INSULATING LAYER-FORMING COMPOSITION AND THE USE THEREOF

Abstract

A composition forming an insulating layer is described, whereby a binder based on an alkoxysilane-functionalized polymer carries the alkoxy-functionalized silane group, containing water and an insulation layer-forming additive. The composition according to the invention results in a relatively high expansion rate, enabling coatings to be applied to achieve the layer thickness required for the respective fire resistance duration in a simple and rapid manner, whereby the layer thickness is reduced to a minimum but offers significant insulating effect. The composition according to the invention is particularly suitable for fire protection, especially for the coating of steel components, such as columns, beams, frame members, in order to increase the fire resistance duration.

Claims

1. A two-component system, comprising: an insulating layer-forming composition comprising (A) an alkoxysilane polymer which is terminated and/or has side groups along the polymer chain alkoxysilane groups of the general formula (I)
Si(R.sup.1).sub.m(OR.sup.2).sub.3-m(I), wherein R.sup.1 is a linear or branched C.sub.1-C.sub.16 alkyl radical, R.sup.2 is a linear or branched C.sub.1-C.sub.6 alkyl radical and m is an integer from 0 to 2, (B) 0.1 to 3 wt. % of water with respect to the polymer (A); and (C) a mixture comprising at least one dehydrogenation catalyst, at least one blowing agent and optionally at least one carbon source and/or at least one thermo-expandable compound, wherein components (A) and (C) are contained in a first component (I) and component (B) is contained in a second component (II), the first component (I) and the second component (II) are separated from each other to inhibit reaction, and wherein the alkoxysilane polymer contains at least two alkoxysilane groups and the content of alkoxy groups of the polymer is from 0.20 to 0.85 mmol/g.

2. The two-component system according to claim 1, wherein the polymer comprises a network selected from the group consisting of a polyether, polyester, polyetherester, polyamide, polyurethane, polyester urethane, polyether urethane, polyetherester urethane, polyamide urethane, polyurea, polyamine, polycarbonate, polyvinyl polyacrylate, polyolefin, polyisobutylene, polysulfide, rubber, neoprene, phenol resin, epoxy resin and melamine.

3. The two-component system according to claim 1, wherein the alkoxysilane polymer contains 2 to 8 alkoxy-functional silane groups.

4. The two-component system of claim 1, wherein the insulation-forming additive further comprises an ash crust stabilizer.

5. The two-component system according to claim 1, wherein the composition further contains at least one further ingredient, wherein the at least one further ingredient is a material selected from the group consisting of plasticizers, crosslinking agents, water scavengers, inorganic fillers and other additives.

6. A two-component system according to claim 1, wherein component (C) comprises at least one carbon source, at least one blowing agent and at least one dehydrogenation catalyst and these compounds are separated from the other components of the composition in order to inhibit reaction.

7. The two-component system according to claim 1, comprising as component (B) 0.6 to 2 wt. % of water with respect to the polymer (A).

8. A method of coating a substrate, comprising: combining said first component (I) and said second component (II) of said two-component system of claim 1 to form an insulating layer-forming composition; and coating said insulating layer-forming composition on a substrate.

9. The method of claim 8, wherein said substrate is a steel construction element.

10. The method of claim 8, wherein said substrate is a non-metallic component.

11. The method of claim 8, wherein said composition serves as a fire protection layer.

12. A coated substrate obtained by the method of claim 8.

13. A cured object obtained by mixing and curing the two-component system of claim 1.

14. A method of protecting a steel construction element from the effects of heat comprising mixing the two-component system according to claim 1 and applying to a surface of a steel construction element.

Description

DETAILED DESCRIPTION OF THE INVENTION

[0020] In order to better understand the invention, the following explanations of the terminology used herein are believed to be useful. For the purposes of the invention: [0021] chemical intumescence means the formation of a voluminous, insulating layer of ash crust through coordinated compounds which react with one another when exposed to heat; [0022] physical intumescence means the formation of a voluminous, insulating layer by the swelling of a compound without a chemical reaction taking place between two compounds, and that gives off gases when exposed to heat, whereby the volume of the compound increases to a multiple of the original volume; [0023] insulating layer forming means that, in event of fire, a solid microporous carbon foam is produced, so that the fine pore and thick foam layer so formed, the so-called ash crust, insulates a substrate against heat depending on the composition; [0024] Carbon source is an organic compound which leaves behind a carbon network by incomplete combustion and does not fully burn to produce carbon dioxide and water (carbonification); these compounds are also referred to as carbon network formers; [0025] acidifier means a compound that under the effect of heat above about 150 C., for example forms a non-volatile acid through decomposition, and thus acts as a catalyst for the carbonification; moreover, it can contribute to lowering the viscosity of the melt of the binder; and thus the term dehydrogenation catalyst is used synonymously; [0026] blowing agent is a compound that decomposes at an elevated temperature into inert, i.e. non-flammable gases, and, where appropriate, inflates the softening binder to form a foam (intumescence); this term is used synonymously with gas formers; [0027] ash crust stabilizer is a so-called network-forming compound which stabilizes the carbon network (ash crust) formed by the interaction of the carbon formation from the carbon source and the gas from the blowing agent or physical intumescence. The principle of operation is that they, in themselves, very soft resulting carbon layers are mechanically bonded by inorganic compounds. The addition of such an ash crust stabilizer contributes to a significant stabilization of the intumescent crust in the event of fire, as these additives increase the mechanical strength of the intumescent layer and/or prevent their dripping off.

