FLUORINE RUBBER COMPOSITION AND RUBBER MOLDED ARTICLE FORMED USING SAME

Abstract

A fluorine rubber composition contains a component A that is a base rubber containing a hydrogen-containing fluorine rubber as a main component, a component B that is a compound having a perfluoropolyether skeleton, and a component C that is a powdery filler having a bulk density of 0.4 g/cm.sup.3 or less. A part or whole of the component B contains an alkenyl group in a molecule. (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B)?4 is satisfied wherein d.sub.B is a density of the component B, p.sub.B is a content of the component B relative to 100 parts by mass of the component A, d.sub.C is the bulk density of the component C, and p.sub.C is a content of the component C relative to 100 parts by mass of the component A.

Claims

1. A fluorine rubber composition comprising: a component A that is a base rubber containing a hydrogen-containing fluorine rubber as a main component; a component B that is a compound having a perfluoropolyether skeleton, a part or whole of the component B containing an alkenyl group in a molecule; and a component C that is a powdery filler having a bulk density of 0.4 g/cm.sup.3 or less, (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B)?4 being satisfied wherein d.sub.B is a density of the component B, P.sub.B is a content of the component B relative to 100 parts by mass of the component A, d.sub.C is the bulk density of the component C, and p.sub.C is a content of the component C relative to 100 parts by mass of the component A.

2. The fluorine rubber composition of claim 1, wherein a percentage of the compound containing an alkenyl group in a molecule in the component B is 20% by mass or more.

3. The fluorine rubber composition of claim 1, wherein the component B contains both the compound containing an alkenyl group in a molecule and a compound containing no alkenyl group in a molecule.

4. The fluorine rubber composition of claim 1, wherein the compound containing an alkenyl group in a molecule in the component B is a one-component material.

5. The fluorine rubber composition of claim 1, wherein the component C contains silica and/or a resin powder.

6. The fluorine rubber composition of claim 1, further comprising a crosslinker.

7. The fluorine rubber composition of claim 6, wherein the crosslinker is an organic peroxide.

8. The fluorine rubber composition of claim 1, further comprising a cross-linking aid.

9. A rubber molded article formed by cross-linking the fluorine rubber composition of claim 1.

10. The rubber molded article of claim 9, wherein a concentration of a CF bond on a surface of the molded article is higher than that in the molded article.

11. The rubber molded article of claim 9, wherein (A.sub.CF/A.sub.CH during irradiation of a surface of the molded article with an X ray)/(A.sub.CF/A.sub.CH during irradiation of a cross-sectional surface of the molded article at a position farthest from the surface of the molded article with an X ray)?2 is satisfied wherein A.sub.CH is a peak area derived from a CH bond at 282 eV to 288 eV, and A.sub.CF is a peak area derived from a CF bond at 288 eV to 296 eV in a C1s peak measured during irradiation with an X ray by X-ray photoelectron spectroscopy.

12. A rubber molded article formed by cross-linking a fluorine rubber composition containing a component A that is a base rubber containing a hydrogen-containing fluorine rubber as a main component, a component B that is a compound having a perfluoropolyether skeleton, a part or whole of the component B containing an alkenyl group in a molecule, and a component C that is a powdery filler having a bulk density of 0.4 g/cm.sup.3 or less, a ratio of a content of the component C to a content of the component B being more than 0.1, a concentration of a CF bond on a surface of the molded article being higher than that in the molded article.

13. A rubber molded article formed by cross-linking a fluorine rubber composition containing a component A that is a base rubber containing a hydrogen-containing fluorine rubber as a main component, a component B that is a compound having a perfluoropolyether skeleton, a part or whole of the component B containing an alkenyl group in a molecule, and a component C that is a powdery filler having a bulk density of 0.4 g/cm.sup.3 or less, a ratio of a content of the component C to a content of the component B being more than 0.1, (A.sub.CF/A.sub.CH during irradiation of a surface of the molded article with an X ray)/(A.sub.CF/A.sub.CH during irradiation of a cross-sectional surface of the molded article at a position farthest from the surface of the molded article with an X ray)?2 being satisfied wherein A.sub.CH is a peak area derived from a CH bond at 282 eV to 288 eV, and A.sub.CF is a peak area derived from a CF bond at 288 eV to 296 eV in a C1s peak measured during irradiation with an X ray by an X-ray photoelectron spectroscopy.

14. The rubber molded article of claim 9, wherein the rubber molded article is a seal.

15. The rubber molded article of claim 14, wherein the seal is for use in a semiconductor production apparatus.

Description

DESCRIPTION OF EMBODIMENTS

[0008] Embodiments will be described in detail below.

