GRAIN-ORIENTED ELECTRICAL STEEL SHEET AND METHOD OF MANUFACTURING SAME

Abstract

Provided is a grain-oriented electrical steel sheet which has been subjected to heat-resistant magnetic domain refining treatment and can effectively suppress carburizing and nitriding during stress relief annealing. The grain-oriented electrical steel sheet has a plurality of grooves on one side that extend linearly across the rolling direction and are lined up at intervals in the rolling direction, and has at least a forsterite film on a surface of the steel sheet, where an average thickness of the forsterite film formed on the floor of the grooves is 0.45 μm or more, and a standard deviation a of the thickness is 0.34 μm or less.

Claims

1. A grain-oriented electrical steel sheet comprising a plurality of grooves on one side of the steel sheet that extend linearly across a rolling direction and are lined up at intervals in the rolling direction, and having at least a forsterite film on a surface of the steel sheet, wherein an average thickness of the forsterite film formed on floor of the grooves is 0.45 μm or more, and a standard deviation σ of the thickness is 0.34 μm or less.

2. A method of manufacturing a grain-oriented electrical steel sheet, comprising a series of processes of subjecting a slab for grain-oriented electrical steel sheet to hot rolling to obtain a hot-rolled sheet, then subjecting the hot-rolled sheet to cold rolling once or two or more times with intermediate annealing performed therebetween to obtain a steel sheet with a final thickness, then subjecting the steel sheet to decarburization annealing, then subjecting the steel sheet to final annealing after applying an annealing separator to a surface of the steel sheet, and then subjecting the steel sheet to final annealing, wherein after the cold rolling and before the applying of an annealing separator, resist ink is applied to one side of the steel sheet, a laser is repeatedly scanned in a linear fashion across a rolling direction of the steel sheet on the applied surface at intervals in the rolling direction, the resist ink is removed from areas irradiated by the laser, and then electrolytic etching is applied on the removed areas to form a plurality of grooves that extend linearly across the rolling direction of the steel sheet and are lined up at intervals in the rolling direction, and the scanning of the laser is performed with an irradiation energy of the laser being less than 30 J/m and a temperature of the steel sheet being 40° C. or higher and lower than 200° C.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0037] In the accompanying drawings:

[0038] FIG. 1 illustrates the location where a samples for cross-sectional observation is collected;

[0039] FIG. 2 illustrates the definition of the floor of a groove;

[0040] FIG. 3 illustrates the relationship between the average forsterite film thickness on the floor of grooves and the increase or decrease in W.sub.17/50 under Condition 1 of Experiment 1;

[0041] FIG. 4 illustrates the relationship between the average forsterite film thickness on the floor of grooves and the increase or decrease in carbon under Condition 1 of Experiment 1;

[0042] FIG. 5 illustrates the relationship between the average forsterite film thickness on the floor of grooves and the increase or decrease in W.sub.17/50 under Condition 2 of Experiment 1;

[0043] FIG. 6 illustrates the relationship between the average forsterite film thickness on the floor of grooves and the increase or decrease in carbon under Condition 2 of Experiment 1; and

[0044] FIG. 7 illustrates the relationship between the irradiation energy and steel sheet temperature during resist peeling, and the average value and standard deviation of the thickness of the resulting forsterite film formed on the floor of grooves of the steel sheet.

DETAILED DESCRIPTION

[0045] The following describes embodiments of the present disclosure in detail.

[0046] A grain-oriented electrical steel sheet of the present disclosure has a plurality of grooves on one side of the steel sheet that extend linearly across a rolling direction and are lined up at intervals in the rolling direction, and it has at least a forsterite film on a surface of the steel sheet. The grain-oriented electrical steel sheet preferably further has a tension coating on the forsterite film. Further, for the grain-oriented electrical steel sheet of the present disclosure, it is essential an average thickness of the forsterite film formed on the floor of the linear grooves be 0.45 μm or more, and a standard deviation σ of the thickness of the forsterite film be 0.34 μm or less.

[0047] The grain-oriented electrical steel sheet of the present disclosure can be suitably obtained with the method of manufacturing a grain-oriented electrical steel sheet of the present disclosure, which will be described later.

[0048] The following describes the results of experiments in which we studied the conditions for forming a forsterite film on the floor of the grooves.

Experiment 1

[0049] A steel slab (slab for grain-oriented electrical steel sheet) was manufactured by continuous casting, where the steel slab had a chemical composition containing C: 0.07 mass %, Si: 3.4 mass %, Mn: 0.1 mass %, Ni: 0.2 mass %, Al: 240 mass ppm, S: 20 mass ppm, N: 90 mass ppm, and Se: 180 mass ppm, with the balance being Fe and inevitable impurities. The slab was heated to 1430° C. and then subjected to hot rolling to obtain a hot-rolled sheet with a thickness of 2.2 mm. The hot-rolled sheet was subjected to hot-rolled sheet annealing at 1100° C. for 20 seconds. Next, the hot-rolled sheet after hot-rolled sheet annealing was subjected to cold rolling to obtain an intermediate thickness of 0.40 mm, and then to intermediate annealing under the conditions of oxidation degree P(H.sub.2O)/P(H.sub.2)=0.40, temperature: 1000° C., and time: 70 seconds. Further, after removing subscales from the surface of the cold-rolled sheet after intermediate annealing by pickling with hydrochloric acid, the sheet was subjected to cold rolling again to obtain a cold-rolled sheet (or simply “steel sheet”) with a final thickness of 0.23 mm.

