Anti-corrosive particles

Abstract

The present invention relates to dispersion of surface modified inorganic particles including (a) fluid comprising a complexing agent, and (b) the surface modified inorganic particles comprising polyvalent metal ions.

Claims

1. A dispersion of surface modified inorganic particles comprising: (a) fluid comprising (i) water and (ii) a complexing agent comprising acidic or basic materials, and (b) particles dispersed throughout said fluid, said particles consisting of surface modified inorganic particles having an average particle diameter of less than about 10 microns, wherein each surface modified inorganic particle consists of (i) an inorganic particle having a particle surface and (ii) polyvalent metal ions along said particle surface, said polyvalent metal ions having replaced protons of hydroxyl groups along said particle surface.

2. A dispersion according to claim 1 wherein said average particle diameter is less than about 3 micron.

3. A dispersion according to claim 1, wherein said average particle diameter is less than about 1 micron.

4. A dispersion according to claim 1, wherein the inorganic particles consist of silica, silicate, alumina, aluminosilicate, titania, zirconia, ceria or mixtures thereof; and the polyvalent metal ions consist of calcium, zinc, cobalt, lead, strontium, lithium, barium, magnesium, manganese, cerium, aluminum, or mixtures thereof.

5. A dispersion according to claim 1 wherein the inorganic particles are in a form of a gel, a colloidal, a precipitate, fumed particles, or mixtures thereof.

6. A dispersion according to claim 1, wherein said complexing agent comprises phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof.

7. A dispersion of surface modified inorganic particles comprising: (a) fluid comprising a complexing agent, said complexing agent comprising (i) phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof, or (ii) one or more alkanolamines, and (b) particles dispersed throughout said fluid, said particles consisting of surface modified inorganic particles, wherein each surface modified inorganic particle consists of (i) an inorganic particle having a particle surface and (ii) polyvalent metal ions along said particle surface, said polyvalent metal ions having replaced protons of hydroxyl groups along said particle surface.

8. A dispersion according to claim 7, wherein said surface modified inorganic particles have an average particle diameter of less than about 10 microns.

9. A dispersion according to claim 7, wherein said surface modified inorganic particles have an average particle diameter of less than about 5 microns.

10. A dispersion according to claim 7, wherein the inorganic particles consist of silica, silicate, alumina, aluminosilicate, titania, zirconia, ceria or mixtures thereof; and the polyvalent metal ions consist essentially of calcium, zinc, cobalt, lead, strontium, lithium, barium, magnesium, manganese, cerium or mixtures thereof.

11. A dispersion according to claim 7, wherein the inorganic particles are in the form of a gel, a colloidal, a precipitate, fumed particles, or mixtures thereof.

12. A dispersion according to claim 7, wherein said fluid further comprises at least one of water, binder, film former, bacteriacide and polymer.

13. A dispersion according to claim 7, wherein said complexing agent comprises phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof.

14. A dispersion according to claim 7, wherein said dispersion is made by a process of milling said surface modified inorganic particles in the presence of the complexing agent.

15. A method of making the dispersion according to claim 7, said method comprising: (a) mixing the surface modified inorganic particles with the fluid comprising the complexing agent; and (b) milling the inorganic particles in the presence of the complexing agent to form an average diameter of less than about 10 microns for the surface modified inorganic oxide particles.

16. A method according to claim 15, wherein said complexing agent comprises phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof.

17. An inorganic oxide dispersion made by the method according to claim 15.

18. A dispersion according to claim 2, wherein the inorganic particles consist of silica, silicate, alumina, or aluminosilicate; and the polyvalent metal ions consist of calcium.

19. A dispersion according to claim 18, wherein said complexing agent comprises phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof.

20. A dispersion according to claim 19, wherein said complexing agent comprises 2-hydroxyphosphonoacetic acid.

21. A dispersion according to claim 19, wherein said fluid further comprises a bacteriacide.

22. A dispersion according to claim 10, wherein said surface modified inorganic particles have an average particle diameter of less than about 5 microns.

23. A dispersion according to claim 22, wherein said complexing agent comprises phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids or mixtures thereof.

24. A dispersion according to claim 23, wherein said fluid further comprises water and a bacteriacide.

25. A dispersion according to claim 24, wherein said particles have an average particle diameter of less than about 1.0 micron, and each surface modified inorganic particle consists of (i) a silica, silicate, alumina, aluminosilicate, titania, zirconia or ceria particle having a particle surface and (ii) calcium, zinc, cobalt, lead, strontium, lithium, barium, magnesium or manganese ions along said particle surface.

26. A dispersion according to claim 25, wherein said complexing agent comprises 2-hydroxyphosphonoacetic acid.

27. A dispersion according to claim 23, wherein said fluid further comprises aluminate ions therein.

28. A dispersion according to claim 22, wherein said complexing agent comprises one or more alkanolamines.

29. A dispersion of surface modified inorganic particles comprising: (a) fluid comprising a complexing agent, said complexing agent being selected from the group consisting of 2-hydroxyphosphonoacetic acid, glycolic acid, 1,2,3-benzotriazole, 2-mercaptobenzothiazole, and (2-benzothiazolythio)succinic acid; and (b) surface modified inorganic particles dispersed throughout said fluid, said surface modified inorganic particles having an average particle diameter of less than about 5 microns and comprising (i) silica, silicate, alumina, aluminosilicate, titania, zirconia or ceria particles or mixtures thereof with each inorganic particle having a particle surface and (ii) polyvalent metal ions selected from the group consisting of calcium, zinc, cobalt, lead, strontium, lithium, barium, magnesium, manganese, cerium, aluminum, or mixtures thereof along said particle surface, said polyvalent metal ions having replaced protons of hydroxyl groups along said particle surface.

