DIFFERENTIATED WIND BLADE FINISHING SYSTEM

Abstract

A wind blade finishing system is provided that is robust, cost effective, and has low volatile organic compounds while reducing overall process time. The wind blade finishing system combines a gel coat, putty, and top coat and has weather resistant properties, and takes the place of processes for producing turbine wind blades covered by gel coat, contouring putty, pore filler, top coat, and leading-edge coating. The finishing system significantly reduces the need for sanding before applying the top coat, and in turn up to 11 hours of time associated with the sanding process, as well as preventing pin holes from showing through the surface of the wind blade without the need of a secondary product/operation thus eliminating pore filler, associated surface preparation and rework. The finishing system reduces overall system cure time, currently averaging 12 hours, and also reduces the number of products/steps needed to a minimum number.

Claims

1. A finishing system for surfaces of a wind turbine blade consisting of: a gel coat; a putty; and a top coat.

2. The finishing system of claim 1 wherein the wind turbine blade comprises glass fiber fabric or nonwoven and epoxy resin/vinyl ester resin.

3. The finishing system of claim 1 wherein the surfaces are whole surfaces especially leading edges of the turbine wind blades.

4. The finishing system of claim 1 wherein the gel coat has a pull-off adhesion strength of 7.9 MPa per ASTM D-4541.

5. The finishing system of claim 1 wherein the gel coat has a gel time of 40 minutes per ASTM D3056.

6. The finishing system of claim 1 wherein the gel coat has a tack free time of 70 minutes.

7. The finishing system of claim 1 wherein the putty has a pull-off strength of 6.9 MPa per ASTM D-4541.

8. The finishing system of claim 1 wherein the putty has a gel time of 5-7 minutes per ASTM D3056.

9. The finishing system of claim 1 wherein the putty has a cure time/minimum waiting time to initiate sanding of 30 minutes.

10. A process of using the finishing system of claim 1 comprising: applying the gel coat to a mold substrate; laying up and infusing the resin with woven fiber cloth to form a shell with an outer surface defining a wind turbine blade; applying the putty to the outer uneven surfaces to form an even surface; sanding the cured putty surface to yield a smooth finished sanded surface; and applying the top coat to the blade surface.

11. The process of claim 10 wherein the wind turbine blade is at least 23 meters in length.

12. The process of claim 10 wherein all the steps are completed in less than 25 hours.

13. The process of claim 10 wherein the top coat is substantially free of pin holes.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] The present invention is further detailed with respect to the following drawings. These figures are not intended to limit the scope of the present invention but rather illustrate certain attributes thereof.

[0009] FIG. 1A shows an existing progression of process steps for wind turbine blade finishing without a gel coat;

[0010] FIG. 1B shows an existing progression of process steps for wind turbine blade finishing with a gel coat;

[0011] FIG. 1C shows the progression of a reduced number of process steps for turbine wind blade finishing with a gel coat of an embodiment of the inventive wind turbine blade finishing system;

[0012] FIGS. 2A-2C illustrate a mandrel test of a gel coat of a first and second competitor and that of an embodiment of the gel coat component of the current invention, respectively; and

[0013] FIGS. 3A and 3B show graphs of UV stability for an embodiment of the inventive top coat versus a first and a second competitor top coat, respectively.

DETAILED DESCRIPTION OF THE INVENTION

[0014] The present invention has utility as a wind blade finishing system that is robust, cost effective, and is low in volatile organic compounds (VOC), while also reducing overall process time. Embodiments of the inventive differentiated wind blade finishing system combine a gel coat, putty and top coat and have excellent weather resistant properties, and takes the place of processes for producing turbine wind blades covered by gel coat, contouring putty, pore filler, top coat, and leading-edge coating. Embodiments of the inventive differentiated finishing system, minimize the need of sanding before applying the top coat, and in turn up to 11 hours of time associated with the sanding process, as well as preventing pin holes from showing through the surface of the wind blade without the need of a secondary product/operation thus eliminating pore filler, associated surface preparation and rework. Embodiments of the inventive differentiated finishing system reduce overall system cure time and process residence time, currently averaging 12 hours, and also reduces the number of products/steps needed to a minimum number. Overall, embodiments of the inventive differentiated wind blade finishing system reduce overall process times by over 25% by reducing the number of processing steps to applying the gel coat to a mold substrate, the laying up and infusing the resin with woven fiber cloth to form a shell with an outer surface defining a wind turbine blade. The putty is then applied to the outer uneven surfaces to form an even surface. The cured putty is then sanded to yield a smooth finished sanded surface. Finally, a top coat is applied to the blade surface. The process is particularly well suited for use with a wind turbine blade is at least 23 meters in length. The aforementioned steps can be completed in less than 25 hours for such a wind turbine blade with approximately 11 hours of surface preparation and 12 hours of curing time; this in contrast to a conventional process that typically takes about 33 hours for such a blade.

