STEEL SHEET AND PLATED STEEL SHEET
20240117476 ยท 2024-04-11
Assignee
Inventors
- Masaaki URANAKA (Tokyo, JP)
- Takuya MITSUNOBU (Tokyo, JP)
- Keitaro MATSUDA (Tokyo, JP)
- Hiroshi TAKEBAYASHI (Tokyo, JP)
- Jun Maki (Tokyo, JP)
Cpc classification
C22C18/04
CHEMISTRY; METALLURGY
C22C38/002
CHEMISTRY; METALLURGY
C22C38/005
CHEMISTRY; METALLURGY
B32B15/013
PERFORMING OPERATIONS; TRANSPORTING
C22C38/12
CHEMISTRY; METALLURGY
C23C2/28
CHEMISTRY; METALLURGY
International classification
Abstract
High strength steel sheet and plated steel sheet having high plateability, LME resistance, and hydrogen embrittlement resistance, that is, steel sheet containing C: 0.05 to 0.40%, Si: 0.2 to 3.0%, Mn: 0.1 to 5.0%, and sol. Al: 0.4 to 1.50%, having an internal oxidation layer including fine granular oxides in a surface layer of the steel sheet, a number density of fine granular oxides in the internal oxidation layer being 4.0/?m.sup.2 or more, and including a surface depleted layer with a steel composition not including oxides which satisfies, by mass %, Si?0.6% and Al?0.05% at a depth of ? of the average depth of the internal oxidation layer calculated from the cross-sectional SEM image of the steel sheet, and a plated steel sheet using the same.
Claims
1. A steel sheet having a chemical composition comprising, by mass %, C: 0.05 to 0.40%, Si: 0.2 to 3.0%, Mn: 0.1 to 5.0%, sol. Al: 0.4 to 1.50%, P: 0.0300% or less, S: 0.0300% or less, N: 0.0100% or less, B: 0 to 0.010%, Ti: 0 to 0.150%, Nb: 0 to 0.150%, V: 0 to 0.150%, Cr: 0 to 2.00%, Ni: 0 to 2.00%, Cu: 0 to 2.00%, Mo: 0 to 1.00%, W: 0 to 1.00%, Ca: 0 to 0.100%, Mg: 0 to 0.100%, Zr: 0 to 0.100%, Hf: 0 to 0.100%, and REM: 0 to 0.100% and having a balance of Fe and impurities, in which steel sheet, an internal oxidation layer including fine granular oxides is present in a surface layer of the steel sheet, and, when examining a cross-section of a surface layer of the steel sheet, a number density of fine granular oxides in the internal oxidation layer is 4.0/?m.sup.2 or more and a surface depleted layer with a steel composition not including the fine granular oxides which satisfies, by mass %, Si?0.6% and Al?0.05% is included at a depth of ? of the average depth of the internal oxidation layer.
2. The steel sheet according to claim 1, wherein the number density of fine granular oxides is 8/?m.sup.2 or more.
3. A plated steel sheet comprising the steel sheet according to claim 1 over which there is a plating layer including Zn.
4. The plated steel sheet according to claim 3 comprising a Zn-plated steel sheet, wherein the Al contained in the plating layer is 0.3 to 1.5 mass %.
5. A plated steel sheet comprising the steel sheet according to claim 2 over which there is a plating layer including Zn.
6. The plated steel sheet according to claim 5 comprising a Zn-plated steel sheet, wherein the Al contained in the plating layer is 0.3 to 1.5 mass %.
Description
BRIEF DESCRIPTION OF DRAWINGS
[0046]
[0047]
DESCRIPTION OF EMBODIMENTS
[0048] <Steel Sheet>
[0049] The steel sheet according to the present invention is a steel sheet having a chemical composition comprising, by mass %, C: 0.05 to 0.40%, [0050] Si: 0.2 to 3.0%, [0051] Mn: 0.1 to 5.0%, [0052] sol. Al: 0.4 to 1.50%, [0053] P: 0.0300% or less, [0054] S: 0.0300% or less, [0055] N: 0.0100% or less, [0056] B: 0 to 0.010%, [0057] Ti: 0 to 0.150%, [0058] Nb: 0 to 0.150%, [0059] V: 0 to 0.150%, [0060] Cr: 0 to 2.00%, [0061] Ni: 0 to 2.00%, [0062] Cu: 0 to 2.00%, [0063] Mo: 0 to 1.00%, [0064] W: 0 to 1.00%, [0065] Ca: 0 to 0.100%, [0066] Mg: 0 to 0.100%, [0067] Zr: 0 to 0.100%, [0068] Hf: 0 to 0.100%, and [0069] REM: 0 to 0.100% and [0070] having a balance of Fe and impurities, in which steel sheet, [0071] an internal oxidation layer including fine granular oxides is present in a surface layer of the steel sheet, and, [0072] when examining a cross-section of a surface layer of the steel sheet, [0073] a number density of fine granular oxides in the internal oxidation layer is 4.0/?m.sup.2 or more and [0074] a surface depleted layer with a steel composition not including the fine granular oxides which satisfies, by mass %, Si?0.6% and Al?0.05% is included at a depth of ? of the average depth of the internal oxidation layer.
[0075] In the production of high strength steel sheet, a steel slab adjusted to a predetermined chemical composition is rolled (typically, hot rolled and cold rolled), then annealed for the purpose of obtaining the desired microstructure etc. In the annealing, the comparatively easily oxidizable constituents in the steel sheet (for example, Si, Mn, and Al) bond with the oxygen in the annealing atmosphere whereby a layer including oxides formed in the vicinity of the surface of the steel sheet. For example, like the steel sheet 1 shown in
[0076] In contrast, as illustrated in
[0077] Further, high strength steel sheet used in an atmospheric environment, particularly high strength steel sheet for automobiles, is used repeatedly exposed in various environments of differing temperature and humidity. Such an environment is called a corrosive atmospheric environment. It is known that hydrogen is generated in the process of corrosion in a corrosive atmospheric environment. Moreover, the hydrogen penetrates deeper than the surface layer region in the steel and segregates at the martensite grain boundaries of the steel sheet microstructure thereby causing embrittlement of the grain boundaries and triggering hydrogen embrittlement cracking (delayed cracking) in the steel sheet. Martensite is a hard structure, so has a high hydrogen susceptibility and is more vulnerable to hydrogen embrittlement cracking. Such cracking can become a problem when working steel sheet. Accordingly, to prevent hydrogen embrittlement cracking, in high strength steel sheet used in a corrosive atmospheric environment, it is effective to reduce the amount of hydrogen built up in the steel, more specifically, the amount of hydrogen built up at positions deeper than the surface layer region of the steel sheet. The inventors discovered that by controlling the form of oxides present at the surface layer of steel sheet, more specifically, by causing fine granular oxides having a grain size and number density in predetermined ranges to be present as oxides, the fine granular oxides function as trap sites for hydrogen penetrating it at the surface layer region of the steel sheet in a corrosive environment and enable a further reduction in the amount of hydrogen built up in steel sheet used in a corrosive environment. Note that the term high hydrogen embrittlement resistance means a state in which the amount of hydrogen built up in steel sheet or plated steel sheet is reduced enough so that hydrogen embrittlement cracking can be sufficiently suppressed.
[0078] The inventors analyzed in detail the relationship between the form of the oxides and their effectiveness as trap sites for hydrogen. As a result, they discovered that, as shown in
[0079] On the other hand, when hot stamping or welding a plated steel sheet that has a plating layer including Zn provided on the steel sheet surface, because of the high temperature during working, sometimes the Zn included in the plating layer will melt. If the Zn melts, the molten Zn will penetrate the steel. If working is performed in that state, sometimes liquid metal embrittlement (LME) cracking will occur inside of the steel sheet and the fatigue properties of the steel sheet will degrade due to LME. The inventors discovered that if the fine granular oxides have the desired number densities, they can contribute not only to improving hydrogen embrittlement resistance but also improving LME resistance. In further detail, they discovered that the fine granular oxides function as trap sites for Zn trying to penetrate the steel during working at a high temperature. Due to this, Zn trying to penetrate the steel during, for example, hot stamping, is trapped by the fine granular oxides at the surface layer of the steel sheet and penetration of Zn into the crystal grain boundaries is suitably suppressed. Accordingly, they discovered that not only for improving the above-mentioned hydrogen penetration resistance but also improving the LME resistance, it is important for fine granular oxides to be made present in large amounts.
[0080] Furthermore, the fine granular oxides are formed by oxidation of the comparatively easily oxidizable constituents in the steel sheet (for example, Si, Mn, Al), so the composition of the steel around the granular oxides (in other words, the metallographic structure) is depleted in these easily oxidizable constituent elements compared to the original steel sheet base material. The region where the elements of the steel composition are depleted compared to the original steel sheet base material is also called a depleted region. A lamellar depleted region is also called a depleted layer. Further, one present at the surface layer of the steel sheet is also called a surface depleted layer. In a depleted region, among the easily oxidizable elements, Si oxidizes relatively easily, whereas Al oxidizes with relatively more difficulty, therefore Si can be made present in a small concentration and Al in a high concentration. The inventors also discovered that if a depleted region with such a low Si and high Al steel composition is present in a desired range, it also contributes to improving LME resistance. In further detail, they discovered that in addition to fine granular oxides functioning as Zn trap sites, if Al is present in the steel composition around the granular oxides, the Al will function as trap sites for the Zn trying to penetrate the steel during working at high temperature from penetrating into the steel grain boundaries and that because LME cracking is more likely to occur the higher the concentration of Si in the steel composition, so LME can be suppressed by keeping the Si to as low a concentration as possible. Due to this, the Zn trying to penetrate the steel during, for example, hot stamping is trapped by the Al in the composition of the steel, the penetration of Zn to the crystal grain boundaries is suitably suppressed, and, since there is a low concentration of Si easily causing LME, LME is less likely to occur. Accordingly, they discovered that it is important that a depleted region with a low Si concentration and high Al concentration be made present in order to improve LME resistance.
[0081] A depleted region in which Si is present in a low concentration and Al is present in a high concentration can also double as a region in which fine granular oxides are distributed, that is, it can be formed inside of the base steel instead of being formed like the external oxidation layer 2 on the surface of the base steel 3 in
[0082] Below, the steel sheet according to the present invention will be explained in detail. Note that the thickness of the steel sheet according to the present invention is not particularly limited but may be, for example, 0.1 to 3.2 mm.
