GLASS/QUARTZ COMPOSITE SURFACE

Abstract

A glass/quartz composite structure comprises quartz grit (and/or nan-glass crystals), quartz powder and glass grit wherein the glass grit is in an amount greater than any other single material by weight of the composite structure (e.g. a combined weight of the quartz grit, quartz powder, glass grit, resin, and coupling agent). Natural stone components, which may include the quartz grit and quartz powder, may be in an amount greater than 30% by weight of the composite structure. The structure may be formed into a 1.2-1.5 cm thick slab for countertops using standard cabinet perimeter support. The slab may be made by mixing the quartz grit, quartz powder, glass grit, and binding resin, pouring the mixture in a mold, and compacting the mixture in the mold. Specific natural mineral components, decorative chips, and/or wet mixture pieces may be added to the composite structure to provide aesthetics of specific natural stones.

Claims

1. A glass/quartz composite structure comprising: glass grit in an amount greater than any other single material by weight of the composite structure; nano-glass crystals in an amount up to 15% by weight of the composite structure to provide increased hardness and scratch resistance; quartz powder in an amount 30-35% by weight of the composite structure; and a binding resin.

2. The glass/quartz composite structure of claim 1, further comprising a silane coupling agent.

3. The glass/quartz composite structure of claim 2, wherein the silane coupling agent is in an amount 1.0-2 percent by weight of the composite structure.

4. The glass/quartz composite structure of claim 2, wherein the binding resin is in an amount 10-14 percent by weight of the composite structure.

5. The glass/quartz composite structure of claim 1, wherein the glass grit comprises cube-shaped glass grit.

6. The glass/quartz composite structure of claim 5, wherein the cube-shaped glass grit is within the range of 100 microns to 650 microns.

7. The glass/quartz composite structure of claim 5, wherein the glass grit comprises cube and conical-shaped glass grit.

8. The glass/quartz composite structure of claim 1, wherein at least 98% of the quartz powder is sized to pass through a 325 mesh sieve.

9. The glass/quartz composite structure of claim 1, wherein the glass grit is sized to pass through a sieve ranging from 8 mesh to 120 mesh.

10. The glass/quartz composite structure of claim 1, wherein the glass grit comprises soda-lime-silica glass.

11. The glass/quartz composite structure of claim 1, wherein the binding resin comprises a polyester resin.

12. The glass/quartz composite structure of claim 1, further comprising: feldspar grit to provide aesthetics of concretes and limestones or other natural stones; and alumina powder to provide aesthetics of pure white marbles.

13. The glass/quartz composite structure of claim 1, wherein the nano-glass crystals are in an amount 5%-10% by weight of the composite structure.

14. A method of manufacturing a glass/quartz composite slab, the method comprising: mixing nano-glass crystals, quartz powder, glass grit, and a binding resin, the glass grit being in an amount greater than any other single material by weight of the composite slab; pouring the mixture in a mold; and compacting the mixture in the mold for 250-320 seconds.

15. The method of claim 14, further comprising heating the compacted mixture in an oven for up to 2.5 hours.

16. The method of claim 14, wherein said mixing includes: preparing a dry mix of the nano-glass crystals and the glass grit; mixing the binding resin with the dry mix to produce a wet mix; and mixing the quartz powder with the wet mix.

17. The method of claim 16, further comprising dispersing wet mixture pieces produced from the wet mix of a previously manufactured glass/quartz composite slab in the mold.

18. The method of claim 17, wherein the wet mix of the previously manufactured glass/quartz composite slab includes pigment.

19. The method of claim 14, further comprising mixing a silane coupling agent with the binding resin.

20. The method of claim 14, further comprising impact breaking glass aggregate in a vertical shaft impact crusher to produce the glass grit.

21. The method of claim 20, further comprising crushing the glass in a cone crusher prior to said impact breaking the glass in the vertical shaft impact crusher.

