Polar modifier systems for high vinyl block copolymerization
11542355 · 2023-01-03
Assignee
Inventors
- Daniel Abraham Elizarrarás Maya (Tampico, MX)
- Christopher J. Hardiman (Farmington, CT)
- Sergio Corona Galván (Las Rozas, ES)
- Sergio Alberto Moctezuma Espiricueto (Altamira, MX)
- Luis Antonio Rodríguez Guadarrama (Madrid, ES)
Cpc classification
C08F297/04
CHEMISTRY; METALLURGY
C08F297/04
CHEMISTRY; METALLURGY
International classification
Abstract
Polar modifier systems based on a blend of DTHFP, ETE, TMEDA, DMTHFMA and/or functionally similar compounds with BDMAEE and SMT are used to make block copolymers having high levels of pendant vinyl double bond repeat units, which is through highly selective 1,2-bond butadiene addition, low vinylcyclopentane formation, unimodal narrow molecular weight distribution, and a low level of randomized co-monomer repeat units. The block copolymers have very high levels of 1,2-vinyl content and high 3,4-vinyl bond addition of the conjugated diene monomer and low vinylcyclopentane content. The polar modifier systems provide a fast polymerization rate, with a unimodal narrow molecular weight distribution. The polar modifier systems allow operation at a higher temperature than in prior art systems, which reduces cooling requirements.
Claims
1. A block copolymer having the formula:
(S-B)n-S, (B-S)n-B, or (S-B)n, wherein S is a vinyl aromatic polymer block, wherein S content in the block copolymer is from 10 to 40 wt %, wherein randomized vinyl aromatic repeat unit content is less than 15 wt % based on total vinyl aromatic content, wherein B is a conjugated diene polymer block, wherein the B block has a vinyl content of more than 85 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units, wherein n is a value from 1 to 5, wherein the B block has a VCP content of less than 6 wt % on a total conjugated diene basis, wherein the molecular weight distribution of the block copolymer has unimodal narrow peak shape with polydispersity of less than 1.08, and wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 50 to 300 kg/mol.
2. The block copolymer of any one of claim 1, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
3. The block copolymer of claim 2, wherein the vinyl content is more than 90 mol %.
4. The block copolymer of any one of claim 1, further comprising hydrogenating the block copolymer, thereby converting at least 90% of originally-existing double bonds of conjugated diene repeat units in the base block copolymer to single bonds.
5. The block copolymer of claim 1, wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 50 to 120 kg/mol.
6. The block copolymer of any one of claim 5, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
7. The block copolymer of claim 6, wherein the vinyl content is more than 90 mol %.
8. A block copolymer having the formula:
((S-B-)m)n-X, or ((B-S)m)n-X, wherein S is a vinyl aromatic polymer block, wherein S content in the block copolymer is from 10 to 40 wt %, wherein randomized vinyl aromatic repeat unit content is less than 15 wt % based on total vinyl aromatic content, wherein B is a conjugated diene polymer block, wherein the B block has a vinyl content of more than 85 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units, wherein the B block has a VCP content of less than 6 wt % on a total conjugated diene basis, wherein m is a value from 1 to 3, wherein n is a value from 2 to 4, wherein X is the residue of a coupling agent, wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 120 to 480 kg/mol, and wherein the block copolymer has more than 15 wt % of di-block un-coupled copolymer having the formula S-B.
9. The block copolymer of any one of claim 8, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
10. The block copolymer of claim 9, wherein the vinyl content is more than 90 mol %.
11. The block copolymer of any one of claim 8, further comprising hydrogenating the block copolymer, thereby converting at least 90% of originally-existing double bonds of conjugated diene repeat units in the base block copolymer to single bonds.
12. The block copolymer of claim 8, wherein the block copolymer having the formula ((S-B-)m)n-X has less than 15 w t% of di-block un-coupled copolymer having the formula S-B.
13. The block copolymer of any one of claim 12, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
14. The block copolymer of claim 13, wherein the vinyl content is more than 90 mol %.
15. The block copolymer of any one of claim 12, further comprising hydrogenating the block copolymer, thereby converting at least 90% of originally-existing double bonds of conjugated diene repeat units in the base block copolymer to single bonds.
16. The block copolymer of claim 8, wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 50 to 120 kg/mol.
17. The block copolymer of any one of claim 16, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
18. The block copolymer of claim 17, wherein the vinyl content is more than 90 mol %.
19. A block copolymer having the formula:
S-B-S-f or ((S-B)n-)-f, wherein S is a vinyl aromatic polymer block, wherein S content in the block copolymer is from 10 to 40 wt %, wherein randomized vinyl aromatic repeat unit content is less than 15 wt % based on total vinyl aromatic content, wherein B is a conjugated diene polymer block, wherein the B block has a vinyl content of more than 85 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units, wherein the B block has a VCP content of less than 6 wt % on a total conjugated diene basis, wherein f is an end group with an —OH or an —NH—R moiety, wherein n is a value from 1 to 5, wherein R is a benzylidene-methyl moiety, wherein the molecular weight distribution of the block copolymer has unimodal narrow peak shape with polydispersity of less than 1.08, and wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 50 to 300 kg/mol.
20. The block copolymer of any one of claim 19, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
21. The block copolymer of claim 20, wherein the vinyl content is more than 90 mol %.
22. The block copolymer of any one of claim 19, further comprising hydrogenating the block copolymer, thereby converting at least 90% of originally-existing double bonds of conjugated diene repeat units in the base block copolymer to single bonds.
23. The block copolymer of claim 19, wherein the GPC peak molecular weight Mp of the block copolymer relative to polystyrene standards is from 50 to 120 kg/mol.
24. The block copolymer of any one of claim 23, wherein the block copolymer has a vinyl content of more than 87 mol % on a conjugated diene repeat unit basis, including 1,2-vinyl, 3,4-vinyl and vinylcyclopentane (VCP) repeat units.
25. The block copolymer of claim 24, wherein the vinyl content is more than 90 mol %.
Description
(1) A better understanding of the invention can be obtained when the detailed description of exemplary embodiments set forth below is considered in conjunction with the attached drawings in which:
(2)
(3)
(4)
(5)
(6)
DETAILED DESCRIPTION OF THE EXEMPLARY EMBODIMENTS
(7) The anionically polymerized polymers can be made by any suitable method known in the art, such as those described in U.S. Pat. Nos. 3,281,383 and 3,753,936. In these methods, the anionically polymerized polymers are made by contacting anionically polymerizable monomers with an organolithium compound as an initiator. The preferred class of these compounds can be represented by the formula RLi wherein R is a hydrocarbon radical selected from the group consisting of aliphatic, cycloaliphatic, and aromatic radicals containing from 1 to 20 carbon atoms, although higher molecular weight initiators can be used. Many anionic polymerization initiators are well known and commercially available. Monofunctional organolithium compounds, such as butyllithium, are examples of commonly used initiators. Specific examples of these initiators include methyllithium, ethyllithium, tert-butyllithium, sec-butyllithium, n-butyllithium, n-decyllithium, isopropyllithium, eicosyllithium, cycloalkyllithium compounds, such as cyclohexyllithium, and aryllithium compounds, such as phenyllithium, naphthllithium, p-toluyllithium, 1,1-diphenylhexyllithium, and the like. Monofunctional organolithium compounds substituted with protected polar functional groups may also be used as initiators for anionic polymerization.
(8) The amount of initiator varies depending upon the desired molecular weight of the anionically polymerized polymer. Number average molecular weights between about 20,000 and 500,000 can be obtained by adding about 0.20 to 5.0 millimoles of the RLi initiator per mole of monomers corrected by the factor 100/(MW of monomer).
(9) Multifunctional organolithium initiators may also be used as initiators to prepare branched and radial copolymers with a desired functionality range of 2 to about 30 anionically polymerized polymers chains per initiator molecule. Multifunctional organolithium initiators are readily prepared by direct addition reaction of a stoichiometric amount of a monofunctional organolithium compound to a polyvinyl compound such as 1,3-diisopropenyl benzene, 1,3,5-tri isopropenyl benzene, 1,3-bis(1-phenylethenyl)benzene, 1,3,5-tris(1-phenylethenyl)benzene, 1,3-divinylbenzene, 1,3,5-trivinylbenzene, and the like. Oligomeric polyvinyl compounds may be used to prepared multifunctional organolithium initiators with high functionality. Monofunctional organolithium compounds, such as butyllithium, are examples of commonly used initiators for the above addition reaction. Specific examples of these commonly used initiators include tert-butyllithium, sec-butyllithium, and n-butyllithium. Monofunctional organolithium compounds substituted with protected polar functional groups may also be used to prepare multifunctional organolithium initiators. Multifunctional organolithium compounds may be combined among them and/or with monofunctional organolithium compounds to partially initiate anionic polymerization with the multifunctional organolithium compound. The partial initiation is achieved by controlling the stoichiometric ratio of multifunctional initiator to monofunctional initiator.
