CARBON NITRIDE BASED COMPOSITE CERAMIC TOOL MATERIALS, PREPARATION METHOD AND CUTTING TOOL THEREOF

Abstract

The present invention relates to the field of new materials technology, in particular to carbon nitride composite ceramic tool materials, preparation method and cutting tools thereof. The raw materials comprise carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt, carbon nitride as the matrix phase, titanium carbonitride as the reinforcing phase are added to the carbon nitride based composite ceramic materials, with molybdenum, nickel and cobalt as a suitable sintering aid, dense composite tool material is obtained with vacuum hot press sintering method. The prepared carbon nitride based composite ceramic tool materials boast the advantages of low cost, high hardness, high bending strength and high fracture toughness, which is an important way to promote the innovation, development and popularization of carbon nitride materials.

Claims

1. Carbon nitride based composite ceramic tool materials, wherein raw materials of the tool materials comprise carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt, and a weight ratio of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is 40 to 70:20 to 45:2 to 8:2 to 8:2 to 8.

2. The materials according to claim 1, wherein the weight ratio of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is 48 to 63:25 to 40:3 to 5:3 to 5:3 to 5.

3. The materials according to claim 1, wherein a particle size of carbon nitride is 1 to 5 μm; or, the particle size of titanium carbonitride is 0.5 to 1.5 μm; or, the particle size of molybdenum is 0.5 to 1.5 μm; or, the particle size of yttrium nickelide is 0.5 to 1.5 μm; or, the particle size of yttrium cobaltide is 0.5 to 1.5 μm.

4. A method of preparing carbon nitride based composite ceramic tool materials according to claim 1, the method comprising: ball milling carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt, respectively, to make raw material powders; mixed ball milling and drying the raw material powders in a set ratio to obtain mixed materials; vacuum hot press sintering the mixed materials to obtain carbon nitride based composite ceramic tool materials.

5. The method according to claim 4, wherein ball milling medium of the ball milling of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is anhydrous ethanol.

6. The method according to claim 5, wherein ball milling time of the raw materials of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is 60 to 72 h; or, a drying temperature of the raw material powders after ball milling is 100 to 120° C.; further, the raw material powders being dried are sieved through a 100 mesh.

7. The method according to claim 4, wherein a medium of the mixed ball milling is anhydrous ethanol.

8. The method according to claim 4, wherein conditions of vacuum hot press sintering are: heating from 15-25° C. to 950-1050° C. at a heating rate of 40 to 60° C./min, while pressurizing to 7.5 to 8.5 MPa; then heating to 1450 to 1600° C. at a heating rate of 15 to 35° C./min, while the pressure is uniformly increased to 28 to 35 MPa; a heat and pressure preservation time is 15 to 85 min; further, the conditions of hot press sintering are: heating from 20° C. to 1000° C. at a heating rate of 50° C./min, while pressurizing to 8 MPa; then heating to 1450° C., 1500° C., 1550° C. or 1600° C. at a heating rate of 30° C./min, while pressurizing uniformly to 32 MPa; a heat and pressure preservation time is 20 min, 40 min, 60 min or 80 min.

9. The method according to claim 4, wherein materials after sintering are cooled with a furnace, and the nitride carbon based composite ceramic cutting tool materials is obtained.

10. A cutting tool, wherein the cutting tool is prepared from nitride carbon based composite ceramic tool materials according to claim 1.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] FIG. 1 shows a SEM image of the carbon nitride based composite ceramic tool materials prepared in Example 1 of the present invention.

DETAILED DESCRIPTION

[0018] It should be pointed out that the following detailed descriptions are all illustrative and are intended to provide further descriptions of the present invention. Unless otherwise specified, all technical and scientific terms used in the present invention have the same meanings as those usually understood by a person of ordinary skill in the art to which the present invention belongs.

[0019] It should be noted that the terms used herein are merely used for describing specific implementations, and are not intended to limit exemplary implementations of the present disclosure. As used herein, the singular form is also intended to include the plural form unless the context clearly dictates otherwise. In addition, it should further be understood that, terms “comprise” and/or “include” used in this specification indicate that there are features, steps, operations, devices, components, and/or combinations thereof.

[0020] An exemplary embodiment of the present invention provides carbon nitride based composite ceramic tool materials, the raw materials comprise carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt, and the weight ratio (%) of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is 40 to 70:20 to 45:2 to 8:2 to 8:2 to 8.