[0028] According to the invention, the alkoxysilane-functional polymer comprises a backbone selected from the group consisting of a polyether, polyester, polyetherester, polyamide, polyurethane, polyester urethane, polyether urethane, polyether/ester urethane, polyamide urethane, polyurea, polyamine, polycarbonate, polyvinyl, polyacrylate, polyolefin such as polyethylene or polypropylene, polyisobutylene, polysulfide, rubber, neoprene, phenol resin, epoxy resin, melamine. The backbone may be linear or branched (linear backbone with side chains along the chain of the backbone) and includes terminating alkoxysilane groups, preferably at least two alkoxysilane groups, i.e. as end groups of a linear backbone, or as end groups of the linear backbone and end groups of the side groups.

[0029] The alkoxy silane has the general formula (I)

Si(R1)m(OR2)3-m(I),

[0030] whereby R.sup.1 is a linear or branched C.sub.1-C.sub.16-alkyl radical, preferably a methyl or ethyl radical, R.sup.2 is a linear or branched C.sub.1-C.sub.6-alkyl radical, preferably a methyl or ethyl radical, and m is an integer from 0 to 2 preferably 0 or 1. Most preferably, the at least two alkoxy silane groups are difunctional (m=1) or trifunctional (m=0) and the alkoxy group is a methoxy or ethoxy group.

[0031] Preferably, the alkoxysilane group, bound to the backbone, may itself act either as an electron donor or an atom via a group such as an additional further functional group (for example, XS, OR, NHR, NR.sub.2), whereby the two functional groups, i.e. the further functional group and the alkoxysilane group are connected to one another via a methylene bridge (XCH.sub.2Si(R.sup.1).sub.m(OR.sup.2).sub.3-m). In this way, an electron interaction (back-bonding) between the silicon atom and the electron donor is caused, whereby electron density is moved from the donor to the silicon atom, which leads to a weakening of the SiO bond, which in turn results in a greatly increased reactivity of the Si-alkoxy groups. This is the so-called a effect. Such compounds are also referred to as a silanes.

[0032] Most preferred is when the alkoxysilane polymers are polymers in which the backbone is terminated with a silane group via a urethane, such as dimethoxy-(methyl)silylmethylcarbamate-terminated polyether, diethoxy(methyl)silylmethyl-carbamate-terminated polyethers, trimethoxysilylmethylcarbamate-terminated polyethers, triethoxysilylmethylcarbamate-terminated polyether or mixtures thereof.

[0033] Examples of suitable polymers include silane-terminated polyether (e.g. Geniosil STP-E 10 and Geniosil STP-E 30 from Wacker Chemie AG) and silane-terminated polyurethanes (e.g. polymer ST61, polymer ST75 and polymer ST77 from Evonik Hanse, Desmoseal S XP 2458, Desmoseal S XP 2636, Desmoseal S XP 2749, Desmoseal S XP 2821 from Bayer, SPUR+*1050 mm, SPUR+*1015LM, SPUR+*3100HM, SPUR+*3200HM from Momentive).

[0034] Usually, these alkoxysilane-functional polymers have a content of the alkoxy groups of 0.20 to 1.0 mmol/g, preferably 0.2 to 0.85 mmol/g, more preferably 0.25 to 0.80 mmol/g, still more preferably from 0.25 to 0.70 mmol/g, even more preferably 0.30 to 0.70 mmol/g, even more preferably 0.35 to 0.70 mmol/g and exceptionally more preferably 0.40 to 0.60 mmol/g.

[0035] As alternative polymers, preferably those are used where the alkoxysilane groups are incorporated non-terminally into the backbone of the polymer, but are specifically laterally distributed over the chain of the backbone. Important properties such as crosslinking density can be controlled through the incorporated multiple crosslinking units. As a suitable example of this, may be mentioned the TEGOPAC product line from Evonik Goldschmidt GmbH such as TEGOPAC BOND 150, TEGOPAC BOND 250 and TEGOPAC SEAL 100. In this context, for example, reference is made to DE 102008000360 A1, DE 102009028640 A1, DE102010038768 A1 and DE 102010038774 A1.

[0036] Usually these alkoxysilane polymers have the polymer 2 to 8 alkoxy silane groups per prepolymer molecule.

[0037] The degree of crosslinking of the binder and thus both the strength of the resulting coating as well as its elastic properties can be adjusted as a function of the alkoxysilane group functionality of the polymer.

[0038] Usually the amount of the binder is 5 to 50 wt.-%, preferably 5 to 40 wt.-%, more preferably 6 to 35 wt.-% and still more preferably 10 to 30 wt. %, with respect to the composition.

[0039] According to the invention, the composition contains water as a further component B. The water acts primarily as a crosslinking agent or as a reactant. This results in more homogeneous and faster curing of the binder, compared with a composition according to WO 2010/131037 A1. The curing of the composition is therefore largely independent of the absolute humidity, and the composition cures reliably and quickly even under extremely dry conditions.