[0015] As used herein, the term substantially free with respect to pin holes, is defined as less than 0.1 total surface area percent and in some instances less than 0.05 total area percent, as measured with a telecentric laser scanning system operating in a bright field rastering mode.

[0016] FIGS. 1A and 1B show the process steps currently involved in wind blade manufacturing for blade finishing without a gel coat and with a gel coat, respectively. FIG. 1C shows the reduction in production steps with the inventive wind blade finishing system that eliminates two or more-time consuming sanding steps. Furthermore, embodiments of the inventive differentiated finishing system address leading edge abrasion concerns either in the primary coating or via an add-on secondary coating. Table 1 list the drawbacks associated with existing blade finishing systems.

TABLE-US-00001 TABLE 1 Process step drawbacks Process Drawbacks Sanding Consuming time, Consumables, 34% of total process True Hours spent on surface preparation Putty Most time-consuming steps are the putty process. Application Application followed by curing and sanding to obtain smooth surface finish Pin Holes Pin holes are a process and chemistry related issue, Hard to see the pores, requires pore filler which adds a sanding step Pore filler Additional costs and time, need of additional sanding, process Difficult process, sometimes ineffective and doesn't fill the pores Cure time Time consuming step, some chemistries are sensitive to environmental conditions like humidity, temperature etc., It decreases output, may need heat cure which add additional processing cost. This curing step consuming 36% of true total process hours Multiple Products Multiple components increase application time, needed in the additional material costs, time and man power finishing process Durability- Necessity of leading edge protection coating which Abrasion/Ero- increase costs, processing time and manpower sion Resistance Weather ability Poor UV stability induces degradation of top coat and decreased abrasion resistance. Multiple repairing processes need to be performed - hence increased maintenance cost

[0017] Embodiments of the inventive finishing system have only three primary components gel coat, putty, and a top coat as opposed to conventional finishing systems that also have a pore filler and a leading-edge coating. The tackiness of the inventive gel coat even after more than 1 hours helps to hold fabrics while laying up the wind blade structure, which eases the fabrication process. Furthermore, embodiments of the transparent and flexible gel coat increase the durability of the applied coating under dynamic load and stress during service conditions of wind blades produced with the inventive finishing system. In addition, sanding/surface preparation is may not require on gel coat applied areas prior to the topcoat application. Embodiments of the inventive rapid curing putty, which can be sanded after 30 minutes without clogging reduces process time significantly. The Quick dry to touch property and long pot life of the inventive top coat also provides for a reduction in process time. The superior abrasion resistance of embodiments of the top coat also serve as a leading-edge coating for the turbine blades.

[0018] The reduced number of coating components (gel coat, putty, and top coat) in embodiments of the inventive differentiated wind blade finishing system versus currently available coating systems that have five or more coating components (gel coat, putty, pore filler, leading edge coat, base coat, etc.) result in reduced processing steps associated surface preparations required before and after the application of additional components including gel coat, pore filler, leading edge coat, etc. In fact, market segment focus (MSF) findings have revealed that, almost 34% of total process time consumed by surface preparation of wind turbine blades occurred during the coating process, which includes putty application followed by sanding, surface preparation prior to the coating, sanding after pore filler application etc. Elimination of just the sanding process saves almost 11 hours of process time per blade. The elimination of the sanding step in the present invention is made possible using a transparent gel coat as one of the components and eliminating pore filler component from present invention. Removing pore filler from the present invention will be managed by addressing pin holes with a low viscous top coat. Furthermore, proper adhesion of coating components may be achieved without any surface preparation.

