STEEL SHEET AND PLATED STEEL SHEET
20190338389 ยท 2019-11-07
Assignee
Inventors
- Yuri Toda (Tokyo, JP)
- Masafumi Azuma (Tokyo, JP)
- Akihiro Uenishi (Tokyo, JP)
- Eisaku Sakurada (Tokyo, JP)
- Tatsuo Yokoi (Tokyo, JP)
- Genichi Shigesato (Tokyo, JP)
Cpc classification
B21B3/02
PERFORMING OPERATIONS; TRANSPORTING
B21B1/02
PERFORMING OPERATIONS; TRANSPORTING
B32B15/01
PERFORMING OPERATIONS; TRANSPORTING
C22C38/002
CHEMISTRY; METALLURGY
C22C38/005
CHEMISTRY; METALLURGY
C22C38/12
CHEMISTRY; METALLURGY
International classification
C22C38/12
CHEMISTRY; METALLURGY
B21B1/02
PERFORMING OPERATIONS; TRANSPORTING
B21B3/02
PERFORMING OPERATIONS; TRANSPORTING
Abstract
When a zone surrounded by a grain boundary that is measured to be 5.0 or more by an EBSD analysis is assumed to be a grain, and when a K value is a value obtained by multiplying an average value of Image Qualities in a grain by 10.sup.3, a Y value is an average crystal misorientation () in the grain, a metallic phase 1 is a metallic phase the K value of which is less than 4.000, a metallic phase 2 is a metallic phase the K value of which is 4.000 or more and the Y value of which is 0.5 to 1.0, a metallic phase 3 is a metallic phase the K value of which is 4.000 or more and the Y value of which is less than 0.5, and a metallic phase 4 is a metallic phase that falls under none of metallic phases 1 to 3, there is provided a steel sheet that has a predetermined chemical composition and includes a microstructure including, in area percent, a metallic phase 1: 1.0% or more and less than 35.0%, a metallic phase 2: 30.0% or more and 80.0% or less, a metallic phase 3: 5.0% or more and 50.0% or less, and a metallic phase 4: 5.0% or less. The steel sheet has a strength as high as 590 MPa or more (further, 780 MPa or more) in terms of tensile strength and has an excellent hole-expansion property.
Claims
1. A steel sheet comprising a chemical composition consisting of, in mass percent: C: 0.01 to 0.20%; Si: 0.005 to 0.10%; Mn: 0.60 to 4.00%; Al: 0.10 to 3.00%; P: 0.10% or less; S: 0.03% or less; N: 0.01% or less; O: 0.01% or less; Ti: 0 to 2.00%; Nb: 0 to 2.00%; V: 0 to 0.30%; Cu: 0 to 2.00%; Ni: 0 to 2.00%; Mo: 0 to 1.00%; Cr: 0 to 2.00%; B: 0 to 0.01%; Ca: 0 to 0.010%; Mg: 0 to 0.010%; Zr: 0 to 0.050%; REM: 0 to 0.1%; Sb: 0 to 0.10%; Sn: 0 to 0.10%; and As: 0 to 0.5%, with the balance: Fe and impurities, and comprising a microstructure that includes, when a zone surrounded by a grain boundary that is measured to be 5.0 or more by an EBSD analysis is assumed to be a grain, and when a K value is a value obtained by multiplying an average value of Image Qualities in a grain by 10.sup.3, a Y value is an average crystal misorientation () in the grain, a metallic phase 1 is a metallic phase the K value of which is less than 4.000, a metallic phase 2 is a metallic phase the K value of which is 4.000 or more and the Y value of which is 0.5 to 1.0, a metallic phase 3 is a metallic phase the K value of which is 4.000 or more and the Y value of which is less than 0.5, and a metallic phase 4 is a metallic phase that falls under none of metallic phases 1 to 3, in area percent: the metallic phase 1: 1.0% or more and less than 35.0%; the metallic phase 2: 30.0% or more and 80.0% or less; the metallic phase 3: 5.0% or more and 50.0% or less; and the metallic phase 4: 5.0% or less.
2. The steel sheet according to claim 1, comprising a microstructure in which the metallic phase 4 is 0%.
3. The steel sheet according to claim 1, wherein 60.0% or more of boundaries of the metallic phase 1 with other metallic phases is a boundary of the metallic phase 1 with the metallic phase 2.
4. The steel sheet according to claim 1, wherein a thickness of the steel sheet is 0.8 to 3.6 mm.
5. The steel sheet according to claim 1, wherein the steel sheet has a tensile strength of 780 MPa or more, and comprises a microstructure including, in area percent: the metallic phase 1: 1.0% or more and less than 35.0%; the metallic phase 2: 30.0% or more and 80.0% or less; the metallic phase 3: 5.0% or more and less than 35.0%; and the metallic phase 4: 5.0% or less.
6. The steel sheet according to claim 1, wherein the steel sheet has a tensile strength of 590 MPa or more and less than 780 MPa, and comprises a microstructure including: the metallic phase 1: 1.0% or more and less than 30.0%; the metallic phase 2: 35.0% or more and 70.0% or less; the metallic phase 3: 35.0% or more and 50.0% or less; and the metallic phase 4: 5.0% or less.
7. A plated steel sheet comprising a galvanized layer on a surface of the steel sheet according to claim 1.
8. A plated steel sheet comprising a galvannealed layer on a surface of the steel sheet according to claim 1.
9. The steel sheet according to claim 3, wherein a thickness of the steel sheet is 0.8 to 3.6 mm.
10. The steel sheet according to claim 3, wherein the steel sheet has a tensile strength of 780 MPa or more, and comprises a microstructure including, in area percent: the metallic phase 1: 1.0% or more and less than 35.0%; the metallic phase 2: 30.0% or more and 80.0% or less; the metallic phase 3: 5.0% or more and less than 35.0%; and the metallic phase 4: 5.0% or less.
11. The steel sheet according to claim 4, wherein the steel sheet has a tensile strength of 780 MPa or more, and comprises a microstructure including, in area percent: the metallic phase 1: 1.0% or more and less than 35.0%; the metallic phase 2: 30.0% or more and 80.0% or less; the metallic phase 3: 5.0% or more and less than 35.0%; and the metallic phase 4: 5.0% or less.
12. The steel sheet according to claim 9, wherein the steel sheet has a tensile strength of 780 MPa or more, and comprises a microstructure including, in area percent: the metallic phase 1: 1.0% or more and less than 35.0%; the metallic phase 2: 30.0% or more and 80.0% or less; the metallic phase 3: 5.0% or more and less than 35.0%; and the metallic phase 4: 5.0% or less.
13. The steel sheet according to claim 3, wherein the steel sheet has a tensile strength of 590 MPa or more and less than 780 MPa, and comprises a microstructure including: the metallic phase 1: 1.0% or more and less than 30.0%; the metallic phase 2: 35.0% or more and 70.0% or less; the metallic phase 3: 35.0% or more and 50.0% or less; and the metallic phase 4: 5.0% or less.
14. The steel sheet according to claim 4, wherein the steel sheet has a tensile strength of 590 MPa or more and less than 780 MPa, and comprises a microstructure including: the metallic phase 1: 1.0% or more and less than 30.0%; the metallic phase 2: 35.0% or more and 70.0% or less; the metallic phase 3: 35.0% or more and 50.0% or less; and the metallic phase 4: 5.0% or less.
15. The steel sheet according to claim 9, wherein the steel sheet has a tensile strength of 590 MPa or more and less than 780 MPa, and comprises a microstructure including: the metallic phase 1: 1.0% or more and less than 30.0%; the metallic phase 2: 35.0% or more and 70.0% or less; the metallic phase 3: 35.0% or more and 50.0% or less; and the metallic phase 4: 5.0% or less.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0079]
DESCRIPTION OF EMBODIMENTS
[0080] 1. Chemical Composition
[0081] A chemical composition of a steel sheet according to the present invention will be described. In the following description, the symbol % for contents means percent by mass.
[0082] C: 0.01 to 0.20%
[0083] C (carbon) is an element necessary to obtain a predetermined amount of a metallic phase 1. When C is less than 0.01%, it is difficult to set the predetermined amount of the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, a lower limit of C is set at 0.01%. To increase the area fraction of metallic phase 1, the lower limit may be set at 0.03% or more, 0.04% or more, or 0.05% or more.
[0084] In contrast, when C is added excessively, it is difficult to set the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, an upper limit of C is set at 0.20%. To increase the area fraction of metallic phase 1, the upper limit may be set at 0.10% or less, 0.08% or less, 0.07% or less, or 0.06% or less.
[0085] Si: 0.005 to 0.10%
[0086] Si (silicon) is an element necessary to obtain a predetermined amount of a metallic phase 3. When Si is less than 0.005%, it is difficult to obtain the predetermined amount of the metallic phase 3. Accordingly, a lower limit of Si is set at 0.10%. To increase the area fraction of metallic phase 3, the lower limit may be set at 0.015% or more, 0.020% or more, 0.025% or more, or 0.030% or more.
[0087] In contrast, when Si is added excessively, the area fraction of the metallic phase 3 becomes excessively high, which makes it difficult to set the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, an upper limit of Si is set at 0.10%. To optimize the area fractions of metallic phase 1 and the metallic phase 3, the upper limit may be set at 0.060% or less, 0.050% or less, or 0.040% or less.
[0088] Mn: 0.60 to 4.00%
[0089] Mn (manganese) is an element necessary to obtain the predetermined amount of a metallic phase 1. When Mn is less than 0.60, it is difficult to set the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, a lower limit of Mn is set at 0.60%. The lower limit is preferably 0.60% or more, more preferably 0.90% or more, still more preferably 1.10% or more, and still more preferably 1.30% or more.
[0090] In contrast, when Mn is added excessively, it is difficult to set the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, an upper limit of Mn is set at 4.00%. The upper limit is preferably 3.00% or less, more preferably 2.50% or less, still more preferably 2.00% or less, and still more preferably 1.80% or less.