(10) Anionic polymerization is typically carried out in inert hydrocarbon solvents at relatively low temperatures under vacuum or an inert atmosphere with highly purified reagents in order to prevent the premature termination of the polymerization reaction. The anionic polymerization reactions may take place in a variety of organic solvents. Examples of suitable solvents include, but are not limited to, pentane, hexane, heptane, octane, cyclopentane, cyclohexane, cycloheptane, benzene, naphthalene, toluene, xylene, methyl ether, methyl ethyl ether, diethyl ether, tetrahydrofuran, acetone, methyl ethyl ketone, and mixtures thereof. Cyclohexane in particular, is well suited for use as the solvent in anionic polymerizations.
(11) The anionic polymerization is normally carried out at temperatures in the range from −100° C. to 150° C., preferably between −75° C. and 75° C. Normally 50 to 90% by weight of a reaction solvent is used to control the viscosity inside the reaction zone, preferably 70 to 85%. Typical residence times for anionic polymerization vary depending on the reaction temperature and initiator level between 0.1 and 5 hours, preferable from 0.2 to 2 hours.
(12) Suitable conjugated dienes for use in building the anionically polymerized polymers of the present invention include, but are not limited to, 1,3 butadiene, isoprene, 1,3-pentadiene, methylpentadiene, phenylbutadiene, 2,3-dimethyl-1,3-butadiene, 2,4-hexadiene, 1,3-hexadiene, 1,3-cyclohexadiene, 3,4-dimethyl-1,3-hexadiene, 1,3-octadiene, 4,5-diethyl-1,3-octadiene, myrcene, farnesene and the like. Other anionically polymerizable monomers that may be used in the production of the anionically polymerized polymers include, but are not limited to, monovinyl aromatic monomers, such as styrene and styrene derivatives including 3-methylstyrene, α-methyl styrene, p-methyl styrene, α,4-dimethylstyrene, t-butyl styrene, o-chlorostyrene, 2-butenyl naphthalene, 4-t-butoxystyrene, 3-isopropenyl biphenyl, 4-vinylpyridine, 2-vinylpyridine and isopropenyl naphthalene, 4-n-propylstyrene. Functionalized conjugated diene monomers and functionalized monovinyl aromatic monomers that may be used in the production of the anionically polymerized polymers include, but are not limited to, silylated monomers, and the like.
(13) In some embodiments of the methods provided here, the anionically polymerized polymers undergo total or partial coupling to prepare branched and radial anionically polymerized polymers. Partial coupling means that a portion of the total living anionically polymerized polymer chain-ends undergo coupling with coupling agents. The coupling agents desirably couple between 2 and 30 anionically polymerized polymer chains, although coupling agents capable of coupling a greater number of chains may also be employed. Suitable coupling agents for use in the total or partial coupling step include, but are not limited to, epoxidized soybean oil, divinylbenzene, tin halides, silicon halides, functionalized tin compounds, functionalized silicon compound such as a silane compound and functionalized oligomeric compounds such as the ones listed in U.S. Pat. No. 7,517,934. The entire disclosure of U.S. Pat. No. 7,517,934 is incorporated herein by reference. Silicon tetrachloride and tin tetrachloride are specific examples of suitable coupling agents, with silicon tetrachloride being particularly well-suited for this application. The partial coupling is achieved by controlling the stoichiometric ratio of coupling agent to living polymer. The partial coupling may provide a polymer blend with desired properties.
(14) Organometallic compounds of different metals from Groups IIa, IIb and IIIa, including magnesium, zinc and aluminum, may be used as polymerization rate modifiers when mixed with alkyllithium initiators. Specific examples of suitable polymerization rate modifiers are dibutyl magnesium, diethyl zinc and triethyl aluminium. The polymerization rate modifiers may be used to control the temperature profile of polymerization. The polymerization rate modifiers contribute to control a polymerization step in either isothermal mode for a pre-established residence time or quasi-adiabatic mode up to a peak temperature.
(15) In some embodiments of the methods provided here, the anionically polymerized polymers are polymerized in batch, programmed-batch and/or semi-batch processes. In additional embodiments of the methods of the present invention, the anionically polymerized polymers may be prepared in continuous and/or semi-continuous mode. The anionic polymerization of the anionically polymerized polymers may take place in situ i.e., in a single reaction zone, or may take place in multiple reaction zones. The former design tends to favor faster reactions while the latter design may be preferred when specially controlled polymerization reactions are desired. In some embodiments, a reaction apparatus having two or more reaction zones (e.g., reaction chambers) may be employed.
(16) As one of skill in the art would recognize, the described synthesis of the anionically polymerized polymers can occur in a reaction setting comprising either a batch, a semi-continuous or a continuous process operated at temperatures, solvent ratios and stream flow rates necessary to reach the described residence time and stoichiometry conditions.
(17) The following examples have the purpose of showing the features of the present invention and are not intended to limit the scope thereof. Comparative examples using previous art technologies are included as reference. Characterization of copolymer microstructure was performed by 300 MHz .sup.1H-NMR technique, and molecular weight characterization using GPC with 3-column set, coupled to differential refractive index detector. Peak molecular weights and polydispersity indexes Mw/Mn reported are referred to calibration curve based on polystyrene standards with narrow molecular weight distribution.
(18) Example 1: Uncoupled SBS block copolymer using preferred polar modifier system of invention: High polar modifier system concentration, high molecular weight copolymer synthesis at low temperature range.
(19) Cyclohexane (5383 g) was charged in to a 7.6-liter stainless steel reactor under inert nitrogen atmosphere. Solvent temperature was stabilized in the reactor at 18.1° C. (Tst1) by means of water circulation through reactor internal coil. Thereafter BDMAEE, DTHFP, n-butyllithium initiator (nBuLi) initiator and SMT were added in the listed order. DTHFP, BDMAEE and SMT molar ratios relative to active lithium content were 4.17, 0.52 and 0.10, respectively. Styrene (84.5 g) was feed to the reactor at a rate adequate to complete its charge in 0.5 minutes. Circulation of water at controlled temperature was continued along first styrene block polymerization. Reactor temperature reached a peak temperature of 19.7° C. in 3 minutes, and a wait time of 2 minutes was practiced, therefore first block homopolymerization time was 5 min (tSt). Then reactor cooling was terminated and immediately after butadiene (344.7 g) was fed in a period of about 2 minutes. Temperature right at the start of butadiene feed was 19.2° C. (Ti-Bd). Butadiene polymerization reached a peak temperature of 43° C. (Tp-Bd), 9 minutes after beginning butadiene loading (tp-Bd). In every case butadiene polymerization occurred without circulation of water thru the jacket. There was a wait time of 3 minutes (twBd) before the second styrene (84.5 g) was fed to reactor. It was detected a peak temperature past 3 minutes of second styrene charge. Past 5 minutes an alcohol was fed to terminate polymer anions. Cyclohexane to overall monomer mass ratio in this procedure was 8. A block copolymer was obtained of following characteristics: Peak molecular weight Mp=277.8 kg/mol, polydispersity index Mw/Mn=1.06, total styrene repeat unit content of 31.9 wt %, random styrene repeat unit content of 3.9 wt %, total vinyl content of 90.9 wt % on a butadiene block basis (1,2-vinyl+VCP), and of 89.4 mol % on repeat unit basis, VCP content of 3.1 wt %. Molecular weight distribution of this SBS copolymer exhibited a unimodal narrow peak shape.
(20) Example 2: Uncoupled SBS block copolymerization using preferred polar modifier system of invention: Medium polar modifier concentration range, medium molecular weight copolymer synthesis at low temperature range.