[0083] [Chemical Composition of Steel Sheet]
[0084] The chemical composition of the steel sheet according to the present invention will be explained next. The % regarding content of the elements, unless otherwise stated, will mean mass %. In the numerical ranges in the chemical composition, a numerical range expressed using to, unless otherwise indicated, will mean a range having the numerical values before and after the to as the lower limit value and the upper limit value.
[0085] (C: 0.05 to 0.40%)
[0086] C (carbon) is an important element for securing the strength of steel. If the C content is insufficient, sufficient strength is liable to be unable to be secured. Furthermore, sometimes the desired form of the internal oxides and/or surface depleted layer will not be achieved due to the insufficient C content. Accordingly, the C content is 0.05% or more, preferably 0.07% or more, more preferably 0.10% or more, even more preferably 0.12% or more. On the other hand, if the C content is excessive, the weldability is liable to degrade. Accordingly, the C content is 0.40% or less, preferably 0.35% or less, more preferably 0.30% or less.
[0087] (Si: 0.2 to 3.0%)
[0088] Si (silicon) is an element effective for improving the strength of steel. If the Si content is insufficient, sufficient strength is liable to be unable to be secured. Furthermore, the desired oxides, particularly fine granular oxides, and/or the surface depleted layer are liable to not be sufficiently formed inside of the steel sheet. Accordingly, the Si content is 0.2% or more, preferably 0.3% or more, more preferably 0.5% or more, even more preferably 1.0% or more. On the other hand, if the Si content is excessive, deterioration of the surface properties is liable to be triggered. Furthermore, coarsening of the granular oxides is liable to be invited. Accordingly, the Si content is 3.0% or less, preferably 2.5% or less, more preferably 2.0% or less.
[0089] (Mn: 0.1 to 5.0%)
[0090] Mn (manganese) is an element effective for obtaining hard structures to improve the strength of steel. If the Mn content is insufficient, sufficient strength is liable to be unable to be secured. Furthermore, the desired oxides, particularly fine granular oxides, and/or the surface depleted layer are liable to not be sufficiently formed inside of the steel sheet. Accordingly, the Mn content is 0.1% or more, preferably 0.5% or more, more preferably 1.0% or more, even more preferably 1.5% or more. On the other hand, if the Mn content is excessive, the metallographic structure is liable to become uneven due to Mn segregation and the workability is liable to decline. Furthermore, coarsening of the granular oxides is liable to be invited. Accordingly, the Mn content is 5.0% or less, preferably 4.5% or less, more preferably 4.0% or less, even more preferably 3.5% or less.
[0091] (Sol. Al: 0.4 to 1.50%)
[0092] Al (aluminum) is an element which acts as a deoxidizing element. If the Al content is insufficient, a sufficient deoxidizing effect is liable to be unable to be secured. Furthermore, the desired oxides, particularly fine granular oxides and/or the surface depleted layer are liable to not be sufficiently formed inside of the steel sheet. The Al content may be 0.4% or more, but to achieve the desired effects sufficiently and obtain fine granular oxides and a surface depleted layer, the Al content should be 0.5% or more, preferably 0.6% or more, more preferably 0.7% or more. On the other hand, if the Al content is excessive, it is liable to trigger a reduction in the workability or a deterioration in surface properties. Furthermore, coarsening of the granular oxides is liable to be invited. Accordingly, the Al content is 1.50% or less, preferably 1.20% or less, more preferably 0.80% or less. The Al content means the content of so-called acid-soluble Al (sol. Al)
[0093] (P: 0.0300% or less)
[0094] P (phosphorus) is an impurity commonly contained in steel. If the P content is more than 0.0300%, the weldability is liable to decline. Accordingly, the P content is 0.0300% or less, preferably 0.0200% or less, more preferably 0.0100% or less, even more preferably 0.0050% or less. The lower limit of the P content is not particularly prescribed, but from the viewpoint of production costs, the P content may be more than 0% or be 0.0001% or more.
[0095] (S: 0.0300% or less)
[0096] S (sulfur) is an impurity commonly contained in steel. If the S content exceeds 0.0300%, the weldability is liable to decline and the amount of precipitated MnS may increase and reduce workability such as bendability. Accordingly, the S content is 0.0300% or less, preferably 0.0100% or less, more preferably 0.0050% or less, even more preferably 0.0020% or less. The lower limit of the S content is not particularly prescribed, but from the viewpoint of desulfurization costs, the S content may be more than 0% or be 0.0001% or more.
[0097] (N: 0.0100% or less)
[0098] N (nitrogen) is an impurity commonly contained in steel. If the N content exceeds 0.0100%, the weldability is liable to decline. Accordingly, the N content is 0.0100% or less, preferably 0.0080% or less, more preferably 0.0050% or less, even more preferably 0.0030% or less. The lower limit of the N content is not particularly prescribed, but from the viewpoint of production costs, the N content may be more than 0% or be 0.0010% or more.
[0099] (B: 0 to 0.010%)
[0100] B (boron) is an element which contributes to increasing hardenability and improving strength and further segregates at the grain boundaries to strengthen the grain boundaries and improve toughness, so may be contained as necessary. Accordingly, the B content is 0% or more, preferably 0.001% or more, more preferably 0.002% or more, even more preferably 0.003% or more. On the other hand, from the viewpoint of securing sufficient toughness and weldability, the B content is 0.010% or less, preferably 0.008% or less, more preferably 0.006% or less.
[0101] (Ti: 0 to 0.150%)
[0102] Ti (titanium) is an element which precipitates during cooling of steel as TiC and contributes to improving strength, so may be contained as necessary. Accordingly, the Ti content is 0% or more, preferably 0.001% or more, more preferably 0.003% or more, even more preferably 0.005% or more, yet even more preferably 0.010% or more. On the other hand, if contained excessively, coarse TiN is formed and the toughness is liable to be harmed, so the Ti content is 0.150% or less, preferably 0.100% or less, more preferably 0.050% or less.
[0103] (Nb: 0 to 0.150%)
[0104] Nb (niobium) is an element which contributes to improving strength through improving hardenability, so may be contained as necessary. Accordingly, the Nb content is 0% or more, preferably 0.010% or more, more preferably 0.020% or more, even more preferably 0.030% or more. On the other hand, from the viewpoint of securing sufficient toughness and weldability, the Nb content is 0.150% or less, preferably 0.100% or less, more preferably 0.060% or less.
[0105] (V: 0 to 0.150%)
[0106] V (vanadium) is an element which contributes to improving strength through improving hardenability, so may be contained as necessary. Accordingly, the V content is 0% or more, preferably 0.010% or more, more preferably 0.020% or more, even more preferably 0.030% or more. On the other hand, from the viewpoint of securing sufficient toughness and weldability, the V content is 0.150% or less, preferably 0.100% or less, more preferably 0.060% or less.
[0107] (Cr: 0 to 2.00%)
[0108] Cr (chromium) is effective for increasing the hardenability of steel and increasing the strength of steel, so may be contained as necessary. Accordingly, the Cr content is 0% or more, preferably 0.10% or more, more preferably 0.20% or more, even more preferably 0.50% or more, yet even more preferably 0.80% or more. On the other hand, if contained excessively, Cr carbides may form in large amounts and conversely the hardenability is liable to be harmed, so the Cr content is 2.00% or less, preferably 1.80% or less, more preferably 1.50% or less.
[0109] (Ni: 0 to 2.00%)
[0110] Ni (nickel) is effective for increasing the hardenability of steel and increasing the strength of steel, so may be contained as necessary. Accordingly, the Ni content is 0% or more, preferably 0.10% or more, more preferably 0.20% or more, even more preferably 0.50% or more, yet even more preferably 0.80% or more. On the other hand, excessive addition of Ni will invite an increase in costs, so the Ni content is 2.00% or less, preferably 1.80% or less, more preferably 1.50% or less.
[0111] (Cu: 0 to 2.00%)
[0112] Cu (copper) is effective for increasing the hardenability of steel and increasing the strength of steel, so may be contained as necessary. Accordingly, the Cu content is 0% or more, preferably 0.10% or more, more preferably 0.20% or more, even more preferably 0.50% or more, yet even more preferably 0.80% or more. On the other hand, from the viewpoint of suppressing a drop in toughness, cracking of slabs after casting, and a drop in weldability, the Cu content is 2.00% or less, preferably 1.80% or less, more preferably 1.50% or less.
[0113] (Mo: 0 to 1.00%)
[0114] Mo (molybdenum) is effective for increasing the hardenability of steel and increasing the strength of steel, so may be contained as necessary. Accordingly, the Mo content is 0% or more, preferably 0.10% or more, more preferably 0.20% or more, even more preferably 0.30% or more. On the other hand, from the viewpoint of suppressing a drop in toughness and weldability, the Mo content is 1.00% or less, preferably 0.90% or less, more preferably 0.80% or less.
[0115] (W: 0 to 1.00%)
[0116] W (tungsten) is effective for increasing the hardenability of steel and increasing the strength of steel, so may be contained as necessary. Accordingly, the W content is 0% or more, preferably 0.10% or more, more preferably 0.20% or more, even more preferably 0.30% or more. On the other hand, from the viewpoint of suppressing a drop in toughness and weldability, the W content is 1.00% or less, preferably 0.90% or less, more preferably 0.80% or less.
[0117] (Ca: 0 to 0.100%)
[0118] Ca (calcium) is an element contributing to inclusion control, particularly fine dispersion of inclusions, and has the action of increasing toughness, so may be contained as necessary. Accordingly, the Ca content is 0% or more, preferably 0.001% or more, more preferably 0.005% or more, even more preferably 0.010% or more, even more preferably 0.020% or more. On the other hand, if contained excessively, degradation of the surface properties will sometimes appear, so the Ca content is 0.100% or less, preferably 0.080% or less, more preferably 0.050% or less.
[0119] (Mg: 0 to 0.100%)
[0120] Mg (magnesium) is an element contributing to inclusion control, particularly fine dispersion of inclusions, and has the action of increasing toughness, so may be contained as necessary. Accordingly, the Mg content is 0% or more, preferably 0.001% or more, more preferably 0.003% or more, even more preferably 0.010% or more. On the other hand, if contained excessively, degradation of the surface properties will sometimes appear, so the Mg content is 0.100% or less, preferably 0.090% or less, more preferably 0.080% or less.
