METHOD AND DEVICE FOR PRODUCING A CONTINUOUS STRIP-SHAPED COMPOSITE MATERIAL

Abstract

The invention relates to a device (10) and to a method for producing a continuous strip-shaped composite material (11). A base material of metal, which is unwound in the form of a metal strip (13) by a first coil-unwinding apparatus (12), and at least one cladding material of metal, which is unwound in the form of a metal strip (15) by a second coil-unwinding apparatus (14), are provided. Then, the metal strips (13, 15) unwound by said coil-unwinding apparatuses (12, 14) are brought together in the hot state, wherein then the unwound metal strips (13, 15) brought toward each other are hot-rolled such that a single continuous strip-shaped composite material (11) is thus formed by roll cladding, said composite material consisting of the base material and the cladding material. Both the base material and the cladding material and the metal strips (13, 15) thereby unwound each consist of steel.

Claims

1-23. (canceled)

24. A method for producing a continuous strip-shaped composite material (11), having the following steps: (i) Provision of a base material of metal, which is unwound in the form of a metal strip (13) formed of steel or alloy steel by a first coil-unwinding apparatus (12), and at least one cladding material of metal, which is unwound in the form of a metal strip (15) formed of steel or alloy steel by a second coil-unwinding apparatus (14); (ii) Joining of the metal strip (13) unwound by the first coil-unwinding apparatus (12) and of the metal strip (15) unwound by the second coil-unwinding apparatus (14); and (iii) Rolling of the unwound metal strips (13, 15) brought towards one another such that a single continuous strip-shaped composite material (11) consisting of the base material and the cladding material is thereby formed, wherein the metal strips (13, 15, 35) unwound by a respective coil-unwinding apparatus (12, 14, 34) are descaled by using high-pressure water before the step (ii), and the rolling of metal strips (13, 15, 35) in step (III) is carried out as hot rolling, characterized in that the first and the second coil-unwinding apparatus (12, 14) are accommodated in a heatable environment (22) during step (i) such that a predefined temperature of at least 720 C. is set for the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14) before steps (ii) and (iii) joining of the metal strips (13, 15) in step (ii) is carried out in a hot condition, with the metal strips (13, 15) each having a temperature of at least 720 C., before the step (iii), a surface temperature of all of the metal strips (13, 15, 35) on opposite to each other surfaces is increased by using induction heating, and during the step (ii) and before the step (iii), the metal strips (13, 15, 35) unwound by the respective coil-unviding apparatus (12, 14, 34) are transported in an inert gas atmosphere (28).

25. The method according to claim 24, characterized in that the metal strips (13, 15), are heated to a temperature above the recrystallization limit, that said heating preferably is implemented by means of an induction heater, before step (ii) and/or during step (ii) and/or before step (iii).

26. The method according to claim 24, characterized in that the cladding material (15) is applied, in step (iii), on opposite sides of the metal strip (13) consisting of the base material, wherein the cladding material consists of the same material and is unwound by respective separate coil-unwinding apparatuses (14, 34), in step (i).

27. The method according to according to claim 24, characterized in that the base material and the at least one cladding material each consist of different grades of steel, wherein a further cladding material in the form of a metal strip (35) is unwound by a third coil-unwinding apparatus (34) in step (i), and subsequent steps (ii) and (iii) are implemented with a total of three layers, which are formed from the metal strips (13, 15, 35) unwound by the respective coil-unwinding apparatuses (12, 14, 34).

28. The method according to claim 27, characterized in that the metal strips (15, 35) each consisting of the cladding material are each formed from different materials, wherein said metal strips (15, 35) are applied either on opposite sides of the metal strip (13) consisting of the base material or on the same side thereof.