[0040] According to the invention, the water content in the composition is up to 5 wt.-% with respect to the polymer amount, whereby the content lies in the range preferably between 0.1 and 5 wt.-%, more preferably between 0.5 and 3 wt.-%, and even more preferably between 0.6 to 2 wt.-%.

[0041] According to the invention, the component C contains one insulation-forming additive, whereby the additive may include both single compounds as well as a mixture of several compounds.

[0042] Useful intumescent additives include those which, by forming an inflated insulating layer of flame-resistant material under the effect of heat, protects the substrate from overheating and thereby prevents or at least delays changes in the mechanical and static properties of the structural elements due to heat. The formation of a voluminous insulating layer, namely a layer of ash crust, may be effected by the chemical reaction of a mixture of appropriately coordinated compounds which react with one another when exposed to heat. Such systems are known to the person skilled in the art under the term chemical intumescence and can be used according to the invention. Alternatively, the voluminous insulating layer may be formed by physical intumescence. In each case, both systems may be used either alone or together in combination according to the invention.

[0043] At least three components are generally required for the formation of an intumescent layer by chemical intumescence, i.e. a carbon source, a dehydrogenation catalyst and a blowing agent that are contained, for example, in coatings in a binder. On heating, the binder softens and the fire-protection additives are released so that they react with one another in the event of chemical intumescence or can swell in the case of physical intumescence. Acid is formed from the dehydrogenation catalyst through thermal decomposition, and serves as a catalyst for carbonification of the carbon sources. At the same time, the blowing agent decomposes to form thermally inert gases causing a swelling of the carbonized (burned) material and optionally the plasticized binder to form a voluminous insulating foam.

[0044] In one embodiment of the invention, in which the insulating layer is formed by chemical intumescence, the intumescent additive comprises at least one carbon network former insofar as the binder cannot be used as such, at least one acidifier, at least one blowing agent and at least one inorganic matrix former. The components of the additive are specially selected so that they develop a synergy, whereby some of the compounds may have several functions.

[0045] The compounds commonly used as a carbon source in intumescent flame retardants and known to persons skilled in the art, such as starch-like compounds, e.g. starch and modified starch, and/or polyhydric alcohols (polyols), such as saccharides and polysaccharides and/or a thermoplastic or thermoset polymeric resin binder such as a phenolic resin, a urea resin, a polyurethane, polyvinyl chloride, poly(methyl)acrylate, polyvinyl acetate, polyvinyl alcohol, a silicone resin and/or a rubber. Suitable polyols are polyols selected from the group including sugar, pentaerythritol, dipentaerythritol, tripentaerythritol, polyvinyl acetate, polyvinyl alcohol, sorbitol, EO-PO polyols. Pentaerythritol, dipentaerythritol, or polyvinyl acetate are preferably used.

[0046] It should be noted that, in event of fire, the binder itself can also have the function of a carbon source.

[0047] The compounds commonly used as dehydrogenation catalysts or acid generators in intumescent fire protection formulations and known to those skilled in the art, such as a salt or an ester of an inorganic, non-volatile acid selected from among sulfuric acid, phosphoric acid or boric acid. Essentially, phosphorus-containing compounds are used and the pallet is very large, since they extend over a plurality of oxidation states of phosphorus, such as phosphines, phosphine oxides, phosphonium compounds, phosphates, elemental red phosphorus, phosphites and phosphates. As for phosphoric acid compounds, by way of example may be mentioned: mono-ammonium phosphate, diammonium phosphate, ammonium phosphate, ammonium polyphosphate, melamine phosphate, melamine phosphate, potassium phosphate, polyol phosphates such as pentaerythritol phosphate, glycerol phosphate, sorbitol phosphate, mannitol phosphate, dulcet phosphate, neoprene tylglycol phosphate, ethylene glycol phosphate, di-pentaerythritol phosphate and the like. A polyphosphate or ammonium polyphosphate is preferably used as a phosphoric acid compound. Compounds such as reaction products of Lamelite C (melamine formaldehyde resin) with phosphoric acid are to be understood among melamine resin phosphates. As sulfuric acid compounds, may be mentioned as examples: ammonium sulfate, ammonium sulfamate, nitroaniline bisulfate, 4-nitroaniline-2-sulfonic and 4,4 dinitro sulfanilamide and the like. Melamine borate may be mentioned as an example of a boric acid compound.

[0048] Suitable blowing agents are the compounds commonly used in flame retardants and known to persons skilled in the art, such as cyanuric acid or isocyanic acid and derivatives thereof, melamine and derivatives thereof. Such blowing agents include cyanamide, dicyanamide, dicyandiamide, guanidine and its salts, biguanide, melamine cyanurate, cyanic acid salts, cyanic acid esters and amides, hexamethoxymethylmelamine, dimelamine pyrophosphate, melamine polyphosphate, melamine phosphate. Preferably hexamethoxymethylmelamine or melamine (cyanuric acid amide) is used.

[0049] Also suitable are components whose action is not limited to a single function, such as melamine, which acts both as an acidifier as well as a blowing agent. Further examples are described in GB 2 007 689 A1, EP 139 401 A1 and U.S. Pat. No. 3,969,291 A1.