22. The method of claim 14, further comprising dispersing decorative chips of previously manufactured glass/quartz composite slabs on a surface of the mixture in the mold.

23. The method of claim 14, further comprising dispersing decorative chips of glass greater than one centimeter at their largest dimension on a surface of the mixture in the mold.

24. A method of mixing quartz and glass aggregates, the method comprising: preparing a dry mix of quartz grit and glass grit; mixing a binding resin with the dry mix to produce a wet mix; mixing a 400-800 mesh microparticle with the wet mix; and, thereafter, mixing quartz powder having a particle size larger than 400 mesh with the wet mix.

25. The method of claim 24, wherein said preparing includes: preparing a first dry mix of quartz grit and glass grit having a first particle size; adding a second dry mix of quartz grit and glass grit to the first dry mix, the second dry mix having a second particle size smaller than the first.

26. The method of claim 24, wherein at least 98% of the quartz powder is sized to pass through a 325-mesh sieve.

27. A method of manufacturing a glass/quartz composite slab, the method comprising: preparing a mixture of quartz grit, quartz powder, glass grit, a binding resin, and microparticles to fill a void volume between the quartz grit and glass grit and increase packing density, the microparticles being in an amount 2-6 percent by weight of the mixture; pouring the mixture in a mold; and compacting the mixture in the mold.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0030] These and other features and advantages of the various embodiments disclosed herein will be better understood with respect to the following description and drawings, in which like numbers refer to like parts throughout, and in which:

[0031] FIG. 1 is a flowchart outlining an exemplary methodology of forming a glass/quartz composite slab; and

[0032] FIG. 2 is a flowchart outlining an exemplary methodology of crushing quartz or glass aggregates.

DETAILED DESCRIPTION

[0033] The detailed description set forth below in connection with the appended drawings is intended as a description of certain embodiments of a glass/quartz composite structure, a slab formed therefrom, and a related method of forming the same and is not intended to represent the only forms that may be developed or utilized. The description sets forth the various structure and/or functions in connection with the illustrated embodiments, but it is to be understood, however, that the same or equivalent structure and/or functions may be accomplished by different embodiments that are also intended to be encompassed within the scope of the present disclosure. It is further understood that the use of relational terms such as first and second, and the like are used solely to distinguish one entity from another without necessarily requiring or implying any actual such relationship or order between such entities.

[0034] The present disclosure generally relates to a method of forming a structure from glass and quartz. The quartz used in the glass/quartz composite structure may be primarily filler where quartz is ground into a powder and becomes part of a composition of resin/filler paste to achieve proper compaction of aggregates. Unit-weight may measure the volume that the graded aggregate quartz and glass and the voids between them will occupy in the resin/filler paste.

[0035] The glass grit in combination with the coupling agent absorbs more resin and improves the binding and strength of the structure. The highly compacted mix may contain more glass than quartz, 10-14% resin, and 1.0-2% coupling agent and 2-6% microparticles. For example, the glass grit may be in an amount greater than any other single material by weight of the composite structure (e.g. a combined weight of the quartz grit, quartz powder, glass grit, resin, and coupling agent), the coupling agent may be in an amount of 1.0-2% by weight of the composite structure, and the binding resin may be in an amount of 10-14% by weight of the composite structure. In the process, the resin/filler paste tends to bond more effectively with rough-surfaced aggregates. In this case, glass and quartz provide more area to which the filler/resin paste can bond. Furthermore, by incorporating glass grit, which has the property of having more micro-porosity, desired aesthetic attributes may be achieved while increasing the strength of the glass/quartz composite structure as needed for thin format slabs for use in countertops. By incorporating 2-6% microparticles to fill the voids between the larger particles, it increases the packing density and reduces the void volume in the mix. The thinner format structures in combination with more translucent glass raw materials enable aesthetic and design advantages of premium natural quartzites that add to the value of the countertop designs. Moreover, glass grit with properties which add to the countertop flex and impact strength and translucency and can be found locally may reduce the cost for raw materials with premium quartz designs and enable thinner structures which consume less raw materials.