29. The method according to claim 24, characterized in that the metal strips (13, 15, 35) unwound by the coil-unwinding apparatuses (12, 14, 34) are laterally guided during step (i) and/or before step (ii) and/or during step (ii) and/or before step (iii) in order to thereby align the respective metal strips (13, 15, 35) with respect to one another, preferably that, for the lateral guidance, at least one lateral-influencing apparatus (26) is provided in the form of a guide ruler, which is moved in the direction of the middle of the strip by means of an actuator, particularly with a predefined force.

30. The method according to claim 24, characterized in that the metal strips (13, 15, 35) unwound by a respective coil-unwinding apparatus (12, 14, 34), are guided in an inert gas atmosphere (28).

31. The method according to claim 24, characterized in that a material quality of the single continuous strip-shaped composite material (11) produced is detected particularly by means of x-ray and/or ultrasound following step (iii), preferably that a process signal is generated by means of a control device based on the detected material quality, said process signal forming a control circuit for the method.

32. The method according to claim 24, characterized in that said method is automatically implemented as a function of at least one predefined process variable, preferably that said process variable is selected from the group formed particularly from the speed, present before step (ii), of the metal strips (13, 15, 35) unwound by the coil-unwinding apparatuses (12, 14, 34), from a temperature difference in the metal strips (13, 15, 35) before step (ii) and/or before step (iii), from the different material properties and the thickness ratio of the matched materials and/or metal strips used, from a respective speed of the working rollers (A1, A2) of the roll-cladding apparatus (16.1; 16.i), and/or from a thickness reduction in the single continuous strip-shaped composite material (11) achieved in step (iii).

33. The method according to claim 24, characterized in that at least one intermediate layer in solid, liquid, or powdered form, which passivates or activates the surfaces of the metal strips (13, 15) opposite one another, is provided between the metal strips (13, 15) to be joined together.

34. A device (10) for producing a continuous strip-shaped composite material (11), comprising at least one first coil-unwinding apparatus (12), with which a metal strip (13) formed of steel or alloy steel is provided which serves as the base material; at least one second coil-unwinding apparatus (14), with which a metal strip (15) formed of steel or alloy steel is provided which serves as the cladding material; at least one rolling mill (16) in the form of a roll-cladding apparatus (16.1), which is arranged in line with the first and the second coil-unwinding apparatus (12, 14) and is arranged downstream thereof; a joining apparatus (18) arranged between the coil-unwinding apparatuses (12, 14, 34) on one side and the roll-cladding apparatus (16.1) on the other side, and at least one cleaning apparatus (20) in form of a high-pressure water descaling apparatus is arranged between the coil-unwinding apparatuses, on one side, and the joining apparatus, on the other side, and with which the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14) are descaled, characterized in that the first and second coil-unwinding apparatuses (12, 14) are arranged in at least one heatable chamber (22) under inert gas atmosphere, wherein the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14) are joined by the joining apparatus (18) in a hot state, at least one temperature-influencing apparatus (30) in form of an induction-heating apparatus is arranged between the joining apparatus (18) and a roll-cladding apparatus (16.1) provided directly downstream thereof, with which opposite surfaces of the metal strips (13, 15) which are unwound by the respective coil-unwinding apparatus (12, 14), can be heated so that a strip-shaped composite material which is formed of the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14), can be hot-rolled in the roll-cladding apparatus (16.1), whereby a single continuous strip-shaped composite material (11) which is formed of a base material and a clad material, is produced, and an inert gas apparatus (28) forms part of the joining apparatus (18), whereby the metal strips (13, 15) unwound by the respective coil-unwinding apparatus (12, 14) are transported in the inert gas device (28) in the inert gas atmosphere.

35. The device (10) according to claim 34, characterized in that at least one coil-unwinding apparatus (12, 14) has a quick-change apparatus, by means of which it is possible to replace coils, preferably that the quick-change apparatus comprises a welding device in order to weld successive metal strips (13, 15) to one another.

