METHOD AND ARRANGEMENT FOR RECOVERY OF SALT
20190337816 ยท 2019-11-07
Inventors
Cpc classification
C02F2103/18
CHEMISTRY; METALLURGY
C01D3/08
CHEMISTRY; METALLURGY
C02F2305/14
CHEMISTRY; METALLURGY
International classification
Abstract
A method for recovery of salts comprises providing (210) of an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca or a material which when brought in contact with water forms an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca. The start material is treated (230) into an enriched aqueous solution having a concentration of CaCl.sub.2 of at least 15% by weight. The treatment (230) comprises at least one of reduction of water content and addition of Ca. The treatment (230) generates a solid mix of Na Cl and KCl. The solid mix of NaCl and KCl is separated (235) from the enriched aqueous solution, giving a depleted aqueous solution comprising ions of Ca and Cl as main dissolved substances. An arrangement for recovery of salts is also disclosed.
Claims
1.-52. (canceled)
53. A method for recovery of salts, comprising the steps of: providing a start material, which when brought in contact with water forms an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca; treating said start material into an enriched aqueous solution having a concentration of CaCl.sub.2 of at least 15% by weight; said treating optionally comprising reduction of water content; and said step of treating generating a solid mix of NaCl and KCl; said treating comprising controlled provision of at least additional ions of Ca into said enriched aqueous solution in excess of what a said initial aqueous solution can provide; and separating said solid mix of NaCl and KCl from said enriched aqueous solution, giving a depleted aqueous solution comprising ions of Ca and Cl as main dissolved substances; adding said solid mix of said NaCl and KCl into an aqueous solution, thereby dissolving at least a part of said solid mix of said KCl and NaCl, to form a mixed aqueous solution; said step of adding said solid mix of said NaCl and KCl into said aqueous solution comprises controlled dissolving said KCl and optionally a part of said NaCl in said aqueous solution at a first temperature to obtain a first concentration of KCl; said first concentration of KCl being lower than a solubility concentration of KCl at said first temperature; and separating said NaCl and KCl into individual fractions from said mixed aqueous solution; said step of separating said NaCl and KCl into individual fractions in turn comprises the steps of: separating any solid NaCl from said mixed aqueous solution at said first temperature; lowering, after said step of separating any solid NaCl, a temperature of said mixed aqueous solution to a second temperature lower than said first temperature; and separating any precipitated KCl from said mixed aqueous solution at said second temperature; and by the further step of heating and recycling, after said separating of said any precipitated KCl, at least a part of said mixed aqueous solution for a further said adding of said solid mix of said NaCl and KCl.
54. The method according to claim 53, wherein said controlled provision of at least additional ions of Ca into said initial aqueous solution is performed to give a weight of said solid mix of NaCl and KCl that is lower than the weight of produced CaCl.sub.2 solution.
55. The method according to claim 53, wherein said reduction of water content comprises evaporation of water.
56. The method according to claim 53, wherein said step of treating said start material comprises at least one of: controlling a temperature of said enriched aqueous solution to exceed a solubility temperature for said concentration of CaCl.sub.2; and controlling said concentration of CaCl.sub.2 to be lower than a solubility concentration for a prevailing temperature of said enriched aqueous solution.
57. The method according to claim 53, wherein said step of treating said start material comprises causing a precipitation comprising chloride salts comprising Na, K and Ca; and in that said step of separating said solid mix of said NaCl and KCl in turn comprises the steps of: separating said precipitation comprising chloride salts of Na, K and Ca; at least partially re-dissolving said separated precipitation comprising chloride salts of Na, K and Ca in an aqueous solution, causing at least salts comprising said Ca to dissolve and give a non-saturated aqueous solution comprising CaCl.sub.2; and separating remaining precipitated NaCl and KCl from said non-saturated water solution of CaCl.sub.2.
58. The method according to claim 53, comprising the further step of: recycling at least a part of said depleted aqueous solution to be used as additives of Ca ions and Cl ions in a further said treating of said start material into an enriched aqueous solution.
59. The method according to claim 53, comprising the further step of: purifying said depleted aqueous solution from residual alkali salts.
60. The method according to claim 53, wherein said step of providing a start material in turn comprises the steps of: obtaining a raw aqueous solution comprising ions of Na, K, Cl and optionally Ca; and pre-treating said raw aqueous solution into said initial aqueous solution by at least one of: removal of sulfate; removal of ammonia; removal of heavy metals; and neutralization.
61. The method according to claim 53, wherein said step of providing a start material comprises washing of air pollution control by-products with an aqueous solution.
62. The method according to claim 53, wherein said step of providing a start material comprises dissolving of salt containing waste material.
63. An arrangement for recovery of salts, comprising: an input section; and a first stage section, comprising a treatment arrangement and a salt mix separator; said input section being arranged for providing a start material comprising at least one of an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca, and a material, which when brought in contact with water forms an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca to said first stage section; said treatment arrangement being arranged for treating said start material provided from said input section into an enriched aqueous solution having a concentration of CaCl.sub.2 of at least 15% by weight, whereby a solid mix of NaCl and KCl is generated; said treatment arrangement optionally comprising a water reduction arrangement; said water reduction arrangement being arranged for removing water from said initial aqueous solution; said salt mix separator being arranged for separating said solid mix of said NaCl and KCl from said enriched aqueous solution, giving a depleted aqueous solution comprising ions of Ca and Cl as main dissolved substances; said treatment arrangement comprises an input for additives; said input for additives being arranged for controlled provision of at least additional ions of Ca into said initial aqueous solution; a second stage section connected to said first stage section for enabling transferring of said solid mix of said NaCl and KCl, said second stage section comprising: a dissolver, arranged for adding said solid mix of said NaCl and KCl into an aqueous solution, thereby dissolving at least a part of said solid mix of said KCl and NaCl, to form a mixed aqueous solution; said dissolver is arranged for controlled dissolving said KCl and optionally a part of said NaCl in said aqueous solution at a first temperature to obtain a first concentration of KCl; said first concentration of KCl being lower than a solubility concentration of KCl at said first temperature; and a separator arrangement, arranged for separating said NaCl and KCl into individual fractions from said mixed aqueous solution said separator arrangement comprises: a NaCl separator for separating any solid NaCl from said mixed aqueous solution at said first temperature; a temperature controller for lowering, downstream of said NaCl separator, a temperature of said mixed aqueous solution to a second temperature, said second temperature being lower than said first temperature; and a KCl separator for separating any precipitated KCl from said mixed aqueous solution at said second temperature; and by further comprising a NaCl/KCl recycling arrangement; said NaCl/KCl recycling arrangement being arranged for heating and recycling, downstream of said KCl separator, at least a part of said mixed aqueous solution to said dissolver.
64. The arrangement according to claim 63, wherein said dissolver is arranged for giving a weight of said solid mix of NaCl and KCl that is lower than the weight of produced CaCl.sub.2 solution.
65. The arrangement according to claim 63, wherein said water reduction arrangement comprises an evaporator.
66. The arrangement according to claim 63, wherein said treatment arrangement comprises a dissolution control, arranged for at least one of: controlling a temperature of said enriched aqueous solution to exceed a solubility temperature for said concentration of CaCl.sub.2; and controlling said concentration of CaCl.sub.2 to be lower than a solubility concentration for a prevailing temperature of said enriched aqueous solution.
67. The arrangement according to claim 63, wherein said treatment arrangement is arranged for causing a solid mix comprising chloride salts of Na, K and Ca; and in that said salt mix separator comprises: a first separator arranged for separating said solid mix comprising chloride salts of Na, K and Ca; a dissolver connected to said first separator and arranged for at least partially re-dissolving said separated solid mix comprising chloride salts of Na, K and Ca in an aqueous solution, causing at least salts comprising said Ca to dissolve and give a non-saturated water solution comprising CaCl.sub.2; a second separator connected to said dissolver and arranged for separating remaining precipitated NaCl and KCl from said non-saturated water solution of CaCl.sub.2.
68. The arrangement according to claim 63, further comprising a partial return arrangement connecting an output from said salt mix separator and an input to said treatment arrangement of said first stage section, said partial return arrangement being arranged for recycling at least a part of said depleted aqueous solution to be used as additive of Ca ions and Cl ions in said treatment arrangement.
69. The arrangement according to claim 63, further comprising a CaCl.sub.2 purifier connected to an output from said salt mix separator, said CaCl.sub.2 purifier being arranged for purifying said depleted aqueous solution from residual alkali salts.