[0091] Al: 0.10 to 3.00%
[0092] Al (aluminum) is an element necessary to obtain a predetermined amount of a metallic phase 3. When Al is less than 0.10%, it is difficult to obtain the predetermined amount of the metallic phase 3. Accordingly, a lower limit of Al is set at 0.10%. The lower limit is preferably 0.20% or more, more preferably 0.30% or more, still more preferably 0.40% or more, and still more preferably 0.55% or more.
[0093] In contrast, when Al is added excessively, the area fraction of the metallic phase 3 becomes high, which makes it difficult to set the metallic phase 1 at 1.0% or more in terms of area fraction. Accordingly, an upper limit of Al is set at 3.00%. The upper limit is preferably 2.00% or less, more preferably 1.50% or less, still more preferably 1.00% or less, and still more preferably 0.80% or less.
[0094] P: 0.10% or less
[0095] P is an impurity element and spoils the hole-expansion property by precipitating in grain boundaries and forming a coarse phosphide. When P is more than 0.10%, the precipitation becomes significant; therefore, P is limited to 0.10% or less. Preferably, P is 0.02% or less. The lower P is, the better it is; a lower limit of P need not be limited particularly, and the lower limit is 0%. However, reducing the lower limit to less than 0.0001% is economically disadvantageous, and therefore 0.0001% may be set as the lower limit.
[0096] S: 0.03% or less
[0097] S (sulfur) is an impurity element and spoils the hole-expansion property by forming a coarse sulfide. When S is more than 0.03%, sulfides are formed excessively, making a deterioration in the hole-expansion property significant; therefore, S is limited to 0.03% or less. More preferably, S is 0.005% or less. The lower S is, the better it is; a lower limit of S need not be limited particularly, and the lower limit is 0%. However, reducing S to less than 0.0001% increases production costs greatly, and 0.0001% is a practical lower limit of S.
[0098] N: 0.01% or less
[0099] N (nitrogen) is an impurity element and spoils the hole-expansion property by forming a coarse nitride. When N is more than 0.01%, nitrides are formed excessively, making a deterioration in the hole-expansion property significant; therefore, N is limited to 0.01% or less. More preferably, N is 0.0030% or less. The lower N is, the better it is; a lower limit of N need not be limited particularly, and the lower limit is 0%. However, reducing N to less than 0.0001% increases production costs greatly, and 0.0001% is a practical lower limit of N.
[0100] O: 0.01% or less
[0101] O (oxygen) is an impurity element and spoils the hole-expansion property by forming a coarse oxide. When O is more than 0.01%, oxides are formed excessively, making a deterioration in the hole-expansion property significant; therefore, O is limited to 0.01% or less. More preferably, O is 0.0050% or less. The lower O is, the better it is; a lower limit of O need not be limited particularly, and the lower limit is 0%. However, reducing N to less than 0.0001% increases production costs greatly, and 0.0001% is a practical lower limit of O.
[0102] Ti: 0 to 2.00%
[0103] Ti (titanium) is an element that enhances the hole-expansion property by refining grains and therefore may be contained as appropriate. When Ti is more than 2.00%, nitrides and carbides in which Ti predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Ti is set at 2.00%. The upper limit is preferably 0.50% or less, more preferably 0.10% or less, still more preferably 0.05% or less. Ti does not necessarily have to be contained, and a lower limit of Ti is 0%. To enhance the hole-expansion property, 0.04% or more of Ti may be contained.
[0104] Nb: 0 to 2.00%
[0105] Nb (niobium) is an element that enhances the hole-expansion property by refining grains and therefore may be contained as appropriate. When Nb is more than 2.00%, nitrides and carbides in which Nb predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Nb is set at 2.00%. The upper limit is preferably 0.20% or less, more preferably 0.05% or less, still more preferably 0.03% or less. Nb does not necessarily have to be contained, and a lower limit of Nb is 0%. To enhance the hole-expansion property, 0.005% of Nb may be contained.
[0106] V: 0 to 0.30%;
[0107] V (vanadium) is an element that enhances the hole-expansion property by refining grains and therefore may be contained as appropriate. When V is more than 2.00%, nitrides and carbides in which V predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of V is set at 2.00%. The upper limit is preferably 0.50% or less, more preferably 0.10% or less, still more preferably 0.05% or less. V does not necessarily have to be contained, and a lower limit of V is 0%. To enhance the hole-expansion property, 0.04% or more of V may be contained.
[0108] Cu: 0 to 2.00%
[0109] Cu (copper) has an effect of increasing the area fraction of the metallic phase 1 and may be contained as appropriate. When Cu is more than 2.00%, it is difficult to obtain the predetermined amount of the metallic phase 3. Accordingly, an upper limit of Cu is set at 2.00%. The upper limit is preferably 1.00% or less, more preferably 0.50% or less, still more preferably 0.20% or less, and still more preferably 0.05% or less. Cu does not necessarily have to be contained, and a lower limit of Cu is 0%. Cu may be contained at 0.01% or more as necessary.
[0110] Ni: 0 to 2.00%
[0111] Ni (nickel) has an effect of increasing the area fraction of the metallic phase 1 and may be contained as appropriate. When Cu is more than 2.00%, it is difficult to obtain the predetermined amount of the metallic phase 3. Accordingly, an upper limit of Cu is set at 2.00%. The upper limit is preferably 1.00% or less, more preferably 0.50% or less, still more preferably 0.20% or less, and still more preferably 0.05% or less. Cu does not necessarily have to be contained, and a lower limit of Cu is 0%. Ni may be contained at 0.01% or more as necessary.
[0112] Mo: 0 to 1.00%
[0113] Mo (molybdenum) has an effect of increasing the area fraction of the metallic phase 3 and may be contained as appropriate. When Mo is more than 1.00%, it is difficult to secure the metallic phase 1 at 1% or more in terms of area fraction. Accordingly, an upper limit of Mo is set at 1.00%. The upper limit is preferably 0.5% or less, more preferably 0.3% or less, still more preferably 0.1% or less, and still more preferably 0.05% or less. Mo does not necessarily have to be contained, and a lower limit of Mo is 0%. Mo may be contained at 0.01% or more as necessary.
[0114] Cr: 0 to 2.00%;
[0115] Cr (chromium) has an effect of increasing the area fraction of the metallic phase 3 and may be contained as appropriate. When Cr is more than 2.00%, it is difficult to secure the metallic phase 1 at 1% or more in terms of area fraction. Accordingly, an upper limit of Cr is set at 2.00%. The upper limit is preferably 1.00% or less, more preferably 0.5% or less, still more preferably 0.25% or less, still more preferably 0.10% or less, and still more preferably 0.05% or less. Cr does not necessarily have to be contained, and a lower limit of Cr is 0%. Cr may be contained at 0.01% or more as necessary.
[0116] B: 0 to 0.01%;
[0117] B (boron) has an effect of increasing the area fraction of the metallic phase 1 and may be contained as appropriate. When B is more than 0.01%, nitrides and carbides in which B predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of B is set at 0.01%. The upper limit is preferably 0.0025% or less, more preferably 0.0015% or less, still more preferably 0.0010% or less, and still more preferably 0.0004% or less. B does not necessarily have to be contained, and a lower limit of B is 0%. B may be contained at 0.0003% or more as necessary.
[0118] Ca: 0 to 0.010%
[0119] Ca (calcium) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which Ca does not spoil other properties of the steel sheet according to the present invention. When Ca is more than 0.010%, oxides in which Ca predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Ca is set at 0.010%. The upper limit is preferably 0.005% or less, more preferably 0.002% or less, and still more preferably 0.0005% or less. Ca does not necessarily have to be contained, and a lower limit of Ca is 0%. Ca may be contained at 0.0003% or more as necessary.
[0120] Mg: 0 to 0.010%
[0121] Mg (magnesium) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which Mg does not spoil other properties of the steel sheet according to the present invention. When Mg is more than 0.010%, oxides in which Mg predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Mg is set at 0.010%. The upper limit is preferably 0.005% or less, more preferably 0.002% or less, still more preferably 0.001% or less, and still more preferably 0.0004% or less. Mg does not necessarily have to be contained, and a lower limit of Mg is 0%. Mg may be contained at 0.0003% or more as necessary.
[0122] Zr: 0 to 0.050%
[0123] Zr (zirconium) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which Zr does not spoil other properties of the steel sheet according to the present invention. When Zr is more than 0.050%, oxides in which Zr predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Zr is set at 0.050%. More preferably, Zr is 0.005% or less. Zr does not necessarily have to be contained, and a lower limit of Zr is 0%. Zr may be contained at 0.0005% or more as necessary.
[0124] REM: 0 to 0.1%
[0125] REM (rare earth metal) is elements that contribute to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which REM does not spoil other properties of the steel sheet according to the present invention. When REM is more than 0.1%, oxides in which REM predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of REM is set at 0.1%. More preferably, REM is 0.005% or less. REM does not necessarily have to be contained, and a lower limit of REM is 0%. REM may be contained at 0.0005% or more as necessary.
[0126] Here, REM is a generic name of Sc (scandium), Y (yttrium), and lanthanoids, 17 elements in total, and a content of REM refers to a total content of the above elements. REM is often added in a form of misch metal but is in some cases added in a form of La and Ce, as well as lanthanoid elements, in combination. Even in these cases, the steel sheet according to the present invention exerts effects of the steel sheet according to the present invention. Even when metallic REM such as metallic La and Ce is added, the steel sheet according to the present invention exerts the effects of the steel sheet according to the present invention.
[0127] Sb: 0 to 0.10%
[0128] Sb (antimony) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which Sb does not spoil other properties of the steel sheet according to the present invention. When Sb is more than 0.10%, oxides in which Sb predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Sb is set at 0.10%. More preferably, Sb is 0.005% or less. Sb does not necessarily have to be contained, and a lower limit of Sb is 0%. Sb may be contained at 0.0002% or more as necessary.
[0129] Sn: 0 to 0.10%
[0130] Sn (tin) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which Sn does not spoil other properties of the steel sheet according to the present invention. When Sn is more than 0.10%, oxides in which Sn predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of Sn is set at 0.10%. More preferably, Sn is 0.005% or less. Sn does not necessarily have to be contained, and a lower limit of Sn is 0%. Sn may be contained at 0.0005% or more as necessary.
