Abrasive tip blade manufacture methods

Abstract

A method is provided for manufacturing a blade. The blade comprises an airfoil (100) having: a root end and a tip (106); a metallic substrate (102) along at least a portion of the airfoil; and an anodized layer (154). The method comprises roughening the tip to form protrusions (158; 402) and anodizing to form the anodized layer so that the protrusions form an abrasive (156; 400).

Claims

1. A method for manufacturing a blade, the blade comprising: an airfoil having: a root end and a tip; a metallic substrate along at least a portion of the airfoil; and an anodized layer; the method comprising: roughening the tip to form protrusions with characteristic heights of 0.025 mm to 0.25 mm, the roughening comprising raising a burr, the raising the burr comprising indenting; and anodizing to form the anodized layer so that the protrusions form an abrasive.

2. The method of claim 1 wherein: the anodized layer is along surfaces of the airfoil beyond the tip.

3. The method of claim 1 wherein: the raising the burr further comprises drawing.

4. The method of claim 1 wherein: the raising the burr comprises forming an intersecting pattern.

5. The method of claim 1 wherein: the raising the burr comprises forming regular pattern.

6. The method of claim 1 wherein: the burr comprises a plurality of burrs with a characteristic height of 0.05 mm to 0.15 mm.

7. The method of claim 1 wherein: the roughening raises at 5% to 25% of the tip surface by at least 0.05 mm.

8. The method of claim 1 wherein: the anodizing converts the entire tip surface to by-volume majority alumina to a depth of 0.025 mm.

9. The method of claim 1 wherein: the roughening creates said protrusions with characteristic heights of 0.05 mm to 0.15 mm.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a partially schematic half-sectional view of a turbofan engine.

(2) FIG. 2 is an enlarged transverse cutaway view of a fan blade tip region of the engine of FIG. 1 taken along line 2-2 and showing a first rub coating.

(3) FIG. 2A is an enlarged view of a blade tip region of FIG. 2 showing burrs.

(4) FIG. 3 is a partial sectional view of a first stage of burr formation.

(5) FIG. 4 is a partial sectional view of a second stage of burr formation.

(6) FIG. 5 is a partial view of a surface having the formed burr.

(7) FIG. 6 is a tip end view of a first coated airfoil.

(8) FIG. 6A is an enlarged view of the airfoil of FIG. 6.

(9) FIG. 7 is an enlarged tip end view of a second coated airfoil.

(10) FIG. 8 is an enlarged tip end view of a third coated airfoil.

(11) FIG. 9 is an enlarged tip end view of a fourth coated airfoil.

(12) FIG. 10 is an enlarged tip end view of a fifth coated airfoil.

(13) FIG. 11 is an enlarged tip end view of a sixth coated airfoil.

(14) FIG. 12 is a partial sectional view of a protrusion on the tip end of the airfoil of FIG. 11, taken along line 12-12.

(15) FIG. 13 is a sectional view of a droplet precursor of the protrusion of FIG. 12.

(16) Like reference numbers and designations in the various drawings indicate like elements.

DETAILED DESCRIPTION

(17) FIG. 1 shows a gas turbine engine 20 having an engine case 22 surrounding a centerline or central longitudinal axis 500. An exemplary gas turbine engine is a turbofan engine having a fan section 24 including a fan 26 within a fan case 28. The exemplary engine includes an inlet 30 at an upstream end of the fan case receiving an inlet flow along an inlet flowpath 520. The fan 26 has one or more stages 32 of fan blades. Downstream of the fan blades, the flowpath 520 splits into an inboard portion 522 being a core flowpath and passing through a core of the engine and an outboard portion 524 being a bypass flowpath exiting an outlet 34 of the fan case.

(18) The core flowpath 522 proceeds downstream to an engine outlet 36 through one or more compressor sections, a combustor, and one or more turbine sections. The exemplary engine has two axial compressor sections and two axial turbine sections, although other configurations are equally applicable. From upstream to downstream there is a low pressure compressor section (LPC) 40, a high pressure compressor section (HPC) 42, a combustor section 44, a high pressure turbine section (HPT) 46, and a low pressure turbine section (LPT) 48. Each of the LPC, HPC, HPT, and LPT comprises one or more stages of blades which may be interspersed with one or more stages of stator vanes.