70. The arrangement according to claim 63, wherein said input section comprises: a supply of a raw aqueous solution comprising ions of Na, K, Cl and optionally Ca; and a pre-treating arrangement connected to said supply of said raw aqueous solution, said pre-treating arrangement being arranged for pre-treating said raw aqueous solution into said initial water solution by at least one of: a sulfate removal arrangement; an ammonia removal arrangement; a heavy metal removal arrangement; and a neutralization arrangement.
71. The arrangement according to claim 63, wherein said input section comprises an air pollution control by-product washing arrangement.
72. The arrangement according to claim 63, wherein said input section being arranged for receiving said initial aqueous solution from an arrangement for dissolving of salt containing waste material.
Description
BRIEF DESCRIPTION OF THE DRAWINGS
[0031] The invention, together with further objects and advantages thereof, may best be understood by making reference to the following description taken together with the accompanying drawings, in which:
[0032]
[0033]
[0034]
[0035]
[0036]
[0037]
[0038]
[0039]
[0040]
[0041]
[0042]
[0043]
[0044]
[0045]
[0046]
[0047]
[0048]
[0049]
[0050]
[0051]
[0052]
DETAILED DESCRIPTION
[0053] Throughout the drawings, the same reference numbers are used for similar or corresponding elements. Some often used terminology in the present disclosure is to be interpreted as follows:
[0054] Air pollution control (APC) by-productsBy-products resulting from the treatment of gas and particles coming out from the incineration chamber. For example, by-products from electrostatic filters often called fly ash, by-products from dry scrubbing of gaseous impurities, by-products from wet scrubbing of gaseous impurities, by-products from treatment of wastewater generated during air pollution control, etc.
[0055] Waste incineration (WI) by productsBy-products resulting from incineration operation including bottom ash and air pollution control (APC) by-Products Air pollution control by-products (APCBP) leach-solutionsolution resulting from contacting air pollution control (APC) by-products with an aqueous solution such as water, salt solution, acid solution or base solution
[0056] By solid substances being present in contact with a solution is understood precipitated substances and/or non-dissolved substances.
[0057] For a better understanding of the proposed technology, it may be useful to begin with a brief overview of waste treatment.
[0058] Incineration is a common method for municipal solid waste treatment achieving up to ca 90 percent volume reduction and up to ca 75 percent mass reduction. Combustion of municipal wastes enables destruction of pathogens and organic contaminants, as well as possible recovery of energy in form of heat and/or electricity. During the incineration of municipal wastes, air pollution control by-products (APCBP) are generated resulting from the treatment of flue gas coming out from the incineration chamber. APC by-products are often considered as hazardous waste when being disposed in a landfill due to high content of water-soluble chloride salts and heavy metal content. The chemical composition of APC by-products depends on the type of waste being incinerated, incineration process, and on process for flue gas treatment as well as wastewater treatment for aqueous effluents. Typical compositions of APC by-products in Sweden are as follows: major components by weight are Ca (20-40%), Si (5-20%), Cl (10-50%), K (1-6%), Na (1-8%), Zn (1-6%) and Al (1-8%). Other elements include Fe (0.5-3%), P (0.05-4%), Mg (1-4%), Ti (0.1-2%), etc. Heavy metals such as Pb, Ti, Cd, Ni, Cr, Cu, B, etc. are usually present in concentrations in the range of 0.001 to 1% by weight. The organic carbon content depends to a large extent on the incineration process and varies usually between 0.2% up to 10% by weight. Inorganic carbon is usually low below 2% by weight.
[0059] Inorganic water-soluble salts in APC by-products, especially chlorides, hold a potential risk of leaching when disposed in landfill. Therefore, APC by-products are usually classified as hazardous waste according to chloride content when being disposed in a landfill. It is known that water-washing of APC by-products can extract the soluble salts and improve the quality of the washed residue to enable disposal in some cases even as non-hazardous waste. Full-scale plants are already in operation for washing APC by-products from their water-soluble chloride salt content.
[0060] However, as discussed before, in many cases, disposal of saline effluents generated in washing operation is problematic. Therefore there is a need for a method that can enable to recover chloride salts from APC by-products washing operations in form of commercial products for sale in order to solve disposal problems, improve the economy of the treatment process, and enable operation in locations lacking the possibility for discharging saline effluents.
[0061] It is known in the art to separate sodium chloride and potassium chloride from their mixtures. The principle for such separation is that the solubility of potassium chloride is increasing and that of sodium chloride is decreasing with increasing temperatures. And, of course, in the opposite direction, the solubility for potassium chloride is decreasing and that of sodium chloride is increasing with decreasing temperatures. Mixtures of sodium chloride and potassium chloride can be present in brines from solution-mining of solid minerals, in salt lakes, brines from sea water desalination, etc. The common way to process such mixtures of sodium chloride and potassium chloride is to crystallize a part of the sodium chloride by evaporation of water, and thereafter to cool the solution to crystallize a part of the potassium chloride. The next step is to recycle and mix the outflow from potassium chloride crystallization with new feed brine and repeat the process. In the mining industry, large volumes of equilibration basins usually guaranty a relatively constant ratio between the dissolved salts (NaCl and KCl) which enable relatively constant settings for operation. It can further be noted that, when separating NaCl and KCl in the mining industry, calcium chloride is generally absent.
[0062] However, a main problem when attempting to recover chloride salts from APCBP leach-solution is that the ratio between the different salts varies greatly with time.
[0063] Chinese patent application CN202007141U suggests recovering sodium chloride and potassium chloride from municipal solid waste incineration fly ash by using the above described principles i.e. using a NaCl evaporator crystallizer and a KCl cooling reactor according to state-of-the-art. Since the NaCl and KCl in the fly-ash wash-water are provided in solution, the settings of the evaporator have to change according to different Na/K ratios which make operation difficult. Furthermore, as can be seen in
[0064] In the cases in which calcium chloride is present in mineral feed solution used for extraction of potassium, such as in the Dead Sea in Israel/Jordan, a high content of dissolved magnesium enables a separation of KCl from the brine by crystallization of Carnallite. The separated brine containing dissolved calcium chloride is not recovered but pumped back to the sea.
[0065]
[0066] Solubility data of the quaternary system NaClKClCaCl.sub.2H.sub.2O is available from a number of sources. In J. Chem. Eng. Data 2015, 60, pp 1886-1891, D. Li et al investigates equilibrium at 303.15 K. In Journal of Thermal Analysis and Calorimetry, vol. 95 (2009) 2, pp 361-367, D. Li et al investigates equilibrium at 308.15 K. In fluid Phase Equilibria 269 (2008) pp 98-103, T Deng et al investigates equilibrium at 288.15 K. In Russian Journal of Physical Chemistry A, 2011, Vol. 85, No. 7, pp 1149-1154, J-M Yang et al investigates solubility in the system NaClCaCl.sub.2H.sub.2O and KClCaCl.sub.2H.sub.2O at 75 C. In journal of Korean Chemical Society, 2010, Vol 54, No. 3, pp. 269-274, J-M Yang et al investigates solubility in the system NaClCaCl.sub.2H.sub.2O and KClCaCl.sub.2H.sub.2O at 50 C.
TABLE-US-00001 TABLE 1 Purity of calcium chloride solutions obtained after crystallization of alkali salts as a function of calcium chloride concentration and temperature Concentration Purity of Temperature of CaCl.sub.2 CaCl.sub.2 solution ( C.) (% of weight) (% CaCl.sub.2) 16 40 94 6 30 85 7 30 83 7 35 91 7 40 93 22 30 80 22 35 88 22 40 92 22 50 92 50 55 90 70 60 94 85 40 82 85 55 90
[0067] Since only a limited data is available in the literature regarding the solubility behavior of mixtures of CaCl.sub.2, NaCl, and KCl, the system of CaCl.sub.2NaClKClH.sub.2O was therefore experimentally investigated for a wide range of temperatures and concentrations. Table 2 shows the purity of calcium chloride solution obtained after crystallization of alkali salts (NaCl and KCl) as a function of calcium chloride concentration and temperature. From table 1 it can be seen that a purity of up to about 94% by weight can be obtained for a calcium chloride solution by salting out a mixture of sodium chloride and potassium chloride at certain combinations of calcium chloride concentrations and temperatures.
[0068] Since it was experimentally shown to be impossible or at least very difficult to separate pure NaCl and KCl from CaCl.sub.2 containing solutions by conventional evaporation and cooling e.g. according to CN202007141U, the approach in the currently presented technology is to separate, at a first stage, a mixture of NaCl and KCl from a CaCl.sub.2 solution and preferably in a second stage to separate NaCl and KCl from that mixture. The first stage thus uses the varying solubilities of NaCl and KCl in high-concentration CaCl.sub.2 solutions to separate Ca from Na and K.