[0009] A fluorine rubber composition according to an embodiment contains components A, B, and C.

[0010] The component A is a base rubber. The component A that is the base rubber contains a hydrogen-containing fluorine rubber as a main component. The hydrogen-containing fluorine rubber herein represents a fluorine rubber containing carbon to which hydrogen is bonded, on a main chain of a polymer. The content of the hydrogen-containing fluorine rubber in the component A is more than 50% by mass, suitably 80% by mass or more, more suitably 90% by mass or more, even more suitably 100% by mass. The component A may contain a fluorine rubber other than the hydrogen-containing fluorine rubber.

[0011] Examples of the hydrogen-containing fluorine rubber include a polymer (PVDF) of vinylidene fluoride (VDF), a copolymer of vinylidene fluoride (VDF) and hexafluoropropylene (HFP), a terpolymer of vinylidene fluoride (VDF), hexafluoropropylene (HFP), and tetrafluoroethylene (TFE), a copolymer (FEP) of tetrafluoroethylene (TFE) and propylene (Pr), a terpolymer of vinylidene fluoride (VDF), propylene (Pr), and tetrafluoroethylene (TFE), a copolymer (ETFE) of ethylene (E) and tetrafluoroethylene (TFE), a terpolymer of ethylene (E), tetrafluoroethylene (TFE), and perfluoromethyl vinyl ether (PMVE), a terpolymer of vinylidene fluoride (VDF), tetrafluoroethylene (TFE), and perfluoromethyl vinyl ether (PMVE), and a copolymer of vinylidene fluoride (VDF) and perfluoromethyl vinyl ether (PMVE). The component A suitably contains one or more kinds of these hydrogen-containing fluorine rubbers.

[0012] The component A more suitably contains a vinylidene fluoride-based fluorine rubber (FKM) containing vinylidene fluoride as a main component, such as a copolymer of vinylidene fluoride (VDF) and hexafluoropropylene (HEP) or a terpolymer of vinylidene fluoride (VDF), hexafluoropropylene (HEP), and tetrafluoroethylene (TFE).

[0013] The component B is a compound having a perfluoropolyether skeleton. The compound B which is the compound having a perfluoropolyether skeleton is a liquid material to be mixed uniformly in the component A. A part or whole of the component B contains an alkenyl group in a molecule. Examples of the alkenyl group include a vinyl group, an allyl group, a butenyl group, a pentenyl group, a hexenyl group, and a heptenyl group. Among these alkenyl groups, the vinyl group is suitable. The number of alkenyl groups in a molecule is suitably plural. In this case, a plurality of alkenyl groups in a molecule may be the same as or different from each other.

[0014] The component B may contain both the compound containing an alkenyl group in a molecule and a compound containing no alkenyl group in a molecule. The percentage of the compound containing an alkenyl group in a molecule in the component B is suitably 20% by mass or more, more suitably 30% by mass or more.

[0015] From the viewpoint of maintaining excellent plasma resistance in a rubber molded article formed using the fluorine rubber composition according to the embodiment and reducing bleeding-out of the component B from the rubber molded article, as described below, the density d.sub.B of the component B is suitably 1.5 g/cm.sup.3 or more, more suitably 1.8 g/cm.sup.3 or more. From the same viewpoint, the density d.sub.B is suitably 2.5 g/cm.sup.3 or less, more suitably 2.0 g/cm.sup.3 or less. When the component B contains a plurality of kinds of compounds, the density d.sub.B of the component B is a sum of product of the density and content ratio of each of the compounds. The density d.sub.B of the component B containing an alkenyl group in a molecule is measured by gas pycnometry defined by JIS Z8837: 2018. The density d.sub.B of the component B containing no alkenyl group in a molecule is measured at 20? C. by an oscillation type density meter method defined by JIS K0061: 2001.

[0016] From the viewpoint of achieving high plasma resistance of the rubber molded article, the content p.sub.B of the component B relative to 100 parts by mass of the component A is suitably 0.1 parts by mass or more, more suitably 1.0 parts by mass or more. From the viewpoint of maintaining excellent plasma resistance in the rubber molded article and reducing bleeding-out of the component B from the rubber molded article, the content p.sub.B is suitably 20 parts by mass or less, more suitably 15 parts by mass or less. When the component B contains a plurality of kinds of compounds, the content p.sub.B of the component B is a sum of the contents of the compounds.

