MOTOR CORE AND MOTOR

Abstract

Provided is a miniaturized motor core with multiple poles for use in motors that require both output density and high efficiency. The motor core is formed by stacking a plurality of electrical steel sheets with a tooth width of 0.5 mm or more and 2.0 mm or less and 12 or more of slots arranged between the teeth, where the electrical steel sheet has an iron loss of 220 W/kg or less when excited at 1.0 T-3000 Hz.

Claims

1. A motor core formed by stacking a plurality of sheet-shaped soft magnetic materials with a tooth width of 0.5 mm or more and 2.0 mm or less and 12 or more of slots arranged between the teeth, wherein the soft magnetic material has an iron loss of 220 W/kg or less when excited at 1.0 T-3000 Hz.

2. The motor core according to claim 1, wherein the soft magnetic material has a magnetic flux density of 1.55 T or more in a magnetic field of 5000 A/m.

3. The motor core according to claim 1, wherein the soft magnetic material is an electrical steel sheet, and the electrical steel sheet has a Si concentration distribution in a thickness direction.

4. A motor comprising the motor core according to claim 1, and a rotor in which 14 or more magnets are arranged in a circumferential direction.

5. A motor having a sealed outer rotor structure, wherein a rotor is arranged outside the motor core according to claim 1.

6. The motor according to claim 4, wherein the rotor is arranged outside the motor core, and the motor has a sealed outer rotor structure.

7. The motor core according to claim 2, wherein the soft magnetic material is an electrical steel sheet, and the electrical steel sheet has a Si concentration distribution in a thickness direction.

8. A motor comprising the motor core according to claim 2, and a rotor in which 14 or more magnets are arranged in a circumferential direction.

9. A motor comprising the motor core according to claim 3, and a rotor in which 14 or more magnets are arranged in a circumferential direction.

10. A motor comprising the motor core according to claim 7, and a rotor in which 14 or more magnets are arranged in a circumferential direction.

11. A motor having a sealed outer rotor structure, wherein a rotor is arranged outside the motor core according to claim 2.

12. A motor having a sealed outer rotor structure, wherein a rotor is arranged outside the motor core according to claim 3.

13. A motor having a sealed outer rotor structure, wherein a rotor is arranged outside the motor core according to claim 7.

14. The motor according to claim 8, wherein the rotor is arranged outside the motor core, and the motor has a sealed outer rotor structure.

15. The motor according to claim 9, wherein the rotor is arranged outside the motor core, and the motor has a sealed outer rotor structure.

16. The motor according to claim 10, wherein the rotor is arranged outside the motor core, and the motor has a sealed outer rotor structure.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] In the accompanying drawings:

[0018] FIG. 1 illustrates a stator core used in a core (iron core) manufacturing test.

DETAILED DESCRIPTION

[0019] The motor core of the present disclosure is formed by stacking a plurality of sheet-shaped soft magnetic materials with a tooth width of 0.5 mm or more and 2.0 mm or less and 12 or more of slots arranged between the teeth, where the soft magnetic material has an iron loss (W.sub.10/3k) of 220 W/kg or less when excited at 1.0 T-3000 Hz.

[0020] The following describes the specifications of the motor core of the present disclosure and the requirements for the soft magnetic material of the motor core, as well as the reasons for their limitation. Note that the effect of the present disclosure can be achieved as long as the soft magnetic material used as the iron core material has the specified magnetic properties and material design, and the effect of the present disclosure does not depend on the composition, thickness, or manufacturing method. As used herein, in addition to an electrical steel sheet, amorphous metal and Permendur can be used as the soft magnetic material. In the following description such as the description of the examples, the “%” for chemical composition of an electrical steel sheet means “mass percent”.

[0021] [Tooth Width: 0.5 mm or More and 2.0 mm or Less]

[0022] By narrowing the tooth width, it is possible to secure a wide slot space to introduce a winding wire, and it is possible to secure the number of windings, which are effective in increasing the output density of a motor. Therefore, the tooth width is set to 2.0 mm or less. It is more preferably 1.5 mm or less. On the other hand, when the tooth width is too small, the magnetic flux density of the iron core may increase excessively, which results in an increase in iron loss, and it is difficult to manufacture the motor core by processing an electrical steel sheet in the first place. Therefore, the tooth width is set to 0.5 mm or more. It is preferably 1.0 mm or more. It is preferably 1.5 mm or less.