[0036] Previous examples of various aspects of such a process were shown in Applicant's provisional patent application No. 62/692,215, the entirety of which is incorporated herein by reference as noted above. In that application, various examples were given as to the size of the quartz and glass grit which could be used to form the glass/quartz composite structure. This disclosure provides further examples of such possible combinations and further discloses aspects of the resultant structures.

[0037] Referring to FIG. 1, the process of forming the glass/quartz composite structure may generally include mixing quartz grit 12 (output of quartz processing 24), glass grit 16 (output of glass processing 30) and inorganic pigment powder 17 to form a dry mixture 18. The total amount of glass grit 16 is preferably more than 50 percent by weight of the quartz/glass aggregate which includes the quartz grit 12 and filler quartz powder 14. The total amount of quartz 20 may be minimized without compromising aesthetic or structural characteristics if the packing density is maintained through the use of conical and cubic shaped glass grit 12 within the range of 100 microns to 1200 microns (16 mesh to 120 mesh) and filler quartz powder 14. An exemplary standard which applies to quartz surfaces and which may be met by the glass/quartz composite structures made by the methodology described herein may include the IAPMO IGC 340-2017 standard.

[0038] With regard to obtaining desired sizes of the filler quartz 14, a desired high purity filler quartz 14 will have a median particle size D50 between 13 to 14 microns and over 95% will pass through a sieve size 325 mesh (45 microns). The filler quartz 14 may be integrated in the wet mixing process step 36. Completely inert and pH neutral, the filler quartz 14 will not alter or initiate when incorporated with the wet mix (e.g. containing a polyester resin 38). The filler quartz 14, having low surface area and hardness, may offer minimal absorption for high loading and stiffening for thermoset high-performance polyester resin systems.

[0039] In one exemplary process, the quartz grit 12, an inorganic or organic pigment color powder 17, and glass grit 16 are added to produce the dry mixture 18 before the step of producing the wet mixture 36, where the resin 38 & coupling agent 40 are then mixed with the quartz grit and glass grit 16. As a final step of the wet mixture 36 process, the filler quartz 14 may then be added and mixed perfectly until the wet mixture reaches a complete homogeneity of wetness as is desirable for the mold process 42. The filler quartz 14 may form 30-35% by weight of the composite structure.

[0040] More specifically, the steps of producing the dry mixture 18 and subsequent wet mixture 36 may proceed as follows and may be performed using a Fournier mixer, for example. First, to produce the dry mixture 18, one or more sizes of quartz grit 12 and glass grit 16 may be added, preferably beginning with larger sizes grit and proceeding to smaller size grit. For example, in a Step 1, a 40-70 mesh grit may be added to the mix at a feeding speed of 8 Hz, and thereafter, in a Step 1A, a 70-120 mesh grit may be mixed in at a feeding speed of 8 Hz. At each such stage, mixing may be performed for 2 minutes at a mixing speed may of 15 to 20 Hz, for example. The dry mixing may allow homogenization of the different particle sizes of mineral aggregates. These steps (Steps 1 and 1A) may also make it possible to ensure good dispersion of dry powder colors (e.g., pigment color powder 17), making it possible to determine the color of the product.

