Pusher pump resistant to corrosion by molten aluminum and having an improved flow profile

Abstract

A bubble pump having a steel tube pump body having an interior formed from a ceramic material that resists attack by molten metal. The pump further has a nitrogen supply line attached to a lower portion of the pump body. The pump body and nitrogen supply line are covered with a ceramic cloth material that resists attack by molten metal. The pump also includes a discharge head attached to the top of the pump body. The discharge head is formed of a cast ceramic material that resists attack by molten metal and includes a distribution chamber therein which has an ellipsoidal dome shape with a generally flat bottom and an ellipsoidal top. The discharge head also includes two discharge nozzles which have a square cross section. These features provide the inventive pump with extended service life and reduced discharge turbulence of the molten metal.

Claims

1. A bubble pump having: a pump body comprising a vertical steel tube configured to allow for the transport of molten metal there through; said pump body having an interior formed from a non-wetting ceramic material cast on a carbon steel tube, the ceramic material being resistant to attack by molten metal; a nitrogen supply line attached to a lower portion of said pump body; said nitrogen supply line and said pump body communicating so as to allow the flow of nitrogen from said nitrogen supply line into the interior of said pump body; and a discharge head attached to the top of said pump body; said discharge head communicating with said pump body so as to allow for transport of molten metal and nitrogen from said pump body, into and then out of said discharge head; wherein said distribution chamber has an ellipsoidal dome shape with a generally flat bottom and an ellipsoidal top; wherein the ellipsoidal dome shape has a horizontal extent and a vertical extent, the horizontal extent being greater than the vertical extent, said discharge head further contains two discharge nozzles in communication with said distribution chamber to allow for the flow of molten metal and nitrogen from said distribution chamber through said discharge nozzles and out of said bubble pump.

2. The bubble pump of claim 1, wherein said ceramic material that resists attack by molten metal is selected from the group consisting of alumina, magnesia, silicate, silicon carbide, graphite, and the mixtures of these ceramic materials.

3. The bubble pump of claim 1, wherein said pump body is wrapped in one or more layers of ceramic cloth to provide the exterior of said pump body with flexible resistance to attack by molten metal.

4. The bubble pump of claim 3, wherein said nitrogen supply line is also wrapped in one or more layers of ceramic cloth to provide the exterior of said pump body with flexible resistance to attack by molten metal.

5. The bubble pump of claim 4, wherein said ceramic cloth is formed of a material that resists attack by molten metal selected from the group consisting of alumina, magnesia, silicate, silicon carbide, graphite, and the mixtures of these ceramic materials.

6. The bubble pump of claim 1, wherein said discharge head is formed of a cast ceramic material that resists attack by molten metal.

7. The bubble pump of claim 6, wherein said cast ceramic material that resists attack by molten metal is selected from the group consisting of alumina, magnesia, silicate, silicon carbide, graphite, and the mixtures of these ceramic materials.

8. The bubble pump of claim 1, wherein said discharge head contains said distribution chamber therein, said distribution chamber in communication with said pump body to allow for the flow of molten metal and nitrogen from said pump body through said distribution chamber.

9. The bubble pump of claim 1, wherein discharge nozzles are located adjacent opposite ends of the horizontal extent and have a square cross section.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a depiction of the prior art pusher pump;

(2) FIG. 2 is a depiction of a cross section of an embodiment of the inventive pump body;

(3) FIG. 3 is a depiction of an embodiment of the preferred discharge head for the inventive pump; and

(4) FIG. 4 is a depiction (not to scale) of a cross section of a preferred embodiment of a pump of the instant invention.

DETAILED DESCRIPTION OF THE INVENTION

(5) Gas lift or Bubble pumps use the artificial lift technique of raising a fluid such as water, oil or even molten metal by introducing bubbles of compressed air, water vapor, nitrogen, etc. into the outlet tube. This has the effect of reducing the hydrostatic pressure in the outlet of the tube vs. the hydrostatic pressure at the inlet side of the tube. The present inventors have sought to improve the pump performance as far as providing more directed melt flow and eliminating the spitting issue, and also significantly increasing the service life of the pumps. Changes in pump design and the incorporation of a cast refractory lining are key factors in the improved inventive pusher pump.