[0050] In one embodiment of the invention, in which the insulating layer is formed by physical intumescence, the intumescent additive comprises at least one thermo-expandable compound as a graphite intercalation compound, which is also known as expandable graphite. This may also be, in particular, homogeneously contained in the binder.

[0051] As expandable graphite intercalation, there are known compounds such as SOx, NOx, halogen and/or strong acids in graphite. These are also referred to as graphite salts. Preferred expandable graphites which release SO.sub.2, SO.sub.3, NO and/or NO.sub.2 at temperatures of, for example 120 to 350 C. on swelling. The expandable graphite may be, for example, in the form of flakes having a maximum diameter in the range of 0.1 to 5 mm. Preferably this diameter lies in the range 0.5 to 3 mm. Suitable expandable graphites are commercially available for the present inventio. Generally, the particles of expandable graphite are uniformly distributed in the fire protection elements according to the invention. However, the concentration of expandable graphite may also be selectively varied pattern-like, flat and/or sandwiched. In this respect, reference is made to EP 1489136 A1, which is incorporated herein by reference.

[0052] In a further embodiment of the invention, the insulating layer is formed through both chemical as well as physical intumescence, so that the intumescent additive includes both a carbon source, a dehydrogenation catalyst and a blowing agent as well as thermally expandable compounds.

[0053] Since the ash crust formed in the event of fire is usually too unstable and, depending on its density and structure, may be blown around by air currents and adversely affect the insulating effect of the coating, at least one ash crust stabilizer is preferably added to the above-mentioned components.

[0054] Compounds commonly used in fire protection formulations as an ash crust stabilizer or matrix former and known to persons skilled in the art, include expandable graphite and particulate metals such as aluminum, magnesium, iron and zinc. The particulate metal may be in the form of a powder, platelets, scales, fibers, threads and/or whiskers, whereby the particulate metal in the form of powder, flakes or scales has a particle size of 50 m, preferably from 0.5 to 10 m. When using the particulate metal in the form of fibers, filaments and/or whiskers, a thickness of 0.5 to 10 m and a length of 10 to 50 m is preferred. Alternatively or additionally an oxide or a compound of a metal from the aluminum, magnesium, iron or zinc group may be used as an ash crust stabilizer, in particular iron oxide, preferably ferric oxide, titanium dioxide, a borate, such as zinc borate and/or a glass frit made of low-melting glasses with a melting temperature preferably at or above 400 C., phosphate or sulfate glasses melamine poly zinc sulfate, ferro glasses or calcium borosilicate. The addition of such an ash crust stabilizer contributes to a significant stabilization of the ash crust in the event of fire, as these additives increase the mechanical strength of the intumescent layer and/or prevent their dripping. Examples of such additives can be found in U.S. Pat. Nos. 4,442,157 A, 3,562,197 A, GB 755 551 A and EP 138 546 A1.

[0055] In addition, an ash crust stabilizer, such as melamine phosphate or melamine borate may be included.

[0056] Optionally, one or more reactive flame retardants may be added to the composition according to the invention. Such compounds are incorporated in the binder. An example according to the invention are reactive organophosphorus compounds such as 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and its derivatives, such as DOPO-HQ, DOPO-NQ, and adducts. Such compounds are described for example by S. V. Levchik, E. D. Weil, Polym. Int. 2004, 53, 1901-1929.

[0057] The intumescent additive may be contained in an amount of 30 to 99 wt.-% in the composition, whereby the amount is substantially dependent on the type of application of the composition (spraying, brushing and the like). The proportion of the component C is set as high as possible in the total formulation in order to achieve the highest possible intumescent rate. Preferably, the proportion of component C in the total formulation is 35 to 85 wt.-%, and particularly preferably 40 to 85 wt.-%.

[0058] In one embodiment, the composition according to the invention further comprises at least one other ingredient selected from among plasticizers, crosslinking agents, water scavengers, organic and/or inorganic aggregates and/or other additives.

[0059] The plasticizer has the task of making the cured polymer network soft. Further, the plasticizer has the function of introducing an additional liquid component, so that the fillers are completely wetted and the viscosity is adjusted so that the coating is capable of processing. The plasticizer may be included in such an amount in the composition that it can sufficiently fulfill the above-described functions.

[0060] Suitable plasticizers include derivatives of benzoic acid, phthalic acid, for example, phthalates, such as dibutyl, dioctyl, dicyclohexyl, diisooctyl, diisodecyl-, dibenzyl- or butyl benzyl phthalate, trimellitic acid, pyromellitic acid, adipic acid, sebacic acid, fumaric acid, maleic acid, itaconic acid, caprylic acid and citric acid, alkyl phosphate esters and derivatives of polyesters and polyethers, epoxidized oils, C.sub.10-C.sub.21-alkyl sulfonic acid esters of phenol and alkyl esters. Preferably, the plasticizer is an ester derivative of terephthalic acid, a triol ester of caprylic acid, a glycol diester, diol esters of aliphatic dicarboxylic acids, an ester derivative of citric acid, secondary alkyl sulfonic acid esters, esters of glycerol derivatives having epoxy groups and ester derivatives of phosphates. Most preferably, the plasticizer is bis(2-ethylhexyl)terephthalate, trihydoxy methyl propyl acrylate, triethylene glycol-bis(2-ethylhexanoate), 1,2-cyclohexanedicarboxylic acid-diisononyl ester, a mixture of 75-85% of secondary sulfonic alkane, 15-25% of secondary and alkane disulfonic acid diphenyl ester, 2-3% of non-sulfonated alkanes, triethyl citrate, epoxidized soybean oil, tri-2-ethylhexyl phosphate or a mixture of n-octyl and n-decylsuccinate.