[0041] After Steps 1 and 1A, the wet mixture 36 may be produced. For example, in a Step 2, a Polyester resin (PER) may be mixed in so that each of the quartz/glass aggregates is well coated with resin over its entire microscopic surface, allowing optimum adhesion to be obtained during the subsequent Steps 3 and 4. The wet mixing step may have a feeding speed of 8 Hz and a mixing speed of 15-20 Hz for 2 minutes, for example. The process may then continue with a Step 3 of mixing in microparticle filler (e.g., alumina, typically 400 to 800 mesh), which may be fed at 8 Hz and mixed at 15-20 Hz for 1 minute, for example. This step may fill the microcavities of the mineral aggregate crystals used in the recipe, facilitating ultra-compaction during the later pressing cycle. With Step 3 serving as a preliminary step before the addition of 45-micron powder, the process may continue with Step 4, in which 45-micron filler (e.g., filler quartz 14) is mixed in, for example, at a feeding speed of 8 Hz and mixing speed of 15-20 Hz for 1 minute. Step 4 may be the last step in the sequence of mixing the different ingredients of the product. The mixture and its homogenization with the PER make it possible to eliminate any form of voids during the subsequent pressing of the mixture by vibro-compaction under vacuum. The mixing may provide motivation for the aggregate to migrate and align into a closely packed environment, with the smaller alumina or other microparticles filling the void between the glass and quartz in the mix. The vibrator force combined with an ultra-homogenization of the ingredients allows the product to obtain high performance physical properties once the polymerization is complete. Lastly, in a Step 5, a final mixing stage may make it possible to standardize the wetness of the mixture before the pressing stage. The high velocity of the mixer at this stage (e.g., 35 Hz for 1 minute, followed by inverted rotation mixing at 45 Hz for 1 minute) ensures that the powder microparticles are well bound to the mineral aggregate crystals.

[0042] As noted above, the dry mixture 18 may be formed by mixing the glass grit 16, the quartz grit 12, and inorganic or organic pigment color powder 17 to form the desired dry mixture 18 before the step of preparing the wet mixture 36. The wet mixture 36 may be formed by adding the aforementioned resin 38, along with a coupling agent 40, to the dry mixture 18. The resin 38 used in forming the quartz slab 10 may be polyester orthophthalic unsaturated resin, although other resins known in the art may also be used without departing from the spirit and scope of the present disclosure.

[0043] The coupling agent 40 may be a silane coupling agent and may be 1.0-2 percent by weight of the composite structure. The coupling agent 40 binds the inorganic materials ((filler quartz 14, quartz grit 12, glass grit 16 and organic matter (resin 38)) and increases the flexural and impact strength of the quartz slab 10 or other end product. An exemplary silane coupling agent is XIAMETER®OFS-6030 silane, which may be used to improve adhesive of free radical cured resins, although other coupling agents 40 known in the art may also be used without departing from the spirit and scope of the present disclosure.

[0044] After pouring the wet mixture 36 in a mold 42 having a cavity in the size and shape corresponding to a rough out of the final quartz/glass blend slab 10 or other product, the wet mixture 36 may be compacted and vibrated under vacuum in the mold 42 to remove entrained air from the wet mixture 36. Aggregates have low internal friction and move closer together within the layer under less compaction energy. This is one of the features to obtain excellent physical properties as described below. Cubic and conical shape glass aggregates have low internal friction and move close together within the aggregate mix to become closely packed. Alternatively, or in addition, the structure may be placed in an oven 44 at 85-90 degrees C. to initiate the polymerization of the resin/filler paste in order for the quartz/glass blend slab 10 to reach optimum physical properties. The end product of the above steps is an unfinished slab 46, which can then be calibrated (e.g. ground) and polished to produce the finished quartz/glass blend slab 10.

[0045] It should be noted that the 400-800 mesh microparticle is smaller than the filler quartz powder (e.g., 325 mesh powder). The microparticle fills the voids between the grit and some of the microporosity in the glass so that there is less void volume. The grit becomes more “highly compacted”. This also reduces the resin needed and improves the efficiency of the vibration compaction vacuum process. 325-mesh powder (45-micron powder) may be mixed with the resin to form the wet mix. The resin/powder mix binds the particles when the resin polymerizes during the oven heating process. By using the 400-800 mesh microparticles with the resin, these microparticles help to fill the voids after the dry mixing of the aggregate. The quartz powder is then added to the wet mix and it flows through the aggregate in the final mixing. The wet mix is then pressed & vibrated to fill the voids and the air in remaining voids is removed with the vacuum.