[0023] [Number of Slots: 12 or More]

[0024] By setting the number of slots to 12 or more, it is possible to cope with the multipolarization described above. There is no upper limit, which may be increased as needed to meet the lower limit of the tooth width depending on the degree of multipolarization. For example, it may be 72 or less.

[0025] [Soft Magnetic Material: Iron Loss of 220 W/Kg or Less when Excited at 1.0 T-3000 Hz] It is possible to effectively reduce the iron loss, which is one of the motor losses, by using a motor core where the iron loss is 220 W/kg or less when a material processed into the shape of the motor core is excited at 1.0 T-3000 Hz. The motor core of the present disclosure has the above-described tooth width and number of slots, which are suitable for motors aiming at multipolarization or high-speed rotation to increase the output density. For motors with such specifications, the excitation frequency of the iron core is about 1000 Hz or higher. In actual motor driving circumstances, the excitation frequency of the iron core is even higher, which is around 3000 Hz, taking the influence of harmonics due to inverter into consideration. In other words, we found that the iron loss when excited at a frequency of 3000 Hz, which is also the iron loss of a material processed to the above-described tooth width and number of slots, reflects the iron loss properties in an actual motor. Therefore, we decided to prepare the motor core with a soft magnetic material with an iron loss of 220 W/kg or less when excited at 1.0 T-3000 Hz. It is more preferably 150 W/kg or less. However, since the use of a soft magnetic material with low iron loss increases the costs, the soft magnetic material may be selected as needed. There is no lower limit, but the iron loss may be, for example, 15 W/kg or more.

[0026] The iron loss described in the present disclosure is assumed to be a value measured and evaluated after subjecting a motor coring test piece to primary winding and secondary winding. However, in the case of a motor with an outer rotor, evaluation by SST (single sheet test) which uses a minute test piece cut out from a motor core with an original machined end face may be performed.

[0027] [Soft Magnetic Material: Magnetic Flux Density of 1.55T or More in Magnetic Field of 5000 A/m]

[0028] By applying a soft magnetic material with a magnetic flux density (B.sub.50) of 1.55 T or more in a magnetic field of 5000 A/m to the motor core, it is easier to obtain a higher motor torque, thereby further increasing the output density of a motor. Battery-powered motors, such as those used in cordless vacuum cleaners and drones, have voltage and current limitations that limit the strength of a field magnet produced by a winding wire around a motor core. In other words, the number of turns of the winding wire is adjusted to obtain a field magnet that achieves the required rotational speed and torque of the motor. However, although an increase in the number of turns strengthens the field magnet, it also increases the required voltage. Therefore, under the above constraints, the available strength of the field magnet is limited to a certain range. In this regard, we examined a motor with the tooth width and the number of slots according to the present disclosure and found that a range of the available strength of the field magnet equivalent to the magnetic flux density B.sub.50, that is, the high magnetic flux density of the iron core material at 5000 A/m effectively contributes to increasing the torque of the motor. It is more preferably 1.60 T or more. It is still more preferably 1.65 T or more. There is no upper limit, but it may be 1.90 T or less, for example.

[0029] [Electrical Steel Sheet: Si Concentration Distribution in Thickness Direction]

