Method for manufacturing ceramic composite material and product thereof

Abstract

The method includes the steps of: a) selecting particles with particular slenderness ratios and diameters from SiC powder to serve as selected SiC material powder; b) coating a PVA coating on particles of the selected SiC material powder so that the PVA coating and the selected SiC material powder are combined into a particulate ceramic material; c) pressing the particulate ceramic material into a ceramic base body; d) sintering the ceramic base body to form a fixed shape and forming completely continuous channels from an inside to a surface thereof by cooling; and e) infiltrating the ceramic base body with molten aluminum. The ceramic composite material made by the method includes a ceramic base body having completely continuous channels from an inside to a surface thereof; an aluminum filler filled in the channels; and an aluminum coating disposed on the ceramic base body and integratedly connecting with the aluminum filler.

Claims

1. A ceramic composite material comprising: a ceramic base body having completely continuous channels from an inside to a surface thereof; an aluminum filler filled in the channels; and an aluminum coating disposed on the ceramic base body and integratedly connecting with the aluminum filler, wherein the ceramic composite material is formed into a bicycle pedal, and wherein a pedal body of the bicycle pedal comprises a shaft hole and a pedal frame.

2. The ceramic composite material of claim 1, wherein the pedal frame is formed with a stud.

3. The ceramic composite material of claim 1, wherein the pedal body comprises a shaft hole and a pedal frame with a front hook and a rear hook.

4. The ceramic composite material of claim 1, wherein the pedal body includes a shaft hole and a pedal frame with four protrusions.

5. The ceramic composite material of claim 4, wherein each protrusion is formed with a hole.

6. The ceramic composite material of claim 1, wherein a thickness of the aluminum coating of the bicycle pedal is between 0.3 mm and 0.7 mm.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a flowchart of the method of the invention;

(2) FIG. 2 is a schematic view of the particulate ceramic material made by step S2 of the method of the invention;

(3) FIG. 3 is a schematic view of the ceramic material made by a conventional wet type granulation approach;

(4) FIG. 4 is a schematic view of temperature control in step S4 of the method of the invention;

(5) FIG. 5 is a schematic view of the first embodiment of the ceramic composite material made by the method of the invention;

(6) FIG. 6 is a schematic view of the second embodiment of the ceramic composite material made by the method of the invention;

(7) FIG. 7 is a schematic view of the third embodiment of the ceramic composite material made by the method of the invention; and

(8) FIG. 8 is a schematic view of the fourth embodiment of the ceramic composite material made by the method of the invention.

DETAILED DESCRIPTION OF THE INVENTION

(9) Please refer to FIG. 1. The method for manufacturing a ceramic composite material of the invention includes the following steps: S1) selecting particles with a slenderness ratio between 1:1.075 and 1:1.09 and a diameter between 3 ?m and 15 ?m from silicon carbide (SiC) powder 11 to serve as selected SiC material powder; S2) mixing the selected SiC material powder with polyvinyl alcohol (PVA) to coat a PVA coating 12 on each particle of the SiC powder 11, wherein the PVA coating and the SiC powder particles are combined into a particulate ceramic material 10, and preferably, and the PVA coating accounts for 0.1%-0.8% w/w (weight by weight) of the particulate ceramic material 10; S3) pressing the particulate ceramic material 10 into a ceramic base body 30; S4) sintering the ceramic base body 30 to form a fixed shape and forming completely continuous channels from an inside to a surface thereof by cooling; and S5) infiltrating the ceramic base body 30 with molten aluminum, wherein the ceramic base body 30 is put in a mold with a preset thickness and then heat up the mold to a constant temperature and make molten aluminum infiltrate the ceramic base body 30 with high pressure and high speed to be casted. Thus a ceramic composite material A is obtained.

(10) In step S1, the SiC powder 11 is divided into several grades according to particle size, and one grade of the SiC powder 11 is selected to serve as the selected SiC material powder. Preferably, the grades are ten in number. Thus, the porosity, density and specific surface can be easily adjusted by the grading.

(11) The step S2 can be deemed as a dry type granulation approach. It is called Diffusive high-speed granulation process. Continuous pores can be formed in the particulate ceramic material 10 without a pore former. Therefore, no toxic organics will be emitted during sintering, and since there are no impurities during sintering, there is no need to extend the sintering time to discharge organics.