(19) In the exemplary engine, the blade stages of the LPC and LPT are part of a low pressure spool mounted for rotation about the axis 500. The exemplary low pressure spool includes a shaft (low pressure shaft) 50 which couples the blade stages of the LPT to those of the LPC and allows the LPT to drive rotation of the LPC. In the exemplary engine, the shaft 50 also drives the fan. In the exemplary implementation, the fan is driven via a transmission (not shown, e.g., a fan gear drive system such as an epicyclic transmission) to allow the fan to rotate at a lower speed than the low pressure shaft.

(20) The exemplary engine further includes a high pressure shaft 52 mounted for rotation about the axis 500 and coupling the blade stages of the HPT to those of the HPC to allow the HPT to drive rotation of the HPC. In the combustor 44, fuel is introduced to compressed air from the HPC and combusted to produce a high pressure gas which, in turn, is expanded in the turbine sections to extract energy and drive rotation of the respective turbine sections and their associated compressor sections (to provide the compressed air to the combustor) and fan.

(21) FIG. 2 shows a cutaway blade 100 showing a blade substrate (e.g., an aluminum alloy) 102 and a polymeric coating 104 (e.g., a polyurethane-based coating) on the substrate. The exemplary coating is along pressure and suction sides and spans the entire lateral surface of the blade between the leading edge and trailing edge. The exemplary coating, however, is not on the blade tip 106. If originally applied to the tip, the coating may have been essentially worn off during rub. Circumferential movement in a direction 530 is schematically shown.

(22) FIG. 2 also shows an overall structure of the fan case facing the blade. This may include, in at least one example, a structural case 120. It may also include a multi-layer liner assembly 122. An inboard layer of the liner assembly may be formed by a rub material 124. The exemplary rub material 124 has an inboard/inner diameter (ID) surface 126 facing the blade tips and positioned to potentially rub with such tips during transient or other conditions.

(23) The exemplary rub material 124 comprises a polymeric matrix material 128 and a filler 130 (e.g., polymeric particles or micro-balloons or glass micro-balloons). The exemplary rub material may be formed as a coating on an ID surface 132 of a substrate 134 of the liner assembly. An exemplary substrate 134 is titanium alloy AMS 4911. The rub material is shown as having an overall thickness TR. Exemplary T.sub.R is 1-10 mm, more particularly, 3-6 mm. Alternative abradable rub material may include metal matrix composites (e.g., formed by thermal spray coating).

(24) FIG. 2A shows the tip region 106 with a tip surface 150 of the substrate bearing a layer 152. The layer 152 has a surface 154 with protrusions 156. As is discussed further below, these protrusions may correspond to protrusions (asperities) in the pre-anodize substrate and may pattern such protrusions 158 remaining in the substrate. The protrusions 156 form abrasive for abrading the abradable rub material 124. Recesses 160 in the surface 154 adjacent the protrusions 156 pattern associated recesses 162 in the substrate.

(25) The layer 152 has a thickness T.sub.c away from the protrusions 154. Exemplary T.sub.c is 0.5-2.0 mils (13 micrometers to 51 micrometers), more particularly, 20 micrometers to 50 micrometers or 20 micrometers to 35 micrometers.

(26) The exemplary layer 152 is not merely localized to the tip but may extend along all or majority areas of those areas of the substrate that form the pressure and suction sides.

(27) The exemplary protrusions 158 are formed by roughening an initial smooth substrate surface. Exemplary roughening comprises plastically deforming. Exemplary plastically deforming (FIGS. 3-4) displaces material from initial surface 150 to form protrusions 158 which are precursors of the protrusions 158. The displacement leaves recesses 162 that serve as precursors of recesses 162. Exemplary height H.sub.1 of protrusions 158 and 158 respectively above a majority level of the surface 150 and 150 may be similar to H.sub.1.

(28) Exemplary asperity height H.sub.1 is 1-10 mils (0.025 mm to 0.25 mm), more narrowly 2-4 mils (0.05 mm to 0.13 mm) or 2-6 mils (0.05 mm to 0.15 mm) and as broad as 0.5-20 mils (0.013 mm to 0.51 mm) above a majority level of the associated surface. Coverage may be more specifically defined as area at half of asperity height compared with the total tip area.