[0021] In the present invention, carbon nitride is used as the matrix phase, titanium carbonitride as the reinforcing phase, and molybdenum, nickel and cobalt as metal phase sintering aids. Research shows that the mechanical properties of the carbon nitride based composite ceramic tool materials obtained with the above raw materials have superior mechanical properties, thus enabling the use of carbon nitride as the matrix phase for the preparation of ceramic tools.

[0022] In some embodiments, the weight ratio (%) of carbon nitride, titanium carbonitride, molybdenum, nickel, and cobalt is 48 to 63:25 to 40:3 to 5:3 to 5:3 to 5.

[0023] In some embodiments, the particle size of carbon nitride is 1 to 5 μm.

[0024] In some embodiments, the particle size of titanium carbonitride is 0.5 to 1.5 μm.

[0025] In some embodiments, the particle size of molybdenum is 0.5 to 1.5 μm.

[0026] In some embodiments, the particle size of nickel is 0.5 to 1.5 μm.

[0027] In some embodiments, the particle size of cobalt is 0.5 to 1.5 μm.

[0028] A second embodiment of the present invention provides a method for preparing the carbon nitride based composite ceramic tool materials, comprising the following steps:

[0029] Ball milling carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt, respectively.

[0030] Mixing and drying the ball milled raw material powders in a set ratio to obtain mixed materials.

[0031] Vacuum hot press sintering of the mixture materials to obtain the carbon nitride based composite ceramic tool material.

[0032] In some embodiments, a ball milling medium for separate ball milling of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is anhydrous ethanol. The addition of anhydrous ethanol gives the material a certain degree of fluidity and viscosity and acts as a dispersant; moreover, the anhydrous ethanol will completely evaporate during the drying process of the ball to milled materials, leaving no residue.

[0033] Further, the time duration for ball milling of the raw materials of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt is 60 to 72 h.

[0034] Further, a drying temperature of the raw material powders after ball milling is 100 to 120° C.

[0035] Further, the dried raw material powders are sieved through a 100 mesh.

[0036] Further, the medium for mixed ball milling is anhydrous ethanol, so as to make the mixing of each phase material more uniformly.

[0037] The vacuum hot press sintering described in the present invention refers to that a process of compression molding and then sintering is carried out under vacuum conditions. In some embodiments, the processing conditions of vacuum hot press sintering are: heating from 15-25° C. to 950-1050° C. at a heating rate of 40 to 60° C./min, while pressurizing to 7.5 to 8.5 MPa; then heating to 1450 to 1600° C. at a heating rate of 15 to 35° C./min, while pressurizing uniformly to 28 to 35 MPa; heat and pressure preservation time is 15 to 85 min. A temperature can be 1445 to 1455° C., 1495 to 1505° C., 1545 to 1555° C. or 1595 to 1600° C. at a heating rate of 15 to 35° C./min. A heat and pressure preservation time after heating to 1450 to 1600° C. and pressurizing can be 15 to 25 min, 35 to 45 min, 55 to 65 min, or 75 to 85 min.

[0038] Further, the processing conditions for hot press sintering are: heating from 20° C. to 1000° C. at a heating rate of 50° C./min while pressurizing to 8 MPa; then heating to 1450° C., 1500° C., 1550° C. or 1600° C. at a heating rate of 30° C./min while pressurizing uniformly to 32 MPa; heat and pressure preservation time is 20 min, 40 min, 60 min or 80 min.

[0039] In some embodiments, after the sintering is completed, the sintered materials are cooled with the furnace to obtain carbon-nitride based composite ceramic tool materials.

[0040] A third embodiment of the present invention provides a cutting tool, prepared from the above nitride carbon-based composite ceramic tool materials.

Example 1

[0041] 1) Raw material powders of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt are respectively ball milled with anhydrous ethanol as the medium, and the ball milling is carried out on a roller ball mill, wherein the carbon nitride powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 5 μm; the titanium carbonitride powder is ball milled for 72 h to disperse the larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; molybdenum powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; nickel powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; cobalt powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm, the ball milled powder are all vacuum dried after ball milling at the drying temperature of 120° C., and sieved through 100 mesh, and the sieved powder is encapsulated for use;