30. A dispersion according to claim 29, wherein said complexing agent comprises 2-hydroxyphosphonoacetic acid.

31. A dispersion according to claim 29, wherein said complexing agent comprises 1,2,3-benzotriazole, 2-mercaptobenzothiazole or (2-benzothiazolythio)succinic acid.

32. A dispersion according to claim 29, wherein said surface modified inorganic particles have an average particle diameter of less than about 1.0 micron and comprise (i) silica particles with a silica particle surface and (ii) calcium ions forming at least a portion of said silica particle surface.

Description

DETAILED DESCRIPTION

(1) The present invention is concerned with corrosion inhibitors suitable for use in protective films, surface treatments, primers, coatings, adhesives and sealants that are intended to provide adhesion and corrosion inhibiting properties to metallic surfaces and structures. As described herein, all of these fields of application are encompassed by the single term coating.

(2) According to the present invention, a corrosion inhibitor comprises particles of an inorganic oxide having corrosion inhibiting ions chemically bound to the particles. As defined herein, the term inorganic oxides means oxides of metals or metalloids. Metals include those elements on the left of the diagonal line drawn from boron to polonium on the periodic table. Metalloids or semi-metals include those elements that are on this line and include also silicon. Examples of inorganic oxides include silica, silicates, alumina, aluminosilicates, titania, zirconia, ceria and the like, or mixtures thereof.

(3) It must be noted that as used herein and in the appended claims, the singular forms a, and, and the include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to an oxide includes a plurality of such oxides and reference to oxide includes reference to one or more oxides and equivalents thereof known to those skilled in the art, and so forth.

(4) About modifying, for example, the quantity of an ingredient in a composition, concentrations, volumes, process temperatures, process times, recoveries or yields, flow rates, and like values, and ranges thereof, employed in describing the embodiments of the disclosure, refers to variation in the numerical quantity that can occur, for example, through typical measuring and handling procedures; through inadvertent error in these procedures; through differences in the ingredients used to carry out the methods; and like proximate considerations. The term about also encompasses amounts that differ due to aging of a formulation with a particular initial concentration or mixture, and amounts that differ due to mixing or processing a formulation with a particular initial concentration or mixture. Whether modified by the term about the claims appended hereto include equivalents to these quantities.

(5) Inhibitive compounds based on inorganic oxides may, for example, be prepared by a process of precipitation or gelation of the oxide in the presence of the required cations and anions under suitable conditions. Inhibitive compounds based on inorganic oxides can alternatively be made through a process of ion-exchange, in which surface protons and hydroxyl groups of the pre-formed oxide are replaced by contacting the oxide with a solution containing the required inhibitive cations and anions, again under suitable conditions. In either case, the inorganic oxides involved are often characterized by having certain surface areas and porosities with corrosion inhibiting ions attached to the internal and/or external surface of the particles, producing surface modified inorganic particles, although ions may be found through the bulk of the particles as well, depending on the method of preparation.

(6) According to the present invention, a corrosion inhibitor may also comprise combinations of inhibitive cations and anions in the form of sparingly soluble metal salts of the anion. Inhibitive compounds in the form of sparingly water-soluble salts can for example be prepared by a process of particle growth and precipitation from slurries or solutions in the presence of the required cations and anions under suitable conditions.

(7) Combinations of inhibitive compounds based on sparingly soluble salts and those based on inorganic oxides may be prepared by mixing the pre-formed substances, mixing pre-formed inorganic oxides or alternatively pre-formed inorganic oxides bearing inhibitive cations and anions with the appropriate inhibitive cations and anions as necessary such that particle growth and precipitation of sparingly soluble salts occurs in the presence of the inorganic oxide, where in all three cases, the inorganic oxide would exist in the presence of polyvalent cations.

(8) Combinations may also be made in which sparingly soluble inhibitive salts are combined with precursors to inorganic oxides like sodium silicate, alkyl silicates such as tetraethyl orthosilicate, aluminum chloride, aluminum hydroxychloride or sodium aluminate and so forth in the case of silica, alumina and aluminosilicates such that precipitation or gelation, or simply formation, of the inorganic oxide occurs, intimately associated with inhibitive cations and anions. Similarly, mixtures of inhibitive cations and anions and precursors to inorganic oxides can be prepared such that particle growth, precipitation and/or gelation of sparingly soluble compounds and oxides occur simultaneously, intimately associated with one another.

(9) Clearly, a number of ways to prepare inhibitive combinations exist according to the composition of the solution or slurry from which the inhibitive compounds are to be prepared and the processing route, allowing for a great variety in properties displayed by the resulting inhibitive compound.

(10) Preferred cations are those of calcium (Ca.sup.2+), magnesium (Mg.sup.2+), zinc (Zn.sup.2+), manganese (Mn.sup.2+), and cations of the rare earth elements such as cerium (Ce.sup.3+/Ce.sup.4+) cations, but other suitable cations may be cobalt (Co.sup.2+), lead (Pb.sup.2+), strontium (Sr.sup.2+), lithium (Li.sup.+), barium (Ba.sup.2+) and aluminium (Al.sup.3+). Preferred anions are those derived from silicate, borate, molybdate, hydrogen phosphate, phosphate, phosphite, nitrophthalates, phosphonate and phosphonocarboxylates as well as azoles and their derivatives such as 1,2,3-benzotriazole, tolytriazole, benzothiazole, 2-mercaptobenzothiazole, benzimidazole, 2-mercaptobenzimidazole and 2-mercaptobenzoxazole but other suitable anions may be permanganate, manganate, vanadate and tungstate. With respect to the aforementioned components providing anions, it is to be understood that the free acid form or any other partially neutralized or fully neutralized form, i.e., the conjugate species may be employed in any particular case as appropriate.

