Synthesis of a Au-(TiO.SUB.2-x./WO.SUB.3-x.) semiconductor composite using fluidized bed chemical vapor deposition (FBCVD)

Abstract

A method of synthesizing an Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite, the method comprising: loading tungsten oxide (WO.sub.3) powder in a fluidized bed reactor followed by H.sub.2 treatment to produce reduced tungsten oxide (WO.sub.3) nanoparticles or WO.sub.3-x nanoparticles; producing reduced titanium dioxide (TiO.sub.2) nanoparticles or TiO.sub.2-y (containing defect states) nanoparticles in-situ; coupling the TiO.sub.2-y nanoparticles with the WO.sub.3-x nanoparticles to provide a titanium dioxide/tungsten oxide nanocomposite (TiO.sub.2-y/WO.sub.3-x); and simultaneous substitutional doping of TiO.sub.2-y and WO.sub.3-x in the titanium dioxide/tungsten oxide nanocomposite (TiO.sub.2-y/WO.sub.3-x) with gold ions (Au) to obtain the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite; wherein x has a value between 0.33 and 0.37. The thus produced composite can be used as a photocatalyst.

Claims

1. A method of synthesizing an Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite, the method comprising: loading tungsten oxide (WO.sub.3) powder in a fluidized bed reactor followed by H.sub.2 treatment to produce reduced tungsten oxide (WO.sub.3) nanoparticles or WO.sub.3-x nanoparticles; producing titanium dioxide (TiO.sub.2) nanoparticles or TiO.sub.2-y nanoparticles in-situ; coupling the TiO.sub.2-y nanoparticles with the WO.sub.3-x nanoparticles to provide a titanium dioxide/tungsten oxide nanocomposite (reduced TiO.sub.2/WO.sub.3-x); and simultaneous substitutional doping of TiO.sub.2-y and WO.sub.3-x in the titanium dioxide/tungsten oxide nanocomposite (reduced TiO.sub.2/WO.sub.3-x) with gold ions (Au) to obtain the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite; wherein x has a value between 0.33 and 0.37.

2. The method of claim 1, wherein the H.sub.2 treatment comprises inputting an airflow into the fluidized bed reactor comprising 5% H.sub.2 and 95% N.sub.2, by volume, at a flowrate of about 130 ml/min to about 140 ml/min.

3. The method of claim 2, wherein the H.sub.2 treatment is conducted at about 600? C.

4. The method of claim 1, wherein the titanium dioxide nanoparticles are produced by reacting a TiCl.sub.4 reagent with deionized water.

5. The method of 1, wherein the gold ions are doped into a crystal lattice of the TiO.sub.2 nanoparticles.

6. The method of claim 1, wherein the gold ions are obtained by adding Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water to the fluidized bed reactor.

7. The method of claim 1, wherein a continuous supply of titanium precursor (TiCl.sub.4), hydrogen, and Au water (Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water) is provided to the fluidized bed reactor.

8. The method of claim 7, wherein the titanium precursor and Au water are input into the fluidized bed reactor using a carrier nitrogen gas at a flowrate of about 65 ml/min to about 75 ml/min.

9. An Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite prepared according to the method of claim 1.

10. The Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite of claim 9, wherein the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite has one or more of a BET surface area of about 250 to about 280 m.sup.2/g, an average pore diameter of about 3.5 to about 4 nm, and a total pore volume of about 0.55 to about 0.65 cm.sup.3/g.

11. The Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite of claim 9, comprising TiO.sub.2 nanoparticles having a spherical shape.

12. The Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite of claim 9, comprising WO.sub.3-x nanoparticles having a needle shape.

13. The Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite of claim 9, comprising reduced TiO.sub.2 nanoparticles and WO.sub.3-x nanoparticles uniformly distributed throughout the composite.

14. A photocatalyst comprising the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite of claim 9.

15. A method of providing photocatalysis comprising exposing the photocatalyst of claim 14 to an environment conducive to photocatalysis.

16. The method of claim 15, wherein the photocatalysis is used to provide one or more of organic pollutant degradation, CO.sub.2 greenhouse gas conversion, H.sub.2 production by water photolysis, biodiesel production, energy conservation, and energy storage.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

(1) FIG. 1 is a schematic diagram of the fabrication system for producing an Au doped (TiO.sub.2-y/WO.sub.3-x) coupled semiconductor photocatalyst by a Fluidized Bed Chemical Vapor Deposition (FBCVD) process.

