Organic thin film transistor with charge injection layer and manufacturing method thereof

Abstract

The invention provides an OTFT and manufacturing method thereof. The OTFT comprises: a substrate; a source/drain electrode layer, formed on the substrate; an organic semiconductor layer, formed on the source/drain electrode layer; an organic insulating layer, formed on the organic semiconductor layer; a charge injection layer, formed on the organic insulating layer; a gate electrode layer, formed on the charge injection layer. The invention also provides a corresponding manufacturing method. The OTFT of the invention provides a novel structure for organic thin film transistor to improve the OTFT device stability; the OTFT prepared by the manufacturing method of OTFT of the present invention improves the OTFT device stability.

Claims

1. An organic thin film structure (OTFT), comprising: a substrate; a source/drain electrode layer, formed on the substrate; an organic semiconductor layer, formed on the source/drain electrode layer; an organic insulating layer, formed on the organic semiconductor layer; a charge injection layer, formed on the organic insulating layer; a gate electrode layer, formed on the charge injection layer; wherein a material of the organic semiconductor layer is pentacene or poly (3-hexylthiophene); wherein a material of the charge injection layer is silica prepared by a sol-gel method; and wherein the material of the charge injection layer is prepared by mixing tetraethylorthosilicate (TEOS), ethanol, water, and HCL in a mass ratio of 1:10:3.5:0.003.

2. The organic thin film structure as claimed in claim 1, wherein a material of the source/drain electrode layer is gold, silver, or indium tin oxide.

3. The organic thin film structure as claimed in claim 1, wherein a material of the organic insulating layer is poly (4-ethylphenol) or cytop.

4. The organic thin film structure as claimed in claim 1, wherein a material of the gate electrode layer is gold, aluminum, or copper.

5. A manufacturing method of organic thin film transistor (OTFT), comprising: Step 1: forming a source/drain electrode layer on a substrate; Step 2: forming an organic semiconductor layer on the source/drain electrode layer, and then covering with an organic insulating layer; Step 3: forming a charge injection layer on the organic insulating layer; Step 4: forming a gate electrode layer on the charge injection layer; wherein a material of the charge injection layer is silica prepared by a sol-gel method, and the material of the charge injection layer is prepared by mixing tetraethylorthosilicate (TEOS), ethanol, water, and HCL in a mass ratio of 1:10:3.5:0.003.

6. An organic thin film structure (OTFT), comprising: a substrate; a source/drain electrode layer, formed on the substrate; an organic semiconductor layer, formed on the source/drain electrode layer; an organic insulating layer, formed on the organic semiconductor layer; a charge injection layer, formed on the organic insulating layer; a gate electrode layer, formed on the charge injection layer; wherein a material of the source/drain electrode layer is gold, silver, or indium tin oxide; wherein a material of the organic semiconductor layer is pentacene or poly (3-hexylthiophene); wherein a material of the organic insulating layer is poly (4-ethylphenol) or cytop; wherein a material of the charge injection layer is silica prepared by a sol-gel method, and the material of the charge injection layer is prepared by mixing tetraethylorthosilicate (TEOS), ethanol, water, and HCL in a mass ratio of 1:10:3.5:0.003.

7. The organic thin film structure as claimed in claim 6, wherein a material of the gate electrode layer is gold, aluminum, or copper.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) To make the technical solution of the embodiments according to the present invention, a brief description of the drawings that are necessary for the illustration of the embodiments will be given as follows. Apparently, the drawings described below show only example embodiments of the present invention. In the drawings:

(2) FIG. 1 is a schematic view showing a conventional OTFT;

(3) FIG. 2 is a schematic view showing the Vth left drift of a conventional OTFT;

(4) FIG. 3 is a schematic view showing the OTFT structure of a preferred embodiment of the present invention;

(5) FIG. 4 is a schematic view showing the Vth left drift of the OTFT of a preferred embodiment of the present invention;

(6) FIGS. 5-8 are schematic views showing a flowchart of the OTFT manufacturing method of a preferred embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(7) Referring to FIG. 3, FIG. 3 is a schematic view showing the OTFT structure of a preferred embodiment of the present invention. The OTFT of the present invention comprises: a substrate 20; a source/drain electrode layer 21, formed on the substrate 20; an organic semiconductor layer 22, formed on the source/drain electrode layer 21; an organic insulating layer 23, formed on the organic semiconductor layer 22; a charge injection layer (CIL) 24, formed on the organic insulating layer 23; a gate electrode layer 25, formed on the charge injection layer 24. The remaining structure included in the conventional OTFT will not be described here. The following only describes the structure related to the present invention.