(11) By way of example, the process of cation exchange with inorganic oxides can be considered. Particles of inorganic oxides such as silica, alumina and other oxides may be prepared such that a proportion of hydroxyl groups are present on the surface of the particles. The particles may differ in porosity from non-porous to highly porous, and may be in any shape from spherical to any non-spherical shape, and may be in the form of a gel, a precipitate, a sol (colloidal), fumed or other common form readily recognized in the art. Such oxide particles may be prepared according to the processes set forth in or referenced by U.S. Pat. Nos. 5,336,794, 5,231,201, 4,939,115, 4,734,226, and 4,629,588 as well as DE1,000,793, GB 1,263,945, DE 1,767332, U.S. Pat. Nos. 5,123,964, 5,827,363, 5,968,470, US2004/0249049 and 2005/0228106 the entire subject matter of which is incorporated herein by reference. Details regarding methods of making these particles may also be found in textbooks such as The Chemistry of Silica by R. K. Iler, John Wiley & Sons, 1979 and Sol-Gel Science by C. J. Brinker and G. W. Scherer, Academic Press, 1990. These kinds of particles are also commercially available, such as, for example, from W. R. Grace & Co.Conn. under the trade names SYLOID, PERKASIL or LUDOX.

(12) The protons of the hydroxyl groups may be replaced by contacting the oxide with a solution containing the required cations. To carry out exchange the oxide may be stirred in water at room temperature and the pH monitored by a meter. Then the substance to be exchanged (e.g. calcium hydroxide or basic zinc carbonate) is added slowly whilst not allowing the pH to rise too far (e.g., above 10.5 for silica or 12 for alumina). The pH needs to be high enough to remove protons but not so high as to dissolve the inorganic oxide. The uptake can be followed by observing the fall of pH over a period of time following the addition of the base. When the pH no longer falls then exchange is complete and the oxide particles may be milled, if necessary, washed and dried under vacuum. Uptake of cations in the oxide can be measured by XRF spectroscopy. Processes for making such exchanged oxides may be found in or referenced by U.S. Pat. Nos. 4,687,595, 4,643,769, 4,419,137 and 5,041,241, the entire subject matter of which is incorporated herein by reference. Typically, the inorganic oxide inhibitor particles will have BET surface areas ranging from about 5 m.sup.2/g up to about 750 m.sup.2/g. with average porosities varying from about 0.1 ml/g to about 3 ml/g.

(13) As noted earlier, similar compounds based on inorganic oxides can for example be prepared by a process of precipitation or gelation of the oxide in the presence of the required cations and anions under suitable conditions and processes for making such compounds may be found for example in U.S. Pat. No. 4,849,297 and GB Patent No. 918,802, the entire subject matter of which is incorporated herein by reference. Similarly, examples of inhibitive compounds based on sparingly soluble salts and processes for preparing them can for example be found in U.S. Pat. Nos. 4,247,526, 4,139,599, 4,294,621, 4,294,808, 4,337,092, 5,024,825, 5,108,728, 5,126,074, 5,665,149, and 6,083,308, U.S. Patent Application No. 2007/0012220 as well as GB Patents Nos. 825,976, 914,707, 915,512, 1,089,245, DE Patents Nos. 2,849,712, 2,840,820, and 1,567,609 and EP Patent No. 522,678, the entire subject matter of which is incorporated herein by reference.

(14) In many cases, the films and coatings employed in anti-corrosion have a limited permeability to water and the mechanism of corrosion inhibition is believed to involve gradual dissolution of the compounds in water with release of ions as the active inhibitors. For such systems to be effective over a long period, the solubility of the compound is very important. If the compound is too soluble, blistering of the coating may occur and the compound will be rapidly depleted; if it is insufficiently soluble the compound will be ineffective. Whether the inhibitive compound is purely a sparingly soluble salt, or based on an inorganic oxide or is some combination of the two, the typical water solubility of such compounds suitable for use in films and coatings results in inhibitive ion concentrations in aqueous media of around 10.sup.5M to 10.sup.2M.

(15) For inhibitive compounds based on inorganic oxides, the inorganic oxide may itself have a certain solubility with respect to the provision of inhibitive substances, according to the nature of the environment in which the corrosion inhibiting particles are used e.g. in the case of silica, silicic acid has a background solubility of about 10.sup.3M with the concentration of silicate being pH dependent having a value of 10.sup.2M for example at a pH of about 10.5.

(16) It is sometimes believed that inhibitors based on inorganic oxides can act to release inhibitive cations and anions into solution by ion exchange with aggressive ions existing in the environment in which the inhibitive particles are used. It would then be permeability of the film or coating to the exchanging ions that would influence the rate of release of the corrosion inhibiting ions in addition to or rather than the mechanism involving solubilisation of inhibitive ions into the permeating aqueous environment. Corrosion inhibiting ions would in that case be preferentially released from the inorganic oxide in those areas where the desired barrier properties of the coating were weakest, leading thereby to improved performance properties.

(17) For reasons related to the ability to incorporate corrosion inhibitors into a wide variety of film and coating systems as well as suitability with respect to corrosion resistance, in addition to the criteria of solubility, the pH of an aqueous slurry of inhibitive compounds will in most cases typically fall within the range of 4 to 10.5 although lower or higher values can be suitable depending on the actual chemistry of the coating or film in question and the nature of the metallic substrate.