36. The device (10) according to claim 34, characterized in that at least one coil-unwinding apparatus (12; 14) has a plurality of unwinding modules, which can be successively placed into an unwind position, preferably that said coil-unwinding apparatus (12; 14) comprises a welding device in order to weld successive metal strips (13, 15) to one another.

37. The device (10) according to claim 34, characterized in that at least one heating apparatus (24) is provided upstream of the joining apparatus (18) and/or as a part thereof, wherein the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14) are guided through said heating apparatus (24), preferably that at least one heating apparatus (24) functions according to the principle of induction heating, more preferably that a separate heating apparatus (24) is provided for each of the unwound metal strips (13, 15).

38. The device (10) according to claim 34, characterized in that at least one lateral-influencing apparatus (26) is provided, which is arranged upstream of the joining apparatus (18) or as a part thereof and/or upstream of the roll-cladding apparatus (16.1), wherein the metal strips (13, 15) unwound by the coil-unwinding apparatuses (12, 14) can be placed in contact with the lateral-influencing apparatus (26) at their side edges in order to be aligned laterally with respect to each other, preferably that the at least one lateral-influencing apparatus (26) is formed in the form of a guide ruler, which can be moved in the direction of the middle of the strip, particularly with a predefined force.

39. The device (10) according to claim 34, characterized by an inert gas apparatus (28), which is provided as a part of the joining apparatus (18) and/or as a part of a roll-cladding apparatus (16.1) arranged downstream directly adjacent to the joining apparatus (18), wherein at least one metal strip (13, 15) unwound by the coil-unwinding apparatuses (12, 14) is guided within said inert gas apparatus (28) in an inert gas atmosphere, preferably that the metal strips (13, 15) unwound by the respective coil-unwinding apparatuses (12, 14) are guided within said inert gas apparatus (28) in an inert gas atmosphere.

40. The device (10) according to claim 34, characterized in that a measuring apparatus (32), by means of which a material quality of the single continuous strip-shaped composite material (11) produced can be detected, particularly through x-ray and/or ultrasound, is provided downstream of a roll-cladding apparatus (16.1).

41. The device (10) according to claim 34, characterized in that a third coil-unwinding apparatus (34) is provided, which is arranged in line with the roll-cladding apparatus (16.1) and with which a further metal strip (35) is provided as a cladding material.

Description

[0040] Exemplary embodiments of the invention are described in the following in detail by means of a schematically simplified drawing.

[0041] Wherein:

[0042] FIG. 1 shows a general side view of a device according to the invention, in which three coil-unwinding apparatuses are used;

[0043] FIG. 2 shows a general side view of a modification of the joining apparatus, which may be part of the device from FIG. 1;

[0044] FIG. 3 shows a generally simplified enlarged view of a modified coil-unwinding apparatus, which may be part of the device from FIG. 1; and

[0045] FIGS. 4a, 4b show sides views of the working rollers of a roll-cladding apparatus, which is part of the device from FIG. 1;

[0046] Preferred embodiments of a device 10 according to the invention and components thereof are explained in the following with reference to FIGS. 1 to 4, wherein said device 10 is used to produce a metal strip in the form of a continuous strip-shaped composite material 11. Equivalent features in the drawing are each provided with the same reference numbers. At this juncture, particular reference is made to the fact that the drawing is merely simplified and particularly not shown to scale.

[0047] FIG. 1 shows a generally simplified side view of the device 10 according to a first embodiment.

[0048] The device 10 comprises a first coil-unwinding apparatus 12, from which a base material is unwound in the form of a metal strip 13. Furthermore, the device 10 comprises a second coil-unwinding apparatus 14 and a third coil-unwinding apparatus 34, from which a cladding material is unwound in the form of metal strips 15 and/or 35. FIG. 1 clearly shows that the second coil-unwinding apparatus 14 and the third coil-unwinding apparatus 34 are arranged on respective opposite sides of the first coil-unwinding apparatus 12. Metal strips 13, 15, and 35 unwound by the aforementioned coil-unwinding apparatuses 12, 14 and 34 are subsequently jointly guided through a joining apparatus 18 and thereby brought towards one another. The device 10 further comprises at least one rolling mill 16 in the form of a roll-cladding apparatus 16.1, which is arranged directly after the joining apparatus 18 and thus downstream thereof. The function of said roll-cladding apparatus 16.1 is explained separately in the following.