[0121] (Zr: 0 to 0.100%)
[0122] Zr (zirconium) is an element contributing to inclusion control, particularly fine dispersion of inclusions, and has the action of increasing toughness, so may be contained as necessary. Accordingly, the Zr content is 0% or more, preferably 0.001% or more, more preferably 0.005% or more, even more preferably 0.010% or more. On the other hand, if contained excessively, degradation of the surface properties will sometimes appear, so the Zr content is 0.100% or less, preferably 0.050% or less, more preferably 0.030% or less.
[0123] (Hf: 0 to 0.100%)
[0124] Hf (hafnium) is an element contributing to inclusion control, particularly fine dispersion of inclusions, and has the action of increasing toughness, so may be contained as necessary. Accordingly, the Hf content is 0% or more, preferably 0.001% or more, more preferably 0.005% or more, even more preferably 0.010% or more. On the other hand, if contained excessively, degradation of the surface properties will sometimes appear, so the Hf content is 0.100% or less, preferably 0.050% or less, more preferably 0.030% or less.
[0125] (REM: 0 to 0.100%)
[0126] A REM (rare earth element) is an element contributing to inclusion control, particularly fine dispersion of inclusions, and has the action of increasing toughness, so may be contained as necessary. Accordingly, the REM content is 0% or more, preferably 0.001% or more, more preferably 0.005% or more, even more preferably 0.010% or more. On the other hand, if contained excessively, degradation of the surface properties will sometimes appear, so the REM content is 0.100% or less, preferably 0.050% or less, more preferably 0.030% or less. Note that REM is an acronym for rare earth metals and indicates elements belonging to the lanthanide series. A REM is normally added as mischmetal.
[0127] In the steel sheet according to the present invention, the balance excluding the above chemical composition is comprised of Fe and impurities. Here, impurities mean constituents which enter from the ore, scraps, and other raw materials and various factors in the manufacturing process when industrially producing steel sheet and are allowable in a range not having a detrimental effect on the properties of the steel sheet according to the present invention.
[0128] In the present invention, the chemical composition of the steel sheet may be analyzed using an elemental analysis technique known to persons skilled in the art. For example, it is performed by inductively coupled plasma-mass spectroscopy (ICP-MS). However, C and S may be measured by combustion-infrared absorption, and N may be measured using inert gas fusion thermal conductivity. These analyses may be performed on samples taken from the steel sheet by a method based on JIS G0417: 1999.
[0129] [Surface Layer]
[0130] In the present invention, the surface layer of the steel sheet means a region from the surface of the steel sheet (in the case of a plated steel sheet, the interface between the steel sheet and plating layer) to a predetermined depth in the thickness direction. The predetermined depth is typically 50 ?m or less.
[0131] As illustrated in
[0132] Furthermore, while not illustrated in
[0133] [Fine Granular Oxides]
[0134] In the present invention, granular oxides mean oxides dispersed as grains inside the crystal grains of the steel or on the crystal grain boundaries. Furthermore, granular means being present away from each other mutually in the steel matrix, having, for example, a 1.0 to 5.0 aspect ratio (maximum linear length (major diameter) traversing the granular oxide/maximum linear length (minor diameter) traversing the oxide perpendicular to the major diameter). Dispersed as grains means that the grains of oxides are not positioned according to a specific rule (for example, linearly) but are positioned randomly. Since granular oxides are in fact typically present three-dimensionally in spherical shapes or substantially spherical shapes in the surface layer of the steel sheet, the granular oxides are typically observed to have circular shapes or substantially circular shapes when a cross-section of the surface layer of the steel sheet is observed. In
[0135] (Grain Size)
[0136] In the present invention, the grain size of the fine granular oxides is 20 nm or more and 100 nm or less. By controlling the grain size in this way, it is possible to obtain fine granular oxides dispersed at the surface layer of the steel sheet, the fine granular oxides function well as trap sites for hydrogen suppressing penetration of hydrogen in a corrosive environment, and, further, the oxides function well as trap sites for Zn able to penetrate a plated steel sheet obtained by forming a plating layer on steel sheet at the time of hot stamping or welding. On the other hand, if the grain size becomes more than 100 nm, the number of the granular oxides will sometimes fall and the desired number density is liable to be unable to be obtained. The grain size of the granular oxides has a lower limit of 20 nm or more. The finer the granular oxides, the higher the specific surface area and the more improved the response as trap sites, but the amount of hydrogen and/or Zn able to be trapped by one grain falls, hydrogen and/or Zn cannot be sufficiently trapped, and the oxides are liable to not sufficiently function as trap sites for hydrogen and/or trap sites for Zn.
[0137] (Number Density)
[0138] In the present invention, the number density of fine granular oxides is 4.0/?m.sup.2 or more. By controlling the number density to such a range, it is possible to make a large amount of fine granular oxides disperse at the surface layer of the steel sheet, the fine granular oxides function well as trap sites for hydrogen suppressing the penetration of hydrogen in a corrosive environment, and further the oxides function well as trap sites for Zn able to penetrate a plated steel sheet obtained by forming a plating layer on steel sheet at the time of hot stamping or welding. On the other hand, if the number density is less than 4.0/25 ?m.sup.2, the number density as trap sites for hydrogen and/or trap sites for Zn is not sufficient, the granular oxides do not sufficiently function as trap sites for hydrogen and/or trap sites for Zn, and good hydrogen embrittlement resistance and/or LME resistance is liable to be unable to be obtained. The number density of granular oxides is preferably 6.0/?m.sup.2 or more, more preferably 8.0/?m.sup.2 or more, further preferably 10.0/?m.sup.2 or more. The larger the amount of granular oxides, the better from the viewpoint of their functioning as trap sites for hydrogen and/or trap sites for Zn, but the granular oxides sometimes become starting points of LME cracking. If more than 30/?m.sup.2, the LME resistance is liable to fall, so the number density of granular oxides may be 30/?m.sup.2 or less, 25/?m.sup.2 or less, or 20/?m.sup.2 or less.
[0139] The grain size and number density of the granular oxides are measured by a scan electron microscope (SEM). The specific measurement is as follows: A cross-section of the surface layer of the steel sheet is examined by a SEM and a SEM image including the fine granular oxides is obtained. From the SEM image, as examined regions, a total of 10 regions of 1.0 ?m (depth direction)?1.0 ?m (width direction) are selected. The examined position of each region is made 1.0 ?m in the region from the steel sheet surface to 1.5 ?m for the depth direction (direction vertical to surface of steel sheet) and is made 1.0 ?m at any position of the SEM image for the width direction (direction parallel to surface of steel sheet). Next, SEM images of the regions selected in the above way are extracted and digitalized to divide them into oxide parts and steel parts. From the digitalized images, the area of each granular oxide part is calculated. The diameter of the circle having an area equal to that area, that is, the circle equivalent diameter, is found as the grain size of each granular oxide (nm). Oxides with a grain size of 20 nm or more and 100 nm or less in range are defined as fine granular oxides. Further, the numbers of fine granular oxides in the digitalized images are counted. The average value of the numbers of fine granular oxides of the total of the 10 regions found in this way is defined as the number density of fine granular oxides (/?m.sup.2). Note that, if only parts of the granular oxides are observed in the examined regions, that is, if not all of the contours of the granular oxides are inside the examined regions, they are not counted in the numbers.
[0140] (Depth of Internal Oxidation Layer)
[0141] In the steel sheet according to the present invention, the internal oxidation layer is a layer formed at the inside of the steel sheet containing fine granular oxides 12. Therefore, the internal oxidation layer is comprised of, from the surface of the steel sheet, a succession of regions in which the fine granular oxides 12 are present up to the furthest positions. Accordingly, the depth of the internal oxidation layer means, as shown in
[0142] The depth R, as shown in
[0143] [Chemical Composition of Oxides]
[0144] In the present invention, the granular oxides (below, also referred to simply as oxides) include one or more of the above-mentioned elements included in the steel sheet in addition to oxygen and typically have chemical compositions including Si, 0, and Fe and in some cases further including Mn and Al. The oxides may also contain elements able to be included in the above-mentioned steel sheet (for example, Cr etc.) in addition to these elements.
[0145] [Surface Depleted Layer]
[0146] In the present invention, the fine granular oxides are formed by oxidation of relatively easily oxidizable constituents in the steel sheet (for example, Si, Mn, and Al), so the composition of the steel around the granular oxides (in other words, the metallographic structure) is depleted in these easily oxidizable constituent elements compared with the base material of the original steel sheet. This region where the elements of the steel composition are depleted compared with the original steel sheet base material will be called a depleted region. A lamellar shaped depleted region is also called a depleted layer while one present at the surface layer of the steel sheet will also be referred to as a surface depleted layer. In the depleted region, among the readily oxidizable elements, Si oxidizes relatively easily and Al oxidizes with difficulty relatively speaking, so Si may be made present at a low concentration and Al at a high concentration. If there is a depleted region where the composition of the steel is low in Si and high in Al present in the desired range, this contributes to improvement of the LME resistance as well. As the reason for this, while not desiring to be bound by any specific theory, it is believed that by Al being present in the composition of the steel around the granular oxides in addition to the granular oxides functioning as Zn trap sites, that Al functions as trap sites for Zn trying to penetrate the steel during working at a high temperature and, further, that the higher the concentration of Si in the steel composition, the easier it is for LME cracking to occur, so LME can be suppressed by making Si as low a concentration as possible. Due to this, at the time of hot stamping or welding, Zn trying to penetrate the steel is trapped by the Al in the composition of the steel, penetration of Zn to the crystal grain boundaries is suitably suppressed, and, further, the Si which easily causes LME is low in concentration, so LME becomes difficult to occur and the LME resistance can be improved.
