SOLID WIRE FOR GAS METAL ARC WELDING

Abstract

Provided is a solid wire for gas metal arc welding, solid wire being suitable as a welding material for high-Mn steel materials and generating less fume during welding. The solid wire of the present invention has a composition containing, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

Claims

1. A solid wire for gas metal arc welding, the solid wire comprising a composition that contains, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

2. The solid wire for gas metal arc welding according to claim 1, wherein the composition further contains at least one selected from the groups A and B in mass %, Group A: at least one selected from V: 1.0% or less, Ti: 1.0% or less, and Nb: 1.0% or less; and Group B: at least one selected from Cu: 1.00% or less, Ca: 0.010% or less, and REM: 0.020% or less.

3. (canceled)

4. A gas metal arc welding method comprising welding a high-Mn steel having a Mn content of 10 to 35% by gas metal arc welding in accordance with JIS Z 3930-2013 using a solid wire for gas metal arc welding and using, as a shielding gas, a mixed gas containing 10 to 40% CO.sub.2 and the balance being an inert gas Ar at a welding current of 180 to 330 A at a fume generation amount of 1200 mg/min or less, the solid wire having a composition that contains, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

5. The gas metal arc welding method according to claim 4, wherein the composition further contains, at least one selected from the groups A and B, in mass %, Group A: at least one selected V: 1.0% or less, Ti: 1.0% or less, and Nb: 1.0% or less; and Group B: at least one selected from Cu: 1.00% or less, Ca: 0.010% or less, and REM: 0.020% or less.

6. (canceled)

7. The gas metal arc welding method according to claim 4, wherein a weld joint formed by the gas metal arc welding method exhibits excellent low-temperature toughness of an absorbed energy of 28 J or more in a Charpy impact test at a test temperature of −196° C., and high strength of a room-temperature tensile strength of 400 MPa or more.

8. A method for producing a weld joint by using the gas metal arc welding method according to claim 4.

9. The gas metal arc welding method according to claim 5, wherein a weld joint formed by the gas metal arc welding method exhibits excellent low-temperature toughness of an absorbed energy of 28 J or more in a Charpy impact test at a test temperature of −196° C., and high strength of a room-temperature tensile strength of 400 MPa or more.

10. A method for producing a weld joint by using the gas metal arc welding method according to claim 5.

11. A method for producing a weld joint by using the gas metal arc welding method according to claim 7.

12. A method for producing a weld joint by using the gas metal arc welding method according to claim 9.

Description

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

[0043] Aspects of the present invention provide a solid wire for gas metal arc welding, and the solid wire is suitable for welding a high-Mn steel material by gas metal arc welding. When the solid wire according to aspects of the present invention is used, high-Mn steel materials can be welded to each other while reducing the amount of fume generated. The solid wire according to aspects of the present invention provides a deposited metal obtained by gas metal arc welding in accordance with JIS Z 3111 having high strength of a 0.2% proof stress of 400 MPa or more at room temperature and excellent cryogenic toughness of an absorbed energy of 28 J or more in a Charpy impact test at a test temperature of −196° C. Accordingly, the solid wire according to aspects of the present invention is a welding material with which a weld joint having high strength and excellent cryogenic toughness can be manufactured.

[0044] The solid wire according to aspects of the present invention has a basic composition containing, in mass %, C: 0.20 to 0.80%, Si: 0.15 to 0.90%, Mn: 15.0 to 30.0%, P: 0.030% or less, S: 0.030% or less, Al: 0.020% or less, Ni: 0.01 to 10.00%, Cr: 6.0 to 15.0%, Mo: 0.01 to 3.50%, O: 0.010% or less, N: 0.120% or less, and the balance being Fe and incidental impurities.

[0045] First, the reasons for limiting the composition of the basic composition are described. In the description below, “mass %” is simply referred to as “%”.

