In this study, the concentrations of radiolabeled liposomes in the blood were monitored for 6 hours after intravenous injection. The results of the experiment are presented in
Transfection of mRNA
[0118] mRNA-based therapeutics hold a great future for new drug candidates. Hence, we tested whether PMGA could be used to prepare mRNA containing LNP. Using the ionizable lipid SM-102 and mRNA encoding for the green fluorescent protein (EGFP), we prepared LNPs. The composition of the LNP comprises: SM-102 as an ionizable cationic lipid, hydrogenated soybean phosphatidylcholine (HSPC) as helper, cholesterol for fluidity and either DMG-PEG or PMGA-DODA as steric and size self-assembled stabilizer (molar ratios respectively of 50:10:38.5:1.5 mol %). LNP with DMG-PEG were formulated as a control. Physicochemical analysis of the formulations showed that replacement of DMG-PEG with PMGA-DODA did not significantly impact the size of the LNPs or their efficiency of mRNA encapsulation (Table 6, Example 7). This confirms that PMGA-DODA can be used to prepare mRNA-containing LNPs comparable to the state-of-the-art.
[0119] As a proof of concept, we tested the ability of PMGA-DODA LNPs to transfect HEK293 cells with EGFP. This cell line was chosen for its documented ease of transfection.
Cytotoxicity
[0120] We evaluated the cytotoxicity of PMGA-DODA in comparison to DSPE-PEG, a polymer-lipid already approved by the US-FDA as part of multiple drug products. Using the MTT assay (colorimetric assay for assessing cell metabolic activity), we compared the viability of a cell line exposed to increasing concentrations of the amphiphilic polymers, as well as liposomes containing PGMA or not. Reduction of the MTT reagent result in a disruption of the tetrazole ring and the formation of a violet-blue water insoluble molecule called formazan. The chromogenic nature of this redox chemical reaction provides a colorimetric based assay to measure the intracellular formation of this formazan when the cells are still alive. Cytotoxicity of liposomes and free polymer were studied on macrophages (RAW 264.7) incubated for 72 hours with concentration up to 20 ?g/mL. The results showed that cell viability decreases with increase of material, as anticipated (
Compositions, Formulations and Medical Uses
[0121] The polymers of the present description can be used to prepare lipid particles (PMGA based lipid particles), liposomes (PMGA based liposomes), polymeric nanoparticles (PMGA-based polymeric nanoparticles) or lipid nanoparticles (PMGA based nanoparticles) for use in the delivery of bioactive agents including nucleic acids (such as mRNA (messenger RNA), siRNA (small interfering RNA), shRNA (shorth harpin RNA), microRNA, gRNA (guide RNA)), small molecules, drugs, and proteins in vivo. PMGA based lipid particles include lipid nanoparticles, liposomes and lipid nanocapsules prepared with PMGA based polymers of the present description. PMGA based lipid particles and PMGA based polymer nanoparticles may include other lipids or polymers such as pegylated lipids or biodegradable polymers which are well known in the art.
[0122] In one aspect, the bioactive agent can be a therapeutic mRNA, which may code for a therapeutic protein. The mRNA may also be a mRNA encoding a vaccine antigen. In some instances, the mRNA may encode multiple proteins.
[0123] In one aspect, a lipid nanoparticle or liposome encapsulating an mRNA encoding a protein of interest (e.g., a therapeutic protein or a vaccine antigen) is provided in some aspects of the invention.
[0124] In certain embodiments, the lipid particle formulation comprises a cationic lipid, a non-cationic lipid (e.g., a phospholipid or fatty acid) and a structural lipid. In certain embodiments, the lipid nanoparticle formulation comprises a cationic lipid, a non-cationic lipid (e.g., phospholipid or fatty acid), a structural lipid, and an ionizable lipid.
[0125] In one aspect, lipid nanoparticle may be formulated using microfluidics technology such as NanoAssemblr Spark?. In one embodiment, the lipid nanoparticles may have a diameter from about 50 to 500 nm, from about 60 to about 500 nm, about 60 to about 400 nm, about 60 to about 300 nm, about 60 to about 200 nm, about 60 to about 100 nm, about 70 to about 100 nm, about 80 to about 100 nm, about 90 to about 120 nm and/or about 100 to about 200 nm.
[0126] In one aspect, liposomes are prepared using the thin film hydration method also known as the Bangham method. In one embodiment, the liposome may have a diameter may have a diameter from about 50 to 500 nm, from about 60 to about 500 nm, about 60 to about 400 nm, about 60 to about 300 nm, about 60 to about 200 nm, about 60 to about 100 nm, about 70 to about 100 nm, about 80 to about 100 nm, about 90 to about 120 nm and/or about 100 to about 200 nm.
[0127] In one embodiment the PMGA polymers can assemble in nanoparticles to form polymeric nanoparticles. Methods for preparing polymeric nanoparticles from polymers include emulsion-solvent evaporation, double emulsion and evaporation, emulsions-diffusion, solvent displacement, salting out and dialysis.