(21) The block copolymer was prepared in a 5.3-liter lab scale batch thru the following steps: (1) charge of cyclohexane solvent to a reactor; (2) stabilization of solvent to a temperature Ti; (3) charge of polar modifiers BDMAEE and DTHFP; (4) charge of n-butyllithium; (5) charge of SMT; (6) charge of styrene monomer; (7) immediate interruption of reactor temperature control to perform polymerization in absence of external cooling or external heating, apart from natural heat loss to the environment (8) homopolymerization of first styrene block for a period of time tSt1, where heat of polymerization gradually raised reactor temperature without detection of temperature drop that evidenced a peak temperature during such period; (9) registration of reactor temperature TiBd and immediate charge of butadiene monomer; (10) butadiene block copolymerization, where heat of reaction raised reactor temperature to a peak temperature TpBd which was registered, as well as time tpBd elapsed from beginning of butadiene charge to the moment TpBd occurred; (11) wait time twBd; (12) charge of second styrene load; (13) polymerization of second polystyrene block until full consumption of styrene monomer; (14) charge of excess equivalents of an alcohol to assure termination of all polymer anions. In this formulation 2938 g of cyclohexane were used, 60.9 g of styrene were used to build polystyrene first block, 246.1 g of butadiene were used to build high vinyl polybutadiene middle block, and 60.9 g of styrene were used to build polystyrene end block. Thus, overall solvent to monomer ratio (S/M) was 8.0. Feed time of each styrene load was 0.5 minutes long. Feed time for butadiene load was 2 minutes long. Active n-butyllithium charge was 4.2 mmol DTHFP, BDMAEE and SMT molar ratios relative to active lithium content were 2.13, 0.27 and 0.05, respectively (See Table 1). First styrene charge was homopolymerized for 3 minutes, from a starting temperature of 10.8° C. to reach 15.0° C. High vinyl polybutadiene block polymerization evolved from a temperature of 15 to a peak temperature of 46.7° C. in 11 minutes (See Table 2). A block copolymer was obtained of following characteristics: total styrene repeat unit content of 34.6 wt %, random styrene repeat unit content of 3.3 wt %, total vinyl content of 87.6 wt % on a butadiene block basis (1,2-vinyl+VCP), total vinyl content of 85.8 mol % on repeat unit basis, VCP content of 3.7 wt % on a butadiene block basis. (See Table 3) Molecular weight distribution of this SBS copolymer exhibited a unimodal narrow peak shape, with molecular weight Mp=142.3 kg/mol and polydispersity index Mw/Mn=1.03; (See Table 4).
(22) Comparative example C1: Uncoupled SBS block copolymerization using polar modifier systems of closest prior art, BDMAEE/SMT at low temperature range.
(23) A block copolymer was prepared in the same 5.3-liter reactor of Example 2. Same procedure of example 2, as well as same amounts of cyclohexane, butadiene and styrene charges were employed. Prior art polar modifier system BDMAEE/SMT was evaluated. As in example 2, BDMAEE was fed before n-butyllithium initiator and SMT was fed after n-butyllithium. Active n-butyllithium charge was 4.4 mmol. BDMAEE and SMT molar ratios relative to active lithium content were 0.59 and 0.05, respectively (See Table 1). First styrene charge homo-polymerization took 11 minutes to reach 15.0° C. from a starting temperature of 10.7° C. High vinyl polybutadiene block polymerization evolved from a temperature of 15° C. to a peak temperature of 46.0° C. in 17 minutes (See Table 2). A block copolymer was obtained of following characteristics: total styrene repeat unit content of 33.7 wt %, random styrene repeat unit content of 4.3 wt %, total vinyl content of 90.6 wt % on a butadiene block basis (1,2-vinyl+VCP), total vinyl content of 88.7 mol % on repeat unit basis, VCP content of 3.8 wt % on a butadiene block basis. (See Table 3) Molecular weight distribution of this SBS copolymer exhibited a bimodal shape, with a main peak at a molecular weight Mp=123.7 kg/mol, and secondary peak at Mp2=178.9 kg/mol, with a polydispersity index Mw/Mn=1.08; (See Table 4 and
(24) Comparative example C2: Uncoupled SBS block copolymerization using polar modifier systems of closest prior art, BDMAEE/SMT at low temperature range. As in example 2, BDMAEE was fed before n-butyllithium initiator and SMT was fed after n-butyllithium. Active n-butyllithium charge was 4.4 mmol. BDMAEE and SMT molar ratios relative to active lithium content were 0.36 and 0.05, respectively (See Table 1). After 15 minutes of first styrene block homo-polymerization reactor temperature barely reached 13.6° C. from a starting temperature of 10.5° C. High vinyl polybutadiene block polymerization evolved from a temperature of 13.6° C. to a peak temperature of 41.2° C. in 42 minutes (See Table 2). A block copolymer was obtained of following characteristics: total styrene repeat unit content of 34.9 wt %, random styrene repeat unit content of 10.6 wt %, total vinyl content of 87.0 wt % on a butadiene block basis (1,2-vinyl+VCP), total vinyl content of 85.0 mol % on repeat unit basis, VCP content of 4.2 wt % on a butadiene basis. (See Table 3) Molecular weight distribution of this SBS copolymer exhibited a unimodal peak slightly skewed towards low molecular weight range, with a main peak at a molecular weight Mp=154.5 kg/mol and a polydispersity index Mw/Mn=1.05; (See Table 4 and
(25) A block copolymer was prepared in the same 5.3-liter reactor of Example 2. Same procedure of example 2, as well as same amounts of cyclohexane, butadiene and styrene charges were employed. Prior art polar modifier system BDMAEE/SMT was evaluated at lower dosage than in Comparative example C1.
(26) TABLE-US-00001 TABLE 1 Initiator and polar modifier system loadings in examples 1 and 2, according with the invention, and comparative examples C1 thru C6, using previous art. n-BuLi, DTHFP, BDMAEE, SMT, TMEDA, DMTHFMA, ETE, mmol mol/ mol/ mol/ mol/ mol/ mol/ Example active Li mol Li mol Li mol Li mol Li mol Li mol 1 3.1 4.17 0.52 0.10 0 0 0 2 4.2 2.13 0.27 0.05 0 0 0 C1 4.4 0 0.59 0.05 0 0 0 C2 4.4 0 0.36 0.05 0 0 0 C3 4.3 3.11 0 0 0 0 0 C4 4.9 0 0 0 0 0 9.3 C5 4.0 0 0 0.12 4.5 0 0 C6 4.6 0 0 0.10 0 3.9 0
(27) TABLE-US-00002 TABLE 2 Polymerization process parameters in examples 1 and 2, according with the invention, and comparative examples C1 thru C6, using previous art. Ti, tSt, Ti-Bd, Tp-Bd, tpBd, twBd, Example ° C. min ° C. ° C. min min 1 18.1 5 19.2 43 9 3 2 10.8 3 15.0 46.7 11 2 C1 10.7 11 15.0 46.0 17 5 C2 10.5 15 13.6 41.2 42 5 C3 10.8 5 14.9 44.6 21 11 C4 10.3 12 14.3 44.0 18 7 C5 10.7 4 15.0 47.6 14 11 C6 10.9 3 15.1 48.7 9 5
(28) TABLE-US-00003 TABLE 3 NMR characterization of SBS copolymer produced in in examples 1 and 2, according with the invention, and comparative examples C1 thru C6, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis 1 31.9 28.0 3.9 87.8 3.1 90.9 89.4 2 34.6 31.3 3.3 83.9 3.7 87.6 85.8 C1 33.7 29.4 4.3 86.8 3.8 90.6 88.7 C2 34.9 24.3 10.6 82.9 4.2 87.0 85.0 C3 34.0 30.2 3.8 78.2 3.0 81.2 79.7 C4 32.9 31.4 1.5 80.2 2.4 82.6 81.4 C5 34.8 31.7 3.1 79.1 4.2 83.3 81.2 C6 34.2 31.2 3.0 71.5 5.1 76.6 74.1
(29) TABLE-US-00004 TABLE 4 GPC characterization of SBS copolymer produced in example 1, according with the invention, and comparative examples C1 thru C6, using previous art. Mp, Example kg/mol Mw/Mn MWD Shape 1 277.4 1.06 Unimodal narrow peak 2 142.3 1.03 Unimodal narrow peak C1 123.7 1.08 Bimodal peak, Mp2 = 179 kg/mol C2 154.5 1.05 Unimodal peak, slightly skewed towards low MW C3 138.5 1.03 Unimodal narrow peak C4 123.7 1.02 Unimodal narrow peak C5 150.6 1.04 Unimodal narrow peak C6 130.3 1.04 Unimodal narrow peak
(30)
(31) When comparing speed of styrene homopolymerization stage of high vinyl copolymer obtained with polar modifier system of the invention DTHFP/BDMAEE/SMT, used in example 2, against prior art modifier system of prior art based on BDMAEE/SMT, used in comparative examples C1, it can be noticed that temperature rise to 15° C. of first styrene block homopolymerization occurred in almost four times shorter period with invention than with prior art. When comparing time to reach butadiene block stage peak temperature, tpBd, polar modifier of invention tested in example 2 enabled also faster butadiene polymerization than prior art used in example C1. In addition, a shorter wait time twBd was needed with invention polar modifier in example 2 than with prior art practiced in example C1 to obtain lower random styrene content in SBS copolymer. Moreover, in example 1 BDMAEE/Li ratio was half of that used in comparative example C1.