[0069]
[0070] In the figure, the steps 210 and 230 are illustrated as being two consecutive steps. However, in alternative embodiments, at least parts of the steps 210 and 230 may be performed simultaneous and/or in dependence of each other, or as one integrated step.
[0071] In one particular example, a ZLD solid waste product being composed of a solid mixture of CaCl.sub.2, NaCl and KCl is fed into a reactor. The solid waste may contain residual moisture. The start material here comprises a material, which when brought in contact with water forms an initial aqueous solution comprising ions of Na, K, Cl and optionally Ca. An aqueous solution e.g. water is therefore also entered into the reactor. A waste product composed of solid CaCO.sub.3 is added to the reactor and concentrated HCl is added into the reactor to convert the added CaCO.sub.3 into CaCl.sub.2 by release of CO.sub.2. All reactants are agitated in room temperature. A solution of 35% CaCl.sub.2 by weight is formed containing a mixture of NaCl and KCl, which is further processed. The ZLD solid waste is not completely dissolved in water to form an aqueous solution. A main part of the NaCl and KCl in the ZLD waste product may not dissolved at all but remain solid through the process. A start material then comprises the minor part of dissolved NaCl and KCl plus the solid mix of salts. The addition of Ca ions and Cl ions then gives the requested CaCl.sub.2 content.
[0072] The mix of NaCl and KCl is of low value as such, and in order to recover valuable products, the mix has to be further processed in order to achieve NaCl and KCl in substantially pure fractions. In the U.S. Pat. No. 2,788,257, a crystallization process for recovering sylvite from sylvite ore is disclosed. An efficient recovery of high-purity KCl is obtained by saturating a brine with respect to KCl. However, NaCl being present in the residual side product becomes by such a process contaminated with residual amounts of KCl. Also in the publication Potassium Compounds by M. B. Freilich et al in Kirk-Othmer Encyclopedia of Chemical Technology, published on-line Sep. 15, 2004, a similar approach is suggested, giving a residue of unsolved NaCl mixed with some amount of KCl and possibly also clay. These procedures can therefore not be used, as such, for producing individual substantially pure fractions of both KCl and NaCl.
[0073] Some attempts, described in the literature, were made to recover salts from solution originating from water washing of fly ash originating from incineration of municipal wastes. Chinese utility patent application CN202007141U suggests recovering of sodium chloride and potassium chloride from such wash solution by using a NaCl evaporator crystallizer and a KCl cooling reactor. Since the NaCl and KCl are provided in solution, the settings of the evaporator have to change according to variations in Na/K ratios which make the operation very difficult. Furthermore, it was found by the present applicant that if calcium chloride is present in the solution it changes the solubility behavior of NaCl and KCl, which makes this process to be impossible or at least very difficult to run. When calcium chloride is present it is impossible or at least very difficult to crystallize pure salts of NaCl and KCl as described later in the text.
[0074] In the here proposed technology, the solid mix of NaCl and KCl is further processed. In further reference to
[0075]
[0076] The first stage section 20 comprises a treatment arrangement 24 and a salt mix separator 28. The treatment arrangement 24 is arranged for treating the start material 18 provided from the input section 10 into an enriched aqueous solution 25 having a concentration of CaCl.sub.2 of at least 15% by weight. The treatment arrangement 24 comprising at least one of a water reduction arrangement 26 and an input for additives 27. The water reduction arrangement 26 is arranged for removing water from the initial aqueous solution 18, for forming the enriched aqueous solution 25. The input for additives 27 is arranged for adding at least Ca ions and optionally Cl ions into the start material 18, for forming the enriched aqueous solution 25. Due to the salting out effect, a solid mix 32 of NaCl and KCl is generated. The salt mix separator 28 is arranged for separating the solid mix 32 of NaCl and KCl from the enriched aqueous solution 25, giving a depleted aqueous solution 34 comprising ions of Ca and Cl as main dissolved substances. As will be discussed in connection with different embodiments further below, this enriched aqueous solution 25 product may be used as it is or may be post-treated for instance to improve the purity.
[0077] In alternative embodiments, at least parts of the input section 10 may be implemented together with the treatment arrangement 24, being dependent on each other or even being integrated into one process unit, as discussed in a particular embodiment further above.
[0078] In a preferred embodiment, the solid mix of NaCl and KCl is further processed. In further reference to
[0079] Exemplary embodiments will now be utilized to illustrate different aspects of methods and arrangements for salt recovery.
[0080] The start material may be provided in different ways. In one embodiment, the step of providing 210 (
[0081] Analogously, in one embodiment, the input section 10 (
[0082] In a particular embodiment, illustrated in
[0083] As a particular practical example, an applied practice is to wash APC by-products with an aqueous solution such as water or condensate. The weight ratio of aqueous solution to APC by-products is generally from about 2 up to 10. This usually results in a saline effluent with a salt concentration of about 4% dissolved salts by weight. Since water-soluble chloride salts is to be recovered form APC by-products, the water in APCBP leach-solution has typically to be removed by evaporation. Therefore, the concentration of salts in the APCBP leach-solution is of outmost importance for the costs for water evaporation. In general, a higher salt concentration will require less evaporation of water per unit salt produced and thus lower operational costs.
[0084] It is, in particular embodiments, possible to increase the salt concentration of APCBP leach-solution by applying membrane based technologies such as reverse osmosis, electro-dialysis reversal, etc. However, APCBP leach-solution is generally high in alkalinity (pH of ca 11-12) and supersaturated with a range of inorganic salts such as gypsum, and various hydroxides which have a very high tendency to foul membranes. Therefore, application of membrane technology to concentrate APCBP leach-solution is usually costly or difficult to operate due to operational problems caused by fouling of membranes, usually by inorganic scale.
[0085] Therefore, in a preferred embodiment, the difficulties of using membrane technology for concentration of APCBP leach-solution is avoided by obtaining a high salt concentration already in the process of washing of APC by-products. Such an approach requires a refined washing operation to obtain a high salt concentration in the APCBP leach-solution and at the same time to obtain a washed residue which fulfils the criteria of low chloride content for disposal.
[0086] In one such embodiment, it was found that the kinetics of chloride release from APC by-products is rapid, resulting in almost complete chloride release within between about one minute to a few minutes. It was also found that it is possible to increase the chloride concentration in the APCBP leach-solution by reusing the leach-solution in a subsequent wash cycle. A concept was thereafter developed for a washing procedure that can enable to obtain a highly saline solution already during the washing process and at the same time to fulfil the disposal criteria for the residue.
[0087] APC by-products contain typically about 20 percent by weight of soluble chloride salts. This means that in order to obtain a salt solution with a concentration of above about 17% salts by weight, the liquid to solid weight ratio during washing should be below 1. One embodiment of a concept for washing APC by-products is shown in
[0088] After filtration, the APC by-products are rinsed with rinse water 15 from the water inlet 64. The rinse water for rinsing can be of different origins, such as recycled condensate water, landfill leachate water, tap water, etc. The amount of rinse water is preferably below 2 liter water per kg of APC by-products. Rinsing can be performed in a single step or in several subsequent steps. It is also possible to improve the rinsing operation by rinsing in a counter-current manner. Washed ashes 16 or APC by-products are removed and exited through the APC by-product outlet 66.
[0089] A concentrate filtrate 76 is produced. A first part of the concentrated filtrate 76 is recovered as a salt solution for further processing to recover its salt content, i.e. the initial aqueous solution. A second part of the concentrated filtrate 76 is diluted with the rinse water 15. The diluted filtrate 78 is typically stored temporarily in a holding tank 72. The diluted filtrate 78 is recycled as recycled leach solution 73 by a recycling pipe 74 to the mixing device 60, for washing the incoming APC by-products 14.
[0090]
[0091]
[0092] In other words, in a particular embodiment, the arrangement for recovery of salt comprises an input section in turn comprising a system for washing of ashes 12 (
[0093] Even though the above washing procedure is exemplified using fresh water as a washing medium it should be clear that any other washing procedures are possible. For example, APC by-products can be washed with an acid solution to dissolve different metallic components such as zinc or phosphorus if present. Recovery of chloride salts according to the present invention can therefore by advantage be combined with other recovery processes such as zinc recovery by precipitation/extraction, phosphorus recovery by precipitation/extraction, recovery of precious metals by selective adsorbents, etc.