[0046] C: 0.20 to 0.80%

[0047] C is an element that has an effect of increasing the strength of the weld metal through solid solution strengthening, stabilizes the austenite phase, and improves the cryogenic impact toughness of the weld metal. To obtain these effects, the C content needs to be 0.20% or more. However, at a C content of more than 0.80%, carbides precipitate, the cryogenic toughness is degraded, and hot crack is likely to occur during welding. Thus, the C content is limited to the range of 0.20 to 0.80%. The C content is preferably 0.40% or more. The C content is preferably 0.60% or less.

[0048] Si: 0.15 to 0.90%

[0049] Si acts as a deoxidizer and has the effects of increasing the yield of Mn, increasing the viscosity of molten metal, stably maintaining the bead shape, and reducing the occurrence of spatter. To obtain these effects, the Si content needs to be 0.15% or more. However, at a Si content exceeding 0.90%, the cryogenic toughness of the weld metal is degraded. Furthermore, Si segregates during solidification and forms a liquid phase at the interface of solidification cells, which lowers the hot crack resistance. Thus, the Si content is limited to the range of 0.15 to 0.90%. Preferably, the Si content is 0.20% or more. Preferably, the Si content is 0.70% or less.

[0050] Mn: 15.0 to 30.0%

[0051] Mn is an inexpensive element that stabilizes the austenite phase, and the Mn content in accordance with aspects of the present invention needs to be 15.0% or more. At a Mn content of less than 15.0%, a ferrite phase is formed in the weld metal, and the cryogenic toughness is significantly degraded. Meanwhile, at a Mn content exceeding 30.0%, excessive Mn segregation occurs during solidification, causing hot crack. Thus, the Mn content is limited to the range of 15.0 to 30.0%. Preferably, the Mn content is 18.0% or more. Preferably, the Mn content is 27.0% or less.

[0052] P: 0.030% or less

[0053] P is an element that segregates at grain boundaries and causes hot crack, and the P content is preferably decreased as much as possible in accordance with aspects of the present invention although 0.030% or less is still allowable. Thus, the P content is limited to 0.030% or less. Excessive reduction increases the refining cost. Thus, the P content is preferably adjusted to 0.003% or more.

[0054] S: 0.030% or less.

[0055] S exists as a sulfide inclusion MnS in the weld metal. MnS serves as a starting point of fracture and thus degrades the cryogenic toughness. Thus, the S content is limited to 0.030% or less. Excessive reduction increases the refining cost. Thus, the S content is preferably adjusted to 0.001% or more.

[0056] Al: 0.020% or less

[0057] Al is an element that acts as a deoxidizer and is added during steel melting. At an Al content exceeding 0.020%, coarse Al.sub.2O.sub.3 is formed and serves as a starting point of fracture during wire drawing process, thereby causing wire breaking. Thus, the Al content is limited to 0.020% or less. Preferably, the Al content is 0.015% or less and more preferably less than 0.009%.

[0058] Ni: 0.01 to 10.00%

[0059] Ni is an element that strengthens austenite grain boundaries, segregates at grain boundaries, and improves the cryogenic toughness. To obtain these effects, the Ni content needs to be 0.01% or more. In addition, Ni also has the effect of stabilizing the austenite phase, and thus further increasing the Ni content stabilizes the austenite phase and improves the cryogenic toughness of the weld metal. However, Ni is expensive, and would bring an economical disadvantage if contained at more than 10.00%. Thus, the Ni content is limited to the range of 0.01 to 10.00%. Preferably, the Ni content is 0.20% or more. Preferably, the Ni content is 8.00% or less.

[0060] Cr: 6.0 to 15.0%

[0061] Cr acts as an element that stabilizes the austenite phase at cryogenic temperatures and improves the cryogenic toughness of the weld metal. Cr also has the effect of improving the strength of the weld metal. In addition, Cr works effectively to increase the liquidus of molten metal and suppress the occurrence of hot crack. Furthermore, Cr, which forms CrP in the liquid phase, has the effect of suppressing hot cracks caused by P. To obtain these effects, the Cr content needs to be 6.0% or more. At a Cr content of less than 6.0%, the aforementioned effects cannot be obtained. Meanwhile, at a Cr content exceeding 15.0%, Cr carbides occur, and the cryogenic toughness is degraded. Furthermore, occurrence of carbides degrades the workability during wire drawing. Thus, the Cr content is limited to the range of 6.0 to 15.0%. Preferably, the Cr content is 7.0% or more.