[0017] Examples of a commercially available material of the compound containing an alkenyl group in a molecule and having a perfluoropolyether skeleton in the component B C21-315 include SIFEL available from Shin-Etsu Chemical Co., Ltd. In particular, SIFEL 3000 series is suitable. The compound containing an alkenyl group in a molecule and having a perfluoropolyether skeleton is suitably a one-component liquid material.

[0018] Examples of a commercially available material of the compound containing no alkenyl group in a molecule and having a perfluoropolyether skeleton in the component B include FOMBLIN Y lubricant available from Solvay S.A. and Krytox GPL oil available from CHEMOURS Company.

[0019] The component C is a powdery filler that is dispersed in the component A and has a bulk density d.sub.C of 0.4 g/cm.sup.3 or less. Examples of the compound C which is the powdery filler include silica, a resin powder, silicon carbide, boron carbide, silicon nitride, and boron nitride.

[0020] The component C contains suitably one or more kinds of these powder fillers, more suitably silica and/or a resin powder. The silica may be dry silica or wet silica. The silica may be either one of hydrophilic silica having an untreated surface or hydrophobic silica having a surface modified with dimethyl dichlorosilane. Examples of the resin powder include a phenolic resin powder, a fluororesin powder, and a polyetherether ketone (PEEK) resin powder.

[0021] From the viewpoint of maintaining excellent plasma resistance in the rubber molded article and reducing bleeding-out of the component B from the rubber molded article, the bulk density d.sub.C of the powdery filler as the component C is suitably 0.01 g/cm.sup.3 or more, more suitably 0.03 g/cm.sup.3 or more. From the same viewpoint, the bulk density d.sub.C is suitably 0.35 g/cm.sup.3 or less, more suitably 0.20 g/cm.sup.3 or less. When the component C contains a plurality of kinds of powder fillers, the bulk density d.sub.C of the component C is a sum of product of the density and content ratio of each of the powdery fillers. The bulk density d.sub.C of the component C is measured in accordance with a method for measuring a tapped bulk density defined by JIS R1628-1997.

[0022] From the viewpoint of maintaining excellent plasma resistance in the rubber molded article and reducing bleeding-out of the component B from the rubber molded article, the content p.sub.C of the component C relative to 100 parts by mass of the component A is suitably 0.1 parts by mass or more, more suitably 1.0 parts by mass or more. From the viewpoint of reducing deposition of the powdery filler from the rubber molded article, the content p.sub.C is suitably 30 parts by mass or less, more suitably 20 parts by mass or less. When the component C contains a plurality of kinds of powdery fillers, the content p.sub.C of the component C is a sum of the contents of the powder fillers.

[0023] The content p.sub.C of the component C is suitably more than the content p.sub.B of the component B from the viewpoint of reducing deposition of the powdery filler from the rubber molded article and reducing bleeding-out of the component B from the rubber molded article.

[0024] From the same viewpoint, a ratio (p.sub.C/p.sub.B) of the content p.sub.C of the component C to the content p.sub.B of the component B is suitably more than 0.1 and 30 or less, more suitably from 0.12 to 25 inclusive, further suitably from 1.0 to 20 inclusive.

[0025] Examples of the silica as a commercially available material of the component C include AEROSIL series and CARPLEX series available from Evonik Industries AG. Examples of the phenolic resin powder include BELLPEARL series available from AIR WATER BELLPEARL INC. Examples of the fluororesin powder include KYNAR series available from Arkema S.A. Examples of the polyetherether ketone (PEEK) resin powder include VESTAKEEP series available from Daicel-Evonik Ltd.

[0026] In the fluorine rubber composition according to the embodiment, (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B)?4 is suitably satisfied. This means that the volume of the component C is four or more times the volume of the component B. From the viewpoint of maintaining excellent plasma resistance in the rubber molded article and reducing bleeding-out of the component B from the rubber molded article, (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B) 10 is more suitably satisfied, (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B)?50 is further suitably satisfied.

[0027] The fluorine rubber composition according to the embodiment may further contain a crosslinker. Examples of the crosslinker include an organic peroxide, a polyol, a polyamine, and a triazine. The crosslinker is suitably an organic peroxide among these crosslinkers.

[0028] Examples of the organic peroxide include 1,1-bis(t-butyl peroxy)-3,5,5-trimethylcyclohexane, 2,5-dimethylhexane-2,5-dihydroperoxide, di-t-butyl peroxide, t-butyl cumyl peroxide, dicumyl peroxide, ?,?-bis(t-butyl peroxy)-p-diisopropylbenzene, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, 2,5-dimethyl-2,5-di(t-butylperoxy)-hexyne-3, benzoyl peroxide, t-butyl peroxybenzene, t-butyl peroxymaleic acid, t-butyl peroxy isopropylcarbonate, and t-butyl peroxybenzoate. The crosslinker includes suitably one or more kinds of these organic peroxides, more suitably 2,5-dimethyl-2,5-di(t-butylperoxy)hexane.