[0147] In the present invention, in the low Si and high Al surface depleted layer, the composition of the steel not containing fine granular oxides (in other words, the metallographic structure) at a depth of ? of the average depth of the internal oxidation layer satisfies, by mass %, and Al?0.05%. If Si is more than 0.6%, LME cracking easily occurs. Therefore, Si?0.6%. The lower limit of Si is not particularly prescribed, but may be 0% or more. Further, Al functions as trap sites for Zn trying to penetrate the steel during high temperature working. If Al is less than 0.05%, it is liable to be unable to sufficiently function as trap sites for Zn. Therefore, Al?0.05%. The greater the Al, the higher the function as trap sites and the more preferable, but if the Al concentration is too high, the effect becomes saturated, so the upper limit of the Al may be made 1.2% or less or 1.0% or less. Further, the concentrations of Si and Al are the concentrations of elements in the steel composition not including the fine granular oxides of the internal oxidation layer and are the concentrations of elements measured at a depth of ? of the average depth R of the internal oxidation layer. The base point of the average depth of the internal oxidation layer is the surface of the steel sheet (in case of plated steel sheet, the interface of the steel sheet and plating layer), but if these have roughnesses, the average line of the surfaces or interfaces at the locations for finding the average depth of the internal oxidation layer is made the base point. The concentrations of elements here are measured by EDS (energy dispersed spectroscopy).
[0148] The surface depleted layer can double as a region in which the fine granular oxides are dispersed and is present at the surface layer of the steel sheet. That is, it is formed at the inside of the base steel. Therefore, if forming a plating layer on the surface of the steel sheet, the steel sheet according to the present invention formed with the depleted region at the inside of the base steel, more particularly the surface depleted layer, can realize more sufficient interdiffusion of plating constituents and steel constituents and higher plateability compared with steel sheet having an external oxidation layer.
[0149] <Plated Steel Sheet>
[0150] The plated steel sheet according to the present invention has a plating layer containing Zn on the above-mentioned steel sheet according to the present invention. This plating layer may be formed on one side of the steel sheet or may be formed on both sides. As the plating layer containing Zn, for example, a hot dip galvanized layer, hot dip galvannealed layer, electrogalvanized layer, electrogalvannealed layer, etc. may be mentioned. More specifically, as the plating type, for example, Zn-0.2% Al (GI), Zn-(0.3 to 1.5)% Al, Zn-4.5% Al, Zn-0.09% Al-10% Fe (GA), Zn-1.5% Al-1.5% Mg, or Zn-11% Al-3% Mg-0.2% Si, Zn-11% Ni, Zn-15% Mg, etc. can be used.
[0151] [Chemical Composition of Plating Layer]
[0152] The chemical composition included in a plating layer containing Zn in the present invention will be explained next. The % regarding content of the elements, unless otherwise stated, will mean mass %. In the numerical ranges in the chemical composition of the plating layer, a numerical range expressed using to, unless otherwise indicated, will mean a range having the numerical values before and after the to as the lower limit value and the upper limit value.
[0153] (Al: 0 to 60.0%)
[0154] Al is an element which is included together with Zn or is alloyed with it and improves the corrosion resistance of the plating layer, so may be included in accordance with need. Therefore, the Al content may be 0%. To form a plating layer containing Zn and Al, preferably the Al content is 0.01% or more. For example, it may be 0.1% or more, 0.3% or more, 0.5% or more, 1.0% or more, or 3.0% or more. On the other hand, if more than 60.0%, the effect of improvement of the corrosion resistance becomes saturated, so the Al content may be 60.0% or less. For example, it may be 55.0% or less, 50.0% or less, 40.0% or less, 30.0% or less, 20.0% or less, 10.0% or less, or 5.0% or less. The detailed mechanism is unclear, but if the Al in the plating layer is 0.3 to 1.5% in range, due to the effect of the Al, the speed of penetration of Zn into the steel grain boundaries is greatly reduced and the LME resistance can be improved. Therefore, from the viewpoint of improvement of the LME resistance, the Al in the plating layer is desirably 0.3 to 1.5%.
[0155] (Mg: 0 to 15.0%)
[0156] Mg is an element which is included together with Zn and Al or is alloyed with the same and improves the corrosion resistance of the plating layer, so may be included in accordance with need. Therefore, the Mg content may be 0%. To form a plating layer containing Zn, Al, and Mg, preferably the Mg content is 0.01% or more. For example, it may be 0.1% or more, 0.5% or more, 1.0% or more, or 3.0% or more. On the other hand, if more than 15.0%, the Mg will not completely dissolve in the plating bath but will float as oxides. If galvanizing by such a plating bath, oxides will deposit on the surface layer causing poor appearance or liable to cause the occurrence of non-plated parts, so the Mg content may be 15.0% or less, for example, may be 10.0% or less or 5.0% or less.
[0157] (Fe: 0 to 15.0%)
[0158] Fe can be included in the plating layer due to diffusion from the steel sheet when forming a plating layer containing Zn on the steel sheet, then heat treating the plated steel sheet. Therefore, Fe is not included in the plating layer in a state not treated by heat, so the Fe content may also be 0%. Further, the Fe content may be 1.0% or more, 2.0% or more, 3.0% or more, 4.0% or more, or 5.0% or more. On the other hand, the Fe content need only be 15.0% or less, for example, may be 12.0% or less, 10.0% or less, 8.0% or less, or 6.0% or less.
[0159] (Si: 0 to 3.0%)
[0160] Si is an element which further improves the corrosion resistance if included in a plating layer containing Zn, in particular a ZnAlMg plating layer, so may be included in accordance with need. Therefore, the Si content may be 0%. From the viewpoint of improvement of the corrosion resistance, the Si content may for example be 0.005% or more, 0.01% or more, 0.05% or more, 0.1% or more, or 0.5% or more. Further, the Si content may be 3.0% or less, 2.5% or less, 2.0% or less, 1.5% or less, or 1.2% or less.
[0161] The basic chemical composition of the plating layer is as explained above. Furthermore the plating layer may contain, optionally, one or more of Sb: 0 to 0.50%, Pb: 0 to 0.50%, Cu: 0 to 1.00%, Sn: 0 to 1.00%, Ti: 0 to 1.00%, Sr: 0 to 0.50%, Cr: 0 to 1.00%, Ni: 0 to 1.00%, and Mn: 0 to 1.00%. While not particularly limited, from the viewpoint of sufficiently manifesting the actions and functions of the basic constituents forming the plating layer, the total content of these optional elements is preferably made 5.00% or less, more preferably 2.00% or less.
[0162] At the plating layer, the balance besides the above constituents is comprised of Zn and impurities. The impurities at the plating layer mean constituents such as the raw material entering due to various factors in the production process when producing the plating layer and not constituents intentionally added to the plating layer. In the plating layer, as impurities, elements besides the basic constituents and optional constituents explained above may be included in trace amounts in a range not impeding the effect of the present invention.
[0163] The chemical composition of the plating layer can be determined by dissolving the plating layer in an acid solution containing an inhibitor for inhibiting corrosion of the steel sheet and measuring the obtained solution by ICP (inductively coupled plasma) emission spectroscopy.
[0164] The thickness of the plating layer may for example be 3 to 50 ?m. Further, the amount of deposition of the plating layer is not particularly limited but for example may be 10 to 170 g/m.sup.2 per side. In the present invention, the amount of deposition of the plating layer is determined by dissolving the plating layer in an acid solution containing an inhibitor for inhibiting corrosion of the base iron and finding the change in weight before and after pickling and peeling off the plating layer.
[0165] [Tensile Strength]
[0166] The steel sheet and plated steel sheet according to the present invention preferably have a high strength. Specifically, they preferably have 440 MPa or more tensile strength. For example, the tensile strength may be 500 MPa or more, 600 MPa or more, 700 MPa or more, or 800 MPa or more. The upper limit of the tensile strength is not particularly prescribed, but from the viewpoint of securing toughness, may for example be 2000 MPa or less. The tensile strength may be measured by taking a JIS No. 5 tensile test piece having a direction perpendicular to the rolling direction as its longitudinal direction and performing a test based on JIS Z 2241(2011).
[0167] The steel sheet and plated steel sheet according to the present invention are high in strength and have a high plateability, LME resistance, and hydrogen embrittlement resistance, so can be suitably used in a broad range of fields such as automobiles, household electric appliances, and building materials, but are particularly preferably used in the automotive field. Steel sheet used for automobiles usually is plated (typically galvanization etc.), so if using the steel sheet according to the present invention as steel sheet for automobiles, the effect of the present invention of having a high plateability is optimally exhibited. Further, steel sheet and plated steel sheet used for automobiles are often hot stamped. In that case, hydrogen embrittlement cracking and LME cracking can become remarkable problems. Therefore, when using the steel sheet and plated steel sheet according to the present invention as steel sheet for automobiles, the effect of the present invention of having a high hydrogen embrittlement resistance and LME resistance is optimally exhibited.
[0168] <Method of Production of Steel Sheet>
[0169] Below, a preferable method of production of the steel sheet according to the present invention will be explained. The following explanation is intended to illustrate the characteristic method for producing the steel sheet according to the present invention and is not intended to limit the steel sheet to one produced by the method of production explained below.
[0170] The steel sheet according to the present invention can be obtained for example by performing a casting step of casting molten steel adjusted in chemical composition to form a steel slab, a hot rolling step of hot rolling the steel slab to obtain hot rolled steel sheet, a coiling step of coiling the hot rolled steel sheet, a cold rolling step of cold rolling the coiled hot rolled steel sheet to obtain cold rolled steel sheet, a pretreatment step of brush grinding the cold rolled steel sheet, and an annealing step of annealing the pretreated cold rolled steel sheet. Alternatively, the hot rolled steel sheet may not be coiled after the hot rolling step, but pickled and then cold rolled as it is.
[0171] [Casting Step]
[0172] The conditions of the casting step are not particularly prescribed. For example, after smelting by a blast furnace or electric furnace etc., various secondary refining operations may be performed, then the molten metal cast by the usual continuous casting, ingot casting, or other method.
[0173] [Hot Rolling Step]
[0174] The thus cast steel slab can be hot rolled to obtain hot rolled steel sheet. The hot rolling step is performed by directly hot rolling the cast steel slab or by reheating after cooling once. If reheating, the heating temperature of the steel slab may for example be 1100? C. to 1250? C. In the hot rolling step, usually rough rolling and finish rolling are performed. The temperatures and rolling reductions of the rolling operations may be suitably changed in accordance with the desired metallographic structure and sheet thickness. For example, the end temperature of the finish rolling may be made 900 to 1050? C. and the rolling reduction of the finish rolling may be made 10 to 50%.
