DYE-SENSITIZED SOLAR CELL

Abstract

The present invention relates to a dye-sensitized solar cell electrode and a dye-sensitized solar cell including the same. A membrane is formed on a surface of a working electrode, thereby preventing a dye from being separated from an oxide semiconductor layer. The membrane is formed on a surface of a counter electrode, thereby enabling electrolyte elements (I.sup., I.sub.3.sup., etc.) to be passed therethrough while not allowing the dye to be adsorbed. The reliability and efficiency of a dye-sensitized solar cell be improved.

Claims

1. A dye-sensitized solar cell comprising: a working electrode comprising a conductive film, an oxide semiconductor on the conductive film, and a dye on the oxide semiconductor; a counter electrode opposing the working electrode; an electrolyte solution between the working electrode and the counter electrode; and a membrane covering at least a part of the dye or the counter electrode.

2. The dye-sensitized solar cell according to claim 1, wherein the membrane covers the dye.

3. The dye-sensitized solar cell according to claim 2, wherein the membrane further covers the oxide semiconductor.

4. The dye-sensitized solar cell according to claim 3, wherein the membrane further covers the conductive film.

5. The dye-sensitized solar cell according to claim 4, further comprising an additional membrane covering the counter electrode.

6. The dye-sensitized solar cell according to claim 1, wherein the membrane covers the counter electrode.

7. The dye-sensitized solar cell according to claim 1, wherein the membrane or the additional membrane comprises: (i) at least one of a condensation product of the following Chemical Formula 1 or a condensation product of the following Chemical Formula 2; and (ii) a condensation product of Chemical Formula 1 and Chemical Formula 2:
A(OR).sub.3[Chemical Formula 1]
(OR).sub.3A-XB(OR).sub.3[Chemical Formula 2] wherein A and B are each independently SiR, GeR, P, PR.sub.2, or Al, each R is independently hydrogen, deuterium, a linear or branched C.sub.1-30 alkyl group, or a C.sub.3-30 cycloalkyl group, and X is O, a C.sub.2-30 alkene, a C.sub.6-30 aryl, an alkoxy, an epoxy, an amine, an ester, an amide, a carbonyl, an ether, a thioether, a thiophene, a furan, or a cyclohexyl.

8. The dye-sensitized solar cell according to claim 1, wherein the membrane passes electrolyte elements therethrough while not passing a dye therethrough.

9. The dye-sensitized solar cell according to claim 1, wherein the membrane includes at least one molecular layer.

10. The dye-sensitized solar cell according to claim 1, wherein the thickness of the membrane is 0.1 to 1000 .

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0014] FIG. 1 shows a dye-sensitized solar cell electrode according to the first embodiment of the present invention.

[0015] FIG. 2 shows a dye-sensitized solar cell electrode according to the second embodiment of the present invention.

[0016] FIG. 3 shows a dye-sensitized solar cell electrode according to the third embodiment of the present invention.

[0017] FIG. 4 is a drawing showing that a trialkoxysilane compound according to the embodiment of the present invention is bonded to the surface of a working electrode through a hydrolysis-condensation reaction.

[0018] FIG. 5 is a graph comparing the electrode activities when a membrane film is applied to the working electrodes according to an example and a comparative example.

[0019] FIG. 6 is a graph comparing the electrode activities when a membrane film is applied to the counter electrodes according to an example and a comparative example.

DETAILED DESCRIPTION

[0020] Hereinafter, the embodiments of the present invention will be explained in detail with reference to the attached drawings so that a person having ordinary knowledge in the art may easily practice them.

[0021] However, the present invention may be realized in various forms, and is not limited to the embodiments explained herein.

[0022] Throughout the specification, when it is described that a part comprises a constructional element, unless specifically described to the contrary, it does not mean that other constructional elements are excluded, but it means that the part may further include other constructional elements.

[0023] FIGS. 1 to 3 are drawings respectively showing a dye-sensitized solar cell according to one embodiment of the present invention.