[0029] The content of the crosslinker relative to 100 parts by mass of the component A is suitably from 0.5 parts by mass to 2.5 parts by mass inclusive, more suitably from 0.5 parts by mass to 2.0 parts by mass inclusive.

[0030] The fluorine rubber composition according to the embodiment may further contain a cross-linking aid. Examples of the cross-linking aid include triallyl cyanurate, trimethallyl isocyanurate, triallyl isocyanurate, triacryl formal, triallyl trimellitate, N,N-m-phenylenebismaleimide, dipropargyl terephthalate, diallyl phthalate, tetraallyl terephthalate amide, triallyl phosphate, bismaleimide, fluorinated triallyl isocyanurate (1,3,5-tris(2,3,3-trifluoro-2-propenyl)-1,3,5-triazin-2,4,6-trione), tris(diallylamine)-S-triazine, triallyl phosphite, N,N-diallyl acrylamide, 1,6-divinyl dodecafluorohexane, hexaallyl phosphoramide, N,N,N,N-tetraallyl phthalamide, N,N,N,N-tetraallyl malonamide, trivinyl isocyanurate, 2,4,6-trivinyl methyltrisiloxane, tri(5-norbornene-2-methylene) cyanurate, and triallyl phosphite. The cross-linking aid includes suitably one or more kinds of these cross-linking aids, more suitably triallyl isocyanurate.

[0031] The content of the cross-linking aid relative to 100 parts by mass of the component A is suitably from 1 part by mass to 10 parts by mass inclusive, more suitably from 2 parts by mass to 5 parts by mass inclusive.

[0032] The fluorine rubber composition according to the embodiment having the configuration described above is cross-linked, thereby obtaining a cross-linked rubber to form a rubber molded article. The fluorine rubber composition according to the embodiment is cross-linked by the action of the crosslinker under heating or the action of irradiation with radial rays, thereby forming a crosslinked structure between molecules of the component A. The component B containing an alkenyl group in a molecule and the cross-linking aid are reacted with the component A, so that they are interposed between molecules of the component A. Accordingly, a crosslinked structure is formed.

[0033] Since the compound having a perfluoropolyether skeleton, which is the component B, is used in the rubber molded article formed by cross-linking the fluorine rubber composition according to the embodiment, excellent plasma resistance can be maintained, specifically a reduction in mass can be reduced even under irradiation with plasma.

[0034] When a fluorine rubber composition forming a seal contains the compound having a perfluoropolyether skeleton, there is a problem that the compound bleeds out from the seal.

[0035] However, the rubber molded article formed by cross-linking the fluorine rubber composition according to the embodiment can reduce bleeding-out of the compound having a perfluoropolyether skeleton, which is the component B. This is considered to be because the powdery filler, which is the component C, is used and the volume of the component C is extremely larger than the volume of the component B, so that the component B is supported on the component C and held in the component A. In addition, the bulk density of the powdery filler, which is the component C, is 0.4 g/cm.sup.3 or less, which is low; thus, deposition of particles of the powdery filler, which is the component C, can be reduced even under irradiation with plasma.

[0036] Since in the rubber molded article formed by cross-linking the fluorine rubber composition according to the embodiment, the fluorine rubber composition contains a powdery filler, which is the component C, in molding processing, the viscosity of the fluorine rubber composition is high. Thus, the compound having a perfluoropolyether skeleton, which is the component B, easily flows. As a result, the component B is segregated in the surface layer, and the concentration of a CF bond on the surface of the molded article is higher than that in the molded article. Accordingly, the CH bond that forms a starting point of deterioration due to attacking by plasma is reduced on the surface of the molded article. Thus, plasma resistance can be enhanced. In quantitative determination, (A.sub.CF/A.sub.CH during irradiation of a surface of the molded article with an X ray)/(A.sub.CF/A.sub.CH during irradiation of a cross-sectional surface of the molded article at a position farthest from the surface of the molded article with an X ray)?2 is suitably satisfied wherein A.sub.CH is a peak area derived from a CH bond at 282 eV to 288 eV, and A.sub.CF is a peak area derived from a CF bond at 288 eV to 296 eV in a C1s peak measured during irradiation with an X ray by X-ray photoelectron spectroscopy. From the viewpoint of maintaining excellent plasma resistance in the rubber molded article and reducing bleeding-out of the component B from the rubber molded article, the ratio is suitably 2.5 or more.