[0175] [Coiling Step]
[0176] The hot rolled steel sheet can be coiled at a predetermined temperature. The coiling temperature may be suitably changed in accordance with the desired metallographic structure etc. and may for example be 500 to 800? C. The hot rolled steel sheet may be heat treated under predetermined conditions before being coiled or after being coiled by being uncoiled. Alternatively, the sheet can be pickled after the hot rolling step without performing a coiling step and then subjected to a later explained cold rolling step.
[0177] [Cold Rolling Step]
[0178] After pickling the hot rolled steel sheet, the hot rolled steel sheet can be cold rolled to obtain cold rolled steel sheet. The rolling reduction of the cold rolling may be suitably changed in accordance with the desired metallographic structure and sheet thickness and may for example be 20 to 80%. After the cold rolling step, for example, the sheet may be air cooled to cool it down to room temperature.
[0179] [Pretreatment Step]
[0180] To obtain large amounts of fine granular oxides at the surface layer of the finally obtained steel sheet and furthermore to obtain a surface depleted layer, it is effective to perform a predetermined pretreatment step before annealing the cold rolled steel sheet. This pretreatment step introduces a large amount of dislocations to the surface of the cold rolled steel sheet. Oxygen etc. diffuses faster at the grain boundaries than inside the grains, so by introducing a large amount of dislocations at the surface of the cold rolled steel sheet, it is possible to form a large number of paths like the case of grain boundaries. For this reason, at the time of annealing, the oxygen rapidly diffuses (penetrates) to the inside of the steel along these dislocations. Further, the speed of diffusion of Si and Al is also improved, so as a result the oxygen bonds with the Si and/or Al inside of the steel and thereby formation of fine granular oxides can be promoted. Further, along with such promotion of formation of internal oxides, a drop in the surrounding concentrations of Si and Al is also promoted, so formation of a surface depleted layer having the desired composition can be promoted. Accordingly, if performing such a pretreatment step, in the later explained annealing step, the desired fine granular oxides and surface depleted layer are easily formed. This pretreatment step includes grinding the cold rolled steel sheet sample by a heavy grinding brush (brush grinding). As the heavy grinding brush, D-100 made by Hotani may be used. At the time of grinding, the surface of the steel sheet may be coated with an NaOH 1.0 to 5.0% aqueous solution. The brush pressure may be 0.5 to 10.0 mm, more preferably 5.0 to 10.0 mm, and the rotational speed may be 100 to 1000 rpm. By performing brush grinding controlled to such coating solution conditions, brush pressure, and rotational speed, in the later explained annealing step, fine granular oxides and a surface depleted layer can be efficiently formed at the surface layer of the steel sheet.
[0181] [Annealing Step]
[0182] The cold rolled steel sheet subjected to the above pretreatment step is annealed. The annealing is preferably performed in a state in which for example 0.1 to 30.0 MPa of tension is applied. If applying tension at the time of annealing, strain can be more effectively introduced into the steel sheet. Due to the strain, dislocations of the metallographic structure of the steel sheet are promoted and it is made easier for oxygen to penetrate the inside of the steel along those dislocations whereby oxides become easier to form inside the steel sheet. As a result, this is advantageous for increase of the number density of the granular oxides, increase of the fineness of the grain size, and formation of the surface depleted layer.
[0183] For suitably forming internal oxides, the holding temperature at the annealing step may be made 700? C. to 900? C. or less, preferably 720 to 870? C. By making it such a range, it is possible to suppress the formation of an external oxidation layer and form oxides inside the steel sheet. If the holding temperature of the annealing step is less than 700? C., the desired internal oxides and/or surface depleted layer are liable to not be sufficiently formed at the time of annealing. If the holding temperature is more than 900? C., an external oxidation layer is formed and internal oxides and/or a surface depleted layer is liable to become difficult to be sufficiently formed at the time of annealing. The temperature elevation rate up to the holding temperature is not particularly limited, but may be 1 to 10? C./s. Further, the temperature elevation may be performed in two stages by a first temperature elevation rate of 1 to 10? C./s and a second temperature elevation rate of 1 to 10? C./s different from the first temperature elevation rate.
[0184] The holding time at the holding temperature of the annealing step may be 10 to 300 seconds, preferably 30 to 250 seconds. By making it such a range, it is possible to suppress the formation of an external oxidation layer and form oxides inside the steel sheet. If the holding time is less than 10 seconds, the desired internal oxides are liable to be unable to be sufficiently formed. If the holding time is more than 300 seconds, an external oxidation layer is liable to be formed at the time of annealing.
[0185] From the viewpoint of causing the formation of fine granular oxides in a large amount and a surface depleted layer during the temperature elevation in the annealing step and, wetting is performed. The atmosphere of that may be made a dew point of ?20 to 10? C., preferably ?10 to 5? C., and 1 to 15 vol % H.sub.2. If the dew point is too low, an external oxidation layer is formed on the surface of the steel sheet and an internal oxidation layer and/or surface depleted layer is liable to not be sufficiently formed and sometimes the plateability, hydrogen embrittlement resistance, and LME resistance will become insufficient. On the other hand, if the dew point is too high, the granular oxides are liable to become coarser and the granular oxides will sometimes not satisfy the desired number density and/or the desired surface depleted layer will sometimes not be obtained. The dew point of the atmosphere during holding (isothermal) in the annealing step may be less than ?20? C. from the viewpoint of maintaining the internal oxidation layer formed during the temperature elevation. If the dew point is ?20? C. or more, the granular oxides will coarsen and sometimes the number density of the desired fine granular oxides will be liable to fall. The hydrogen embrittlement resistance and/or LME resistance will sometimes become insufficient.
[0186] The temperature when starting wetting during the temperature elevation may be less than 600? C. If starting wetting at more than 600? C., the internal oxidation layer and/or surface depleted layer are liable to not be sufficiently formed before reaching the holding temperature.
[0187] Furthermore, it is effective to remove the internal oxidation layer of the steel sheet when performing the annealing step, in particular before the brush grinding. During the above-mentioned rolling step, in particular the hot rolling step, sometimes an internal oxidation layer is formed at the surface layer of the steel sheet. Such an internal oxidation layer formed in a rolling step is liable to inhibit the formation of fine granular oxides and/or a surface depleted layer at the annealing step, so that internal oxidation layer is preferably removed before annealing by pickling etc. More specifically, the depth of the internal oxidation layer of the cold rolled steel sheet when performing an annealing step may be made 0.5 ?m or less, preferably 0.3 ?m or less, more preferably 0.2 ?m or less, still more preferably 0.1 ?m or less.
[0188] By performing the steps explained above, it is possible to obtain steel sheet comprised of steel sheet with a surface layer containing fine granular oxides in a sufficiently large amount and formed with a surface depleted layer.
[0189] <Method of Production of Plated Steel Sheet>
[0190] Below, a preferable method of production of the plated steel sheet according to the present invention will be explained. The following explanation is intended to illustrate the characteristic method for producing the plated steel sheet according to the present invention and is not intended to limit the plated steel sheet to one produced by the method of production explained below.
[0191] The plated steel sheet according to the present invention can be obtained by performing a plating step for forming a plating layer containing Zn on the steel sheet produced in the above way.
[0192] [Plating Step]
[0193] The plating step may be performed according to a method known to persons skilled in the art. The plating step may for example be performed by hot dip coating and may be performed by electroplating. Preferably, the plating step is performed by hot dip coating. The conditions of the plating step may be suitably set considering the chemical composition, thickness, amount of deposition, etc. of the desired plating layer. After the plating, alloying may be performed. Typically, the conditions of the plating step may be set so as to form a plating layer containing Al: 0 to 60.0%, Mg: 0 to 15.0%, Fe: 0 to 15%, Ni: 0 to 20%, and Si: 0 to 3% and having a balance of Zn and impurities. More specifically, the conditions of the plating step may for example be suitably set so as to form Zn-0.2% Al (GI), Zn-(0.3 to 1.5)% Al, Zn-4.5% Al, Zn-0.09% Al-10% Fe (GA), Zn-1.5% Al-1.5% Mg, or Zn-11% Al-3% Mg-0.2% Si, Zn-11% Ni, Zn-15% Mg. From the viewpoint of improvement of the LME resistance, the Al in the plating layer is preferably 0.3 to 1.5%.
EXAMPLES
[0194] Below, examples will be used to explain the present invention in more detail, but the present invention is not limited to these examples in any way.
Example 1: Regarding Examples and Comparative Examples of Steel Sheet
[0195] (Preparation of Steel Sheet Samples)
[0196] Molten steels adjusted in chemical compositions were cast to form steel slabs. The steel slabs were hot rolled, pickled, then cold rolled to obtain cold rolled steel sheets. Next, the sheets were air-cooled down to room temperature. The cold rolled steel sheets were pickled, then the internal oxidation layers formed by rolling were removed down to the internal oxidation layer depth (lam) before annealing described in Table 1. Next, samples were taken from the cold rolled steel sheets by the method based on JIS G0417: 1999 and the chemical compositions of the steel sheets were analyzed by ICP-MS etc. The measured chemical compositions of the steel sheets are shown in Table 1. The thicknesses of the steel sheets used were 1.6 mm in all cases.
[0197] Next, some of the cold rolled steel sheets were coated with an NaOH 2.0% aqueous solution, pretreated by brush grinding using a heavy grinding brush (D-100 made by Hotani) at a brush pressure of 2.0 mm and speed of 600 rpm, then were annealed by the dew point and holding temperature shown in Table 1 to prepare the different steel sheet samples. In all of the steel sheet samples, the temperature elevation rate at the time of annealing was made 6.0? C./s up to 500? C. and 2.0? C./s from 500? C. to the holding temperature. In the annealing, some of the cold rolled steel sheets were annealed in a state with 30.0 MPa of tensions applied while the other cold rolled steel sheets were annealed without tension applied. The presence of any pretreatment and the conditions of the annealing (presence of any tension, wetting zone, dew point (? C.), hydrogen concentration (vol %), wetting start temperature (? C.) in the temperature elevation step, and temperature elevation end temperature (holding temperature (? C.)) are shown in Table 1. The holding time was made 10 to 300 seconds. Note that in each steel sheet sample, a JIS No. 5 tensile test piece having a direction perpendicular to the rolling direction as its longitudinal direction was taken and subjected to a tensile test based on JIS Z 2241(2011). As a result, for No. 1, the tensile strength was less than 440 MPa while for all the others, it was 440 MPa or more.