[0131] As: 0 to 0.5%
[0132] As (arsenic) is an element that contributes to enhancement of the hole-expansion property by inhibiting generation of coarse oxides and coarse sulfides and therefore may be added within a range in which As does not spoil other properties of the steel sheet according to the present invention. When As is more than 0.5%, oxides in which As predominates are formed excessively, which degrades the hole-expansion property; therefore an upper limit of As is set at 0.5%. More preferably, As is 0.005% or less. As does not necessarily have to be contained, and a lower limit of As is 0%. As may be contained at 0.0005% or more as necessary.
[0133] The steel sheet according to the present invention contains the elements described above, with the balance having the chemical composition consisting of Fe and impurities. Note that the impurities mean components that are mixed in producing the steel product industrially, from materials such as ores and scraps or owing to other factors.
2. Microstructure
[0134] For the steel sheet according to the present invention, a K value and a Y value are used as indices to distinguish grains making up a microstructure in terms of dislocation density of a grain.
[0135] First, the K value is defined as a value obtained by multiplying a grain average image quality (GAIQ) value by 10.sup.3, which is obtained by performing analysis using the GAIQ method described below on a measurement value resulting from measurement by the EBSD method. The Y value is defined as a grain average misorientation (GAM) value, which is obtained by performing analysis using the GAM method, to be described later, on the measurement value resulting from the measurement by the EBSD method. The K value is an index that indicates how high a crystallinity is and an index useful for evaluating a dislocation density of a grain. The Y value is an index that is useful for evaluating a crystal misorientation of a grain. Both of the K value and the Y value are therefore used to identify microstructures in the steel sheet according to the present invention.
[0136] Next, a calculation method in the GAIQ method will be described. On a rolling-direction perpendicular cross section that lies at a depth position of a sheet thickness t (t area) from a steel sheet surface, the EBSD analysis is performed on a zone that is 200 m long in a rolling direction and 100 m long in a rolling-surface normal direction at a measurement interval of 0.2 m, so as to obtain crystal orientation information. The EBSD analysis is here performed using an apparatus including a thermal field emission scanning electron microscope (JSM-7001F from JEOL) and an EBSD detector (DVC5-type detector from TSL solutions) and involves measurement with an exposure time of 60 msec, using TSL OIM Data Collection 6 that comes with an EBSD analyzer. Next, in the obtained crystal orientation information, a zone having a crystal misorientation of 5 or more is defined as a grain, and an average value of Image Quality values in a grain is calculated by the GAIQ method. Here, the Image Quality value is one of analytical parameters that are built in OIM Analysis Version 7.0.1, a piece of software coming with an EBSD analyzer, and refers to how high a crystallinity of a measured zone is. That is, a zone having a high dislocation density shows a decreased Image Quality value because a disorder occurs in its crystallinity.
[0137] Next, a calculation method of an average misorientation () of a grain will be described. In the obtained crystal orientation information, a zone having a crystal misorientation of 5 or more is defined as a grain, and an average crystal misorientation of a grain is calculated by the GAM method. The average crystal misorientation of a grain refers to a Grain Average Misorientation (GAM) value, which is one of analytical parameters built in OIM Analysis Version 7.0.1, a piece software coming with an EBSD analyzer, and is obtained by calculating misorientations between neighboring measurement points and calculating an average value of the misorientations for every measurement point in the grain.
[0138] Based on the K value and the Y value obtained in the manner described above, metallic phases can be classified as follows.
[0139] Metallic phase 1: a metallic phase having a K value of less than 4.000
[0140] Metallic phase 2: a metallic phase having a K value of 4.000 or more and a Y value of 0.5 to 1.0
[0141] Metallic phase 3: a metallic phase having a K value of 4.000 or more and a Y value of less than 0.5
[0142] Metallic phase 4: a metallic phase falling under none of metallic phases 1 to 3
[0143] Metallic phase 1: 1.0% or more and less than 35.0%
[0144] The metallic phase 1 is a steel micro-structure necessary for ensuring a strength of the steel sheet. When the metallic phase 1 is less than 1.0% in terms of area fraction, it is difficult to ensure a minimum tensile strength, and therefore a lower limit of the metallic phase 1 is set at 1.0%. The lower limit is preferably 2.0% or more, more preferably 3.0% or more, still more preferably 5.0% or more. In contrast, when the metallic phase 1 is 35.0% or more in terms of area fraction, a proportion of a boundary of a metallic phase 1 with a metallic phase 2 tends to account for less than 60.0% of boundaries of the metallic phase 1 with other metallic phases, which may degrade the hole-expansion property; therefore, the metallic phase 1 is set at less than 35.0%. The metallic phase 1 is preferably less than 32.0%, more preferably less than 30.0%, and still more preferably less than 25.0%.
[0145] When the metallic phase 1 is 30.0% or more in terms of area fraction, it is difficult to set the tensile strength at less than 780 MPa, and therefore, in a case where the intention is to obtain a steel sheet having a tensile strength of 590 MPa or more and less than 780 MPa, the metallic phase 1 is set at less than 30.0%. In a case where the intention is to obtain a steel sheet having a tensile strength of 780 MPa or more, the metallic phase 1 may not be changed from 1.0% or more and less than 35.0%.
[0146] Metallic phase 2: 30.0% or more and 80.0% or less
[0147] The metallic phase 2 is a steel micro-structure important for obtaining an excellent hole-expansion property that is necessary in press molding. When the metallic phase 2 is less than 30.0% in terms of area fraction, it is difficult to ensure a predetermined hole-expansion property; therefore, a lower limit of the metallic phase 2 is set at 30.0%. The lower limit is preferably 40.0% or more, more preferably 50.0% or more, and still more preferably 60.0% or more. In contrast, when the metallic phase 2 is more than 80.0% in terms of area fraction, untransformed austenite is reduced excessively, failing to obtain 1.0% or more of the metallic phase 1, which makes it difficult to ensure a minimum tensile strength; therefore, an upper limit of the metallic phase 2 is set at 80.0%. The upper limit is preferably 78.0% or less, more preferably 76.0% or less, and still more preferably 75.0% or less.
[0148] In the steel sheet having a tensile strength of 590 MPa or more and less than 780 MPa, in a case where the metallic phase 2 is less than 35.0% in terms of area fraction, there is a risk that a problem arises in that the hole-expansion property deteriorates, and when the metallic phase 2 is more than 70.0%, there is a risk that a problem arises in that the elongation deteriorates. Consequently, in the case where the intention is to obtain the steel sheet having a tensile strength of 590 MPa or more and less than 780 MPa, it is preferable to set the metallic phase 2 at 35.0% or more and 70.0% or less. In the case where the intention is to obtain the steel sheet having a tensile strength of 780 MPa or more, the metallic phase 2 may be 30.0% or more and 80.0% or less.
[0149] Metallic phase 3: 5.0% or more and 50.0% or less
[0150] The metallic phase 3 is a steel micro-structure necessary for ensuring an excellent ductility that is necessary in press molding. When the metallic phase 3 is less than 5.0% in terms of area fraction, it is difficult to obtain a predetermined ductility; therefore, a lower limit of the metallic phase 3 is set at 5.0%. A lower limit of the metallic phase 3 is preferably 10.0% or more, more preferably 15.0% or more or 20.0% or more. In contrast, when the metallic phase 3 is 50.0% or more in terms of area fraction, untransformed austenite is reduced excessively, failing to obtain 1.0% or more of the metallic phase 1, which makes it difficult to ensure a minimum tensile strength; therefore, an upper limit of the metallic phase 3 is set at 50.0%. The upper limit is preferably 45.0% or less, more preferably 40.0% or less, and still more preferably 30.0% or less.
[0151] When the metallic phase 3 is 35.0% or more in terms of area fraction, it is difficult to obtain a tensile strength of 780 MPa or more, and therefore, in the case where the intention is to obtain the steel sheet having a tensile strength of 780 MPa or more, it is preferable to set the metallic phase 3 at 5.0% or more and less than 35.0%. Conversely, in the case where the intention is to obtain the steel sheet having a tensile strength of 590 MPa or more and less than 780 MPa, it is preferable to set the metallic phase 3 at 35.0% or more and 50.0% or less.
[0152] Metallic phase 4: 5.0% or less
[0153] The metallic phase 4, which falls under none of the metallic phases 1 to 3, is a hard structure and serves as a starting point of a crack in hole expansion, degrading the hole-expansion property. The metallic phase 4 is therefore limited to 5.0% or less in total in terms of area fraction. The limitation is preferably 4.0% or less, more preferably 3.0% or less, still more preferably 2.0% or less, still more preferably 1.2% or less, and most preferably 0%. Structure observation of a metallic phase 4 under an optical microscope showed that the metallic phase 4 included upper bainite, lower bainite, pearlite, cementite, and retained austenite. Conversely, the EBSD analysis according to the present invention was performed on upper bainite, lower bainite, pearlite, cementite, and retained austenite, with the result that all of them fell under the metallic phase 4.
[0154] As seen from the above, the steel micro-structure of the steel sheet according to the present invention includes the metallic phases 1 to 4 (the metallic phase 4 may be 0%). In particular, to enhance the hole-expansion property while maintaining the tensile strength, it is preferable that the steel micro-structure is made such that a boundary of a metallic phase 1 with a metallic phase 2 accounts for 60.0% or more of boundaries of the metallic phase 1 with other metallic phases. A proportion of the boundary of the metallic phase 1 with the metallic phase 2 to the boundaries of the metallic phase 1 with the other metallic phases is preferably 70.0% or more, more preferably 80.0% or more, and still more preferably 90.0% or more. Although the reason why the hole-expansion property can be enhanced while maintaining the tensile strength by limiting the proportion within such a range is under investigation, but it is considered that the enhancement is brought by the following mechanism.
[0155]
[0156] In the example illustrated in
[0157] To form the microstructure illustrated in
[0158] The steel sheet according to the present invention is a steel sheet on a surface of which a galvanized layer or a galvannealed layer is formed by a conventional method. As the galvanized layer or the galvannealed layer, for example, the following layers are preferable.
(a) A galvanized layer made of Fe at less than 7% by mass, with the balance consisting of Zn, Al, and impurities, or a galvannealed layer obtained by alloying the galvanized layer.