(12) In the diffusive high-speed granulation process, preferably, the selected SiC material powder is high-speed stirred with diffusive blades to be flown up, the PVA is evenly sprayed to combine with the selected SiC material powder to form the particulate ceramic material 10. In other words, the SiC powder 11 is flown up and combines with sprayed liquid PVA to form the particulate ceramic material 10. The PVA covering the SiC powder 11 to form the PVA coating 12. Normally, particles of the SiC powder 11 can be adhered with each other by PVA to form irregularly spherical particulate ceramic material 10 as shown in FIG. 2. The time consuming in the granulation step is very short and a very small amount of PVA is needed, so wearing of the SiC powder 11 in the granulation step can be effectively reduced to avoid the slenderness ratio of the SiC powder 11 is varied. On the other hand, the PVA coating 12 may increase the porosity in the subsequent step.

(13) In comparison with the wet type granulation approach which adds PVA as an adhesive and stirs SiC powder and PVA in a container. Stirring easily causes clumps. The conventional dry type granulation approach needs more PVA (about 3.0% w/w). As shown in FIG. 3, many SiC powder particles 21 are adhered to a PVA clump 22 to form a particulate ceramic powder material. The shape of this particulate ceramic powder material is approximately spherical, so it has better mobility to be hard to form pores. The differences between the granulation step and the conventional wet type granulation approach are listed as follows:

(14) a) The invention keeps the shapes of particles of the SiC powder 11 complete to avoid the slenderness ratio of the SiC powder 11 from varying.

(15) b) The particulate ceramic material 10 made by step S2 keeps pores to improve porosity of the ceramic base body 30.

(16) c) The conventional wet type granulation approach needs a PVA adhesive over 3.0 wt %. The PVA accounts for below 0.8 wt % of the particulate ceramic material 10.

(17) d) The conventional wet type granulation approach needs a large amount of organic solvents, so it harmful to environment protection.

(18) The particulate ceramic material 10 made by step S2 can form pores by mechanical bridging. A continuous pore structure can be formed in the ceramic base body 30. This can solve the problem of discontinuous pores made by a pore former or foam. Also, the porosity of the ceramic base body 30, the structural strength and the specific surface area.

(19) Step S3 presses the particulate ceramic material 10 into the ceramic base body 30 with proper pressure according to actual requirements. Preferable pressure is 300-1500 kg/cm.sup.2. In this step, the mold will be adjusted in time to make pressure evenly distributed in the ceramic base body 30. After the particulate ceramic material is pressed into a ceramic base body 30, let the ceramic base body 30 sit for 24 hours to completely release stress. Thus, the ceramic base body 30 has even density distribution and great structural strength.

(20) Step S4 sinters the ceramic base body 30 between 1050? C. and 1450? C. according to a predetermined temperature control process (such as heating-keeping-cooling). A preferred embodiment of the temperature control process is shown in FIG. 4. In the heating section, the ceramic base body 30 is heating up for 8-12 hours to a predetermines sintering temperature between 1050? C. and 1450? C. (depending on the grading of the particulate ceramic material 10. In the sintering section, keep the sintering temperature to sinter for 2-8 hours. Finally, in the cooling section, the sintered ceramic base body 30 is cooled for 6-8 hours to a normal temperature.

(21) In step S5, the mold is heated between 200? C. and 600? C.

(22) A ceramic composite material A made by the above method, as shown in FIG. 5, includes a ceramic base body 30 having completely continuous channels from an inside to a surface thereof, an aluminum filler filled in the channels and an aluminum coating 40 disposed on the ceramic base body 30 and integratedly connecting with the aluminum filler.

(23) FIG. 6 shows a BMX pedal using the ceramic composite material A of the invention. The pedal body 1 adopts the ceramic composite material A formed by a ceramic base body 30 infiltrated with aluminum and an aluminum coating 40. The pedal body 1 includes a shaft hole 110 and a pedal frame 120. The pedal frame 120 is formed with studs 130. FIG. 7 shows a clipless pedal for a road bike. The pedal body 1 includes a shaft hole 110 and a pedal frame with a front hook 14 and a rear hook 15. FIG. 8 shows a pedal for a mountain bike. The pedal body 1 includes a shaft hole 110 and a pedal frame with four protrusions 16 and four holes 17.

(24) Aluminum infiltrates and coats the ceramic base body 30 to improve structural strength and protect the ceramic base body 30.

(25) It will be appreciated by persons skilled in the art that the above embodiments have been described by way of example only and not in any limitative sense, and that various alterations and modifications are possible without departure from the scope of the invention as defined by the appended claims.