(32) When comparing molecular weight distribution obtained with polar modifier of invention DTHFP/BDMAEE/SMT, used in example 2, against prior art based on polar modifier system BDMAEE/SMT, of comparative example C1, it can be noticed that an unimodal narrow peak was obtained with invention, whereas a wide bimodal peak was obtained with prior art (see
(33) In comparative example C2, that evaluated prior art BDMAEE/SMT polar modifier system with a BDMAEE/Li ratio lower than in comparative example C1, but still higher amount of BDMAEE than in invention example 2, polymerization proceeded at still lower speed and incorporated much more random styrene repeat units in the copolymer. Its molecular weight distribution improved towards a unimodal peak, but still appeared slightly wider than that of invention example 2, and skewed towards low molecular weight range, evidencing some premature termination of polymer anions.
(34) Invention example 2, based on DTHFP/BDAMEE/SMT polar modifier system produced SBS block copolymer with very high level of 1,2-vinyl butadiene repeat units, slightly higher than what obtained in comparative example C2 based on polar modifier system of prior art BDMAEE/SMT. Advantageously, VCP level was slightly lower in invention example 2 than in comparative examples C1 and C2.
(35) When comparing invention example 2, based on DTHFP/BDMAEE/SMT polar modifier system against other prior art polar modifier systems, as DTHFP in comparative example C3, ETE in comparative example C4, TMEDA/SMT in comparative example C5 and DMTHFMA/SMT in comparative example C6, it can be noticed that invention polar modifier system conducts to faster polymerization than most of prior art polar modifier systems, and just slightly slower than with DMTHFMA/SMT system. Molecular weight distribution unimodality and narrowness of copolymer obtained by invention was competitive with these other polar modifier systems, as reveal by low values of polydispersity index Mw/Mn. Nevertheless, none of these other prior art polar modifier systems was capable of surpassing 1,2-vinyl incorporation level of invention. Moreover, TMEDA/SMT tried in comparative example C5 and DMTHFMA/SMT produced higher levels of VCP than invention example 1.
(36) Examples 3 thru 8: Uncoupled SBS block copolymerization using preferred polar modifier system invention, at medium temperature range. An S-b-B-b-S type block copolymer was prepared in a lab scale batch reactor thru the following steps: (1) charge of cyclohexane solvent to a reactor; (2) stabilization of solvent to a temperature Ti; (3) charge of polar modifiers BDMAEE and DTHFP; (4) charge of n-butyllithium; (5) charge of SMT; (6) charge of styrene monomer; (7) immediate interruption of reactor temperature control to perform polymerization in absence of external cooling or heating, apart from natural heat loss to the surroundings (8) homopolymerization of first styrene block, where heat of polymerization gradually raised reactor temperature up to a peak temperature TpSt at a time tpSt elapsed from beginning of styrene charge and such peak temperature; (9) a wait time of 10 minutes past TpSt, where a slight temperature drop occurred; (10) registration of reactor temperature TiBd and immediate charge of butadiene monomer; (11) butadiene block copolymerization, where heat of reaction raised reactor temperature to a peak temperature TpBd which was registered, as well as time tpBd elapsed from beginning of butadiene charge to the moment TpBd occurred; (12) wait time of 1 minute past TpBd, where a slight temperature drop occurred; (13) charge of second styrene load; (14) polymerization of second polystyrene block until full consumption of styrene monomer; (15) charge of excess equivalents of an alcohol to assure termination of all polymer anions. In this formulation 2795 g of cyclohexane were used, 63.6 g of styrene were used to build polystyrene first block, 246.1 g of butadiene were used to build high vinyl polybutadiene middle block, and 63.6 g of styrene were used to build polystyrene end block. Thus, overall solvent to monomer ratio was 7.5. Feed time of each styrene load was 0.5 minutes long. Feed time for butadiene load was 2 minutes long. Active initiator content and polar modifier molar ratios to initiator are shown in Table 5. High vinyl polybutadiene block was polymerized in a temperature range from 22.8 to 56.8° C. Process parameters Ti, TpSt, tpSt, TiBd, TpBd and tpBd are listed in Table 6. SBS copolymer characterization of product from this example is shown in Table 7 and Table 8.
(37) Examples 9 thru 11: Uncoupled SBS block copolymerization using alternative polar modifier system invention, at medium temperature range. The same operations listed in examples 3 thru 7 were employed, but DTHFP was replaced by either ETE, TMEDA or DMTHFMA. Active n-butyllithium and polar modifier system dosages for these examples are reported in Table 5. High vinyl polybutadiene block was polymerized in a temperature range from 23 to 59.8° C. Process parameters Ti, TpSt, tpSt, TiBd, TpBd and tpBd are listed in Table 6 for each example. SBS copolymer characterization of products from these examples is shown in Table 7 and Table 8.
(38) Comparative examples C7 and C8. Uncoupled SBS block copolymerization using polar modifier system of closest prior art, at medium temperature range. The same procedure described in examples 3 thru 7 was employed, but DTHFP was avoided. Active n-butyllithium and polar modifier system dosages for these comparative examples are reported in Table 5. High vinyl polybutadiene block was polymerized in a temperature range from 23.5 to 57° C. Process parameters Ti, TpSt, tpSt, TiBd, TpBd and tpBd are listed in Table 6 for each comparative example. SBS copolymer characterization of products from these comparative examples is shown in Table 7 and Table 8.
(39) TABLE-US-00005 TABLE 5 Initiator and polar modifier system loadings in example 3 thru 11, according with the invention, and comparative examples C7 and C8 using previous art. n-BuLi, DTHFP, ETE, TMEDA, DMTHFMA, BDMAEE, SMT, mmol mol/ mol/ mol/ mol/ mol/ mol/ Example active Li mol Li mol Li mol Li mol Li mol Li mol 3 4.7 2.60 0 0 0 0.74 0.06 4 3.8 3.02 0 0 0 0.80 0.04 5 4.4 0.36 0 0 0 0.61 0.05 6 4.0 2.17 0 0 0 0.58 0.05 7 4.0 2.15 0 0 0 0.27 0.05 8 5.9 1.95 0 0 0 0.52 0.02 9 4.8 0 2.52 0 0 0.72 0.05 10 4.0 0 0 3.03 0 0.87 0.07 11 5.0 0 0 0 2.41 0.69 0.05 C7 4.7 0 0 0 0 0.92 0.06 C8 4.7 0 0 0 0 0.74 0.06
(40) TABLE-US-00006 TABLE 6 Polymerization process parameters in example 3 thru 11, according with the invention, and comparative examples C7 and C8, using previous art. TpSt, tpSt, Ti-Bd, Tp-Bd, tpBd, Example Ti, ° C. ° C. min ° C. ° C. min 3 18.4 23.4 7 23.0 56.8 9 4 18.1 23.0 12 22.8 55.4 11 5 21.5 26.3 13 26.1 56.4 17 6 20.2 25.2 9 25.0 58.7 10 7 18.2 23.1 7 22.9 55.6 12 8 18.1 23.0 9 22.9 55.1 12 9 18.2 23.6 4 23.2 56.5 10 10 18.2 23.1 15 23.0 58.4 7 11 18.8 24.3 6 23.5 59.8 7 C7 18.3 23.5 15 23.5 57.0 10 C8 19.4 23.5 30 23.5 55.8 13
(41) TABLE-US-00007 TABLE 7 NMR characterization of SBS copolymer produced in in example 3 thru 11, according with the invention, and comparative examples C7 and C8, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis 3 34.3 33.3 1.0 84.1 4.7 88.8 86.5 4 34.9 32.8 2.1 83.3 4.2 87.5 85.4 5 34.3 32.7 1.6 83.5 3.7 87.2 85.3 6 34.1 33.1 1.0 82.7 4.6 87.3 85.0 7 34.2 32.5 1.7 81.9 3.9 85.7 83.9 8 34.3 33.2 1.1 80.9 4.2 85.1 83.0 9 34.6 33.6 1.0 83.4 4.1 87.5 85.5 10 34.9 32.5 2.3 83.3 6.8 90.1 86.7 11 33.0 32.5 0.5 81.9 4.6 86.4 84.2 C7 34.1 33.1 1.0 85.5 5.0 90.5 88.0 C8 34.3 32.6 1.7 86.2 4.1 90.4 88.3
(42) TABLE-US-00008 TABLE 8 GPC characterization of SBS copolymer produced in example 3 thru 11, according with the invention, and comparative examples C7 and C8, using previous art. Mp, Mw/ Example kg/mol Mn MWD Shape 3 129.8 1.04 Unimodal narrow peak 4 158.0 1.04 Unimodal narrow peak 5 137.6 1.06 Unimodal narrow peak 6 151.9 1.05 Unimodal narrow peak 7 150.1 1.05 Unimodal narrow peak 8 102.2 1.03 Unimodal narrow peak 9 125.8 1.07 Unimodal narrow peak 10 151.3 1.05 Unimodal narrow peak 11 121.5 1.04 Unimodal narrow peak C7 129.2 1.10 Bimodal peak, Mp2 = 183.8 kg/mol C8 175.7 1.08 Bimodal peak, Mp2 = 132.6 kg/mol
(43)
(44) In invention examples 3 thru 8, based on polar modifier system DTHFP/BDMAEE/SMT, polar modifier ratios of DTHFP, BDMAEE and SMT relative to active lithium were swept in a wide composition range.