[0049] The joining apparatus 18 is used to bring the unwound metal strips 13, 15, and 35 towards one another. With the embodiment shown in FIG. 1, it may be provided that said metal strips are placed in contact with each other as early as the joining apparatus 18. With an alternative embodiment of the joining apparatus 18, which is shown generally simplified in the side view from FIG. 2 and is part of the device from FIG. 1, the unwound metal strips do not make contact with one another within the joining apparatus 18 but rather not until outside and downstream when they enter the roll-cladding apparatus 16.1 positioned directly adjacent thereto. For this alternative joining apparatus 18 according to FIG. 2, it should be referenced at this juncture that only metal strips 13 and 15 are shown in the representation of FIG. 2 for simplification purposes, wherein metal strip 35, which is unwound by the third coil-unwinding apparatus 34, is not shown.

[0050] FIG. 2 shows a transport direction indicated with the arrow labeled T, in which the continuous strip-shaped composite material 11 produced is transported and/or moved (from left to right in the drawing plane). With respect to the representations from FIG. 1, it is clear that the composite material 11 herein is moved in the same direction, namely from left to right (when viewed in the drawing plane).

[0051] The speed at which the unwound metal strips 13, 15, and 35 are transported in the direction of the joining apparatus 18 can be controlled, preferably regulated. This is possible by means of a suitable actuation of a motorized drive, which can be provided for each of the individual coil-unwinding apparatuses 12, 14, and 34. Said motorized drives of the individual coil-unwinding apparatuses are preferably actuated by a common control device (not shown).

[0052] Thus, metal strips 13, 15, and 35 preferably enter the joining apparatus 18 at the same speed.

[0053] The device 10 comprises heating apparatuses 24, each of which are arranged in a line between the individual coil-unwinding apparatuses 12, 14, 34 and the joining apparatus 18. Specifically, a first heating apparatus 24.1 is arranged between the first coil-unwinding apparatus 12 and the joining apparatus 18. In the same manner, a second heating apparatus 24.2 is arranged between the second coil-unwinding apparatus 14 and the joining apparatus 18, wherein a third heating apparatus 24.3 is arranged between the third coil-unwinding apparatus 34 and the joining apparatus 18. The unwound metal strips 13, 15, 35 are guided through the assigned heating apparatuses 24.1, 24.2, and 24.3 and, in doing so, are heated according to the principle of through heating. As a result of this, potential temperature differences between the individual metal strips, which can be adjusted, e.g., as a result of transport distances of different length, are balanced. Thus, metal strips 13, 15, 35 enter the joining apparatus 18 at a predefined temperature.

[0054] The device 10 has lateral-influencing apparatuses, each of which are arranged upstream of the joining apparatus 18 and in line with the respective coil-unwinding apparatuses 12, 14, 34. Said lateral-influencing apparatuses are merely indicated symbolically by the reference number 26 in the representation of FIG. 2 and may be formed, for example, by guide rulers. Accordingly, the unwound metal strips are laterally guided by these guide rulers and thereby aligned relative to one another. At this juncture, it should be specifically referenced that said lateral-influencing apparatuses 26 may also be arranged within the joining apparatus 18 and thus be formed as a part of said joining apparatus 18.

