ENERGY-EFFICIENT SOLVENT-FREE METHOD FOR PRODUCING METAL CHELATES

Abstract

The invention relates to a method for producing, amongst other things, amino-acid and/or hydroxycarboxylic-acid metal chelates, a solvent-free mixture of at least one metal oxide, metal hydroxide, metal carbonate or oxalate, and the solid organic acid is subjected to intensive mechanical stress. According to the invention, this is done in that the reaction partners are introduced in particle form into a fluid stream of a fluid-bed countercurrent mill operating without grinding elements, wherein mechanical activation of at least one of the reaction partners is effected by collision processes within a reaction chamber formed in a region of the fluid stream, and a solid body reaction to form the metal chelate is triggered. The novel method operates very energy-efficiently and with a high specific yield. It leads to a product having compact particles in the small, single-digit micrometer range having a comparatively narrow particle size distribution and a large surface. The product is homogenous and very pure. Thermal loading or decomposition of the organic chelate ligands, in particular of the amino acids, is likewise avoided, as are contaminants from milling and grinding element abrasion.

Claims

1-17. (canceled)

18. A metal chelate composition comprising at least one metal chelate compound having a polyvalent metal cation; and at least one chelate ligand which comprises at least one chelating acid from the group consisting of alpha- and beta-amino acids and hydroxycarboxyclic acids, wherein said metal chelate composition is composed at least of the group consisting of metal oxide, metal hydroxide, metal carbonate or metal oxalate and at least one solid organic acid which comprises at least one chelating acid from the group consisting of alpha- and beta-amino acids and hydroxycarboxylic acids, wherein the at least one metal chelate compound is present in the form of particles of which 90% have a diameter of not more than 15 μm and 50% have a diameter of not more than 5 μm and that the metal chelate compound is free of abraded material from mills and milling media.

19. The metal chelate composition as claimed in claim 18, wherein 99.9% of the particles of the at least one metal chelate compound have a diameter of not more than 25 μm.

20. The metal chelate composition as claimed in claim 18, wherein stoichiometric ratio of the at least one chelating ligand to the at least one metal compound in the at least one metal chelate compound ranges from 0.5:1 (mol/mol) to 4:1 (mol/mol).

21. The metal chelate composition as claimed in claim 18, wherein at least one metal of the at least one metal chelate compound is selected from the group consisting of zinc (Zn), copper (Cu), manganese (Mn), selenium (Se), iron (Fe), calcium (Ca), magnesium (Mg), nickel (Ni), cobalt (Co), vanadium (V), chromium (Cr) and molybdenum (Mo).

22. The metal chelate composition as claimed in claim 18, wherein the least one metal chelate compound present is a 2:1 amino acid-metal chelate compound of zinc or copper or a 3:1 amino acid-metal chelate compound of iron or manganese.

23. The metal chelate composition as claimed in claim 18, wherein the at least one metal chelate compound comprises one or more of zinc bisglycinate, zinc bislysinate, zinc bismethionate, copper bisglycinate, copper bislysinate, copper bismethionate, selenium methionate, selenium cysteinate, iron bisglycinate, iron trisglycinate, iron bislysinate, iron trislysinate, iron bismethionate, iron trismethionate, manganese bisglycinate, manganese trisglycinate, manganese bislysinate, manganese trislysinate, manganese bismethionate, and managanese trismethionate.

24. A composition containing the process product of the process for preparing amino acid- or hydroxycarboxylic acid-metal chelates, comprising: preparing a solvent-free mixture of at least one metal compound from the group consisting of metal oxide, metal hydroxide and metal salt, and at least one solid organic acid which comprises at least one chelating acid from the group consisting of alpha- and beta-amino acids and hydroxycarboxylic acids, by introducing each of the at least one metal compound and the at least one solid organic compound in particulate form into a fluid jet of a fluidized-bed opposed-jet mill operating without milling media; and subjecting the solvent-free mixture to mechanical stress in said fluidized-bed opposed-jet mill which is sufficient for causing mechanical activation of at least one of the at least one metal compound and the at least one solid organic acid by particle collision events within a reaction space formed in a jet region of the fluid jet which is sufficient for and a solid-state reaction to form a metal chelate particles wherein 90% of the metal chelate particles have a diameter of not more than 15 μm and 50% of the metal chelate particles have a diameter of not more than 5 μm.