(18) By way of example, in the case of simple cation exchange with inorganic oxides, and depending on the proportion of hydroxyl groups on the inorganic oxide, it has been found that up to 2.5 millimoles/g of cation may be combined with the oxide whilst satisfying the criteria of solubility and pH. Since, as indicated above, the technique of ion-exchange is relatively simple the selection of preferred inorganic oxides and the treatments to give maximum uptake of corrosion inhibiting cations can be determined by simple comparative experiments. A lower limit consistent with the requirements of solubility and pH would be 0.05 millimoles/g.

(19) The corrosion inhibiting particles may act as filler for the coating and may be included in relatively large amounts of up to 40% wt, based on the composition to be applied and up to 80% wt based on the dry film weight.

(20) Again by reference to the case of simple cation exchange with inorganic oxides, and having regard to the quantity of cations which can be combined with the oxide as discussed previously, it will be seen that the coatings in that case may contain up to 2 millimoles/g of corrosion inhibiting cations based on the dry film weight.

(21) Control over actual solubility's and pH values is obtained according to the broad range of compositions falling within the scope of the corrosion inhibitor chemistry reviewed above and the variety of ways by which corrosion inhibitors and combinations of corrosion inhibitors may be prepared as outlined above, where nature of the ions being combined, pore structures where inorganic oxides are involved as well as nature of the inorganic oxide are important considerations.

(22) In accordance with the present invention, it has been found that attempting to mill inorganic oxide particles in the presence of polyvalent metal ions to less than a few microns, or mixing small inorganic oxide particles in the presence of polyvalent metal ions, results in dispersions that may be unsuitable for use in certain coating compositions.

(23) The polyvalent cations may arise from the pre-existing association of inhibitive cations with the inorganic oxide such as in the case of ion-exchanged oxides, or those produced by precipitation or co-gelation, or by addition of polyvalent cations during milling in the form of soluble or sparingly soluble compounds or they may be present according to any of the variety of ways by which combinations of inhibitive compounds can be prepared as discussed earlier.

(24) The polyvalent metal ions may cause significant aggregation of the small inorganic oxide particles or cause instability with respect to aggregation, agglomeration, high viscosities or settling when attempting to produce such small inorganic particles by milling.

(25) The present invention alleviates this problem with the use of suitable acidic or basic agents to produce stable dispersions of small particles by controlling pH and/or by complexing the cations, thereby avoiding or minimizing excessive viscosity build-up, reagglomeration of particles and hard settling of the dispersed particles that may otherwise occur during or after milling.

(26) Accordingly, an embodiment of the present invention includes a dispersion of surface modified inorganic particles having fluid or liquid, the surface modified inorganic particles being modified by polyvalent metal ions and have an average particle diameter of about ten microns or less.

(27) As utilized herein, the term surface modified inorganic particle relates to inorganic oxide particles in the presence of polyvalent cations, where the polyvalent cations may arise from processes such as are involved in preparing corrosion inhibitors based on inorganic oxides, from the presence of soluble and sparingly soluble compounds such as those involved in preparing corrosion inhibitors based on sparingly soluble salts and/or from other types of combinations of corrosion inhibiting species and compounds as previously detailed, under conditions such that uptake of the cations by the inorganic oxide can be expected.

(28) The average particle diameter may be less than about 10 microns, about 9 microns, about 8 microns, about 7 microns, 6 microns, about 5 microns, about 4 microns, about 3 microns, about 2 microns or less than about 1 micron. In a more typical embodiment, the average particle diameter is less than about 1 micron.

(29) The polyvalent metal ions may include calcium, zinc, cobalt, lead, strontium, lithium, barium, magnesium, manganese and cations of the rare earth elements such as cerium or mixtures thereof. In a more typical embodiment, the polyvalent metal ions include those of calcium, magnesium, manganese, zinc, and rare earth elements such as cerium.

(30) The particles may be corrosion inhibitors based on inorganic oxides, such as silicas and aluminas, milled separately or in combination with other inorganic oxides. Other examples include inorganic oxides and corrosion inhibitors based on inorganic oxides milled in combination with partially or sparingly soluble metal salts as described earlier, such as those based on phosphates, phosphates, hydrogenphosphates, phosphonates, phosphonocarboxylates, borates, molybdates nitrophthalates, azole derivatives, permanganate, manganate, vanadate and tungstate and any suitable combination thereof. Mixtures of different particle types are also included as are combinations of inhibitive compounds based on sparingly soluble salts and those based on inorganic oxides that may be prepared simultaneously in various ways according to the composition of the solution or slurry from which the inhibitive compounds are to be prepared and the processing route as described earlier.

(31) Another embodiment of the present invention relates to a dispersion of surface modified inorganic particles including (a) fluid comprising a stabilizing or complexing agent, and (b) the surface modified inorganic particles comprising polyvalent metal ions. The present invention also relates to coating compositions including the above-mentioned dispersion.

(32) In some cases, the added substance used to stabilize the dispersion and/or complex the polyvalent cations may be a soluble or partially soluble component of the corrosion inhibiting compound, particle or mixture of particles. The added substances may be discrete compounds or may be oligomeric or polymeric in nature.