(b) A galvanized layer made of Fe at 7 to 15% by mass, with the balance consisting of Zn, Al, and impurities, or a galvannealed layer obtained by alloying the galvanized layer.
[0159] A main subject of the present invention is a steel sheet having a tensile strength of 590 MPa or more and 980 MPa or less. An upper limit of the tensile strength may be set at 960 MPa or 930 MPa, as necessary. A sheet thickness of the steel sheet is mostly 0.8 to 3.6 mm. A lower limit of the sheet thickness may be set at 1.0 mm, 1.8 mm, 2.0 mm, or 2.2 mm, and an upper limit of the sheet thickness may be set at 3.4 mm, 3.2 mm, or 2.0 mm.
3. Producing Method
[0160] A producing method for the steel sheet according to the present invention will be described below. The present inventors have confirmed that the microstructure according to the present invention can be obtained by making the steel sheet have the chemical composition described above and producing the steel sheet by a method satisfying at least the following conditions.
[0161] A slab to be subjected to hot rolling may be any slab produced by a conventional method and is not limited to a slab that has a specific chemical composition and specific properties. For example, any slab produced by a typical method, such as a continuously cast slab and a thin slab caster, may be acceptable.
(1) Machining Before Rough Rolling Process
[0162] Before a rough rolling process, the slab is machined such that a width of the slab in its width direction is reduced by a decrement W of 30 to 60%. Through this process, lattice defects can be introduced evenly into the slab. These even lattice defects facilitate recrystallization of austenite grains in rolling in one pass before finished rolling. When the decrement W is less than 30%, it is difficult to introduce the lattice defects evenly into the slab, which makes it difficult to obtain 30.0% or more of the metallic phase 2 in terms of area fraction. The decrement W may be set as appropriate within a range that allows a reduction in the width of the slab in the width direction, and an upper limit of the decrement is not limited to a specific one; however, a practical upper limit of the decrement is about 60% for reasons of producibility.
(2) Hot Rolling Process
[0163] (2a) The rolling in one pass before the finished rolling is performed under conditions including temperature: 880 to 950 C. and rolling reduction: 15 to 25%.
[0164] Through this process, a drive force brought by the even lattice defects that have been introduced in the above process (1) forms austenite grains having fewer lattice defects. In a case where the temperature is less than 880 C. or the rolling reduction is more than 25%, the lattice defects are introduced excessively into the austenite, which makes it difficult to obtain 30.0% or more of the metallic phase 2 in terms of area fraction. In a case where the temperature is more than 950 C. or the rolling reduction is less than 15%, the austenite grains coarsen, hindering the recrystallization of the austenite grains. As a result, the austenite grains having fewer lattice defects cannot be obtained, which makes it difficult to obtain 30.0% or more of the metal phase 2 in terms of area fraction.
(2b) The finished rolling is performed under conditions including temperature: 870 to 940 C. and rolling reduction: 6 to 10%.
[0165] Through this process, a moderate amount of lattice defects is introduced into the austenite grains. This small amount of lattice defects act as nuclei in phase transformation into the metallic phase 2 in a next cooling process. In a case where the temperature is less than 870 C. or the rolling reduction is more than 10%, the lattice defects are introduced excessively into the austenite, which makes it difficult to obtain 30.0% or more of the metallic phase 2 in terms of area fraction. In a case where the temperature is more than 940 C. or the rolling reduction is less than 6%, the lattice defects introduced into the austenite grains are decreased excessively, which makes it difficult to obtain 30.0% or more of the metallic phase 2 in terms of area fraction.
(3) Cooling Process
[0166] (3a) A time between an end of the finish rolling to a start of water cooling is set at 0.5 seconds or less.
[0167] After the finished rolling, the water cooling is started within 0.5 seconds. By starting the water cooling immediately after the end of the rolling, it is possible to inhibit the austenite grains from coarsening, enabling the predetermined amount of the metallic phase 3 to be obtained in the subsequent cooling process. When the time until the start of the water cooling is more than 0.5 seconds, the coarsening of the austenite grains occurs, and nucleation sites are decreased, which makes it difficult to obtain the predetermined amount of the metallic phase 3. The time from the end of the finish rolling to the start of the water cooling may be set as appropriate as long as the time allows the cooling, and therefore a lower limit of the time is not limited to specific one; it is however difficult to set the time at 0.01 second or less in an actual operation, and therefore a practical lower limit of the time is about 0.01 second.
(3b) An average cooling rate for a temperature range of 870 to 720 C. is set at 50 to 140 C./sec.
[0168] When the average cooling rate for a temperature range of 870 to 720 C. is less than 50 C./sec, the coarsening of the austenite grains occurs, and nucleation sites of the metallic phase 3 are decreased, which makes it difficult to obtain the predetermined amount of the metallic phase 3. In contrast, when the average cooling rate is more than 140 C./sec, diffusion of carbon is inhibited excessively, and the austenite is stabilized, which makes it difficult to obtain the predetermined amount of the metallic phase 3 in a subsequent process.
(3c) A cooling time for a temperature range of 720 C. or less and more than 630 C. is set at 2 to 10 seconds. That is, an average cooling rate for this temperature region is set at 45 to 9 C./sec.
[0169] Through this process, it is possible to produce the predetermined amount of the metallic phase 3. Here, in a case where the cooling time is less than 2 seconds, transformation into the metallic phase 3 does not progress sufficiently, failing to obtain the predetermined amount of the metallic phase 3. In contrast, in a case where the cooling time is more than 10 seconds, the transformation from the austenite into the metallic phase 3 progresses excessively, which makes it difficult to obtain the predetermined amount of the metallic phase 1 in the subsequent process.
[0170] Here, in a case where the cooling time for the temperature range of 720 C. or less and more than 630 C. is 5 seconds or more, it is not possible to set the metallic phase 3 at less than 35.0% in terms of area fraction. Accordingly, in a case where the intention is to obtain the steel sheet having a tensile strength of 780 MPa or more, this cooling time is set at less than 5 seconds, and in a case where the intention is to obtain the steel sheet having a tensile strength of 590 MPa or more and less than 780 MPa, this cooling time is set at 5 seconds or more.
(3d) A cooling time for a temperature range of 630 C. or less and more than 600 C. is set at 2 seconds or more and less than 6 seconds. That is, an average cooling rate for this temperature range is set at 15 to 5 C./sec.
[0171] Through this process, it is possible to produce the metallic phase 2. In a case where the cooling time is less than 2 seconds, carbon contained in untransformed austenite cannot diffuse sufficiently, which causes the metallic phase 4 to be produced in a large amount. In contrast, in a case where the cooling time is 6 seconds or more, the metallic phase 4 is produced in a large amount from the austenite, leading to a deterioration in the hole-expansion property.
(3e) Cooling (e.g., water cooling) is performed such that an average cooling rate for a temperature range of 600 C. or less and more than 450 C. is 50 to 100 C./sec.
[0172] Through this process, it is possible to set the metallic phase 4 at 5.0% or less. When the average cooling rate is less than 50 C./sec, the area fraction of the metallic phase 4 increases excessively, degrading the hole-expansion property. In contrast, when the average cooling rate is more than 100 C./sec, diffusion of carbon is inhibited excessively, and the austenite is stabilized, which makes it difficult to obtain the predetermined amount of the metallic phase 1 in a subsequent process.
(d) Coiling Process
[0173] The steel sheet is coiled at a temperature of 25 C. or more and 400 C. or less. Through this process, it is possible to bring about transformation from the austenite into the metallic phase 1. When the coiling temperature is more than 400 C., setting the metallic phase 4 at 5.0% or less fails, degrading the hole-expansion property. The coiling is difficult to perform at a room temperature or lower in an actual operation, and therefore, a lower limit of the coiling temperature is set at 25 C.
(5) Additional Processes
[0174] The steel sheet that has been coiled in the above process (4) may be uncoiled, pickled, and then subjected to cold rolling. By subjecting the steel sheet to the cold rolling after performing the pickling to remove oxides on a surface of the steel sheet, it is possible to plan enhancement in the tensile strength, enhancement in chemical treatment properties, enhancement in platability, and the like. The pickling may be performed once or a plurality of times.
[0175] A rolling reduction in the cold rolling is preferably 30 to 80%. When the rolling reduction is less than 30%, the tensile strength is not enhanced; therefore the rolling reduction is set at 30% or more. The rolling reduction is preferably 40% or more. In contrast, when the rolling reduction is more than 80%, the tensile strength increases excessively, degrading the ductility and the hole-expansion property; therefore the rolling reduction is set at 80% or less. The rolling reduction is preferably 70% or less.
[0176] The microstructure of the steel sheet according to the present invention that is defined with the K value and the Y value is a structure obtained through the above processes (1) to (4); therefore, the K value and the Y value do not change greatly even when the cold rolling is performed on the steel sheet, and the microstructure remains substantially unchanged after the cold rolling. Accordingly, even when the tensile strength increases by performing the cold rolling on the steel sheet, the hole-expansion property does not deteriorate.
[0177] The steel sheet subjected to the cold rolling may be put into a continuous annealing line to be annealed at 750 to 900 C. The present inventors empirically confirmed that the K value and the Y value do not change greatly by the annealing at 750 to 900 C. Therefore, performing the annealing on the steel sheet subjected to the cold rolling does not degrade the hole-expansion property. An annealing temperature is preferably 800 to 850 C. from the viewpoint of inhibiting the K value and the Y value from changing as much as possible.
[0178] An annealing time is not limited to a specific one. The annealing time may be set as appropriate such that the K value and the Y value are inhibited from changing as much as possible.
[0179] In the producing method for the plated steel sheet according to the present invention, the steel sheet produced by the producing method for a steel sheet according to the present invention is galvanized by a conventional method. In the producing method for the galvannealed steel sheet according to the present invention, the steel sheet produced by the producing method for a steel sheet according to the present invention is galvannealed by a conventional method.
[0180] The K value and the Y value of the microstructure do not change at a plating temperature and an alloying temperature in the conventional method, and therefore the hole-expansion property of the steel sheet does not deteriorate at the temperatures.