[0062] Mo: 0.01% to 3.50%

[0063] Mo is an element that strengthens austenite grain boundaries, segregates at grain boundaries, and improves the strength of the weld metal. These effects are prominent when the Mo content is 0.01% or more. At a Mo content exceeding 0.01%, Mo also has the effect of improving the strength of the weld metal through solid solution strengthening. Meanwhile, at a Mo content exceeding 3.50%, Mo precipitates as carbides, which degrade the hot workability, and degrades the wire manufacturability such as inducing cracks during wire drawing. Thus, the Mo content is limited to the range of 0.01 to 3.50%. Preferably, the Mo content is 0.1% or more. Preferably, the Mo content is 3.0% or less.

[0064] O: 0.010% or less

[0065] Oxygen (O) is an inevitable element and is separated as oxides by flotation after addition of deoxidizers such as Al, Si, and Mn. At an O content exceeding 0.010%, coarse oxides are formed, and, particularly when Al is contained in an amount exceeding 0.020%, coarse Al.sub.2O.sub.3 (oxide) is formed. The coarse oxide (Al.sub.2O.sub.3) serves as a starting point of fracture, and wire manufacturability is degraded. Thus, the oxygen (O) content is limited to 0.010% or less. Preferably, the oxygen (O) content is 0.008% or less.

[0066] N: 0.120% or less

[0067] Although N is an inevitable element, as with C, N is an element that effectively contributes to improve the strength of the weld metal, stabilizes the austenite phase, and contributes to stably improve the cryogenic toughness. These effects are prominent when the N content is 0.003% or more. Meanwhile, at a N content exceeding 0.120%, nitrides are formed, and the low-temperature toughness is degraded. Thus, the N content is limited to 0.120% or less. Preferably, the N content is 0.004% or more. Preferably, the N content is 0.080% or less.

[0068] The above-mentioned components are the basic components of the solid wire according to aspects of the present invention; however, in accordance with aspects of the present invention, in addition to the above-mentioned basic composition, at least one selected from V: 1.0% or less, Ti: 1.0% or less, and Nb: 1.0% or less, and/or at least one selected from Cu: 1.00% or less, Ca: 0.010% or less, and REM: 0.020% or less may be contained as necessary as optional components.

[0069] At least one selected from V: 1.0% or less, Ti: 1.0% or less, and Nb: 1.0% or less

[0070] All of V, Ti, and Nb are elements that promote formation of carbides and contribute to improve the strength of the weld metal, and the solid wire according to aspects of the present invention may contain at least one selected from these elements as necessary.

[0071] V is a carbide-forming element, causes precipitation of fine carbides, and thereby contributes to improve the strength of the weld metal. To obtain these effects, the V content is preferably 0.001% or more; however, at a V content exceeding 1.0%, carbides coarsen and become starting points of cracks during wire drawing of the solid wire, and thus the wire drawability and the wire manufacturability are degraded. Thus, if V is to be contained, the V content is preferably limited to 1.0% or less. Preferably, the V content is 0.002% or more. Preferably, the V content is 0.8% or less.

[0072] Ti is a carbide-forming element, causes precipitation of fine carbides, and contributes to improve the strength of the weld metal. In addition, Ti causes precipitation of carbides at the interface of solidification cells of the weld metal and contributes to suppress the occurrence of hot crack. To obtain these effects, the Ti content is preferably 0.001% or more; however, at a Ti content exceeding 1.0%, carbides coarsen and become starting points of cracks during wire drawing of the solid wire, and thus the wire drawability and the wire manufacturability are degraded. Thus, if Ti is to be contained, the Ti content is preferably limited to 1.0% or less. Preferably, the Ti content is 0.002% or more. Preferably, the Ti content is 0.8% or less.