[0061] Commercially available examples of plasticizers are EASTMAN DOTP Plasticizer (Eastman Chemical Company), Esterex NP 343 (Excon Mobil Corporation), Solusolv 2075 (Solutia Inc.), Hexamoll DINCH (BASF SE), Mesamoll 11 (Lanxess Germany GmbH), triethylcitrate (Sigma Aldrich), Paraplex G-60 (Hallstar Company), Disflammol TOF (Lanxess Germany GmbH) and TP LXS Uniplex ODS (Lanxess Germany GmbH).

[0062] In the composition, the plasticizer may be included preferably in an amount of 0.1 to 40 wt.-%, more preferably 1 to 35 wt.-%, and even most preferably 5 to 25 wt. %, with respect to the total composition.

[0063] Further, the composition may contain at least one catalyst or a further crosslinking agent, whereby this, if present, is designed to inhibit reaction separately from the component B. The crosslinking agent enables various properties, such as adhesion to the substrate, better wetting of the additives and curing the composition to be optimized and customized.

[0064] Suitable catalysts are selected from pure tin-containing compounds. Suitable further crosslinking agents are selected from a reactive alkoxysilane or an oligomeric organofunctional alkoxysilane. Preferably, the catalyst is a tin-containing tin-containing compound. Preferably, the additional crosslinking agent is an oligomeric vinyl-functional alkoxysilane, an oligomeric amino-functional/alkyl-functional alkoxysilane, an oligomeric amino-functional alkoxysilane, an amino-functional alkoxysilane, a alkyl-functional alkoxysilane, an epoxy-functional alkoxysilane, a vinyl-functional alkoxysilane, a vinyl-functional/alkyl-functional alkoxysilane, a mercapto alkoxysilane, a methacryl-functional alkoxysilane or silicic acid esters.

[0065] Suitable catalysts or other cross-linking agents are, for example: dibutyltin dilaurate (DBTL), dioctyltin (DOTL), which due to its less toxic properties is preferred over the DBTL, hexadecyltri methoxysilane, iso-butyltriethoxysilane, iso-butyltrimethoxysilane, methyltriethoxysilane, methyltrimethoxysilane, octyltrichlorosilane, octyltriethoxysilane, propyltriethoxysilane, propyltrimethoxysilane, bis(3-triethoxysilylpropyl)amine, bis(3-trimethoxysilylpropyl)amine, 3-aminopropylmethyldiethoxysilane, 3-aminopropyltriethoxysilane, 3-aminopropyltri methoxysilane, 2-aminoethyl-3-amino-propylmethyldimethoxysilane, 2-aminoethyl-3-amino-propyltrimethoxysilane, 3-glycidyloxypropyltriethoxysilane, 3-glycidyloxypropyltrimethoxysilane, 3-mercaptoprobyltri methoxysilane, 3-methacryloxypropyltrimethoxysilane, methacryloxymethyl-methyldimethoxysilane, methacryloxymethyl-timethoxysilane, 3-methacryloxypropyltriacetoxysilane, ethylpolysilicate, tetraethyl orthosilicate, tetramethyl orthosilicate, tetra-n-propyl orthosilicate, vinyltrichlorosilane, vinyltriethoxysilane, vinyltrimethoxysilane, vinyltriacetoxysilane, vinyltris(2-methoxyethoxy)silane, N-cyclohexylaminomethyltriethoxysilane, cyclohexyl-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-3-aminopropyltrimethoxysilane, 3-(2-aminomethylamino) propyltriethoxysilane, N-(2-aminoethyl)-3-amino-prolymethyldimethoxysilane, 3-ureidopropyltrimethoxysilane, N-methyl[3-(trimethoxysilyl)propyl]carbamate, N-trimethoxysilyl methyl-O-methyl carbamate, N-dimethoxy(methyl)silyl-methyl-O-methyl carbamate, tris-[3(trimethoxysilyl) propyl]isocyanurate or combinations of these.

[0066] Commercially available examples of this include: Dynasylan 1146, Dynasylan 6490, Dynasylan 6498, Dynasylan SIVO 210, Dynasylan SIVO 214, Dynasylan 9116, Dynasylan IBTEO, Dynasylan IBTMO, Dynasylan MTES, Dynasylan MTMS, Dynasylan OCTCS, Dynasylan OCTEO, Dynasylan OCTMO, Dynasylan PTEO, Dynasylan PTMO, Dynasylan 1122 Dynasylan 1124, Dynasylan 1133, Dynasylan 1204, Dynasylan 1505, Dynasylan 1506, Dynasylan AMEO, Dynasylan AMEO-T, Dynasylan AMMO, Dynasylan 1411, Dynasylan DAMO, Dynasylan DAMO-T, Dynasylan GLYEO, Dynasylan GLYMO, Dynasylan MTMO, Dynasylan MEMO, Dynasylan 40, Dynasylan A, Dynasylan M, Dynasylan P, Dynasylan VTC, Dynasylan VTEO, Dynasylan VTMO, Dynasylan VTMOEO, Dynasylan 6598 (respectively from Evonik Industries AG), Geniosil GF9, Geniosil GF 91, Geniosil GF 92, Geniosil XL 926, Geniosil GF 93, Geniosil GF 94, Geniosil GF 95, GF 96 Geniosil, Geniosil GF 98, Geniosil XL 10, Geniosil XL 12, Geniosil GF 56, Geniosil GF 62, Geniosil GF 31, Geniosil XL 32, Geniosil XL 33, Geniosil GF 39, Geniosil GF 60, Geniosil XL 63, Geniosil XL 65, Geniosil GF 69, Geniosil GF 80 and Geniosil GF 82 (respectively from Wacker Chemie AG).