[0024] Referring to FIGS. 1 to 3, a dye-sensitized solar cell 100 according to the present invention includes a working electrode (110), a counter electrode (120), an electrolyte solution (130), and a membrane (140). Specifically, the working electrode (110) includes a conductive film (112) and an oxide semiconductor (113) to which a dye (114) is adsorbed on a substrate (111), and the counter electrode (120) includes a conductive film (122) and a catalyst layer (123) on a substrate (121).

[0025] The membrane (140) according to the present invention is formed so as to cover the surface of the working electrode (110), the surface of the counter electrode (120), or both surfaces of the working electrode (110) and the counter electrode (120). Specifically, the membrane (140) may be formed so as to cover only the surface of the working electrode (110) of a dye-sensitized solar cell electrode or to cover only the surface of the counter electrode (120) of a dye-sensitized solar cell electrode, or it may be formed on both surfaces of the working electrode (110) and the counter electrode (120) of a dye-sensitized solar cell electrode to cover the whole dye-sensitized solar cell electrode.

[0026] A substrate (111 or 121) is a constructional element corresponding to a base for constituting a working electrode (110) or a counter electrode (120), and it performs a function of transferring electrons.

[0027] As the substrate (111 or 121), any known substrates may be used, and specifically, a glass substrate, a soda lime glass substrate, and the like may be used. A conductive film (112 or 122) is formed on the substrate (111 or 121) of the working electrode (11) or counter electrode (120), and it performs a function as a passage that transfers electrons. Specifically, in the working electrode (110), the conductive film (112) transfers electrons from the oxide semiconductor (113) to the substrate (111), and in the counter electrode (120), the conductive film (122) transfers electrons from the substrate (121) to the catalyst layer (123).

[0028] The oxide semiconductor (113) is formed on the conductive film (112) of the working electrode (110), and it consists of porous metals and performs a function of adsorbing a dye and transferring electrons that are generated from the dye by light to the conductive film.

[0029] The oxide semiconductor (113) may be selected from the group consisting of known materials such as titanium dioxide (TiO.sub.2), tin dioxide (SnO.sub.2), zinc oxide (ZnO), and the like, and combinations thereof.

[0030] The dye (114) is bonded with the oxide semiconductor (113) and absorbs light to produce electrons.

[0031] The dye (114) is not specifically limited in terms of the constructional materials, but any known dyes may be used, and specifically, an organic dye or a ruthenium-based dye may be used.

[0032] The catalyst layer (123) is formed on the conductive film (122) of the counter electrode (120), and performs a function of an electron donor that donates electrons to the electrolyte. As the catalyst layer (123), platinum (Pt), a carbon-based material, and the like may be used, and specifically, platinum (Pt) may be used.

[0033] The electrolyte solution (130) exists in a void between the working electrode (110) and the counter electrode (120), and performs a function of reducing the dye of the working electrode again through the counter electrode, after electrons generated from the dye flow to an external conducting wire through the working electrode. As the electrolyte solution, any electrolyte known to be used in a dye-sensitized solar cell may be used, and specifically, imidazole-based compounds and iodine may be used. Specifically, the electrolyte solution (130) may consist of a solution of I.sub.3.sup./I.sup. in which 0.70 M of 1-methyl-3-propyl-immidazolium iodide, 0.10 M of Lit, 40 mM of 12 (iodine), and 0.5 M of 4-tert-butylpyridine are dissolved in 3-methoxypropionitrile, but is not limited thereto.

[0034] The dye-sensitized solar cell according to one embodiment of the present invention includes the membrane (140) that covers at least a part of dye (113) or counter electrode (120). Specifically, the membrane (140) may be formed so as to cover the counter electrode (120) or cover the dye (114) of the working electrode (110), the membrane (140) may be formed so as to cover the dye (114) and the oxide semiconductor (113), and the membrane may be formed so as to cover the dye (114), the oxide semiconductor (113), and the conductive film (112). Further, the membrane (140) may cover the dye (114), the oxide semiconductor (113), and the conductive film (112) of the working electrode (110), and simultaneously, an additional membrane (141) may be formed to cover the counter electrode (120).

[0035] The membrane (140) according to one embodiment of the present invention may include at least one of a condensation product of the following Chemical Formula 1 or a condensation product of the following Chemical Formula 2, and a condensation product of Chemical Formula 1 and Chemical Formula 2.