25. The composition according to claim 24 wherein the fluidized bed and the reaction space is formed in a fluid stream section in a crossing region of a jet direction of at least two fluid nozzles.

26. The composition according to claim 24 wherein the fluidized-bed opposed-jet mill is operated at flow velocities ranging from about 300 to 1000 m/s, and at a milling gas pressure ranging from about 5 to 10 bar.

27. The composition according to claim 24 wherein each of the at least one metal compound and the at least one solid organic acid are transported by a transport device into a milling chamber and reach the reaction space in an interior of the milling chamber in free fall.

28. The composition according to claim 24 wherein a fluid in the fluid jet is a gas selected from the group consisting of air, nitrogen, argon, carbon dioxide, and steam, in each case either individually or in admixture.

29. The composition according to claim 24 wherein the at least one metal compound is a metal carbonate or metal oxalate.

30. The composition according to claim 24 wherein the at least one metal compound contains at least one metal or a mixture of metals selected from the group consisting of zinc (Zn), copper (Cu), manganese (Mn), selenium (Se), iron (Fe), calcium (Ca), magnesium (Mg), nickel (Ni), cobalt (Co), vanadium (V), chromium (Cr) and molybdenum (Mo).

31. The composition according to claim 24 wherein the subjecting step is performed such that 99.9% of the metal chelate particles have a diameter of not more than 25 μm.

32. A method of using a metal chelate composition comprising providing a metal chelate composition as recited in claim 24 as a fodder additive, a nutrient, a nutritional supplement, a food additive, a medicament, an antiseptic, a part of a pharmaceutical composition, a fermentation additive, a fertilizer additive, a seed treatment agent, a crop protection agent, a catalyst for chemical reactions, or an electroplating additive.

Description

[0094] To better illustrate the invention, reference is made the accompanying figures. The figures show:

[0095] FIG. 1: in-principle sketch of an apparatus for the reaction milling in a fluidized-bed opposed-jet mill,

[0096] FIG. 1a: sectional view from the side,

[0097] FIG. 1b: sectional view from above;

[0098] FIG. 2a: scanning electron micrograph of zinc-glycine chelate (at left),

[0099] FIG. 2b: scanning electron micrograph of zinc oxide (at right),

[0100] FIG. 2c: particle size distribution, measured on zinc bisglycinate,

[0101] FIG. 2d: scanning electron micrograph of copper glycinate

[0102] FIG. 3: ATR-IR spectrum of glycine;

[0103] FIG. 4: ATR-IR spectrum of methionine;

[0104] FIG. 5: ATR-IR spectrum of zinc-glycine chelate;

[0105] FIG. 6: ATR-IR spectrum of zinc-methionine chelate;

[0106] FIG. 7: ATR-IR spectrum of copper-glycine chelate.

[0107] FIG. 1 shows a schematic depiction of the reaction milling in a fluidized-bed opposed-jet mill 10, with the sketch being limited to the important elements of the apparatus. These are supplemented by apparatus elements which are not shown for starting material provision and introduction, product discharge, instrumentation and the like.

[0108] The fluidized-bed opposed-jet mill depicted is of the type which is commercially available and is used, for example, for very fine comminution of solids (milling, jet milling). In the example shown here, the mill is a fluidized-bed opposed-jet mill having a three-nozzle system.

[0109] Figure la schematically shows the apparatus, namely the fluidized-bed opposed-jet mill 10, in a sectional view from the side, while FIG. 1b shows the same fluidized-bed opposed-jet mill 10 in a sectional view from above, depicting the nozzle arrangement. Identical parts are denoted by the same reference numerals.