[0042] 2) According to an attached parameter table of the embodiment, 63% weight ratio of carbon nitride powder with a particle size of 5 μm, 25% weight ratio of titanium carbonitride powder with a particle size of 0.5 μm, 4% weight ratio of molybdenum powder with a particle size of 0.5 μm, 4% weight ratio of nickel powder with a particle size of 0.5 μm, 4% weight ratio of cobalt powder with a particle size of 0.5 μm, are poured into a mixing tank, adding anhydrous ethanol as the medium, and are ball milled in the ball mill for 48 h to mix all the phase materials uniformly. The composite ceramic materials are vacuum dried at 120° C. and sieved through 100 mesh to obtain a well-dispersed composite ceramic material powder, and is encapsulated for use;

[0043] 3) The mixed composite ceramic material powder is put into a graphite mold, and then into a vacuum hot press sintering furnace. In a vacuum environment, adopt hot press sintering method at an uniform pressure; heating from 20° C. to 1000° C. at a heating rate of 50° C./min while pressurizing to 8 MPa; then heating to 1600° C. at a heating rate of 30° C./min while pressurizing uniformly to 32 MPa; heat and pressure preservation time is 60 min; cooling to 20° C. with the furnace, the carbon nitride based composite ceramic tool materials is obtained, as shown in FIG. 1, the tool material has a dense organization with fine and uniform crystal particle.

[0044] The experiment parameters of the embodiment are shown in table 1.

TABLE-US-00001 TABLE 1 Weight Ratio of the Components wt. % Sintering carbon titanium Temperature/ Holding Pressure/ Example nitride carbonitride molybdenum nickel cobalt ° C. Time/min MPa 1 63 25 4 4 4 1600 60 32 2 58 30 4 4 4 1600 60 32 3 53 35 4 4 4 1600 60 32 4 48 40 4 4 4 1600 60 32

Example 2

[0045] 1) Raw material powders of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt are respectively ball milled with anhydrous ethanol as the medium, and the ball milling is carried out on a roller ball mill, wherein the carbon nitride powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 5 μm; the titanium carbonitride powder is ball milled for 72 h to disperse the larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; molybdenum powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; nickel powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; cobalt powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm, the ball milled powder are all vacuum dried after ball milling at the drying temperature of 120° C., and sieved through 100 mesh, and the sieved powder is encapsulated for use;

[0046] 2) According to the attached parameter table of the embodiment, 58% weight ratio of carbon nitride powder with a particle size of 5 μm, 30% weight ratio of titanium carbonitride powder with a particle size of 0.5 μm, 4% weight ratio of molybdenum powder with a particle size of 0.5 μm, 4% weight ratio of nickel powder with a particle size of 0.5 μm, 4% weight ratio of cobalt powder with a particle size of 0.5 μm, are poured into the mixing tank, adding anhydrous ethanol as the medium, and are ball milled in the ball mill for 48 h to mix all the phase materials uniformly. The composite ceramic materials are vacuum dried at 120° C. and sieved through 100 mesh to obtain a well-dispersed composite ceramic material powder, and is encapsulated for use;

[0047] 3) The mixed composite ceramic material powder is put into a graphite mold, and then into a vacuum hot press sintering furnace. In a vacuum environment, adopt hot press sintering method at an uniform pressure; heating from 20° C. to 1000° C. at a heating rate of 50° C./min while pressurizing to 8 MPa; then heating to 1600° C. at a heating rate of 30° C./min while pressurizing uniformly to 32 MPa; heat and pressure preservation time is 60 min; cooling to 20° C. with the furnace, the carbon nitride based composite ceramic tool material is obtained.

[0048] The experiment parameters of the embodiment are shown in table 1.

Example 3

[0049] 1) Raw material powders of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt are respectively ball milled with anhydrous ethanol as the medium, and the ball milling is carried out on a roller ball mill, wherein the carbon nitride powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 5 μm; the titanium carbonitride powder is ball milled for 72 h to disperse the larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; molybdenum powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; nickel powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; cobalt powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm, the ball milled powder are all vacuum dried after ball milling at the drying temperature of 120° C., and sieved through 100 mesh, and the sieved powder is encapsulated for use;

[0050] 2) According to the attached parameter table of the embodiment, 53% weight ratio of carbon nitride powder with a particle size of 5 μm, 35% weight ratio of titanium carbonitride powder with a particle size of 0.5 μm, 4% weight ratio of molybdenum powder with a particle size of 0.5 μm, 4% weight ratio of nickel powder with a particle size of 0.5 μm, 4% weight ratio of cobalt powder with a particle size of 0.5 μm, are poured into the mixing tank, adding anhydrous ethanol as the medium, and are ball milled in the ball mill for 48 h to mix all the phase materials uniformly. The composite ceramic materials are vacuum dried at 120° C. and sieved through 100 mesh to obtain a well-dispersed composite ceramic material powder, and is encapsulated for use;