[0067] The additional crosslinking agent may contain, individually or as a mixture of several agents, with respect to the binder, preferably an amount of 0.1 to 10 wt.-%, more preferably of 0.5-7 wt.-%, and most preferably from 1-5 wt.-%.

[0068] A water scavenger is usually added to the composition to prevent premature reaction of the alkoxysilane with the polymer due to residual moisture which may be present in the composition components, in particular in the fillers and/or additives, or the humidity. The moisture in the formulations is trapped. Preferably, the water scavenger is an organofunctional alkoxysilane or an oligomeric organofunctional alkoxysilane, more preferably a vinyl-functional alkoxysilane, an oligomeric vinyl-functional alkoxysilane, a vinyl-functional/alkyl-functional alkoxysilane, an oligomeric amino-functional/alkyl-functional alkoxysilane, an acetoxy-functional/alkyl-functional alkoxysilane, an amino-functional alkoxysilane, an oligomeric amine functional alkoxysilane, a carbamatosilane or methacryloxy-functional alkoxysilane. Most preferably, the water scavenger is di-tert-butoxydiacetoxysilane, bis(3-triethoxysilylpropyl)amine, bis(3trimethoxypropyl)amine, 3-aminopropyl methyldiethoxysilane, 3-aminopropyl triethoxysilane, vinyltriethoxysilane, vinyl-trimethoxysilane, vinyl-tris(2-methoxyethoxy)silane, N-cyclohexylaminomethyltriethoxysilane, vinyl-dimethoxymethylsilane, vinyltriacetoxysilane, 3-methacryloxypropyl trimethoxysilane, methacryloxymethyl-methylditrimethoxysilane, methacryloxymethyltrimethoxysilane, 3-methacryloxypropyltriacetoxysilane, N-meth[3-(trimethoxysilyl)propyl]carbamate, N-tri-O-methyl carbamate methoxysilylmethyl, N-dimethoxy(methyl)silyl methyl-O-methylcarbamate, or combinations thereof.

[0069] Commercially available examples of this include: Dynasylan 1146, Dynasylan 6490, Dynasylan 6498, Dynasylan BDAC, Dynasylan 1122, Dynasylan 1124, Dynasylan 1133, Dynasylan 1204, Dynasylan 1505, Dynasylan 1506, Dynasylan AMEO, Dynasylan AMEO-T, Dynasylan VTEO, Dynasylan VTMO, Dynasylan VTMOEO, Dynasylan 6598, (respectively from Evonik Industries AG), Geniosil XL 926, Geniosil XL 10, Geniosil XL 12, Geniosil GF 56, Geniosil GF 62, Geniosil GF 31, Geniosil XL 32, Geniosil XL 33, Geniosil GF 39 Geniosil, GF 60, Geniosil XL 63 and Geniosil XL 65 (respectively from Wacker Chemie AG).

[0070] The added amount of water scavenger depends on the water content of the components of the formulation, excluding the extra added water (component B) and is usually in the range of about 1 wt. %. With respect to the total composition, the water scavenger can be used in an amount of 0.1 to 2 wt.-%, preferably from 0.2 to 2 wt.-%, more preferably from 0.2 to 1.8 wt.-% and even more preferably 0.25 to 1.5 wt.-%.

[0071] The composition may also contain, in addition to the additives already described and if appropriate, customary auxiliary agents such as wetting agents, for example those based on polyacrylates and/or polyphosphates, defoamers, such as silicone defoamers, dyes, fungicides, and various fillers, such as vermiculite, inorganic fibers, silica sand, glass microspheres, mica, silica, mineral wool, and the like.

[0072] Additional additives, such as thickeners and/or rheology additives and fillers may be added to the composition. Rheological additives that may be used include anti-settling, anti-sag and thixotropic agents, preferably polyhydroxycarbonic acid amides, urea derivatives, salts of unsaturated carboxylic esters, alkyl ammonium salts of acidic phosphoric acid derivatives, ketoximes, amine salts of p-toluenesulfonic acid, amine salts of sulfonic acid derivatives and aqueous or organic solutions or mixtures of the compounds. In addition, rheology additives may be used on the basis of pyrogenic or precipitated silicas or silanized pyrogenic or precipitated silicas. It is preferable that the rheology additives are pyrogenic silicas, modified and unmodified sheet silicates, precipitated silicas, cellulose ethers, polysaccharides, polyurethane and acrylic thickeners, urea derivatives, castor oil derivatives, polyamides and fatty acid amides and polyolefins, insofar as they are in solid form, powdered cellulose and/or suspending agents, such as xanthan gum.