[0055] The previously mentioned roll-cladding apparatus 16.1 is used to implement hot rolling for metal strips 13, 15, 35 and thus to produce a continuous strip-shaped composite material 11 therefrom by means of roll cladding. The side view from FIG. 4b generally shows three-layer roll welding of three matching materials in simplified form, which may consist, e.g., of metal strips 13, 15, 35 when they are placed in contact with working rollers A1, A2 of the roll-cladding apparatus 16.1 and are guided between said working rollers A1, A2. The side view from FIG. 4b clearly shows that a composite is formed from metal strips 13, 15, 35 when they jointly enter the roll-cladding apparatus 16.1, said composite then being hot-rolled and/or roll-cladded to form the strip-shaped composite material 11 by working rollers A1, A2 of the roll-cladding apparatus.

[0056] With the representation according to FIG. 4b, the metal strip 13 serves as a base material, wherein the other two metal strips, 15 and 35, serve as the cladding material, which is cladded on opposite sides of the metal strip 13. Reference is made with respect to this that different material and/or steel grades can be used for the base material (in the form of metal strip 13) on one side and for the cladding material (in the form of metal strips 15, 35) on the other side. The cladding material used for metal strips 15, 35 may consist of the same material or alternatively consist of different steel grades for each. Furthermore, reference is made to the fact that, contrary to the representation in FIG. 4b, the two metal strips 15, 35 may also be applied or cladded on the same side of metal strip 13.

[0057] After the roll-cladding apparatus 16.1 and/or downstream thereof, further rolling mills and/or roll-cladding apparatuses may be provided, with which hot rolling is implemented for the strip-shaped composite material 11. FIG. 1 shows, indicated by reference number 16.i, that at least one further roll-cladding apparatus or a plurality of such rolling mills may be arranged in the rolling line 17, downstream of roll-cladding apparatus 16.1. Furthermore, further rolling mills may be provided in the rolling line 17 downstream of roll-cladding apparatuses 16.i.

[0058] As shown by the representation in FIG. 2, the device 10 comprises a cleaning apparatus in the form of a descaling apparatus 20, which is arranged upstream of the joining apparatus 18. Metal strips 13, 15, 35 are suitably descaled by said descaling apparatus 20, which is therefore particularly advantageous because said metal strips each consist of steel or a steel alloy. Furthermore, the side view from FIG. 2 shows that the device 10 comprises an inert gas apparatus 28, which is integrated into the joining apparatus 18. In the representation from FIG. 2, the inert gas apparatus 28 is only indicated in simplified form by dashed lines. Before they are guided through the roll-cladding apparatus 16.1, metal strips 13, 15, 35 are guided through the inert gas apparatus 28 by means of hot rolling and/or roll cladding, which effectively reduces fresh scaling on the surfaces opposite one another of said metal strips 13, 15, 35.

[0059] The joining of the unwound metal strips 13, 15, 35 by means of hot rolling in step (iii) can be further improved in that a surface temperature of at least one of these matched materials is influenced, preferably increased, at their opposite respective sides. To this end, a temperature-influencing apparatus 30, which is symbolically shown in simplified form in the representation from FIG. 2, is arranged directly upstream of the roll-cladding apparatus 16.1.

[0060] The device further comprises at least one measuring apparatus 32, with which the material quality of the continuous strip-shaped composite material 11, which has been produced by means of hot rolling through the roll-cladding apparatus 16.1, can be detected. The measuring apparatus 32 is arranged, for example, after or downstream of the roll-cladding apparatus 16.1 and preferably functions according to the x-ray and/or ultrasound principle. To this end, it may be provided the corresponding sensors of the measuring apparatus 32 are to be arranged above and/or below the continuous strip-shaped composite material 11 such that an upper side and/or a lower side of the metal strip, in the form of said composite material 11, can thereby be tested with respect to its material quality and/or surface quality.

[0061] Separating apparatuses 36, for example in the form of pendulum or cylindrical shears or the like, are arranged at various points along the process line of the device 10. Said separating apparatuses 36 enable removal and/or discharging of non-useable material. As a supplement and/or alternative, a discontinuous rolling operation of individual strips and/or an emergency operation with only one of the coil-unwinding apparatuses 12, 14, 34 can be implemented by using said separating apparatuses 36. The separating can also be implemented with the goal of improving the downstream process steps and/or for producing the lengths of the end product produced in this system. Reference is made with respect to this that the positions of the respective separating apparatuses 36 shown in FIG. 1 should only be considered examples.