[0128] Compositions incorporating PMGA based lipid particles can include pharmaceutically acceptable carrier, diluent, or excipient. The expression pharmaceutically acceptable carrier, diluent, or excipient and equivalent expressions, refer to a non-toxic carrier, diluent, or excipient that does not destroy the pharmacological activity of the compound or lipid nanoparticle with which it is formulated.
[0129] Compositions described herein may be administered orally, parenterally, by inhalation spray, topically, rectally, nasally, buccally, or via an implanted reservoir. The term parenteral as used herein includes subcutaneous, intravenous, intramuscular, intraarticular, intrasynovial, intrasternal, intrathecal, intrahepatic, and intralesional injection or infusion techniques. Other modes of administration also include intradermal or transdermal administration.
[0130] Injectable preparations, for example, sterile injectable aqueous or oleaginous suspensions may be formulated according to the known art using suitable dispersing or wetting agents and suspending agents. The sterile injectable preparation may also be a sterile injectable solution, suspension or emulsion in a nontoxic parenterally acceptable diluent or solvent, for example, as a solution in 1,3-butanediol. Among the acceptable vehicles and solvents that may be employed are water, Ringer's solution, U.S.P. and isotonic sodium chloride solution. In addition, sterile, fixed oils are conventionally employed as a solvent or suspending medium. For this purpose, any bland fixed oil can be employed including synthetic mono- or diglycerides. In addition, fatty acids such as oleic acid are used in the preparation of injectables.
[0131] Injectable formulations can be sterilized, for example, by filtration through a bacterial -retaining filter, or by incorporating sterilizing agents in the form of sterile solid compositions which can be dissolved or dispersed in sterile water or other sterile injectable medium prior to use.
[0132] The amount of compound that may be combined with carrier materials to produce a composition in a single dosage form will vary depending upon the patient to be treated and the particular mode of administration.
[0133] As used herein, the term effective amount means that amount of a compound that will elicit the biological or medical response of a tissue, system, animal or human that is being sought, for instance, by a researcher or clinician. Furthermore, the term therapeutically effective amount means any amount which, as compared to a corresponding subject who has not received such amount, results in treatment, healing, prevention, or amelioration of a disease, disorder, or symptom thereof, or a decrease in the rate of advancement of a disease or disorder. The term also includes within its scope amounts effective to enhance normal physiological function.
[0134] As used herein, the terms treatment, treat, and treating refer to reversing, alleviating, delaying the onset of, or inhibiting the progress of a disease or disorder, or one or more symptoms thereof, as described herein. In some embodiments, treatment may be administered after one or more symptoms have developed. In other embodiments, treatment may be administered in the absence of symptoms. For example, treatment may be administered to a susceptible individual prior to the onset of symptoms (e.g., in light of a history of symptoms and/or in light of genetic or other susceptibility factors). Treatment may also be continued after symptoms have resolved, for example to prevent or delay their recurrence.
[0135] As used herein, the term vaccine refers a therapeutic of preventive treatment of a disease or disorder. In some embodiments, a vaccine capable of eliciting an immune response in a subject or patient may be administered as a prophylaxis to prevent an infection by an infectious agent such as a virus. Vaccines include preparations that are capable of providing immunity against one or more conditions related to infectious diseases such as influenza, coronavirus (e.g., SARS COV-2 and variants), measles, human papillomavirus, rabies, meningitis, whooping cough, tetanus, plague, hepatitis, and tuberculosis and can include mRNAs encoding infectious disease derived antigens and/or epitopes. Vaccines also include preparations that direct an immune response against cancer cells and can include mRNAs encoding tumor cell derived antigen and/or epitopes. In some embodiments, a vaccine capable of eliciting an immune response can be administered intramuscularly via a composition including a PMGA based polymers as defined herein.
[0136] The term patient or subject as used herein refers to an animal such as a mammal. A subject may therefore refer to, for example, mice, rats, dogs, cats, horses, cows, pigs, guinea pigs, primates including humans and the like. Preferably the subject is a human.
[0137] It will be understood that the total daily dose of the compound will be decided by the attending physician within the scope of sound medical judgment. For instance, a specific dosage or treatment regimen for any particular patient will depend upon a variety of factors, including age, body weight, general health, sex, diet, time of administration, rate of excretion, drug combination, the judgment of the treating physician, and the severity of the symptoms associated with the disease or disorder.
EXAMPLES
[0138] The following non-limiting examples are illustrative embodiments and should not be construed as further limiting the scope of the present invention. These examples will be better understood with reference to the accompanying figures. The polymers used or described in the present may be prepared by conventional chemical synthesis such as those described in the Examples section below. Additionally, the various synthetic steps may be performed in an alternate sequence or order to give the desired compounds.
[0139] Unless otherwise indicated, all numbers expressing quantities of ingredients, reaction conditions, concentrations, properties, stabilities, and so forth used in the specification and claims are to be understood as being modified in all instances by the term about. At the very least, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques. Accordingly, unless indicated to the contrary, the numerical parameters set forth in the present specification and attached claims are approximations that may vary depending upon the properties sought to be obtained. Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the embodiments are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contain certain errors resulting from variations in experiments, testing measurements, statistical analyses and such.