[0198] (Analysis of Surface Layer of Steel Sheet Samples: Number Density of Fine Grained Oxides)
[0199] Each steel sheet sample prepared in the above way was cut to 25 mm?15 mm. The cut sample was buried in a resin and polished to a mirror surface. At the cross-section of each steel sheet sample, 1.0 ?m?1.0 ?m regions were examined by a SEM at 10 locations. The examined positions were made the 1.0 ?m from 0.2 to 1.2 ?m from the steel sheet surface for the depth direction (direction vertical to surface of steel sheet) and 1.0 ?m of any position of the SEM image for the width direction (direction parallel to surface of steel sheet). The SEM images of the regions of the steel sheet samples obtained were digitalized, the areas of the granular oxide parts were calculated from the digitalized images, the grain size of each granular oxide (nm) was found as the diameter of the circle having an area equal to that area, that is, the circle equivalent diameter, and oxides with a grain size of 20 nm to 100 nm in range were defined as fine granular oxides. Further, the numbers of fine granular oxides in the SEM images were counted. The average value of the numbers of fine granular oxides in the digitalized images of the 10 locations found was defined as the number density of fine granular oxides. The number density of fine granular oxides for each steel sheet sample (/?m.sup.2) is shown in Table 1.
[0200] (Analysis of Surface Layer of Steel Sheet Samples: Surface Depleted Layer) Each steel sheet sample was evaluated for a surface depleted layer by analyzing the constituents of the steel structure not containing oxides at a depth of ? of the average depth of the internal oxidation layer calculated from the cross-sectional SEM image using TEM-EDS. Satisfying Si?0.6% and Al?0.05% is indicated as Yes, while not satisfying Si?0.6% and Al?0.05% is indicated as No.
[0201] (Evaluation of Plateability)
[0202] Each steel sheet sample was plated and measured for area ratio of non-plated parts on the surface of that plated steel sheet so as to evaluate the plateability. Specifically, hot dip galvanization-0.2% Al plating (bath temperature 450 to 470? C.) was performed. A 1 mmxl mm region of the surface of each plated steel sheet sample formed with the plating layer was examined under an optical microscope, parts at which the plating layer was formed (plated parts) and parts where the plating layer was not formed (non-plated parts) were judged from the examined image, the area ratio of the non-plated parts (area of non-plated parts/area of observed image) was calculated, and the plateability was evaluated by the following criteria. The results are shown in Table 1. [0203] Evaluation A: area ratio of plated parts of 95% or more (area ratio of non-plated parts of 5.0% or less) [0204] Evaluation B: area ratio of plated parts of less than 95% and 90% or more (area ratio of non-plated parts of more than 5.0% and 10% or less)
[0205] (Analysis of Composition of Plating Layer)
[0206] The composition of each plating layer was found by dipping a sample cut to 30 mm?30 mm in a 10% aqueous hydrochloric acid solution containing an inhibitor (Ibit made by Asahi Chemical), peeling off the plating layer by pickling, then analyzing the plating constituents dissolved in the aqueous solution by ICP.
[0207] (Evaluation of LME Resistance)
[0208] Each 100?100 mm plated steel sheet sample was spot welded and was cut to 50 mm?100 mm size to prepare two sheets. The two sheets of Zn-based plated steel sheet samples were spot welded using a dome radius type tip size 8 mm welding electrode at a weld angle of 7?, weld force of 4.0 kN, weld time 0.5 second, and weld current 7 kA to obtain a welded member.
[0209] The welded part was polished at its cross-section, then examined under an optical microscope and measured for length of LME cracking occurring at the cross-section of the welded part and evaluated as follows. The results are shown in Table 1. The plating type in Table 1 was made GA in each case. The plating type of Table 2 was as described in Table 2: [0210] Evaluation AAA: no LME cracking [0211] Evaluation AA: LME crack length more than 0 ?m to 100 ?m [0212] Evaluation A: LME crack length more than 100 ?m to 200 ?m [0213] Evaluation B: LME crack length more than 200 ?m
[0214] (Evaluation of Hydrogen Embrittlement Resistance)
[0215] Each 50 mm?100 mm plated steel sheet sample was treated to form zinc phosphate using a zinc phosphate-based conversion coating (Surfdine SD5350 series: made by Nippon Paint Industrial Coating), then was formed with an electrodeposition coating (PN110 Powernix Grey: made by Nippon Paint Industrial Coating) to 20 ?m and was baked at a 150? C. baking temperature for 20 minutes to form a coating on the plated steel sheet sample. Next, the amount of diffusible hydrogen after electrodeposition coating was measured by the thermal desorption method for evaluation. Specifically, in measurement of the amount of diffusible hydrogen, a test piece was heated to 400? C. in a heating furnace provided with a gas chromatography device. The sum of the amount of hydrogen discharged until falling to 250? C. was measured. Based on the measured amount of diffusible hydrogen, the hydrogen embrittlement resistance (amount of hydrogen built up in sample) was evaluated by the following criteria The results are shown in Table 1. [0216] Evaluation AA: amount of diffusible hydrogen of 0.2 ppm or less [0217] Evaluation A: amount of diffusible hydrogen of more than 0.2 ppm to 0.4 ppm [0218] Evaluation B: amount of diffusible hydrogen of more than 0.4 ppm
TABLE-US-00001 TABLE 1 Depth of internal oxidation layer Tensile before strength Chemical composition (mass %) annealing Brushing No. Class [MPa] Fe C Si Mn Al P S N B Others Pickling (?m) grinding 1 Comp. ex. 420 Bal. 0.03 1.8 2.0 0.8 0.0006 0.0010 0.0022 0.00002 Yes 0.3 Yes 2 Ex. 500 Bal. 0.05 1.0 2.0 0.4 0.0010 0.0020 0.0031 0.00002 Yes 0.2 Yes 3 Ex. 550 Bal. 0.10 2.0 2.0 0.5 0.0120 0.0014 0.0025 0.00002 Yes 0.1 Yes 4 Ex. 490 Bal. 0.10 0.6 2.0 0.5 0.0080 0.0010 0.0030 0.00003 Hf: 0.002 Yes 0.2 Yes 5 Ex. 530 Bal. 0.10 1.5 2.2 0.5 0.0010 0.0020 0.0021 0.00002 B: 0.001 Yes 0.2 Yes 6 Ex. 680 Bal. 0.20 0.5 2.0 0.8 0.0030 0.0022 0.0012 0.00001 Mg: 0.004 Yes 0.1 Yes 7 Ex. 760 Bal. 0.20 1.0 2.0 0.8 0.0020 0.0013 0.0034 0.00002 Zr: 0.055 Yes 0.2 Yes 8 Ex. 810 Bal. 0.20 1.0 2.0 0.8 0.0012 0.0021 0.0024 0.00002 B: 0.001 Yes 0.1 Yes 9 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0024 0.0041 0.0022 0.00002 Yes 0.1 Yes 10 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0010 0.0025 0.0027 0.00002 Yes 0.1 Yes 11 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0098 0.0020 0.0011 0.00002 Yes 0.3 Yes 12 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0077 0.0026 0.0018 0.00001 Yes 0.1 Yes 13 Comp. ex. 850 Bal. 0.20 4.5 2.0 1.2 0.0010 0.0024 0.0020 0.00000 Yes 0.1 Yes 14 Comp. ex. 440 Bal. 0.20 0 2.0 1.2 0.0550 0.0022 0.0022 0.00001 Yes 0.1 Yes 15 Comp. ex. 790 Bal. 0.20 1.7 6.1 1.2 0.0015 0.0014 0.0032 0.00002 Yes 0.1 Yes 16 Comp. ex. 520 Bal. 0.20 1.7 0 0.8 0.0017 0.0010 0.0026 0.00002 Yes 0.1 Yes 17 Comp. ex. 880 Bal. 0.20 1.7 2.0 1.9 0.0090 0.0021 0.0030 0.00003 Yes 0.3 Yes 18 Comp. ex. 760 Bal. 0.20 1.8 2.0 0.2 0.0046 0.0028 0.0044 0.00002 Yes 0.3 Yes 19 Comp. ex. 790 Bal. 0.20 1.7 2.0 0.7 0.0071 0.0031 0.0052 0.00002 Yes 0.1 Yes 20 Comp. ex. 910 Bal. 0.40 1.6 2.0 0.7 0.0027 0.0034 0.0021 0.00002 Yes 2.5 Yes 21 Ex. 1050 Bal. 0.20 2.4 2.5 0.7 0.0015 0.0040 0.0023 0.00002 Cr: 0.8 Yes 0.2 Yes 22 Ex. 1060 Bal. 0.20 3.0 2.3 0.7 0.0025 0.0028 0.0013 0.00002 Cu: 0.009 Yes 0.2 Yes 23 Ex. 1120 Bal. 0.20 1.5 2.3 0.7 0.0060 0.0026 0.0014 0.00001 Ti: 0.03 Yes 0.1 Yes 24 Ex. 840 Bal. 0.20 0.7 2.2 0.7 0.0065 0.0021 0.0016 0.00002 Ni: 0.5 Yes 0.1 Yes 25 Ex. 940 Bal. 0.25 0.7 2.2 0.7 0.0012 0.0034 0.0021 0.00002 Yes 0.1 Yes 26 Ex. 970 Bal. 0.25 1.0 2.2 1.2 0.0040 0.0020 0.0018 0.00000 Nb: 0.017 Yes 0.1 Yes 27 Ex. 1140 