[0037] The rubber molded article formed by cross-linking the fluorine rubber composition according to the embodiment is not particularly limited, but is suitably a seal, more suitably a seal for use in semiconductor production apparatuses.

[0038] The hardness of the cross-linked rubber obtained by cross-linking the fluorine rubber composition according to the embodiment, measured with a type A durometer in accordance with JIS K6253-3: 2012 is suitably 50 A or more, more suitably 55 A or more, and suitably 95 A or less, more suitably 90 A or less.

[0039] The tensile strength at break of the cross-linked rubber obtained by cross-linking the fluorine rubber composition according to the embodiment, measured using a dumbbell-shaped No. 3 test piece with a thickness of 2 mm at a standard test temperature in accordance with JIS K6251: 2017 is suitably 5.0 MPa or more, more suitably 10.0 MPa or more. The elongation at break of the cross-linked rubber is suitably 50% or more, more suitably 100% or more. The tensile stress at 100% elongation of the cross-linked rubber is suitably 1.0 MPa or more, more suitably 1.5 MPa or more.

[0040] The compression set of the cross-linked rubber obtained by cross-linking the fluorine rubber composition according to the embodiment, measured at a test temperature (200?2?) C for a test time of 72 hours in accordance with JIS K6262: 2013 is suitably 80% or less, more suitably 50% or less.

EXAMPLES

[0041] (Seal)

[0042] The following seals of Examples 1 to 13 and Comparative Examples 1 to 7 were produced. The composition of each of the seals is shown also in Tables 1 and 2. The density of a compound having a perfluoropolyether skeleton and containing an alkenyl group in a molecule was measured by gas pycnometry defined by JIS Z8837: 2018. The density of a component having a perfluoropolyether skeleton and containing no alkenyl group in a molecule was measured at a temperature of 20? C. by an oscillation type density meter method defined by JIS K0061: 2001. The bulk density of a powdery filler was measured in accordance with a method for measuring a tapped bulk density defined by JIS R1628-1997.

Example 1

[0043] A hydrogen-containing fluorine rubber (DAI-EL G912 available from Daikin Industries, Ltd.) including a terpolymer of vinylidene fluoride, hexafluoropropylene, and tetrafluoroethylene was used as a component A. Relative to 100 parts by mass of the component A, 1 part by mass (p.sub.B) of compound 1 (SIFEL 3000 series X-71-359 available from Shin-Etsu Chemical Co., Ltd., density d.sub.B: 1.85 g/cm.sup.3) having a perfluoropolyether skeleton and containing a vinyl group in a molecule, which was a one-component liquid material as a component B, 10 parts by mass (p.sub.C) of hydrophilic dry silica 1 (AEROSIL 200 available from Evonik Industries AG., bulk density d.sub.C: 0.05 g/cm.sup.3) having an untreated surface, which was a powdery filler as a component C, 1.5 parts by mass of 2,5-dimethyl-2,5-di(t-butylperoxy)hexane (PERHEXA 25B available from Nippon Oil & Fats Co., Ltd.), which was an organic peroxide as a crosslinker, and 4 parts by mass of triallyl isocyanurate (TAIC available from Nippon Kasei Chemical Co., Lit.), which was a cross-linking aid were mixed. The resultant mixture was then kneaded with an open roll. Thus, a fluorine rubber composition was prepared. This fluorine rubber composition was cross-linked, thereby producing a seal (AS-214 O-ring). The cross-linking of the fluorine rubber composition was performed by primary cross-linking through press-molding at 160? C. for 10 minutes and secondary cross-linking through holding for 4 hours in a geer oven set at 200? C. The seal obtained was taken as Example 1.

Example 2

[0044] A seal was produced in the same manner as in Example 1 except that 0.2 parts by mass (p.sub.C) of hydrophobic dry silica 2 (AEROSIL R972 available from Evonik Industries AG., bulk density d.sub.C: 0.05 g/cm.sup.3) having a surface treated with dimethyl dichlorosilane, which was a powdery filler as a component C, was mixed relative to 100 parts by mass for preparation of a fluorine rubber composition. The seal obtained was taken as Example 2.

Example 3

[0045] A seal was produced in the same manner as in Example 1 except that the dry silica 2 used in Example 2, which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 3.

Example 4

[0046] A seal was produced in the same manner as in Example 1 except that wet silica (CARPLEX #80 available from Evonik Industries AG., bulk density d.sub.C: 0.15 g/cm.sup.3), which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 4.