Example 1-Preparation of Starting Materials
(i) Preparation of DODA-CTA
[0140] ##STR00007##
[0141] The alkyled transfer agent was prepared according to the following procedure: 1.5895 g (3.33 mmol) of 4-cyano-[4(dodedyl sulfanyl thiocarbonyl) sulfanyl] pentanoic acid (CTA), 2.5692 g (4.92 mmol, 1.25 eq) of dioctadecylamine (DODA), 1.0151 g (4.92 mmol, 1.25 eq) of dicyclohexylcarbodiimide (DCC), 686 ?L (0.5 g, 3.93 mmol) of diisoproprylethylamine (DIPEA) in 40 mL of chloroform were reacted together overnight under an inert atmosphere. To confirm completion of the reaction, thin-layer chromatography was used with a mobile phase of 2:1 hexane/ethyl acetate (EtAc) and revealed with ninhydrin solution (200 mg of ninhydrin in 100 mL ethanol). At the end of the reaction, chloroform was evaporated to dryness under reduced pressure on a rotary evaporator, solubilised in a small quantity of a 2:1 v/v mixture of hexane and EtAc, and purified by silica gel chromatography. The product was identified by thin layer chromatography and all fractions containing DODA-CTA were pooled together. Evaporation of the solvent afforded an orange/brown viscous liquid. Finally, the product was solubilised in a small quantity of chloroform and precipitated in acetonitrile. The structure was confirmed (
(ii) Preparation of Solketal Acrylate (SKA)
[0142] ##STR00008##
[0143] The synthesis of SKA was achieved according to the following the procedure: at room temperature, triethylamine (40 mL, 0.29 mol) was added slowly to a mixture of solketal and acryloyl chloride (20 mL, 0.25 mol) in dichloromethane (200 mL). The round bottom flask was kept in an ice bath, during the addition of triethylamine. The reaction was left to stir for 6 hours at room temperature. The salt of triethylamine hydrochloride was filtered under vacuum and washed twice with 20 mL of dichloromethane. The filtrate was then washed thrice with a saturated aqueous solution of NaHCO.sub.3 to remove all the triethylamine. The organic layer was dried over anhydrous MgSO.sub.4 and the solvent was evaporated under reduced pressure to give an orange product (
(iii) Preparation of Monomer Glycerol Acrylate
##STR00009##
[0144] The deprotection of the acetal group of solketal acrylate was conducted according the following procedure: 1,589 g of Amberlyst 15? resin was hydrated by gentle stirring in 7 mL of methanol during 30 minutes. The methanol was removed by filtration and 80 mL of a methanol solution of solketal acrylate (7.8 g, 41.9 mmol) was added to the resin and stirred for 2 hours at room temperature. The reaction was filtered and washed with 30 mL of methanol and the solvent was removed by evaporation under reduced pressure to yield a brownish product. To remove impurities and unreacted material, the crude monoglycerol acrylate was dissolved in 10 mL of ultrapure water. The solution was extracted with 100 mL of chloroform and purified on a small alumina column (in a small glass pasteur pipette). .sup.1H NMR (D.sub.2O, 400 MHz) : 6 3.65 (2H, t, J=5 Hz, CH.sub.2OH), 4.0 (1H, d, J=5 Hz, CHOH), 4.15-4.4 (2H, dd, J=4-6 Hz, OCH.sub.2CH-), 6.0 (1H, d, J=10 Hz, CH.sub.2=CH-), 6.25 (1H, dd, J=10 Hz, CHC(?O)-), 6.5 (1H, d, J=17 Hz, CH.sub.2?CH-). (
Example 2Preparation of Monoglycerol Acrylate Based-Polymers
[0145] ##STR00010##
(i) Preparation of CTA-PMGA-DODA2k for n=10 (M=2,000 g/mol)
[0146] Quantities are given for the synthesis of 1 g of polymer.
[0147] Reagents: 825 mg of monoglycerol acrylate (MGA), 312.2 mg of DODA-CTA and 5.6 mg of Al BN (molar ratio of MGA/DODA-CTA=1.2?10).
[0148] Solvents: 2.4 mL of methanol and 5.6 mL of dioxane.
[0149] Preparation method: the polymer CTA-PMGA-DODA2k was synthesized following the procedure described in (ii).
(ii) Preparation of CTA-PMGA-DODA6.5k for n=45 (M=6,500 g/moh
[0150] A typical procedure of polymerisation is the reversible addition-fragmentation chain transfer (RAFT) method. In a typical reaction to obtain a molecular weight of 6500 g/mol, 222 ?L of a 10 mg/mL solution of azobisisobutyronitrile (AIBN) was added to MGA (1.053 g, 7.312 mmol) and DODA-CTA (122.6 mg, 0.135 mmol) in 9.1 mL of 1,4-dioxane and 3.1 mL of methanol. The solution was degassed by bubbling nitrogen for 15 minutes before initiating the reaction. The reaction was polymerised at 70? C. for 72 hours under stirring. The polymer was precipitated in a conical centrifuge tube (50 mL) of diethyl ether and freeze-dried. .sup.1H NMR (CDCl.sub.3/MeOD-d6, 400 MHz): ? 0.85 ppm (9H, t, CH.sub.3), 1.20 (84H, m, alkyl chain), 1.50 (2H,s, S[CH.sub.2CH]-), 2.20-2.30 (1H, s, [CH.sub.2CH]-), 3.30 (2H, s, CH.sub.2OH), 3.65 (1H, s, CHOH), 3.80-4.0 (2H, s, OCH.sub.2CH-). (
(iii) Preparation of CTA-PMGA-DODA10k for n=80 (M=10,000 g/mol)
[0151] Quantities are given for the synthesis of 1 g of polymer.