(29) Examples of mechanical deformation include raising a burr with a cutting tool such as is done in making a file. This may be done as discrete local asperities or as ridges. Ridges may be formed by a drawing operation where a tool is drawn across the surface (e.g., in a line (straight or arcuate)) or may be formed using an elongate edge tool. The drawing may be fully across the surface or may be a shorter drawing to leave closed-ended elongate recesses or indentations and associated protrusions.

(30) One example of an arcuate recess is one that is along or generally follows the median of the tip platform (e.g., the shape of the tip end face of airfoil). For example, a series of ridges and associated grooves may be along the median and then spaced proportionately between the median and the respective suction side perimeter or pressure side perimeter of the tip. For either such arcuate features or for the other features described above, it may be advantageous to keep the distribution of such features spaced away from the tip perimeter to improve fatigue life (reduce/minimize debit in fatigue life associated with the asperities). Bending stresses on the blade at the tip will generally be minimum near the median and progressively greater toward the pressure side perimeter and suction side perimeter (typically going into tension in one direction and compression in the opposite direction). Keeping the asperities away from the perimeter reduces the possibility of crack initiation at these high stress locations. An exemplary amount of recessing keeps the asperities recessed from the perimeter by approximately one-eighth of the local blade thickness, more broadly, one-eighth to one-quarter. As the amount of recessing is initially increased from zero, it will be a progressive benefit. However, at some point, the benefit will reduce and also have to be weighed against the detriment of losing the abrasive capability. Thus, the exemplary one-eighth recessing creates an abrasive zone of 75% of the local blade thickness while the one-quarter recessing yields 50%. An alternative lower limit on beneficial recessing may be 5% or 10% rather than the one-eighth. Alternative upper limits may reach one-third.

(31) FIGS. 3 and 4 show a tool 200 having a tip 202, a leading surface 204, and a trailing surface 206. Lateral (side) surfaces are not shown. The exemplary tool is plunged into the surface 150 by translation in a direction 540 (FIG. 4). Exemplary direction 540 is slightly off parallel to the surface (e.g., by an exemplary 5 to 20). However, a broader range of angles including normal indentation is possible. Exemplary movement raises the protrusion 158 as a burr ahead of the tool. With an exemplary narrow indenter, FIG. 5 shows the burr 158 as generally crescent-shaped with a base at the leading end of the recess 162 and two sides or arms extending back along the sides of the recess 162 and vertically and horizontally tapering toward the trailing end of the recess 162.

(32) FIG. 6 is an end view of a tip with FIG. 6A showing the pattern of protrusions and recesses in the direction of blade motion in the ultimate engine as shown as 550. FIG. 6 further shows the blade leading edge 110, trailing edge 112, pressure side 114, and suction side 116. The exemplary protrusions and recesses are aligned with the recesses ahead of the protrusions in that direction. The exemplary recesses are patterned so that one or more of several properties may be achieved. First, the recesses are of sufficient density so as to at least partially overlap in location transverse to the direction 530. In this way, all areas of the abradable material swept by the tip will encounter protrusions. This helps avoid uneven wear of the abradable material. Furthermore, the pattern may be selected so that, overall, any given axial location along the abradable material encounters similar numbers of protrusions so as to also promote even wear. Thus having rows of protrusions parallel to direction 500 would not be particularly desirable. Offset rows oriented differently (FIG. 7), may however, provide some benefit as is discussed further below in the context of elongate protrusions.

(33) FIG. 8 shows elongate protrusion-recess pairs oriented axially (normal to the direction 530). The axial configuration offers benefits of simplicity of design as it is conceptually easy to achieve smooth and uninterrupted axial coverage over the width of the mating abradable. Furthermore, it is conceptually simple to increase or reduce the spacing of protrusion-recess pairs to provide an optimal balance between the volume of abradable cut and the required number of protrusions doing the cutting. For example, if too few protrusions are provided for cutting a desired amount of abradable, the protrusions may exhibit excessive wear. In that case, protrusion spacing would be reduced to provide more protrusions to share the work of cutting. Conversely, if too many protrusions are provided, the abradables may deplete at an excessive rate while the protrusions may have longer lifespans than anticipated. In that case, the protrusion spacing could be increased.