Example 5

[0047] A seal was produced in the same manner as in Example 3 except that 1 part by mass of a compound 1 (Fomblin Y lubricant available from Solvay S.A., density: 1.91 g/cm.sup.3) having a perfluoropolyether skeleton and containing no alkenyl group in a molecule, which was a liquid material as a component B, was further mixed relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Example 5.

[0048] The density d.sub.B of the component B was 1.88 g/cm.sup.3.

Example 6

[0049] A seal was produced in the same manner as in Example 3 except that 5 parts by mass of the compound 1 having a perfluoropolyether skeleton and containing a vinyl group in a molecule, which was the one-component liquid material as the component B, was mixed relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Example 6.

Example 7

[0050] A seal was produced in the same manner as in Example 3 except that 1 part by mass of a compound 2 (Krytox GPL oil 107 available from CHEMOURS Company, density: 1.90 g/cm.sup.3) having a perfluoropolyether skeleton and containing no alkenyl group in a molecule, which was a component B, was further mixed relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Example 7. The density d.sub.B of the component B was 1.88 g/cm.sup.3.

Example 8

[0051] A seal was produced in the same manner as in Example 5 except that 5 parts by mass of the compound 1 having a perfluoropolyether skeleton and containing no alkenyl group in a molecule, which was the liquid material as the component B, was mixed relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Example 8. The density d.sub.B of the component B was 1.90 g/cm.sup.3.

Example 9

[0052] A seal was produced in the same manner as in Example 1 except that 1 part by mass of a mixed material (SIFEL 3000 series X-71-369-N available from Shin-Etsu Chemical Co., Ltd.) obtained by mixing a compound 2 (d.sub.B: 1.90 g/cm.sup.3) having a perfluoropolyether skeleton and containing a vinyl group in a molecule, which was a one-component liquid material as a component B and silica (d.sub.C: 0.05 g/cm.sup.3) as a component C at a mass ratio of the component B: the component C=89:11, was mixed relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Example 9.

Example 10

[0053] A seal was produced in the same manner as in Example 1 except that a phenolic resin powder 1 (BELLPEARL R100 available from AIR WATER BELLPEARL INC., bulk density d.sub.C: 0.35 g/cm.sup.3), which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 10.

Example 11

[0054] A seal was produced in the same manner as in Example 1 except that a phenolic resin powder 2 (BELLPEARL R200 available from AIR WATER BELLPEARL INC., bulk density d.sub.C: 0.38 g/cm.sup.3), which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 11.

Example 12

[0055] A seal was produced in the same manner as in Example 1 except that a fluororesin (PVDF) powder (KYNAR MG15 available from Arkema S.A., bulk density d.sub.C: 0.32 g/cm.sup.3), which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 12.

Example 13

[0056] A seal was produced in the same manner as in Example 1 except that a polyetherether ketone (PEEK) resin powder (VESTAKEEP 2000UFP10 available from Daicel-Evonik Ltd., bulk density d.sub.C: 0.25 g/cm.sup.3), which was a powdery filler as a component C, was mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Example 13.

Comparative Example 1

[0057] A seal was produced in the same manner as in Example 1 except that components B and C were not mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 1.

Comparative Example 2

[0058] A seal was produced in the same manner as in Example 1 except that a component C was not mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 2.

Comparative Example 3

[0059] A seal was produced in the same manner as in Example 5 except that the compound 1 having a perfluoropolyether skeleton and containing a vinyl group in a molecule, which was the one-component liquid material as a component B, was not mixed for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 3.

Comparative Example 4

[0060] A seal was produced in the same manner as in Example 1 except that a phenolic resin powder 3 (BELLPEARL R800 available from AIR WATER BELLPEARL INC., bulk density d.sub.C: 0.60 g/cm.sup.3), which was a powdery filler, was mixed instead of component C for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 4.

Comparative Example 5

[0061] A seal was produced in the same manner as in Example 1 except that a fluororesin (PTFE) powder (LUBRON L-5 available from Daikin Industries, Ltd., bulk density d.sub.C: 0.61 g/cm.sup.3), which was a powdery filler, was mixed instead of component C for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 5.

Comparative Example 6

[0062] A seal was produced in the same manner as in Example 1 except that MT carbon black (Thermax N990 available from Cancarb Limited., bulk density d.sub.C: 0.66 g/cm.sup.3), which was a powdery filler, was mixed instead of component C for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 6.