(6) FIG. 1 is a depiction of the prior art pusher pump. The pump includes a pump body 1 which consists of a carbon steel pipe or tube. The pump also includes outflow nozzles 2a, 2b. There is a nitrogen supply line 3 which supplies nitrogen bubbles to the pump body 1. A support bar 5 is connected to the nitrogen supply line 3 and pump body 1. The nitrogen supply line 3 has a connector 3 which attached to the external supply of nitrogen. In operation the nitrogen bubbles rise in pump body 1, causing an upward flow of molten metal. The molten metal enters the open bottom 4 of the tubular pump body and is ejected from outflow nozzles 2a, 2b. Since the molten metal is taken from below the surface of the melt, it does not contain floating dross and other contaminants. The two nozzles 2a, 2b direct clean fresh metal to either side of the steel sheet as it is passed through the metal bath and thereby coated.

(7) This prior art pump is subject to corrosion and deterioration in the molten metal, particularly where the metal is agitated by bubbling nitrogen and flow eddies. These prior art pusher pumps, made from carbon steel, last only up to 24 hours of constant operation and develop holes in the discharge head. Changing dross moving pumps during the production run leads to disruption in production and contamination of molten metal surface.

(8) To combat this corrosion and deterioration, the present inventors have formed an in-situ cast ceramic liner inside the inventive pump body. FIG. 2 is a depiction of a cross section of the inventive pump body 1. The inner cast layer 8 is formed of a ceramic material that is non-wetting to molten metal and can withstand the temperatures of the molten metal. The material is cast on the interior of a carbon steel shell tube 6. The protective inner cast layer lining 8 is preferably made of materials selected from the group consisting of alumina, magnesia, silicate, silicon carbide, graphite, and the mixtures of these ceramic materials.

(9) Further, the outside of the carbon steel tube 6 is covered with a flexible ceramic cloth wrap 7 to extend life of the steel. The wrap 7 is superior to the standard ceramic lining outside the steel because it does not crack during use. It should be noted that the nitrogen supply tube is formed of carbon steel and is also covered in the wrap 7. Further, any steel support brackets should also be covered in the wrap 7.

(10) In addition to improved corrosion resistance from the cast ceramic liner 8 and the ceramic wrap 7, the inventive bubble pump has improved flow characteristic over the prior art pump. FIG. 3 is a depiction of the preferred discharge head 10 for the inventive pump 1. The head 10 is cast from the same class of ceramic material that is non-wetting to molten metal and can withstand the temperatures of the molten metal. It can be the same material as that in the ceramic liner of the pump body, or may be a different material if conditions make this advantageous. Further, it may be advantageous in some instances to cast metal support structures within the ceramic head 10 to provide enhanced mechanical strength and durability. It should be noted that the shape within the block of ceramic is actually the open hollow area shape cast into the block for fluid flow.

(11) Within the head is a distribution chamber 9 having an ellipsoidal dome shape with a generally flat bottom and an ellipsoidal top. This extended internal dome concept was introduced to accommodate the gas volume expansion and provide higher and more stable discharge flow than the prior art carbon steel pusher pump. Also cast into the discharge head 10 are two discharge outlets 2a, 2b. The square discharge nozzle design was introduced to provide more laminar discharge without spitting. As can be seen in FIG. 1, the prior art conventional discharge design has round nozzles 2a, 2b. The efficiency of square nozzles 2a, 2b was evaluated initially by water modeling, and then plant trials confirmed that this design provided much more directed melt flow and eliminated the spitting issues of the prior art.

(12) Finally, FIG. 4 is a depiction (not to scale) of a cross section of a pump of the instant invention. Specifically shown are all of the inventive features of the present invention. First there is an interior 11 surrounded by the cast ceramic liner 8 within the carbon steel shell tube 6 of the pump body 1. Then there is the external ceramic cloth 7 wrapping the carbon steel shell tube 6 of the pump body 1 and the carbon steel nitrogen supply line 3. Next there is the cast ceramic discharge head 10 which incorporates the inventive distribution chamber 9 which has an ellipsoidal dome shape with a generally flat bottom and an ellipsoidal top. Finally there are the square discharge nozzles 2a, 2b introduced to provide more laminar discharge without spitting.

(13) All of these inventive features provide the inventive pump with extended service life between failures of the pusher pump and reduced discharge turbulence in the molten metal.