[0094] APCBP leach-solution is primarily composed of a mixture of water-soluble chloride salts such as calcium chloride, sodium chloride and potassium chloride. If water is used as the washing medium, the pH of the wash water is typically high above pH 11.5. A generally high pH level combined with usually a high content of dissolved calcium results generally in low content of carbonates, fluorides and silicates as these anions form water-insoluble precipitates such as calcium carbonate, calcium fluoride and calcium silicate having very low solubility at high pH level. The content of dissolved iron is usually low as ferrous and ferric iron form insoluble iron hydroxides at high pH level. The nitrate content is generally low in APC by-products. It was also found that dioxins are essentially not released into solution and are incorporated in the washed APC by-products residue in a non-leachable form suitable for disposal in a landfill.
[0095] However, APCBP leach-solution can contain a range of impurities such as suspended solids (inorganic or organic) and dissolved compounds such as sulfates, ammonia, ammonia-metal complexes, hydroxides (e.g. Ca(OH).sub.2, KOH, NaOH), heavy metals (e.g. Cd, Ni, Zn, As, Pb, Cr in form of dissolved cations, dissolved anions, oxyanions or ammonia complex), amphoteric metals such as aluminium forming dissolved hydroxy-anion at high pH, etc. Thus, in a preferred embodiment, APCBP leach-solution is pre-treated for removal of non-wanted substances, preferably before recovery of soluble chloride salts.
[0096] In
[0097] In an analogous embodiment of an arrangement for salt recovery, as illustrated by some dashed parts in
[0098] Pretreatment of the APCBP leach-solution can be done by any treatment technology to separate non-wanted substances from a saline solution. In general, a preferred pretreatment is to add suitable chemicals to the APCBP leach-solution to induce precipitation of the impurities followed by a solid/liquid separation. Suspended solids (inorganic and/or organic) can usually be removed by flocculation and sedimentation. However, other possibilities also exist such as floatation, filtration, etc. Dissolved organic carbon is generally low. If present, it can be removed by adsorption on e.g. activated carbon, oxidation by addition of hydrogen peroxide, etc.
[0099] Dissolved sulfate can generally be removed by precipitation in form of calcium sulfate di-hydrate (gypsum) by adjusting the ratio of Ca to S in the APCBP leach-solution to form an excess of Ca over S.
[0100] In most cases, the calcium concentration in APCBP leach-solution is higher than the sulfate content and no adjustment has to be made. In case the APCBP leach-solution has a high soluble sulfate content in relation to dissolved calcium, the calcium content can be increased by mixing a water-soluble Ca containing APC by-product during the washing, addition of APCBP leach-solution with a high dissolved Ca content, addition of CaCl.sub.2, recycling of a part of recovered CaCl.sub.2, etc. In general, gypsum precipitation enables to reduce sulfate concentration to ca 1500 mg/I (ca 500 mg S per liter). In many cases, the APCBP leach-solution is supersaturated regarding dissolved gypsum and the only treatment required is to break the super-saturation i.e. induce precipitation. Examples for such treatment include aging of the APCBP leach-solution, agitation, aeration, seeding with crystals, quiet settling, etc.
[0101] If the dissolved sulfate content has to be further reduced it is possible to further reduce sulfate concentration by precipitating sulfate in form of ettringite Ca.sub.6Al.sub.2(SO.sub.4).sub.3(OH).sub.12.26H.sub.2O which has a lower solubility compared to gypsum. Ettringite can be precipitated by adding an aluminium source such as alum to the APCBP leach-solution. Ettringite precipitation can reduce the sulfate content to <200 mg per liter (<66 mg S per liter). Of course, any other method for separation of dissolved sulfate is possible such as precipitation with barium salts such as BaCl.sub.2, BCO.sub.3, BaS, or Ba(OH).sub.2, etc.
[0102] In other words, in one embodiment of the method for salt recovery, the removal of sulfate is performed by at least one of gypsum precipitation by addition of Ca ions, ettringite precipitation by addition of Al ions; and barium sulfate precipitation by addition of Ba ions.
[0103] Analogously, in one embodiment of an arrangement for salt recovery, the sulfate removal arrangement comprises a sulfate removal ion adding arrangement and a sulfate removal separator. The sulfate removal ion adding arrangement is arranged for adding at least one of Ca ions, Al ions and Ba ions to cause precipitation of gypsum, ettringite, and barium sulfate, respectively. The sulfate removal separator is arranged to separate any precipitation of gypsum, ettringite, and barium sulfate.
[0104] APCBP leach-solution usually contains also a range of dissolved metals and heavy metals. Several techniques can be used for separation of metals such as adjustment of pH to induce the precipitation of metals as hydroxides. If the pH is too low it can be increased by addition of a base and if the pH is too high it can be decreased by addition of an acid. Of course, a combination of both pH increase and pH decrease and vice versa with accompanying solid/liquid separation can be performed. Different metal hydroxides can have minimum solubility at different pH level. The adjustment of the pH may, as will be discussed more in detail below, also be necessary for other reasons.
[0105] An effective way of removing heavy metals from APCBP leach-solution is to precipitate heavy metals as sulfides. Metal sulfides have a very low solubility at high pH levels from neutral to alkaline which means that precipitation of heavy metals can be done by addition of inorganic salts of sulfides to the APCBP leach-solution with or without pH adjustment. Examples of inorganic sulfides include sodium sulfide, hydrogen sulfide, calcium sulfide, iron sulfide, etc. Of course, other forms of sulfides such as e.g. 1, 3, 5-triazine-2, 4, 6-triathione sodium salt known as TMT 15 can be used as well as other organic forms of sulfides. Table 2 shows some experimental results of heavy metal removal from APCBP leach-solution by addition of inorganic sodium sulfide without any pH adjustment.
TABLE-US-00002 TABLE 2 Removal of dissolved heavy metals from APCBP leach-solution by addition of sodium sulphide without any pH adjustment. As Pb Cd Cu Cr Ni Zn mg/l mg/l mg/l mg/l mg/l mg/l mg/l Before sulphide precipitation 0.0016 220 0.00014 0.56 0.33 0.0016 11 After sulphide precipitation 0.0014 0.00081 <0.0001 0.001 0.0023 0.0013 <0.005
[0106] It is usually common to combine sulfide precipitation with a flocculation operation to enhance solid/liquid separation by e.g. sedimentation. Common inorganic chemical additives to induce flocculation include ferric chloride, ferrous chloride, aluminium chloride, ferric hydroxide, ferrous hydroxide, aluminium hydroxide, magnesium chloride, magnesium hydroxide, calcium carbonate, etc. In addition to inorganic compounds, polymers (non-ionic, anionic, or cationic) are also commonly used for flocculation with/or without sulfide precipitation.
[0107] Heavy metals can also be removed from APCBP leach-solution by precipitation in form of phosphates. For that purpose, a phosphorus source such as phosphoric acid, mono-calcium phosphate, ammonium phosphate, potassium phosphate, etc. can be added to the APCBP leach-solution to cause precipitation of heavy metals as phosphates. The solubility of metal phosphates is generally much lower than that of calcium phosphate which enables to precipitate heavy metals as phosphates even in the presence of high concentrations of dissolved calcium. Of course, precipitation of heavy metal phosphates can be combined with flocculation operation as described before and with other heavy metal precipitation agents as described previously.
[0108] In addition to precipitation techniques, heavy metals can be removed from APCBP leach-solution by processes based on chemical reduction. Examples include addition of zinc, aluminium, etc. in elemental form as a reducing agent to precipitate heavy metals in elemental form.
[0109] Another possibility for heavy metal separation from APCBP leach-solution is to remove heavy metals by use of a material that can adsorb the heavy metals. Suitable materials include various chelating resins, such as e.g. resinex CH-80, containing thiol groups that enable to adsorb heavy metals even in the presence of high concentration of calcium in solution.
[0110] In other words, in one embodiment of a method for salt recovery, the removal of heavy metals is performed by at least one of sulfide precipitation by addition of S ions, hydroxide precipitation by addition of hydroxide ions, hydronium ions and/or an acid and phosphate precipitation by addition of phosphate ions. In a particular embodiment, the removal of heavy metals further comprises flocculation by hydroxide ions of Fe, Al, and/or Mg and/or by polymers. In a particular embodiment, the removal of heavy metals comprises adsorption in chelating resins.
[0111] Analogously, in one embodiment of an arrangement for salt recovery, the heavy metals removal arrangement comprises a heavy metals removal ion adding arrangement and a heavy metals removal separator. The heavy metals removal ion adding arrangement is arranged for adding at least one of S ions, hydroxide ions, hydronium ions and/or an acid and phosphate ions to cause precipitation of sulfide, hydroxide, and phosphate, respectively, of heavy metals. The heavy metals removal separator is arranged to separate any precipitation of sulfide, hydroxide, and phosphate of heavy metals. In a particular embodiment, the heavy metals removal arrangement further comprises means for removal of heavy metals by flocculation by hydroxide ions of Fe, Al, and/or Mg and/or by polymers. In a particular embodiment, the heavy metals removal arrangement comprises means for adsorption of heavy metals in chelating resins.
