INSTALLATION FOR RECYCLING COMPOSITE MATERIALS WITH CARBON FIBER AND/OR GLASS FIBER REINFORCEMENT AND METHOD FOR RECYCLING IN SAID INSTALLATION

Abstract

The invention relates to a installation (4) for recycling composite materials comprising a horizontal reactor (5) with a first zone (1), second zone (2) and third zone (3), which are leak-tight and independent, aligned with and separated from one another by means of gates that allow the passage of the composite material to be recycled only when the process has ended in a previous zone. The first zone (1) comprises a rotation mechanism (9) for rotating the material and gas outlet means (8). The second zone (2) comprises air injectors (10) and gas outlet means (11). The third zone (3) comprises cooling means.

The invention also relates to a method for recycling composite materials comprising a first pyrolysis phase, a second gassing phase for gassing the material resulting from the first phase, and a third cooling phase for cooling the reinforcement material.

Claims

1. An installation (4) for recycling composite materials with carbon fiber and/or glass fiber reinforcement, wherein said reinforcement is contained in a matrix with which said composite material is formed, characterized in that it comprises a horizontal reactor (5) split into a first zone (1), second zone (2) and third zone (3), which are leak-tight and independent, arranged aligned with and separated from one another by means of respective separation gates (6) that allow the passage of the composite material to be recycled from a previous zone to the next zone only when the process has ended in said previous zone, wherein the first zone (1) further comprises an intake gate (7) for taking in the composite material, a rotation mechanism (9) for rotating said composite material and first gas outlet means (8) for the gases generated by the decomposition of the matrix, wherein the second zone (2) comprises air injectors (10) and second gas outlet means (11) for the gases generated by air reacting with matrix residues, and wherein the third zone (3) comprises an outlet gate (12) for the reinforcement material and cooling means for cooling the reinforcement material.

2. The installation (4) for recycling composite materials with carbon fiber and/or glass fiber reinforcement according to claim 1, characterized in that it comprises a drive mechanism for the passage of the resulting composite from the first zone (1) to the second zone (2).

3. The installation (4) for recycling composite materials with carbon fiber and/or glass fiber reinforcement according to claim 1, characterized in that it comprises a drive mechanism for the passage of the resulting material from the second zone (2) to the third zone (3).

4. The installation (4) for recycling composite materials with carbon fiber and/or glass fiber reinforcement according to claim 1, characterized in that the cooling means of the third zone (3) is formed by a coil (13) cooled by means of the passage of water.

5. The installation (4) for recycling composite materials with carbon fiber and/or glass fiber reinforcement according to claim 1, characterized in that the horizontal reactor (5) has a shell (16) made of aluminum, at least on an inner surface thereof.

6. A method for recycling composite materials with carbon fiber and/or glass fiber reinforcement, wherein said reinforcement is contained in a matrix with which said composite material is formed and wherein the method comprises: providing an installation (4) comprising a horizontal reactor (5) split into a first zone (1), second zone (2) and third zone (3), which are leak-tight and independent, arranged aligned with and separated from one another by means of respective separation gates (6) that allow the passage of the composite material to be recycled from a previous zone to the next zone only when the process has ended in said previous zone, wherein the first zone (1) further comprises an intake gate (7) for taking in the composite material, a rotation mechanism (9) for rotating said composite material and first gas outlet means (8) for the gases generated by the decomposition of the matrix, wherein the second zone (2) comprises air injectors (10) and second gas outlet means (11) for the gases generated by air reacting with matrix residues, and wherein the third zone (3) comprises an outlet gate (12) for the reinforcement material and cooling means for cooling the reinforcement material; a first phase consisting of pyrolysis, wherein the composite material enters the first zone (1), which is leak-tight and independent of the horizontal reactor (5) in which it is heated to a temperature comprised between 500 and 700 C. in a controlled atmosphere with an absence of oxygen, and with continuous rotational movement; wherein in this first phase, the matrix thermally decomposes without combusting, generating an exit of gases due to the decomposition thereof, the composite resulting from this first phase being a combination of the reinforcement material and matrix residues; a second phase consisting of gassing the material resulting from the first phase, wherein when the process performed in the first zone (1) ends, the resulting material enters the second zone (2), which is leak-tight and independent of the horizontal reactor (5) in which air intake is performed at the same time the resulting composite is heated to a temperature comprised between 500 and 700 C., keeping same in a fixed position; wherein the air introduced in this second phase reacts with the matrix residues, generating the exit of gases due to said reaction, the material resulting from this second phase being reinforcement material; and a third phase consisting of the entrance of the reinforcement material in the third zone (3), which is leak-tight and independent of the horizontal reactor (5), when the process performed in the second zone (2) ends, it being in this third zone (3) where the cooling of the reinforcement material by cooling means is performed.