EXAMPLE
[0181] Next, examples of the present invention will be described, but conditions described in the examples are merely an example of conditions that was taken for confirming feasibility and effects of the present invention, and the present invention is not limited to this example of conditions. The present invention can include various conditions as long as the conditions achieve the objective of the present invention without departing from the gist of the present invention.
Example 1
[0182] From slabs having compositions shown in Table 1 and Table 2, steel sheets were produced under conditions shown in Table 3 and Table 4.
TABLE-US-00001 TABLE 1 Steel Chemical composition (mass %, balance: Fe and impurities) No. C Si Mn Al P S N O Ti Nb V A1 0.048 0.024 1.46 0.34 0.010 0.002 0.002 0.001 0.05 0.01 A2 0.048 0.024 1.48 0.34 0.009 0.003 0.003 0.001 0.13 0.02 A3 0.017 0.030 1.60 0.74 0.008 0.003 0.003 0.003 A4 0.067 0.042 1.34 0.55 0.020 0.003 0.001 0.003 A5 0.121 0.049 1.51 0.42 0.015 0.003 0.001 0.002 A6 0.282* 0.043 1.65 0.90 0.020 0.002 0.002 0.003 A7 0.053 0.010 1.58 0.83 0.008 0.003 0.001 0.004 A8 0.044 0.046 1.87 0.79 0.009 0.002 0.001 0.002 0.01 A9 0.058 0.100 1.84 0.40 0.014 0.004 0.001 0.003 A10 0.061 0.122* 1.62 0.62 0.008 0.004 0.002 0.002 A11 0.064 0.022 0.27* 0.38 0.010 0.002 0.002 0.003 A12 0.039 0.051 0.80 1.02 0.013 0.005 0.001 0.002 A13 0.066 0.047 1.28 0.88 0.006 0.004 0.003 0.001 A14 0.042 0.034 2.84 0.40 0.014 0.002 0.002 0.004 A15 0.061 0.050 4.22* 0.99 0.018 0.002 0.001 0.002 A16 0.078 0.035 1.76 0.19 0.009 0.003 0.002 0.002 A17 0.078 0.035 1.98 0.67 0.009 0.004 0.001 0.000 A18 0.063 0.046 1.71 2.12 0.008 0.002 0.003 0.001 A19 0.058 0.026 1.53 3.18* 0.005 0.004 0.002 0.003 A20 0.043 0.016 1.80 0.43 0.008 0.002 0.001 0.004 0.05 A21 0.057 0.021 1.88 0.67 0.005 0.004 0.003 0.002 0.06 A22 0.071 0.023 1.77 0.36 0.014 0.004 0.001 0.003 0.06 A23 0.046 0.027 1.94 0.77 0.019 0.003 0.003 0.002 A24 0.069 0.014 1.64 0.99 0.007 0.003 0.003 0.005 A25 0.075 0.042 1.30 0.37 0.011 0.002 0.002 0.004 A26 0.060 0.052 1.19 0.36 0.012 0.005 0.003 0.001 A27 0.042 0.032 1.55 0.47 0.014 0.002 0.002 0.002 A28 0.055 0.026 1.68 0.78 0.006 0.003 0.002 0.005 A29 0.056 0.029 1.50 0.91 0.009 0.002 0.002 0.002 A30 0.044 0.024 1.46 0.34 0.010 0.002 0.002 0.001 A31 0.046 0.024 1.43 0.34 0.010 0.002 0.002 0.001 A32 0.048 0.027 1.46 0.34 0.010 0.002 0.002 0.001 The mark * indicates that the value fell out of the range defined in the present invention.
TABLE-US-00002 TABLE 2 Steel Chemical composition (mass %, balance: Fe and impurities) No. Cu Ni Mo Cr B Ca Mg Zr REM Sb Sn As A1 0.0001 0.001 0.001 0.001 A2 0.11 0.002 0.002 A3 0.01 0.001 0.001 0.001 A4 0.01 0.02 0.0001 0.001 0.003 0.002 A5 0.01 0.01 0.0001 0.001 0.002 0.001 A6 0.02 0.03 0.0002 0.002 0.001 0.003 A7 0.01 0.02 0.0001 0.001 0.001 A8 0.01 0.01 0.001 0.001 0.001 A9 0.02 0.02 0.0001 0.001 0.001 0.002 A10 0.01 0.01 0.0001 0.001 0.002 0.001 A11 0.01 0.01 0.0001 0.001 0.001 A12 0.02 0.02 0.0002 0.002 0.003 0.001 A13 0.01 0.01 0.0002 0.001 0.001 A14 0.01 0.01 0.0001 0.001 0.003 A15 0.02 0.01 0.0001 0.001 0.001 0.002 A16 0.01 0.01 0.0001 0.001 0.002 0.002 A17 0.03 0.02 0.0001 0.001 0.001 0.001 A18 0.01 0.01 0.0001 0.001 0.003 0.002 A19 0.01 0.01 0.0001 0.001 0.001 0.001 A20 0.01 0.01 0.001 A21 0.01 0.01 A22 0.01 0.01 0.002 0.001 0.001 A23 0.32 0.01 0.001 0.001 0.001 A24 0.01 0.43 0.001 0.001 0.001 A25 0.01 0.01 0.30 0.001 0.001 0.001 A26 0.01 0.01 0.20 0.001 0.001 0.001 A27 0.01 0.02 0.0008 0.002 0.001 0.001 A28 0.02 0.01 0.002 0.001 0.002 0.001 A29 0.01 0.01 0.002 0.001 0.001 0.001 A30 A31 0.030 A32 0.040
TABLE-US-00003 TABLE 3 Process Process Process Process (3a) (3b) Process (2a) (2b) Time From Average (1) Rolling Rolling Finishing To Cooling Steel Decrement Temp. Reduction Temp. Reduction Water Cooling Rate No. No. (%) ( C.) (%) ( C.) (%) (Sec) ( C./Sec) 1 A1 40 920 20 902 8 0.20 60 2 A2 40 915 20 892 8 0.20 63 3 A3 59 907 24 892 10 0.14 125 4 A4 42 885 19 863 8 0.24 121 5 A5 47 938 18 923 8 0.41 93 6 A6 29 937 19 917 11 0.24 136 7 A7 44 897 17 888 10 0.16 132 8 A8 41 936 25 916 8 0.37 106 9 A9 39 928 17 910 10 0.26 78 10 A10 58 874 19 877 10 0.02 118 11 A11 43 916 13 900 6 0.25 66 12 A12 33 942 21 940 10 0.09 84 13 A13 45 909 19 894 8 0.28 79 14 A14 42 942 21 928 9 0.28 59 15 A15 47 923 18 902 5 0.44 119 16 A16 40 901 21 873 10 0.14 115 17 A17 35 906 20 878 7 0.04 56 18 A18 32 886 17 868 9 0.17 122 19 A19 51 902 20 892 7 0.46 131 20 A20 34 894 21 876 5 0.14 96 21 A21 36 906 21 895 10 0.35 72 22 A22 47 950 21 935 9 0.32 111 23 A23 53 942 20 929 9 0.25 59 24 A24 44 929 20 911 6 0.22 121 25 A25 56 917 23 904 8 0.45 75 26 A26 34 910 20 897 11 0.04 134 27 A27 34 955 24 923 6 0.46 67 28 A28 57 903 26 901 9 0.33 56 29 A29 51 951 14 942 8 0.26 60 30 A30 57 909 21 896 10 0.09 118 31 A31 58 899 19 877 10 0.15 101 32 A32 56 881 20 871 10 0.11 96 33 A1 21# 885 22 868 10 0.38 60 34 A1 55 912 20 892 3# 0.05 84 35 A1 48 931 15 911 12# 0.34 50 36 A1 47 899 21 864 9 0.26 139 37 A1 36 874 19 879 8 0.04 73 38 A1 53 936 22 919 10 0.34 125 39 A1 40 933 23 910 9 0.26 119 40 A1 42 948 24 922 6 0.44 46 41 A1 42 949 19 920 10 0.12 71 42 A1 50 891 24 879 5 0.43 90 43 A1 38 922 23 903 7 0.23 52 44 A1 37 912 20 897 8 0.22 62 45 A1 59 905 24 892 10 0.18 127 The mark # indicates that the value fell out of the recommended condition.
TABLE-US-00004 TABLE 4 Process Process Process Process (4) (3c) (3d) (3e) Average Cooling Cooling Cooling Cooling Sheet Steel Time Time Time Rate Plating Thickness No. No. (Sec) (Sec) (Sec) ( C./Sec) Galvanizing Galvannealing (mm) 1 A1 6.4 3.0 70 40 No No 3.0 2 A2 6.3 0.9# 70 43 No No 3.0 3 A3 5.9 3.0 94 384 No No 2.1 4 A4 7.2 3.6 66 233 No No 2.0 5 A5 7.3 4.0 53 313 No No 2.4 6 A6 6.7 2.3 79 160 No No 2.1 7 A7 7.1 3.9 60 100 No No 2.5 8 A8 7.7 5.5 84 63 No No 2.5 9 A9 7.1 2.8 87 106 No No 1.9 10 A10 7.7 5.7 74 264 No No 2.1 11 A11 7.5 3.0 97 178 No No 2.5 12 A12 8.3 3.5 70 366 No No 2.3 13 A13 7.8 4.5 78 89 No No 2.5 14 A14 6.7 4.9 58 269 No No 2.3 15 A15 6.0 5.1 99 333 No No 2.2 16 A16 7.4 3.7 70 156 No No 2.5 17 A17 6.2 3.5 79 298 No No 2.3 18 A18 5.9 5.9 72 362 No No 2.0 19 A19 6.8 4.6 96 271 No No 2.3 20 A20 7.1 5.2 98 139 No No 2.4 21 A21 7.1 4.4 75 66 No No 2.2 22 A22 6.2 2.8 70 180 No No 2.3 23 A23 7.9 4.7 94 191 No No 2.5 24 A24 7.6 2.2 51 85 No No 2.6 25 A25 7.5 5.4 59 131 No No 2.3 26 A26 7.3 5.6 50 190 No No 2.1 27 A27 7.3 4.0 52 296 No No 2.5 28 A28 6.7 3.2 71 213 No No 2.5 29 A29 7.4 2.4 85 36 No No 2.1 30 A30 5.9 3.0 90 205 No No 2.1 31 A31 6.2 2.8 94 340 No No 2.1 32 A32 6.0 3.0 85 365 No No 2.1 33 A1 6.6 5.3 62 325 No No 2.6 34 A1 7.6 4.5 59 79 No No 2.4 35 A1 7.1 2.4 80 221 No No 2.3 36 A1 6.3 0.6# 77 217 No No 2.3 37 A1 7.8 6.7# 57 95 No No 1.9 38 A1 7.3 6.2 38# 335 No No 2.3 39 A1 7.5 5.9 54 429# No No 2.4 40 A1 6.9 4.3 92 344 Yes No 2.5 41 A1 7.9 3.0 57 113 Yes No 2.3 42 A1 6.0 6.0 81 80 Yes Yes 2.1 43 A1 7.3 1.8# 71 21 No No 2.9 44 A1 6.4 7.2# 71 30 No No 2.9 45 A1 2.4# 9.6# 81 217 No No 2.1 The mark # indicates that the value fell out of the recommended condition.