[0073] The composition according to the invention is formulated as a two or multi-component system. Preferably it is packaged as a two-component system, in which the component A and the component B are divided into two components, component I and component II in order to inhibit reaction.

[0074] The further components of the composition are divided according to their compatibility with each other and with the compounds contained in the composition and may be present in one of the two components or in both components. If added, the water scavenger and cross-linking agent should be formulated separately from the components contained in component B.

[0075] Further, the division of the other components, in particular the solid components, depend on what amounts are to be included in the composition. By appropriate allocation, a higher proportion may possibly arise with respect to the total composition.

[0076] It is also possible, that a component only contains the component B. Alternatively, the component B may, together with other components such as plasticizers, additives, and/or fillers, may be included in one component of the two-component system.

[0077] The component C may be included as a total mixture or as individual components in a component or multiple components. The distribution of the component C is carried out as a function of the compatibility of the compounds contained in the composition, so that neither a reaction of the compounds contained in the composition can take place with one another, nor mutual reaction of these compounds with the compounds of the other components. This is dependent on the compounds used.

[0078] Preferably, component C, comprising at least one carbon source, at least one blowing agent and at least one dehydrogenation catalyst, is divided in such a way in component I and component II, that these compounds (the individual components of the intumescent component) and the other components, i.e. components (A) and (B) are separated in order to inhibit reaction of the composition. This ensures that the highest possible proportion of fillers can be achieved. This leads to a high intumescence, even in the case of low coating thicknesses of the composition.

[0079] If the intumescent additive contains an ash crust stabilizer, then this may be included in either component I or in component II. Alternatively, the ash crust stabilizer may also be divided between the two components I and II. Accordingly, the ash crust stabilizer is so divided between component I and component II that component I or component II contains at least a portion of the ash crust stabilizer while component I or component II optionally contains a further part of the ash crust stabilizer.

[0080] The composition is applied as a paste with a brush, a roller or by spraying onto the substrate, in particular a metallic substrate. Preferably, the composition is applied by means of an airless spray method.

[0081] When compared with the solvent and water-based systems and the system according to WO 2010/131037 A1, the composition according the invention is characterized by relatively rapid curing through hydrolysis and an associated polycondensation reaction, and thus physical drying out is unnecessary. Moreover, the curing properties and the properties of the dried (cured) composition can be controlled via the water content in the composition. This is particularly important when the coated components must be loaded or processed quickly, either by coating with a topcoat or when moving or transporting the components. The coating is thus significantly less susceptible to external influences at the site, such as being hit by (rain) water or dust and dirt, which can lead, in the case of solvent or water-based systems, to the leaching of water-soluble ingredients, such as ammonium polyphosphate, or to a reduced intumescence on collecting dust. Due to the low fusion point of the binder and the high solids content, the rate of expansion itself is high when exposed to heat even in the case of low layer thickness.

[0082] Therefore, the two or multi-component coating composition according to the invention is suitable in particular as a flame-retardant coating, preferably in the form of a sprayable coating for metallic and non-metallic substrates. The substrates are not limited and include components, especially steel components and wooden components, as well as individual cables, cable bundles, cable trays and cable ducts or other cabling.

[0083] The composition according to the invention is used mainly in the construction industry as a coating, in particular as a fire protection coating for steel construction elements, but also for construction elements made from other materials, such as concrete or wood, as well as a fire protection coating for single cable, cable bundles, cable trays and cable ducts or other cabling.

[0084] A further object of the invention is, therefore, the use of the composition according to the invention as a coating, particularly as a coating for structural elements or components of steel, concrete, wood and other materials, such as plastics, especially as a fire protection coating.

[0085] The present invention also relates to objects that are protected when the composition according to the invention is cured. The objects have excellent intumescent properties.

[0086] The following examples serve to illustrate the invention.

Exemplary Embodiments

[0087] The ingredients listed below are used for the production of intumescent compositions according to the invention. The individual components are respectively mixed by means of a dissolver and homogenized. These mixtures are then mixed either before spraying or preferably during spraying and applied.

[0088] The curing of the composition is monitored and the intumescent factor and relative ash crust stability then determined. For this purpose, the compositions are each placed in a circular Teflon mold of about 2 mm depth and 48 mm diameter. The samples are cured at a temperature of +22 C. and a relative humidity of 35%.

[0089] Wedge-shaped samples (1-10 mm) are molded for the determination of the curing time. The curing time corresponds to the time taken for the layer thickness h.sub.A to be cured.