7. The method according to claim 6, wherein the installation (4) comprises a drive mechanism for the passage of the resulting composite from the first zone (1) to the second zone (2).

8. The method according to claim 6, wherein the installation (4) comprises a drive mechanism for the passage of the resulting material from the second zone (2) to the third zone (3).

9. The method according to claim 6, wherein the cooling means of the third zone (3) is formed by a coil (13) cooled by means of the passage of water.

10. The method according to claim 6, wherein the horizontal reactor (5) has a shell (16) made of aluminum, at least on an inner surface thereof.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0046] For the purpose of helping to better understand the features of the invention according to a preferred practical embodiment thereof, a series of drawings is provided as an integral part of said description in which the following is depicted with an illustrative and non-limiting character:

[0047] FIG. 1 shows a schematic view of a longitudinal section of the installation for recycling composite materials with carbon fiber and/or glass fiber reinforcement, for a preferred embodiment of the invention.

[0048] FIG. 2 shows a view of section A-A of the installation for recycling composite materials with carbon fiber and/or glass fiber reinforcement for a preferred embodiment of the invention.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT OF THE INVENTION

[0049] In view of the drawings, it can be seen how in a preferred embodiment of the invention, the installation 4 for recycling composite materials with carbon fiber and/or glass fiber reinforcement, said reinforcement being contained in a matrix together with the one forming said composite material herein proposed comprises a horizontal reactor 5 split into a first zone 1, a second zone 2 and a third zone 3, which are leak-tight and independent, arranged aligned with and separated from one another by means of respective separation gates 6 that allow the passage of the composite material to be recycled from a previous zone to the next zone only when the process has ended in said previous zone.

[0050] In this preferred embodiment of the invention, we consider that the composite material is formed by a polymer matrix, a polyester, for example, and a reinforcement consisting of carbon fiber.

[0051] As shown in FIG. 1, the first zone 1 comprises an intake gate 7 for taking in the composite material and first gas outlet means 8 for the gases generated by the decomposition of the matrix.

[0052] As can be seen in FIG. 2, this first zone 1 further comprises a rotation mechanism 9 for rotating the composite material to achieve a homogenous temperature throughout the material to be decomposed.

[0053] As shown in FIG. 1, the second zone 2 comprises air injectors 10 and second gas outlet means 11 for the gases generated by air reacting with matrix residues.

[0054] In this preferred embodiment of the invention, the air reaches the injectors through an air intake 17 with a flow rate regulator 18 for regulating the air flow. The injectors in this case have diffusers.

[0055] It can also be seen in said FIG. 1 that the third zone 3 comprises an outlet gate 12 for the reinforcement material and cooling means for cooling the reinforcement material, i.e., the carbon fiber that was part of the initial composite material.

[0056] In this preferred embodiment of the invention, said cooling means, as shown in FIG. 1, are formed by a coil 13 cooled by means of the passage of water introduced through a cooling water intake 14 and after running through the coil 13 cooling the reinforcement material, it exits through a cooling water outlet 15.