[0073] Nb is a carbide-forming element, causes precipitation of carbides, and contributes to improve the strength of the weld metal. In addition, Nb causes precipitation of carbides at the interface of solidification cells of the weld metal and contributes to suppress the occurrence of hot crack. To obtain these effects, the Nb content is preferably 0.001% or more; however, at a Nb content exceeding 1.0%, carbides coarsen and become starting points of cracks during wire drawing of the solid wire, and thus the wire drawability and the wire manufacturability are degraded. Thus, if Nb is to be contained, the Nb content is preferably limited to 1.0% or less. Preferably, the Nb content is 0.002% or more. Preferably, the Nb content is 0.8% or less.

[0074] At least one selected from Cu: 1.00% or less, Ca: 0.010% or less, and REM: 0.020% or less

[0075] Cu is an element that contributes to stabilize austenite, Ca and REM are elements that contribute to improve workability, and at least one selected from Cu, Ca, and REM may be contained as necessary.

[0076] Cu is an element that stabilizes the austenite phase, stabilizes the austenite phase even at cryogenic temperatures, and thus improves the cryogenic toughness of the weld metal. To obtain these effects, the Cu content needs to be 0.01% or more. However, when Cu is contained in a large amount exceeding 1.00%, hot ductility is degraded, and the wire manufacturability is degraded. Thus, if Cu is to be contained, the Cu content is preferably limited to 1.00% or less. Preferably, the Cu content is 0.02% or more. Preferably, the Cu content is 0.8% or less.

[0077] Ca combines with S in molten metal to form a sulfide CaS with a high melting point. Since the CaS has a higher melting point than MnS, CaS remains spherical without advancing in the rolling direction during hot working of the solid wire, and thus CaS advantageously improves the workability of the solid wire. These effects are prominent when the Ca content is 0.001% or more. Meanwhile, at a Ca content exceeding 0.010%, arc is disturbed during the welding, which renders it difficult to conduct stable welding. Thus, if Ca is to be contained, the Ca content is preferably limited to 0.010% or less. Preferably, the Ca content is 0.001% or more. Preferably, the Ca content is 0.008% or less.

[0078] REM is a powerful deoxidizer and takes the form of REM oxides in the weld metal. REM oxides act as nucleation sites during solidification and thus refine crystal grains and contribute to improve the strength of the weld metal. These effects are prominent when the REM content is 0.001% or more. However, at a REM content exceeding 0.020%, stability of the arc is degraded. Thus, if REM is to be contained, the REM content is preferably limited to 0.020% or less. Preferably, the REM content is 0.002% or more. Preferably, the REM content is 0.018% or less.

[0079] The balance other than the above-mentioned components is Fe and incidental impurities.

[0080] Next, a method of manufacturing the solid wire according to aspects of the present invention is described.

[0081] Manufacturing a solid wire according to aspects of the present invention may be any common method for manufacturing solid wires for welding, and no limitation is imposed on the method except for the use of molten steel having the aforementioned composition.

[0082] Preferably, the solid wire according to aspects of the present invention is manufactured by performing the following steps sequentially: a casting step that involves smelting a molten steel having the aforementioned composition in a common smelting furnace such as an electric heating furnace or a vacuum melting furnace and casting the resulting molten steel into, for example, a mold having a predetermined shape; a heating step of heating the obtained steel ingot to a predetermined temperature; a hot rolling step of hot-rolling the heated steel ingot to obtain a steel material having a predetermined shape (rod shape); and a cold rolling step that involves cold-rolling (cold wire drawing) the obtained steel material (rod shape) multiple of times and, if necessary, annealing the steel material at an annealing temperature of 900 to 1200° C. so as to form a wire of desired dimensions.