[0110] As can be seen in FIG. 1a, a milling chamber 1 is connected via a feed conduit 2 to a milling stock reservoir 3 from which the milling stock is fed into the milling chamber 1. In this working example, the solid, premixed reaction milling stock is introduced from the reservoir 3 in free fall and thus without additional energy input through the feed conduit 2 into the milling chamber 1 which provides or comprises a reaction space 1 for the reaction milling according to the invention.

[0111] As an alternative, it would be possible to provide internals, for example distributing internals, and also additional transport means in the feed conduit 2, especially when introduction does not occur from above but instead, for example, from the side. Furthermore, it is possible in alternative embodiments not shown here to keep the reactants in stock in a plurality of separate reservoirs and mix them either immediately before the milling chamber 1, which can occur in one of the feed conduits 2 or in a separate mixing chamber, or to convey the reactants separately from the respective reservoirs and meter them into the milling chamber 1, where the mixing can occur within the milling chamber itself.

[0112] The fluidized-bed opposed-jet mill 10 has at least two fluid nozzles 4 which have to be directed toward one another or be arranged at an angle relative to one another in order to generate a collision zone in the center of the nozzle arrangement.

[0113] As can be seen from FIG. 1b, three fluid nozzles 4 for introduction of the milling jets are depicted in the example shown, with the nozzles or jet direction vectors crossing in a narrowly delimited zone where the particles collide and subsequently react with one another. The fluid nozzles 4 are arranged in a plane perpendicular to the plane of the drawing of figure la and lie in the plane of the drawing of FIG. 1b, oriented at angles of 120° relative to one another in each case. A fluidized bed 5 composed of milling stock and gas is formed in the center of the nozzle arrangement, i.e. in a collision zone which is formed by means of the gas jets leaving the fluid nozzles 4.

[0114] The milling stock particles present in each case in the center of the fluid nozzles 4 directed toward one another within the fluidized bed and the actual reaction space 5 formed thereby, here the reactants for the chelate formation reaction of the invention, are accelerated by the gas stream to such an extent that the chemical reaction and the associated product formation is triggered after the particle collisions.

[0115] The actual reaction space 5 in which the solid-state reaction takes place is located within the above-described collision zone in the fluidized bed.

[0116] FIG. 2a shows a scanning electron micrograph of a sample of a zinc glycinate (zinc bisglycinate) produced according to the invention compared to the zinc oxide (ZnO) used as starting material for the metal compound in FIG. 2b.

[0117] It can readily be seen that compact particles without a significant proportion of oversized particles, i.e. no needles as can be seen at right in FIG. 2b for the zinc oxide starting material, are formed by means of the process of the invention. As a result, the product displays better further processability and scatterability. The particle sizes are in a narrow one-figure micron range with a relatively narrow particle size distribution. The product is therefore very homogeneous and has a comparatively high surface area. The product can therefore be distributed readily, e.g. finely distributed in relatively complex compositions, and metered, but also readily compacted. Since no undesirable foreign salts and by-products are present, the amino acid density and metal density in the product are high.

[0118] The particle size distribution of the zinc bisglycinate produced as described in working example 1 and shown in FIG. 2a was examined more closely by means of laser light scattering. The results are shown in graph form in FIG. 2c.

[0119] The overwhelming proportion of the particles has a diameter in the range from about 1 to 4 μm. The narrow particle size distribution which can be read off from the individual diameter curve is reflected in typical ratios for the (volumetric) D10, D50 and D90 values.

[0120] 99% of the particles have diameters of less than 10.00 μm (D.sub.99),

[0121] 90% of the particles have diameters of less than 6.82 μm (D.sub.90),

[0122] 50% of the particles have diameters of less than 3.41 μm (D.sub.50) and

[0123] 10% of the particles have diameters of less than 0.86 μm (D.sub.10).

[0124] Further tests on other amino acid chelates according to the invention gave D.sub.50 values in the range from 1 to 5 μm. D.sub.50 is therefore preferably in the range from 1 to 5 μm, more preferably from 1.5 to 3.5 μm.

[0125] The D90 values are preferably in the range from 4 to 7 μm, and the D99 values were less than 15 μm in each of the cases examined.