[0046] As noted above, specific natural mineral components (e.g. quartz, feldspar, bauxite, nano-glass, etc.) may be added in order to provide the aesthetics of specific natural stones. Such mineral components may be added to the wet mixture 36 for example, either before or after the wet mixture 36 is placed in the mold 42. It is also contemplated that such mineral components may be added to the dry mixture 18. The natural mineral components, which may include the quartz grit 12 and filler quartz powder 14, may be greater than 30% by weight of the composite structure, and the resulting finished quartz slab 10 may constitute agglomerated stone or a crystalline glass slab for purposes of U.S. Customs and Border Protection classification (depending on whether an all-glass aggregate plus filler quartz powder or a quartz-glass aggregate is used).

[0047] In order to produce decorative veins and other aesthetic features in the finished quartz slab 10, pieces of previously manufactured finished quartz slabs 10 may be fed back into the manufacturing process as decorative chips 48. For example, unused pieces derived from scraps and/or discarded slabs 10 may be crushed and formed into decorative chips 48 that may be about 1 centimeter or greater in length (e.g. 1.0-2.0 cm). With the wet mixture 36 having been poured in the mold 42, the decorative chips 48 may then be dispersed (e.g. by hand) on the surface of the wet mixture 36 to form veins or other arrangements of the decorative chips 48. The dispersing the decorative chips 48, the wet mixture 36 may be compacted and vibrated under vacuum in the mold 42 to remove air from the wet mixture 36 and/or the structure may be placed in an oven 44 as described above. Compaction may be achieved, for example, with the use of a vacuum vibration press (“VVP”) as described in U.S. Pat. No. 9,221,190, the entire disclosure of which is hereby wholly incorporated by reference. The resulting unfinished slab 46 may then be calibrated (e.g. ground) and polished to produce the finished quartz/glass blend slab 10 with the arrangement of decorative chips 48 on the surface thereof. In this way, the decorative chips 48 may be used to simulate the appearance of calcite crystals and other mineral deposits in natural stone in the finished quartz slab 10.

[0048] Instead of or in addition to the decorative chips 48 being derived from previously finished quartz slabs 10, the decorative chips 48 may be glass chips derived from product glass 28. By dispersing decorative chips 48 of glass that are greater than one centimeter (e.g. 1.0-2.0 cm) at their largest dimension on the surface of the wet mixture 36 while it is in the mold 42, the finished quartz slab 10 may be made in a way that results in a categorization as an agglomerated stone slab or a glass slab for purposes of U.S. Customs and Border Protection (depending if the composite grit is made with all glass components). It is contemplated that the finished slabs 10 may have these features as well. For example, a sufficiently large quantity of crushed glass 16 that is 0.2 mm or larger and therefore visible may be produced by a 70 mesh screen and added to the dry mixture 18 as described above.

[0049] Alternatively, or in addition, wet mixture pieces (e.g. balls) may be produced from the majority glass wet mix 36, including pigment additives 17, to be used to decorate subsequently produced wet mixtures 36 in the mold 42. For example, as shown in FIG. 1, wet mixture balls 37 may be removed from the wet mixture 36 and thereafter incorporated into the wet mixture 36 of a batch having different color or other properties.

[0050] The decorative chips 48 and/or wet mixture pieces 37 (e.g. greater than 1 cm in width) may be used to expand the design flexibility for providing the aesthetics of natural stones. Decorative chips 48 produced from slab pieces may be placed in the slab veins to simulate calcite crystals in white marble designs. In some cases, the slab veins may be produced by a stamp or roller prior to placing the decorative chips 48. Glass chips of greater than 1 cm in width crushed from glass trim may be used to simulate quartz crystals in large grain designs. Majority glass wet mixture pieces 37 (e.g. balls) produced from the wet mixture raw materials and pigment powder may be dispersed on the surface of the wet mixture to provide decorative accent chips in concrete and limestone designs. It is also contemplated that the wet mixture pieces 37 may be placed in the bottom of the mold 42 prior to filling the mold 42 with the wet mixture 36. As the wet mixture 36 is compacted and vibrated in the mold 42, the wet mixture pieces 37 may spread out in the wet mixture 36 without mixing in completely, thus producing the desired localized design elements.