[0152] Reagents: 1116 mg of monoglycerol acrylate (MGA), 70.3 mg of DODA-CTA and 1.3 mg of AIBN (molar ratio of MGA/DODA-CTA=1.2?80).
[0153] Solvents: 4 mL of methanol and 8 mL of dioxane.
[0154] Preparation method: the polymer CTA-PMGA-DODA10k was synthesized following the procedure described in (ii).
(iv) Deprotection of CTA-PMGA-DODA to Give the DODA-Terminated Poly(Monoglycerol Acrylate) or PMGA-DODA
[0155] ##STR00011##
[0156] The removal of thiocarbonylthio end groups by radical-addition-fragmentation was conducted as follows: [PMGA]:[AIBN]:[Lauroyl peroxide, LPO]=1:20:2. The reaction was reacted for 4 hours at 80? C. and precipitated in diethyl ether. The polydispersity index and change in molecular weight were determined by GPC (Table 1, Example 3).
Example 3Preparation and Characterization of the Liposomes
[0157] (i) Preparation of the liposomes
[0158] The liposomes were prepared by the hydration of lipid film followed by extrusion through polycarbonate membranes as follows: 40 mg/mL solutions of HSPC and cholesterol were prepared in 3:1 chloroform/methanol and stored at ?20? C. until further use. The alkylated polymer solution was prepared at 20 mg/mL in methanol. In a round bottom flask, each of these solutions were added (693 ?L for HSPC, 234 ?L for cholesterol and 210 ?L for PMGA-DODA or CTA-PMGA-DODA (both for polymer with n=45; M=6,500 g/mol), which corresponds to 1.4?10.sup.?6 mol) and the solvent was evaporated under reduced pressure for 1 hour at 50? C. The lipid film was hydrated with 600 ?L of a HEPES saline buffer pH=7.4 (HEPES 20 mmol/L, 144 mmol/L NaCl) or 10 mM of HEPES buffer with 35 mM of 8-Hydroxypyrene-1,3,6-trisulfonic acid trisodium salt (HPTS) and 50 mM of p-xylene-bis-pyridinium bromide (DPX) pH=7.4 and sonicated for 1 hour. The HPTS/DPX buffer was used to prepare liposomes with quenched fluorescence for experiments studying the impact of osmotic shock. The solution was vortexed and hydrated at 4? C. for 24 hours. The suspension was then extruded while heating through 400-200-100-50 nm polycarbonate membranes (Whatman Nuclepore track-etched) using a LiposoFast manual extruder (Avestin). The size and polydispersity index (PDI) were confirmed by dynamic light scattering (DLS) using a Malvern Zetasizer Nano S (Malvern Instruments), at 22? C. with a 173?-backscatter angle. The phosphorous content was determined by a Bartlett phosphorous colorimetric assay, as described in detail elsewhere (Food Chemistry 2020, 126736 and The Journal of biological chemistry 1959, 234 (3), 466-468). Standard curve was prepared with potassium phosphate (K.sub.3PO.sub.4, dried overnight in an oven) in water at a range from 0 to 32 mM. Liposomes radiolabelled for the animal studies were prepared following the same procedure, but with smaller quantities: 23.1 ?L of HSPC (40 mg/mL in chloroform), 7.8 ?L of cholesterol (40 mg/mL in chloroform) and 20 ?L of 14 C-Cholesteryl oleate (0.1 ?Ci/?L) was added to the round bottom flask for the control liposome. Liposomes with CTA-PMGA-DODA also contained 14 ?L (20 mg/mL in methanol) of the alkylated polymer. The same recipes were used for in vitro study but with a small quantity of 1,1-Dioctadecyl-3,3,3,3-tetramethylindodiocarbocyanine perchlorate (DID, 0.065 mg). For the liposome control 12 ?L of DSPE-PEG (20 mg/mL in CHCl.sub.3) was added to the rest of the formulation.
TABLE-US-00001 TABLE 1 Size and polydispersity index of all the formulations used for the different experiments. Size Polydispersity Formulation (nm) index (PDI) Polymer CTA-PMGA-DODA.sub.6.5k 110.5 0.218 Polymer PMGA-DODA.sub.6.5k 105.4 0.265 Control liposome (HSPC/Cholesterol) 104.6 0.054 Liposome CTA-PMGA-DODA.sub.6.5k 120.4 0.118 Liposome PMGA-DODA.sub.6.5k 123.8 0.097 Polymer PMGA-DODA.sub.6.5k FITC-Cadaverine 102.9 0.055 Liposome PMGA-DODA.sub.6.5k FITC-Cadaverine 113 0.082
(ii) Purification of the Liposomes
[0159] All the formulations of liposomes were purified by size exclusion chromatography. The void volume of the column (1?20 cm) was determined to use a control liposome with HSPC/Cholesterol (ca. 4.5 mL). Fraction containing liposomes was identified by adding 10?L of a methanol solution of Nile red (1?10.sup.?5 M) as a hydrophobic dye since its fluorescence is well-known to be negligible in aqueous medium and instantly increase in hydrophobic environment found in membrane such as bilayer. Aliquot (100 ?L) of each fraction was used to measure the fluorescence ((?ex/em: 549/628 nm).