(34) FIG. 9 shows such pairs oriented generally chordwise. The chordwise orientation offers the benefits of conceptually simple design, low cost manufacturing, complete coverage across the axial width of the blade path, may minimized fatigue life debit when the features are located near the center of the tip width. Furthermore, chordwise ridges act as labyrinth seal features and provide reduction in air leakage over the tip of the airfoil.

(35) FIG. 10 shows a combination of intersecting axial and chordwise pairs.

(36) Formation of protrusions without corresponding recesses may be achieved by additive methods. Additive methods include plasma spray, laser powder sintering, electro-spark deposition, and sputtering.

(37) FIG. 11 shows a pattern of individual protrusions 400 formed by an additive process.

(38) FIG. 12 shows a protrusion 400 in the oxide layer and a small remaining portion of a protrusion 402 formed by a droplet 402 (FIG. 13) applied to the original substrate tip.

(39) Alternative, but likely more costly, subtractive methods may remove material from the surface to leave high points. Exemplary subtractive methods include micro-machining, etching, laser ablation, and electro-discharge machining (EDM) to roughen the surface to create protrusions such as those discussed above for displacement processes or additive processes.

(40) An exemplary manufacture process involves forming the blade substrate by conventional means (e.g., forging and/or machining and peening). Some blade configurations have a titanium leading edge separated from an aluminum substrate by a slight gap (e.g., epoxy-filled for galvanic isolation). Asperities may be formed in the metal of the tip surface by incursion of a tool. An exemplary tool may be a conical diamond tool with included angle of 60 degrees (more broadly, an exemplary 45 to 75) and tip radius of 0.001 inch (0.024 mm) (more broadly, 0.01 mm to 0.10 mm or 0.01 mm to 0.05 mm).

(41) Repeated incursion at an exemplary 30 degree angle to the tip surface (more broadly, 5 to 50 or 15 to 45 or 20 to 40) creates asperities raised from the tip surface by 0.003 inch (0.08 mm) (more broadly, 0.04 mm to 0.20 mm or 0.05 mm to 0.15 mm). This is repeated until the tip is covered by asperities at a spacing of about 0.010 inch (0.25 mm). The tip of the blade is then treated by a sulfuric acid anodize process to create a 0.001 inch (0.025 mm) thick (more broadly, 0.02 mm to 0.04 mm or 0.01 mm to 0.05 mm) layer of aluminum oxide on the asperities. The gas path surfaces and Ti leading edge may be masked to prevent interaction with the anodize process.

(42) Exemplary masking methods may include silicone masking tape and wax dipping to protect the majority of the part.

(43) For blades having polymer coatings on the airfoil pressure and suction side surfaces, such coating could also be used to mask if the polymer coating was applied before rather than after the anodize process.

(44) Relative to uncoated tips or alternative coatings the exemplary coating may have one or more of several advantages. For example, the hard coated asperities act as an abrasive when in rub interaction with an abradable outer air seal and result in a reduced blade temperature rise compared with an untreated blade tip. This reduced temperature rise is sufficient in one example to suppress the blade temperature to below 350 F. (177 C.) which prevents the thermally induced spallation of a polyurethane erosion resistant coating on the gas path surfaces. Another advantage is improved durability compared with polymer bonded abrasive tip materials. The polymer bonded materials have an inherent temperature limitation associated with the softening of the polymer matrix. This limits their use to the coolest stages of the engine and also results in a wear ratio with the outer air seal material in the range of 0.05 to 0.01. The present hard coated asperity tip material may exhibit a very small wear ratio with the outer air seal in the order of 0.0001. This is advantageous for the retention of blade length during rub interaction. The hard coated asperities do not suffer the same temperature limitation and may be used throughout the engine.

(45) The use of first, second, and the like in the following claims is for differentiation within the claim only and does not necessarily indicate relative or absolute importance or temporal order. Similarly, the identification in a claim of one element as first (or the like) does not preclude such first element from identifying an element that is referred to as second (or the like) in another claim or in the description.

(46) Where a measure is given in English units followed by a parenthetical containing SI or other units, the parenthetical's units are a conversion and should not imply a degree of precision not found in the English units.

(47) One or more embodiments have been described. Nevertheless, it will be understood that various modifications may be made. For example, when applied to an existing baseline configuration, details of such baseline may influence details of particular implementations. Accordingly, other embodiments are within the scope of the following claims.