Bal. 0.30 1.0 5.0 1.2 0.0099 0.0025 0.0026 0.00002 V: 0.046 Yes 0.1 Yes 28 Ex. 680 Bal. 0.30 0.8 0.3 1.2 0.0110 0.0023 0.0021 0.00000 Yes 0.1 Yes 29 Ex. 780 Bal. 0.35 0.5 3.0 0.7 0.0092 0.0024 0.0029 0.00002 Mo: 0.09 Yes 0.2 Yes 30 Ex. 830 Bal. 0.35 1.0 2.2 0.7 0.0091 0.0018 0.0020 0.00001 REM: 0.001 Yes 0.1 Yes 31 Ex. 930 Bal. 0.40 1.0 2.2 0.7 0.0045 0.0017 0.0017 0.00002 W: 0.005 Yes 0.4 Yes 32 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0035 0.0018 0.0021 0.00002 Yes 0.1 Yes 33 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0082 0.0010 0.0016 0.00002 Ca: 0.0008 Yes 0.1 Yes 34 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0080 0.0015 0.0024 0.00001 Yes 0.1 Yes 35 Comp. ex. 960 Bal. 0.40 1.0 2.2 0.7 0.0100 0.0020 0.0026 0.00002 Yes 0.1 Yes 36 Comp. ex. 750 Bal. 0.20 1.0 2.3 0.7 0.0055 0.0022 0.0026 0.00002 Yes 0.2 No 37 Comp. ex. 750 Bal. 0.20 1.0 2.3 0.7 0.0055 0.0022 0.0026 0.00002 Yes 0.2 Yes Annealing conditions Form of internal Dew point oxidation layer (? C.) Hydrogen Wetting Temp. elev. Fine granular Temp. conc. start temp. End temp. Number density No. Tension Wetting zone elev. Holding (vol %) (? C.) (? C.) (/?m.sup.2) 1 Yes Temp. elev. 0 ?40 4 480 780 0.0 2 No Temp. elev. 0 ?45 4 500 700 4.0 3 Yes Temp. elev. 0 ?60 4 550 780 4.1 4 Yes Temp. elev. 0 ?50 4 400 780 4.3 5 Yes Temp. elev. 0 ?50 4 350 760 5.3 6 Yes Temp. elev. 0 ?45 4 450 780 4.0 7 Yes Temp. elev. 0 ?40 4 250 800 8.0 8 Yes Temp. elev. 0 ?40 4 300 780 7.5 9 Yes Temp. elev. ?40 ?40 4 400 780 0 10 Yes Temp. elev. 20 ?45 4 400 780 0.0 11 No Temp. elev. 0 ?35 4 580 980 1.1 12 No Temp. elev. 0 ?40 4 400 650 0 13 Yes Temp. elev. 0 ?45 4 300 780 1.5 14 Yes Temp. elev. 0 ?50 4 300 780 0 15 No Temp. elev. 0 ?50 4 300 780 1.0 16 Yes Temp. elev. 0 ?50 4 300 780 0 17 Yes Temp. elev. 0 ?50 4 300 780 1.5 18 Yes Temp. elev. 0 ?50 4 300 780 4.1 19 Yes Temp. elev. + 0 0 4 500 780 1.2 isothermal 20 Yes Temp. elev. 0 ?40 4 550 780 0 21 Yes Temp. elev. 0 ?60 4 300 780 6.5 22 Yes Temp. elev. 0 ?55 4 250 820 5.5 23 Yes Temp. elev. 0 ?60 4 400 780 5.0 24 Yes Temp. elev. 0 ?40 4 400 780 6.0 25 Yes Temp. elev. 0 ?40 4 300 840 6.5 26 Yes Temp. elev. 0 ?40 4 250 780 10.5 27 Yes Temp. elev. 0 ?35 4 400 860 11.0 28 Yes Temp. elev. 0 ?35 4 300 780 12.0 29 Yes Temp. elev. 0 ?55 4 200 780 6.0 30 Yes Temp. elev. 0 ?60 4 250 780 4.0 31 Yes Temp. elev. 0 ?60 4 400 820 5.0 32 Yes Temp. elev. 0 ?40 4 300 780 6.5 33 Yes Temp. elev. 0 ?45 4 350 900 4.0 34 Yes Temp. elev. 0 ?40 4 300 780 5.5 35 No Temp. elev. 0 ?40 4 400 780 2.3 36 Yes Temp. elev. 0 ?40 4 400 780 2.0 37 Yes Temp. elev. 0 ?45 4 650 750 0.0 Depleted layer Si ? Tensile 0.6% strength and before Performance Al ? plating Hydrogen LME No. 0.05% [MPa] Plating type Plateability desorption resistance 1 No 390 a B B B 2 Yes 530 a A A A 3 Yes 580 b A A A 4 Yes 590 a A A A 5 Yes 780 a A A A 6 Yes 680 a A A A 7 Yes 760 a A A AA 8 Yes 830 c: 0.3% Al A A AAA 9 No 790 b B B B 10 No 810 a B B B 11 Yes 860 a B B B 12 No 860 b B B B 13 Yes 910 b A B B 14 No 850 b B B B 15 Yes 590 a A B B 16 No 440 b B B B 17 Yes 780 a A B B 18 No 610 a A B B 19 Yes 810 a A B B 20 No 690 b B B B 21 Yes 1020 a A A A 22 Yes 1190 c: 1.2% Al A A AA 23 Yes 1120 a A A A 24 Yes 760 c: 0.9% Al A A AA 25 Yes 910 a A A A 26 Yes 860 a A AA AA 27 Yes 970 c: 0.8% Al A AA AAA 28 Yes 590 a A AA AA 29 Yes 780 a A A A 30 Yes 780 c: 1.5% Al A A AA 31 Yes 690 a A A A 32 Yes 690 b A A A 33 Yes 570 a A A A 34 Yes 460 a A A A 35 Yes 940 a A B B 36 Yes 790 a A B B 37 No 780 a B B B
Example 2: Regarding Examples and Comparative Examples of Plated Steel Sheets
[0219] (Preparation of Samples of Plated Steel Sheet)
[0220] The samples of steel sheets of Example 1 were cut to 100 mm?200 mm sizes, then were plated in various ways shown in Table 2. In Table 2, the plating type a means hot dip galvannealed steel sheet (GA), the plating type b means hot dip galvanized-0.2% Al-plated steel sheet (GI), and the plating type c means hot dip galvanized-(0.3 to 1.5)% Al-plated steel sheet (Al content described in Table 2). In the hot dip galvanization step, the cut samples were dipped in a 440? C. hot dip galvanization bath for 3 seconds. After dipping, they were pulled out at 100 mm/s. N.sub.2 wiping gas was used to control the amount of plating deposition to 50 g/m.sup.2. For the plating type a, alloying was performed after that at 500? C.
[0221] The samples of plated steel sheet obtained for Example 2 were evaluated by evaluation method similar to Example 1 for the respective evaluation items, that is, the number densities of the fine granular oxides, the surface depleted layer, the plateability, and the hydrogen embrittlement resistance. It was confirmed that results similar to Example 1 were obtained. The tensile strength changed somewhat depending on the plating treatment, but in the same way as Example 1, in No. 1, the tensile strength was less than 440 MPa, while in the others, it was 440 MPa or more. Regarding the LME resistance, the LME resistance was improved when the content of Al in the plating type c was 0.3 to 1.5 mass %. The results are shown in Table 2.
TABLE-US-00002 TABLE 2 Depth of internal oxidation layer Tensile before strength Chemical composition (mass %) annealing Brush No. Class [MPa] Fe C Si Mn Al P S N B Others Pickling (?m) grinding 1 Comp. ex. 420 Bal. 0.03 1.8 2.0 0.8 0.0006 0.0010 0.0022 0.00002 Yes 0.3 Yes 2 Ex. 500 Bal. 0.05 1.0 2.0 0.4 0.0010 0.0020 0.0031 0.00002 Yes 0.2 Yes 3 Ex. 550 Bal. 0.10 2.0 2.0 0.5 0.0120 0.0014 0.0025 0.00002 Yes 0.1 Yes 4 Ex. 490 Bal. 0.10 0.6 2.0 0.5 0.0080 0.0010 0.0030 0.00003 Hf: 0.002 Yes 0.2 Yes 5 Ex. 530 Bal. 0.10 1.5 2.2 0.5 0.0010 0.0020 0.0021 0.00002 B: 0.001 Yes 0.2 Yes 6 Ex. 680 Bal. 0.20 0.5 2.0 0.8 0.0030 0.0022 0.0012 0.00001 Mg: 0.004 Yes 0.1 Yes 7 Ex. 760 Bal. 0.20 1.0 2.0 0.8 0.0020 0.0013 0.0034 0.00002 Zr: 0.055 Yes 0.2 Yes 8 Ex. 810 Bal. 0.20 1.0 2.0 0.8 0.0012 0.0021 0.0024 0.00002 B: 0.001 Yes 0.1 Yes 9 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0024 0.0041 0.0022 0.00002 Yes 0.1 Yes 10 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0010 0.0025 0.0027 0.00002 Yes 0.1 Yes 11 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0098 0.0020 0.0011 0.00002 Yes 0.3 Yes 12 Comp. ex. 820 Bal. 0.20 1.8 2.0 0.8 0.0077 0.0026 0.0018 0.00001 Yes 0.1 Yes 13 Comp. ex. 850 Bal. 0.20 4.5 2.0 1.2 0.0010 0.0024 0.0020 0.00000 Yes 0.1 Yes 14 Comp. ex. 440 Bal. 0.20 0 2.0 1.2 0.0550 0.0022 0.0022 0.00001 Yes 0.1 Yes 15 Comp. ex. 790 Bal. 0.20 1.7 6.1 1.2 0.0015 0.0014 0.0032 0.00002 Yes 0.1 Yes 16 Comp. ex. 520 Bal. 0.20 1.7 0 0.8 0.0017 0.0010 0.0026 0.00002 Yes 0.1 Yes 17 Comp. ex. 880 Bal. 0.20 1.7 2.0 1.9 0.0090 0.0021 0.0030 0.00003 Yes 0.3 Yes 18 Comp. ex. 760 Bal. 0.20 1.8 2.0 0.2 0.0046 0.0028 0.0044 0.00002 Yes 0.3 Yes 19 Comp. ex. 790 Bal. 0.20 1.7 2.0 0.7 0.0071 0.0031 0.0052 0.00002 Yes 0.1 Yes 20 Comp. ex. 910 Bal. 0.40 1.6 2.0 0.7 0.0027 0.0034 0.0021 0.00002 Yes 2.5 Yes 21 Ex. 1050 Bal. 0.20 2.4 2.5 0.7 0.0015 0.0040 0.0023 0.00002 Cr: 0.8 Yes 0.2 Yes 22 Ex. 1060 Bal. 0.20 3.0 2.3 0.7 0.0025 0.0028 0.0013 0.00002 Cu: 0.009 Yes 0.2 Yes 23 Ex. 1120 Bal. 0.20 1.5 2.3 0.7 0.0060 0.0026 0.0014 0.00001 Ti: 0.03 Yes 0.1 Yes 24 Ex. 840 Bal. 0.20 0.7 2.2 0.7 0.0065 0.0021 0.0016 0.00002 Ni: 0.5 Yes 0.1 Yes 25 Ex. 940 Bal. 0.25 0.7 2.2 0.7 0.0012 0.0034 0.0021 0.00002 Yes 0.1 Yes 26 Ex. 970 Bal. 0.25 1.0 2.2 1.2 0.0040 0.0020 0.0018 0.00000 Nb: 0.017 Yes 0.1 Yes 27 Ex. 1140 Bal. 0.30 1.0 5.0 1.2 0.0099 0.0025 0.0026 0.00002 V: 0.046 Yes 0.1 Yes 28 Ex. 680 Bal. 0.30 0.8 0.3 1.2 0.0110 0.0023 0.0021 0.00000 Yes 0.1 Yes 29 Ex. 780 Bal. 0.35 0.5 3.0 0.7 0.0092 0.0024 0.0029 0.00002 Mo: 0.09 Yes 0.2 Yes 30 Ex. 830 Bal. 0.35 1.0 2.2 0.7 0.0091 0.0018 0.0020 0.00001 REM: 0.001 Yes 0.1 Yes 31 Ex. 930 Bal. 0.40 1.0 2.2 0.7 0.0045 0.0017 0.0017 0.00002 W: 0.005 Yes 0.4 Yes 32 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0035 0.0018 0.0021 0.00002 Yes 0.1 Yes 33 