Method of recycling carbon fiber prepreg waste and transparent thermoplastic waste

Abstract

The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste includes shredding of a volume of transparent thermoplastic waste and a volume of carbon fiber prepreg waste, where the carbon fiber prepreg waste includes a colored backing film. The colored backing film may have a plurality of colors associated therewith, yielding a mixture of multi-colored shreds. A mold is filled with the shredded volume of transparent thermoplastic waste, and the mold is inserted and compressed in a hot press. The shredded volume of transparent thermoplastic waste is cured in the hot press to produce a transparent sheet. The shredded volume of carbon fiber prepreg waste is then heated, such as, for example, with hot air, and then spread on the transparent sheet. The heated, shredded volume of carbon fiber prepreg waste and the transparent sheet are hot pressed to form a colored sheet with a transparent protective layer.

Claims

1. A method of recycling carbon fiber prepreg waste and transparent thermoplastic waste, comprising the steps of: shredding a volume of transparent thermoplastic waste; shredding a volume of carbon fiber prepreg waste, wherein the carbon fiber prepreg waste includes a colored backing film; filling a mold with the shredded volume of transparent thermoplastic waste; inserting and compressing the mold in a hot press; curing the shredded volume of transparent thermoplastic waste in the hot press to produce a transparent sheet; heating the shredded volume of carbon fiber prepreg waste; spreading the heated, shredded volume of carbon fiber prepreg waste on the transparent sheet; and hot pressing the heated, shredded volume of carbon fiber prepreg waste and the transparent sheet to form a colored sheet with a transparent layer.

2. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 1, wherein the colored backing film has a plurality of colors.

3. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 1, wherein the step of filling the mold with the shredded volume of transparent thermoplastic waste comprises filling a closed mold with the shredded volume of transparent thermoplastic waste.

4. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 1, wherein the step of heating the shredded volume of carbon fiber prepreg waste comprises heating the shredded volume of carbon fiber prepreg waste with hot air.

5. A method of recycling carbon fiber prepreg waste and transparent thermoplastic waste, comprising the steps of: shredding a volume of transparent thermoplastic waste; crushing hard material waste to produce waste particles, wherein the hard material waste has at least one color associated therewith; shredding a volume of carbon fiber prepreg waste; filling a mold with the shredded volume of transparent thermoplastic waste; inserting and compressing the mold in a hot press; curing the shredded volume of transparent thermoplastic waste in the hot press to produce a transparent sheet; spreading the waste particles on the transparent sheet; heating the shredded volume of carbon fiber prepreg waste; spreading the heated, shredded volume of carbon fiber prepreg waste on the waste particles on the transparent sheet; and hot pressing the heated, shredded volume of carbon fiber prepreg waste, the waste particles and the transparent sheet to form a colored sheet with a transparent layer.

6. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 5, wherein the step of filling the mold with the shredded volume of carbon fiber prepreg waste comprises filling a closed mold with the shredded volume of carbon fiber prepreg waste.

7. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 5, wherein the hard material waste is selected from the group consisting of ceramic, marble, stone, colored glass and granite.

8. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 5, wherein the step of heating the shredded volume of carbon fiber prepreg waste comprises heating the shredded volume of carbon fiber prepreg waste with hot air.

9. A method of recycling carbon fiber prepreg waste and transparent thermoplastic waste, comprising the steps of: shredding a volume of transparent thermoplastic waste; removing a colored backing film from a volume of carbon fiber prepreg waste; shredding the volume of carbon fiber prepreg waste; shredding the colored backing film; curing the volume of carbon fiber prepreg waste in an autoclave to produce a cured sheet; filling a mold with the shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet, wherein the shredded colored backing film is sandwiched between the shredded volume of transparent thermoplastic waste and the cured sheet; inserting and compressing the mold in a hot press; and curing the shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet in the hot press to produce a colored sheet with a transparent layer.

10. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 9, wherein the colored backing film has a plurality of colors.

11. The method of recycling carbon fiber prepreg waste and transparent thermoplastic waste as recited in claim 9, wherein the step of filling the mold with the shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet comprises filling a closed mold with the shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet.

Description

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(1) A method of recycling carbon fiber prepreg waste includes recycling carbon fiber prepreg waste, such as offcuts, scrap, defective material and the like, into colored, non-structural elements, such as flat panels. Uncured carbon fiber prepreg waste is first collected. The carbon fiber prepreg waste can include the backing film associated with the carbon fiber prepreg (typically in the form of a colored polyethylene layer). The uncured carbon fiber prepreg waste is then shredded and inserted into either an open or a closed mold. The mold is then inserted into a hot press, where the shredded carbon fiber prepreg waste is cured under selected temperature and pressure for a selected period of time, dependent upon the particular volume of waste and the desired recycled product. Alternatively, the shredded carbon fiber prepreg waste may be rolled in a hot metallic roller to produce the recycled panel. As a further alternative, the shredded carbon fiber prepreg waste may be extruded in a hot melt extruder to produce a recycled element. The recycled prepreg waste can be used as sustainable non-structural elements for subsidiary applications relating to construction or aerospace, for example.

(2) In an example of hot press curing using an open mold, an open square mold with 25 inch sides was filled with shredded carbon fiber prepreg waste (including the associated colored polyethylene backing material). The shredded carbon fiber prepreg waste was held in the mold between two aluminum foil layers which had been coated with a thin industrial wax, which is commonly used as a mold release agent. The hot press was heated for 30 minutes to a temperature of 100 F. to provide ample time for the mold to absorb the heat. Then, the mold was heated in the press at 270 F., under a pressure of 1500 lbs., for a period of 30 minutes. After 30 minutes, the pressure was released and the hot press heater was switched off. The mold was removed from the hot press and left to cool to room temperature. The aluminum foil films were removed, yielding a colored panel of recycled carbon fiber prepreg waste.