A(OR).sub.3[Chemical Formula 1]

(OR).sub.3A-XB(OR).sub.3[Chemical Formula 2]

[0036] Herein, A and B are each independently SiR, GeR, P, PR.sub.2, or Al, each R is independently hydrogen, deuterium, a linear or branched C.sub.1-30 alkyl group, or a C.sub.3-30 cycloalkyl group, and X is O or one of a C.sub.2-30 alkene, a C.sub.6-30 aryl, an alkoxy, an epoxy, an amine, an ester, an amide, a carbonyl, an ether, a thioether, a thiophene, a furan, and a cyclohexyl.

[0037] The membrane (140) may include silane compounds or phosphorus compounds, and specifically, one or more selected from the group consisting of isooctyltrimethoxysilane, acrylate and methacrylate functional silanes, aldehyde functional silanes, amino functional silanes, cyclic azasilanes, water-borne aminoalkyl silsesquioxane oligomers, anhydride functional silanes, azide functional silanes, carboxylate, phosphonate and sulfonate functional silanes, epoxy functional silanes, ester functional silanes, halogen functional silanes, hydroxyl functional silanes, isocyanate and masked isocyanate functional silanes, phosphine and phosphate functional silanes, sulfur functional silanes, vinyl and olefin functional silanes, multi-functional and polymeric silanes, UV active and fluorescent silanes, chiral silanes, biomolecular probes, trihydrosilanes, dipodal silyl hydrides, dipodal silanesnon-functional, and organosilane-modified silica nanoparticles may be used.

[0038] More specifically, the membrane (140) may consist of the following compounds, but is not limited thereto.

##STR00001## ##STR00002##

[0039] The membrane (140) according to one embodiment of the present invention is a semi-permeable membrane through which dye does not pass, but through which electrolyte elements (I.sup., I.sub.3.sup., etc.) do pass. Thus, the membrane (140) may be formed on the surface of a working electrode to prevent the dye (114) bonded to oxide semiconductor (113) of the working electrode (110) from being separated to decrease a fill factor, and it may be formed on the surface of a counter electrode to prevent the dye (114) that is separated from the working electrode (110) and moves around the electrolyte solution (130) from being bonded to the counter electrode to decrease a fill factor.

[0040] The membrane (140) may consist of at least one molecular layer, and the thickness of the membrane (140) may be controlled according to the molecular size of a material constituting the molecular layer.

[0041] The membrane (140) may be formed with a thickness of 0.1 to 1000 , and specifically, it may be formed with a thickness of 0.1 to 500 .

[0042] It was confirmed that if the membrane (140) is formed with a thickness of the above range, the effect of preventing dye separation, and the transparency, are excellent.

[0043] A dye-sensitized solar cell according to one embodiment of the present invention includes: a working electrode; a counter electrode; an electrolyte solution; and a membrane covering the surface of the working electrode, the surface of the counter electrode, or both surfaces of the working electrode and the counter electrode.

[0044] The dye-sensitized solar cell (100) including the membrane (140) according to one embodiment of the present invention can remarkably improve energy conversion efficiency by preventing an electron loss passage that may be generated while electrons produced by light are transferred to the external circuit, preventing the separation of dye (114) due to hyperabsorption, and also preventing the separated dye (114) from being readsorbed to the counter electrode (120), thereby remarkably improving the reliability and efficiency of the dye-sensitized solar cell electrode.

[0045] Hereinafter, examples are presented for better understanding of the present invention, but these examples are presented only as illustrations of the present invention and the scope of the present invention is not limited thereby.

[Example 1] Preparation of a Dye-Sensitized Solar Cell

[0046] A dye-sensitized solar cell including a working electrode on which a membrane is formed, as shown in FIG. 2, was prepared by a common preparation process of a dye-sensitized solar cell, except that the surfaces of a working electrode, that is, the surface of a conductive substrate, the surface of an oxide semiconductor layer (TiO.sub.2) formed on the working electrode, and the surface of a dye adsorbed on the surface of the oxide semiconductor layer, were dipped in a solution including isooctyltrimethoxysilane.

[0047] Herein, the working electrode was treated with an isooctyltrimethoxysilane solution, after the dye was adsorbed.