[0030] When an electrical steel sheet is used as the soft magnetic material, the electrical steel sheet has a Si concentration distribution in the thickness direction. In other words, it has a higher Si concentration in a surface layer than in the center of the thickness, which not only improves the iron loss properties at high frequencies but also can suppress deterioration of iron loss properties due to punching. For the Si concentration distribution that achieves such magnetic properties, the difference ΔSi between the Si concentration in the mid-thickness and the Si concentration in the surface layer is preferably 1.5 mass % to 3.5 mass %. This is because if ΔSi is less than 1.5 mass %, it is difficult to obtain an effective high-frequency iron loss improving effect. On the other hand, if ΔSi exceeds 3.5 mass %, hysteresis loss may increase, resulting in larger motor losses at relatively low speeds. Siliconizing treatment, cladding treatment, or the like may be used to provide the Si concentration distribution to the electrical steel sheet, and there is no need to specifically limit the manufacturing method. The Si concentration in the surface layer may be 3.5 mass % or more. It is preferably 4.5 mass % or more. The Si concentration in the surface layer may be 7.0 mass % or less. It is preferably 6.5 mass % or less. The Si concentration in the mid-thickness may be 1.5 mass % or more. It is preferably 2.5 mass % or more. The Si concentration in the mid-thickness may be 5.5 mass % or less. It is preferably 4.0 mass % or less. As used herein, the surface layer is a range from the surface to ⅓ of the thickness, and the Si concentration in the surface layer is the average Si concentration in this thickness range.

[0031] A motor core is prepared by stacking a plurality of sheet-shaped soft magnetic materials having the above configuration. As used herein, the number of the sheet-shaped soft magnetic materials may be appropriately adjusted according to the required output of a motor.

[0032] In manufacturing the motor core, we assume punching as a means of processing the soft magnetic material, which is the raw material, into the shape of the core. However, if the above requirements are met, the desired effect can also be obtained even the soft magnetic material is processed with a laser.

[0033] The motor core is combined with a rotor to form a motor. The following describes the motor according to the present disclosure.

[Rotor: 14 or More Magnets Arranged in Circumferential Direction]

[0034] The number of magnets in the rotor is set to 14 or more to obtain the effect of increasing the motor torque by multipolarization. In other words, the torque of a magnet motor is expressed by the following equation, and the following equation indicates that increasing the number of poles (the number of pole pairs×2) is an effective design guideline for increasing the torque. An increase in the number of poles corresponds to an increase in the number of magnets in the rotor. The following equation indicates that, although multipolarization is effective for increasing the torque, the excitation frequency of the iron core increases as the number of poles increases because there is a proportional relationship between the excitation frequency f of the iron core and the number of pole pairs P.sub.n. Among iron losses, an eddy current loss increases in proportion to the square of the excitation frequency f, and the increase in iron loss due to an increase in frequency becomes remarkable especially when the number of magnets is 14 or more. Therefore, in the motor having the tooth width and the number of slots according to the present disclosure, a high motor torque is realized while suppressing an increase in loss by combining an iron core material with an iron loss of 220 W/kg or less when excited at 1.0 T-3000 Hz, especially when the number of magnets is 14 or more. The number of magnets is preferably 16 or more and more preferably 20 or more. There is no upper limit to the number of magnets. However, as the number of poles increases (the number of magnets increases), the excitation frequency (proportional to the number of magnets×rotation speed) increases, the iron loss increases, and the costs increase. These factors may be taken into consideration when designing the motor, and the number may be determined as appropriate. It may be, for example, 48 or less.

T=P.sub.n{ψ.sub.ai.sub.q+L.sub.d−L.sub.q)i.sub.di.sub.q}

T: motor torque
P.sub.n: number of pole pairs
ψ.sub.a: flux linkage due to magnetic flux of magnet
i.sub.d,q: current in d or q axis
L.sub.d,q: inductance in d or q axis

[0035] [Motor: Sealed Outer Rotor Structure]

[0036] First, the motor preferably has an outer rotor structure, because when a rotor is arranged outside the motor core, it is possible to arrange many magnets to promote multipolarization. Further, a sealed structure, which does not require the introduction of cooling air, renders it possible to prevent entrapment of foreign matters that increase the risk of failure.