Comparative Example 7

[0063] A seal was produced in the same manner as in Example 2 except that 1 part by mass of a compound 1 having a perfluoropolyether skeleton and containing no alkenyl group in a molecule, which was the liquid material used in Example 5, was mixed as a component B relative to 100 parts by mass of the component A for preparation of a fluorine rubber composition. The seal obtained was taken as Comparative Example 7. The density d.sub.B of the component B was 1.88 g/cm.sup.3.

TABLE-US-00001 TABLE 1 Examples 1 2 3 4 5 6 7 8 9 10 11 12 13 Compo- Hydrogen- 100 100 100 100 100 100 100 100 100 100 100 100 100 nent containing A fluorine rubber Compo- Compound 1 1 1 1 1 1 5 1 1 1 1 1 1 nent containing B alkenyl (p.sub.B) group Compound 2 0.89 containing alkenyl group Compound 1 1 5 containing no alkenyl group Compound 2 1 containing no alkenyl group Compo- Dry silica 1 10 nent Dry silica 2 0.2 10 10 10 10 10 C Wet silica 10 (p.sub.C) Silica 0.11 Phenolic 10 resin powder 1 Phenolic 10 resin powder 2 PVDF 10 resin powder PEEK 10 resin powder Cross- Organic 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 1.5 linker Peroxide Cross- TAIC 4 4 4 4 4 4 4 4 4 4 4 4 4 linking aid p.sub.C/p.sub.B 10 0.2 10 10 5 2 5 1.7 0.12 10 10 10 10 d.sub.B (g/cm.sup.3) 1.85 1.85 1.85 1.85 1.88 1.85 1.88 1.90 1.90 1.85 1.85 1.85 1.85 d.sub.C (g/cm.sup.3) 0.05 0.05 0.05 0.15 0.05 0.05 0.05 0.05 0.05 0.35 0.38 0.32 0.25 (p.sub.C/d.sub.C)/(p.sub.B/d.sub.B) 370 7.4 370 123 188 74.0 188 63.3 4.70 52.9 48.7 57.8 74.0 Plasma Mass 0.65 0.55 0.60 0.67 0.40 0.21 0.41 0.19 0.67 0.69 0.68 0.59 0.63 resistance reduction A A A A A A A A A A A A A rate (%) Presence or Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- Ab- absence sence sence sence sence sence sence sence sence sence sence sence sence sence (none) of particles Bleeding-out A A A A A A A A A A A A A (A.sub.CF/A.sub.CH for surface)/ 3.2 3.5 3.3 3.0 3.9 4.6 3.8 4.9 3.1 2.5 2.4 2.8 2.7 (A.sub.CF/A.sub.CH for cross- sectional surface) XPS evaluation A A A A A A A A A A A A A Hardness 73 57 72 71 71 69 71 68 57 64 62 63 64 Tensile Tensile 16.3 14.4 18.3 18.5 18.1 17.4 17.5 17.4 14.0 17.1 13.2 13.9 9.6 Properties strength at break (MPa) Elongation 150 350 180 180 180 190 180 190 340 180 180 310 240 at break (%) Tensile 6.0 1.4 5.9 6.1 5.8 5.5 5.7 5.4 1.4 4.8 3.9 2.6 4.2 stress at 100% elongation (MPa) Compression Set (%) 31 32 30 25 30 32 29 33 31 21 28 29 38

TABLE-US-00002 TABLE 2 Comparative Examples 1 2 3 4 5 6 7 Component A Hydrogen-containing 100 100 100 100 100 100 100 fluorine rubber Component B Compound 1 containing 1 1 1 1 1 (p.sub.B) alkenyl group Compound 2 containing alkenyl group Compound 1 containing 1 1 no alkenyl group Compound 2 containing no alkenyl group Component C Dry silica 2 10 0.2 (p.sub.C) Powdery filler Phenolic resin powder 3 10 (p.sub.C) PTFE resin powder 10 MT carbon black 10 Crosslinker Organic Peroxide 1.5 1.5 1.5 1.5 1.5 1.5 1.5 p.sub.C/P.sub.B 10 10 10 10 0.1 d.sub.B (g/cm.sup.3) 1.85 1.91 1.85 1.85 1.85 1.88 d.sub.C (g/cm.sup.3) 0.05 0.60 0.61 0.66 0.05 (p.sub.C/d.sub.C)/(P.sub.B/d.sub.B) 382 30.8 30.3 28.0 3.76 Plasma Mass reduction rate (%) 1.0 0.17 0.11 0.73 0.29 0.96 0.19 resistance B A A B A B A Presence or absence Absence Absence Absence Presence Presence Presence Absence of particles Bleeding-out B B A B A B (A.sub.CF/A.sub.CH for surface)/ 1.6 5.9 6.1 2.6 3.5 1.8 5.9 (A.sub.CF/A.sub.CH for cross-sectional surface) XPS evaluation B A A A A B A Hardness 57 57 71 62 59 63 57 Tensile Tensile strength at break (MPa) 14.7 13.3 18.1 11.3 13.9 18.9 13.8 Properties Elongation at break (%) 340 330 170 170 320 190 350 Tensile stress at 100% 1.4 1.3 5.8 3.1 1.8 4.3 1.4 elongation (MPa) Compression Set (%) 30 33 31 38 29 29 33