[0126] FIG. 2d shows a scanning electron micrograph of a further product according to the invention, namely a copper bisglycinate produced as described in working example 4.

[0127] The micrographs of the various amino acid chelates (for ZnGly.sub.2 and CuGly.sub.2) very clearly demonstrate that the process uniformly gives homogeneous and finely divided amino acid chelates regardless of the starting compound.

[0128] FIGS. 3 to 7 show infrared spectra which will be discussed in more detail below.

Analytical Methods

[0129] In the case of the preparation according to the invention of amino acid-metal chelates, the analysis of such compounds and thus the proof of the occurrence of a (mechano)chemical reaction is carried out by means of characteristic band positions, band shapes and band intensities in the infrared spectrum (IR), see, for example, H. Günzler, H.-U. Gremlich, IR-Spektroskopie, 4.sup.th Edition, Wiley-VCH GmbH & Co. KGaA, Weinheim, 2003; G. Socrates, Infrared and Raman Characteristic Group Frequencies: Tables and Charts, third edition, John Wiley & Sons, 2004; R. M. Silverstein, F. X. Webster, D. J. Kiemie, Spectrometric Identification of Organic Compounds, John Wiley & Sons, Inc., 2005; J. Liu, Y. Hou, S. Gao, M. Ji, R. Hu, Q. Shi, J. Therm. Anal. calorim. 1999, 58, 323-330; M. Pedersen, H. D. Ashmead, U.S. Pat. No. 6,518,240 (B1) 2003; J. J.-C. Ko, S. X.-J. Xie, EP 2204099 (A1) 2010. This analysis is preferably carried out using the known technique of attenuated total reflection, thus as ATR-IR. This procedure allows direct measurement of a sample without any sample preparation and thus without contamination with auxiliaries (for example potassium bromide in the case of conventional sample preparation as KBr pellet) which could in turn influence the measurement, e.g. by reducing the measurement resolution by band broadening or falsification of the band shape (Christiansen effect). The latter undesirable effect caused by a particle size which is too large does not occur in the case of the product material produced according to the invention since this material occurs as compact particles in a small single-figure micron range with a comparatively large surface area (FIG. 2a, d).

[0130] The structural characterization of, for example, zinc bismethionate may be found in R. B. Wilson, P. de Meester and D. J. Hodgson, Inorg. Chem. 1977, 16, 1498-1502 or M. Rombach, M. Gelinky, H. Vahrenkamp, Inorg. Chim. Acta 2002, 334, 25-33. In the present case, too, it was demonstrated by means of such spectroscopic reference measurements that the products produced according to the invention are structurally the same as wet-chemically-produced reference material, sometimes commercially available. This is emphasized particularly because the “American Association of Feed Control Officials” (AAFCO) define such chelates as products of the reaction of a metal ion of a soluble metal salt with an amino acid (see, for example, S. D. Ashmead, M. Pedersen, U.S. Pat. No. 6,426,424 (B1) 2002). In particular, the chelate formation was demonstrated by significant changes in the IR spectrum during the course of the production process of the invention, which will be illustrated below with the aid of suitable examples.