Example 4Properties of the Liposomes (with Polymer with n=45; M=6,500 g/mol)
[0160] (i) Stability of the Polymer into the BilayerSynthesis of a Fluorescent Polymer as a Tracking Device
##STR00012##
[0161] A fluorescent molecule was attached to the polymer as a label. 1% mol of acrylic acid was added to the RAFT reaction in order to get a carboxylic function where a terminal amine can be conjugated by peptide crosslinking.
##STR00013##
[0162] The procedure was conducted as follows: 100 mg of the alkylated polymer (PMGA-DODA with 1% of acrylic acid) was dissolved in 2 mL of carbonate buffer 0.1M pH=10.5 (sodium bicarbonate 12.5 mmol/L, sodium carbonate anhydrous 87.5 mmol/L). Then, 5 mg of 1-Ethyl-3-(3-dimethylaminopropryl)carbodiimide (EDC) and 1.725 mg of fluorescein cadaverine (2.40 ?mol) was added to the mixture and left under stirring overnight. The polymer was dialyzed against water for 24 hours using a 3500 MWCO regenerated cellulose membrane (Spectra/Pore 3 dialysis membrane, RC trial kit), and the unreacted dye was further removed by purification on a Sephadex? G-75 column (20?1 cm).
##STR00014##
(ii) Critical Micellar Concentration (CMC)
[0163] Nile red can be used to measure the CMC of surfactants and polymolecular architectures by following the fluorescence of the dye: the critical micelle concentration coincides with a strong increase in the intensity of the fluorescence (?.sub.ex/em: 549/628 nm). Serial dilutions of polymers were made in the range of 2.5 to 7?10.sup.?4 mg/mL. 200 ?L of each sample were used with 10 ?L of Nile Red solution in methanol (1?10.sup.?5 M). Fluorescence was read in a 96-well plate (?.sub.ex/em: 549/628 nm).
TABLE-US-00002 TABLE 2 Critical micelle concentration of the polymer DODA-PMGA compared to commercial products such has sodium dodecyl sulfate (SDS) CTA-PMGA- PMGA- Compound DSPE-PEG SDS DODA.sub.6.5k DODA.sub.6.5k CMC (mg/mL) 0.11 2 0.018 0.42
(iii) Polymer Incorporation into the Lipid Bilayer (for Polymer with n=45; M=6,500 g/mol)
[0164] Dialysis of the fluorescent liposome was performed as follows: 400 ?L of the liposome formulation was dissolved in 8 mL of HEPES 1X buffer. The polymer solution (210 ?L) was hydrated and extruded as per the liposome formulation protocol, but without lipids and cholesterol. Then again 400 ?L of this solution was dissolved in 8 mL of the buffer. 2.8 mL of the stock solution was placed in a 5-cm dialysis bag with a MWCO of 100 KDa (Spectrum? labs, biotech, CE, dialysis kit, #08-700-131). The polymer and the liposome were dialyzed under gentle stirring against a solution of 0.9% NaCl for 120 hours, samples were collected inside the dialysis bag. The sample was protected from light during all the dialysis experiment. To ensure sink conditions, the dialysate was changed at each time point. The starting lipid concentration for the liposome was around 0.54 mM, determined by the phosphorous colorimetric assay.
(iv) Stability of the Liposomes
[0165] In order to understand if the incorporation of the CTA-PMGA-DODA (for polymer with n=45; M=6,500 g/mol) to liposomes can affect their stability in different conditions, we used a water-soluble fluorescent dye (HPTS) and encapsulated it with a proximity quencher (DPX) inside the aqueous cavity of the liposome. This system allows to monitor the disruption of the vesicles by a strong increase in fluorescence when the dye and the quencher are released in the surrounding environment. Liposomes hydrated with HEPES solution containing HPTS/DPX were purified by SEC on a 1?20 cm gravity flow column pack with Sephadex? G-25. Then, 10 ?L of the purified liposomes suspensions were added to 1 mL of buffer, either HEPES pH=7.4 or 0.1 M citrate buffer pH=5.2 (0.063 M sodium citrate dihydrate and 0.037 M citric acid). The buffer with liposomes was incubated for 1 hour at 37? C. and 60? C. and the fluorescence was measured every 15 minutes. Triton X 20% (v/v) was added at the end (after 60 minutes) to measure the disruption of the liposome, resulting in the complete release of the dye (?.sub.ex/em: 413/512 nm).