[0051] 3) The mixed composite ceramic material powder is put into a graphite mold, and then into a vacuum hot press sintering furnace. In a vacuum environment, adopt hot press sintering method at an uniform pressure; heating from 20° C. to 1000° C. at a heating rate of 50° C./min while pressurizing to 8 MPa; then heating to 1600° C. at a heating rate of 30° C./min while pressurizing uniformly to 32 MPa; heat and pressure preservation time is 60 min; cooling to 20° C. with the furnace, the carbon nitride based composite ceramic tool material is obtained.

[0052] The experiment parameters of the embodiment are shown in table 1.

Example 4

[0053] 1) Raw material powders of carbon nitride, titanium carbonitride, molybdenum, nickel and cobalt are respectively ball milled with anhydrous ethanol as the medium, and the ball milling is carried out on a roller ball mill, wherein the carbon nitride powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 5 μm; the titanium carbonitride powder is ball milled for 72 h to disperse the larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; molybdenum powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; nickel powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm; cobalt powder is ball milled for 72 h to disperse larger agglomerated particles and obtain a powder with an uniform particle size of 0.5 μm, the ball milled powder are all vacuum dried after ball milling at the drying temperature of 120° C., and sieved through 100 mesh, and the sieved powder is encapsulated for use;

[0054] 2) According to the attached parameter table of the embodiment, 48% weight ratio of carbon nitride powder with a particle size of 5 μm, 40% weight ratio of titanium carbon nitride powder with a particle size of 0.5 μm, 4% weight ratio of molybdenum powder with a particle size of 0.5 μm, 4% weight ratio of nickel powder with a particle size of 0.5 μm, 4% weight ratio of cobalt powder with a particle size of 0.5 μm, are poured into the mixing tank, adding anhydrous ethanol as the medium, and are ball milled in the ball mill for 48 h to mix all the phase materials uniformly. The composite ceramic materials are vacuum dried at 120° C. and sieved through 100 mesh to obtain a well-dispersed composite ceramic material powder, and is encapsulated for use;

[0055] 3) The mixed composite ceramic material powder is put into a graphite mold, and then into a vacuum hot press sintering furnace. In a vacuum environment, adopt hot press sintering method at an uniform pressure; heating from 20° C. to 1000° C. at a heating rate of 50° C./min while pressurizing to 8 MPa; then heating to 1600° C. at a heating rate of 30° C./min while pressurizing uniformly to 32 MPa; heat and pressure preservation time is 60 min; cooling to 20° C. with the furnace, the carbon nitride based composite ceramic tool material is obtained.

[0056] The experiment parameters of the embodiment are shown in table 1.

Comparative Example 1

[0057] A difference with Example 1 is that titanium carbonitride is omitted and the rest is the same as that in Example 1.

Comparative Example 2

[0058] A difference with Example 1 is that molybdenum is omitted and the rest is the same as that in Example 1.

Comparative Example 3

[0059] A difference with Example 1 is that nickel is omitted and the rest is the same as that in Example 1.

Comparative Example 4

[0060] A difference with Example 1 is that cobalt is omitted and the rest is the same as that in Example 1.

[0061] The mechanical properties of the carbon nitride based composite ceramic tool materials prepared in examples 1 to 4 and comparative example 1 to 4 are shown in Table 2, and shows that a Vickers hardness, bending strength, and fracture toughness of the embodiments are greatly improved.

TABLE-US-00002 TABLE 2 Vickers Bending Fracture Toughness/ Hardness/GPa Strength/MPa MPa .Math. m.sup.1/2 Example 1 13.3 1015 7.15 Example 2 13.5 1036 7.89 Example 3 13.9 1076 8.45 Example 4 14.0 1090 8.75 Comparative 7.2 453 4.21 example 1 Comparative 12.7 966 7.6 example 2 Comparative 12.9 899 7.9 example 3 Comparative 12.8 933 8.0 example 4

[0062] The foregoing descriptions are merely preferred embodiments of the present invention, but not intended to limit the present invention. A person skilled in the art may make various alterations and variations to the present invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention shall fall within the protection scope of the present invention.