[0112] An additional impurity which may be present in APCBP leach-solution is nitrogen usually in form of ammonia at high pH level. Ammonia can be present in dissolved form or in form of metal complexes. It was found that ammonia could be removed from the APCBP leach-solution by agitation as shown in
[0113] Ammonia can also be removed from APC by-products before the washing operation. In this alternative the APC by-products are moisten and aged to release its ammonia content before the washing operation. Another alternative is to remove ammonia from the APCBP leach-solution by stripping in conventional ammonia stripping columns using e.g. air or steam as stripping medium. Another possibility for removal of ammonia is at a later stage of the treatment processes during water evaporation. Ammonia gas can be removed together with water vapors and be separated from the water during the condensation of the water vapors. Removed ammonia can usually be recovered in a useful form such as aqueous/liquid ammonia or an ammonium salt solution such as ammonium sulfate which can be used as a fertilizer.
[0114] In other words, in one embodiment of a method for salt recovery, the removal of ammonia is performed by stripping by air or steam.
[0115] Analogously, in one embodiment of an arrangement for salt recovery, the ammonia removal arrangement comprises a stripping arrangement by air or steam.
[0116] In summary, there are various ways to remove non-wanted substances from APCBP leach-solution. Removal of impurities in a pretreatment step prior to salt recovery is generally preferred. However, impurities can also be removed at a later stage of the treatment by applying the same principal techniques. An additional alternative is not to remove impurities in pretreatment but to let the impurities end up in the recovered water-soluble salt. Thereafter, the recovered water-soluble salt can be recrystallized and in that way impurities may be separated.
[0117] If impurities such as gypsum, metal sulfides, precipitated calcium carbonate, etc. are removed in a pretreatment by addition of suitable chemicals followed by settling, the sediment can be pumped back to the APC by-products washing operation. In that way, separate removal of impurities is not required and the impurities can be incorporated in the washed APC by-products in a non-leachable form suitable for disposal in a landfill.
[0118] After the pretreatment, a concentrated brine of the desired quality can be formed suitable for subsequent salt recovery operation.
[0119]
[0120] As was also concluded from the experiments on the CaNa-K-Cl system, a high salting-out effect, i.e. a high purity of the remaining CaCl.sub.2 in the solution, was obtained close to the solubility limit for each temperature. In one embodiment, it is preferred to control the enriched aqueous solution to keep the CaCl.sub.2 in the solution, but still be near the solubility limit. This can be achieved by controlling the temperature and/or the concentration. Therefore, in one embodiment, the step 230 of treating the start material comprises the step 236, in which a temperature of the enriched aqueous solution is controlled, and/or the step 237, in which the concentration of CaCl.sub.2 is controlled. The step 236, comprises controlling of a temperature of the enriched aqueous solution to exceed a solubility temperature for the concentration of CaCl.sub.2. In a preferred embodiment, the temperature of the enriched aqueous solution is controlled to be within 20 C., more preferably within 10 C., and most preferably within 5 C. from a solubility temperature for the prevailing concentration of CaCl.sub.2. The step 237 comprises controlling of the concentration of CaCl.sub.2 to be lower than a solubility concentration for a prevailing temperature of the enriched aqueous solution.
[0121]
[0122] In cases in which the APCBP leach-solution is composed of mainly sodium chloride and/or potassium chloride with only a minor content of calcium chloride, the APCBP leach-solution is preferably mixed with a recycled calcium chloride solution 38, obtained from a later described depleted aqueous solution 34, to obtain the desired excess of calcium chloride. Addition of calcium chloride can thus be performed by using recycled CaCl.sub.2 solution from later in the process. However, other, external CaCl.sub.2 sources 89, may also be added through an additive inlet 88. It should be emphasized that mixing of a recycled calcium chloride solution, i.e. the depleted aqueous solution 38, or external sources of CaCl.sub.2 can take place before entering the water reduction arrangement 26, or after the water reduction arrangement 26 as indicated by dotted lines in
[0123] A preferred way of performing water reduction in the water reduction arrangement 26 and in particular evaporation in the evaporator 33 is to operate under vacuum at temperatures below 80 C., since such vacuum evaporation systems are generally cost effective. However, it should be clear than any evaporation technology can be used, e.g. operating without vacuum, at higher temperatures.
[0124] After evaporation, with or without addition of a calcium chloride source, the solution is concentrated to obtain a calcium chloride concentration of more than 15% by weight, preferably more than 30% by weight and more preferably more than 35% by weight. In other words, in one preferred embodiment, the treatment arrangement 24 is arranged for concentrating the initial aqueous solution into an enriched aqueous solution having a concentration of CaCl.sub.2 of at least 35% by weight. Concentrating of the initial aqueous solution is also connected to consumption of energy or other resources. An unnecessary concentrated solution may therefore not be the most cost efficient solution. Therefore, in one preferred embodiment, the treatment arrangement 24 is arranged for concentrating the initial aqueous solution into an enriched aqueous solution having a concentration of CaCl.sub.2 of at most 44% by weight.
[0125] In the embodiment illustrated in
[0126] The second control action is performed by controlling a heat exchanger 82 to which the enriched aqueous solution 25 is fed, preferably after the water reduction arrangement 26 and the input for additives 27. The concentrated calcium chloride solution, i.e. the enriched aqueous solution 25, is preferably cooled by the heat exchanger 82 to a temperature preferably lower than 30 C., more preferably lower than 20 C. It should, however, be emphasized that as can be seen from table 1 a wide range of temperatures and concentrations are possible in order to obtain a relatively pure calcium chloride solution by crystallizing a mixture of sodium chloride and potassium chloride by a salting out mechanism. One approach is to keep the temperature/concentration conditions close to the saturation limit. Therefore, in one embodiment, the dissolution control 86 is arranged for keeping a temperature of the enriched aqueous solution to be within 20 C., preferably within 10 C., and most preferably within 5 C. from a solubility temperature for the concentration of CaCl.sub.2.
[0127]
[0128] Returning to
[0129] The obtained calcium chloride solution, i.e. the depleted aqueous solution 34, has a concentration of preferably over 36 percent by weight and a purity of 90-94%. The rest of the solvated substances being residual sodium chloride and potassium chloride. The obtained calcium chloride solution can be directly used without further treatment in applications such as de-icing, dust control, etc. As mentioned further above, the calcium chloride solution can also be used for increasing the content of Ca ions in the treatment of the start material. In other words, one embodiment of the method comprises the further step of: recycling at least a part of the depleted aqueous solution to be used as additives of Ca ions and Cl ions in a further treating of the start material into an enriched aqueous solution. A corresponding arrangement further comprises a partial return arrangement 37 connecting an output 39 from the salt mix separator 28, possibly via the below described CaCl.sub.2 purifier 30, and an input to the treatment arrangement 24 of the first stage section 20. The partial return arrangement 37 is thereby arranged for recycling at least a part of the depleted aqueous solution 34, i.e. a recycled calcium chloride solution 38, to be used as additive of Ca ions and Cl ions in the treatment arrangement 24.
[0130] The obtained calcium chloride solution, i.e. the depleted aqueous solution 34, can also be further treated in a CaCl.sub.2 purifier 30 to increase its purity as will be discussed later. In other words, one embodiment of the method comprises the further step of purifying the depleted aqueous solution 34 from residual alkali salts. A corresponding embodiment of an arrangement further comprises a CaCl.sub.2 purifier 30 connected to an output from the salt mix separator 28. The CaCl.sub.2 purifier 30 is arranged for purifying the depleted aqueous solution from residual alkali salts.
[0131] A solution of CaCl.sub.2 36 is output from the first stage section 20.
[0132] Control of the ionic composition of the initial aqueous solution, e.g. the APCBP leach solution in the present invention comprises modification of the original ionic composition of NaCl and KCl to CaCl.sub.2 obtained by contacting the start material with water. The modification of the ionic composition of the above described initial aqueous solution is controlled in a way that during the separation of the solid mix of NaCl and KCl from dissolved CaCl.sub.2, the weighed of the solid mix of NaCl and KCl is preferably lower than the weight of produced CaCl.sub.2 solution in order to enable technical separation of the solid salt mixture from the solution. In general, this would mean to form a slurry which can technically be transported into a solid liquid separation device.