EXAMPLES

Example 1

[0037] [Influence of Iron Core Material and Motor Properties]

[0038] Motors having a sealed outer rotor structure were prepared using the iron core material (soft magnetic material) listed in Table 1, where the motors had the motor core (stator iron core) and the rotor illustrated in FIG. 1, 14 poles, and 21 slots, and the tooth width was 1.6 mm. Si steel, silicon-gradient steel (steel with Si concentration gradient), and Permendur were obtained by punching using a press mold. Because it was difficult to subject amorphous metal to punching, a desired core shape was cut out by subjecting a core material, which was obtained by stacking and bonding amorphous metal, to wire electric discharge machining. The core using Permendur was annealed at 800° C. for two hours in a dry Ar atmosphere. The magnetic properties of the iron core material listed in Table 1 were measured as follows. A ring core with an outer diameter of 55 mm, an inner diameter of 35 mm, and a stacking thickness of 10.0 mm was prepared by wire electric discharge machining, the ring core was subjected to primary winding and secondary winding, and the iron loss W.sub.10/3k and the magnetic flux density B.sub.50 were measured.

[0039] The motor was driven at 11000 rpm-0.25 Nm, and the motor loss under each set of conditions were evaluated as follows.

[0040] Motor loss (W)=input power (W)−motor output (W)

[0041] Copper loss (W)=winding resistance (Ω)×current (Arms).sup.2

[0042] Motor iron loss (W)=motor loss (W)−copper loss (W)

[0043] Further, the temperature inside the motor was measured with a thermocouple thermometer when the motor had been driven for 20 minutes under the same conditions.

TABLE-US-00001 TABLE 1 Si Average concentration Si Iron Si in surface concentration Sheet loss Magnetic flux concentration layer at center thickness W.sub.10/3k density B.sub.50 No. Core material (mass %) (mass %) (mass %) (mm) (W/kg) (T) 1 1.0% Si steel 1.0 1.0 1.0 0.2 480 1.70 2 2.0% Si steel 2.0 2.0 2.0 0.2 430 1.68 3 3.0% Si steel 3.0 3.0 3.0 0.2 370 1.67 4 6.5% Si steel 6.5 6.5 6.5 0.2 198 1.51 5 Silicon-gradient steel 3.5 4.0 2.5 0.2 213 1.69 6 Silicon-gradient steel 5.5 6.5 3.5 0.2 195 1.56 7 1.0% Si steel 1.0 1.0 1.0 0.1 223 1.69 8 2.0% Si steel 2.0 2.0 2.0 0.1 189 1.67 9 3.0% Si steel 3.0 3.0 3.0 0.1 155 1.65 10 6.5% Si steel 6.5 6.5 6.5 0.1 89 1.49 11 Silicon-gradient steel 3.5 4.0 2.5 0.1 95 1.66 12 Silicon-gradient steel 5.5 6.5 3.5 0.1 99 1.53 13 Amorphous 10.0 10.0 10.0 0.025 40 1.51 (10%Si—12%B—Fe) 14 Permendur 0.0 0.0 0.0 0.2 187 2.34 (48%Co—2%V—Fe) 15 Permendur 0.0 0.0 0.0 0.1 113 2.31 (48%Co—2%V—Fe) Motor Si iron Copper Motor Motor Motor concentration loss loss loss efficiency temperature No. distribution (W) (W) (W) (%) (° C.) Remarks 1 No 67 45 112 74.4 158 Comparative Example 2 No 59 47 106 75.8 153 Comparative Example 3 No 55 49 104 76.2 149 Comparative Example 4 No 37 48 85 80.6 134 Example 5 Yes 29 42 71 83.8 98 Example 6 Yes 24 45 69 84.2 90 Example 7 No 52 46 98 77.6 146 Comparative Example 8 No 38 43 81 81.5 120 Example 9 No 36 44 80 81.7 110 Example 10 No 27 49 76 82.6 107 Example 11 Yes 15 43 58 86.7 86 Example 12 Yes 12 48 60 86.3 80 Example 13 No 26 49 75 82.9 100 Example 14 No 42 39 81 81.5 110 Example 15 No 37 40 77 82.4 102 Example

[0044] According to the results listed in Table 1, it can be understood that using an iron core material (soft magnetic material) with a W.sub.10/3k of 220 W/kg or less effectively reduces the motor iron loss. Further, the copper loss can also be effectively reduced under the conditions using an iron core material with an iron loss of 220 W/kg or less and a magnetic flux density B.sub.50 of 1.55 T or more. In Examples, the temperature of the motor was reduced because both the motor iron loss and the copper loss were reduced. The heat resistance temperature of an insulation coating of a winding wire in a motor is generally about 180° C. Because the temperature in the motor according to the present disclosure is about 140° C. or lower as described above, it can be confirmed that there is no problem with a sealed motor.