[0050] One side of the steel sheet was masked by printing and applying resist ink using a groove roller with grooves with a width of 100 mm to 250 mm at a circumferential pitch of 3 mm, and electrolytic etching was performed to form grooves with a depth of 25 μm in areas that were not printed with resist (Resist Condition 1). Another condition is that, after resist ink was applied to one side of the steel sheet, a laser was repeatedly scanned in a linear fashion in a direction orthogonal to the rolling direction (width direction) and at intervals of 3 mm in the rolling direction so that the resist ink was peeled off and removed at intervals of 3 mm in the rolling direction. Subsequently, electrolytic etching was performed in the same manner as in Condition 1 to form grooves with a depth of 25 μm (Resist Condition 2). After electrolytic etching, the resist ink remaining on the steel sheet under was removed under both conditions. The laser irradiation was performed with a galvano scanner method by a single mode fiber laser with a peeling width of 100 mm to 250 mm, and the irradiation energy was set to 25 J/m so as to continuously peel off the resist ink from one end to the other end in the width direction of the steel sheet. The temperature of the steel sheet when irradiated with the laser was changed in various ways. In the present specification, the temperature of the steel sheet is defined as the temperature at the surface of the steel sheet on the laser irradiated side of the steel sheet, which can be measured by a non-contact infrared radiation thermometer, for example.

[0051] Next, the steel sheet was subjected to decarburization annealing where it was retained at an oxidation degree P(H.sub.2O)/P(H.sub.2)=0.44 to 0.60 and a soaking temperature of 820° C. for 300 seconds. Next, an annealing separator composed mainly of MgO was applied to the surface of the steel sheet, and the steel sheet was subjected to final annealing for the purposes of secondary recrystallization, formation of a forsterite film and purification under the conditions of 1160° C. and 10 hours. Then, tension coating was performed in which an insulating coating made of 60 mass % colloidal silica and aluminum phosphate was applied and baked at 850° C. This tension coating application process also serves as flattening annealing.

[0052] The thickness of the forsterite film formed on the floor of the grooves of a test piece obtained after the tension coating application process was investigated with the method described below, and the average value and standard deviation were calculated. A sample where an average thickness of the forsterite film on the floor of the grooves was 0.31 μm to 0.82 μm and the standard deviation was 0.22 μm to 0.74 μm was obtained under Resist Condition 1, and a sample where an average thickness of the forsterite film on the floor of the grooves was 0.32 μm to 0.91 μm and the standard deviation was 0.05 μm to 0.43 μm was obtained under Resist Condition 2, respectively.

[0053] [[Measurement of Forsterite Film Thickness at Floor of Groove]]

[0054] As illustrated in FIG. 1, a sample for cross-sectional observation is collected in the rolling direction to include six linear grooves. Further, the cross section of the sample is observed by SEM to measure the thickness of the forsterite film on the floor of the grooves.

[0055] In the present specification, the floor of a groove is defined as an area centered at the center of the groove and having a width half the groove width w, as illustrated in FIG. 2. The groove width w means the length of an area where resist ink is not applied during electrolytic etching (non-applied area) along a direction orthogonal to a direction in which the linear groove extends (the rolling direction in FIG. 2). The center of the groove means a location at the center of the groove width win the rolling direction.

[0056] The thickness of the forsterite film is measured for any five linear grooves in one sample for cross-sectional observation, the results are averaged, and the average value is defined as the thickness of the forsterite film at the location. In one steel sheet sample (width direction: 1000 mm×rolling direction: 500 mm), samples for cross-sectional observation are collected at 20 locations, the forsterite film thickness on the floor of the grooves of each sample is calculated, and their average value and standard deviation are determined.

[0057] The forsterite film area can be determined based on the contrast of SEM observation images, but in some cases, it is easier to determine based on the contrast of reflected electron images (BSE). When it is difficult to determine based on the contrast of images, the presence or absence of Mg by elemental analysis using EDX may be appropriately used to determine if it is a forsterite film area. In the present specification, it was determined based on the contrast of images in BSE images.

[0058] [[Magnetic Property Measurement]]

[0059] The test piece after tension coating application process was sheared to a size of 30 mm×280 mm and then subjected to stress relief annealing under conditions of an argon atmosphere, 800° C. and 3 hours (to eliminate the effects of shearing) to obtain a sample, and magnetic property measurement was performed by the Epstein test method. To further investigate the effect of stress relief annealing in a carburizing atmosphere, the sample was again annealed at 870° C. for 2 hours in mixed gases of CO: 0.5 vol %, CO.sub.2: 13 vol %, H.sub.2O: 2.5 vol %, Hz: 1 vol %, and N.sub.2 (dew point: 20° C.) as the residual gas, and magnetic property measurement was performed with the Epstein test method.

[0060] The Epstein test results of the sample before and after the stress relief annealing in the carburizing atmosphere mixed gases were compared to determine the increase or decrease in W.sub.17/50 (iron loss when excited at 50 Hz to 1.7 T). Further, the carbon content was chemically analyzed before and after the stress relief annealing in the mixed gases. The results of chemical analysis before and after the annealing in the carburizing atmosphere mixed gases were compared to determine the increase or decrease in carbon.