[0083] Aspects of the present invention may also be implemented as a gas metal arc welding method. The gas metal arc welding method according to aspects of the present invention can involve welding a high-Mn steel having a Mn content of 10 to 35% by gas metal arc welding in accordance with JIS Z 3930-2013 using a solid wire for gas metal arc welding and using, as a shielding gas, a mixed gas containing 10 to 40% CO.sub.2 and the balance being an inert gas Ar at a welding current of 180 to 330 A at a fume generation amount of 1200 mg/min or less, the solid wire having a composition that contains, in mass %,

[0084] C: 0.20 to 0.80%,

[0085] Si: 0.15 to 0.90%,

[0086] Mn: 15.0 to 30.0%,

[0087] P: 0.030% or less,

[0088] S: 0.030% or less,

[0089] Al: 0.020% or less,

[0090] Ni: 0.01 to 10.00%,

[0091] Cr: 6.0 to 15.0%,

[0092] Mo: 0.01 to 3.50%,

[0093] O: 0.010% or less,

[0094] N: 0.120% or less, and

[0095] the balance being Fe and incidental impurities.

[0096] Furthermore, this gas metal arc welding method can be implemented as a gas metal arc welding method for forming a weld joint having excellent low-temperature toughness and high strength, exhibiting an absorbed energy of 28 J or more in a Charpy impact test at a test temperature of −196° C. and a room-temperature tensile strength of 400 MPa or more.

[0097] In the gas metal arc welding method, the chemical composition may further contain, in mass %, at least one selected from V: 1.0% or less, Ti: 1.0% or less, and Nb: 1.0% or less. The chemical composition may further contain, in mass %, at least one selected from Cu: 1.00% or less, Ca: 0.010% or less, and REM: 0.020% or less.

[0098] Aspects of the present invention can also be implemented as a method for manufacturing a weld joint by using the gas metal arc welding method described above.

[0099] The present invention will now be further described through examples.

EXAMPLES

[0100] Molten steels having compositions indicated in Table 1 were smelted in a vacuum melting furnace, and casted into 1000 kg steel ingots. The obtained steel ingots were heated to 1200° C., then hot-rolled, and then cold-rolled to obtain 1.2 mmϕ solid wires for gas metal arc welding. During the manufacture of the wires, the manufacturability of each solid wire was evaluated by measuring the rolling load (drawing load), observing cracks, observing a cross section of the wire, etc. When it was judged that the rolling load (drawing load) was too high to perform a rolling (drawing) process, occurrence of cracks was observed, or the process could not further continue due to the occurrence of cracks, for example, the wire manufacturability was evaluated as “Poor”. Otherwise, the wire manufacturability was evaluated as “Good”.

[0101] As a comparative example, flux cored wires constituted by steel sheaths and metal powders and flux powders enclosed in the steel sheaths were prepared. A thin steel sheet (sheet thickness: 0.5 mm) that has a 0.1% C-0.2% Si-0.5% Mn-balance Fe composition in mass % was used as a steel sheath material and cold-bended in the width direction into a letter-U-shape. Metal powders and flux powders both of which components were adjusted to yield the wire compositions indicated in Table 2 were enclosed in the obtained steel sheaths, and the resulting products were cold-drawn into flux cored wires (diameter: 1.2 mmϕ) for welding. The amounts of components indicated in Table 2 are the total values of the steel sheaths, the metal powders, and the flux powders.

[0102] Next, by using the obtained solid wires or flux cored wires as welding materials, gas metal arc welding was performed in a weld fume collector in accordance with JIS Z 3930, the fume generated was collected by a filter material (made of glass fibers), and fume generation amounts (mg/min) were measured. The gas metal arc welding conditions were as follows: current: 250 A, voltage: 34 V, welding speed: 30 cm/min, shielding gas: 80% Ar+20% CO.sub.2 (flow rate: 20 L/min).

[0103] High-Mn steel plates for cryogenic temperatures (plate thickness: 12 mm) were prepared as test plates and butted to form a 45° V groove in accordance with JIS Z 3111, and gas metal arc welding were performed by using obtained solid wires or flux cored wires as welding materials so as to obtain deposited metals in the grooves. The high-Mn steel plates for cryogenic temperatures used as the test plates had a 0.5% C-0.4% Si-25% Mn-3% Cr-balance Fe composition in mass %.