[0045] As used herein, the iron loss is a value obtained by cutting a minute test piece for SST from the tooth portion of the motor core without additional processing of the end of the original tooth, and conducting a general magnetic property test.

Example 2

[0046] [Influence of Tooth Width]

[0047] Motors were prepared based on a motor having the outer rotor structure with 14 poles and 21 slots illustrated in FIG. 1, the tooth width of the motors was changed as listed in Table 2, and the motor efficiency was measured when various core materials (thickness: 0.1 mm) listed in Table 2 were used in each motor. The measurement results are also listed in Table 2.

TABLE-US-00002 TABLE 2 Si Si Average concentration concen- Iron Magnetic Motor Motor Tooth Si concen- in surface tration loss flux iron Copper Motor effi- width tration layer at center W.sub.10/3k density B.sub.50 loss loss loss ciency No. (mm) Core material (mass %) (mass %) (mass %) (W/kg) (T) (W) (W) (W) (%) Remarks 1 0.5 3.0% Si steel 3.0 3.0 3.0 146 1.62 45 37 82 81.2 Example 2 0.5 Silicon-gradient 5.5 6.5 3.5 90 1.56 15 43 58 86.7 Example steel 3 1.0 1.0% Si steel 1.0 1.0 1.0 223 1.69 71 46 117 73.2 Comparative Example 4 1.0 3.0% Si steel 3.0 3.0 3.0 146 1.62 37 44 81 81.4 Example 5 1.0 Silicon-gradient 5.5 6.5 3.5 90 1.56 12 45 57 87.0 Example steel 6 1.5 1.0% Si steel 1.0 1.0 1.0 223 1.69 65 47 112 74.5 Comparative Example 7 1.5 3.0% Si steel 3.0 3.0 3.0 146 1.62 34 46 80 81.7 Example 8 1.5 Silicon-gradient 5.5 6.5 3.5 90 1.56 10 46 56 87.1 Example steel 9 2.0 1.0% Si steel 1.0 1.0 1.0 223 1.69 52 46 98 77.6 Comparative Example 10 2.0 3.0% Si steel 3.0 3.0 3.0 146 1.62 30 47 77 82.4 Example 11 2.0 Silicon-gradient 5.5 6.5 3.5 90 1.56 9 46 55 87.5 Example steel 12 2.5 1.0% Si steel 1.0 1.0 1.0 223 1.69 19 46 65 85.1 Comparative Example 13 2.5 3.0% Si steel 3.0 3.0 3.0 146 1.62 14 42 56 87.1 Comparative Example 14 2.5 Silicon-gradient 5.5 6.5 3.5 90 1.56 9 43 52 88.1 Comparative steel Example 15 3.0 1.0% Si steel 1.0 1.0 1.0 223 1.69 16 49 65 85.2 Comparative Example 16 3.0 3.0% Si steel 3.0 3.0 3.0 146 1.62 13 42 55 87.4 Comparative Example 17 3.0 Silicon-gradient 5.5 6.5 3.5 90 1.56 8 44 52 88.2 Comparative steel Example

[0048] From Table 2, it can be understood that, when the teeth are 0.5 mm or more and 2.0 mm or less and the core material has an iron loss W.sub.10/3k of 220 W/kg or less, an increase in iron loss is effectively suppressed. It can also be seen that a material with Si concentration gradient in the thickness direction has almost no increase in iron loss, and as result, its efficiency is maintained at a high level even if the tooth width is small.

[0049] The above examples were evaluated by applying a motor core to a motor with a sealed outer rotor structure, but note that the scope of the present disclosure is not limited to the motor type disclosed in the examples as long as the requirements of the present disclosure are met.