[0051] The final quartz/glass blend slab 10 may have a thickness of, for example, 1.2-1.5 cm. Such a thickness may provide a number of properties. For example, a 1.2 cm thick quartz/glass blend slab 10 may have a flex strength greater than 120 MPA (dry) per the ASTM C880 standard. The ASTM C880 test method covers a procedure for determining the flexural strength of stone by use of a simple beam using quarter-point loading. When testing in a dry condition, specimens are placed in an oven for at least 48 hours at 140 degrees Fahrenheit until three successive hourly weight measurements give the same value. Alternatively, specimens can be tested in a wet condition by immersing the specimens in water for 48 hours at room temperature. Upon completion of conditioning, each specimen is placed onto the testing machine and the quarter point loading blocks are brought into contact with the specimen. A load is applied at a constant stress rate of 600 psi/min until failure is observed and the maximum load is recorded.

[0052] The 1.2 cm thick quartz/glass blend slab 10 may have an impact resistance of greater than 40 J/m on an ASTM D256 standard Izod impact test. The ASTM D256 test is a pendulum impact test that indicates the energy to break standard test specimens of specified size under stipulated parameters of specimen mounting (using an un-notch sample) and pendulum velocity-at-impact.

[0053] The 1.2 cm thick quartz/glass blend slab 10 may have a breaking strength of greater than 1300 lbf. in an ASTM C648 test and a 2 cm thick quartz/glass blend slab 10 may have a breaking strength of greater than 4100 lbf. The ASTM C648 test method provides means for establishing whether or not a lot of ceramic tile meets the strength requirements which may appear in tile specifications. Tile strength is the force in pounds-force (or newtons), as read from a pressure gauge, necessary to cause the tile to break. In the ASTM C648 test, the tile is loaded into a three-point support and the load applicator is positioned directly in the center of the tile. Force is applied to the test specimen at a constant rate until the tile breaks into two or more pieces.

[0054] In addition, the finished quartz/glass blend slab 10 may have various qualitative features. For example, the finished quartz/glass blend slab 10 may be translucent, either through the veining, or through other portions of the slab. The translucency allows for at least some portion of light from a light source placed on one side of the quartz/glass blend slab 10 to be visible on the other side. This property may be utilized in installations where lighting is placed under a slab being used as a countertop. The light then shows through to a top of the countertop, where it is visible to a user.

[0055] Obtaining good flex and impact strength for the glass/quartz composite structure requires a highly compacted 1.2-1.5 cm slab 10 or other product where the glass grit shapes interlock well with the quartz shapes and are bound together with the resin 38. The silane or other coupling agent 40 helps the resin 38 to link the organic material with the inorganic material. Because the glass has more micro-porosity than quartz aggregates, it allows some absorption of the resin/filler paste into the glass. In the recipe preparation, unit-weight preferably measures the volume that the graded aggregate quartz and glass and the voids between them will occupy in the resin/filler paste. A technique of void volume calculation may be used to perfectly balance the % volume of aggregates and % volume of resin/filler paste used. The impact crushing of the glass to produce the desired cubic and/or conical shapes is highly important in forming the tight interlock achieved with the compacting press. In the process, the resin/filler paste tends to bond more effectively with rough-surfaced aggregates such as glass, and rough-surfaced particles provide more area to which the filler/resin paste can bond. The vibration during compaction allows for the resin/filler paste to migrate throughout the structure. The polymerization of the resin after compaction binds the shapes and forms an interlocked structure which is then polished into a finished slab 10 for use in countertops.