[0090] A muffle furnace is preheated to 600 C. in order to determine the intumescent factor and the relative stability of the ash crust. Multiple measurements of the sample thickness are carried out using callipers and the mean h.sub.M determined. Then, the samples are each placed in a cylindrical steel mold and heated for 30 min in a muffle furnace. After cooling to room temperature, the foam height H.sub.E1 is first destructively determined (mean value of the multiple measurements). The intumescent factor I is calculated as follows:

Intumescent factor I: I=h.sub.E1:h.sub.M

[0091] Then a defined weight (m=105 g) is allowed to fall from a defined height (h=100 mm) onto the foam in the cylindrical steel mold in order to determine the foam height H.sub.E2 remaining, following this partially destructive action. The relative ash crust stability is calculated as follows:

relative ash crust stability (ACS): ACS=h.sub.E2:h.sub.E1

[0092] The following composition was prepared as the component C and the mixture was used in the amount indicated in each case for the comparative example and the following examples 1-3:

[0093] Component C:

TABLE-US-00001 Compounds Quantity [g] Pentaerythritol 8.7 Melamine 8.7 Ammonium polyphosphate 16.6 Titanium dioxide 7.9

Comparative Example 1

[0094] Component A

TABLE-US-00002 Compounds Quantity [g] Dimethoxy(methyl)silylmethylcarbamat- 11.0 terminated polyether.sup.1 Vinyldimethoxymethylsilane.sup.2 0.5 Di-(2-ethylhexyl)adipate.sup.3 2.2 3-aminopropyltriethoxysilane.sup.4 0.3 .sup.1GENIOSIL STP-E 10 (methoxy content approximately 0.4-0.5 mmol/g) .sup.2GENIOSIL XL 12 (water scavenger) .sup.3Plastomoll DOA (plasticizer) .sup.4Dynasylan AMEO (crosslinking agent)

[0095] Component C

TABLE-US-00003 Compounds Quantity [g] as indicated above 21.0

Comparative Example 2

[0096] An aqueous dispersion technology based on a commercial fire protection product (Hilti CFP S-WB) is used for comparison.

Comparative Example 3

[0097] A standard epoxy-amine system (Jeffamin T-403, liquid, solvent-free and crystallization-stable epoxy resin, consisting of low molecular epoxy resins based on bisphenol A and bisphenol F (Epilox AF 18-30, Leuna-Harze GmbH) and 1,6-hexanediol diglycidyl ether), which is filled to 60% with an intumescent mixture is tested analogously to the above examples as a further comparison.

Comparative Example 4

[0098] A standard epoxy-amine system (isophoronediamine, trimethylolpropane and liquid, solvent-free and crystallization-stable epoxy resin consisting of low molecular weight epoxy resins based on bisphenol A and bisphenol F (Epilox AF 18-30, Leuna-Harze GmbH)), which is filled to 60% with an intumescent mixture is tested analogously to the above examples as a further comparison.

Example 1

[0099] Component A

TABLE-US-00004 Compounds Quantity [g] GENIOSIL STP-E 10 10.96 GENIOSIL XL 12 0.47 Plastomoll DOA 2.21 Dynasylan AMEO 0.32

[0100] Component B

TABLE-US-00005 Compounds Quantity [g] Water 0.06

[0101] Component C

TABLE-US-00006 Compounds Quantity [g] as indicated above 21.0

Example 2

[0102] Component A

TABLE-US-00007 Compounds Quantity [g] GENIOSIL STP-E 10 10.88 GENIOSIL XL 12 0.48 Plastomoll DOA 2.22 Dynasylan AMEO 0.32

[0103] Component B

TABLE-US-00008 Compounds Quantity [g] Water 0.19

[0104] Component C

TABLE-US-00009 Compounds Quantity [g] as indicated above 21.0

Example 3

[0105] Component A

TABLE-US-00010 Compounds Quantity [g] GENIOSIL STP-E 10 10.78 GENIOSIL XL 12 0.48 Plastomoll DOA 2.20 Dynasylan AMEO 0.32

[0106] Component B

TABLE-US-00011 Compounds Quantity [g] Water 0.32

[0107] Component C

TABLE-US-00012 Compounds Quantity [g] as indicated above 21.0

Example 4

[0108] Component A

TABLE-US-00013 Compounds Quantity [g] GENIOSIL STP-E 10 9.42 GENIOSIL XL 12 0.41 Plastomoll DOA 3.77 Dynasylan AMEO 0.27

[0109] Component B

TABLE-US-00014 Compounds Quantity [g] Water 0.14

[0110] Component C

TABLE-US-00015 Compounds Quantity [g] as indicated above 21.0

[0111] On the one hand, the results shown in Table 1 clearly show that the curing of the compositions according to the invention is much faster than the comparative composition. Already with a water content of 0.5 wt.-% based on the polymer, a composition according to the invention cures about five times faster than the comparative composition of

[0112] comparable thickness. At a water content of 1.5%, the curing can be reduced by a factor of 8.5.

TABLE-US-00016 TABLE 1 Results of the measurements of the curing time Sample thickness h.sub.A Sample (mm) Curing time 1 7 3 hours 2 10 2 hours 3 10 2 hours 4 10 2 hours Comparative example 1 6 17 hours Comparative example 2 2 10 days Comparative example 3 10 12 hours Comparative example 4 10 1 day .sup.1)not measured

TABLE-US-00017 TABLE 2 Results of measurements of the intumescent factor and the ash crust stability Intumescent Relative ash crust Sample factor I stability ACS thickness h.sub.M Sample (multiple) (multiple) (mm) 1 18.7 0.25 1.1 2 19.5 0.32 1.3 3 15.3 0.30 1.5 4 20.0 0.26 1.2 Comparative example 3 22 0.04 1.6 Comparative example 4 1.7 0.60 1.2 .sup.1)not measured