(45) When comparing polymerization speed of invention examples 3 thru 8 based on DTHFP/BDMAEE/SMT against comparative examples C7 and C8 that used prior art BDMAEE/SMT polar modifier systems, most of compositions tried with invention polar modifier system obtained shorter polymerization times to reach first styrene block peak temperature and shorter times to reach butadiene polymerization peak temperature.
(46) Advantageously, molecular weight distributions of invention examples 3 thru 8, based on DTHFP/BDMAEE/SMT polar modifier system, in every case exhibited a narrow unimodal peak shape with low polydispersity index Mw/Mn, whereas comparative compositions C7 and C8, based on prior art BDMAEE/SMT polar modifier system, produced wide bimodal molecular weight distributions with high polydispersity index Mw/Mn.
(47) Invention examples 9 thru 11 show options of appropriate polar modifiers that can replace DTHFP component of DTHFP/BDMAEE/SMT polar modifier system. Namely, systems ETE/BDMAEE/SMT, TMEDA/BDMAEE/SMT and DMTHFMA/BDMAEE/SMT perform as well as DTHFP/BDMAEE/SMT, rendering high speed polymerization of very high vinyl content block copolymers, with unimodal narrow molecular weight distribution. DTHFP/BDMAEE/SMT polar modifier system is a preferred option, as ETE/BDMAEE/SMT conducts to slightly higher polydispersity index Mw/Mn, TMEDA/BDMAEE/SMT lags in styrene homopolymerization step and produces higher VCP contents, while DMTHFMA/BDMAEE/SMT produces slightly lower 1,2-vinyl content. Nevertheless, this alternative invention systems still surpass performance of prior art systems described.
(48) Although block copolymerization was carried out at higher temperature in invention examples 3 thru 11 than in comparative examples C2 thru C6, higher incorporation level of 1,2-vinyl content was obtained with the invention than with prior art also capable of producing narrowly molecular weight distributed SBS copolymer.
(49) Example 12. Uncoupled SBS block copolymerization using preferred polar modifier system invention, at high temperature range. An S-b-B-b-S type block copolymer was prepared in a lab scale stirred batch reactor, with relatively low thermal insulation level, using the following procedure: Cyclohexane (2720 g) was charged in to a stirred reactor under nitrogen atmosphere, and its temperature was stabilized at 43.3° C. (Ti). Thereafter BDMAEE, DTHFP, n-butyllithium initiator and SMT were added to the reactor in the listed order. Active initiator content and polar modifier molar ratios to initiator are shown in Table 9. Then, a first part of styrene monomer (56.4 g) was charged to the reactor. Styrene feed operation was completed in 0.5 minutes. Reactor temperature control was discontinued thereafter, thus polymerization was carried out in the absence of external cooling, nor external heating, apart from heat dissipation to the environment. A peak temperature of 46.2° C. (TpSt1) was detected passed 2 minutes of styrene load (tpSt1). Then, a wait time of 3 minutes was practiced. By then, reactor temperature dropped to 44.2° C. (TiBd) and butadiene (227.5 g) feed operation began. Butadiene charge was completed in 2 minutes. Butadiene heat of polymerization raised reactant mass to a peak temperature of 61.1° C. (TpBd) in a period of 5 minutes (tpBd), counted from start of butadiene feed operation. Then, a wait time of 2 minutes (twBd) was taken between butadiene polymerization peak temperature and the beginning of second styrene load. Second styrene load to reactor (56.4 g) took 30 seconds to get completed. Second styrene load was polymerized for long enough time to be fully consumed, and then an alcohol was feed to reactor to terminate anionic polymer anions. Cyclohexane solvent to overall monomer feed ratio (S/M) in this example was 8. Process parameters Ti, TpSt1, tpSt1, TiBd, TpBd, tpBd and twBd are listed in Table 10. SBS copolymer characterization of product from this example is shown in Table 11 and Table 12.
(50) Comparative example C9. Uncoupled SBS block copolymerization using polar modifier system of prior art, at high temperature range. An S-b-B-b-S type block copolymer was prepared in a lab scale stirred batch reactor, with relatively low thermal insulation level, using the following procedure: Cyclohexane (2862 g) and styrene monomer (63.0 g) were charged in to a stirred reactor under nitrogen atmosphere, and their temperature was stabilized at a temperature of 39.9° C. (Ti). Thereafter TMEDA, SMT and n-butyllithium initiator were added to the reactor in the listed order, and reactor temperature control was shut off. Active initiator content and polar modifier molar ratios to initiator are shown in Table 9. A peak temperature of 44.5° C. (TpSt1) was detected passed 5 minutes of initiator load (tpSt1). Then reactor was cooled down for 15 minutes to reach a temperature of 28° C. (TiBd). From this point on polymerization continued in absence of intended heating or cooling, apart from heat dissipation to the surroundings. Then butadiene (255.4 g) feed operation began. Butadiene charge was completed in 5 minutes. Butadiene heat of polymerization raised reactant mass to a peak temperature of 62.7° C. (TpBd) in a period of 10 minutes (tpBd), counted from start of butadiene feed operation. Then, a wait time of 5 minutes (twBd) was taken between butadiene polymerization peak temperature and the beginning of second styrene load. Second styrene load to reactor (63.0 g) was let polymerize for long enough time to be fully consumed. Then an alcohol was feed to reactor to terminate anionic polymer anions. Cyclohexane solvent to overall monomer feed ratio (S/M) in this example was 7.5. Process parameters Ti, TpSt1, tpSt1, TiBd, TpBd, tpBd and twbd are listed in Table 10. SBS copolymer characterization of product from this example is shown in Table 11 and Table 12.
(51) TABLE-US-00009 TABLE 9 Initiator and polar modifier system loadings, as well as overall solvent to monomer (S/M) ratio in example 12, according with the invention, and in comparative example C9, using previous art. n-BuLi, DTHFP, BDMAEE, TMEDA, SMT, mmol mol/ mol/ mol/ mol/ Example active Li mol Li mol Li mol Li mol S/M 12 5.1 1.7 0.21 0 0.04 8 C9 4.8 0 0 3.8 0.08 7.5
(52) TABLE-US-00010 TABLE 10 Polymerization process parameters in example 12, according with the invention, and in comparative example C9, using previous art. Ti, TpSt1, tpSt1, Ti-Bd, Tp-Bd, tpBd, twBd, Example ° C. ° C. min ° C. ° C. min mm 12 43.3 46.2 2.0 44.2 61.1 5 2 C9 39.9 44.5 4.8 28 62.7 10 5
(53) TABLE-US-00011 TABLE 11 NMR characterization of SBS copolymer produced in example 12, according with the invention, and comparative examples C9, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis 12 33.5 31.1 2.4 77.9 4.0 81.9 79.9 C9 33.0 31.8 1.2 73.1 7.8 80.9 77.1
(54) TABLE-US-00012 TABLE 12 GPC characterization of SBS copolymer produced in examples 12, according with the invention, and in comparative examples C9, using previous art. Mp Example kg/mol Mw/Mn MWD Shape 12 109.8 1.03 Ummodal narrow peak C9 130.7 1.04 Ummodal narrow peak
(55) Comparison of example 12, based on polar modifier system DTHFP/BDMAEE/SMT against comparative example C9, based on prior art polar modifier system TMEDA/SMT shows that invention polar modifier system conducts to higher 1,2-vinyl and much lower VCP repeat unit incorporation in the polybutadiene block than prior art when performed at high polymerization temperature. Moreover, butadiene polymerization spanned over a 44 to 61° C. temperature range in example 10, which is a more exigent condition (higher average polymerization temperature) than butadiene polymerization spanning in a range from 28 to 62° C. in comparative example C9. Both cases, invention and prior art conducted to unimodal narrow molecular weight distributions.