(3) As noted above, alternatively, a closed mold may be used. For example, a typical two-piece, metallic mold can be used to produce a recycled product having a desired size and shape. The shredded carbon fiber prepreg waste can be added to the mold and the mold can then be inserted in the hot press. The temperature, pressure and time can be selected dependent upon the volume of waste used, as well as the particular recycled element being produced.

(4) As a further alternative, as noted above, the shredded carbon fiber prepreg waste can be rolled using a hot metallic roller. Again, the temperature, pressure and time can be selected dependent upon the volume and type of waste used, as well as the particular dimensions of the recycled panel being produced. The roller would allow for production of a continuous sheet or the like. Additionally, a recycled element can be produced by forcing the shredded carbon fiber prepreg waste into a hot melt extruder. Here, the temperature of the hot melt extruder's heaters may be selected, as well as the pressure produced by the extruder screw(s). The temperature and pressure can be selected dependent upon the volume and type of waste used, as well as the particular size and shape of the recycled element being produced.

(5) In an alternative method of recycling carbon fiber prepreg waste and transparent thermoplastic waste, both a volume of transparent thermoplastic waste and a volume of carbon fiber prepreg waste are shredded. The carbon fiber prepreg waste can include a colored backing film. The transparent thermoplastic waste may be any suitable type of transparent thermoplastic waste material, such as polyethylene terephthalate (PET) or the like. The colored backing film may have a plurality of colors associated therewith, yielding a mixture of multi-colored shreds. A mold is filled with the shredded volume of transparent thermoplastic waste, and the mold is inserted and compressed in a hot press. The mold may be a closed mold. The shredded volume of transparent thermoplastic waste is cured in the hot press to produce a transparent sheet. Hot pressing may be performed in a temperature controlled system, with the selected parameters being dependent upon the particular choice of the transparent thermoplastic material. As an alternative, injection molding may be used. Depending on the desired thickness of the transparent sheet, the volume of initial transparent thermoplastic material may be adjusted.

(6) The shredded volume of carbon fiber prepreg waste is then heated, such as, for example, with hot air, and then spread on the transparent sheet. For example, the shredded volume of carbon fiber prepreg waste may be heated with hot air in a hot air oven or chamber. The hot air is applied to heat the carbon fiber prepreg waste to a temperature around the epoxy temperature used to produce the carbon fiber prepreg. The heated, shredded volume of carbon fiber prepreg waste and the transparent sheet are hot pressed to form a colored sheet with a transparent protective layer. The temperature, pressure and curing time of the hot pressing are variable, dependent upon the desired material properties of the final product.

(7) In an alternative embodiment, rather than providing a colored backing film, a hard material waste is crushed to produce hard waste particles having at least one color associated therewith. For example, the hard material waste may be waste ceramic, waste marble, waste stone, waste colored glass, waste granite or the like. A volume of transparent thermoplastic waste and a volume of carbon fiber prepreg waste are both separately shredded, similar to the previous embodiment, and a mold is filled with the shredded volume of transparent thermoplastic waste. The mold may be a closed mold. The transparent thermoplastic waste may be any suitable type of transparent thermoplastic waste material, such as polyethylene terephthalate (PET) or the like.

(8) The mold is inserted and compressed in a hot press, and the shredded volume of transparent thermoplastic waste is cured in the hot press to produce a transparent sheet. Hot pressing may be performed in a temperature controlled system, with the selected parameters being dependent upon the particular choice of the transparent thermoplastic material. As an alternative, injection molding may be used. Depending on the desired thickness of the transparent sheet, the volume of initial transparent thermoplastic material may be adjusted.

(9) The waste particles are spread on the transparent sheet and, separately, the shredded volume of carbon fiber prepreg waste is heated, such as with hot air, for example. For example, the shredded volume of carbon fiber prepreg waste may be heated with hot air in a hot air oven or chamber. The hot air is applied to heat the carbon fiber prepreg waste to a temperature around the epoxy temperature used to produce the carbon fiber prepreg. The heated, shredded volume of carbon fiber prepreg waste is then spread on the waste particles on the transparent sheet. The heated, shredded volume of carbon fiber prepreg waste, the waste particles and the transparent sheet are hot pressed to form a colored sheet with a transparent protective layer. The temperature, pressure and curing time of the hot pressing are variable, dependent upon the desired material properties of the final product.

(10) In a further alternative embodiment, a colored backing film is removed from a volume of carbon fiber prepreg waste, and the colored backing film and the volume of carbon fiber prepreg waste are each shredded separately. The colored backing film may have a plurality of colors associated therewith, yielding a mixture of multi-colored shreds. A volume of transparent thermoplastic waste is also shredded. The transparent thermoplastic waste may be any suitable type of transparent thermoplastic waste material, such as polyethylene terephthalate (PET) or the like. The volume of carbon fiber prepreg waste is cured in an autoclave to produce a cured sheet, which is left to cool.

(11) A mold is filled with the shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet, such that the shredded colored backing film is sandwiched between the shredded volume of transparent thermoplastic waste and the cured sheet. The mold may be a closed mold. The mold is inserted and compressed in a hot press. The shredded volume of transparent thermoplastic waste, the shredded colored backing film and the cured sheet are cured in the hot press to produce a colored sheet with a transparent layer.

(12) It is to be understood that the method of recycling carbon fiber prepreg waste and transparent thermoplastic waste is not limited to the specific embodiments described above, but encompasses any and all embodiments within the scope of the generic language of the following claims enabled by the embodiments described herein, or otherwise shown in the drawings or described above in terms sufficient to enable one of ordinary skill in the art to make and use the claimed subject matter.