[0019] A primary concern during turbine wind blade manufacturing is the generation of pinholes during the coating process. Currently, blade manufacturers eliminate these pin holes using pore fillers as a finishing component which requires an additional sanding process for a better result, but this process is sometimes inefficient to cover the pinholes and introduces additional cost to their process. Embodiments of the present invention eliminate pore filler which results in the elimination of additional sanding time and in turn over all processing time. The features of pore filler have been incorporated into the topcoat of the inventive differentiated wind blade finishing system. The inventive topcoat covers pin holes and eliminates the sanding process and the associated additional process time.

[0020] Embodiments of the inventive gel coat provide improved flexibility and mechanical properties as compared to existing gel coats. Turbine wind blades are generally manufactured out of fiber reinforced epoxy/unsaturated polymer matrices; glass fiber reinforced plastics (GFRP) that are expected to last at least 20 years in a challenging service environment. Generally, the length of the blade is around 60 meters long and to enhance the efficiency and energy yield of wind turbines, the length of the blades is being increased to 80-90 meters. The longer blades experience more deflection across the length of the blade hence increasing dynamic load and stress throughout the blade length. This adversely affects the durability of coating components and hence the protection of blades will be damaged. In order to enhance the life of coating components, flexibility of coating components especially the gel coat component has been improved in embodiments of the inventive differentiated wind blade finishing system. FIGS. 2A-2C illustrate a mandrel test of a gel coat of a first and second competitor and that of an embodiment of the gel coat component of current invention which reveals the flexibility of gel coat of current invention that is much better than the competitor grades. As is readily seen in FIGS. 2A and 2B, the first and second competitor grades cracked during the mandrel test, and the gel coat of current invention did not crack as shown in FIG. 2C.

[0021] Certain embodiments of the inventive putty have rapid curing characteristics under room temperature conditions. The rapid curing putty can be sanded after 30 minutes without clogging which reduces process time significantly as against the competitor, which can be sanded only after 120 minutes.

[0022] Embodiments of the inventive top coat provide excellent UV stability under QUV-B conditions and reduce maintenance costs associated with wind turbine blades having the inventive top coat. FIGS. 3A and 3B show graphs of UV stability for an embodiment of the inventive top coat versus a first and a second competitor top coat, respectively.

[0023] It is to be understood that in instances where a range of values are provided that the range is intended to encompass not only the end point values of the range but also intermediate values of the range as explicitly being included within the range and varying by the last significant figure of the range. By way of example, a recited range of from 1 to 4 is intended to include 1-2, 1-3, 2-4, 3-4, and 1-4.

EXAMPLES

Example 1

[0024] A specific embodiment of the inventive differentiated wind blade finishing system has three components a gel coat, putty, and a top coat. The properties of these finishing components are depicted in tables 2A, 2B, and 2C below.

TABLE-US-00002 TABLE 2A Gel coat properties Properties of Gel coat Test Test Standard Current invention Pull-off adhesion ASTM D 4541 7.9 MPa Strength Mandrel Bend Test ASTM D 522, 12 mm cylinder No cracks Gel Time ASTM D3056 40 minute Tack Free Time Manual 70 minute

TABLE-US-00003 TABLE 2B Putty properties Properties of Putty Test Test Standard Current invention Mandrel Bend Test (RT) ASTM D 522, 12 mm No cracking cylinder Mandrel Bend Test ASTM D 522, 63 mm No cracking (40 C.) Pull-off Strength ASTM D 4541 6.9 MPa Condensing water ASTM D4585 340 hrs No blistering Environment Gel time ASTM D3056 5-7 min Cure Time/Minimum 30 min waiting time to initiate sanding

TABLE-US-00004 TABLE 2C Top coat properties Properties of Top coat Test Parameter/Standards Current invention Mandrel Bend Test ASTM D 522, 12 mm cylinder No cracks Adhesion X-Cut ASTM D3359 Method A 5A Gloss 60 Degrees angle, ISO 2813 45 Taber abrasion CS 10 Wheel, 1000 grs weight, 0.08 g (Weight loss) 2000 cycles ASTM D 4060 Pot life 80 min Dry to touch 65 min

[0025] Patent documents and publications mentioned in the specification are indicative of the levels of those skilled in the art to which the invention pertains. These documents and publications are incorporated herein by reference to the same extent as if each individual document or publication was specifically and individually incorporated herein by reference.