(56) Comparative example C10. Uncoupled SBS block copolymerization using polar modifier system of prior art at high concentration, at high temperature range.
(57) TABLE-US-00013 TABLE 13 Initiator and polar modifier system loadings, as well as overall solvent to monomer (S/M) ratio in comparative example C10, using previous art. Sodium tert- BDMAEE, butoxide, Example mol/Li mol mol/Li mol S/M C10 0.95 0.35 8
(58) TABLE-US-00014 TABLE 14 NMR characterization of SBS copolymer produced in comparative example C10, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis C10 26.4 25.3 1.1 77.7 8.3 86.0 81.5
(59) TABLE-US-00015 TABLE 15 GPC characterization of SBS copolymer produced in comparative example C10, using previous art. Mp, Example kg/mol Mw/Mn MWD Shape C10 986.6 9.47 Tri-modal wide peak, Mp2 = 16.8 kg/mol Mp3 = 107.1 kg/mol
(60) Example 13 and 14. Uncoupled SBS block copolymerization using preferred polar modifier system of invention, at low monomer concentration level. An S-b-B-b-S type block copolymer was prepared in a lab scale batch reactor thru the following steps: (1) charge of cyclohexane solvent to a reactor; (2) stabilization of solvent to a temperature Ti; (3) charge of polar modifiers BDMAEE and DTHFP; (4) charge of n-butyllithium; (5) charge of SMT; (6) charge of styrene monomer; (7) immediate interruption of reactor temperature control to perform polymerization in absence of external cooling or heating, apart from natural heat loss to the surroundings (8) homopolymerization of first styrene block for a total time tSt, during which period heat of polymerization gradually raised reactor temperature up to a peak temperature TpSt at a time tpSt elapsed from beginning of styrene charge and such peak temperature; (10) registration of reactor temperature TiBd and immediate charge of butadiene monomer; (11) butadiene block copolymerization, where heat of reaction raised reactor temperature to a peak temperature TpBd which was registered, as well as time tpBd elapsed from beginning of butadiene charge to the moment TpBd occurred; (12) wait time of twBd past TpBd, where a slight temperature drop occurred; (13) charge of second styrene load; (14) polymerization of second polystyrene block until full consumption of styrene monomer; (15) charge of excess equivalents of an alcohol to assure termination of all polymer anions. In these formulations 2805 g of cyclohexane were used, 41.8 g of styrene were used to build polystyrene first block, 171.1 g of butadiene were used to build high vinyl polybutadiene middle block, and 41.8 g of styrene were used to build polystyrene end block. Thus, overall solvent to monomer ratio was 11.0. Feed time of each styrene load was 0.5 minutes long. Feed time for butadiene load was 2 minutes long. Active initiator content and polar modifier molar ratios to initiator are shown in Table 16. Process parameters Ti, TpSt, tpSt, tSt TiBd, TpBd, tpBd and twBd are listed in Table 17. SBS copolymer characterization of product from this example is shown in Table 18 and Table 19.
(61) Comparative examples C11 and C12. Uncoupled SBS block copolymerization using polar modifier system of prior art, at low monomer concentration level: The same steps of procedure described in examples 10 and 11 were employed, but usage of DTHFP was avoided. In these formulations 4228 g of cyclohexane were used, 68.2 g of styrene were used to build polystyrene first block, 287.7 g of butadiene were used to build high vinyl polybutadiene middle block, and 68.2 g of styrene were used to build polystyrene end block. Thus, overall solvent to monomer ratio was 10.0. Active n-butyllithium and polar modifier system dosages for these comparative examples are reported in Table 16. Process parameters Ti, TpSt, tpSt, tSt, TiBd, TpBd and tpBd are listed in Table 17 for each comparative example. SBS copolymer characterization of products from these comparative examples is shown in Table 18 and Table 19.
(62) TABLE-US-00016 TABLE 16 Initiator and polar modifier system loadings, as well as overall solvent to monomer (S/M) ratio in examples 13 and 14, according with the invention, and in comparative examples C11 and C12, using previous art. n-BuLi, DTHFP, BDMAEE, SMT, mmol mol/ mol/ mol/ Example active Li mol Li mol Li mol S/M 13 3.5 3.5 0.44 0.09 11 14 3.2 2.0 0.49 0.05 11 C11 4.7 0 1.09 0.12 10 C12 5.2 0 0.49 0.11 10
(63) TABLE-US-00017 TABLE 17 Polymerization process parameters in examples 13 and 14, according with the invention, and in comparative examples C11 and C12, using previous art. Ti, TpSt, tpSt, tSt, Ti-Bd, Tp-Bd, tpBd, twBd, Example ° C. ° C. min min ° C. ° C. min min 13 34.1 36.0 2 13 33.6 46.2 5 5 14 30.6 32.3 2 14 30.7 39.4 8 11 C11 19.8 22.6 10 15 22.5 40.0 8 9 C12 19.8 N.D. N.D. 20 22.8 34.3 21 5 N.D. = Not detected
(64) TABLE-US-00018 TABLE 18 NMR characterization of SBS copolymer produced in examples 13 and 14, according with the invention, and comparative examples C11 and C12, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis 13 33.3 31.8 1.5 84.0 4.7 88.6 86.4 14 33.9 31.6 2.3 84.0 3.8 87.8 85.9 C11 31.9 30.5 1.4 86.8 5.1 91.9 89.4 C12 30.9 21.0 9.9 88.2 2.1 90.3 89.2
(65) TABLE-US-00019 TABLE 19 GPC characterization of SBS copolymer produced in examples 13 and 14, according with the invention, and in comparative examples C11 and C12, using previous art. mp, Example kg/mol Mw/Mn MWD Shape 13 118.5 1.05 Unimodal narrow peak 14 129.1 1.05 Unimodal narrow peak C11 149.6 1.06 Big shoulder at 121 kg/mol C12 135.5 1.05 Unimodal narrow peak
(66)
(67) Analysis of examples 13 and 14, based on invention polar modifier system DTHFP/BDMAEE/SMT, shows that those where robust against lower monomer concentration during polymerization, producing high 1,2-vinyl and low VCP repeat unit contents in polybutadiene block, at high polymerization rate of styrene and butadiene blocks and with narrow unimodal molecular weight distribution in final product. On the other hand, employing prior art polar modifier system BDMAEE/SMT with polymerization at diluted monomer regime, conducted to bimodal weight distribution when BDMAEE/Li ratios was high, or to very slow polymerization rate and very high level of random styrene incorporation in the copolymer when BDMAEE/Li was low.
(68) Examples 15 and 16. SB block copolymerization using preferred polar modifier system followed by coupling step. (S-b-B).sub.n—X type copolymers were prepared in a lab scale stirred reactor using the following procedure: Cyclohexane (2792 g) was charged in to a stirred reactor under nitrogen atmosphere, and its temperature was stabilized at approximately 18° C. (Ti). Thereafter BDMAEE, DTHFP, n-butyllithium initiator and SMT were added to the reactor in the listed order. Active initiator content and polar modifier molar ratios to initiator are shown in Table 20. Then, styrene monomer (63.6 g) was charged to the reactor. Styrene feed operation was completed in 30 seconds. Reactor cooling was interrupted thereafter. It was registered a peak temperature (TpSt) for first styrene homo-polymerization stage as well as reaction time (tpSt) elapsed from beginning of first styrene load up to such moment. Then, a wait time of 10 minutes was practiced in both examples Immediately afterwards reactor temperature was registered (Ti-Bd) and butadiene (246.1 g) feed operation began. Butadiene charge was completed in 2 minutes. Butadiene heat of polymerization raised reactant temperature, and when it reached 55.8±0.3° C. (TSiCl4) a shot of silicon tetrachloride coupling agent was fed to the reactor. Dosage of silicon tetrachloride (SiCl4) is shown in Table 20. Record was taken of butadiene reaction time up to coupling agent shot (tSiCl4), counted from start of butadiene feed operation. An alcohol solution shot, with hydroxyl equivalents in excess to n-butillithium initially fed to reactor, was fed to the reactor 6 minutes after SiCl4 shot. Cyclohexane to overall monomer feed ratio in these examples was 9.0. Process parameters Ti, TpSt, tpSt, TiBd, TSiCl4, tSiCl4 are listed in Table 21. SBS copolymer characterization of product from this example is shown in Table 22 and Table 23.