(v) Cytotoxicity of the PMGA-liposome (for polymer with n=45; M=6,500 g/mol)
[0166] To measure the toxicity of the polymer we used MTT assays as follows: murine macrophage cells (RAW 264.7) were seeded at a concentration of 50 000 cells/wells in DMEM media with sodium pyruvate, 10% fetal bovine serum (FBS) and an antibiotic. The cells were incubated 24 hours at 37? C. with 5% CO.sub.2 before further use. Liposome and free polymer solution were prepared in range of 0-20 ?g quantity of material. 100 ?L were added to the cell and left for 72 hours in the incubator. In the meantime, a solution of 3-(4,5-dimethylthiazoyl-2-yl)-2,5-diphenyl tetrazolium bromide salt (MTT) at a concentration of 5 mg/mL in sterile PBS was prepared. After incubation, 10 ?L of the MTT solution was added in each well and incubated for 4 hours. The media was removed and replaced by 100 ?L of dimethyl sulfoxide (DMSO). The absorbance was read at ?=570 nm.
Example 5In vitro Study
[0167]
TABLE-US-00003 TABLE 3 Dynamic light scattering (DLS) size for all the formulation use for in vitro work Size Name (nm) PD Control liposome for RAW 264.7 120.9 0.212 PMGA-DODA.sub.6.5k liposome for RAW 264.7 116.4 0.237 Control liposome for RAW 264.7 + GalNAc 123.4 0.238 PMGA-DODA.sub.6.5k liposome for RAW 264.7 + GalNAc 120.2 0.124 Control liposome for RAW 264.7 + Mannan 113.6 0.246 PMGA-DODA.sub.6.5k liposome for RAW 264.7 + Mannan 110.4 0.186 Control liposome A20 124.9 0.187 PMGA-DODA.sub.6.5k liposome A20 110.3 0.234 Control liposome dendritic cells 108.8 0.260 PMGA-DODA.sub.6.5k liposome dendritic cells 121.9 0.189 Control liposome MTT assay 115.9 0.199 PMGA-DODA.sub.6.5k liposome MTT assay 114.9 0.076 Control liposome U87 126.9 0.215 PMGA-DODA.sub.6.5k liposome U87 116.1 0.133 Control liposome A549 117.2 0.367 PMGA-DODA.sub.6.5k liposome A549 125.4 0.132 DSPE-PEG liposome A549 125.7 0.252
(i) Internalization with Macrophages Cells RAW 264.7
[0168] Uptake in different cells line: the liposomes were all formulated as previously described with DID as a fluorophore reference for flow cytometry analysis. First, we use murine macrophages cells (RAW 264.7). About 550 000 cells were plated in each wells the night before with DMEM medium containing 10% FBS and an antibiotic. Solution of 0.1 and 0.025 mg/mL of liposomes were prepared. 10 ?L of each solution was added into the wells and incubated for 2 hours. The cells were suspended by up and down pipetting, and the suspension was washed with PBS. Before Flow cytometry reading, the cells suspensions where centrifuged at 300 g for 5 minutes at 4? C., the medium were aspirated, and the cell pellets where resuspended 2 times in FACS buffer (2% FBS with 1 mM EDTA in PBS). Flow cytometry experiment (fluorescence-assisted cell sorting, FACS) was conducted on a BD LSRII (BD Biosciences) and the data were analyzed using the FlowJo V10 software (Tree Star Inc., BD) with the 640 nm laser (660/20 filter).
(ii) Internalization in Dendritic Cells
[0169] Primary mouse dendritic cells differentiated from bone narrow were seeded at a concentration of 200 000 cells/wells with DMEM medium (10% FBS and antibiotic). 10 ?L of 0.1, 0.2, 0.5 and 1 mg/mL were added to the cells and incubated for 2 hours. The same process for cytometry analysis was used.
(iii) Internalization in B Cells
[0170] The same protocol was used to assess the internalization in B-cells derived from lymphoma old BALB/c mouse (A-20) with 500 000 cells/wells. The cell culture media was RPMI with glutamine and 10% FBS. The concentration of the solutions used were 0.5, 0.1 and 0.05 mg/mL. For adherent cells trypsin solution of 2.5% is required to detach the cells from the plate. 100 ?L of the trypsin solution is added to the plate after washing the cells with PBS and incubated for 3-5 minutes at 37? C. Then a volume minimum of fresh media 5 times the trypsin is added to the plate before further washing and flow cytometry analysis. Experiments were also conducted on a glioblastoma cell line (U87-MG) and adenocarcinoma cells derived from primary lung tumors (A549) where 250 000 cells were plate in each well in EMEM medium (with Earle's salt, glutamine, 10% FBS and antibiotic) and DMEM respectively. The concentration of liposome used were 0.01 and 0.1 mg/mL for U87-MG, and 0.05, 0.1 and 0.5 mg/mL for A549 cells. 10 ?L of each solution was added into the wells and the cells were incubated 2 hours and 4 hours respectively. Those cell lines are also adherent, which required the use of trypsin has mentioned before. The rest of the protocol was done has previously described.