[0056] Glass impacting and crushing to form the desired shapes for the tight interlocking of the structure may achieve the necessary flex and impact strength for 1.2-1.5 cm structures to be used for countertops and achieve the weight and cost advantages from the use of less raw materials. High purity glass grit allows to obtain very translucent composite slabs with better flex and impact strength than other translucent product available in the market such as natural onyx.

[0057] Preferably, the aggregates have a certain level of rough surface, also called micro-porosity of surface, which may be measured and controlled by the execution of Brunauer-Emmett-Teller (BET) Surface Area Analysis and Barrett-Joyner-Halenda (BJH) Pore Size and Volume Analysis.

[0058] Setting the correct voids volume ratio of the filler/resin paste may be executed using the test method ASTM C29/C29M-09 Standard Test Method for Bulk Density (Unit Weight) and Voids in Aggregate.

[0059] Technical data of a finished quartz/glass blend slab 10 made in accordance with the methodology described herein is shown in the table below.

TABLE-US-00001 UNIT OF AVERAGE CHARACTER- TEST MEASURE- RANGE OF ISTICS METHOD MENT VALUES Density ASTM C97 g/cm.sup.3 2.3-2.4 Flexural Strength ASTM C880 MPa 100-140 (Dry) (Modules Rupture) 120-156 (Wet) Water Absorption ASTM C97 %    0.03 Compressive ASTM C170 MPa 143-150 (Dry) Strength 126-146 (Wet) Coefficient of ASTM C531 Inch/° F. 2.3 × 10.sup.−5 Thermal Expansion Barcol Hardness ASTM D2583 Index (0-100) 87 Abrasion Resistance ASTM C501 Wear Index 95 Minimum Gloss Gloss Meter % Incident light 45% Minimum reflected at 60° Breaking Strength ASTM C648 lbf 4160  Impact Resistance ASTM D256 J/M 40-61 Stain Resistance ANSI Z124 Pass/Fail Pass Wear & Cleanability ANSI Z124 Pass/Fail Pass Boiling Water NEMA LD No Effect Resistance 3-3.5 Color Fastness ANSI Z124 Pass/Fail Pass Moderate Chemical ANSI Z124 Pass/Fail Pass Resistance

[0060] Aspects of the present disclosure which address the formation of the desired grit sizes and shapes from the vertical shaft impactor will be discussed in more detail below with reference to FIG. 2.

[0061] In order to obtain quartz and glass aggregates having the desired shape, e.g. cubic, angular, or round shapes, a two-phase crushing process may be used involving two different types of crushers. As a first step, once the glass 50 or quartz 51 aggregates are transformed to a particle size <4 inches (<100 mm), the glass 50 or quartz 51 aggregates are introduced into a cone or jaw crusher 60 in order to transform the glass 50 or quartz 51 aggregates to a particle size <50 mm. In the case of quartz aggregates 51, a preliminary control step of manual selection 62 of the quartz may be executed to remove quartz impurities and contamination prior to transferring the quartz to the cone or jaw crusher 60. After crushing the glass 50 or quartz 51 aggregates in the cone or jaw crusher 60, the resulting particle size glass 50 or quartz 51 aggregates are transferred to a dryer unit 63 before being introduced into a VSI (Vertical Shaft Impact) crusher 64 for a second crushing step.

[0062] The VSI crusher 64 can provide cube shaped aggregate with less dust than a ball mill crusher. The VSI crusher 64 provides for the particles to impact themselves and produces cube shaped particles with less internal cracks and fissures and with less waste than the ball mill crusher. The ball mill crusher produces spherical and round particles but generates more dust and the potential for cracks and fissures in the glass grit which may reduce the tensile strength of the glass grit. The air circulation within the VSI crusher 64 maintains a low level of fine dust produced, which may be less than 20% of the smallest sieved fraction for each particle size of glass 50 or quartz 51 aggregate. The VSI crusher 64 may then feed the desired particle size glass 50 or quartz 51 aggregates to a first magnetic separator stage 65 (of 3 magnetic separator stages 65, 71, 78) in order to remove any iron contaminants before the first 70 of two vibrating sieve stages 70, 76.