(2) FIGS. 2A-2D show: XRD spectrum (2A), Raman spectrum (2C), SEM image (2C); and SEM-EDX elemental mapping of O, Ti, W and Au (2D) in the TiO.sub.2-yWO.sub.3-x hybrid powder.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

(3) The following definitions are provided for the purpose of understanding the present subject matter and for construing the appended patent claims.

Definitions

(4) Throughout the application, where compositions are described as having, including, or comprising specific components, or where processes are described as having, including, or comprising specific process steps, it is contemplated that compositions of the present teachings can also consist essentially of, or consist of, the recited components, and that the processes of the present teachings can also consist essentially of, or consist of, the recited process steps.

(5) It is noted that, as used in this specification and the appended claims, the singular forms a, an, and the include plural references unless the context clearly dictates otherwise.

(6) In the application, where an element or component is said to be included in and/or selected from a list of recited elements or components, it should be understood that the element or component can be any one of the recited elements or components, or the element or component can be selected from a group consisting of two or more of the recited elements or components. Further, it should be understood that elements and/or features of a composition or a method described herein can be combined in a variety of ways without departing from the spirit and scope of the present teachings, whether explicit or implicit herein.

(7) The use of the terms include, includes, including, have, has, or having should be generally understood as open-ended and non-limiting unless specifically stated otherwise.

(8) The use of the singular herein includes the plural (and vice versa) unless specifically stated otherwise. In addition, where the use of the term about is before a quantitative value, the present teachings also include the specific quantitative value itself, unless specifically stated otherwise. As used herein, the term about refers to a ?10% variation from the nominal value unless otherwise indicated or inferred.

(9) Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood to one of ordinary skill in the art to which the presently described subject matter pertains.

(10) Where a range of values is provided, for example, concentration ranges, percentage ranges, or ratio ranges, it is understood that each intervening value, to the tenth of the unit of the lower limit, unless the context clearly dictates otherwise, between the upper and lower limit of that range and any other stated or intervening value in that stated range, is encompassed within the described subject matter. The upper and lower limits of these smaller ranges may independently be included in the smaller ranges, and such embodiments are also encompassed within the described subject matter, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the described subject matter.

(11) Throughout the application, descriptions of various embodiments use comprising language. However, it will be understood by one of skill in the art, that in some specific instances, an embodiment can alternatively be described using the language consisting essentially of or consisting of.

(12) For purposes of better understanding the present teachings and in no way limiting the scope of the teachings, unless otherwise indicated, all numbers expressing quantities, percentages or proportions, and other numerical values used in the specification and claims, are to be understood as being modified in all instances by the term about. Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties sought to be obtained. At the very least, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.

(13) In an embodiment, the present subject matter relates to a method of synthesizing an Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite, comprising loading tungsten oxide (WO.sub.3) powder in a fluidized bed reactor followed by H.sub.2 treatment to produce reduced tungsten oxide (WO.sub.3) nanoparticles or WO.sub.3-x nanoparticles; producing reduced titanium dioxide (TiO.sub.2), aka TiO.sub.2-y nanoparticles in-situ; coupling the TiO.sub.2-y nanoparticles with the WO.sub.3-x nanoparticles to provide a titanium dioxide/tungsten oxide nanocomposite (TiO.sub.2-y/WO.sub.3-x); and simultaneous substitutional doping of TiO.sub.2-y and WO.sub.3-x in the titanium dioxide/tungsten oxide nanocomposite (TiO.sub.2-y/WO.sub.3-x) with gold (Au) to obtain the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite; wherein x has a value between 0.33 and 0.37 and TiO.sub.2-y has defect states.

(14) Accordingly, the present subject matter relates to a two-stage process on a single site with the flexibility and ease to reduce WO.sub.3 nanoparticles and then In-situ (i) produce of TiO.sub.2-y nanoparticles, (ii) couple TiO.sub.2-y with WO.sub.3-x, and (iii) Au doped both the coupled semiconductors (TiO.sub.2-y/WO.sub.3-x).

(15) The procedure described herein also has the advantage of producing a single step novel in-situ nano Au(TiO.sub.2/WO.sub.3) photocatalyst.

(16) In an embodiment of the present production methods, the H.sub.2 treatment can comprise inputting an airflow into the fluidized bed reactor comprising about 5% H.sub.2 and about 95% N.sub.2, by volume, at a flowrate of about 130 ml/min to about 140 ml/min, or about 135 ml/min. In certain embodiments in this regard, the H.sub.2 treatment can be conducted at about 600? C.

(17) In certain embodiments of the present production methods, the titanium dioxide nanoparticles can be produced by reacting a TiCl.sub.4 reagent or Ti precursor with water.

