HYBRID COMPONENT AND PROCESS FOR PRODUCTION THEREOF

Abstract

A hybrid component has least one metal component, which has been overmolded with plastic at least in regions. A process for producing the hybrid component comprises processing a surface region of the metal component with a laser beam, and mounting and shrinking a shrink tube onto the processed surface region of the metal component or applying a sealing material to the processed surface region of the metal.

Claims

1. A process for producing a hybrid component having at least one metal component, which has been overmolded with plastic at least in regions, comprising the following steps: a) processing a surface region of the metal component, such that nano- and/or microstructures are introduced into that surface region, b1) mounting and shrinking a shrink tube onto the processed surface region of the metal component, or b2) applying a sealing material to the processed surface region of the metal component.

2. The process as claimed in claim 1, wherein the metal component has edges in the surface region processed by the laser beam which is provided with the sealing material or on which the shrink tube is mounted and shrunk, and these edges are rounded off with the laser beam by mechanical processing prior to the processing of the surface region.

3. The process as claimed in claim 1, wherein the metal component is an elongate component, and the processed surface region is a coherent strip that runs at an angle.

4. The process as claimed in claim 1, wherein the metal component has an inward narrowing or constriction on each of the opposite sides in the processed surface region.

5. The process as claimed in claim 4, wherein the shrink tube is mounted and shrunk on in the region of the narrowing or constriction.

6. The process as claimed in claim 1, wherein the overmolding is effected in an injection molding operation in an injection mold into which the metal component is placed for this purpose.

7. The process as claimed in claim 1, wherein the sealing material, if it is an elastomer, is applied to the processed surface region in an injection molding operation in an injection mold into which the metal component is placed for this purpose.

8. The process as claimed in claim 1, wherein the sealing material, if it is an adhesive or varnish, is applied in liquid form to the processed surface region, or the sealing material, if it is an adhesive, is applied as a film to the processed surface region.

9. The process as claimed in claim 1, wherein the processed surface region and/or the adhesive film is heated before and/or during the application of the adhesive film to the processed surface region.

10. The process as claimed in claim 1, wherein the processed surface region and/or the injection mold is heated during the overmolding of the shrink tube or sealing material with the plastic.

11. A hybrid component having at least one metal component, which has been overmolded with plastic at least in regions, wherein the metal component, in a surface region provided with nano- and/or microstructures by processing, has a shrink tube that has been shrunk on there, or a layer of a sealing material, and the shrink tube or the sealing material has been overmolded with the plastic on its side remote from the processed surface region with the plastic in contact with the shrink tube or with the sealing material.

12. The hybrid component as claimed in claim 11, wherein the hybrid component has multiple elongate metal components in the form of conductor tracks, arranged parallel to one another, each of which has a surface region that has been processed by laser, and which has such an adjoining shrunk-on shrink tube or such a layer of sealing material applied to the processed surface region, wherein the processed surface regions of the multiple conductor tracks have been jointly overmolded with plastic.

13. (canceled)

Description

[0023] Further features of the present invention will be apparent from the appended claims, the description of a preferred working example that follows, and the appended drawings. The drawings show:

[0024] FIG. 1 a hybrid component produced by the process of the invention in a first oblique view,

[0025] FIG. 2 the hybrid component from FIG. 1 in a second oblique view,

[0026] FIG. 3 a cross section through the hybrid component from FIG. 1,

[0027] FIG. 4 various phases of the production of the hybrid component from FIG. 1.

[0028] The hybrid component 10 shown in FIG. 1 comprises three solid metal components 11, each of which is integrated into a common plastic component 12. Ultimately, the metal components 11 form metal bushings through the plastic component 12.

[0029] In the present working example, the solid metal components 11 are conductor tracks, especially composed of copper. Such hybrid components 10 having conductor tracks find use in electric motors, for example. However, it will be apparent that the present invention is not limited to such hybrid components.