[0061] The average value and standard deviation of the thickness of the forsterite film formed on the floor of the grooves, and the increase or decrease in W.sub.17/50 and the increase or decrease in carbon (carburizing quantity) before and after the stress relief annealing in the carburizing atmosphere mixed gases are listed in Table 1 and FIGS. 3 and 4 (Resist Condition 1) and FIGS. 5 and 6 (Resist Condition 2), respectively.

TABLE-US-00001 TABLE 1 Forsterite film thickness Before and after stress relief annealing on the floor of grooves in carburizing atmosphere mixed gases Standard Increase or Increase or Experiment 1 Average deviation decrease in decrease in Test No. Resist Condition (μm) (μm) W.sub.17/50 (W/kg) carbon (ppm) 1 Condition 1 (groove roller) 0.32 0.23 0.55 135 2 Condition 1 (groove roller) 0.31 0.30 0.64 145 3 Condition 1 (groove roller) 0.38 0.22 0.53 143 4 Condition 1 (groove roller) 0.42 0.36 0.58 147 5 Condition 1 (groove roller) 0.43 0.41 0.63 156 6 Condition 1 (groove roller) 0.49 0.39 0.49 132 7 Condition 1 (groove roller) 0.51 0.47 0.52 135 8 Condition 1 (groove roller) 0.50 0.51 0.57 140 9 Condition 1 (groove roller) 0.61 0.45 0.58 143 10 Condition 1 (groove roller) 0.59 0.49 0.53 132 11 Condition 1 (groove roller) 0.62 0.44 0.51 128 12 Condition 1 (groove roller) 0.63 0.53 0.35 140 13 Condition 1 (groove roller) 0.68 0.56 0.61 172 14 Condition 1 (groove roller) 0.71 0.47 0.38 120 15 Condition 1 (groove roller) 0.73 0.53 0.37 123 16 Condition 1 (groove roller) 0.78 0.56 0.25 110 17 Condition 1 (groove roller) 0.81 0.63 0.28 105 18 Condition 1 (groove roller) 0.82 0.74 0.31 123 Forsterite film thickness Before and after stress relief annealing Steel sheet on the floor of grooves in carburizing atmosphere mixed gases temperature Standard Increase or Increase or Experiment 1 during laser Average deviation decrease in decrease in Test No. Resist Condition scanning (° C.) (μm) (μm) W.sub.17/50 (W/kg) carbon (ppm) 19 Condition 2 (laser peeling) 40 0.32 0.08 0.49 153 20 Condition 2 (laser peeling) 35 0.33 0.17 0.53 145 21 Condition 2 (laser peeling) 30 0.39 0.11 0.47 136 22 Condition 2 (laser peeling) 25 0.41 0.22 0.44 138 23 Condition 2 (laser peeling) 15 0.43 0.29 0.42 142 24 Condition 2 (laser peeling) 60 0.52 0.09 0.08 8 25 Condition 2 (laser peeling) 70 0.49 0.17 0.09 6 26 Condition 2 (laser peeling) 100 0.53 0.27 0.12 7 27 Condition 2 (laser peeling) 220 0.52 0.39 0.27 64 28 Condition 2 (laser peeling) 80 0.61 0.10 0.06 5 29 Condition 2 (laser peeling) 90 0.59 0.21 0.07 6 30 Condition 2 (laser peeling) 120 0.62 0.28 0.08 7 31 Condition 2 (laser peeling) 250 0.60 0.43 0.25 72 32 Condition 2 (laser peeling) 130 0.68 0.05 0.02 8 33 Condition 2 (laser peeling) 140 0.67 0.17 0.04 6 34 Condition 2 (laser peeling) 150 0.71 0.28 0.08 4 35 Condition 2 (laser peeling) 270 0.72 0.41 0.22 56 36 Condition 2 (laser peeling) 160 0.82 0.26 0.05 5 37 Condition 2 (laser peeling) 240 0.83 0.42 0.23 47 38 Condition 2 (laser peeling) 180 0.89 0.31 0.03 3 39 Condition 2 (laser peeling) 230 0.91 0.38 0.19 56

[0062] It was found that, when the average thickness of the forsterite film formed on the floor of the grooves is 0.45 μm or more, there are conditions under which the increase in iron loss can be suppressed to a low level and the carburizing quantity can be suppressed to a low level for both the increase and decrease in iron loss W.sub.17/50 and the increase and decrease in carbon (carburizing quantity). Further detailed investigation revealed that, in a steel sheet with an average forsterite film thickness of 0.45 μm or more, the condition under which the increase in iron loss and the increase in carburizing quantity can be significantly suppressed is that the standard deviation of the forsterite film thickness is 0.34 μm or less. It is considered that, when the forsterite film thickness is formed with such a low standard deviation, high denseness of the forsterite film can be obtained.

[0063] Further, a forsterite film thickness in the above specified range was achieved only under Resist Condition 2, where resist peeling by laser was performed.

[0064] Next, we experimentally searched for conditions under which steel sheets with a forsterite film where the average thickness is 0.45 μm or more and the standard deviation of the thickness is 0.34 μm or less formed in the floor of the grooves can be stably obtained, and we found that it is necessary to satisfy the following three conditions.