(18) In further embodiments of the present production methods, the gold ions can be doped into a crystal lattice of the TiO.sub.2 nanoparticles. Further, the gold ions can be obtained by adding Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water to the fluidized bed reactor.

(19) In additional embodiments of the present production methods, a continuous supply of titanium precursor (TiCl.sub.4), hydrogen, and Au water (Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water) can be provided to the fluidized bed reactor. In this regard, the titanium precursor and Au water can be input into the fluidized bed reactor using a carrier nitrogen gas at a flowrate of about 65 ml/min to about 75 ml/min, or about 70 ml/min.

(20) In certain embodiments, the TiCl.sub.4 (titanium precursor) and Au water (Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water) can be transported separately through bubbling the carrier gas of N.sub.2 (purity >99.0 wt. %) into the fluidized bed reactor. The TiCl.sub.4 reagent on reaction with water can produce TiO.sub.2 with simultaneous doping of Au ions into its crystal lattice. Also, in situ Au is doped in the reduced WO.sub.3-x powder and gets coupled with Au-doped TiO.sub.2-y in the fluidized bed.

(21) According to another embodiment, the present subject matter relates to an Au(TiO.sub.2/WO.sub.3) semiconductor composite prepared according to the methods described herein.

(22) In certain embodiments in this regard, the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite can have one or more of a BET surface area of about 250 to about 280 m.sup.2/g, or about 260 m.sup.2/g, an average pore diameter of about 3.5 to about 4 nm, or about 3.7 nm, and a total pore volume of about 0.55 to about 0.65 cm.sup.3/g, or about 0.58 cm.sup.3/g.

(23) In further embodiments, the TiO.sub.2-y nanoparticles can have a spherical shape. In other embodiments, the WO.sub.3-x nanoparticles can have a needle shape. In certain embodiments in this regard, the TiO.sub.2-y nanoparticles and WO.sub.3-x nanoparticles can be uniformly distributed throughout the composite.

(24) The reduced, coupled, and doped nano-photocatalyst with homogeneity and high surface area as described herein can have a lot of applications in environmental remediation, medical treatment (cancer treatment), energy conservation (fuel and solar cells and batteries), value added products (CO.sub.2 conversion), and green hydrogen production (photolysis of water), etc.

(25) In an additional embodiment, the present subject matter relates to a photocatalyst comprising the Au(TiO.sub.2-y/WO.sub.3-x) semiconductor composite as described herein.

(26) In a further embodiment, the present subject matter relates to a method of providing photocatalysis comprising exposing the photocatalyst as described herein to an environment conducive to photocatalysis.

(27) In certain embodiments in this regard, the photocatalysis can be provided by exposing the photocatalyst herein to an environment conducive to photocatalysis. Accordingly, the photocatalysis can be used to provide one or more of organic pollutant degradation, CO.sub.2 greenhouse gas conversion, H.sub.2 production by water photolysis, biodiesel production, energy conservation, and energy storage.

(28) The present subject matter can be better understood by referring to the following examples.

EXAMPLES

Example 1

Preparation of Photocatalyst

(29) Chemical vapor deposition was used to synthesize Au(TiO.sub.2-y/WO.sub.3-x) hybrid powders in a fluidized bed reactor, as schematically illustrated in FIG. 1. The fluidized bed reactor was made of quartz glass having dimensions of 35 mm diameter and 30 mm length and equipped with a porous stainless-steel disc of pore size 20 ?m installed at the bottom and employed as the gas distributor. At the reactor outlet a porous stainless steel filter element with a 10 ?m pore size was utilized to make sure that no powder particles make their way to the scrubber. High-purity nitrogen served as both a carrier gas and a fluidizing gas during the delivery of the precursor. Mass flow controllers (MKS Instruments, model 1179A) were used to regulate the flow rates. In order to detect the pressure drop across the powder bed and calculate the minimum fluidization velocity, pressure transducers (model Omega PX277) were positioned above the distributor plate and at the fluidization column's outlet.

(30) The synthesis condition is shown in Table 1, below. Firstly, the WO.sub.3 powders were prepared by crash precipitation method from the ammonium paratungstate (NH.sub.4).sub.10H.sub.2(W.sub.2O.sub.7).sub.6) as tungsten precursor. 20 g of the WO.sub.3 powder was charged into the reactor followed by supplying nitrogen to maintain a normalized pressure drop ?P/?P.sub.o of unity for fluidization, the bed height was 0.55 (H/H.sub.o). The ?P/?P.sub.o is defined as the ratio of the pressure drop throughout the entire bed to the normal pressure brought about by the particle weight, represented by the equation ?P.sub.o=mg A.sup.?1, where A is the fluidized bed column's cross-sectional area and m is the weight of the particles in the bed. Secondly, continuous supply of titanium precursor (TiCl.sub.4), hydrogen, and Au water (Tetrachloroaurate(III) trihydrate (HAuCl.sub.4.Math.3H.sub.2O) dissolved in deionized water) was made possible using the inert nitrogen as carrier gas to produce the In-situ Au(TiO.sub.2-y/WO.sub.3-x) hybrid nano powders.