(8) The main feature of the present invention is to add a charge injection layer 24 between the gate electrode layer 25 and the organic insulating layer 23 so that the OTFT, when under NBTS, can trap electrons in the charge injection layer 24 to make Vth shift to right so as to compensate the Vth left shift caused by hole trapped at the interface between the organic semiconductor layer 22 and the organic insulating layer 23 to reduce the total Vth shift in the device.

(9) Referring to FIG. 4, FIG. 4 is a schematic view showing he Vth left drift of the OTFT of a preferred embodiment of the present invention. In FIG. 4, the horizontal axis represents the gate voltage Vg in volts and the vertical axis represents the drain current Id in amps. The corresponding time of the Vth curve increases from 0 second to 2000 seconds. By inserting the charge injection layer 24 between the gate electrode layer 25 and the organic insulating layer 23, when the gate electrode is in a negative bias voltage state (such as, Vgs=40V) for a long time, the electrons in the gate electrode are injected into the charge injection layer under a negative bias and trapped at the interface between the gate electrode and the charge injection layer. When Vgs=0V, these electrons trapped in the charge injection layer interface will induce holes to accumulate in the organic semiconductor layer, causing the device to turn on in advance and Vth to drift to the right. At the same time, the hole trapping at the interface between the organic semiconductor layer and the organic insulating layer causes the Vth to drift to the left and the total device Vth shift decreases.

(10) Referring to FIGS. 5-8, FIGS. 5-8 are schematic views showing a flowchart of the OTFT manufacturing method of a preferred embodiment of the present invention.

(11) The manufacturing method of organic thin film transistor (OTFT) of the present invention comprises:

(12) Step 1: forming a source/drain electrode layer 21 on a substrate 20. The source/drain electrode layer 21 corresponds to the source electrode/drain electrode of the OTFT, and the material may be conductive material with high work function, such as, gold (Au), silver (Ag) or indium tin oxide (ITO), as shown in FIG. 5.

(13) Step 2: forming an organic semiconductor layer 22 on the source/drain electrode layer 21, and then covering with an organic insulating layer 23. A patterned organic semiconductor layer material, such as, pentacene, poly (3-hexylthiophene) (P3HT), and so on, can be formed on the source/drain electrode layer 21 by vacuum evaporation or the like, and then covered with an organic insulating layer, such as, Poly (4-ethylphenol) (PVP), cytop, and so on, as shown in FIG. 6.

(14) Step 3: forming a charge injection layer 24 on the organic insulating layer 23. The material of the charge injection layer 24 is silica prepared by sol-gel method. The material of the charge injection layer is prepared by mixing tetraethylorthosilicate (TEOS), ethanol, water and HCL in a mass ratio of 1:10:3.5:0.003, as shown in FIG. 7.

(15) Step 4: forming a gate electrode layer 25 on the charge injection layer 24. The gate electrode layer 25 corresponds to forming a gate electrode, and the material can be gold (Au), aluminum (Al) or copper (Cu).

(16) In summary, the invention provides a novel structure for organic thin film transistor to improve the OTFT device stability; the OTFT prepared by the manufacturing method of OTFT of the present invention improves the OTFT device stability.

(17) It should be noted that in the present disclosure the terms, such as, first, second are only for distinguishing an entity or operation from another entity or operation, and does not imply any specific relation or order between the entities or operations. Also, the terms comprises, include, and other similar variations, do not exclude the inclusion of other non-listed elements. Without further restrictions, the expression comprises a . . . does not exclude other identical elements from presence besides the listed elements.

(18) Embodiments of the present invention have been described, but not intending to impose any unduly constraint to the appended claims. Any modification of equivalent structure or equivalent process made according to the disclosure and drawings of the present invention, or any application thereof, directly or indirectly, to other related fields of technique, is considered encompassed in the scope of protection defined by the claims of the present invention.