[0065] (1) After cold rolling and before applying an annealing separator (i.e., before final annealing), resist ink is applied to one side of the steel sheet.

[0066] (2) A laser is repeatedly scanned in a linear fashion across the rolling direction of the steel sheet on the applied surface of the steel sheet, which has been applied with the resist ink, at intervals in the rolling direction, the resist ink is removed from areas irradiated by the laser, and then electrolytic etching is performed on the removed areas to form a plurality of grooves that extend linearly across the rolling direction of the steel sheet and are lined up at intervals in the rolling direction.

[0067] (3) The scanning of the laser is performed under conditions where an irradiation energy of the laser is less than 30 J/m, and a temperature of the steel sheet is 40° C. or higher and lower than 200° C.

[0068] The condition (1) means that, to form a good forsterite film on the floor of the grooves, the grooves need to be formed at least before the final annealing in which the forsterite film is formed (more specifically, before an annealing separator is applied).

[0069] Regarding the condition (2), when resist ink is printed as in conventional cases, resist ink from an adjacent printed area inevitably drips in a non-printed area (an area where grooves are formed by etching), resulting in non-uniform width of the non-printed area and non-uniform groove width after formation. When such non-uniform groove width occurs, there will be a variation in the digging of grooves during etching according to the local variation in groove width. As a result, the unevenness on the floor of the grooves becomes severe, and the thickness of the forsterite film formed on the floor varies. Therefore, the object of the present disclosure cannot be achieved in this case.

[0070] On the other hand, with the method of peeling off resist ink by laser irradiation as in the present disclosure, the width of the peeled part of resist ink is uniform, that is, within about ±10 μm, so that the digging of grooves is uniform during etching. As a result, it is considered that the formation of grooves using laser scanning under predetermined conditions is one factor that allows the thickness of a forsterite film formed thereon to be uniform and satisfies the requirement for the standard deviation of the forsterite film thickness.

[0071] The condition (3) is explained below with reference to experiments clarifying that the condition is suitable for the present disclosure.

Experiment 2

[0072] A steel slab (slab for grain-oriented electrical steel sheet) was manufactured by continuous casting, where the steel slab had a chemical composition containing C: 0.07 mass %, Si: 3.4 mass %, Mn: 0.1 mass %, Ni: 0.2 mass %, Al: 240 mass ppm, S: 20 mass ppm, N: 90 mass ppm, and Se: 180 mass ppm, with the balance being inevitable impurities. The slab was heated to 1430° C. and then subjected to hot rolling to obtain a hot-rolled sheet with a thickness of 2.2 mm. The hot-rolled sheet was subjected to hot-rolled sheet annealing at 1100° C. for 20 seconds. Next, the hot-rolled sheet after hot-rolled sheet annealing was subjected to cold rolling to obtain an intermediate thickness of 0.40 mm, and to intermediate annealing under the conditions of oxidation degree P(H.sub.2O)/P(H.sub.2)=0.40, temperature: 1000° C., and time: 70 seconds. Further, after removing subscales from the surface of the cold-rolled sheet after intermediate annealing by pickling with hydrochloric acid, the sheet was subjected to cold rolling again to obtain a steel sheet with a final thickness of 0.23 mm.

[0073] After resist ink was applied to one side of the steel sheet, a laser was repeatedly scanned in a linear fashion in a direction orthogonal to the rolling direction and at intervals of 3 mm in the rolling direction so that the resist ink was peeled off and removed at intervals of 3 mm in the rolling direction. The laser irradiation was performed with a galvano scanner method by a single mode fiber laser with a peeling width of 100 mm to 250 mm, and the irradiation energy was set to 15 J/m to 50 J/m to peel off the resist ink continuously and completely from one end to the other end in the width direction of the steel sheet. At that time, the laser irradiation was performed with the temperature of the steel sheet changed between 15° C. to 250° C. Next, electrolytic etching was performed to form grooves with a depth of 25 μm. After the electrolytic etching, the resist ink remaining on the steel sheet was removed.

[0074] Next, the steel sheet was subjected to decarburization annealing where it was retained at an oxidation degree P(H.sub.2O)/P(H.sub.2)=0.44 to 0.60 and a soaking temperature of 820° C. for 300 seconds. Next, an annealing separator composed mainly of MgO was applied to the surface of the steel sheet, and the steel sheet was subjected to final annealing for the purposes of secondary recrystallization, formation of a forsterite film and purification under the conditions of 1160° C. and 10 hours. Then, tension coating was performed in which an insulating coating made of 60 mass % colloidal silica and aluminum phosphate was applied and baked at 850° C. This tension coating application process also serves as flattening annealing.

[0075] Next, the thickness of the forsterite film formed on the floor of the grooves was investigated with the method described above, and the average value and standard deviation were calculated.

[0076] The relationship between the irradiation energy and steel sheet temperature during resist peeling, and the average value and standard deviation of the thickness of the resulting forsterite film formed on the floor of the grooves of the steel sheet are summarized in Table 2 and FIG. 7. As a result, it was found that, when laser scanning is performed under conditions where the laser irradiation energy is less than 30 J/m and the steel sheet temperature is 40° C. or higher and lower than 200° C., the average thickness of the forsterite film formed on the floor of the grooves is 0.45 μm or more, and the standard deviation σ of the thickness is 0.34 μm or less.