[0104] The gas metal arc welding was performed using each solid wire (diameter: 1.2 mm) or flux cored wire (diameter: 1.2 mm) having the composition indicated in Table 1 or 2 in a flat position without preheating, where the conditions were current: 180 A to 330 A (DCEP), voltage: 24 V to 33 V, welding speed: 30 cm/min, interpass temperature: 100° C. to 150° C., shielding gas: Ar-10-40% CO.sub.2.

[0105] After the welding, deposited metals were observed with an optical microscope to determine the presence or absence of weld cracks. Weld cracks are hot cracks, and samples from which cracks were observed were evaluated as “Poor” as having degraded hot crack resistance. Samples from which cracks were not observed were evaluated as “Good” as having excellent hot crack resistance.

[0106] The appearance of weld beads was observed with naked eye and evaluated. Samples from which undercut, overlap, or pit was observed were evaluated as “Poor” as having poor weld bead appearance. Samples from which none of these was observed were evaluated as “Good” as having good bead appearance.

[0107] Tensile test pieces of the deposited metals (parallel part diameter: 6 mmϕ) and Charpy impact test pieces (V notch) of the deposited metals were taken from the obtained deposited metals in accordance with JIS Z 3111, and the test pieces were subjected to tensile tests and impact tests.

[0108] The tensile tests were performed at room temperature on three test pieces, and the average value of the obtained values (0.2% proof stress) was assumed to be the tensile property of the deposited metal prepared by using the corresponding wire. The Charpy impact tests were performed on three test pieces to determine absorbed energies vE.sub.−196 at a test temperature of −196° C., and the average value thereof was assumed to be the cryogenic toughness of the deposited metal obtained by using the corresponding wire.

[0109] The results are indicated in Table 3.

TABLE-US-00001 TABLE 1 Steel Chemical components (mass %) No. C Si Mn P S Al Ni Cr Mo O N V, Ti, Nb Cu, Ca, REM Remarks A 0.65 0.58 26.0 0.012 0.021 0.004 6.91 7.2 1.51 0.003 0.020 — — Conforming Example B 0.72 0.42 17.4 0.005 0.016 0.002 4.17 7.5 1.25 0.005 0.100 — — Conforming Example C 0.55 0.26 23.4 0.017 0.024 0.012 3.10 7.4 0.01 0.008 0.081 — — Conforming Example D 0.71 0.72 18.2 0.021 0.013 0.005 7.12 10.2 2.13 0.003 0.004 — — Conforming Example E 0.59 0.21 20.4 0.026 0.008 0.001 1.28 8.2 1.54 0.001 0.013 V: 0.8, — Conforming Ti: 0.3 Example F 0.39 0.37 27.1 0.013 0.027 0.004 2.12 14.7 0.05 0.002 0.112 Nb: 0.2 — Conforming Example G 0.43 0.48 24.2 0.025 0.028 0.012 4.81 12.3 2.81 0.005 0.050 — Cu: 0.12 Conforming Example H 0.51 0.17 18.2 0.016 0.024 0.018 2.46 9.2 3.20 0.001 0.006 — — Conforming Example I 0.27 0.41 15.3 0.014 0.017 0.004 0.02 9.3 1.84 0.007 0.005 — REM: 0.011 Conforming Example J 0.75 0.82 23.8 0.009 0.015 0.007 2.31 8.9 3.05 0.008 0.008 — REM: 0.011 Conforming Example K 0.36 0.37 29.4 0.016 0.009 0.009 8.77 12.1 1.51 0.007 0.011 Ti: 0.9 Ca: 0.001 Conforming Example L 0.45 0.75 21.6 0.016 0.010 0.013 3.60 10.5 0.12 0.002 0.012 Ti: 0.1, Cu: 0.81, REM: 0.018 Conforming Nb: 0.4 Example M 0.48 0.44 17.2 0.017 0.008 0.015 6.25 6.8 0.32 0.004 0.090 V: 0.1 Ca: 0.006 Conforming Example N 0.14 0.30 18.1 0.023 0.019 0.012 1.41 6.2 0.04 0.006 0.080 Nb: 0.8 — Comparative Example O 0.25 0.46 20.5 0.016 0.016 0.003 1.27 5.7 0.05 0.007 0.005 V: 0.4, — Comparative Ti: 0.2 Example P 0.37 0.28 40.3 0.018 0.027 0.004 0.04 8.6 0.60 0.003 0.120 — Ca: 0.002, Comparative REM: 0.006 Example Q 0.51 0.38 24.6 0.013 0.015 0.012 0.08 9.4 2.78 0.003 0.090 Ti: 1.2, Ca: 0.001 Comparative Nb: 1.5 Example R 0.39 0.72 19.2 0.021 0.024 0.022 2.51 7.3 1.54 0.009 0.080 — — Comparative Example S 0.42 0.53 24.6 0.007 0.008 0.018 6.13 8.5 0.82 0.013 0.004 V: 0.2, — Comparative Nb: 0.9 Example T 0.46 0.27 12.8 0.012 0.006 0.007 3.14 9.8 1.24 0.005 0.050 V: 0.1 Cu0.57 Comparative Example U 0.53 0.62 26.2 0.026 0.021 0.009 <0.001 10.4 <0.001 0.003 0.042 — — Comparative Example V 0.42 1.50 18.8 0.025 0.013 0.013 4.72 11.8 0.36 0.005 0.080 Ti: 0.4 Cu: 0.21, Ca: 0.001 Comparative Example W 0.47 0.25 18.2 0.038 0.021 0.015 1.29 14.2 1.28 0.007 0.090 — Ca: 0.007, Comparative REM: 0.013 Example X 0.96 0.42 26.2 0.008 0.012 0.012 3.14 13.9 1.88 0.009 0.012 — — Comparative Example Y 0.36 0.07 19.7 0.016 0.014 0.003 1.76 9.2 0.84 0.001 0.070 — Comparative Example