[0064] (Test Method)

[0065] <Plasma Resistance>

[0066] Each of Examples 1 to 13 and Comparative Examples 1 to 7 was placed in a compact plasma etching unit (manufactured by SHINKO SEIKI CO., LTD.), and irradiated with 02 plasma for 30 minutes to be exposed to the O.sub.2 plasma. A mass reduction rate between before and after the exposure was then determined. A mass reduction rate of less than 0.7% was evaluated as A. A mass reduction rate of 0.7% or more was evaluated as B. The presence or absence of deposition of particles on a surface of the seal after the exposure to the 02 plasma was visually checked. In the irradiation with O.sub.2 plasma, a high-frequency power supply of 1,500 W was used. For a reactant gas, O.sub.2 and CF.sub.4 were used, and the flow rate thereof was 50:1. The pressure was 100 Pa.

[0067] <Presence or Absence of Bleeding-out of Component B>

[0068] Each of Examples 1 to 13 and Comparative Examples 2 to 7 was pressed on a black acrylic board. Then, a case where a transfer mark of the seal due to the component B was not recognized was evaluated as A, and a case where a transfer mark of the seal due to the component B was recognized was evaluated as B.

[0069] <XPS Measurement>

[0070] In a C1s peak measured during irradiation of each of a surface and a cross-sectional surface of the seal of each of Examples 1 to 13 and Comparative Examples 1 to 7 with an X ray by X-ray photoelectron spectroscopy, a peak area A.sub.CH derived from a CH bond at 282 eV to 288 eV and a peak area A.sub.CF derived from a CF bond at 288 eV to 296 eV were measured. Then, a (A.sub.CF/A.sub.CH during irradiation of the surface of the seal with an X ray)/(A.sub.CF/A.sub.CH during irradiation of the cross-sectional surface of the seal at a position farthest from the surface of the seal with an X ray) was calculated. A ratio of 2 or more was evaluated as A. A ratio of less than 2 was evaluated as B. Herein, the position in the cross-sectional surface of the seal, farthest from the surface of the seal is a center of a circular cross-sectional surface of an O-ring which is the seal.

[0071] In the X-ray photoelectron spectroscopy, data was shifted by charging. Thus, based on XPS data of fluorine rubber (Viton A available from Du Pont Elastomers) recorded on NIST X-ray Photoelectron Spectroscopy Database (https://srdata.nist.gov/xps/Default.aspx), a peak of F1s was matched with 688.80, and in the C1s peak, the peak area A.sub.CH derived from a CH bond at 282 eV to 288 eV and the peak area A.sub.CF derived from a CF bond at 288 eV to 296 eV were determined.

[0072] <Hardness>

[0073] For the cross-linked rubber formed using each of Examples 1 to 13 and Comparative Examples 1 to 7, the hardness was measured with a type A durometer in accordance with JIS K6253-3: 2012.

[0074] <Tensile Properties>

[0075] For the cross-linked rubber formed using each of Examples 1 to 13 and Comparative Examples 1 to 7, a tensile test was performed at a standard test temperature using a dumbbell-shaped No. 3 test piece with a thickness of 2 mm in accordance with JIS K6251: 2017 to measure the tensile strength at break, the elongation at break, and the tensile stress at 100% elongation.

[0076] <Compression Set>

[0077] Each of Examples 1 to 13 and Comparative Examples 1 to 7 was cut into a half to obtain a test piece. Then, the compression set of the test piece was measured at a test temperature of (200?2?) C for a test time of 72 hours in accordance with JIS K6262: 2013.

[0078] (Test Results)

[0079] The test results are shown in Tables 1 and 2. As can be seen from Tables 1 and 2, in Examples 1 to 13, both excellent plasma resistance caused by a small mass reduction rate and reduction of bleeding-out of the component B were achieved, and in Comparative Examples 1 to 7, any one of them was inferior.

INDUSTRIAL APPLICABILITY

[0080] The present invention is useful in the technical field of a fluorine rubber composition and a rubber molded article formed using the same.