(69) Comparative examples C13 and C14, using prior art. The same polymerization procedure as in examples 15 and 16 was performed, but polar modifier system lacked DTHFP. Active initiator content, polar modifier molar ratios to initiator, and silicon chloride dosage are shown in Table 20. Process parameters Ti, TpSt, tpSt, TiBd and tSiCl4 are listed in Table 21. SBS copolymer characterization of product from this example is shown in Table 22 and Table 23.
(70) TABLE-US-00020 TABLE 20 Initiator, polar modifier system, and coupling agent loadings in examples 15 and 16, according with the invention, and comparative examples C13 and C14, using previous art. n-BuLi, DTHFP, BDMAEE, SMT, mmol mol/ mol/ mol/ SiCl.sub.4, Example active Li mol Li mol Li mol mmol 15 4.5 2.7 0.76 0.06 1.09 16 4.8 2.5 0.71 0.05 1.16 C13 4.5 0 0.76 0.06 1.09 C14 4.5 0 0.96 0.06 1.09
(71) TABLE-US-00021 TABLE 21 Polymerization process parameters in examples 15 and 16, according with the invention, and comparative examples C13 thru C14, using previous art. Ti TpSt, tpSt, TiBd, TSiCl4, tSiCl4, Example ° C. ° C. min ° C. ° C. min 15 18.1 23.1 7.0 22.8 56.0 6.7 16 18.1 23.1 7.5 22.9 55.9 6.9 C13 18.3 23.4 28.0 23.4 55.5 13.0 C14 18.3 23.4 17.0 23.2 56.1 9.5
(72) TABLE-US-00022 TABLE 22 NMR characterization of SBS copolymer produced in examples 15 and 16, according with the invention, and in comparative examples C13 and C14, using previous art. Total Block Random 1,2-vinyl, VCP, Total vinyl, Total vinyl, Styrene, styrene, styrene, wt %, wt %, 1,2 +VCP, 1,2 +VCP, Example wt % wt % wt % Bd basis Bd basis wt %, Bd basis mol %, Bd basis 15 21.2 20.9 0.3 85.9 3.4 89.4 87.7 16 21.2 20.9 0.3 85.8 3.5 89.2 87.5 C13 21.5 21.2 0.3 86.5 3.8 90.2 88.4 C14 21.7 21.4 0.2 86.2 4.0 90.2 88.2
(73) TABLE-US-00023 TABLE 23 GPC characterization of SBS copolymer produced in examples 15 and 16, according with the invention, and in comparative examples C13 thru C14, using previous art. Coupled SBS Mp.sub.uc, copolymer, Example kg/mol wt % 15 119.7 79.9 16 111.9 85.3 C13 127.1 44.7 C14 118.1 51.5 Mp.sub.uc = Peak molecular weight of un-coupled fraction.
(74)
(75) When comparing coupling efficiency and molecular weight distribution obtained with polar modifier of invention DTHFP/BDMAEE/SMT, used in example 15 and 16, against such parameters when using prior art based on polar modifier system BDMAEE/SMT, as in comparative examples C13 and C14, it can be evidenced that invention polar modifier system provides livingness to much higher amount of polymer anions up to end of butadiene consumption than closest prior polar modifier system does. SiCl.sub.4 load was planned for a theoretical maximum coupling efficiency of 95% to 96% if every polymer anion would remain alive when SiCl.sub.4 charge occurred. In comparative examples C13 and C14 about half of polymeric anions were unable to participate in the coupling reaction, confirming that about half of polymeric anions had terminated before SiCl4 charge. It is worthwhile to notice that cyclohexane, styrene and butadiene loadings of these examples agreed with cyclohexane, first styrene and butadiene loadings of Example 3 thru 11 and comparative examples C7 and C8. Therefore, livingness of polymer anions up to the end of butadiene consumption evidenced in examples 15 and 16 applies to examples 3 thru 11, that shared preferred polar modifier system DTHFP/BDMAEE/SMT and obtained unimodal narrow molecular weight distributed un-coupled SBS product. On the other hand, same degree of premature termination of polymer anions evidenced in comparative examples C13 and C14 applies for comparative examples C7 and C8, all of them using closest prior art system BDMAEE/SMT, and showing wide bimodal molecular weight distributions.
(76) Example 17 (Hypothetical). Linear SBS block copolymer of example 2 synthesized using preferred polar modifier system of this invention, further hydrogenated to obtain a linear high vinyl SEBS.
(77) Linear SBS from example 2 exhibiting 87.6 wt % total vinyl content and still dissolved in cyclohexane (solvent to polymer ratio 8.0, w/w) was deactivated by adding 2-methyl-2,4-pentanediol in a molar ratio alcohol/Li active=0.5. Thereafter polymer solution was heated up to 90° C. and 0.25 mmol of hydrogenation catalyst (Cp.sub.2 Ti(PhOCH.sub.3).sub.2 or Cp.sub.2 Ti (CH.sub.2 PPh.sub.2) as described in U.S. Pat. No. 5,985,995A) per 100 g of polymer were added, followed by hydrogen addition up to a pressure of 8 kg/cm.sup.2 was reached. Hydrogen uptake was completed in 45 minutes. .sup.1H NMR analysis, showed it was obtained a SEBS having 99.6% hydrogenation. Therefore, a novel linear SEBS derived from a SBS having 87.6 wt % vinyl content was thus obtained.
(78) Example 18 (Hypothetical). Linear SBS block copolymer of example 10 synthesized using preferred polar modifier system of this invention, further hydrogenated to obtain a linear high vinyl SEBS.
(79) Linear SBS from example 10 exhibiting 90.1 wt % total vinyl content and still dissolved in cyclohexane (solvent to polymer ratio 7.5, w/w) was deactivated by adding 2-methyl-2,4-pentanediol in a molar ratio alcohol/Li active=0.5. Thereafter polymer solution was heated up to 90° C. and 0.25 mmol of hydrogenation catalyst (Cp.sub.2 Ti(PhOCH.sub.3).sub.2 or Cp.sub.2 Ti (CH.sub.2 PPh.sub.2) as described in U.S. Pat. No. 5,985,995A) per 100 g of polymer were added, followed by hydrogen addition up to a pressure of 8 kg/cm.sup.2 was reached. Hydrogen uptake was completed in 45 minutes. .sup.1H NMR analysis revealed it was obtained a SEBS having 99.6% hydrogenation. Therefore, a novel linear SEBS derived from a SBS having 90.1 wt % vinyl content was thus obtained.
(80) Example 19 (Hypothetical). Star-type SBS block copolymer of example 15 synthesized using preferred polar modifier system of this invention, further hydrogenated to obtain star-type high vinyl SEBS.
(81) Star-type SBS block copolymer from example 15 exhibiting 89.4 wt % total vinyl content and still dissolved in cyclohexane (solvent to polymer ratio 8.0, w/w) was deactivated by adding 2-methyl-2,4-pentanediol in a molar ratio alcohol/Li active=0.5. Thereafter polymer solution was heated up to 90° C. and 0.25 mmol of hydrogenation catalyst (Cp.sub.2 Ti(PhOCH.sub.3).sub.2 or Cp.sub.2 Ti (CH.sub.2 PPh.sub.2) as described in U.S. Pat. No. 5,985,995A) per 100 g of polymer were added, followed by hydrogen addition up to a pressure of 8 kg/cm.sup.2 was reached. Hydrogen uptake was completed in 45 minutes. As revealed by .sup.1H NMR analysis, it was obtained a star-type SEBS having 99.6% hydrogenation. Therefore, a novel star-type SEBS derived from a star-type SBS having 89.4 wt % vinyl content was thus obtained.
(82) SEBS from examples 17 to 19 being derived from high vinyl content SBS are novel materials that must be more compatible with polypropylene than known SEBS.
(83) Example 20 (Hypothetical). Linear SBS block copolymer of example 10 synthesized using preferred polar modifier system of this invention, further subjected to end-functionalization and further subjected to hydrogenation to obtain a linear high vinyl end-functionalized SEBS-f.
(84) Linear SBS from example 8 exhibiting 90.1 wt % total vinyl content and still dissolved in cyclohexane (solvent to polymer ratio 8.0, w/w) was end-functionalized with OH or secondary amine functional groups by adding quantitative amounts of either propylene oxide or n-benzylidenemethylamine (molar ratio functionalization agent/Li active=1.0). Thereafter, polymer solution was heated up to 90° C. and 0.25 mmol of hydrogenation catalyst (Cp.sub.2 Ti(PhOCH.sub.3).sub.2 or Cp.sub.2 Ti (CH.sub.2 PPh.sub.2) as described in U.S. Pat. No. 5,985,995A) per 100 g of polymer were added, followed by hydrogen addition up to a pressure of 8 kg/cm.sup.2 was reached. Hydrogen uptake was completed in 45 minutes. As revealed by .sup.1H NMR analysis, it was obtained an end-functionalized SEBS-f having 99.6% hydrogenation. Therefore, novel linear SEBS-OH or SEBS-NHR derived from a linear SBS having 90.1 wt % vinyl content were thus obtained.