[0183] In Table 3 and Table 4, PROCESS (1) means the machining performed before the rough rolling process and shows, in the tables, its decrements W (%) in length of the slabs in the width direction. PROCESS (2a) and PROCESS (2b) means the rolling in one pass before the finished rolling and the finished rolling, respectively, and show, in the tables, their temperatures ( C.) and their rolling reductions (%). PROCESS (3a) refers to retention performed from the end of the finish rolling until the start of the water cooling and shows, in the tables, its retention times. PROCESS (3b) refers to the cooling process for the temperature range of 870 to 720 C. and shows, in the tables, its average cooling rates ( C./sec) in the temperature range. PROCESS (3c) refers to the cooling process for the temperature range of 720 C. or less and more than 630 C. and shows, in the tables, its cooling times (sec) in the temperature range. PROCESS (3d) refers to the cooling process for the temperature range of 630 C. or less and more than 600 C. and shows, in the tables, its cooling times (sec) in the temperature range. PROCESS (3e) refers to the cooling process for the temperature range of 600 C. or less and more than 450 C. and shows, in the tables, its average cooling rates ( C./sec) in the temperature range. PROCESS (4) refers to the coiling process and shows, in the tables, its coiling temperatures ( C.).
[0184] On the obtained steel sheets, their steel micro-structures, mechanical properties, and hole-expansion properties were measured.
<Measurement of Steel Micro-Structure>
[0185] On a rolling-direction perpendicular cross section that lies at a depth position of a sheet thickness t (t area) from a steel sheet surface, the EBSD analysis is performed on a zone that is 200 m long in a rolling direction and 100 m long in a rolling-surface normal direction at a measurement interval of 0.2 m, so as to obtain crystal orientation information. The EBSD analysis was here performed using an apparatus including a thermal field emission scanning electron microscope (JSM-7001F from JEOL) and an EBSD detector (HIKARI detector from TSL solutions) at an analyzing speed of 200 to 300 points/sec. Next, in the obtained crystal orientation information, a zone having a crystal misorientation of 5 or more is defined as a grain, an average misorientation of the grain is calculated, and proportions of grains having the misorientations of less than 0.5 or 0.5 to 1.0 are calculated.
[0186] The average crystal misorientation of a grain in the present invention is an average value of Grain Average Misorientations (GAM), each of which is an orientation spread of the grain, and is obtained by calculating misorientations between neighboring measurement points and calculating an average value of the misorientations for every measurement point in the grain. Values of the GAM were calculated with OIM Analysis Version 7.0.1, a piece of software coming with an EBSD analyzer.
[0187] An average value of Image Qualities in a grain in the present invention actually means an average value of values obtained by analyzing, by the Grain average image quality (GAIQ) method, measurement values from measurement by the EBSD method.
[0188] In the GAIQ, on an assumption that a zone having a crystal misorientation of 50 or more is defined as a grain in crystal orientation information obtained by the EBSD analysis, a proportion of grains having an in-grain average dislocation density of less than 4000 is calculated. The values of the GAIQ can be calculated with OIM Analysis Version 7.0.1, a piece of software coming with an EBSD analyzer.
[0189] Based on the K value and the Y value obtained in the manner described above, metallic phases were classified as follows.
[0190] Metallic phase 1: a metallic phase having a K value of less than 4.000
[0191] Metallic phase 2: a metallic phase having a K value of 4.000 or more and a Y value of 0.5 to 1.0
[0192] Metallic phase 3: a metallic phase having a K value of 4.000 or more and a Y value of less than 0.5
[0193] Metallic phase 4: a metallic phase falling under none of metallic phases 1 to 3
<Measurement of Mechanical Properties>
[0194] The tensile strength and the elongation are evaluated in such a manner that a JIS No. 5 specimen is taken in a direction perpendicular to a rolling direction of a steel sheet and a tensile test is performed in conformity with JIS Z 2242 to measure a tensile strength (TS) and a total elongation (El).
<Hole-Expansion Property>
[0195] The hole-expansion property is evaluated in such a manner that a hole expansion test is performed in conformity with JFS-T1001-1996 of The Japan Iron and Steel Federation Standard to measure a hole expansion rate (HER).
[0196] Results of the above are shown in Table 5.
TABLE-US-00005 TABLE 5 Steel Micro- Proportion Of Mechanical Structure (Area %) Boundary Between Properties Steel Metallic Metallic Metallic Metallic Metallic Phase 1 And TS EL No. No. Phase 1 Phase 2 Phase 3 Phase 4 Metallic Phase 2 (%) (MPa) (%) (%) 1 A1 2.3 52.6 45.1 0.0 92 644 108.8 27.9 2 A2 3.5 23.0* 48.5 25.0* 43** 600 91.0 30.3 3 A3 1.5 49.4 49.1 0.0 92 637 111.1 31.3 4 A4 2.6 51.8 45.6 0.0 97 618 118.3 31.7 5 A5 2.2 55.4 42.4 0.0 91 597 105.7 27.4 6 A6 0.0* 39.6 36.3 24.1* 0** 620 52.4 33.4 7 A7 3.3 58.7 38.0 0.0 71 666 103.2 28.5 8 A8 2.8 56.0 41.2 0.0 86 652 107.8 31.9 9 A9 2.1 50.9 47.0 0.0 90 638 110.2 32.1 10 A10 0.0* 41.5 58.5* 0.0 0** 575 108.8 34.5 11 A11 0.0* 45.6 54.4* 0.0 0** 517 109.9 34.1 12 A12 2.6 49.0 48.4 0.0 77 605 108.5 30.4 13 A13 2.8 52.7 44.5 0.0 84 625 107.4 30.9 14 A14 3.3 55.3 41.4 0.0 88 637 107.9 27.7 15 A15 2.8 42.5 36.6 18.1* 90 969 106.6 30.2 16 A16 3.3 60.1 36.6 0.0 93 618 107.9 29.1 17 A17 3.2 56.9 39.9 0.0 91 595 103.2 31.5 18 A18 2.0 55.6 42.4 0.0 89 608 103.1 33.6 19 A19 0.4* 44.1 55.5* 0.0 0** 511 102.4 35.2 20 A20 2.3 52.7 45.0 0.0 91 648 109.8 30.8 21 A21 2.2 52.4 45.4 0.0 90 641 109.9 30.2 22 A22 2.6 52.0 45.4 0.0 92 653 111.0 31.2 23 A23 3.5 57.4 39.1 0.0 91 627 108.3 30.9 24 A24 3.6 57.4 39.0 0.0 92 623 109.3 30.6 25 A25 2.0 49.2 48.8 0.0 90 616 110.1 30.7 26 A26 2.4 49.1 48.5 0.0 89 620 110.2 28.2 27 A27 3.7 58.0 38.3 0.0 70 649 103.9 29.7 28 A28 2.2 52.7 45.1 0.0 94 639 116.4 28.0 29 A29 2.4 52.3 45.3 0.0 90 643 117.2 27.9 30 A30 2.1 52.1 45.8 0.0 92 637 111.1 30.8 31 A31 1.8 49.6 48.6 0.0 91 630 109.2 31.0 32 A32 2.3 50.1 47.6 0.0 90 642 112.6 30.7 33 A1 2.2 8.5* 45.2 44.1* 4** 646 90.5 28.1 34 A1 2.3 13.2* 45.1 39.4* 6** 647 92.1 28.0 35 A1 2.6 18.5* 45.0 33.9* 11** 648 90.9 28.3 36 A1 2.2 7.7* 45.2 44.9* 10** 641 89.8 28.2 37 A1 2.4 10.7* 45.2 41.7* 13** 647 89.2 29.4 38 A1 2.6 12.4* 45.1 39.9* 21** 639 89.2 27.7 39 A1 2.4 44.9 45.3 7.4* 62 643 89.5 28.5 40 A1 2.4 52.4 45.2 0.0 94 650 108.7 28.1 41 A1 2.4 51.3 45.2 1.1 96 644 103.3 27.7 42 A1 2.5 51.2 45.0 1.3 91 651 101.1 27.9 43 A1 27.8 22.7* 45.0 4.5 43** 637 58.6 28.4 44 A1 0.4* 54.6 45.0 0.0 99 554 101.2 29.9 45 A1 2.2 95.5* 2.3* 0.0 97 601 120.3 12.1 The mark * indicates that the value fell out of the range defined in the present invention. The mark ** indicates that the value fell out of the preferable range in the present invention.
[0197] As shown in Table 5, inventive examples of the present invention have tensile strengths of 590 MPa or more and sufficient hole-expansion properties.
Example 2
[0198] From slabs having chemical compositions shown in Table 6 and Table 7, steel sheets were produced under conditions shown in Table 8 and Table 9.