Example 6In vivo Pharmacokinetics
[0171] All animal studies were conducted using approved protocols from Universite Laval (Canadian Council on Animal Care standards and Animal Research: Reporting In Vivo Experiments Guidelines). Pharmacokinetic was carried according to method already published by our laboratory (Journal of Controlled Release 2018, 287, 121-131). Healthy animals were housed in a controlled environment (22? C., 12 hours day/night cycle) with ad libitum access to food and water. A total of 11 healthy male mice were divided in three groups (3-3-5). As a blank, liposomes without polymer on the surface were injected intravenously by the subclavian vein at a concentration of 2 mg/kg of phospholipids. Approximately 30-50 ?L of blood was collected at various times (0.25, 0.5, 1, 2 ,4, 6 Hours). Six hours post-injection, blood was collected by cardiac puncture for a terminal timepoint. Animals were euthanized by a cardiac perfusion with 3 mL of isotonic phosphate-buffered saline solution pH=7.2 (potassium phosphate 1.1 mmol/L, NaCl 150 mmol/L, disodium phosphate 3 mmol/L) and organs were collected. Biological samples were digested at 58? C. (in Solvable?, Perkin Elmer?), bleached with 30% hydrogen peroxide, and assessed by scintillation counting, using Hionic Fluor? (Perkin Elmer?) as a scintillation cocktail.
TABLE-US-00004 TABLE 4 Size and zeta potential of all liposome formulations used for in vivo study Zeta Size potential Name (nm) PD (mV) Control liposome HSPC/Cholesterol 100.3 0.075 ?14.0 Liposome CTA-PMGA-DODA.sub.6.5k 122.6 0.142 ?5.65 Liposome PMGA-DODA.sub.6.5k 106 0.075 ?3.82
[0172] In order to analyse the cellular distribution into the spleen and the lymph node, control or PMGA liposomes (2 mg/kg) were injected into balb/c mice by subcutaneous hock injection. The spleen and the popliteal lymph node were collected 24 hours post-injection and placed in cold PBS with 2 vol % fetal bovine serum (FBS). Cellular suspension was prepared by mechanically disrupted the organs on a 40 ?m cell strainer into a 6 wells plate containing 2 ml of PBS with 2% FBS on ice. Filtered cells were washed twice by centrifugation in 2 vol % FBS in PBS and counted on a hemocytometer. Erythrocytes were lysed by suspending the cells in Lysing Buffer (BD Biosciences) for 5 minutes. Then Saline buffer (PBS) were added and centrifuge. Cell suspensions of 5?10.sup.6 cells/ml were labelled with antibodies mix and FC block (ThermoFisher). The panel of fluorophores and the reference numbers for antibodies are listed in Supplementary info. Control animals that had not received liposome were used to determine the background, and the positive signal for DiD fluorophore.
TABLE-US-00005 TABLE 5 Biodistribution profile in the organs after i.v injection (2 mg/kg), n represents the number of mice. % ID per gram of blood Liposome Liposome Control CTA-PMGA- PMGA- liposome DODA.sub.6.5k DODA.sub.6.5k Time (h) (n = 6) (n = 5) (n = 5) 0.25 25 ? 5 17 ? 2 17 ? 2 0.5 20 ? 5 12 ? 1 13 ? 1 1 16 ? 2 9 ? 2 11 ? 2 2 14 ? 3 8 ? 1 12 ? 2 4 12 ? 1 9 ? 1 11 ? 2 6 7 ? 1 8 ? 1 10 ? 1 AUC (% ID h .Math. g.sup.?1) 81 ? 11 54 ? 7 68 ? 9 Kel (h.sup.?1) 0.38 ? 0.04 0.37 ? 0.07 0.31 ? 0.05
Example 7Preparation of LNP with mRNA
[0173] mRNA-containing lipid nanoparticles were formulated using the Spark? Nanoassemblr (Precision Nanosystem). Ethanol solutions of the lipids (50 mM, 50 mol % SM-102, 10 mol % HSPC, 38.5 mol % Cholesterol and 1.5 mol % of PMGA-DODA (for polymer with n=45; M=6,500 g/mol)) were prepared, as well as a 0.464 mg/mL solution of GFP-encoding mRNA (Trilink) in 0.1M RNase free acetate buffer (pH=4, 0.02269 M sodium acetate, 0.07731M acetic acid). The mRNA concentration in the solution was assessed by UV-spectrophotometry (NanoDrop? spectrophotometers, ThermoFisher). Each batch of nanoparticles was prepared using 12 ?L of the lipid mix, and 24 ?L of the mRNA solution (N/P=6). As per the Precision Nanosystem's protocol, these solutions were rapidly mixed and diluted in 36 ?L of sterile PBS without Ca.sup.2+ and Mg.sup.2+. After formulation, the LNPs were further diluted in 72 ?L of PBS. The efficacy of encapsulation was measured using the ribogreen assay (Invitrogen, Quant-it?, Ribogreen ARN assay kit, ThermoFisher #R11490). The LNP were diluted into 1X TE buffer (10 mmol/L Tris, 1 mmol/L EDTA) or 2% Triton buffer in TE solution. A calibration curve in TE buffer was set up using RNA stock solution prepared at 0.464 mg/mL (range between 2.5 and 0.1 ug/mL final concentration) to allow the quantification of free mRNA in the sample. The plate was incubated at 37? C. for 10 minutes to lyse the RNA-LNP in presence of Triton. 100 ?L of the Ribogreen solution (1:100 Rigogreen reagent: TE buffer) was added in each well and the fluorescence was measured (?ex/em: 485/528 nm) with Spectramax 13 (Molecular devices). The mRNA encapsulated was calculated by substracting the free mRNA to the LNP associated and comparing it to the calibration curve. The size of the LNP was confirmed by DLS (
TABLE-US-00006 TABLE 6 Size and efficiency of mRNA encapsulation for LNP LNP Size (nm) PD Encapsulation (%) DMG-PEG 147 0.306 92.4 PMGA-DODA.sub.6.5k 171.6 0.129 96.7
Example 8Transfection
[0174] The human embryonic kidney immortalized cells (HEK293) were plate the day before the experiment at a concentration of 125 000 cells/wells. The DMEM media was replaced with reduced serum media the day of the transfection, such has optiMEM? (Gibco, #31985062). The LNP were diluted to 40,100 and 1000X and 20 pL of each solution were add to the cells and incubated for 24 hours at 37? C. with 5% CO.sub.2. After transfection, the cells were trypsined has previously described and wash 2 times with FACS buffer. The transfection was analyzed by flow cytometry using the 488 nm laser (525/25 filter).