(85) End-functionalized SEBS from example 20 are new materials exhibiting OH or amine polar groups combined with high butylene enrichment along the central EB block. These novel materials are useful as reactive polymers to effect chain-extension reactions useful to produce novel segmented block copolymers and to be used more efficiently in engineering plastics impact modification and polymer blends compatibilization.
EMBODIMENTS OF THE INVENTION
(86) Embodiment 1. A polar modifier system for making block copolymers of vinyl aromatic monomers and conjugated diene monomers by organolithium initiated anionic polymerization, comprising:
(87) (a) a compound having the structure of formula (I):
(88) ##STR00006##
(89) wherein R.sub.1 thru R.sub.14 independently are —H or —C.sub.nH.sub.2n+1 groups, wherein n=1 to 6, and
(90) wherein ditetrahydrofurfurylpropane (DTHFP) is a preferred compound that has the structure of formula (I).
(91) (b) a compound having the structure of formula (V):
(92) ##STR00007##
(93) wherein m=1 to 2, n=1 to 2; and
(94) wherein R.sub.1 to R.sub.4 independently are —C.sub.xH.sub.2x+1 groups, wherein x=1 to 6, and
(95) wherein bis[2-(N,N-dimethylamino)ethyl] ether is a preferred compound that has the structure of formula (V); and
(96) (c) a sodium alkoxide compound, preferably sodium mentholate
(97) wherein the molar ratio of ditetrahydrofurfurylpropane to the organolithium initiator is within the range of about 0.36:1 to about 4.2:1, preferably about 1.5:1 to about 3.5:1 and more preferably about 2.5:1 to about 3.0;
(98) wherein the molar ratio of bis[2-(N,N-dimethylamino)ethyl] ether to the organolithium initiator is within the range of about 0.1:1 to about 1.5:1, or about 0.2:1 to about 1:1, preferably about 0.3:1 to about 1:1, more preferably about 0.4:1 to about 0.9:1;
(99) wherein the molar ratio of sodium alkoxide compound to the organolithium initiator is within the range of about 0.01:1 to about 0.3:1, or about 0.02:1 to about 0.2:1, or preferably about 0.03:1 to about 0.15:1, or more preferably about 0.04:1 to about 0.10:1.
(100) Embodiment 2. A polar modifier system for making block copolymers of vinyl aromatic monomers and conjugated diene monomers by organolithium initiated anionic polymerization, comprising:
(101) (a) a compound having the structure of formula (II):
(102) ##STR00008##
(103) wherein R1 is a —C.sub.nH.sub.2n+1 group, wherein n=1 to 6; and
(104) wherein R2 thru R7 independently are —H or —C.sub.xH.sub.2x+1 groups, wherein x=1 to 6.
(105) (b) a compound having the structure of formula (V):
(106) ##STR00009##
(107) wherein m=1 to 2, n=1 to 2; and
(108) wherein R.sub.1 to R.sub.4 independently are —C.sub.xH.sub.2x+1 groups, wherein x=1 to 6, and
(109) wherein bis[2-(N,N-dimethylamino)ethyl] ether is a preferred compound that has the structure of formula (V); and
(110) (c) a sodium alkoxide compound, preferably sodium mentholate,
(111) wherein the molar ratio of ethyltetrahydrofurfuryl ether to the organolithium initiator is within the range of about 0.3:1 to about 4:1, preferably about 1:1 to about 3:1 and more preferably about 1.5:1 to about 2.5:1,
(112) wherein the molar ratio of bis[2-(N,N-dimethylamino)ethyl] ether to the organolithium initiator is within the range of about 0.1:1 to about 1.5:1, or about 0.2:1 to about 1:1, preferably about 0.3:1 to about 1:1, more preferably about 0.4:1 to about 0.9:1;
(113) wherein the molar ratio of sodium alkoxide compound to the organolithium initiator is within the range of about 0.01:1 to about 0.3:1, or about 0.02:1 to about 0.2:1, or preferably about 0.03:1 to about 0.15:1, or more preferably about 0.04:1 to about 0.10:1.
(114) Embodiment 3. A polar modifier system for making block copolymers of vinyl aromatic monomers and conjugated diene monomers by organolithium initiated anionic polymerization, comprising:
(115) (a) a compound having the structure of formula (III):
(116) ##STR00010##
(117) wherein R.sub.1 to R.sub.4 independently are —CH.sub.3 or —CH.sub.2CH.sub.3 groups; and
(118) wherein R.sub.5 is a —H or a —C.sub.nH.sub.2n+1 group, wherein n=1 to 2, and
(119) wherein N,N,N′,N′-tetramethyl ethylenediamine is a preferred compound that has the structure of formula (III).
(120) (b) a compound having the structure of formula (V):
(121) ##STR00011##
(122) wherein m=1 to 2, n=1 to 2; and
(123) wherein R.sub.1 to R.sub.4 independently are —C.sub.xH.sub.2x+1 groups, wherein x=1 to 6, and
(124) wherein bis[2-(N,N-dimethylamino)ethyl] ether is a preferred compound that has the structure of formula (V); and
(125) (c) a sodium alkoxide compound, preferably sodium mentholate,
(126) wherein the molar ratio of N,N,N′,N′-tetramethyl ethylenediamine to the organolithium initiator is within the range of about 1:1 to about 4:1, preferably about 1.5:1 to about 3:1 and more preferably about 2:1 to about 3:1,
(127) wherein the molar ratio of bis[2-(N,N-dimethylamino)ethyl] ether to the organolithium initiator is within the range of about 0.1:1 to about 1.5:1, or about 0.2:1 to about 1:1, preferably about 0.3:1 to about 1:1, more preferably about 0.4:1 to about 0.9:1;
(128) wherein the molar ratio of sodium alkoxide compound to the organolithium initiator is within the range of about 0.01:1 to about 0.3:1, or about 0.02:1 to about 0.2:1, or preferably about 0.03:1 to about 0.15:1, or more preferably about 0.04:1 to about 0.10:1.
(129) Embodiment 4. A polar modifier system for making block copolymers of vinyl aromatic monomers and conjugated diene monomers by organolithium initiated anionic polymerization, comprising:
(130) (a) a compound having the structure of formula (IV):
(131) ##STR00012##
(132) wherein R.sub.1 to R.sub.6 independently are —H or —C.sub.nH.sub.2n+1 groups, wherein n=1 to 6;
(133) wherein R.sub.7 and R.sub.8 independently are —C.sub.xH.sub.2x+1 groups, wherein x=1 to 2, and
(134) wherein tetrahydrofurfuryl-N,N-dimethylamine is a preferred compound that has the structure of formula (IV).
(135) (b) a compound having the structure of formula (V):
(136) ##STR00013##
(137) wherein m=1 to 2, n=1 to 2; and
(138) wherein R.sub.1 to R.sub.4 independently are —C.sub.xH.sub.2x+1 groups, wherein x=1 to 6, and
(139) wherein bis[2-(N,N-dimethylamino)ethyl] ether is a preferred compound that has the structure of formula (V); and
(140) (c) a sodium alkoxide compound, preferably sodium mentholate,
(141) wherein the molar ratio of tetrahydrofurfuryl-N,N-dimethylamine to the organolithium initiator is within the range of about 1:1 to about 4:1, preferably about 1.5:1 to about 3:1 and more preferably about 2:1 to about 3:1,
(142) wherein the molar ratio of bis[2-(N,N-dimethylamino)ethyl] ether to the organolithium initiator is within the range of about 0.1:1 to about 1.5:1, or about 0.2:1 to about 1:1, preferably about 0.3:1 to about 1:1, more preferably about 0.4:1 to about 0.9:1;
(143) wherein the molar ratio of sodium alkoxide compound to the organolithium initiator is within the range of about 0.01:1 to about 0.3:1, or about 0.02:1 to about 0.2:1, or preferably about 0.03:1 to about 0.15:1, or more preferably about 0.04:1 to about 0.10:1.
(144) Having described the invention above, various modifications of the techniques, procedures, materials, and equipment will be apparent to those skilled in the art. It is intended that all such variations within the scope and spirit of the invention be included within the scope of the appended claims.