[0030] The hybrid component 10 is an injection molding, in which case the metal components 11 are ultimately insert parts that have been overmolded with the plastic used in the injection molding process.

[0031] In order to significantly increase the leaktightness or the longevity of the leaktightness between the respective metal component 11 and the overmolded plastic, the hybrid component 10 is produced in accordance with the invention in a special way.

[0032] As shown in FIG. 4 in particular, the individual metal components 11, before being overmolded in the later injection molding process, are first processed in that surface region 13 in which they are subsequently overmolded or onto which the plastic is injected, in such a way that nano- and/or microstructures that are three-dimensional in particular are introduced into it, which bring about an increase in surface area in the surface region 13 and/or have depressions comprising undercuts, and/or hooks.

[0033] More preferably, these are introduced by exposure to a laser beam of a laser (not shown) or a laser unit. This is done in such a way that, in this surface region 13, the surface of the metal components 11 is altered in each case by at least partial melting of the metal material. But it is also possible to use other suitable methods, such as chemical etching.

[0034] In the present case, the processed surface region 13 is in strip form in each case and extends circumferentially (in circumferential direction) and coherently along four mutually adjacent sides of the metal component 11 which is virtually cuboidal in the present case, namely along two front sides and reverse sides of large area and along narrow sides that connect these. In the present case, this is angled relative to the longitudinal extent of the metal component 11 (here essentially perpendicularly).

[0035] It will be apparent that, depending on the application, the shape or outline of the surface region may also be different.

[0036] In the surface region 13 thus processed, a shrink tube 14 which is known per se is then mounted and shrunk on in each case.

[0037] Next, the metal components 11 are then inserted as insert parts into an injection mold (not shown) together with the shrink tube 14 and overmolded with the plastic of the later plastic component 12.

[0038] The prior processing of the surface region 13, as has been shown, massively increases leaktightness between the metal component 11 and the shrink tube 14, and hence ultimately also between the plastic component 12 and the metal component 11.

[0039] In order to achieve a more homogeneous distribution of stress and to minimize notch effects, it is additionally advantageous to round off the outer edges 15 of the metal components 11 in the processed surface region 13 by known mechanical methods, especially prior to the processing of the surface region 13; cf. FIG. 4 in particular.

[0040] It may further be the case that the metal components 11 are provided with an inward narrowing or constriction 16 on each of the opposite sides in the processed surface region 13, or that metal components 11 provided with these are used. Then the respective shrink tube 14 is mounted and shrunk onto this narrowing/constriction 16. This improves the fit of the respective shrink tube 14 on the processed surface region 13.

[0041] It has been found that, incidentally, it would also be possible to dispense with the shrink tube 14. Instead, it is alternatively also possible to use an adhesive layer, especially a layer of latently reactive hotmelt adhesive or an elastomer or a varnish.

[0042] Such latently reactive hotmelt adhesives have long been known. These are notable in that they are solid and storable at room temperature and curable at higher temperatures; cf. also EP 2712879A1 with further references.

[0043] The use of such adhesive in particular rather than the shrink tube 14 leads in a similar manner to the elevated leaktightness or longevity of leaktightness which is desired in accordance with the invention in the bond between metal component 11 and the adjoining plastic.

[0044] The same applies to the use of a varnish. Varnishes, in a manner customary in the art, comprise liquid or else pulverulent coating materials that are applied thinly to articles and, through chemical or physical processes (for example evaporation of the solvent), are built up to form a continuous, solid film. Varnishes generally consist of binders such as resins, dispersions or emulsions, fillers, pigments, solvents, and additives.

[0045] Elastomers are known to be dimensionally stable but elastically deformable plastics, the glass transition point of which is below the use temperature. These plastics can be elastically deformed under tensile and compressive stress, but then return to their original, undeformed shape.

LIST OF REFERENCE NUMERALS

[0046] 10 hybrid component [0047] 11 metal component [0048] 12 plastic component [0049] 13 processed surface region [0050] 14 shrink tube [0051] 15 outer edges [0052] 16 constriction