ATR-IR Analysis, Spectroscopic Proof of Chelate Formation

[0131] In the course of IR analysis for the purpose of demonstrating the chelate formation when carrying out the process of the invention, the change in position of the nitrogen-hydrogen stretching vibration NH of the ammonium group is of particular importance. This band is shifted from about 3150 wave numbers (cm.sup.−1, unit of the abscissa of the IR spectrum) in the case of the amino acid glycine (FIG. 3) or from less than 2950 cm.sup.−1 in the case of methionine (FIG. 4) to about 3440 cm.sup.−1 for zinc glycinate (FIG. 5) or about 3295 cm.sup.−1 for zinc methionate (FIG. 6) by chelate formation. The wave number differences which occur demonstrate the participation of the nitrogen atom in complexation, thus chelate formation itself. Further bands in this region above 3000 cm.sup.−1 are essentially attributable to the presence of water of crystallization. In addition, harmonics of intense fundamental vibrations of the upper fingerprint region are to be found there. The asymmetric carboxylate stretching vibration v.sub.as(COO.sup.−) of the amino acids which is originally present appears at about 1575 cm.sup.−1. Its position barely moves during the course of chelate formation. The position of the symmetric pendant of the carboxylate vibration v.sub.sym(COO.sup.−) also remains stable. Nevertheless, the formation of a chelate in the course of the reaction according to the invention can also be recognized unambiguously in this upper fingerprint region since only in the case of the free amino acid is a deformation vibration δ.sub.sym (NH.sub.3.sup.+) at about 1500 cm.sup.−1 detected (e.g. δ.sub.sym(NH.sub.3.sup.+, glycine): 1498 cm.sup.−1, δ.sub.sym(NH.sub.3.sup.+, methionine): cm.sup.−1, δ.sub.sym(NH.sub.3.sup.+, lysine): 1511 cm.sup.−1) , but this disappears during the course of reaction milling and chelate formation. The respective metal-nitrogen vibration in these chelates is found at only low wave numbers in the lower fingerprint region, e.g. Met-N (zinc methionate) at 419 cm.sup.−1, because of the relatively high atomic masses of the metals. The significant changes there in the IR spectrum of the metal chelates compared to the corresponding spectra of the free amino acids are likewise unambiguous evidence of chelate formation during the course of the process of the invention.

[0132] In the case of copper bisglycinate compared to the starting material glycine, signals are present at about 3330, 3260 and 3160 cm.sup.−1 in the IR region of the chelate bands (cf. FIG. 7).

SUMMARY OF THE ADVANTAGES OF THE INVENTION

[0133] The invention provides an energy-efficient process carried out in the absence of solvent for preparing amino acid-metal chelates. Energy savings compared to previous processes arise firstly from the fact that no wet-chemical reactions with subsequent drying are required. Although a mechanochemical reaction is realized, no milling media and additional masses, for example counterweights in the case of reactions in excentric vibratory mills, are required, as otherwise in the prior art. The process product is therefore kept free of abraded metal from the milling media. A mixture of the starting materials amino acid/hydroxycarboxylic acid and metal oxide, metal carbonate or metal oxalate fed in under atmospheric pressure is preferably converted mechanochemically into the corresponding metal chelate solely by means of the fluid jet (gas jet) in a fluidized-bed opposed-jet mill due to the particle collisions initiated by the gas streams. The energy efficiency also arises from the fact that the process of the invention operates solely by means of the milling gas jet without additional introduction of thermal energy, radiative energy or the like being necessary. The autogenous reaction process which is therefore novel for complete chemical conversion of the starting materials allows the combination of organic acids, preferably naturally occurring amino acids such as glycine, methionine or lysine, with oxides, carbonates or oxalates of trace element metals, in particular of zinc, copper, manganese, selenium, iron, calcium, magnesium, nickel, cobalt, vanadium, chromium or molybdenum. Sought-after fodder additives and nutritional supplements, e.g. zinc (bis)glycinate, zinc (bis)methionate, zinc (bis)lysinate, copper (bis)glycinate, copper (bis)methionate, copper (bis)lysinate and many more, are obtained in this way. The use of hydroxycarboxylic acids instead of amino acids, which is likewise possible, leads first and foremost to food additives; other (industrial) uses of such chelate compounds are known. The process product is obtained in very structurally homogeneous and very pure form. Thermal stressing or decomposition of the organic chelate ligands, in particular the amino acids, is avoided as is contamination by abraded material from mills and milling media.

[0134] In contrast to known processes using various mills, for example excentric vibratory mills, the fluidized-bed opposed-jet mill also works in continuous operation.

[0135] The water of reaction is removed together with the exiting milling gas without extra energy input.

LIST OF REFERENCE NUMERALS

[0136] 10 Fluidized-bed opposed-jet mill [0137] 1 Milling chamber [0138] 2 Feed conduit [0139] 3 Milling stock reservoir [0140] 4 Fluid nozzle (milling gas nozzle) [0141] 5 Fluidized bed (reaction space)