TABLE-US-00006 TABLE 6 Steel Chemical composition (mass %, balance: Fe and impurities) No. C Si Mn Al P S N O Ti Nb V B1 0.042 0.020 1.46 0.31 0.011 0.003 0.003 0.001 0.10 0.02 B2 0.048 0.024 1.48 0.34 0.009 0.003 0.003 0.001 0.13 0.02 B3 0.019 0.028 1.60 0.74 0.008 0.003 0.003 0.003 B4 0.068 0.040 1.32 0.56 0.020 0.003 0.001 0.003 B5 0.120 0.047 1.49 0.39 0.015 0.003 0.001 0.002 B6 0.280* 0.045 1.68 0.92 0.020 0.002 0.002 0.003 B7 0.050 0.013 1.61 0.80 0.008 0.003 0.001 0.004 B8 0.046 0.045 1.88 0.76 0.009 0.002 0.001 0.002 0.01 B9 0.060 0.097 1.85 0.37 0.014 0.004 0.001 0.003 B10 0.059 0.120* 1.65 0.61 0.008 0.004 0.002 0.002 B11 0.063 0.019 0.30* 0.36 0.010 0.002 0.002 0.003 B12 0.042 0.048 0.81 0.99 0.013 0.005 0.001 0.002 B13 0.069 0.047 1.30 0.89 0.006 0.004 0.003 0.001 B14 0.045 0.036 2.83 0.41 0.014 0.002 0.002 0.004 B15 0.059 0.050 4.21* 1.00 0.018 0.002 0.001 0.002 B16 0.050 0.050 1.55 0.05* 0.007 0.002 0.002 0.003 B17 0.076 0.033 1.76 0.21 0.009 0.003 0.002 0.002 B18 0.076 0.034 1.98 0.70 0.009 0.004 0.001 0.000 B19 0.063 0.048 1.72 2.10 0.008 0.002 0.003 0.001 B20 0.058 0.025 1.55 3.20* 0.005 0.004 0.002 0.003 B21 0.046 0.016 1.77 0.40 0.008 0.002 0.001 0.004 0.05 B22 0.058 0.021 1.86 0.66 0.005 0.004 0.003 0.002 0.06 B23 0.070 0.025 1.75 0.36 0.014 0.004 0.001 0.003 0.06 B24 0.043 0.030 1.92 0.74 0.019 0.003 0.003 0.002 B25 0.066 0.015 1.63 0.98 0.007 0.003 0.003 0.005 B26 0.077 0.042 1.30 0.36 0.011 0.002 0.002 0.004 B27 0.057 0.049 1.21 0.34 0.012 0.005 0.003 0.001 B28 0.042 0.033 1.53 0.44 0.014 0.002 0.002 0.002 B29 0.053 0.023 1.69 0.75 0.006 0.003 0.002 0.005 B30 0.058 0.026 1.50 0.94 0.009 0.002 0.002 0.002 B31 0.055 0.015 2.0 0.75 0.009 0.003 0.002 0.003 B32 0.044 0.042 1.7 0.35 0.017 0.002 0.001 0.005 B33 0.051 0.016 1.3 0.63 0.005 0.003 0.002 0.001 B34 0.068 0.017 1.3 0.76 0.007 0.003 0.002 0.002 B35 0.045 0.025 1.7 0.82 0.019 0.002 0.002 0.004 B36 0.074 0.015 1.9 0.36 0.006 0.004 0.001 0.002 The mark * indicates that the value fell out of the range defined in the present invention.
TABLE-US-00007 TABLE 7 Steel Chemical composition (mass %, balance: Fe and impurities) No. Cu Ni Mo Cr B Ca Mg Zr REM Sb Sn As B1 0.001 B2 0.11 0.002 B3 0.001 B4 0.01 0.002 B5 0.01 0.001 B6 0.02 0.003 B7 0.01 0.001 B8 0.01 0.001 B9 0.02 0.002 B10 0.01 0.001 B11 0.01 0.001 B12 0.02 0.001 B13 0.01 B14 0.01 0.003 B15 0.02 0.002 B16 0.02 0.001 B17 0.01 0.002 B18 0.03 0.001 B19 0.01 0.002 B20 0.01 0.001 B21 0.01 B22 0.01 B23 0.01 0.001 B24 0.32 0.001 B25 0.01 0.43 0.001 B26 0.01 0.30 0.001 B27 0.01 0.20 0.001 B28 0.01 0.001 B29 0.02 0.001 B30 0.01 0.002 0.001 B31 0.0015 B32 0.008 B33 0.030 B34 0.040 B35 0.070 B36 0.090
TABLE-US-00008 TABLE 8 Process Process Process (3a) Process Process (2a) (2b) Time From (3b) (1) Rolling Rolling Finishing To Average Steel Decrement Temp. Reduction Temp. Reduction Water Cooling Cooling Rate No. No. (%) ( C.) (%) ( C.) (%) (Sec) ( C./Sec) 1 B1 40 920 20 902 8 0.20 60 2 B2 40 915 20 895 8 0.20 63 3 B3 59 908 21 890 10 0.15 128 4 B4 40 893 19 871 9 0.24 121 5 B5 50 941 19 924 7 0.40 94 6 B6 32 932 21 921 9 0.26 132 7 B7 43 901 19 887 10 0.15 129 8 B8 40 939 23 919 7 0.38 107 9 B9 42 935 19 912 9 0.24 74 10 B10 58 881 16 871 9 0.05 125 11 B11 42 915 16 906 6 0.22 60 12 B12 36 947 21 939 8 0.06 83 13 B13 45 914 20 898 9 0.30 79 14 B14 40 943 20 924 10 0.30 66 15 B15 45 926 20 907 6 0.48 125 16 B16 50 935 18 918 7 0.27 129 17 B17 40 897 21 881 10 0.14 119 18 B18 32 908 20 884 6 0.08 55 19 B19 31 883 18 871 9 0.14 125 20 B20 50 905 20 898 6 0.43 127 21 B21 31 899 21 878 6 0.18 95 22 B22 38 906 24 895 8 0.36 79 23 B23 46 948 24 936 7 0.35 107 24 B24 55 944 17 921 9 0.27 65 25 B25 47 922 17 905 6 0.24 120 26 B26 59 919 22 911 9 0.42 79 27 B27 33 905 17 898 9 0.04 138 28 B28 35 948 24 927 7 0.45 60 29 B29 59 910 24 902 10 0.35 56 30 B30 51 948 17 937 9 0.24 54 31 B31 46 883 20 871 8 0.36 66 32 B32 53 896 19 873 9 0.29 63 33 B33 34 948 16 923 7 0.28 88 34 B34 34 944 20 924 6 0.37 132 35 B35 47 921 20 907 9 0.31 107 36 B36 37 929 19 922 9 0.10 61 37 B1 24# 891 21 873 9 0.36 65 38 B1 56 913 23 893 4# 0.05 79 39 B1 48 934 17 911 12# 0.38 55 40 B1 50 940 21 918 8 0.70# 82 41 B1 34 912 20 906 8 0.08 35# 42 B1 47 935 23 927 6 0.29 108 43 B1 49 891 19 871 9 0.26 132 44 B1 38 881 18 872 9 0.08 79 45 B1 50 939 20 922 9 0.35 121 46 B1 42 925 22 917 10 0.23 112 47 B1 43 944 23 930 7 0.40 51 48 B1 43 949 22 924 8 0.10 64 49 B1 53 888 21 871 6 0.44 87 50 B1 40 920 20 902 8 0.20 60 51 B1 40 920 20 902 8 0.20 60 The mark # indicates that the value fell out of the recommended condition.
TABLE-US-00009 TABLE 9 Process Process Process (3e) Process (3c) (3d) Average (4) Cooling Cooling Cooling Coiling Sheet Steel Time Time Rate Temperature Plating Thickness No. No. (Sec) (Sec) ( C./Sec) ( C.) Galvanizing Galvannealing (mm) 1 B1 4.5 3.0 70 40 No No 3.0 2 B2 5.0 1.0# 70 43 No No 3.0 3 B3 2.9 2.8 93 390 No No 2.1 4 B4 3.9 3.8 64 238 No No 2.1 5 B5 4.0 3.8 52 315 No No 2.5 6 B6 4.4 2.4 77 161 No No 2.1 7 B7 3.2 4.1 59 103 No No 2.5 8 B8 4.3 5.4 83 71 No No 2.4 9 B9 4.8 2.6 86 102 No No 2.0 10 B10 4.5 5.9 75 270 No No 2.0 11 B11 4.6 2.9 95 194 No No 2.4 12 B12 4.1 3.8 68 370 No No 2.3 13 B13 4.9 4.3 76 104 No No 2.5 14 B14 2.6 5.0 56 273 No No 2.4 15 B15 2.6 5.1 99 329 No No 2.2 16 B16 2.3 4.5 90 191 No No 2.4 17 B17 3.6 3.8 70 157 No No 2.4 18 B18 2.1 3.6 78 304 No No 2.4 19 B19 4.0 5.9 71 379 No No 2.1 20 B20 2.3 4.7 97 284 No No 2.4 21 B21 2.1 5.3 99 158 No No 2.4 22 B22 2.5 4.3 73 65 No No 2.3 23 B23 2.3 2.5 69 191 No No 2.2 24 B24 3.5 4.7 95 186 No No 2.5 25 B25 4.3 2.4 51 95 No No 2.5 26 B26 4.9 5.3 58 141 No No 2.2 27 B27 3.0 5.6 51 204 No No 2.0 28 B28 2.1 4.3 52 301 No No 2.4 29 B29 3.0 3.0 70 211 No No 2.5 30 B30 3.1 2.1 85 35 No No 2.0 31 B31 4.8 4.5 84 132 No No 2.5 32 B32 2.9 5.1 59 326 No No 2.4 33 B33 3.7 4.7 76 309 No No 2.5 34 B34 3.2 5.1 54 129 No No 2.1 35 B35 3.1 2.3 52 267 No No 2.5 36 B36 3.4 4.8 72 385 No No 2.1 37 B1 4.4 5.6 62 324 No No 2.5 38 B1 3.1 4.8 58 87 No No 2.4 39 B1 4.7 2.6 78 230 No No 2.3 40 B1 2.7 3.0 64 295 No No 2.5 41 B1 3.4 2.9 58 37 No No 2.2 42 B1 1.0# 2.2 81 223 No No 2.4 43 B1 3.1 0.8# 76 216 No No 2.4 44 B1 3.4 6.8# 55 113 No No 2.0 45 B1 2.8 5.9 39# 354 No No 2.4 46 B1 2.6 5.9 55 417# No No 2.4 47 B1 4.0 4.2 91 360 Yes No 2.4 48 B1 4.2 2.7 58 113 Yes No 2.3 49 B1 2.5 5.7 80 94 Yes Yes 2.1 50 B1 4.9 1.7# 70 40 No No 3.0 51 B1 4.9 7.1# 70 40 No No 3.0 The mark # indicates that the value fell out of the recommended condition.