(33) The stabilizing and complexing agents may include various phosphorus and phosphorus free acidic substance as well as basic substances such as amines and alkanolamines. Of course the actual species present and state of ionization will depend on the pH and/or state of acidity or basicity at the point of use. Examples of phosphorus containing acidic substances include phosphorus acid, phosphoric acid, tri- and polyphosphoric acids, organophosphonic acids containing one phosphonic acid group per molecule such as 2-hydroxyphosphonoacetic acid, 2-phosphonobutane-1,2,4-tricarboxylic acid, phosphonated oligomers and polymers of maleic and acrylic acids as well as co-oligomers and copolymers thereof. Other examples include organophosphonic acids containing two or more phosphonic acid groups per molecule like diphosphonic acids such as alkylmethane-1-hydroxy-1,1-diphosphonic acids where the alkyl group may be substituted or unsubstituted and contain from 1 to 12 carbon atoms e.g. methyl-1-hydroxy-1,1-diphosphonic acid or propyl-1-hydroxy-1,1-diphosphonic acid. Also suitable are amino compounds containing two or more N-alkylene phosphonic acid groups per molecule such as alkylamino-di(alkylene phosphonic acids) where the alkyl group can be substituted or unsubstituted and have from 1-12 carbon atoms e.g propyl, isopropyl, butyl, hexyl, or 2-hydroxyethyl and the alkylene group may have from 1 to 5 carbon atoms as well as amino-tri(alkylene phosphonic acids) such as nitrilo-tris-(methylene phosphonic acid) and nitrilo-tris-(propylene phosphonic acid). Other suitable aminoderivatives from amino compounds are alkylene diamine-tetra-(alkylene phosphonic acids), such as ethylene diamine-tetra-(methylene phosphonic acid), dialkylene triamine-penta-(alkylene phosphonic acids such as diethylene triamine-penta-(methylene phosphonic acid) and so on.

(34) Phosphorus free acidic substances include hydroxyacids which may be monocarboxylic acids with one or more hydroxyl groups such as glycolic acid, lactic acid, mandelic acid, 2,2-bis-(hydroxymethyl)-propionic acid, 2,2-bis-(hydroxymethyl)-butyric acid, 2,2-bis-(hydroxymethyl)-valeric acid, 2,2,2-tris-(hydroxymethyl)-acetic acid and 3,5.dihydroxybenzoic acid, dicarboxylic acids with one or more hydroxyl groups such as tartaric acid and tricarboxylic acids with one or more hydroxyl groups such as citric acid. Phosphorus free acidic substances also include polymers of methacrylic acid, acrylic acid and maleic anhydride or maleic acid as well as copolymers thereof such as acrylate-acrylic acid copolymers, olefin-maleic anhydride copolymers like isobutylene-maleic anhydride copolymers, styrene-maleic acid copolymers and vinyl alkyl ether-maleic acid copolymers like poly(vinyl methyl ether-co-maleic acid). Phosphorus free acidic substances further include azoles and their derivatives containing two or more heteroatoms such as 1,2,3-benzotriazole, tolytriazole, benzothiazole, 2-mercaptobenzothiazole, benzimidazole, 2-mercaptobenzimidazole, benzoxazole, 2-mercaptobenzoxazole and (2-benzothiazolylhio)succinic acid.

(35) Basic substances include alkanolamines, which may be a monoalkanolamine, a dialkanolamine, a trialkanolamine, these being primarily the ethanolamines and their N-alkylated derivatives, 1-amino-2-propanols and their N-alkylated derivatives. 2-amino-1-propanols and their N-alkylated derivatives and 3-amino-1-propanols and their N-alkylated derivatives or a mixture thereof. Examples of suitable monoalkanolamines include 2-aminoethanol(ethanolamine), 2-(methylamino)-ethanol, 2-(ethylamino)-ethanol, 2-(butylamino)-ethanol, 1-methyl ethanolamine (isopropanolamine), 1-ethyl ethanolamine, 1-(m)ethyl isopropanolamine, n-butylethanolamine, cyclohexanolamine, cyclohexyl isopropanolamine, n-butylisopropanolamine, 1-(2-hydroxypropyl)-piperazine, 4-(2-hydroxyethyl)-morpholine and 2-Amino-1-propanol. Examples of suitable di-alkanolamines are diethanolamine (2,2-iminodiethanol), 3-amino-1,2-propanediol, 2-amino-1,3-propanediol, diisobutanolamine (bis-2-hydroxy-1-butyl)amine), dicyclohexanolamine and diisopropanolamine (bis-2-hydroxy-1-propyl)amine). An example of a suitable trialkanolamine is tris(hydroxymethyl)aminomethane. Cyclic aliphatic amines may also be used such as morpholine, piperazine and their N-alkyl derivatives as well as fatty amines. Mixtures of any of the above phosphorus containing, phosphorus free or amine substances are also suitable. Also included are azole derivatives with amine functionality, such as 3-amino-1,2,4-triazole.

(36) Preferred stabilizing or complexing agents include phosphorus acid, phosphoric acid, tri- and polyphosphoric acids and organophosphonic acids containing one or more phosphonic acid groups per molecule such as 2-hydroxyphosphonoacetic acid, together with monocarboxylic acids and dicarboxylic acids with one or more hydroxyl groups per molecule such as glycolic acid. Preferred stabilizing or complexing agents include azole derivatives, such as 1,2,3-benzotriazole, 2-mercaptobenzothiazole and (2-benzothiazolylhio)succinic acid.

(37) Another embodiment of the present invention relates to a method of making a dispersion of surface modified inorganic particles including mixing the surface modified inorganic particles and a fluid and milling the inorganic particles to form particles having an average diameter of about ten microns or less, wherein the inorganic oxide particles are surface modified with polyvalent metal ions.