[0133] Modifying of the weight ratio may comprise controlled provision of at least additional ions of Ca to modify the original ionic composition obtained by reacting the start material with water. Provision of at least additional ions of Ca can be performed by several means. Addition of calcium chloride from later in the process has been discussed here above.
[0134] An additional alternative for provision of Ca ions can be addition of an acid to the start material in order to dissolve non-water soluble calcium containing compounds. In such a way additional calcium ions are provided over dissolved calcium ions obtained by only contacting the start material with water.
[0135] Provision of additional calcium ions over the original ionic composition of the solution obtained by contacting the start material with water can be done as stated before by recycling calcium chloride from a later step in the process. Solid liquid separation of the salt mixture from the solution preferably requires that a sufficient amount of calcium chloride solution is present with regards to the amount of solid salt mixture to enable the separation to be technically feasible. However, an alternative to separate in a technically feasible manner a mixture composed of relatively little calcium chloride solution in relation to a larger amount of solid salt mixture is to perform the separation in several steps.
[0136] One such example is to separate the solid mixture of salts from liquid calcium chloride in for example two subsequent steps. The first separation step is carried out in a higher temperature than the second separation step. At a higher temperature the solubility of the salt mixture in calcium chloride is higher which means that the amount of solid salt mixture to liquid calcium chloride is lower which can enable an easy technical separation of the solids from the liquid. After the first separation of the solids, the solution can be further cooled to a lower temperature thus enabling the precipitation of additional solid mixture of salts. However, since a first part of the solids has been already removed, the amount of solid salt mixture to liquid calcium chloride is now lower than the original ratio of solids to liquids compared to if the salt separation would have been done in a single step at the lower temperature.
[0137] A practical application of this approach can be to recycle a solution having calcium chloride as a main component through an evaporation chamber operated at ca 80 C. To continuously remove the precipitated mixture of salts at a first temperature of between 80 C. and 40 C., thereafter to recycle the calcium chloride containing filtrate back to be mixed with the feed solution entering the evaporation chamber. Separation of solids at the first temperature can be done by any suitable solid liquid separation technique such as filtration, centrifugation, cyclonic separation, etc.
[0138] In this example, a first part of the filtrate is recycled back to be mixed with the feed solution entering the evaporation chamber and a second part of the filtrate is cooled to a second temperature of between 40 C. to 0 C. preferably about 15 C. which results in the precipitation of a second part of the salt mixture which is removed from the solution with a suitable solid liquid separation device. The two parts of the separated salt mixtures in the two subsequent steps are thereafter mixed together to be treated for the separation of NaCl and KCl according to the principles of the present invention.
[0139] It has been experimentally shown that the crystallized alkali salt mixture crystallizes in a form that can be easily separated from the concentrated calcium chloride solution. A dry matter content of over 90 percent by weight could be reached. The separated salt mixture is thereafter washed with water or preferably a recycled process solution saturated with regard to NaCl and/or KCl to remove residual calcium chloride present in cake water. It has been satisfyingly shown in experiments with artificial solutions that water washing enables to obtain a mixture of NaCl and KCl with less than 0.2% residual CaCl.sub.2.
[0140] However, when operating with APCBP leach-solution having a pH level of 11.8 before evaporation and a pH of 9.3 after evaporation, the crystallized mixture of NaCl and KCl contained also a water-insoluble calcium component of generally above 5% by weight. It was impossible to wash off the calcium component from the crystallized salt mixture by either using water or a salt solution. In further experiments it was, however, found that the calcium component was soluble in hydrochloric acid. The conclusion was that since APCBP leach-solution has generally a high pH, during the concentration of the APCBP leach-solution a precipitate of calcium hydroxide is formed.
[0141] The solubility of calcium hydroxide in water is ca 1.5 grams per kg solution at 20 C. and the solubility decrease to about 1 gram per kg solution at 70 C. Therefore, during the evaporation of MSWIFA wash-water, the high alkalinity results in the precipitation of calcium hydroxide according to e.g. the following chemical reaction:
CaCl.sub.2+2NaOH.fwdarw.Ca(OH).sub.2+2NaCl
Up to about 5% of the calcium content in APCBP leach-solution was found to be precipitated in this form together with NaCl and KCl which in many applications may be an unacceptable level of impurity.
[0142] However, the formation of calcium hydroxide could be easily eliminated by neutralizing the APCBP leach-solution with hydrochloric acid e.g. prior to evaporation. Consumption of hydrochloric acid for that purpose was moderate in the order of about 8 kg of 30% HCl per ton of APCBP leach-solution. It should be clear that neutralization of the APCBP leach-solution can be done before evaporation, after evaporation, or even during post treatment operation of the recovered salts.
[0143] Satisfyingly, it was experimentally proven that after neutralization of APCBP leach-solution with hydrochloric acid, crystallized NaCl+KCl mixture after washing contained only 0.03% residual calcium hydroxide by weight.
[0144] Similarly, if the acid aqueous solutions are used as start material, partial or full neutralization may be requested at some stage during the processes. This can be performed by e.g. adding a base or a basic oxide. It should be clear that neutralization of the aqueous solution can be done before evaporation, after evaporation, or even during post treatment operation of the recovered salts.
[0145] In other words, in one embodiment of the method, the neutralization comprises one of addition of an acid and addition of a base. In a corresponding embodiment of an arrangement for recovery of salt, the neutralization arrangement comprises a neutralization adding arrangement, arranged for adding one of an acid and a base.
[0146] The mixture of NaCl+KCl can thereafter be separated by e.g. state of the art techniques, c.f.
[0147] However, in an alternative embodiment, a much more efficient way of separating the salt mixture is based on a temperature cycling. Returning to
[0148] The alkali salt mixture, i.e. the solid mix 32 composed of sodium chloride and potassium chloride is thus fed into the hot process solution 90 for dissolving mainly its potassium chloride content. The solubility of potassium chloride is increasing with increased temperature and therefore a high temperature is as mentioned above usually preferred.
[0149] The dissolution of potassium chloride from the solid salt mixture can be done e.g. by feeding the solid mix 32 of NaCl and KCl into the dissolver 42, e.g. a stirred reactor 41. The rate of feeding the solid mix 32 into the stirred reactor 41 can be controlled by measuring the potassium concentration in solution. This can be done by using a potassium online measuring electrode, or any other direct/indirect measurement of soluble potassium. Such measurements of potassium content are, as such, well-known in the art and are therefore not described more in detail. The potassium concentration in the solution, i.e. the mixed aqueous solution 43, should be kept below its saturation level at the operational temperature. In that way, complete dissolution of the potassium content from the mixed salts can be assured.
[0150] Since the recycled aqueous solution 90 is at least almost saturated with sodium chloride but considerably below saturation regarding potassium chloride at the operational temperature, a selective dissolution of potassium chloride takes place. This means that potassium chloride from the solid mix 32 is dissolved but at least the main part of the sodium chloride is kept in solid crystal form. It has satisfyingly been experimentally found that despite of the fact that the solid mix 32 of the two salts (NaCl and KCl) are co-crystallized at high temperature during water evaporation, potassium chloride was not locked inside sodium chloride crystals, which enables complete dissolution of the potassium content even when using a saturated hot sodium chloride solution as dissolving medium.
[0151] The above described control of the feeding of the solid mix 32 of salt to the dissolver 42 enables to process a feed of solid mix 32 that change in composition with time, which is typical for processing APC by-products as described before. The actual ratio between KCl and NaCl is not necessary to know in detail, as long as the potassium chloride content is not allowed to reach saturation. This is very different from separation techniques based on evaporation from aqueous solutions with varying salt ratios, where the entire process has to be planned from the actual ratio.
[0152] After dissolution of potassium from the solid mix 32 of salt, the slurry 43 is fed to the separator arrangement 44, where a NaCl separator 45, a solid/liquid separation device such as a centrifuge, belt filter, filter press, disk filter, drum filter, etc. is arranged for separation of solid sodium chloride 48. The sodium chloride 48 is preferably washed e.g. with water to remove residual potassium chloride in the adhering cake water. It was experimentally found that a sodium chloride 48 product with a purity of over 99% could be produced from APCBP leach-solution in that manner. Of course, the sodium chloride 48 can be post processed to increase its quality even further e.g. by recrystallization, etc.
[0153] The solution 96 after separation of solid sodium chloride 48 at high temperature is saturated with sodium chloride and contains also a relatively high concentration of dissolved potassium chloride below, but close to, its saturation level at the high temperature.