[0199] In Table 8 and Table 9, PROCESS (1) means the machining performed before the rough rolling process and shows, in the tables, its decrements W (%) in length of the slabs in the width direction. PROCESS (2a) and PROCESS (2b) means the rolling in one pass before the finished rolling and the finished rolling, respectively, and show, in the tables, their temperatures ( C.) and their rolling reductions (%). PROCESS (3a) refers to retention performed from the end of the finish rolling until the start of the water cooling and shows, in the tables, its retention times. PROCESS (3b) refers to the cooling process for the temperature range of 870 to 720 C. and shows, in the tables, its average cooling rates ( C./sec) in the temperature range. PROCESS (3c) refers to the cooling process for the temperature range of 720 C. or less and more than 630 C. and shows, in the tables, its cooling times (sec) in the temperature range. PROCESS (3d) refers to the cooling process for the temperature range of 630 C. or less and more than 600 C. and shows, in the tables, its cooling times (sec) in the temperature range. PROCESS (3e) refers to the cooling process for the temperature range of 600 C. or less and more than to 450 C. and shows, in the tables, its average cooling rates ( C./sec) in the temperature range. PROCESS (4) refers to the coiling process and shows, in the tables, its coiling temperatures ( C.).
[0200] On the obtained steel sheets, their steel micro-structures, mechanical properties, and hole-expansion properties were measured.
<Measurement of Steel Micro-Structure>
[0201] On a rolling-direction perpendicular cross section that lies at a depth position of a sheet thickness t (t area) from a steel sheet surface, the EBSD analysis is performed on a zone that is 200 m long in a rolling direction and 100 m long in a rolling-surface normal direction at a measurement interval of 0.2 m, so as to obtain crystal orientation information. The EBSD analysis is here performed using an apparatus including a thermal field emission scanning electron microscope (JSM-7001F from JEOL) and an EBSD detector (DVC5-type detector from TSL solutions) and involves measurement with an exposure time of 60 msec, using TSL OIM Data Collection 6 that comes with an EBSD analyzer. Next, in the obtained crystal orientation information, a zone having a crystal misorientation of 5 or more is defined as a grain, an average crystal misorientation of the grain is calculated, and proportions of grains having the average crystal misorientations of less than 0.5 or 0.5 to 1.00 are calculated.
[0202] The average crystal misorientation of a grain in the present invention is an average value of Grain Average Misorientations (GAM), each of which is an orientation spread of the grain, and is obtained by calculating misorientations between neighboring measurement points and calculating an average value of the misorientations for every measurement point in the grain. Values of the GAM were calculated with OIM Analysis Version 7.0.1, a piece of software coming with an EBSD analyzer.
[0203] An average value of Image Qualities in a grain in the present invention actually means an average value of values obtained by analyzing, by the Grain average image quality (GAIQ) method, measurement values from measurement by the EBSD method.
[0204] In the GAIQ, on an assumption that a zone having a crystal misorientation of 5 or more is defined as a grain in crystal orientation information obtained by the EBSD analysis, a proportion of grains having an in-grain average dislocation density of less than 4000 is calculated. The values of the GAIQ can be calculated with OIM Analysis Version 7.0.1, a piece of software coming with an EBSD analyzer.
[0205] Based on the K value and the Y value obtained in the manner described above, metallic phases were classified as follows.
[0206] Metallic phase 1: a metallic phase having a K value of less than 4.000
[0207] Metallic phase 2: a metallic phase having a K value of 4.000 or more and a Y value of 0.5 to 1.0
[0208] Metallic phase 3: a metallic phase having a K value of 4.000 or more and a Y value of less than 0.5
[0209] Metallic phase 4: a metallic phase falling under none of metallic phases 1 to 3
<Measurement of Mechanical Properties>
[0210] The tensile strength and the elongation are evaluated in such a manner that a JIS No. 5 specimen is taken in a direction perpendicular to a rolling direction of a steel sheet and a tensile test is performed in conformity with JIS Z 2242 to measure a tensile strength (TS) and a total elongation (El).
<Hole-Expansion Property>
[0211] The hole-expansion property is evaluated in such a manner that a hole expansion test is performed in conformity with JFS-T1001-1996 of The Japan Iron and Steel Federation Standard to measure a hole expansion rate (HER).
[0212] Results of the above are shown in Table 10.
TABLE-US-00010 TABLE 10 Steel Micro- Proportion Of Boundary Mechanical Structure (Area %) Between Metallic Phase Properties Steel Metallic Metallic Metallic Metallic 1 And Metallic Phase 2 TS EL No. No. Phase 1 Phase 2 Phase 3 Phase 4 (%) (MPa) (%) (%) 1 B1 8.0 75.0 17.0 0.0 94 788 97.0 23.0 2 B2 5.0 10.0* 18.0 67.0* 14** 798 91.0 22.1 3 B3 4.1 65.2 30.7 0.0 92 785 97.5 26.1 4 B4 8.7 74.6 16.7 0.0 96 790 97.7 24.6 5 B5 32.4 54.4 13.2 0.0 67 897 98.3 26.5 6 B6 0.0* 60.3 8.5 31.2* 0** 949 44.0 25.0 7 B7 32.0 54.7 13.3 0.0 62 908 96.3 24.7 8 B8 8.6 74.7 16.7 0.0 91 800 98.1 25.3 9 B9 3.2 66.2 30.6 0.0 93 785 96.4 24.7 10 B10 0.0* 44.7 55.3* 0.0 0** 523 98.9 26.9 11 B11 0.0* 45.8 54.2* 0.0 0** 524 98.7 26.8 12 B12 3.9 65.5 30.6 0.0 87 785 99.5 24.7 13 B13 7.2 76.5 16.3 0.0 93 795 95.9 24.8 14 B14 31.4 55.1 13.5 0.0 63 905 95.6 22.6 15 B15 0.0* 60.9 7.1 32.0* 4** 969 44.2 25.4 16 B16 32.8 65.9 1.3* 0.0 69 978 95.1 19.6 17 B17 32.5 54.3 13.2 0.0 65 907 97.9 25.5 18 B18 8.7 74.7 16.6 0.0 92 793 97.3 26.1 19 B19 3.8 65.2 31.0 0.0 86 787 99.1 23.7 20 B20 0.0* 44.3 55.7* 0.0 0** 518 98.8 26.5 21 B21 8.3 74.9 16.8 0.0 90 796 96.9 26.4 22 B22 8.8 73.8 17.4 0.0 92 791 98.3 26.2 23 B23 8.6 74.7 16.7 0.0 97 794 96.9 25.8 24 B24 32.8 54.9 12.3 0.0 68 897 97.9 25.4 25 B25 31.9 54.9 13.2 0.0 66 910 98.3 25.9 26 B26 6.3 70.4 21.3 2.0 98 794 98.4 26.4 27 B27 6.1 69.4 21.0 3.5 95 801 97.8 25.5 28 B28 12.7 73.4 13.9 0.0 67 804 97.4 25.6 29 B29 8.5 74.2 17.3 0.0 92 799 98.4 26.3 30 B30 7.7 75.9 16.4 0.0 91 799 97.2 25.4 31 B31 16.0 74.5 9.5 0.0 62 920.0 96.2 20.9 32 B32 7.7 75.2 17.1 0.0 91 792.0 97.5 21.6 33 B33 7.6 74.6 17.8 0.0 95 790.0 95.0 22 34 B34 7.8 75.7 16.5 0.0 96 792.0 96.4 22.1 35 B35 7.9 74.9 17.2 0.0 95 792.0 96.6 20.3 36 B36 7.8 75.1 17.1 0.0 96 793.0 95.1 19.9 37 B1 6.7 5.0* 16.7 71.6* 9** 797 91.0 22.1 38 B1 5.2 4.1* 16.2 74.5* 7** 794 91.2 22.3 39 B1 6.3 5.1* 17.3 71.3* 11** 790 91.4 22.4 40 B1 20.6 77.3 2.1* 0.0 66 897 95.1 19.5 41 B1 21.3 77.2 1.5* 0.0 63 893 95.4 17.9 42 B1 32.8 65.1 2.1* 0.0 72 978 95.2 19.3 43 B1 4.7 9.7* 18.5 67.1* 13** 812 91.0 22.1 44 B1 4.1 9.4* 17.3 69.2* 16** 812 90.4 22.4 45 B1 4.7 9.3* 17.9 68.1* 17** 800 90.9 22.2 46 B1 0.0* 75.4 17.2 7.4* 0** 804 90.1 22.4 47 B1 8.0 75.0 17.0 0.0 93 801 97.0 23.0 48 B1 6.9 75.1 16.9 1.1 94 800 95.7 23.1 49 B1 7.2 73.8 17.7 1.3 93 794 95.1 22.4 50 B1 33.6 27.5* 34.4 4.5 43** 799 57.8 23.0 51 B1 0.4* 65.2 34.4 0.0 98 549 98.6 26.7 The mark * indicates that the value fell out of the range defined in the present invention. The mark ** indicates that the value fell out of the preferable range in the present invention.
[0213] As shown in Table 10, inventive examples of the present invention have tensile strengths of 780 MPa or more and sufficient hole-expansion properties.
INDUSTRIAL APPLICABILITY
[0214] According to the present invention, a steel sheet and a plated steel sheet that has a strength as high as 590 MPa or more (furthermore, 780 MPa or more) in terms of tensile strength and has an excellent hole-expansion property are provided.
REFERENCE SIGNS LIST
[0215] 1 Crystal structure having a K value of less than 4 [0216] 2 Crystal structure having a K value of 4 or more and a Y value of 0.5 to 1.0 [0217] 3 Crystal structure having a K value of 4 or more and a Y value of less than 0.5