[0048] The conditions were as follows.

[0049] On FTO glass, a DTY5 photoelectrode paste (8 m, Dongjin Semichem Co., Ltd., Korea) was coated by a doctor blade method. The paste on the photoelectrode was calcined at 450 C. for 30 minutes to form a TiO.sub.2 thin film layer with a thickness of 8 m.

[0050] The calcined thin film layer was immersed in a dye solution in which 0.5 mM of Z907 dye was dissolved in an ethanol solvent, at room temperature for 20 hours. The TiO.sub.2 thin film coated with the dye was rinsed with ethanol, and immersed in an isooctyltrimethoxysilane solution for 30 minutes. The TiO.sub.2 thin film on which a silane membrane was formed was rinsed again with ethanol, and thereafter, a solar cell was manufactured according to a common solar cell manufacturing method.

[0051] Herein, as a redox electrolyte solution used in a solar cell, a solution in which 1.0 M of 1,3-dimethyl imidazolium iodide, 30 mM of iodine, 50 mM of LiI, 0.1 M of guanidinium thiocyanate, and 0.5 M of t-butylpyridine were dissolved in mixed solvents of valeronitrile and acetonitrile at a volume ratio of 15:85 was used.

[Example 2] Preparation of a Dye-Sensitized Solar Cell

[0052] A dye-sensitized solar cell including a counter electrode on which a membrane is formed, as shown in FIG. 3, was prepared by a common preparation process of a dye-sensitized solar cell, except that the surface of a counter electrode was dipped in a solution including isooctyltrimethoxysilane.

[0053] Herein, the counter electrode was treated with an isooctyltrimethoxysilane solution, after platinum was formed.

[0054] The conditions were as follows.

[0055] On FTO glass, a DTY5 photoelectrode paste (8 m, Dongjin Semichem Co., Ltd., Korea) was coated by a doctor blade method. The paste on the photoelectrode was calcined at 450 C. for 30 minutes to form a TiO.sub.2 thin film layer with a thickness of 8 m.

[0056] The calcined thin film layer was immersed in a dye solution in which 0.2 mM of D35 was dissolved in mixed solvents of acetonitrile and t-butyl alcohol at a volume ratio of 1:1, at room temperature for 20 hours. The TiO.sub.2 thin film coated with the dye was rinsed with ethanol to prepare a working electrode.

[0057] In order to prepare a counter electrode, a solution of 7 mM HPtCl.sub.6 was dripped on a FTO glass, and then calcined at 450 C. for 20 minutes to form a catalyst layer. The catalyst layer was immersed in an isooctyltrimethoxysilane solution for 30 minutes, then rinsed with ethanol, and thereafter, a solar cell was manufactured according to a common solar cell manufacturing method.

[Comparative Example 1] Preparation of a Dye-Sensitized Solar Cell

[0058] A dye-sensitized solar cell was prepared by the same method as Example 1, except that a membrane was not formed on either a working electrode or a counter electrode.

[Comparative Example 2] Preparation of a Dye-Sensitized Solar Cell

[0059] A dye-sensitized solar cell was prepared by the same method as Example 2, except that a membrane was not formed on either a working electrode or a counter electrode.

[Experiment 1] Comparison of the Properties of Dye-Sensitized Solar Cells

[0060] In order to evaluate the performance of a dye-sensitized solar cell, the properties (open circuit voltage (Voc), current density (Jsc), fill factor (FF), and photo conversion efficiency ()) of the dye-sensitized solar cells prepared in Example 1 and Comparative Example 1 were measured and are shown in the following Table 1 and FIG. 5.

TABLE-US-00001 TABLE 1 Voc (V) Jsc (mA/cm.sup.2) FF (%) (%) Example 1 0.760 10.37 73.52 5.79 Comparative 0.729 10.05 76.40 5.59 Example 1

[0061] As shown in Table 1, it was confirmed that when a membrane was formed on all the surfaces of a working electrode including the surface of a oxide semiconductor layer and the surface of the dye, the recombination of electrons was prevented, and thus the open circuit voltage was increased and the separation of dye was prevented, and thus, the current density was improved and the efficiency of a cell was generally increased.