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0082 0.0010 0.0016 0.00002 Ca: 0.0008 Yes 0.1 Yes 34 Ex. 950 Bal. 0.40 1.0 2.2 0.7 0.0080 0.0015 0.0024 0.00001 Yes 0.1 Yes 35 Comp. ex. 960 Bal. 0.40 1.0 2.2 0.7 0.0100 0.0020 0.0026 0.00002 Yes 0.1 Yes 36 Comp. ex. 750 Bal. 0.20 1.0 2.3 0.7 0.0055 0.0022 0.0026 0.00002 Yes 0.2 No 37 Comp. ex. 750 Bal. 0.20 1.0 2.3 0.7 0.0055 0.0022 0.0026 0.00002 Yes 0.2 Yes Annealing conditions Form of internal Dew point Temp. oxidation layer (? C.) Hydrogen Wetting elevation Fine granular Temp. conc. start temp. end temp. Number density No. Tension Wetting zone elev. Holding (vol %) (? C.) (? C.) (/?m.sup.2) 1 Yes Temp. elev. 0 ?40 4 480 780 0.0 2 No Temp. elev. 0 ?45 4 500 700 4.0 3 Yes Temp. elev. 0 ?60 4 550 780 4.1 4 Yes Temp. elev. 0 ?50 4 400 780 4.3 5 Yes Temp. elev. 0 ?50 4 350 760 5.3 6 Yes Temp. elev. 0 ?45 4 450 780 4.0 7 Yes Temp. elev. 0 ?40 4 250 800 8.0 8 Yes Temp. elev. 0 ?40 4 300 780 7.5 9 Yes Temp. elev. ?40 ?40 4 400 780 0 10 Yes Temp. elev. 20 ?45 4 400 780 0.0 11 No Temp. elev. 0 ?35 4 580 980 1.1 12 No Temp. elev. 0 ?40 4 400 650 0 13 Yes Temp. elev. 0 ?45 4 300 780 1.5 14 Yes Temp. elev. 0 ?50 4 300 780 0 15 No Temp. elev. 0 ?50 4 300 780 1.0 16 Yes Temp. elev. 0 ?50 4 300 780 0 17 Yes Temp. elev. 0 ?50 4 300 780 1.5 18 Yes Temp. elev. 0 ?50 4 300 780 4.1 19 Yes Temp. elev. + 0 0 4 500 780 1.2 isothermal 20 Yes Temp. elev. 0 ?40 4 550 780 0 21 Yes Temp. elev. 0 ?60 4 300 780 6.5 22 Yes Temp. elev. 0 ?55 4 250 820 5.5 23 Yes Temp. elev. 0 ?60 4 400 780 5.0 24 Yes Temp. elev. 0 ?40 4 400 780 6.0 25 Yes Temp. elev. 0 ?40 4 300 840 6.5 26 Yes Temp. elev. 0 ?40 4 250 780 10.5 27 Yes Temp. elev. 0 ?35 4 400 860 11.0 28 Yes Temp. elev. 0 ?35 4 300 780 12.0 29 Yes Temp. elev. 0 ?55 4 200 780 6.0 30 Yes Temp. elev. 0 ?60 4 250 780 4.0 31 Yes Temp. elev. 0 ?60 4 400 820 5.0 32 Yes Temp. elev. 0 ?40 4 300 780 6.5 33 Yes Temp. elev. 0 ?45 4 350 900 4.0 34 Yes Temp. elev. 0 ?40 4 300 780 5.5 35 No Temp. elev. 0 ?40 4 400 780 2.3 36 Yes Temp. elev. 0 ?40 4 400 780 2.0 37 Yes Temp. elev. 0 ?45 4 650 750 0.0 Depleted layer Si ? Tensile 0.6% strength and after Performance Al ? plating Plating Hydrogen LME No. 0.05% [MPa] type Plateability desorption resistance 1 No 390 a B B B 2 Yes 510 a A A A 3 Yes 570 b A A A 4 Yes 580 a A A A 5 Yes 770 a A A A 6 Yes 680 a A A A 7 Yes 750 a A A AA 8 Yes 790 c: 0.3% Al A A AAA 9 No 770 b B B B 10 No 800 a B B B 11 Yes 850 a B B B 12 No 850 b B B B 13 Yes 900 b A B B 14 No 840 b B B B 15 Yes 550 a A B B 16 No 440 b B B B 17 Yes 780 a A B B 18 No 600 a A B B 19 Yes 800 a A B B 20 No 700 b B B B 21 Yes 1000 a A A A 22 Yes 1180 c: 1.2% Al A A AA 23 Yes 1030 a A A A 24 Yes 780 c: 0.9% Al A A AA 25 Yes 900 a A A A 26 Yes 860 a A AA AA 27 Yes 980 c: 0.8% Al A AA AAA 28 Yes 590 a A AA AA 29 Yes 770 a A A A 30 Yes 780 c: 1.5% Al A A AA 31 Yes 680 a A A A 32 Yes 670 b A A A 33 Yes 570 a A A A 34 Yes 460 a A A A 35 Yes 930 a A B B 36 Yes 780 a A B B 37 No 780 a B B B
[0222] In the present examples, a case where the tensile strength was 440 MPa or more, the plateability was evaluated as A, the hydrogen embrittlement resistance was evaluated as AA or A, and the LME resistance was evaluated as AAA, AA, or A was evaluated as a high strength steel sheet or plated steel sheet having a high plateability, hydrogen embrittlement resistance, and LME resistance. Throughout Examples 1 and 2, in Sample Nos. 2 to 8 and 21 to 34, the chemical compositions, number densities of the fine granular oxides, and surface depleted layers of the steel sheets satisfied the ranges of the present invention, so these had high plateability, LME resistance, and hydrogen embrittlement resistance. In Sample No. 1, the amount of C insufficient and a sufficient strength was not obtained. Not only that, but also the desired internal oxidation layer, fine granular oxides, and surface depleted layer were not obtained, so a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 9, the dew point at the time of temperature elevation in annealing was low, the desired internal oxidation layer and surface depleted layer were not formed, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 10, the dew point at the time of temperature elevation in annealing was high, fine granular type internal oxides were not formed but coarsening ended up occurring, the desired surface depleted layer was not obtained, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 11, the holding temperature at the time of annealing was high, an internal oxidation layer was not sufficiently formed, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 12, the holding temperature at the time of annealing was low, internal oxidation did not proceed, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample Nos. 13 and 15, the amount of Si and amount of Mn were respectively excessive and, in each, the granular oxides became coarser and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample Nos. 14 and 16, the amount of Si and amount of Mn were respectively insufficient and, in each, the desired oxidation layer and surface depleted layer were not formed and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 17, the amount of Al was excessive, the granular oxides became coarsened, and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample No. 18, the amount of Al was insufficient, the desired surface depleted layer was not formed, and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample No. 19, the dew point was made 0? C. not only at the time of temperature elevation in annealing, but also at the time of holding in annealing, so the wetting time became longer, the granular oxides coarsened, and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample No. 20, the depth of the internal oxidation layer before annealing was great, the desired internal oxides and surface depleted layer could not be formed after annealing, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained. In Sample No. 35, tension was not applied at the time of annealing, so an internal oxidation layer was not sufficiently formed and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample No. 36, brush grinding was not performed before annealing, so an internal oxidation layer was not sufficiently formed and a high hydrogen embrittlement resistance and LME resistance were not obtained. In Sample No. 37, the wetting start temperature was 600? C. or more, an internal oxidation layer was not sufficiently formed, and a high plateability, hydrogen embrittlement resistance, and LME resistance were not obtained.
[0223] In the invention examples, large numbers of the fine granular oxides were confirmed and the predetermined surface depleted layers were confirmed to be obtained by EDS. For this reason, high plateability, hydrogen embrittlement resistance, and LME resistance were obtained. On the other hand, in the comparative examples, internal oxidation layers and/or surface depleted layers were not suitably formed in the vicinities of the steel sheet surfaces. For this reason, they were confirmed to feature at least one of a low plateability, penetration of a large amount of hydrogen, or inferior LME resistance.
INDUSTRIAL APPLICABILITY
[0224] According to the present invention, high strength steel sheet and plated steel sheet having a high plateability, LME resistance, and hydrogen embrittlement resistance can be provided. The steel sheet and plated steel can be suitably used for home electric appliances, building materials, and other applications, in particular for automobiles. As steel sheet for automobile use and plated steel sheet for automobile use, higher collision safety and longer life can be expected. Therefore, the present invention can be said to be extremely high in value in industry.
REFERENCE NOTATIONS
[0225] 1. steel sheet [0226] 2. external oxidation layer [0227] 3. base steel [0228] 11. steel sheet [0229] 12. fine granular oxides [0230] 14. base steel