(38) In this embodiment, dispersions of small particles where the dispersions contain inorganic particles are obtained in the presence of polyvalent cations by wet-milling techniques, with addition of the suitable acidic, basic or complexing substances described above prior to milling whereby pH is adjusted and/or cations are complexed. The cations are present intentionally or are present as a result of prior preparation techniques. In some cases, the added substance may be a soluble or partially soluble component of the corrosion inhibiting composition that is to be milled and extra additions of the substance may not then be necessary. Stable dispersions are thereby obtained, avoiding or minimizing excessive viscosity build-up, reagglomeration of particles and hard settling that may otherwise occur during or after wet milling.

(39) The average particle sizes produced are about 10 microns or less and all or most of the particles in the dispersion may be less than 1 micron. The particles may be non-porous, substantially non-porous or porous according to the nature of the inorganic oxide used in the process or prepared during the overall process of preparing the inhibitor. In the light of the previous discussion, porosities may therefore vary up to about 3 ml/g. Milling may commonly be carried out in an aqueous phase but may also be carried out in a non-aqueous phase. For the non-aqueous embodiments, suitable solvents may be any of the known solvents commonly used in coatings applications such as alcohols, esters, ketones, glycol ethers, aromatic and aliphatic hydrocarbons, as well as aprotic solvents such as N-Methyl pyrrolidone, N-Ethyl pyrrolidone, Dimethyl sulphoxide, N,N-Dimethylformamide and N,N-Dimethylacetamide. For the case where the particles already exist as suitably small particles but in an aqueous phase either as a consequence of particle formation and growth in that phase, a situation encompassed by the embodiments described earlier, or as a result of milling larger particles in the aqueous phase, the inorganic oxides may be transferred to any of the solvent classes mentioned above by techniques known in the prior art. Examples are those discussed in the Journal of Colloidal & Interface Science 197, 360-369, 1998 A. Kasseh & E. Keh, Transfers of Colloidal Silica from water into organic solvents of intermediate polarities and the Journal of Colloidal & Interface Science 208, 162-166, 1998 A. Kasseh & E. Keh, Surfactant mediated transfer of Colloidal Silica from water into an immiscible weakly polar solvent or recited in U.S. Pat. Nos. 2,657,149, 2,692,863, 2,974,105, 5,651,921, 6,025,455, 6,051,672, 6,376,559 and GB Patent No. 988,330, the entire subject matter of which is incorporated herein by reference. Introduction of polyvalent cations, stabilizing and complexing components and/or combination with sparingly soluble salts may occur prior to solvent transfer or following solvent transfer.

(40) The corrosion inhibiting particles may be included in protective and adhesion promoting coatings and layers, such as surface pretreatments, surface films, anti-corrosive primers, adhesives and sealants and the present invention includes protective coatings and adhesion promoting coatings and layers containing corrosion inhibiting particles as described above. The protective coatings and adhesion promoting coatings and layers may be based on any of the known types of organic and inorganic chemistries used in anti-corrosion e.g. epoxy resins, polyesters resins, phenolic resins, amino resins such as melamine-formaldehyde, urea-fomaldehyde or benzoguanamine resins, vinyl resins, alkyd resins, chlorinated rubbers or cyclised rubbers, acrylic and styrene-acrylic chemistries, styrene.butadiene resins, epoxy-esters, silicate based coatings such as zinc-rich silicates, sol-gel coatings based on alkyl silicates and/or colloidal silicas, films, treatments and coatings derived from organofunctional silanes, as well as acidic or alkaline metal pretreatment solutions and primer-pretreatment solutions.

EXAMPLES

(41) The following Examples are given as specific illustrations of the claimed invention. It should be understood, however, that the invention is not limited to the specific details set forth in the Examples.

Example 1

(42) A 10 L Drais Laboratory Pearl mill (available from Draiswerke, Inc,) is filled with 1.2 Kg of ZrO.sub.2 beads (0.6-1 mm in diameter). An aqueous slurry of Shieldex C303 pigment (available from W. R. Grace & Co.), having an average particle size of 3-4 m, to which is added a small amount of 2-hydroxyphosphonoacetic acid is circulated for 6 hours at a rotor speed of 2800 rpm (slow setting) and at a pump speed of 40% of the maximum. Subsequently, 0.2% by weight of Acticide 1206 bacteriacide (available from Thor Chemicals) is mixed in. The suspension of Shieldex C303 pigment and water is stirred for 1 hour at room temperature before addition under mixing of the solution of 2-hydroxyphosphonoacetic acid. This causes the pH to drop from 8.42 to 8.04. The composition of the slurry in % by weight is Shieldex C303 pigment 16.21%; water 72.93%; 10.66% of a 5% aqueous solution of 2-hydroxyphosphonoacetic acid and 0.2% Acticide 1206 bacteriacide.

(43) Following milling, a free flowing dispersion of Ca/SiO2 particles results, having an average particle size of about 0.3 m which remains stable on storage for more than 90 days. 98% of the particles are less than 1 m. Particle size is determined with a Mastersizer 2000 light scattering equipment available from Malvern Instruments.

Example 2

Comparative

(44) The above example is repeated except that 2-hydroxyphosphonoacetic acid is not added to the mixture. This led to a fairly viscous dispersion in which the particles reagglomerated on milling, with a reagglomeration peak appearing at an average size of about 10 m.

Example 3

Comparative

(45) 2-hydroxyphosphonoacetic acid is again not added and different milling conditions are adopted. A 2 L vertical laboratory pearl mill (available from Draiswerke, Inc.), half filled with ZrO.sub.2 beads (0.6-1 mm in diameter) is used at a rotor speed of 2000 rpm. Milling is carried out for 6 hours. The resulting dispersion has a greater tendency to reagglomerate, becoming more viscous with a peak appearing at a size of about 10 to 100 m.