Example 9Drug Loading
[0175] Liposomes with or without PMGA were prepared by the hydration of a lipid film with 100 mM citrate buffer (pH 4), followed by extrusion on polycarbonate membranes. The control and PMGA-containing formulations contained HSPC/Cholesterol at a 60:40 mol %, and HSPC/Cholesterol/PMGA at a 58:40:2 mol %, respectively. After hydration, formulations were extruded on polycarbonate membranes with pores ranging from 400-50 nm, to afford vesicles with hydrodynamic diameters between 90-130 nm. A transmembrane pH gradient was generated by exchanging the outside buffer with isotonic hepes buffer saline (HBS, pH 7.4, 22 mM HEPES, 147 mM NaCl) on a Sephadex G-25 column (1?20 cm). (Transmembrane pH-gradient liposomes to treat cardiovascular drug intoxication, ACS Nano., 2010, 4, 7552). The concentration in liposomes was measured by the phosphate assay (Drinkable lecithin nanovesicles to study the biological effects of individual hydrophobic macronutrients and food preferences, Food Chem., 2020, 322, 126736).
[0176] To load doxorubicin, a solution of doxorubicin HCl (5 mg/mL) was incubated with liposomes (HSPC liposomes: 0.0031 mmol/mL of phospholipid and HSPC-PMGA liposomes: 0.0024 mmol/mL) at a volume ratio of 0.3:1, for 18 hours at 37? C. The non-encapsulated doxorubicin was removed by size exclusion chromatography. The liposomes concentration was evaluated by the phosphate assay as above, and the doxorubicin concentration was measured by reverse-phase high performance chromatography (C18 4.6?100 mm, with a gradient of pH 5 citric acid buffer and methanol). The doxorubicin (Retention time 4.37 min) was detected by UV absorbance (480 nm) and fluorescence spectroscopy (?ex/Em: 480/490 nm). For both formulations, the process resulted in a drug loading of 14 wt %, showing that incorporation of PMGA in the liposome membrane does not compromise the remote loading of weakly basic molecules within the vesicles.
Example 10In vitro Study
[0177] The cytotoxicity of the formulations of Example 9 was evaluated in RAW 267.4 cells. One thousand eight hundred and fifty cells (1850 cells) cultivated in DMEM supplemented with 10% FBS were placed in 96 well plates, 24 hours before the experiment. These cells were then incubated with increasing quantities of doxorubicin for 2, 4, 8 and 24 hours, after which non-internalized liposomes were removed and replaced by fresh media. Cells were cultivated for a total of 48 hours, and cell viability was evaluated using the sulforhodamine B (SRB) assay. The range of doxorubicin concentrations tested were between 78 and 2.4 ?M. For all incubation times, the IC50 of the doxorubicin encapsulated in PMGA-containing liposomes was between 1.3 and 2.9 times lower, than control liposomes without PMGA. This shows that the increased internalization observed previously translates into improved pharmacology of cytotoxic drugs.
[0178] Altogether, these experiments demonstrate that 1) the incorporation of PMGA in the liposome membrane does not compromise the ability of the vesicles as drug carriers, and 2) the incorporation of PMGA in the liposome membrane allows to potentiate the therapeutic activity of a model cytotoxic drug in vitro.
[0179] Although the invention has been illustrated and described with respect to one or more implementations, equivalent alterations and modifications will occur to others skilled in the art upon the reading and understanding of this specification. In addition, while a particular feature of the invention may have been disclosed with respect to only one of several implementations, such feature may be combined with one or more other features of the other implementations as may be desired and advantageous for any given or particular application.
[0180] Accordingly, it is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims. Any publication, document, patent, patent application or publication referred to herein should be construed as incorporated by reference each in their entirety for all purposes.