[0077] In FIG. 7, the lower limit of the steel sheet temperature (40° C. or higher) is indicated by solid lines, and the upper limit of the steel sheet temperature (lower than 200° C.) and the upper limit of the irradiation energy (less than 30 J/m) are indicated by dotted lines.

TABLE-US-00002 TABLE 2 Forsterite film thickness Laser scanning conditions on the floor of grooves Irradiation Steel sheet Standard Experiment 2 energy temperature Average deviation Test No. (J/m) (° C.) (μm) (μm) Remarks 1 15 50 0.68 0.05 Within the scope 2 20 50 0.64 0.04 Within the scope 3 25 50 0.72 0.03 Within the scope 4 28 50 0.71 0.12 Within the scope 5 30 50 0.44 0.33 Outside the scope 6 32 50 0.49 0.40 Outside the scope 7 35 50 0.53 0.42 Outside the scope 8 40 50 0.47 0.37 Outside the scope 9 45 50 0.41 0.32 Outside the scope 10 50 50 0.25 0.18 Outside the scope 11 20 15 0.65 0.39 Outside the scope 12 20 20 0.63 0.36 Outside the scope 13 20 25 0.64 0.37 Outside the scope 14 20 30 0.66 0.35 Outside the scope 15 20 35 0.68 0.36 Outside the scope 16 20 40 0.67 0.21 Within the scope 17 20 60 0.68 0.05 Within the scope 18 20 80 0.69 0.06 Within the scope 19 20 100 0.63 0.07 Within the scope 20 20 150 0.62 0.05 Within the scope 21 20 180 0.64 0.04 Within the scope 22 20 195 0.61 0.12 Within the scope 23 20 220 0.58 0.38 Outside the scope 24 20 250 0.59 0.42 Outside the scope 25 30 15 0.42 0.31 Outside the scope 26 30 25 0.41 0.28 Outside the scope 27 30 40 0.43 0.32 Outside the scope 28 35 15 0.53 0.42 Outside the scope 29 35 25 0.52 0.38 Outside the scope 30 35 40 0.55 0.40 Outside the scope 31 28 100 0.72 0.06 Within the scope 32 28 150 0.73 0.05 Within the scope 33 28 195 0.74 0.15 Within the scope 34 28 220 0.78 0.38 Outside the scope 35 30 75 0.45 0.37 Outside the scope 36 30 100 0.44 0.36 Outside the scope 37 30 150 0.46 0.38 Outside the scope 38 30 200 0.47 0.37 Outside the scope

[0078] One condition for satisfying that the average forsterite film thickness is 0.45 μm or more and the standard deviation σ of the thickness is 0.34 μm or less is that the laser irradiation energy is less than 30 J/m. We speculate the reason is as follows.

[0079] When the laser irradiation energy is high, strain remains in the steel sheet around the irradiated area (i.e., the area where grooves will be formed in the next process), resulting in variation in the digging of grooves during electrolytic etching, which is the next process. As a result, the thickness of the forsterite film formed on the floor of the grooves also varies due to the severe unevenness on the floor of the grooves.

[0080] Another condition for satisfying that the average forsterite film thickness is 0.45 μm or more and the standard deviation σ of the thickness is 0.34 μm or less is that laser scanning is performed under conditions of a steel sheet temperature of 40° C. or higher and lower than 200° C. We speculate the reason is as follows.

[0081] When the steel sheet temperature is 40° C. or higher, the temperature distribution in the resist ink thin film becomes uniform when irradiated by the laser, resulting in uniform tenacity in the resist ink thin film. As a result, it is easier to peel off the ink uniformly during the laser irradiation, so that the shape of the grooves is stabilized, and variation in the thickness of the forsterite film formed on the floor of the grooves hardly occurs. On the other hand, when the steel sheet temperature is raised too high above 200° C., the resist ink cannot be peeled off well by the laser irradiation because the resist ink thin film becomes too soft.

[0082] [[Method of Forming Groove]]

[0083] As described above, the linear grooves in the present embodiment are formed by applying and adhering resist ink for etching to one side of a steel sheet and then performing electrolytic etching on non-applied areas. After that, the steel sheet is applied with an annealing separator and then subjected to final annealing. It is preferable to form linear grooves on the steel sheet after final cold rolling and before decarburization annealing. The non-applied area, which relates to the groove formation pattern, can be suitably formed with a method of applying resist ink to the entire surface on one side of the steel sheet and then peeling off and removing the ink by laser irradiation under the above conditions. The formation of a uniform and dense forsterite film on the floor of the grooves is important for suppressing nitriding and carburizing during stress relief annealing, so that it is essential to form the grooves before the application of annealing separator and final annealing in which the forsterite film is formed.

[0084] In the present specification, “across the rolling direction” is preferably within ±30 degrees as a deviation with respect to a direction orthogonal to the rolling direction of the linear grooves. Further, in the present specification, a “linear” shape includes not only solid lines but also dotted lines, dashed lines, and other point line shapes.

[0085] A method of manufacturing the grain-oriented electrical steel sheet is not limited in terms of a method of forming grooves for the above-described magnetic domain refining and matters not directly related to the control of the thickness of the forsterite film formed on the floor of the grooves. However, the recommended chemical composition and manufacturing conditions of the steel sheet are exemplified below.