(31) TABLE-US-00001 TABLE 1 Synthesis condition of Au-(TiO.sub.2?y-WO.sub.3?x) nanoparticles Bed Carrier nitrogen (N.sub.2) gas flow temperature TiCl.sub.4 Au-H.sub.2O 5% H.sub.2 Sample (? C.) ml min.sup.?1 ml min.sup.?1 ml min.sup.?1 Au-(TiO.sub.2?WO.sub.3?x) 600 70 70 135

(32) The textural properties of the prepared Au(TiO.sub.2-y/WO.sub.3-x) powder by N.sub.2 physisorption are shown in Table 2, below.

(33) TABLE-US-00002 TABLE 2 Textural properties of the prepared Au-(TiO.sub.2?y/WO.sub.3?x) powder by N.sub.2 physisorption BET Pore Total pore surface diameter volume Sample area (m.sup.2 g.sup.?1) (nm) (cm.sup.3 g.sup.?1) Au-(TiO.sub.2?y/WO.sub.3?x) 260 3.7 0.58

(34) In comparison to conventional techniques, including, for example, sol-gel, hydrothermal, chemical vapor deposition, precipitation, microwave, solvothermal, laser ablation etc., the proposed method produced a novel photocatalyst (AuTiO.sub.2-y/WO.sub.3-x) with enhanced activity under light illumination as well in the dark (absence of light) due to its higher specific surface area and mesoporosity, excellent homogeneity, good contact between the two semiconductors and improved UV-Vis-NIR range light photons absorption and energy storage ability. The photocatalyst can be employed in organic pollutant degradation, CO.sub.2 greenhouse conversion, H.sub.2 production by water photolysis, biodiesel production and for energy conservation and storage etc.

Example 2

Characterization of Photocatalyst

(35) FIG. 2A shows the X-ray diffractogram (XRD) of the prepared crystalline hybrid sample (Au(TiO.sub.2-y/WO.sub.3-x)) by Fluidized bed chemical vapor deposition method. The crystalline peaks observed for tetragonal anatase TiO.sub.2-y(ICDD ref. card no. 21-1272) at 2? position were at 25.2? (101), 38.0? (004), 48.2? (200), 53.8? (116), and 55.1? (200), while for monoclinic WO.sub.3-x(ICDD ref. card no. 43-1035) the peaks position at 2? position were at 23.1? (002), 23.6? (020), 24.3? (020), 27.7? (112), 33.4? (022), 34? (202), 41.8? (222) and 49.9? (400). Moreover, no characteristic peak was observed for the dopant gold (Au), this might be due to its relatively very weak diffraction intensity or low content of gold.

(36) FIG. 2B shows the Raman spectrum of the synthesized powder. The peaks observed at 145.0 cm.sup.?1 (1-E.sub.g), 396.0 cm.sup.?1 (B.sub.1g), 520.0.sup.cm?1 (A.sub.1g) and 6421 cm.sup.?1 (3-E.sub.g) are typical of the tetragonal anatase TiO.sub.2 structure, while for the monoclinic WO.sub.3 the characteristic peaks were observed at 272.0 cm.sup.?1 (W-O-W), 717.0 cm.sup.?1 (O-W-O) and 807.1 cm.sup.?1 (W-O-W).

(37) FIG. 2C portrays the field emission scanning electron microscope (FESEM) image of the prepared powder. The TiO.sub.2-y particles are in a spherical shape having a smooth surface, while the WO.sub.3-x particles exhibit a needle shape structure. In addition, both the semiconductors photocatalyst are uniformly distributed. The homogeneity is further confirmed by the SEM-EDX analysis, the elemental mapping is shown in FIG. 2D, which illustrates the even distribution of Ti (titanium) and W (tungsten) throughout the hybrid composite. This implies a high degree of contact between TiO.sub.2 and WO.sub.3-x semiconductors photocatalyst.

(38) It is to be understood that the present methods and products are not limited to the specific embodiments described above, but encompasses any and all embodiments within the scope of the generic language of the following claims enabled by the embodiments described herein, or otherwise shown in the drawings or described above in terms sufficient to enable one of ordinary skill in the art to make and use the claimed subject matter.