TABLE-US-00002 TABLE 2 Flux cored Chemical components (mass %) No. C Si Mn P S Al Ni Cr Mo O N V, Ti, Nb Cu, Al, REM Remarks C1 0.61 0.34 18.8 0.012 0.008 0.009 2.12 10.4 1.21 0.140 0.0008 — — Comparative Example C2 0.55 0.31 26.1 0.003 0.008 0.002 0.05 6.9 1.22 0.120 0.0007 — — Comparative Example C3 0.29 0.55 24.2 0.024 0.024 0.017 2.19 13.7 0.01 0.180 0.0005 — — Comparative Example C4 0.34 0.28 18.2 0.016 0.026 0.012 6.82 9.4 2.11 0.160 0.0004 — — Comparative Example

TABLE-US-00003 TABLE 3 Fume generation Weld metal properties* properties** Fume 0.2% Steel generation proof Absorbed Wire No./Flux Wire amount Hot crack Weld bead stress energy No. cored No. manufacturability (mg/min) resistance appearance (MPa) vE.sub.−196 (J) Remarks 1 A Good 729 Good Good 496 76 Example 2 B Good 556 Good Good 455 46 Example 3 C Good 673 Good Good 421 80 Example 4 D Good 575 Good Good 523 52 Example 5 E Good 613 Good Good 481 41 Example 6 F Good 748 Good Good 518 76 Example 7 G Good 691 Good Good 567 73 Example 8 H Good 568 Good Good 504 57 Example 9 I Good 511 Good Good 428 49 Example 10 J Good 688 Good Good 537 68 Example 11 K Good 794 Good Good 576 64 Example 12 L Good 642 Good Good 458 70 Example 13 M Good 551 Good Good 416 83 Example 14 N Good 566 Good Good 370 48 Comparative Example 15 O Good 616 Poor Good 373 68 Comparative Example 16 P Good 1011 Poor Good 499 52 Comparative Example 17 Q Poor *** *** *** *** *** Comparative Example 18 R Poor *** *** *** *** *** Comparative Example 19 S Poor *** *** *** *** *** Comparative Example 20 T Good 461 Good Good 439 11 Comparative Example 21 U Good 733 Good Good 451 16 Comparative Example 22 V Good 593 Poor Good 484 14 Comparative Example 23 W Good 571 Poor Good 507 71 Comparative Example 24 X Good 731 Poor Good 586 42 Comparative Example 25 Y Good 597 Good Poor 432 53 Comparative Example 26 C1 Good 1747 Good Good 466 49 Comparative Example 27 C2 Good 2184 Good Good 440 72 Comparative Example 28 C3 Good 2073 Good Good 474 63 Comparative Example 29 C4 Good 1706 Good Good 486 40 Comparative Example *In accordance with JIS Z 3930-2013. **In accordance with JIS Z 3111. ***) Unmeasurable.