[0086] [Chemical Composition]

[0087] The chemical composition of a slab for grain-oriented electrical steel sheet of the present disclosure is a chemical composition capable of secondary recrystallization. In the case of using an inhibitor, for example, Al and N are added in appropriate amounts when using a AlN-based inhibitor, and Mn and Se and/or S are added in appropriate amounts when using a MnS/MnSe-based inhibitor. Both inhibitors may be used together. In this case, the optimal content of Al, N, S, and Se are, respectively, Al: 0.01 mass % to 0.065 mass %, N: 0.005 mass % to 0.012 mass %, S: 0.005 mass % to 0.03 mass %, and Se: 0.005 mass % to 0.03 mass %. Note that Al, N, S, and Se are purified in final annealing, and their contents are reduced to the level of inevitable impurities.

[0088] An inhibitorless grain-oriented electrical steel sheet in which the contents of Al, N, S, and Se are limited may be used in the present disclosure. In such a case, the contents of Al, N, S, and Se are preferably limited to, respectively, Al: less than 100 mass ppm, N: less than 50 mass ppm, S: less than 50 mass ppm, and Se: less than 50 mass ppm.

[0089] Other components of the chemical compositions are described below. C: 0.08 mass % or less

[0090] When the C content exceeds 0.08 mass %, it becomes difficult in the manufacturing processes to reduce the C content to 50 mass ppm or less at which point magnetic aging will not occur. Therefore, the C content is preferably 0.08 mass % or less. The lower limit is not particularly limited, as a material containing no C can still be secondary recrystallized. However, it is usually 0.001 mass % or more.

[0091] Si: 2.0 mass % to 8.0 mass %

[0092] Si is an element effective in enhancing the electrical resistance of the steel and improving the iron loss. When the Si content is less than 2.0 mass %, the iron loss reduction effect is insufficient. On the other hand, when the content exceeds 8.0 mass %, the workability significantly deteriorates, and the magnetic flux density also tends to decrease. Therefore, the Si content is preferably 2.0 mass % or more. The Si content is preferably 8.0 mass % or less.

[0093] Mn: 0.005 mass % to 1.0 mass %

[0094] Mn is an element necessary for improving the hot workability. However, when the content is less than 0.005 mass %, the addition effect is poor. On the other hand, when the content exceeds 1.0 mass %, the magnetic flux density of a product sheet tends to decrease. Therefore, the Mn content is preferably 0.005 mass % or more. The Mn content is preferably 1.0 mass % or less.

[0095] In addition to the suitable basic components described above, the following elements may be appropriately contained as suitable optionally added components to improve the magnetic properties.

[0096] At least one selected from the group consisting of Ni: 0.03 mass % to 1.50 mass %, Sn: 0.01 mass % to 1.50 mass %, Sb: 0.005 mass % to 1.50 mass %, Cu: 0.03 mass % to 3.0 mass %, P: 0.03 mass % to 0.50 mass %, Mo: 0.005 mass % to 0.10 mass %, and Cr: 0.03 mass % to 1.50 mass %.

[0097] Ni is useful for improving the hot-rolled sheet microstructure and improving the magnetic properties. However, when the content is less than 0.03 mass %, the effect of improving the magnetic properties is small. On the other hand, when the content exceeds 1.50 mass %, secondary recrystallization becomes unstable, and the magnetic properties tend to deteriorate. Therefore, the Ni content is preferably 0.03 mass % or more. The Ni content is preferably 1.50 mass % or less.

[0098] Further, Sn, Sb, Cu, P, Mo, and Cr are elements useful for improving the magnetic properties. However, when the content of each added element is below the lower limit described above, the effect of improving the magnetic properties is small. On the other hand, when the content of each added element exceeds the upper limit described above, the development of secondary recrystallized grains tends to be inhibited. Therefore, the content of each added element is preferably in the above-described range.

[0099] The balance other than the above-described elements is preferably inevitable impurities and Fe, which is a main component, that are incorporated during the manufacturing processes. In a product sheet (grain-oriented electrical steel sheet), the amount of the components other than C and inhibitor components contained in the steel material (slab for grain-oriented electrical steel sheet) is also contained in the product sheet as it is. On the other hand, C is reduced by decarburization annealing, and it is preferably reduced to 0.003 mass % or less in a product sheet to prevent an increase in iron loss due to magnetic aging. The inhibitor components are purified in the final annealing described below, and their contents are preferably reduced to the level of inevitable impurities in a product sheet.

[0100] The following describes a method of manufacturing a grain-oriented electrical steel sheet of the present disclosure.

[0101] [Heating]

[0102] A slab suitably having the above chemical composition may be heated according to a conventional method prior to hot rolling. The heating temperature is preferably 1150° C. or higher. The heating temperature is preferably 1450° C. or lower.

[0103] [Hot Rolling]

[0104] Hot rolling is suitably performed after the heating to obtain a hot-rolled sheet. Alternatively, the slab may be directly subjected to hot rolling without heating, after casting. In the case of thin slab or thinner cast steel, hot rolling may be performed separately, or the preparation of thin slab or thinner cast steel may be combined with hot rolling.

[0105] In the case of performing hot rolling, it is preferable to set the rolling temperature in the rough rolling final pass to 900° C. or higher and the rolling temperature in the finish rolling final pass to 700° C. or higher.