[Experiment 2] Comparison of the Properties of Dye-Sensitized Solar Cells

[0062] In order to evaluate the reliability of a dye-sensitized solar cell, the properties (open circuit voltage (Voc), current density (Jsc), fill factor (FF), and photo conversion efficiency ()) of the dye-sensitized solar cells prepared in Example 1 and Comparative Example 1 were measured and are shown in the following Table 2 and FIG. 6.

TABLE-US-00002 TABLE 2 Voc (V) Jsc (mA/cm.sup.2) FF (%) (%) Example 2 0.663 8.87 66.75 3.92 Comparative 0.638 8.89 49.30 2.80 Example 2

[0063] As shown in Table 2, it was confirmed that when a membrane was formed on the surface of a counter electrode, the dye separated from a working electrode was prevented from being readsorbed to a counter electrode, and thus the open circuit voltage was increased and a fill factor was significantly improved, and the reliability and efficiency of a cell were generally increased.

[Experiment 3] Comparison of the Reliabilities of Dye-Sensitized Solar Cells

[0064] When storing at 60 C., FF changes were compared, and are shown in Table 3, (without a membrane) and Table 4 (with a membrane).

TABLE-US-00003 TABLE 3 Jsc Time (h) Voc (V) Isc (mA) (mA/cm.sup.2) FF (%) Eff. (%) 0 8.6154 501.0793 10.6431 49.7377 2.50107 15 8.6879 478.3682 10.1608 48.9334 2.368888 48 8.6603 488.619 10.3785 42.3034 2.08516 96 8.6257 475.0865 10.091 36.701 1.751874 168 8.6417 443.0722 9.411 31.342 1.397842

TABLE-US-00004 TABLE 4 Jsc Time (h) Voc (V) Isc (mA) (mA/cm.sup.2) FF (%) Eff. (%) 0 8.7035 491.7924 10.4459 49.9176 2.4888 15 8.7367 468.7227 9.9559 49.6609 2.3689 48 8.7806 491.1402 10.432 49.1221 2.4676 96 8.7349 483.3442 10.2664 49.0793 2.4137 168 8.6903 486.6368 10.3364 49.5094 2.4389 264 8.6169 496.9152 10.5547 48.8938 2.4387 528 8.5027 502.2829 10.6687 48.6653 2.421 768 8.435 493.9712 10.4922 48.6412 2.3608 1032 8.4154 501.0793 10.6431 48.185 2.3668

[0065] A dye-sensitized solar cell including a counter electrode on which a membrane is formed, as shown in FIG. 3, was prepared by a common preparation process of a dye-sensitized solar cell, except that the surface of the counter electrode was dipped in a solution including isooctyltrimethoxysilane.

[0066] Herein, the counter electrode was treated with an isooctyltrimethoxysilane solution, after platinum was formed.

[0067] The conditions were as follows.

[0068] On FTO glass, a DTY5 photoelectrode paste (8 m, Dongjin Semichem Co., Ltd., Korea) was coated by a screen printing method. The paste on the photoelectrode was calcined at 450 C. for 30 minutes to form a TiO.sub.2 thin film layer with a thickness of 4 m.

[0069] The calcined thin film layer was immersed in a dye solution in which 0.2 mM of D35 was dissolved in mixed solvents of acetonitrile and t-butyl alcohol at a volume ratio of 1:1, at room temperature for 20 hours. The TiO.sub.2 thin film coated with the dye was rinsed with ethanol to prepare a working electrode.

[0070] In order to prepare a counter electrode, a solution of 7 mM HPtCl.sub.6 was dripped on FTO glass, and then calcined at 450 C. for 20 minutes to form a catalyst layer. The catalyst layer was immersed in an isooctyltrimethoxysilane solution for 30 minutes, then rinsed with ethanol, and thereafter, a solar cell was manufactured according to a common solar cell manufacturing method.

[0071] The dye-sensitized solar cell module including a counter electrode treated with a membrane according to the present invention exhibited excellent effects, particularly in terms of FF, compared to a dye-sensitized solar cell module that was not treated with a membrane, and even after about 1000 hours, it maintained stable efficiency within 5%.