[0154] The solution 96 is thereafter cooled in a temperature controller 46 to below 100 C., more preferably below 40 C. and most preferably below 20 C. The temperature should at least be lower than the temperature in the dissolver 42. By cooling the solution, the solubility of sodium chloride is being increased but that of potassium chloride is decreased. This leads to selective precipitation of potassium chloride, while the sodium chloride content instead is brought further from the solubility limit. The slurry 97 is thereafter separated in a KCl separator 47, where a solid/liquid separation device such as a centrifuge, belt filter, filter press, disk filter, drum filter, etc. is arranged for separation of solid potassium chloride 50. The potassium chloride 50 is preferably washed e.g. with water to remove residual sodium chloride in the adhering cake water. It was experimentally found that a potassium chloride 50 product with a purity of over 99% could be produced from APCBP leach-solution in that manner. Of course, the potassium chloride 50 can be post processed to increase its quality even more e.g. by recrystallization, etc. The solution 92 after separation of solid potassium chloride 50 at low temperature is saturated with regard to potassium chloride but under-saturated regarding sodium chloride.
[0155] The solution 92 after separation of solid potassium chloride is brought to a NaCl/KCl recycling arrangement 91. The NaCl/KCl recycling arrangement 91 is arranged to increase the temperature of the solution 92 to the desired operational temperature for being provided to the dissolver 42. This is performed by use of any possible means for heat exchange 94. In a preferred embodiment, the means for heat exchange 94 cooperates with the temperature controller 46, as indicated by the dotted line 95, to reuse some heat extracted from the temperature controller 46 in the means for heat exchange. The temperature is preferably increased to above 50 C. more preferably about 100 C., as discussed before. By increasing the temperature, the recycled aqueous solution 90 becomes essentially saturated regarding sodium chloride again, but considerably under-saturated regarding potassium chloride. This solution 90 is therefore, recycled back to be contacted with more feed of the solid mix 32 of NaCl+KCl.
[0156] Since the system for separation of NaCl/KCl according to this embodiment is based on only heat exchange and not on evaporation of water, closed loop of recirculating process solution may be formed. It should be clear that addition of water/salt solution or diversion of a bleed can be required in order to keep a constant water balance. Hence water can be both added and/or removed with cake water adhering to the salts. Other reasons for bleeding a solution out of the closed cycle are e.g. control of a low steady state concentration of dissolved calcium chloride which enters the system via cake water, etc. Removed bleed can be recycled back to be mixed with e.g. feed solution to the evaporator 33, etc.
[0157] In other words, in one embodiment, the dissolver 42 is arranged for dissolving the KCl and optionally a part of the NaCl in the aqueous solution at a first temperature to obtain a first concentration of KCl. The first concentration of KCl is lower than a solubility concentration of KCl at the first temperature. The separator arrangement 44 comprises a NaCl separator 45 for separating any solid NaCl 48 from the mixed aqueous solution at the first temperature. The separator arrangement 44 further comprises a temperature controller 46 for lowering a temperature of the mixed aqueous solution 96 to a second temperature. The temperature controller 46 is situated downstream of the NaCl separator 45. The second temperature is lower than the first temperature. The separator arrangement 44 further comprises a KCl separator 47 for separating any precipitated KCl 50 from the mixed aqueous solution at the second temperature. The arrangement for recovery of salts further comprises a NaCl/KCl recycling arrangement 91, situated downstream of the KCl separator 47. The NaCl/KCl recycling arrangement 91 is arranged for heating and recycling at least a part of the mixed aqueous solution to the dissolver 42.
[0158]
[0159] The process according to the technology presented herein is robust and can handle the variability in the ratios of salts, e.g. in the incoming APCBP leach-solution. Separation of all three salts is possible with a single evaporator which means low capital cost. The process is simple with simple process control and only heat exchange is needed for NaCl and KCl crystallization. No evaporation of water occurs during this part of the process, which means that the operational costs are low.
[0160] Recently it has been found that the best deicing effect can be obtained by combining sodium chloride and calcium chloride to be used in form of a solution for deicing purposes. Tests were made using various combinations of sodium chloride and calcium chloride in order to find the optimal composition of a deicing solution. In the tests it was found that if there is too much calcium chloride mixed with sodium chloride, the road surface does not dry up in a satisfactory manner.
[0161] According to the optimization tests it was found that there is a breakpoint when the road salt solution contains 20 parts of a calcium chloride solution (36% by weight) mixed with 80 parts of a sodium chloride solution (23% by weight). The specific mixture is equivalent to 17.9% weight sodium chloride, 8% weight calcium chloride, and 74.1% weight of water.
[0162] At this specific mixing ratio, the road dries up as fast as if pure sodium chloride solution had been used. The specific mixture was clearly superior to the use of each of the salts separately in pure form. The main advantages were as follows: [0163] Fast dryingeven on pedestrian and bicycle paths where the drying effect of car traffic is lacking [0164] Lower freezing temperaturesgood results for ice control down to minus 15 degrees [0165] Fewer re-freezing eventstraditional deicing requires often spreading of road salt two times per night because of re-freezing during the morning. Using the specific mixture of sodium chloride and calcium chloride only a single spreading per night is required. The number of call-outs per season is estimated to be reduced by about 30%. [0166] Activating the road salt by sweepingIt was found that due to residual calcium chloride in the asphalt, the road salt could be activated one more time by just sweeping without an additional application of road salt [0167] Improve the air quality around the roadsthe road salt mixture was found to bind small dust particles [0168] To replace a third of sodium chloride with calcium chloride is also more environmentally friendly to the arable land along the road. It was found that it results in better soil structure which means higher yields for crops along the road (20 m distance from the road), as well as less leaching of phosphorus and nitrogen to the ditches
[0169] A main advantage of the present technology is that it enables to produce an efficient road salt from waste incineration fly ash. The invention enables to separate the three salts: sodium chloride, potassium chloride and calcium chloride in pure forms. Separated sodium chloride can be stored in pure solid form during the summer (in which there is no need for road salt). A part of the separated calcium chloride can be used for dust control during the summer. A second part of the calcium chloride is mixed with the stored sodium chloride in a specific formula to form an efficient road salt during winter time. Purified condensate can be used as a water source. Separated potassium chloride has a high commercial value as a fertilizer and therefore can be granulated to be used as a potassium fertilizer or be used as a raw material for production of compound fertilizers, etc.
[0170] In this way, the present technology enables to valorize fly ash in a practical way that enables manageable logistics for outlets for recovered salts present in fly ash.
[0171] Several alternatives exist for post treating the recovered calcium chloride solution to increase its purity. In other words, one embodiment of an arrangement for salt recovery further comprises a CaCl.sub.2 purifier 30 (
[0172]
[0173] The double salt of KCl.CaCl.sub.2 105 can thereafter be broken by dissolving in a purifier dissolver 106 in liquid, typically water 109, to form a calcium chloride solution below saturation at a concentration of below 60% CaCl.sub.2 by weight, preferably below 44% CaCl.sub.2 by weight. After breaking the double salt, potassium chloride is precipitated and the slurry 107 is provided to a second purifier separator 108. In the second purifier separator 108, the precipitated potassium chloride 50 can be separated from the calcium chloride solution by any suitable solid/liquid separation. The calcium chloride solution 110 with residual dissolved potassium after separating precipitated KCl 50 can be recycled back to the purifier concentrating arrangement 100 to be concentrated to over 60% by weight again.
[0174] In other words, in one embodiment of an arrangement for salt recovery, the CaCl.sub.2 purifier 30 comprises a purifier concentrating arrangement 100. The purifier concentrating arrangement 100 is arranged for increasing a CaCl.sub.2 concentration to be above 60% by weight. This is performed by at least one of removing water from the depleted aqueous solution and adding CaCl.sub.2. The CaCl.sub.2 purifier 30 further comprises a purifier temperature control 102, arranged for controlling a temperature of the depleted aqueous solution 101 to exceed a solubility temperature for the concentration of CaCl.sub.2, causing KClCaCl.sub.2 to precipitate. The CaCl.sub.2 purifier 30 also comprises a first purifier separator 104, connected to the purifier concentrating arrangement 100. The first purifier separator 104 is arranged for separating the precipitated KClCaCl.sub.2 105, giving a purified CaCl.sub.2 aqueous solution 36. The CaCl.sub.2 purifier 30 further comprises a purifier dissolver 106, connected to the first purifier separator 104. The purifier dissolver 106 is arranged for re-dissolving the separated precipitated KCl.CaCl.sub.2 105 in an aqueous solution into a non-saturated aqueous solution 107 of CaCl.sub.2, causing KCl to precipitate. The CaCl.sub.2 purifier 30 further comprises a second purifier separator 108, connected to the purifier dissolver 106. The second purifier separator 108 is arranged for separating precipitated KCl 50. In a further embodiment, the CaCl.sub.2 purifier further comprises a purifier recycling arrangement 110, connected between the second purifier separator 108 and the purifier concentrating arrangement 100. The purifier recycling arrangement 110 is arranged for recycling the non-saturated aqueous solution 110 of CaCl.sub.2 to the purifier concentrating arrangement 100.