[0106] [Hot-Rolled Sheet Annealing]

[0107] After this, the hot-rolled sheet is optionally subjected to hot-rolled sheet annealing. At this time, the hot-rolled sheet annealing temperature is preferably set in the range of 800° C. or higher and 1100° C. or lower to highly develop a Goss texture in a product sheet. When the hot-rolled sheet annealing temperature is lower than 800° C., there remains a band texture resulting from hot rolling, which makes it difficult to obtain a primary recrystallization texture of uniformly-sized grains and tends to impede the growth of secondary recrystallization. On the other hand, when the hot-rolled sheet annealing temperature exceeds 1100° C., the grain size after hot-rolled sheet annealing coarsens excessively, which makes it extremely difficult to obtain a primary recrystallization texture of uniformly-sized grains.

[0108] [Cold Rolling]

[0109] Next, the sheet is subjected to cold rolling once, or twice or more with intermediate annealing performed therebetween to obtain a steel sheet with a final thickness. The intermediate annealing temperature is preferably 800° C. or higher. The intermediate annealing temperature is preferably 1150° C. or lower. The intermediate annealing time is preferably about 10 seconds to 100 seconds.

[0110] [Decarburization Annealing]

[0111] Next, the steel sheet is subjected to decarburization annealing. The decarburization annealing is preferably performed under conditions of annealing temperature: 750° C. to 900° C., oxidizing atmosphere P(H.sub.2O)/P(H.sub.2): 0.25 to 0.60, and annealing time: about 50 seconds to 300 seconds.

[0112] As described above, it is preferable to form grooves on the steel sheet after final cold rolling and before decarburization annealing.

[0113] [Application of Annealing Separator]

[0114] Next, an annealing separator is applied to one side or both sides of the steel sheet. It is preferable to apply an annealing separator to both sides of the steel sheet. The main component of the annealing separator is MgO, and the amount applied is preferably about 8 g/m.sup.2 to 15 g/m.sup.2 on each side of the steel sheet to form a forsterite film with a predetermined thickness.

[0115] [Final Annealing]

[0116] Next, the steel sheet is subjected to final annealing for the purposes of secondary recrystallization and formation of a forsterite film.

[0117] From the viewpoint of forming a forsterite film with a predetermined thickness, the annealing temperature and annealing time are preferably 1100° C. or higher and 30 minutes or longer, respectively.

[0118] [Tension Coating and Flattening Annealing]

[0119] After the final annealing, correcting the shape by flattening annealing is effective in improving the stacking factor when the grain-oriented electrical steel sheet is processed into an iron core. The flattening annealing is preferably performed with an annealing temperature of 750° C. to 950° C. and an annealing time of about 10 seconds to 200 seconds.

[0120] In the present disclosure, the steel sheet surface is preferably applied with a tension coating (insulating coating) before or after the flattening annealing. The tension coating is such a coating that imparts tension to the steel sheet for iron loss reduction. Examples of the tension coating include inorganic coating containing silica and ceramic coating, which can be applied with conventional methods such as physical deposition, chemical deposition, and the like.

[0121] The grain-oriented electrical steel sheet of the present disclosure can be suitably obtained by the processes described above, and all of the processes and manufacturing conditions not described above may be according to conventional methods.

EXAMPLES

[0122] A steel slab (slab for grain-oriented electrical steel sheet) was manufactured by continuous casting, where the steel slab had a chemical composition containing C: 0.07 mass %, Si: 3.4 mass %, Mn: 0.1 mass %, Ni: 0.2 mass %, Al: 240 mass ppm, S: 20 mass ppm, N: 90 mass ppm, and Se: 180 mass ppm, with the balance being inevitable impurities. The slab was heated to 1430° C. and then subjected to hot rolling to obtain a hot-rolled sheet with a thickness of 2.2 mm. The hot-rolled sheet was subjected to hot-rolled sheet annealing at 1100° C. for 20 seconds. Next, the hot-rolled sheet after hot-rolled sheet annealing was subjected to cold rolling to obtain an intermediate thickness of 0.40 mm, and then to intermediate annealing under the conditions of oxidation degree P(H.sub.2O)/P(H.sub.2)=0.40, temperature: 1000° C., and time: 70 seconds. Next, after removing subscale from the surface of the hot-rolled sheet after intermediate annealing by pickling with hydrochloric acid, the steel sheet was cold rolled again to obtain a steel sheet with a final thickness of 0.23 mm.

[0123] Grooves were formed on one side of the steel sheet under the conditions listed in Table 3.

[0124] The groove formation patterns listed in Table 3 are as follows. The groove width was adjusted to 150 μm in all cases.

[0125] I After final annealing, grooves with a depth of 10 μm were formed by a gear-shaped roller at intervals of 5 mm.

[0126] II After final annealing, grooves with a depth of 15 μm were formed by high-output laser irradiation.

[0127] III After applying resist ink in a pattern with non-applied areas at intervals of 3 mm using a groove roller, grooves with a depth of 20 μm were formed in the non-applied areas by electrolytic etching.

[0128] IV After applying resist ink in a pattern with non-applied areas at intervals of 3 mm using an inkjet printer (200 dpi), grooves with a depth of 20 μm were formed in the non-applied areas by electrolytic etching.