Example 4

(46) An anti-corrosive pigment is prepared in-situ by reacting together silica gel, having a particle size of 3-4 m (available from W. R. Grace & Co.Conn.), Ca(OH).sub.2, and 2-hydroxyphosphonoacetic acid. The resultant mixture is then subjected to pearl milling for about 30 minutes in a laboratory Dispermat mill (available from DISPERMAT) using 1 mm glass beads at a rotor speed of 1800 rpm. This results in a free flowing dispersion of Ca/SiO.sub.2/HPA particles having an average particle size of about 2 m. The composition of the slurry in % by weight is silica gel 5.60%; water 81.12%; 5.52% Ca(OH).sub.2 and 7.76% of a 50% aqueous solution of 2-hydroxyphosphonoacetic acid. After adding the Ca(OH).sub.2 to the suspension of silica in water, the mixture is aged for 16 hours at 40 C. prior to adding the solution of 2-hydroxyphosphonoacetic acid at a rate such that the pH does not drop below 9. The reaction mixture is aged at 90 C. for 1 hour prior to cooling and milling. The particles in the milled dispersion do not reagglomerate after sitting for over 90 days, and the dispersion may be added to a variety of protective coating formulations.

Example 5

(47) Anti-corrosive tests are carried out on Example 1 and compared to the Shieldex C303 pigment alone, since the dispersions of Examples 2 and 3 are not stable. In the absence of being able to apply coatings down to a thickness of a micron or so, tests are carried out in a water-borne acrylic coating applied by applicator bar to Sendzimir galvanized steel (i.e., Chemetall Test Panels) so as to obtain a dry film thickness of about 40 m in order to assess whether the dispersion offers any improvements in anti-corrosive performance compared to Shieldex C303 pigment alone. The formulations employed are given below in Table 3, in which the dispersion is incorporated by simple stirring, whereas Shieldex C303 pigment is incorporated with the aid of glass beads in the normal way.

(48) After 7 days of drying at room temperature, the coated panels are scribed and subjected to salt spray (using ASTM B117) for 240 hours, after which the panels are briefly rinsed, dried and evaluated within 30 minutes of withdrawal from the salt spray cabinet. The results are given in Table 1, where ratings are given on a scale of 0 to 5 in which 0 signifies no breakdown and 5 signifies complete breakdown.

(49) TABLE-US-00001 TABLE 1 Salt spray results for Example 1 against Shieldex C303 pigment in a water-borne acrylic coating on galvanized steel (Ratings are from 0 to 5 with 0 being best) Crosshatch Scribe Adhesion Blistering Adhesion Loss Loss Rusting Shieldex 0 3 5 2 C303 pigment Example 1 0 1 2 0

(50) The results in Table 1 show that improvements in anti-corrosive performance are found for the dispersion of the present invention compared to a commercial product coupled with simpler incorporation.

Example 6

(51) Anti-corrosive tests are also carried out on Example 4. In this case, a zinc-free dispersion of the present invention is compared against a commercially available zinc based anti-corrosive pigment (Heucophos ZPO anticorrosive pigments available from Heubach GmbH) commonly used in water-borne acrylic coatings. Shieldex AC5, a commercially available zinc-free anti-corrosive pigment is also included in the testing as a reference. Coatings are applied by applicator bar to cold rolled steel (Q-Panels S412 available from the Q-Panel Co.) so as to obtain a dry film thickness of about 40 m. The formulations employed are given below in Table 3, where again the dispersion is incorporated by simple stirring, but Heucophos ZPO pigment is incorporated with the aid of glass beads as referenced herein.

(52) As in Example 5, the coated panels are scribed and subjected to salt spray (using test ASTM B117) for 240 hours, after 7 days of drying at room temperature. Subsequently, the panels are briefly rinsed, dried and evaluated within 30 minutes of withdrawal from the salt spray cabinet. The results are given in Table 2, where again ratings are given on a scale of 0 to 5 in which 0 signifies no breakdown and 5 signifies complete breakdown.

(53) TABLE-US-00002 TABLE 2 Salt spray results for Example 4 on cold rolled steel against a standard zinc-based anti-corrosive pigment and a standard zinc-free pigment in a water-borne acrylic coating (Ratings are from 0 to 5 with 0 being best) Scribe Adhesion Crosshatch Blistering Loss Adhesion Loss Rusting Heucophos ZPO 0 1 0 1 pigment Shieldex AC5 3 3 5 4 pigment Example 4 0 1 0 1

(54) The results in Table 2 demonstrate that a zinc-free dispersion according to the present invention provides superior anticorrosion properties over commercially available heavy metal and zinc-free coatings.