[0063] The first sieve stage 70 of the two vibrating sieve stages 70, 76 may produce particle size glass 50 or quartz 51 aggregates of 16-26 mesh 73 and 26-40 mesh 74. All the particle size glass 50 or quartz 51 aggregates larger than 16 mesh may recirculate 72 back to the VSI crusher 64 to repeat the second crushing step. The particle size glass 50 or quartz 51 aggregates that are not larger than 16 mesh may pass through the second magnetic separator stage 71 to eliminate any iron contaminants, and the particle size glass 50 or quartz 51 aggregates that are not smaller than 40 mesh may then be bagged in porous bags (e.g. superbags) according to their size (e.g. 16-26 mesh and 26-40 mesh), thus producing the product glass 28 or quartz 22 for use in the method of FIG. 1.

[0064] Meanwhile, the second sieve stage 76 of the two vibrating sieve stages 70, 76 may produce particle size glass 50 or quartz 51 aggregates of 40-70 mesh 79 and 70-120 mesh 80. At this stage, all the particle size glass 50 or quartz 51 aggregates larger than 40 mesh may recirculate 77 back to the VSI crusher 64 to repeat the second crushing step. The particle size glass 50 or quartz 51 aggregates that are not over 40 mesh may pass through the third and final magnetic separator stage 78 to make a final screen to eliminate any iron contaminants before being bagged in a porous bag (e.g. superbags) according to their size (e.g. 40-70 mesh and 70-120 mesh), thus producing the product glass 28 or quartz 22 for use in the method of FIG. 1.

[0065] Using the grit size and shapes of the glass aggregate in combination with quartz powder to produce the desired aesthetic will be described in more detail below.

[0066] The glass grit aggregate size in the range of 16-26 mesh, 26-40 mesh, 40-70 mesh and 70-120 mesh can be used to produce the desired aesthetic from a large grain design, medium grain, small grain and fine grain designs. The following are 2 examples of aggregate compositions used to produce desired grit (grain) sizes and aesthetics:

[0067] Large Grain: 8-16 mesh quartz (10%); 16-26 mesh glass (10%); 26-40 mesh glass (12%); 40-70 mesh glass (10.5%); 70-120 mesh glass (14%); 325 mesh quartz powder (30%); resin (10%); coupling and other agents (2%); 0.5-1.0% majority glass chips and/or pieces 4-8 mesh (some 1.0 cm wide)

[0068] Small Grain (pure white): 40-70 mesh glass (30%); 70-120 mesh glass (21%); 325 mesh quartz powder (32%); resin: (12.5%); coupling agents & pigments (2%); 2% aluminum trioxide powder; 0.25-0.5% majority glass chips and/or pieces 1.0-1.5 cm wide.

[0069] The recipe preparation considers unit-weight measures the volume that graded aggregate quartz, glass and the voids between them will occupy in resin/filler. The technique of Void Volume calculation may be used to perfectly balance the % volume of aggregates and % volume of resin/filler used while obtaining the desired aesthetic.

[0070] Having the desired shape of aggregate, the optimum packing using the Void Volume technique, and resin & coupling agents for binding allows for a highly compacted glass/quartz composite structure that provides superior strength in a finished surface using the mixing process described above.

[0071] The above description is given by way of example, and not limitation. Given the above disclosure, one skilled in the art could devise variations that are within the scope and spirit of the invention disclosed herein, including various ways of creating the dry mix. Further, the various features of the embodiments disclosed herein can be used alone, or in varying combinations with each other and are not intended to be limited to the specific combination described herein. Thus, the scope of the claims is not to be limited by the illustrated embodiments.