[0129] V After applying resist ink to one side of the steel sheet, a laser was repeatedly scanned in a linear fashion in a direction orthogonal to the rolling direction and at intervals of 3 mm in the rolling direction so that the resist ink was peeled off and removed at intervals of 3 mm in the rolling direction. The laser irradiation was performed with a galvano scanner method by a single mode fiber laser to peel off the resist ink continuously and completely from one end to the other end in the width direction of the steel sheet. Next, electrolytic etching was performed to form grooves with a depth of 25 μm.

[0130] In the above groove formation patterns, when resist ink was applied, the resist ink remaining on the steel sheet was removed after electrolytic etching.

[0131] Next, the steel sheet was subjected to decarburization where it was retained at an oxidation degree P(H.sub.2O)/P(H.sub.2) of 0.44 and a soaking temperature of 820° C. for 300 seconds. Next, an annealing separator composed mainly of MgO was applied to the surface of the steel sheet, and final annealing was performed for the purposes of secondary recrystallization, formation of a forsterite film and purification under the conditions of 1160° C. and 10 hours. Then, tension coating was performed in which an insulating coating made of 60 mass % colloidal silica and aluminum phosphate was applied and then baked at 850° C. to obtain a test piece. This tension coating application process also serves as flattening annealing.

[0132] The thickness of the forsterite film formed on the floor of the grooves of the test piece thus obtained was investigated, and the average value and standard deviation of the forsterite film thickness were calculated in the same manner as in Experiment 1 described above.

[0133] The test piece was sheared to a size of 30 mm×280 mm and then subjected to stress relief annealing under conditions of an argon atmosphere, 800° C. and 3 hours (to eliminate the effects of shearing), and then the sample was subjected to magnetic property measurement with the Epstein test method. To further investigate the effect of stress relief annealing in a carburizing atmosphere, stress relief annealing was again performed at 820° C. for 2 hours in ammonia decomposition gas (mixed gas) with NH.sub.3: 12 vol % to 15 vol % and N.sub.2:H.sub.2=1:3 as residual gas. The sample after stress relief annealing was subjected to magnetic property measurement with the Epstein test method. The results of Epstein tests before and after the stress relief annealing using the nitriding atmosphere mixed gases were compared to determine the increase or decrease in W.sub.17/50. Further, the amount of nitrogen was chemically analyzed before and after the stress relief annealing, and the results of the chemical analysis before and after the annealing were compared to determine the increase or decrease in nitrogen.

[0134] Table 3 listed the average value and standard deviation of the thickness of the forsterite film formed on the floor of the grooves, as well as the increase or decrease in W.sub.17/50 and the increase or decrease in nitrogen (nitriding quantity) before and after the stress relief annealing in the nitriding atmosphere mixed gas. In Table 3, irradiation energy and steel sheet temperature are indicated as “-” for test Nos. 1 to 4, where laser scanning for the purpose of removing resist ink was not performed.

[0135] As listed in Table 3, when a forsterite film satisfying the predetermined average thickness and standard deviation was formed on the floor of the grooves under the conditions of the present disclosure, nitriding during stress relief annealing could be effectively suppressed, and a grain-oriented electrical steel sheet with excellent magnetic properties could be obtained.

TABLE-US-00003 TABLE 3 Forsterite film thickness Before and after stress relief annealing on the floor of grooves in nitriding atmosphere gas Groove Irradiation Steel sheet Standard Increase or Increase or Example formation energy temperature Average deviation decrease in W.sub.17/50 decrease in carbon Test No. pattern (J/m) (° C.) (μm) (μm) (W/kg) (ppm) Remarks 1 I — — No forsterite film formed 0.42 235 Comparative Example 2 II — — No forsterite film formed 0.45 226 Comparative Example 3 III — — 0.66 0.48 0.18 83 Comparative Example 4 IV — — 0.67 0.37 0.15 65 Comparative Example 5 V 15 60 0.72 0.04 0.02 13 Example 6 V 20 60 0.73 0.03 0.01 15 Example 7 V 25 60 0.72 0.02 0.01 12 Example 8 V 27 60 0.71 0.13 0.02 18 Example 9 V 29 60 0.55 0.23 0.02 19 Example 10 V 32 60 0.48 0.38 0.15 64 Comparative Example 11 V 35 60 0.55 0.43 0.16 69 Comparative Example 12 V 40 60 0.47 0.35 0.19 62 Comparative Example 13 V 45 60 0.43 0.31 0.25 82 Comparative Example 14 V 50 60 0.27 0.18 0.27 153 Comparative Example 15 V 20 15 0.63 0.40 0.16 72 Comparative Example 16 V 20 20 0.61 0.37 0.15 67 Comparative Example 17 V 20 25 0.68 0.39 0.13 57 Comparative Example 18 V 20 30 0.72 0.40 0.12 54 Comparative Example 19 V 20 35 0.69 0.37 0.11 42 Comparative Example 20 V 20 40 0.75 0.19 0.03 13 Example 21 V 20 50 0.72 0.06 0.02 9 Example 22 V 20 80 0.74 0.05 0.01 7 Example 23 V 20 100 0.69 0.08 0.01 8 Example 24 V 20 150 0.68 0.06 0.01 7 Example 25 V 20 180 0.62 0.03 0.02 11 Example 26 V 20 195 0.63 0.09 0.03 17 Example 27 V 20 220 0.64 0.37 0.13 55 Comparative Example 28 V 20 250 0.61 0.45 0.18 82 Comparative Example