[0110] All of Examples of the present invention have excellent wire manufacturability and can be regarded as welding materials that generate less fume, that is, the amounts of fume generated when gas metal arc welding are performed with a welding current of 250 A in accordance with JIS Z 3930-2013 are 1200 mg/min or less.

[0111] In addition, all of Examples of the present invention were free of weld cracks (hot cracks) during welding and thus had excellent hot crack resistances and can be considered to be welding materials from which deposited metals having excellent weld bead appearances are obtained.

[0112] Furthermore, all Examples had yield strengths (0.2% proof stress) of 400 MPa or more at room temperature and absorbed energies vE.sub.−196 of 28 J or more in the Charpy impact test at a test temperature of −196° C. Thus, all Examples can be regarded as welding materials (solid wires) with which weld metals having both high strength and excellent cryogenic toughness can be obtained.

[0113] In contrast, in each Comparative Example outside the scope of the present invention, either the amount of fume generated was more than 1200 mg/min, the wire manufacturability was poor, welding cracks (hot cracks) had occurred and had degraded hot crack resistance, the weld bead was defective and had poor appearance, the 0.2% proof stress was less than 400 MPa at room temperature, or the absorbed energy vE.sub.−196 was less than 28 J. Thus, in Comparative Examples, a deposited metal with which less fume is generated during welding, and which has both high strength and excellent cryogenic toughness was not obtained.

[0114] The wire No. 14 of Comparative Example had a C content below the range according to aspects of the present invention, and the wire No. 15 of Comparative Example had a Cr content below the range according to aspects of the present invention. Thus, the 0.2% proof stresses of the deposited metals were less than 400 MPa, and the desired high strength was not achieved. In the wire No. 15, furthermore, hot cracks had occurred.

[0115] The wire No. 16 of Comparative Example had a Mn content above the range according to aspects of the present invention, and thus hot cracks had occurred.

[0116] The wire No. 17 of Comparative Example had a Ti content and a Nb content above the ranges according to aspects of the present invention, the wire No. 18 of Comparative Example had an Al content above the range according to aspects of the present invention, and the wire No. 19 of Comparative Example had an oxygen (O) content above the range according to aspects of the present invention. Thus, the wire drawabilities were degraded, and the wires could not be drawn to a desired wire diameter.

[0117] The wire No. 20 of Comparative Example had a Mn content below the range according to aspects of the present invention, and thus the stability of the austenite phase was low, and the cryogenic toughness was degraded to less than 28 J in terms of the absorbed energy vE.sub.−196.

[0118] The wire No. 21 of Comparative Example had a Ni content below the range according to aspects of the present invention, and thus the cryogenic toughness was degraded to less than 28 J in terms of the absorbed energy vE.sub.−196.

[0119] The wire No. 22 of Comparative Example had a Si content above the range according to aspects of the present invention, the wire No. 23 of Comparative Example had a P content above the range according to aspects of the present invention, and the wire No. 24 of Comparative Example had a C content above the range according to aspects of the present invention. Thus, hot cracks had occurred, and hot crack resistance was degraded. The wire No. 22 also had degraded cryogenic toughness, since the absorbed energy vE.sub.−196 was less than 28 J.

[0120] The wire No. 25 of Comparative Example had a Si content below the range according to aspects of the present invention, and thus good bead shape was not obtained, and pits occurred. Each of wires No. 26, No. 27, No. 28, and No. 29 is a flux cored wire, and a large amount of fume exceeding 1200 mg/min had been generated during welding.