(55) TABLE-US-00003 TABLE 3 Water-Borne Acrylic Formulations to assess Example 1 on galvanized steel against Shieldex C303 anticorrosive pigment and Example 4 on cold rolled steel against a standard zinc-based anti-corrosive pigment and a standard zinc-free pigment. 1 2 3 4 5 1). Neocryl XK-85 11.20 11.20 9.84 11.20 9.90 2). Water 5.23 5.23 0.88 5.23 0.88 3). Drew 210-693 0.14 0.14 0.12 0.14 0.12 4). Disperse-Ayd W33 1.43 1.43 1.26 1.43 1.26 5). Acrysol TT935 0.29 0.29 0.25 0.29 0.26 6). Water 0.30 0.30 0.26 0.30 0.27 7). Ser-AD FA179 0.48 0.48 0.42 0.48 0.42 8). Butyl Glycol 2.15 2.15 1.89 2.15 1.90 9). Neocryl BT-24 2.74 2.74 2.41 2.64 2.42 10). Aerosil R972 0.57 0.57 0.52 0.57 0.52 11a). Shieldex C303 3.39 11b). Shieldex AC5 3.39 11c). Example 1* 19.87 11d). Heucophos ZPO 6.72 11e). Example 4* 17.68 12). TiO.sub.2 Kronos 2190 4.31 4.31 3.79 4.15 3.81 13). Talc 20MOOS 10.18 10.18 8.94 9.81 10.69 14). Hostatint Black 0.81 0.81 0.71 0.78 0.72 GR-30 15). Neocryl XK-85 44.66 44.66 39.24 42.64 39.48 16). Texanol 1.11 1.11 0.98 1.08 0.98 17). Nacorr 1652 1.91 1.91 1.68 1.91 1.69 18). Resydrol AX 237W 5.06 5.06 4.45 4.88 4.47 19). Butyl Glycol 2.42 2.42 2.13 2.25 2.14 20). Octa Soligen 0.06 0.06 0.05 0.05 0.05 Co-10% 21). Ammonia 25% 0.36 0.36 0.32 0.34 0.32 22). Water 1.20 1.20 0.96 100.00 100.00 100.00 100.00 100.00 *The dispersions had a concentration of about 15% by weight.

Example 7

(56) Calcium hydroxide (3.1 g) and 1,2,3-benzotriazole (BTA) (26.9 g) in a 1:5 molar ratio are added under stirring to water (70 g) so as to achieve a solution having a solid content of 30% by weight. To 100 g of LUDOX AM silica (an aluminate modified colloidal silica obtainable from W. R. Grace & Co.Conn., having a solid content 0f 34% by weight), 20 g of the BTA containing solution is added slowly under stirring to produce a fine particle dispersion having a calcium content of 0.25 mmoles/g silica and a BTA content of 0.15 g/g silica, expressed alternatively as 6.3% by weight of BTA based on the total water content of the dispersion. The pH of the dispersion is 8.5. Adding calcium hydroxide without BTA led to immediate gelation.

Example 8

(57) The anti-corrosive properties of example 7 are determined as follows. To 100 g of the dispersion of example 7, 0.39 g of sodium chloride is added under stirring so that after dissolution, the concentration of sodium chloride based on the total water content of the dispersion is about 0.1M. Aluminium alloy 2024-T3 was used as the test electrode in a three electrode configuration employing a saturated Ag/AgCl reference electrode and a platinum counter electrode in which the sodium chloride containing dispersion is used as the electrolyte. Four hours after the test electrode came into contact with the electrolyte, a current-voltage curve is generated by sweeping 250 mV either side of the rest potential under potentiodynamic conditions using Gi118AC electrochemical corrosion test equipment (available from ACM Instruments). The slope of the curve 10 mV either side of the rest potential is used as a measure of corrosion inhibition in which the slope has units of resistance. Three comparisons are employed. The first involved adding 0.39 g of NaCl under stirring to 100 g of LUDOX AM silica to produce a dispersion about 0.1M in NaCl without calcium or BTA. The second involved preparing a solution of calcium hydroxide (0.767 g) and BTA (6.684 g) in a 1:5 molar ratio in 0.1M NaCl (100 g) so that the resulting concentration of BTA is 6.3% by weight of BTA based on the total water content of the solution. The third is simply a 0.1M sodium chloride solution. The results are shown in Table 4.

(58) TABLE-US-00004 TABLE 4 Slope of the current-voltage curve 10 mV either side of the rest potential on 2024-T3 aluminum alloy after 4 hours of contact with inhibited electrolytes, 0.1M in sodium chloride. Appearance of curre nt- Inhibitor Slope (ohms .Math. cm.sup.2) voltage curve Example 7 ~10.sup.6 Smooth LUDOX AM silica ~10.sup.7 Jagged Ca/BTA ~10.sup.3 Smooth BLANK Unmeasurable Unstable
As can be seen, both Example 7 and LUDOX AM silica provide evidence of corrosion inhibition on 2034-T3 compared to BTA alone and the blank, but only Example 7 provides stable inhibition as evidenced by a high slope and a smooth curve, where a jagged curve is indicative of alternating surface breakdown and repair.

(59) While the invention has been described with a limited number of embodiments, these specific embodiments are not intended to limit the scope of the invention as otherwise described and claimed herein. It may be evident to those of ordinary skill in the art upon review of the exemplary embodiments and description herein that further modifications and variations are possible. All parts and percentages in the examples, as well as in the remainder of the specification, are by weight unless otherwise specified. Further, any range of numbers recited in the specification or claims, such as that representing a particular set of properties, units of measure, conditions, physical states or percentages, is intended to literally incorporate expressly herein by reference or otherwise, any number falling within such range, including any subset of numbers within any range so recited. For example, whenever a numerical range with a lower limit, R.sub.L, and an upper limit R.sub.U, is disclosed, any number R falling within the range is specifically disclosed. In particular, the following numbers R within the range are specifically disclosed: R=R.sub.L+k(R.sub.UR.sub.L), where k is a variable ranging from 1% to 100% with a 1% increment, e.g., k is 1%, 2%, 3%, 4%, 5% . . . 50%, 51%, 52% . . . 95%, 96%, 97%, 98%, 99%, or 100%. Moreover, any numerical range represented by any two values of R, as calculated above is also specifically disclosed. Any modifications of the invention, in addition to those shown and described herein, will become apparent to those skilled in the art from the foregoing description. Such modifications are intended to fall within the scope of the appended claims.