[0057] In this preferred embodiment of the invention, the installation 4 for recycling comprises a drive mechanism (not depicted in the drawings) for the passage of the resulting composite from the first zone 1 to the second zone 2, and likewise another drive mechanism (not depicted in the drawings) for the passage of the resulting material from the second zone 2 to the third zone 3.

[0058] The horizontal reactor 5 of this preferred embodiment of the invention has shell 16 made of aluminum, at least on the inner surface thereof.

[0059] This specification further proposes a method for recycling composite materials formed in this case by polyester with carbon fiber reinforcement by means of the installation 4 defined above. This method comprises a first phase, a second phase and a third phase.

[0060] The first phase is performed in the first zone 1 of the horizontal reactor 5 of the installation 4 for recycling, and in order for this first phase to start, the composite material enters said first zone 1 and the gates 6, 7 thereof are closed so that it is a zone that is leak-tight and independent of the second zone 2 arranged right after it.

[0061] In this first phase, pyrolysis is performed on the composite material, heating it to a temperature comprised between 500 and 700 C. in a controlled atmosphere with an absence of oxygen, and with continuous rotational movement to assure homogeneity of the temperature in the material.

[0062] The matrix formed by the polyester thereby thermally decomposes without combusting. The composite resulting from this first phase is a combination of the reinforcement material, in this case carbon fiber, and matrix residues, which are condensable liquids and non-condensable gases generated by decomposition of the matrix. These gases are pushed out by means of the first gas outlet means 8.

[0063] Once this pyrolysis process ends, the separation gate 6 between the first zone 1 and the second zone 2 is opened and the resulting material goes to said second zone 2, wherein the second phase of the method starts once this separation gate 6 is closed again, such that the second zone 2 is leak-tight and independent of the first zone 1 and the third zone 3, which are arranged before and after same.

[0064] This second phase consists of gassing the material resulting from the first phase by means of an air intake in the second zone 2 through air injectors 10. The air intake is performed at the same time the resulting composite is heated to a temperature comprised between 500 and 700 C. In this second phase, the material is arranged on a fixed support 19, such that it is kept in a fixed, non-rotating position.

[0065] The air that is introduced reacts with matrix residues, generating the exit of gases due to said reaction, the material resulting from this second phase being the reinforcement material, in this case carbon fiber.

[0066] Then once this phase ends, the separation gate 6 between the second zone 2 and the third zone 3 is opened and the reinforcement material obtained goes to said third zone 3. Now said separation gate 6 closes again. Since the outlet gate 12 is also kept closed, the third zone 3 is a zone which is leak-tight and independent and after that time the third phase of the method can start.

[0067] Said third phase consists of cooling the reinforcement material, i.e., the obtained carbon fiber, by the cooling means. Once cooled, the carbon fiber exits the third zone 3 through the outlet gate 12 and the process ends.

[0068] The described embodiment is only an example of the present invention. Therefore, the details, terms and specific phrases used herein must not be considered to be limiting, but rather must be understood only as a basis for the claims and as a representative basis providing a comprehensible description, and providing sufficient information to the person skilled in the art in order to apply the present invention.

[0069] Significant improvements are achieved over the prior art with the installation and method for recycling composite materials with carbon fiber and/or glass fiber reinforcement herein proposed.

[0070] Therefore, this installation, which allows performing three phases independently, allows for a reinforcement material with a higher quality than when the phases intermingle as they are performed in one and the same chamber continuously. At the same time, this installation allows reusing the gases resulting from the decomposition of the matrix. Furthermore, the fibers are obtained with the same nature that they had from the start, i.e., they are not cut or ground, so they can be reused in many uses.

[0071] Performing the three phases also contributes to a higher quality of the material obtained as a result of the rotation of the material performed in the first phase and the fixed position it keeps in the second.

[0072] All this results in an installation for recycling and a method for recycling that are very effective, resulting in a high quality reinforcement material and gases that can be reused, and all this at a low cost and with enormous simplicity of the installation.