[0062] The device 10 may also comprise a rolling line 17, with which the continuous strip-shaped composite material 11 produced can be rolled out to smaller thicknesses.

[0063] At least one reel 38 is provided at the end of the rolling line 17 in order to wind the continuous strip-shaped composite material 11 into a coil. A plurality of such reels 38 may expediently also be provided, with corresponding (not shown) apparatuses for switching among the individual reels 38. As a supplement and/or alternative, at least one storage area or the like may also be provided at the end of the rolling line 17 in order to remove sheets and/or heavy plates therefrom.

[0064] The device 10 according to FIG. 1 can be modified to the extent that a total of only two coil-unwinding apparatuses are used, e.g. the first coil-unwinding apparatus 12 and the second coil-unwinding apparatus 14. A joining of the metal strips 13, 15 unwound therefrom and the subsequent hot rolling into a single continuous strip-shaped composite material 11 then corresponds to the representation according to FIG. 2. In addition, reference is made for such modification of the device 10 to the extent that a joining, e.g., of only two matched materials, which may consist of metal strip 13 and metal strip 15, is shown in the simplified side view from FIG. 4a.

[0065] A further modification of the device 10 according to FIG. 1 may take place in the manner such that at least one of the coil-unwinding apparatuses 12, 14, 34 is accommodated in a heatable chamber 22. This is shown in simplified form in the representation from FIG. 3. Such accommodation of a coil-unwinding apparatus 12, 14, 34 in the heatable chamber 22 ensures that a metal strip 13, 15, 35 unrolled therefrom already has a predefined temperature with respect to a joining of the individual metal strips 13, 15, 35 and the subsequent hot rolling to form a single continuous strip-shaped composite material 11. Preferably, all of the coil-unwinding apparatuses 12, 14, 34 are each accommodated separately in a heatable chamber 22.

[0066] The method according to the invention for producing the continuous strip-shaped composite material 11 can be implemented with the previously explained embodiments of the device 10 according to the invention. Said method can be implemented automatically, and preferably regulated, as a function of at least one of the aforementioned process variables.

LIST OF REFERENCE NUMBERS

[0067] 10 Device [0068] 11 Continuous strip-shaped composite material [0069] 12 First coil-unwinding apparatus [0070] 13 Metal strip (which is unwound by the first coil-unwinding apparatus 12) [0071] 14 Second coil-unwinding apparatus [0072] 15 Metal strip (which is unwound by the second coil-unwinding apparatus 14) [0073] 16.1 Roll-cladding apparatus [0074] 16.1 (Further) roll-cladding apparatus(es) [0075] 17 Rolling line [0076] 18 Joining apparatus [0077] 20 Cleaning apparatus (e.g. descaling apparatus) [0078] 22 (Heatable) chamber (for accommodating a coil-unwinding apparatus) [0079] 24.1 First heating apparatus (e.g. induction heater) [0080] 24.2 Second heating apparatus (e.g. induction heater) [0081] 24.3 Third heating apparatus (e.g. induction heater) [0082] 26 Lateral-influencing apparatus (e.g. guide ruler) [0083] 28 Inert gas apparatus [0084] 30 Temperature-influencing apparatus [0085] 32 Measuring apparatus [0086] 34 Third coil-unwinding apparatus [0087] 35 Metal strip (which is unwound by the third coil-unwinding apparatus 34) [0088] 36 Separating apparatus (e.g. cylindrical shears) [0089] 38 Reel [0090] A1, A2 Working rollers (of roll-cladding apparatus 16.1) [0091] T Transport direction (for the strip-shaped composite material 11)