[0175]
[0176] An additional alternative to further purify the calcium chloride solution is illustrated in
[0177] In other words, in one embodiment of an arrangement for salt recovery, the CaCl.sub.2 purifier 30 comprises a Mg and P adding reactor 120 arranged for adding Mg ions 124 and phosphate ions 125 to the depleted aqueous solution 34, causing precipitation of MgKPO.sub.4. The CaCl.sub.2 purifier 30 further comprises a struvite separator 122, arranged for separating the precipitated MgKPO.sub.4 123, giving a purified CaCl.sub.2 aqueous solution 36.
[0178]
[0179] Of course, any other methods used for removal of potassium chloride from calcium chloride can be used for further purification of the produced calcium chloride solution. Examples include treating with ammonia e.g. according to U.S. Pat. No. 3,279,897 or treating with organic additive e.g. according to U.S. Pat. No. 3,359,079.
[0180] In alternative embodiments, the main process of separating Ca from K and Na can be modified to directly give a higher purity of the CaCl.sub.2 solution. However, the purity of the initial NaCl and KCl mix is degraded and additional measures have to be taken for assuring high purity end products. As shown in
[0181] Thereafter the enriched aqueous solution 25 is transferred to the salt mix separator 28. The salt mixture containing Na, K as well as Ca salts 141, and in this particular embodiment containing the double salt of KCl.CaCl.sub.2, can be separated in a first separator 140 by any suitable solid/liquid operation to remove the salt mixture containing Na, K as well as Ca salts 141 from a purified calcium chloride solution 34. The purified calcium chloride solution 36 can be further processed e.g. to form solid flakes for sale, etc.
[0182] The salt mixture containing Na, K as well as Ca salts 141, and in this particular embodiment containing the double salt of KCl.CaCl.sub.2 can thereafter be broken in a dissolver 142 by dissolving at least a part of the salt mixture in a liquid 143, typically water, to form a calcium chloride solution 144 below saturation at a concentration of below 60% CaCl.sub.2 by weight, preferably below 44% CaCl.sub.2 by weight. After breaking the double salt, sodium chloride and potassium chloride may form a solid mixture, as in previous embodiments. This solid mix 32 of sodium chloride and potassium chloride can be separated in a second separator 145 from the remaining calcium chloride solution 147 by any suitable solid/liquid separation equipment. The calcium chloride solution 147 with residual dissolved potassium after separating precipitated KCl+NaCl can be recycled back by a recycling arrangement 146 to the input for additives, to participate in the concentration to over 60% by weight. The solid mix 32 of NaCl and KCl may be further processed as described above.
[0183] In other words, in one embodiment of an arrangement for salt recovery, the treatment arrangement 24 is arranged for causing a solid mix comprising chloride salts of Na, K and Ca. The salt mix separator 28 comprises a first separator 140 arranged for separating the solid mix 141 comprising chloride salts of Na, K and Ca. The salt mix separator 28 further comprises a dissolver 142 connected to the first separator 140 and arranged for at least partially re-dissolving the separated solid mix 141 comprising chloride salts of Na, K and Ca in an aqueous solution. This causes at least salts comprising the Ca to dissolve and give a non-saturated water solution 144 comprising CaCl.sub.2. The salt mix separator 28 further comprises a second separator 145 connected to the dissolver 142 and arranged for separating remaining precipitated NaCl and KCl from the non-saturated water solution 144 of CaCl.sub.2). In a further embodiment, the salt mix separator 28 comprises a recycling arrangement 146 connected between the second separator 145 and an input of the treatment arrangement 24. The recycling arrangement 146 is arranged for recycling the non-saturated aqueous solution 147 of CaCl.sub.2 to be used as additive of Ca ions and Cl ions in the treatment arrangement 24.
[0184] In this embodiment, the treatment arrangement comprises a concentrator arranged for concentrating the start material 18 into an enriched aqueous solution 25 having a concentration of CaCl.sub.2 above 60% by weight, causing KClCaCl.sub.2 to precipitate. The first separator 140 is thus arranged for separating the precipitated NaCl and KClCaCl.sub.2 141. The dissolver 142 is arranged for partially re-dissolving the separated precipitated NaCl and KCl.CaCl.sub.2 in an aqueous solution into a non-saturated aqueous solution 144 of CaCl.sub.2, causing at least the KCl.CaCl.sub.2 to dissolve and give the non-saturated aqueous solution 147 of CaCl.sub.2. In a further embodiment, the dissolver is arranged to give a non-saturated aqueous solution 147 of CaCl.sub.2 with a concentration exceeding 36% by weight.
[0185]
[0186] In this particular embodiment, the step of treating 230 (
[0187] A further treatment alternative for the process according to the invention can also be illustrated by
[0188] The solid mixture of the three salts 141 is thereafter treated by dissolving in the dissolver 142 in a liquid 143 such as water or salt solution to form a calcium chloride solution 144 below saturation at a concentration of below 60% CaCl.sub.2 by weight, preferably below 44% CaCl.sub.2 by weight. A mixture of sodium chloride and potassium chloride 32 can be thereafter separated in the second separator 145 from the calcium chloride solution 147 and processed according to the principles described before. The calcium chloride solution 147 can be recycled back by the recycling arrangement 14 back into the process or recovered as product.
[0189] In other words, in one embodiment of an arrangement for salt recovery, treatment arrangement 24 comprises a concentrator arranged for concentrating the start material 18 into an enriched aqueous solution 25 having a concentration of CaCl.sub.2 of less than 60% by weight. The temperature control is arranged for controlling a temperature of the enriched aqueous solution 25 to cause precipitation of NaCl, KCl and CaCl.sub.2 with crystal water. The first separator 140 is arranged for separating the precipitated NaCl, KCl and CaCl.sub.2 with crystal water. The dissolver 142 is arranged for partially re-dissolving the separated precipitated NaCl, KCl and CaCl.sub.2 with crystal water in the non-saturated aqueous solution of CaCl.sub.2, causing at least the CaCl.sub.2 with crystal water to dissolve and give the non-saturated aqueous solution of CaCl.sub.2. The solid mix 32 of NaCl and KCl is then separated by the second separator 145.
[0190] With reference to
[0191] Even if processing of APC by-products is the main application of the present disclosure it should be clear that any salt containing solution (NaCl and/or KCl, optionally CaCl.sub.2) or solid salts can be treated according to the disclosed principles. For example, incineration waste (IW) by-products such as bottom ash can in some cases contain high concentration of water soluble salts.
[0192] In addition, solid residues from ZLD systems treating e.g. wastewater from shale gas fracking operation, RO desalination concentrates, ion-exchange softeners concentrate, landfill leachate, mine waters, etc. (not limited to described examples) can be collected and processed for salt recovery in a central plant. Wastes containing a single salt component e.g. NaCl, KCl, or CaCl.sub.2 can be mixed in a central plant treating a multiple components of the salts NaCl, KCl and CaCl.sub.2. The principles in the following disclosure can also be used for separating mixture of pure salts of NaCl and KCl originating from extraction from minerals, salt lakes, etc.
[0193] Processing solids can be done by dissolving in a liquid such as water, salt solution or recycled process solution to form a concentrated calcium chloride solution with crystallized mixture of sodium chloride and potassium chloride even without any evaporation of water just by adding enough solid CaCl.sub.2 with the waste products. CaCl.sub.2 can also be formed e.g. by addition of lime and hydrochloric acid. In addition to evaporation also other concentration technologies can be used for increasing CaCl.sub.2 concentration such as membrane technologies, removing water by precipitation of crystal water with inorganic compounds, etc. The precipitated alkali salts can thereafter be separated according to the principles disclosed in the present application. Of course, additional steps for pretreatment may be required such as removal of magnesium by precipitation in form of Mg(OH).sub.2 at high pH, etc.
[0194] The detailed embodiments described above are only a few examples of how a method and arrangement for recovering salts can be arranged. In conclusion, the embodiments described above are to be understood as illustrative examples of the present invention. It will be understood by those skilled in the art that various modifications, combinations and changes may be made to the embodiments without departing from the scope of the present invention. The scope of the present invention is, however, defined by the appended claims.